KR101667263B1 - Apparatus for and Method of manufacturing Complex waterproof sheet with multiple overlap construction and Complex waterproof sheet with multiple overlap construction manufactured thereby - Google Patents

Apparatus for and Method of manufacturing Complex waterproof sheet with multiple overlap construction and Complex waterproof sheet with multiple overlap construction manufactured thereby Download PDF

Info

Publication number
KR101667263B1
KR101667263B1 KR1020140148607A KR20140148607A KR101667263B1 KR 101667263 B1 KR101667263 B1 KR 101667263B1 KR 1020140148607 A KR1020140148607 A KR 1020140148607A KR 20140148607 A KR20140148607 A KR 20140148607A KR 101667263 B1 KR101667263 B1 KR 101667263B1
Authority
KR
South Korea
Prior art keywords
film
nonwoven fabric
coating
finished product
semi
Prior art date
Application number
KR1020140148607A
Other languages
Korean (ko)
Other versions
KR20160050463A (en
Inventor
채혁수
윤세한
Original Assignee
주식회사 한보엔지니어링
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 한보엔지니어링 filed Critical 주식회사 한보엔지니어링
Priority to KR1020140148607A priority Critical patent/KR101667263B1/en
Publication of KR20160050463A publication Critical patent/KR20160050463A/en
Application granted granted Critical
Publication of KR101667263B1 publication Critical patent/KR101667263B1/en

Abstract

본 발명은 건축물의 옥상 바닥면, 수처리 시설 구조물의 내부면, 지하구조물 슬래브 또는 외벽면, 터널, 교량 슬래브면 등의 방수시공에 사용되는 필름 삽입형태의 다중 겹침 구조를 가지는 복합방수시트 제조장치 및 제조방법 및 그에 의해 제조된 복합방수시트에 관한 것으로, 제1 부직포를 제공하는 제1 부직포제공부; 상기 제1 부직포제공부로부터 제공되는 제1 부직포를 코팅하기 위한 제1 코팅제를 제공하는 제1 코팅제공부; 상기 제1 코팅제공부로부터 제공되는 제1 코팅제에 필름을 제공하기 위한 필름제공부; 상기 제1 부직포제공부로부터 제공받은 제1 부직포와 상기 제1 코팅제공부로부터 제공받은 제1 코팅제와 상기 필름제공부에서 제공받은 필름을 압출부착하여 반제품으로 생성하는 제1 압출부착부; 상기 제1 압출부착부로부터 생성된 반제품을 코팅하기 위한 제2 코팅제를 제공하는 제2 코팅제공부; 상기 제2 코팅제공부로부터 제공되는 제2 코팅제에 제2 부직포를 제공하는 제2 부직포제공부; 및 상기 제1 압출부착부로부터 생성된 반제품과 상기 제2 코팅제공부로부터 제공받은 제2 코팅제와 상기 제2 부직포제공부로부터 제공받은 제2 부직포를 압출부착하여 완제품으로 생성하기 위한 제2 압출부착부를 포함한다.The present invention relates to an apparatus for manufacturing a composite waterproof sheet having a multi-layer structure of a film insertion type used for waterproof construction such as a roof top floor of a building, an inner surface of a water treatment facility structure, a slab or an outer wall surface of an underground structure, And a composite waterproof sheet produced thereby, comprising: a first nonwoven fabric providing unit for providing a first nonwoven fabric; A first coating agent providing a first coating agent for coating the first nonwoven fabric provided from the first nonwoven fabricator; A film supplier for providing a film to the first coating agent provided from the first coating agent study; A first extrusion attachment unit for extruding and attaching a first coating material supplied from the first nonwoven fabric supply unit, a first coating material supplied from the first coating material supply unit, and a film supplied from the film supply unit to produce a semi-finished product; A second coating agent providing a second coating agent for coating the semi-finished product produced from the first extrusion attachment portion; A second nonwoven fabric providing unit for providing a second nonwoven fabric to a second coating material provided from the second coating material study; And a second extrusion attachment unit for extruding and attaching the semi-finished product produced from the first extruded attachment unit, the second coating material provided from the second coating material study and the second nonwoven fabric supplied from the second nonwoven material supply unit to the finished product, .

Description

다중 겹침 구조를 가지는 복합방수시트 제조장치 및 제조방법 및 그에 의해 제조된 복합방수시트{Apparatus for and Method of manufacturing Complex waterproof sheet with multiple overlap construction and Complex waterproof sheet with multiple overlap construction manufactured thereby}BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an apparatus and a method for manufacturing a composite waterproof sheet having a multi-layered structure, and a composite waterproof sheet produced by the method and a composite waterproof sheet,

본 발명은 다중 겹침 구조를 가지는 복합방수시트 제조장치 및 제조방법 및 그에 의해 제조된 복합방수시트에 관한 것으로, 보다 상세하게는 건축물의 옥상 바닥면, 수처리 시설 구조물의 내부면, 지하구조물 슬래브 또는 외벽면, 터널, 교량 슬래브면 등의 방수시공에 사용되는 필름 삽입형태의 다중 겹침 구조를 가지는 복합방수시트 제조장치 및 제조방법 및 그에 의해 제조된 복합방수시트에 관한 것이다.
The present invention relates to an apparatus and a method for manufacturing a composite waterproof sheet having a multi-layer structure, and a composite waterproof sheet manufactured thereby. More particularly, the present invention relates to a roof waterproof sheet, The present invention relates to an apparatus and a method for manufacturing a composite waterproof sheet having a multi-layer structure of a film insertion type used for waterproof construction such as a surface, a tunnel, and a bridge slab surface, and a composite waterproof sheet produced thereby.

일반적으로 방수시트제조는 시트와 도막재를 복합시키는 형태로 공장에서 제작되어 현장에서 옮겨 시공하게 되는데, 이는 시트재와 도막재를 접착제 또는 열융착 공법으로 접착하기 때문에 시트와 도막재의 층간 부착력이 약하여 제품의 품질확보가 곤란하고, 현장 시공시 층간 박리로 인한 문제가 발생될 수 있다.Generally, a waterproof sheet is manufactured in a factory in the form of a combination of a sheet and a coating material, and is transferred from the site. Since the sheet material and the coating material are adhered by an adhesive agent or a heat fusion method, It is difficult to secure the quality of the product, and problems may arise due to interlayer delamination at the time of site construction.

또한, 최근 개발되고 있는 복합방수시트는 코익스트루더(Co-Extruder) 기술을 이용하여 고분자 수지를 직접 분사 코팅하는 방식으로, 그 코팅 과정에서 직접 분사에 의해 필름을 형성시킬 때 이러한 유동성을 가지는 액화 고분자의 직접 코팅방식은 공정결점 등이 발생될 수 있다. 대부분의 복합 방수 시트에서 사용되는 부직포에 직접 분사할 때에는 보통의 부직포가 가지는 표면의 요철로 인해 분사량의 차이가 발생하며, 이러한 분사량의 차이는 시공 후 시공하자의 원인이 될 수 있다.In addition, the recently developed composite waterproof sheet is a method in which a polymer resin is directly spray-coated by a co-extruder technique, and when the film is formed by direct injection in the coating process, Direct coating method of liquefied polymer may cause process defects and the like. When spraying directly onto a nonwoven fabric used in most composite waterproof sheets, there is a difference in the injection amount due to the unevenness of the surface of the ordinary nonwoven fabric, and the difference in the injection amount may cause the construction failure after the construction.

한국등록실용신안 제20-0146233호(1999. 02. 25 등록)는 폴리프로필렌(polypropylene), 폴리에틸렌(polyethylene), 폴리에스테르(polyester) 및 나일론(Nylon 혹은 Polyamide) 등의 합성수지로 이루어진 부직포의 상부에 이들 부직포와 동일한 재료의 합성수지 필름, 그물형 합성사 및 합성수지 마대 등을 라미네이팅(laminating)처리함으로서 소형 금속제품 및 금속제 중량물의 포장과 포장지로서의 사용후 타용도의 합성수지 제품으로 재생이 가능하도록 합성수지 부직포를 이용한 방수 및 방청 포장필름에 관한 것으로, 내부 포장물에 대하여 방수 및 방청효과를 얻기 위한 포장필름에 있어서, 종이 이상의 함침, 흡수력을 갖는 합성수지 부직포에 방청약품을 흡수시킨 방청층(layer)과 상기 방청층에 일체로 부착되는 합성수지층과 망사형 합성사층으로 이루어진 방수층을 포함하여 상기 방청층과 방수층이 동일재료의 합성수지로서의 이루어짐을 특징으로 하는 합성수지 부직포를 이용한 방수 및 방청 포장필름을 제공한다.Korean Registered Utility Model No. 20-0146233 (registered on Feb. 25, 1999) is a nonwoven fabric made of synthetic resin such as polypropylene, polyethylene, polyester and nylon (Nylon or Polyamide) After laminating synthetic resin film, net synthetic yarn and synthetic resin yarn of the same material as those of nonwoven fabric, it is used as packaging and wrapping paper for small metal products and heavy metal products, and then used as a synthetic resin product for other purposes A packaging film for obtaining a waterproof and rustproofing effect on an inner package, comprising a rust preventive layer absorbing rust preventive chemicals in a synthetic resin nonwoven fabric having impregnation and absorption ability higher than paper, And a waterproof layer composed of a synthetic resin layer and a mesh synthetic layer integrally attached thereto Wherein the rust-preventive layer and the water-proof layer are made of the same material as synthetic resin, and a waterproof and rust-protective packaging film using the synthetic resin nonwoven fabric.

한국등록특허 제10-0310941호(2001. 09. 21 등록)는 시공면에 아스팔트와 합성고무 및 기타 첨가제를 혼합하여 박리지 위에 도착하여 제조한 방수시트를 부착하거나 아스팔트와 합성고무라텍스 및 기타 첨가제를 혼합하여 제조한 도막재를 도포한 위에 신율 40100% 인장강도 100200/인 불포화 폴리에스테르의 수지액을 분사 또는 로울링에 의하여 도포한 다음 유리섬유를 깔고 그 위에 폴리에스테르 수지액을 분사 또는 로울링 도포하여 유리섬유에 침투시키는 연결부위가 없는 다층 복합 방수 시공 공법이다.Korean Registered Patent No. 10-0310941 (Registered on Mar. 21, 2001) is a method of applying asphalt, synthetic rubber, and other additives to the surface of a building, , A resin solution of an unsaturated polyester having an elongation of 40100% and a tensile strength of 100200 / is applied by spraying or rolling, and then a glass fiber is laid, and a polyester resin liquid is sprayed or rolled thereon It is a multilayer composite waterproofing method which does not have a connection part to be applied and penetrate into glass fiber.

그러나 상술한 바와 같은 종래의 다중 겹침 구조를 가지는 복합방수시트는, 고분자 수지를 직접 분사하는 방식으로 방수층의 두께가 일정하지 않아 공정 불량을 일으킬 수 있으며 시공 후에도 하자가 많이 발생하는 단점이 있다.
However, the composite waterproof sheet having the above-described conventional multi-layered structure has a disadvantage that the thickness of the waterproof layer is not uniform due to the direct spraying of the polymer resin, which may cause a process failure and cause a lot of defects even after the application.

한국등록실용신안 제20-0146233호Korean Registered Utility Model No. 20-0146233 한국등록특허 제10-0310941호Korean Patent No. 10-0310941

본 발명이 이루고자 하는 기술적 과제는, 전술한 바와 같은 문제점을 해결하기 위한 것으로, 건축물의 옥상 바닥면, 수처리 시설 구조물의 내부면, 지하구조물 슬래브 또는 외벽면, 터널, 교량 슬래브면 등의 방수시공에 사용되는 필름 삽입형태의 다중 겹침 구조를 가지는 복합방수시트 제조장치 및 제조방법 및 그에 의해 제조된 복합방수시트에 관한 것이다.
SUMMARY OF THE INVENTION The present invention has been made in order to solve the above-mentioned problems, and it is an object of the present invention to provide a waterproofing structure for a roof top floor of a building, an inner surface of a water treatment facility structure, an underground structure slab or an outer wall surface, a tunnel, a bridge slab surface, An apparatus and a method for manufacturing a composite waterproof sheet having a multi-layer structure of a film insertion type used, and a composite waterproof sheet produced thereby.

이러한 과제를 해결하기 위해, 본 발명의 한 특징에 따르면, 제1 부직포를 제공하는 제1 부직포제공부; 상기 제1 부직포제공부로부터 제공되는 제1 부직포를 코팅하기 위한 제1 코팅제를 제공하는 제1 코팅제공부; 상기 제1 코팅제공부로부터 제공되는 제1 코팅제에 필름을 제공하기 위한 필름제공부; 상기 제1 부직포제공부로부터 제공받은 제1 부직포와 상기 제1 코팅제공부로부터 제공받은 제1 코팅제와 상기 필름제공부에서 제공받은 필름을 압출부착하여 반제품으로 생성하는 제1 압출부착부; 상기 제1 압출부착부로부터 생성된 반제품을 코팅하기 위한 제2 코팅제를 제공하는 제2 코팅제공부; 상기 제2 코팅제공부로부터 제공되는 제2 코팅제에 제2 부직포를 제공하는 제2 부직포제공부; 및 상기 제1 압출부착부로부터 생성된 반제품과 상기 제2 코팅제공부로부터 제공받은 제2 코팅제와 상기 제2 부직포제공부로부터 제공받은 제2 부직포를 압출부착하여 완제품으로 생성하기 위한 제2 압출부착부를 포함하는 다중 겹침 구조를 가지는 복합방수시트 제조장치를 제공한다.According to one aspect of the present invention, there is provided a nonwoven fabric comprising: a first nonwoven fabric providing unit for providing a first nonwoven fabric; A first coating agent providing a first coating agent for coating the first nonwoven fabric provided from the first nonwoven fabricator; A film supplier for providing a film to the first coating agent provided from the first coating agent study; A first extrusion attachment unit for extruding and attaching a first coating material supplied from the first nonwoven fabric supply unit, a first coating material supplied from the first coating material supply unit, and a film supplied from the film supply unit to produce a semi-finished product; A second coating agent providing a second coating agent for coating the semi-finished product produced from the first extrusion attachment portion; A second nonwoven fabric providing unit for providing a second nonwoven fabric to a second coating material provided from the second coating material study; And a second extrusion attachment unit for extruding and attaching the semi-finished product produced from the first extruded attachment unit, the second coating material provided from the second coating material study and the second nonwoven fabric supplied from the second nonwoven material supply unit to the finished product, The present invention provides a composite waterproof sheet manufacturing apparatus having a multi-layer structure including a plurality of waterproofing sheets.

일 실시 예에서, 상기 제1 압출부착부로부터 생성된 반제품을 수용하는 반제품수용부를 더 포함하는 것을 특징으로 한다.In one embodiment, the apparatus further includes a semi-finished product accommodating portion for accommodating the semi-finished product generated from the first extrusion attachment portion.

일 실시 예에서, 상기 반제품수용부에서 수용된 반제품을 상기 제2 코팅제공부로 공급하는 반제품공급부를 더 포함하는 것을 특징으로 한다.In one embodiment, the present invention is further characterized by a semi-finished product supply unit for supplying semi-finished products received in the semi-product receiving unit to the second coating member study unit.

일 실시 예에서, 상기 제2 압출부착물에서 생성된 완제품을 서로 감아서 수용하는 완제품수용부를 더 포함하는 것을 특징으로 한다.In one embodiment, the present invention is characterized by further comprising an article receiving portion for winding and receiving the articles produced in the second extrusion attachment.

본 발명의 다른 한 특징에 따르면, 제1 부직포제공부가 제1 부직포를 제공하는 단계; 제1 코팅제공부가 상기 제1 부직포를 코팅하는 제1 코팅제를 제공하는 단계; 필름제공부가 상기 제1 코팅제에 필름을 제공하는 단계; 제1 압출부착부가 상기 제1 부직포와 상기 제1 코팅제와 상기 필름을 압출부착하여 반제품으로 생성하는 단계; 제2 코팅제공부가 상기 반제품을 코팅하기 위한 제2 코팅제를 제공하는 단계; 제2 부직포제공부가 상기 제2 코팅제에 제2 부직포를 제공하는 단계; 및 제2 압출부착부가 상기 반제품과 상기 제2 코팅제와 상기 제2 부직포를 압출부착하여 완제품으로 생성하는 단계를 포함하는 다중 겹침 구조를 가지는 복합방수시트 제조방법을 제공한다.According to another aspect of the present invention, there is provided a method of manufacturing a nonwoven fabric, comprising: providing a first nonwoven fabric providing portion; Providing a first coating for coating the first nonwoven fabric with a first coating material; Providing a film to the first coating agent; Forming a first extruded and adhered portion by extrusion bonding the first nonwoven fabric, the first coating agent, and the film to produce a semi-finished product; Providing a second coating agent for coating the semi-finished article; Providing a second nonwoven fabric to the second coating material; And a second extrusion attachment unit extruding the semi-finished product, the second coating material, and the second nonwoven fabric to produce an article as a finished product.

일 실시 예에서, 반제품수용부가 상기 반제품을 수용하는 단계를 더 포함하는 것을 특징으로 한다.In one embodiment, the semi-finished product receiving portion further includes receiving the semi-finished product.

일 실시 예에서, 반제품공급부가 상기 반제품을 상기 제2 코팅제공부로 공급하는 단계를 더 포함하는 것을 특징으로 한다.In one embodiment, the semi-finished product supply unit further comprises supplying the semi-finished product to the second coating agent curing step.

일 실시 예에서, 완제품수용부가 상기 완제품을 수용하는 단계를 더 포함하는 것을 특징으로 한다.In one embodiment, the finished article receiving portion further comprises receiving the finished article.

본 발명의 또 다른 한 특징에 따르면, 방수층을 이루는 필름; 상기 필름의 양측에 각각 형성되어, 상기 필름을 코팅하여 방수막을 이루는 코팅제; 및 상기 코팅제의 양측에 각각 형성되어, 상기 필름 및 상기 코팅제를 보강하기 위한 부직포를 포함하는 다중 겹침 구조를 가지는 복합방수시트를 제공한다.According to another aspect of the present invention, there is provided a film comprising a waterproof layer; A coating agent formed on both sides of the film to form a waterproof film by coating the film; And a nonwoven fabric formed on both sides of the coating agent for reinforcing the film and the coating agent, respectively, the composite waterproof sheet having a multiple lapping structure.

일 실시 예에서, 상기 필름은, 메탈로센 LLDPE, LDPE, 부텐 LLDPE, 산화방지제, 슬립제를 혼합한 것을 특징으로 한다.
In one embodiment, the film is characterized by a mixture of metallocene LLDPE, LDPE, butene LLDPE, antioxidant, and slip agent.

본 발명에 의하면, 건축물의 옥상 바닥면, 수처리 시설 구조물의 내부면, 지하구조물 슬래브 또는 외벽면, 터널, 교량 슬래브면 등의 방수시공에 사용되는 필름 삽입형태의 다중 겹침 구조를 가지는 복합방수시트 제조장치 및 제조방법 및 그에 의해 제조된 복합방수시트를 제공함으로써, 고분자 필름 양면에 부직포를 부착시키기 위하여 사용한 동일계열의 고분자 수지가 다시 막 형태로 도포되어 다중 겹침 구조를 가지게 됨으로 우수한 방수 성능을 가지는 효과가 있다.
According to the present invention, a composite waterproof sheet having a multi-layer structure of a film insertion type used for waterproof construction such as roof top floor of a building, inner surface of a water treatment facility structure, underground structure slab or outer wall surface, tunnel, bridge slab surface, And a composite waterproof sheet produced by the method, the polymer resin of the same series used for attaching the nonwoven fabric to both surfaces of the polymer film is applied again in a film form to have a multi-layered structure, .

도 1은 본 발명의 실시 예에 따른 다중 겹침 구조를 가지는 복합방수시트 제조장치를 설명하는 도면이다.
도 2는 도 1에 있는 다중 겹침 구조를 가지는 복합방수시트 제조장치의 예를 설명하는 도면이다.
도 3은 본 발명의 실시 예에 따른 다중 겹침 구조를 가지는 복합방수시트 제조방법을 설명하는 도면이다.
도 4는 본 발명의 실시 예에 따른 다중 겹침 구조를 가지는 복합방수시트를 설명하는 도면이다.
도 5 내지 도 7은 도 4에 있는 다중 겹침 구조를 가지는 복합방수시트를 설명하는 이미지이다.1 is a view for explaining an apparatus for producing a composite waterproof sheet having a multi-layer structure according to an embodiment of the present invention.
Fig. 2 is a view for explaining an example of a composite waterproof sheet manufacturing apparatus having the multilayer structure shown in Fig. 1. Fig.
3 is a view for explaining a method of manufacturing a composite waterproof sheet having a multi-layer structure according to an embodiment of the present invention.
4 is a view illustrating a composite waterproof sheet having a multi-layer structure according to an embodiment of the present invention.
5 to 7 are images explaining the composite waterproof sheet having the multi-layered structure shown in Fig.

아래에서는 첨부한 도면을 참고로 하여 본 발명의 실시 예에 대하여 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 상세히 설명한다. 그러나 본 발명에 관한 설명은 구조적 내지 기능적 설명을 위한 실시 예에 불과하므로, 본 발명의 권리범위는 본문에 설명된 실시 예에 의하여 제한되는 것으로 해석되어서는 아니 된다. 즉, 실시 예는 다양한 변경이 가능하고 여러 가지 형태를 가질 수 있으므로 본 발명의 권리범위는 기술적 사상을 실현할 수 있는 균등물들을 포함하는 것으로 이해되어야 한다. 또한, 본 발명에서 제시된 목적 또는 효과는 특정 실시예가 이를 전부 포함하여야 한다거나 그러한 효과만을 포함하여야 한다는 의미는 아니므로, 본 발명의 권리범위는 이에 의하여 제한되는 것으로 이해되어서는 아니 될 것이다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those skilled in the art can easily carry out the present invention. However, the description of the present invention is merely an example for structural or functional explanation, and the scope of the present invention should not be construed as being limited by the embodiments described in the text. That is, the embodiments are to be construed as being variously embodied and having various forms, so that the scope of the present invention should be understood to include equivalents capable of realizing technical ideas. Also, the purpose or effect of the present invention should not be construed as limiting the scope of the present invention, since it does not mean that a specific embodiment should include all or only such effect.

한편, 본 발명에서 서술되는 용어의 의미는 다음과 같이 이해되어야 할 것이다.Meanwhile, the meaning of the terms described in the present invention should be understood as follows.

어떤 구성요소가 다른 구성요소에 "연결되어" 있다고 언급된 때에는, 그 다른 구성요소에 직접적으로 연결될 수도 있지만, 중간에 다른 구성요소가 존재할 수도 있다고 이해되어야 할 것이다. 반면에, 어떤 구성요소가 다른 구성요소에 "직접 연결되어" 있다고 언급된 때에는 중간에 다른 구성요소가 존재하지 않는 것으로 이해되어야 할 것이다. 한편, 구성요소들 간의 관계를 설명하는 다른 표현들, 즉 "~사이에"와 "바로 ~사이에" 또는 "~에 이웃하는"과 "~에 직접 이웃하는" 등도 마찬가지로 해석되어야 한다.It is to be understood that when an element is referred to as being "connected" to another element, it may be directly connected to the other element, but there may be other elements in between. On the other hand, when an element is referred to as being "directly connected" to another element, it should be understood that there are no other elements in between. On the other hand, other expressions that describe the relationship between components, such as "between" and "between" or "neighboring to" and "directly adjacent to" should be interpreted as well.

단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한 복수의 표현을 포함하는 것으로 이해되어야 하고, "포함하다" 또는 "가지다" 등의 용어는 설시된 특징, 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것이 존재함을 지정하려는 것이며, 하나 또는 그 이상의 다른 특징이나 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.It should be understood that the singular " include "or" have "are to be construed as including a stated feature, number, step, operation, component, It is to be understood that the combination is intended to specify that it does not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, or combinations thereof.

여기서 사용되는 모든 용어들은 다르게 정의되지 않는 한, 본 발명이 속하는 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가진다. 일반적으로 사용되는 사전에 정의되어 있는 용어들은 관련 기술의 문맥상 가지는 의미와 일치하는 것으로 해석되어야 하며, 본 발명에서 명백하게 정의하지 않는 한 이상적이거나 과도하게 형식적인 의미를 지니는 것으로 해석될 수 없다.
All terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs, unless otherwise defined. Commonly used predefined terms should be interpreted to be consistent with the meanings in the context of the related art and can not be interpreted as having ideal or overly formal meaning unless explicitly defined in the present invention.

이제 본 발명의 실시 예에 따른 다중 겹침 구조를 가지는 복합방수시트 제조장치 및 제조방법 및 그에 의해 제조된 복합방수시트에 대하여 도면을 참고로 하여 상세하게 설명한다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS An apparatus and a method for manufacturing a composite waterproof sheet having a multi-layer structure according to an embodiment of the present invention and a composite waterproof sheet manufactured thereby will be described in detail with reference to the drawings.

도 1은 본 발명의 실시 예에 따른 다중 겹침 구조를 가지는 복합방수시트 제조장치를 설명하는 도면이다.1 is a view for explaining an apparatus for producing a composite waterproof sheet having a multi-layer structure according to an embodiment of the present invention.

도 1을 참조하면, 복합방수시트 제조장치(A)는 제1 부직포제공부(100), 제1 코팅제공부(200), 필름제공부(300), 제1 압출부착부(400), 제2 코팅제공부(500), 제2 부직포제공부(600) 및 제2 압출부착부(700)를 포함한다.Referring to FIG. 1, the composite waterproof sheet manufacturing apparatus A includes a first nonwoven fabricator 100, a first coating agent study 200, a film supplier 300, a first extrusion attachment unit 400, A coating agent studying unit 500, a second nonwoven fabric providing unit 600, and a second extrusion attaching unit 700.

제1 부직포제공부(100)는 제1 부직포(30a)를 제공하는데, 제1 부직포(30a)는 합성섬유 부직포일 수 있으며, 저분자물질을 연결하여 사슬 모양으로 이어 소정의 고분자물질로 조립함으로써 만들어진다.The first nonwoven fabric providing part 100 provides a first nonwoven fabric 30a which may be a synthetic fiber nonwoven fabric and is formed by connecting low molecular materials to form a chain and assembling them with a predetermined polymer material .

합성된 고분자는 용제로 녹이거나 열로 용융하여 가는 구멍으로부터 압출해서 굳히고 감는다. 방사방법에는 용융, 건식, 습식의 세 가지가 있다. 실 모양이 될 수 있는 고분자는 많지만, 그 중에서 염색성, 내구성, 촉감, 내수성, 내추성, 내열성, 강도, 내마모성 등의 여러 성질이 의료용공업용 목적에 알맞은 것만이 실용적 가치를 가진 합성섬유가 된다. 합성섬유와 플라스틱은 분자구조상 엄격한 구별이 없으며, 합성섬유는 플라스틱이 섬유의 형태로 된 것이라고 할 수 있지만, 실 모양이 아닌 분자로 구성되는 플라스틱은 섬유화가 곤란하다.The synthesized polymer is melted with a solvent or melted by heat, and extruded from holes to be hardened and wound. There are three spinning methods: melting, dry and wet. There are many polymers that can be thread-shaped, but synthetic fibers with practical value are merely suitable for medical industrial purposes, such as dyability, durability, touch, water resistance, shrinkage resistance, heat resistance, strength and abrasion resistance. Synthetic fibers and plastics have no strict distinction in molecular structure. Synthetic fibers can be said to be plastic in the form of fibers, but plastics made of non-threadlike molecules are difficult to fabricate.

일 실시 예에서, 제1 부직포(30a)는 장섬유를 사용하여 만든 부직포일 수 있으며, 전체 면적에 균일한 균제도를 가지기 위해 니들 펀칭 후 연속적인 카렌터링을 하여 제조한다. 장섬유는 무연 또는 약간의 꼬임을 가함으로써 실을 만들 수 있고, 방적의 방법에 의하지 않는다.In one embodiment, the first nonwoven fabric 30a may be a nonwoven fabric made of long fibers, and is manufactured by continuous carotening after needle punching to have a uniform uniformity over the entire area. Long fibers can be threaded by applying no twist or slight twist, and not by spinning method.

제1 코팅제공부(200)는 제1 부직포제공부로부터 제공되는 제1 부직포를 코팅하기 위한 제1 코팅제를 제공한다.The first coating agent study 200 provides a first coating agent for coating the first nonwoven fabric provided from the first nonwoven fabricator.

일 실시 예에서, 제1 코팅제공부(200)는 폴리에틸렌수지를 압출롤링시켜 제1 부직포제공부로부터 제공되는 제1 부직포를 코팅시킬 수 있으며, 이는 필름을 코팅시켜 방수 기능을 높일 수 있다.In one embodiment, the first coating material study 200 may extrude and roll the polyethylene resin to coat the first nonwoven fabric provided from the first nonwoven fabricator, which may enhance the waterproof function by coating the film.

일 실시 예에서, 제1 코팅제공부(200)는 필름과 동일 계열의 고분자 수지가 도포될 수 있으며, 이러한 고분자 수지는 다시 막 형태로 도포되어 다중 겹침으로 인해 방수 기능을 높일 수 있다.In one embodiment, the first coating material study 200 may be coated with the polymer resin of the same series as the film, and the polymer resin may be applied again in a film form to improve the waterproof function due to multiple overlapping.

일 실시 예에서, 제1 코팅제공부(200)는 익스트루더 및 T-Die를 통해 직접 압출되는 필름 양면과 함께 라미네이팅 시킨 다음 냉각 및 권취하여 압출할 수 있다.In one embodiment, the first coating material study 200 may be laminated together with both sides of the film extruded directly through the extruder and T-die, followed by cooling and winding and extrusion.

일 실시 예에서, 제1 코팅제공부(200)는 제1 부직포제공부(100)의 하면에 형성되어 제1 코팅제공부(200)와 제1 부직포제공부(100)가 서로 롤링되어 압출부착될 수 있다.In one embodiment, the first coating material study 200 is formed on the lower surface of the first nonwoven fabricator 100 so that the first coating material study 200 and the first nonwoven material providing unit 100 can be rolled together and extruded have.

필름제공부(300)는 제1 코팅제공부(200)로부터 제공되는 제1 코팅제에 필름을 제공한다.The film supplier 300 provides a film to the first coating material provided from the first coating material studying unit 200.

일 실시 예에서, 필름제공부(300)는 제1 코팅제공부(200)로부터 제공되는 제1 코팅제에 필름을 제공하는데, 여기서 필름은 메탈로센(Metallocene) LLDPE(Linear Low Density Polyethylene Film), LDPE(Low Density Polyethylene), 부텐(butene) LLDPE, 산화방지제, 슬립제를 혼합할 수 있다.In one embodiment, the film supplier 300 provides a film to the first coating material provided from the first coating material study 200, wherein the film is a metallocene LLDPE (Linear Low Density Polyethylene Film), LDPE (Low Density Polyethylene), butene LLDPE, an antioxidant, and a slip agent.

LLDPE(Linear Low Density Polyethylene Film)는 선형저밀도 폴리에틸렌으로 고중량 제품 포장용 필름, 각종 래미네이션 필름, 스트레치용 필름, 특수 산업용 필름, 비닐하우스용 필름 등으로 사용하는 친환경 폴리에틸렌 소재이며, 필름 성형 시에 가공성, 혼련성도 우수하다. 여기서 LLDPE(Linear Low Density Polyethylene Film)는 메탈로센(Metallocene) LLDPE와 부텐(butene) LLDPE일 수 있다.LLDPE (Linear Low Density Polyethylene Film) is a linear low density polyethylene which is an environmentally friendly polyethylene material used for high weight packaging film, various lamination film, stretch film, special industrial film and vinyl house film. It is also excellent in kneading ability. Here, LLDPE (Linear Low Density Polyethylene Film) may be a metallocene LLDPE and a butene LLDPE.

LDPE(Low Density Polyethylene)는 저밀도 폴리에틸렌으로 상온에서 투명한 고체(밀도가 0.91~0.94의 것임)로 결정화가 낮아 가공성과 유연성, 투명성이 우수해 투명필름, 전선피복, 각종 랩 등의 원료로 사용될 수 있다.LDPE (Low Density Polyethylene) is a low-density polyethylene, which is transparent at room temperature and has a low crystallinity (density is 0.91 ~ 0.94). It has excellent processability, flexibility and transparency and can be used as a raw material for transparent film, wire coating and various wraps .

산화방지제는 페닐-베타-나프틸아민계열일 수 있으며, 슬립제는 fatty amide 또는 fatty acid계열일 수 있다.The antioxidant may be phenyl-beta-naphthylamine-based, and the slip agent may be fatty amide or fatty acid series.

일 실시 예에서, 필름은 메탈로센(Metallocene) LLDPE(Linear Low Density Polyethylene Film) 31~33중량%, LDPE(Low Density Polyethylene) 31~33중량%, 부텐(butene) LLDPE 31~33중량%, 산화방지제 1~3중량%, 슬립제 1~3중량%의 함량으로 혼합될 수 있다.In one embodiment, the film comprises 31-33 wt.% Of Metallocene LLDPE (Linear Low Density Polyethylene Film), 31-33 wt.% LDPE (Low Density Polyethylene), 31-33 wt.% Butene LLDPE, 1 to 3% by weight of an antioxidant, and 1 to 3% by weight of a slip.

일 실시 예에서, 필름제공부(300)는 제1 코팅제공부(200)의 하면에 형성되어, 필름제공부(300)와 제1 코팅제공부(200)를 압출부착할 수 있다.In one embodiment, the film supplier 300 may be formed on the lower surface of the first coating material studying unit 200 to extrude and attach the film providing unit 300 and the first coating material studying unit 200.

제1 압출부착부(400)는 제1 부직포제공부(100)로부터 제공받은 제1 부직포와 제1 코팅제공부(200)로부터 제공받은 제1 코팅제와 필름제공부(300)로부터 제공받은 필름을 압출부착하여 반제품으로 생성한다.The first extrusion attachment unit 400 extrudes the first nonwoven fabric supplied from the first nonwoven fabricator 100 and the first coating material supplied from the first coating material study 200 and the film supplied from the film supplier 300, To produce a semi-finished product.

여기서, 제1 압출부착부(400)는 제1 부직포, 제1 코팅제, 필름을 압출부착하여 일체화된 반제품으로 생성될 수 있다.Here, the first extrusion attachment unit 400 may be formed as an integrated semi-finished product by extruding the first nonwoven fabric, the first coating material, and the film.

다중 겹침 구조를 가지는 복합방수시트는 제1 압출부착부(400)로부터 생성된 반제품을 수용하고 수용된 반제품을 제2 코팅제공부(500)로 공급해주기 위해, 반제품수용부(800)와 반제품공급부(900)가 일치된 구조를 가질 수 있다.The composite waterproof sheet having a multilayered structure includes a semi-finished product receiving portion 800 and a semi-finished product supplying portion 900 for receiving the semi-finished product generated from the first extrusion attachment portion 400 and supplying the received semi-finished product to the second coating agent study 500 ) Can be matched.

일 실시 예에서, 반제품수용부(800)는 제1 압출부착부(400)로부터 생성된 반제품을 롤링장치에 의해 롤링되면서 수용될 수 있다. 또한, 반제품수용부(800)는 제1 압출부착부(400)로부터 생성된 반제품을 롤링장치에 의해 롤링되어 수용공간에 수용될 수 있다. 이때의 공정은 제1 부직포, 제2 코팅제, 필름을 일체화 시켜 수용공간에 수용시킬 수 있다.In one embodiment, the semi-finished product receiving portion 800 can be accommodated by rolling the semi-finished product produced from the first extrusion attachment portion 400 by the rolling device. In addition, the semi-finished product accommodating portion 800 can be rolled by the rolling device to be accommodated in the accommodating space after the semi-finished product produced from the first extrusion attachment portion 400 is rolled. At this time, the first nonwoven fabric, the second coating, and the film may be integrated into the receiving space.

일 실시 예에서, 반제품수용부(800)는 제1 압출부착부(400)로부터 생성된 반제품을 롤링장치에 의해 롤링되면서 수용되고, 제2 코팅제공부(500)로 공급해줄 수 있다. 이는 수용공정과 공급공정을 연속적으로 함으로써, 제작 시간을 단축시켜 줄 수 있다. 이러한 다중 겹침 구조를 가지는 복합방수시트는 다중 겹침 구조를 가지도록 하여 우수한 방수 성능을 발휘할 수 있도록 한다.In one embodiment, the semi-finished product receiving unit 800 is accommodated while being rolled by the rolling device and supplied to the second coating material studying unit 500 by the semi-finished product produced from the first extrusion attachment unit 400. This can shorten the production time by making the receiving process and the supplying process continuous. The composite waterproof sheet having such a multi-layered structure has a multi-layered structure to exhibit excellent waterproof performance.

제2 코팅제공부(500)는 제1 압출부착부로부터 생성된 반제품을 코팅하기 위해 제2 코팅제를 제공한다.The second coating agent study 500 provides a second coating agent to coat the semi-finished product produced from the first extrusion attachment.

일 실시 예에서, 제2 코팅제공부(500)는 제1 압출부착부로부터 생성된 반제품의 하면인 필름의 하면에 압출되어 생성될 수 있다.In one embodiment, the second coating material study 500 can be produced by being extruded on the lower surface of the film, which is the lower surface of the semi-finished product produced from the first extrusion attachment portion.

제2 부직포제공부(600)는 제2 코팅제공부로부터 제공되는 제2 코팅제에 제2 부직포를 제공한다.The second nonwoven fabricator 600 provides a second nonwoven fabric to the second coating material provided from the second coating material study.

일 실시 예에서, 제2 부직포제공부(600)는 제2 코팅제공부(500)의 하면에 롤링되면서 제2 코팅제공부(500)와 압출형성될 수 있다.In one embodiment, the second nonwoven fabricator 600 may be extruded with the second coating material 500 while rolling on the lower surface of the second coating material 500.

제2 압출부착부(700)는 제1 압출부착부(400)로부터 생성된 반제품과 제2 코팅제공부(500)로부터 제공받은 제2 코팅제와 제2 부직포제공부로부터 제공받은 제2 부직포를 압출부착하여 완제품으로 생성한다.The second extrusion attachment portion 700 is formed by extruding and bonding the semi-finished product produced from the first extrusion attachment portion 400, the second coating material supplied from the second coating material studying unit 500 and the second nonwoven fabric supplied from the second nonwoven material supply unit To produce finished products.

다중 겹침 구조를 가지는 복합방수시트는 완제품수용부(1000)를 포함할 수 있으며, 완제품수용부(1000)는 제2 압출부착부(700)에서 생성된 완제품을 서로 감아서 수용할 수 있다.
The composite waterproof sheet having the multiple overlap structure may include the finished product receiving portion 1000 and the finished product receiving portion 1000 may be wound around the finished products produced in the second extrusion attachment portion 700 and accommodated.

도 2는 도 1에 있는 다중 겹침 구조를 가지는 복합방수시트 제조장치의 예를 설명하는 도면이다.Fig. 2 is a view for explaining an example of a composite waterproof sheet manufacturing apparatus having the multilayer structure shown in Fig. 1. Fig.

도 2를 참조하면, 다중 겹침 구조를 가지는 복합방수시트는 제1 압출부착부(400)로부터 생성된 반제품을 수용하고, 수용된 반제품을 제2 코팅제공부(500)로 공급해주기 위해 반제품수용부(800)와 반제품공급부(900)가 분리된 구조를 가질 수 있다.Referring to FIG. 2, the composite waterproof sheet having a multi-layered structure includes a semi-finished product receiving part 800 for receiving the semi-finished product produced from the first extrusion attachment part 400 and supplying the received semi-finished product to the second coating material studying part 500 And the semi-finished product supply unit 900 may be separated from each other.

일 실시 예에서, 반제품공급부(900)는 반제품수용부(800)에 수용된 반제품을 제2 코팅제공부(500)로 공급하도록 이송시킨 후 공정을 수행할 수 있다. 반제품공급부(900)는 롤링 이송장치에 넣고 롤링된 반제품을 풀어서 공급해준다. 이는 공정을 연속적으로 수행하지 않고 1회에 필름 일면에 제1 부직포를 압출부착시킨 뒤에 반제품공급부(900)로 이송시켜 2회에 필름 다른 일면에 제2 부직포를 압출부착시키는 구조를 함으로써, 불량을 최소화시킬 수 있어 효과적이다. 이러한 다중 겹침 구조를 가지는 복합방수시트는 다중 겹침 구조를 가지도록 하여 우수한 방수 성능을 발휘할 수 있도록 한다.
In one embodiment, the semi-finished product supply unit 900 may carry out a process after the semi-finished product accommodated in the semi-product receiving unit 800 is fed to the second coating material study unit 500. The semi-finished product supply unit 900 is fed into a rolling conveying unit to unroll and supply the rolled semi-finished product. This is because the first nonwoven fabric is extruded and adhered to one side of the film at one time, and the second nonwoven fabric is extruded and adhered to the other side of the film two times by being fed to the semi-finished product supply unit 900, It can be minimized and effective. The composite waterproof sheet having such a multi-layered structure has a multi-layered structure to exhibit excellent waterproof performance.

도 3은 본 발명의 실시 예에 따른 다중 겹침 구조를 가지는 복합방수시트 제조방법을 설명하는 도면이다.3 is a view for explaining a method of manufacturing a composite waterproof sheet having a multi-layer structure according to an embodiment of the present invention.

도 3을 참조하면, 다중 겹침 구조를 가지는 복합방수시트 제조방법은 제1 부직포를 제공하는 단계(S100), 제1 코팅제를 제공하는 단계(S200), 필름을 제공하는 단계(S300), 반제품으로 생성하는 단계(S400), 제2 코팅제를 제공하는 단계(S500), 제2 부직포를 제공하는 단계(S600) 및 완제품으로 생성하는 단계(S700)를 포함한다.Referring to FIG. 3, a method for manufacturing a composite waterproof sheet having a multi-layer structure includes steps of providing a first nonwoven fabric (S100), providing a first coating material (S200), providing a film (S300) (S500), providing a second coating (S500), providing a second nonwoven fabric (S600), and creating a finished product (S700).

제1 부직포를 제공하는 단계(S100)는 제1 부직포제공부(100)가 제1 부직포(30a)를 제공하는데, 제1 부직포(30a)는 합성섬유 부직포일 수 있으며, 저분자물질을 연결하여 사슬 모양으로 이어 소정의 고분자물질로 조립함으로써 만들어진다.The step of providing the first nonwoven fabric (S100) may include providing the first nonwoven fabric (100) with a first nonwoven fabric (30a), which may be a synthetic fiber nonwoven fabric, And then assembled with a predetermined polymer material.

일 실시 예에서, 제1 부직포를 제공하는 단계(S100)는 제1 부직포를 롤링하는 단계(미도시)를 포함할 수 있으며, 제1 부직포를 롤링하는 단계(미도시)는 롤링 장치로 롤링된 제1 부직포(30a)를 풀어서 제1 부직포(30a)를 제공해줄 수 있다.In one embodiment, step S100 of providing the first nonwoven may comprise rolling (not shown) of the first nonwoven, wherein rolling (not shown) of the first nonwoven may comprise rolling The first nonwoven fabric 30a may be loosened to provide the first nonwoven fabric 30a.

제1 코팅제를 제공하는 단계(S200)는 제1 코팅제공부(200)가 제1 부직포(30a)를 코팅하는 제1 코팅제(20a)를 제공한다.The step S200 of providing the first coating agent provides the first coating agent 20a coating the first nonwoven fabric 30a with the first coating agent study 200. [

일 실시 예에서, 제1 코팅제공부(200)는 폴리에틸렌수지를 압출롤링시켜 제1 부직포제공부로부터 제공되는 제1 부직포를 코팅시킬 수 있으며, 이는 필름을 코팅시켜 방수 기능을 높일 수 있다.In one embodiment, the first coating material study 200 may extrude and roll the polyethylene resin to coat the first nonwoven fabric provided from the first nonwoven fabricator, which may enhance the waterproof function by coating the film.

일 실시 예에서, 제1 코팅제공부(200)는 필름과 동일 계열의 고분자 수지가 도포될 수 있으며, 이러한 고분자 수지는 다시 막 형태로 도포되어 다중 겹침으로 인해 방수 기능을 높일 수 있다.In one embodiment, the first coating material study 200 may be coated with the polymer resin of the same series as the film, and the polymer resin may be applied again in a film form to improve the waterproof function due to multiple overlapping.

일 실시 예에서, 제1 코팅제공부(200)는 익스트루더 및 T-Die를 통해 직접 압출되는 필름 양면과 함께 라미네이팅 시킨 다음 냉각 및 권취하여 압출할 수 있다.In one embodiment, the first coating material study 200 may be laminated together with both sides of the film extruded directly through the extruder and T-die, followed by cooling and winding and extrusion.

일 실시 예에서, 제1 코팅제공부(200)는 제1 부직포제공부(100)의 하면에 형성되어 제1 코팅제공부(200)와 제1 부직포제공부(100)가 서로 롤링되어 압출부착될 수 있다.In one embodiment, the first coating material study 200 is formed on the lower surface of the first nonwoven fabricator 100 so that the first coating material study 200 and the first nonwoven material providing unit 100 can be rolled together and extruded have.

필름을 제공하는 단계(S300)는 필름제공부(300)가 제1 코팅제(20a)에 필름을 제공한다.Providing the film (S300), the film supplier (300) provides the film to the first coating (20a).

일 실시 예에서, 필름을 제공하는 단계(S300)는 필름제공부(300)가 제1 코팅제공부(200)로부터 제공되는 제1 코팅제(20a)에 필름을 제공하는데, 여기서 필름은 메탈로센(Metallocene) LLDPE(Linear Low Density Polyethylene Film), LDPE(Low Density Polyethylene), 부텐(butene) LLDPE, 산화방지제, 슬립제를 혼합할 수 있다.In one embodiment, providing the film (S300) includes providing the film to the first coating (20a) provided by the film supplier (300) from the first coating study (200), wherein the film is metallocene Metallocene LLDPE (Low Density Polyethylene Film), LDPE (Low Density Polyethylene), butene LLDPE, antioxidant and slip agent.

일 실시 예에서, 필름을 제공하는 단계(S300)는 메탈로센(Metallocene) LLDPE(Linear Low Density Polyethylene Film) 31~33중량%, LDPE(Low Density Polyethylene) 31~33중량%, 부텐(butene) LLDPE 31~33중량%, 산화방지제 1~3중량%, 슬립제 1~3중량%의 함량으로 혼합된 필름을 제공할 수 있다.In one embodiment, the step of providing the film (S300) comprises 31 to 33 wt% of Metallocene LLDPE (Linear Low Density Polyethylene Film), 31 to 33 wt% of LDPE (Low Density Polyethylene) 31 to 33% by weight of LLDPE, 1 to 3% by weight of an antioxidant, and 1 to 3% by weight of a slip.

반제품으로 생성하는 단계(S400)는 제1 압출부착부(400)가 제1 부직포(30a)와 제1 코팅제(20a)와 필름(10)을 압출부착하여 반제품으로 생성한다.In step S400 of producing a semi-finished product, the first extrusion attachment unit 400 extrudes and attaches the first nonwoven fabric 30a, the first coating agent 20a, and the film 10 to produce a semi-finished product.

여기서, 제1 압출부착부(400)는 제1 부직포(30a), 제1 코팅제(20a), 필름(10)을 압출부착하여 일체화된 반제품으로 생성될 수 있다.The first extrusion attachment portion 400 may be formed as an integrated semi-finished product by extruding the first nonwoven fabric 30a, the first coating material 20a, and the film 10.

다중 겹침 구조를 가지는 복합방수시트는 반제품을 수용하는 단계(S800)를 포함할 수 있으며, 반제품을 수용하는 단계(S800)는 반제품수용부(800)가 반제품을 수용하도록 한다.The composite waterproof sheet having the multiple overlap structure may include a step S800 of receiving the semi-finished product, and the step S800 of receiving the semi-finished product allows the semi-finished product receiving portion 800 to receive the semi-finished product.

일 실시 예에서, 반제품을 수용하는 단계(S800)는 제1 압출부착부(400)로부터 생성된 반제품을 롤링장치에 의해 롤링되면서 반제품수용부(800)에 수용될 수 있다. 또한, 반제품수용부(800)는 제1 압출부착부(400)로부터 생성된 반제품을 롤링장치에 의해 롤링되어 수용공간에 수용될 수 있다. 이때의 공정은 제1 부직포, 제2 코팅제, 필름을 일체화 시켜 수용공간에 수용시킬 수 있다.In one embodiment, the step S800 of accepting the semi-finished product can be accommodated in the semi-finished product receiving portion 800 while rolling the semi-finished product produced from the first extrusion attachment portion 400 by the rolling device. In addition, the semi-finished product accommodating portion 800 can be rolled by the rolling device to be accommodated in the accommodating space after the semi-finished product produced from the first extrusion attachment portion 400 is rolled. At this time, the first nonwoven fabric, the second coating, and the film may be integrated into the receiving space.

다중 겹침 구조를 가지는 복합방수시트는 공급하는 단계(S900)를 포함할 수 있으며, 공급하는 단계(S900)는 반제품공급부(900)가 반제품을 제2 코팅제공부(500)로 공급한다.The composite waterproof sheet having a multi-layer structure may include a supply step S900, and in the supplying step S900, the semi-finished product supply unit 900 supplies the semi-finished product to the second coating solution studying unit 500. [

일 실시 예에서, 공급하는 단계(S900)는 반제품공급부(900)가 반제품수용부(800)에 수용된 반제품을 제2 코팅제공부(500)로 공급하도록 이송시킨 후 공정을 수행할 수 있다. 반제품공급부(900)는 롤링 이송장치에 넣고 롤링된 반제품을 풀어서 공급해준다. 이는 공정을 연속적으로 수행하지 않고 1회에 필름 일면에 제1 부직포를 압출부착시킨 뒤에 반제품공급부(900)로 이송시켜 2회에 필름 다른 일면에 제2 부직포를 압출부착시키는 구조를 함으로써, 불량을 최소화시킬 수 있어 효과적이다. 이러한 다중 겹침 구조를 가지는 복합방수시트는 다중 겹침 구조를 가지도록 하여 우수한 방수 성능을 발휘할 수 있도록 한다.In one embodiment, the supplying step S900 may carry out the process after the semi-finished product supplying unit 900 transfers the semi-finished product accommodated in the semi-finished product receiving unit 800 to the second coating material studying unit 500. [ The semi-finished product supply unit 900 is fed into a rolling conveying unit to unroll and supply the rolled semi-finished product. This is because the first nonwoven fabric is extruded and adhered to one side of the film at one time, and the second nonwoven fabric is extruded and adhered to the other side of the film two times by being fed to the semi-finished product supply unit 900, It can be minimized and effective. The composite waterproof sheet having such a multi-layered structure has a multi-layered structure to exhibit excellent waterproof performance.

제 2 코팅제로 제공하는 단계(S500)는 제2 코팅제공부(500)가 반제품을 코팅하기 위한 제2 코팅제를 제공한다.Step S500 of providing with the second coating agent provides the second coating agent 500 for coating the semi-finished product.

일 실시 예에서, 제 2 코팅제로 제공하는 단계(S500)는 제2 코팅제공부(500)가 제1 압출부착부(400)로부터 생성된 반제품의 하면인 필름(10)의 하면에 압출되어 생성될 수 있다.In one embodiment, the step S500 of providing the second coating agent is performed by pressing the second coating agent 500 on the lower surface of the film 10, which is the lower surface of the semi-finished product produced from the first extrusion attachment portion 400, .

제2 부직포를 제공하는 단계(S600)는 제2 부직포제공부(600)가 제2 코팅제(20a)를 제공한다.Providing the second nonwoven fabric (S600) provides the second nonwoven fabricator (600) with a second coating (20a).

완제품으로 생성하는 단계(S700)는 제2 압출부착부(700)가 반제품과 제2 코팅제(20a)와 제2 부직포(30a)를 압출부착하여 완제품으로 생성한다.In the step S700, the second extrusion attachment unit 700 extrudes the semi-finished product, the second coating agent 20a, and the second nonwoven fabric 30a to produce an article as an article.

다중 겹침 구조를 가지는 복합방수시트 제조방법은 완제품을 수용하는 단계(S1000)를 포함할 수 있으며, 완제품을 수용하는 단계(S1000)는 제2 압출부착부(700)에서 생성된 완제품을 서로 감아서 수용할 수 있다.
The method for manufacturing a composite waterproof sheet having a multiple overlap structure may include a step S1000 for receiving an article and a step S1000 for accommodating the article to be finished by winding the articles produced in the second extrusion attachment unit 700 Can be accommodated.

도 4는 본 발명의 실시 예에 따른 다중 겹침 구조를 가지는 복합방수시트를 설명하는 도면이다.4 is a view illustrating a composite waterproof sheet having a multi-layer structure according to an embodiment of the present invention.

도 4를 참조하면, 다중 겹침 구조를 가지는 복합방수시트는 필름(10), 코팅제(20) 및 부직포(30)를 포함한다.Referring to FIG. 4, the composite waterproof sheet having a multi-layer structure includes a film 10, a coating agent 20, and a nonwoven fabric 30.

다중 겹침 구조를 가지는 복합방수시트는 직접 코팅 방식이 아닌 필름을 삽입하는 형태로, 필름(10)은 방수기능을 갖는다.The composite waterproof sheet having a multilayer structure is a structure in which a film is inserted instead of a direct coating type, and the film 10 has a waterproof function.

일 실시 예에서, 필름(10)은 생산 및 검사가 완료된 필름으로, PE(폴리에틸렌), EVA, PET(폴리에틸렌테레프탈레이트) 및 코팅제(20) 코팅제(20)를 혼합하여 제조된 것일 수 있다.In one embodiment, the film 10 may be one that has been produced and inspected and made by mixing PE (polyethylene), EVA, PET (polyethylene terephthalate), and coating 20 coating 20.

일 실시 예에서, 필름(10)은 메탈로센(Metallocene) LLDPE(Linear Low Density Polyethylene Film), LDPE(Low Density Polyethylene), 부텐(butene) LLDPE, 산화방지제, 슬립제를 혼합하여 제조된 것일 수 있다.In one embodiment, the film 10 may be one produced by mixing Metallocene LLDPE (Linear Low Density Polyethylene Film), LDPE (Low Density Polyethylene), butene LLDPE, antioxidant, have.

일 실시 예에서, 필름은 메탈로센(Metallocene) LLDPE(Linear Low Density Polyethylene Film) 31~33중량%, LDPE(Low Density Polyethylene) 31~33중량%, 부텐(butene) LLDPE 31~33중량%, 산화방지제 1~3중량%, 슬립제 1~3중량%의 함량으로 혼합될 수 있다.In one embodiment, the film comprises 31-33 wt.% Of Metallocene LLDPE (Linear Low Density Polyethylene Film), 31-33 wt.% LDPE (Low Density Polyethylene), 31-33 wt.% Butene LLDPE, 1 to 3% by weight of an antioxidant, and 1 to 3% by weight of a slip.

코팅제(20)는 필름(10)의 양측면에 각각 형성되며, 다시 말하면 코팅제(20)는 필름(10)의 양측면을 코팅제(20)로 도포하여 방수층이 형성될 수 있다.The coating agent 20 is formed on both sides of the film 10, that is, the coating agent 20 may be coated with the coating agent 20 on both sides of the film 10 to form a waterproof layer.

더욱 자세히는 코팅제(20)는 제1 코팅제(20a)와 제2 코팅제(20b)를 포함할 수 있으며, 제1 코팅제(20a)는 필름(10)의 상면에 압출부착되며, 제2 코팅제(20b)는 필름(10)의 하면에 압출부착되어 각각 형성될 수 있다.More specifically, the coating agent 20 may include a first coating agent 20a and a second coating agent 20b. The first coating agent 20a is extruded on the upper surface of the film 10, and the second coating agent 20b ) May be formed by extrusion and attached to the lower surface of the film 10, respectively.

코팅제(20)는 필름(10)의 양측면에 각각 코팅됨으로써, 코팅막 형태로 3중 겹침 구조를 가지게 됨으로 우수한 방수 성능을 가질 수 있다.Since the coating agent 20 is coated on both sides of the film 10, the coating agent 20 has a triple-layered structure in the form of a coating film, and thus can have excellent waterproof performance.

부직포(30)는 코팅제(20)의 양측면에 각각 형성되어, 필름(10) 및 코팅제(20)를 보강하도록 한다.The nonwoven fabric 30 is formed on both sides of the coating agent 20 so as to reinforce the film 10 and the coating agent 20.

더욱 자세히는 부직포(30)는 제1 부직포(30a) 및 제2 부직포(30b)를 포함할 수 있으며, 제1 부직포(30a)는 제1 코팅제(20a)의 상면에 형성되며 제2 부직포(30b)는 제2 코팅제(20b)의 하면에 형성되어, 필름(10) 및 코팅제(20)를 보강할 수 있다.More specifically, the nonwoven fabric 30 may include a first nonwoven fabric 30a and a second nonwoven fabric 30b. The first nonwoven fabric 30a may be formed on the upper surface of the first coating material 20a, May be formed on the lower surface of the second coating 20b to reinforce the film 10 and the coating 20.

일 실시 예에서, 부직포(30)는 고분자 합성 섬유를 사용할 수 있으며, 장섬유를 사용하여 전체 면적에 균일한 균제도를 가지기 위해 니들 펀칭하여 연속적인 카렌더링을 실시하여 제조할 수 있다.In one embodiment, the nonwoven fabric 30 may be made of polymeric synthetic fibers, and may be manufactured by continuous pouring of a needle by punching the continuous fibers to have a uniform uniformity over the entire area.

일 실시 예에서, 제2 부직포(30b)는 제1 부직포(30a)와 동일할 수 있으며, 시공 시에 바닥 즉 콘크리트면에 부착이 되는 부분으로 시공 현장에서 바닥면의 요철 또는 돌출 부위에 의해 필름(10) 및 코팅제(20)가 손상되지 않도록 하기 위해 제1 부직포(30a)보다 두께가 클 수 있다.
In one embodiment, the second nonwoven fabric 30b may be the same as the first nonwoven fabric 30a and is attached to the floor, that is, the concrete surface at the time of construction. In the construction site, The thickness of the first nonwoven fabric 30a may be greater than the thickness of the first nonwoven fabric 30a in order to prevent the first nonwoven fabric layer 10 and the coating material 20 from being damaged.

도 5 내지 도 7은 도 4에 있는 다중 겹침 구조를 가지는 복합방수시트를 설명하는 이미지이다.5 to 7 are images explaining the composite waterproof sheet having the multi-layered structure shown in Fig.

도 5는 다중 겹침 구조를 가지는 복합방수시트의 전체 확대 모습을 나타낸 도면이며, 도 6은 다중 겹침 구조를 가지는 복합방수시트의 상단 부직포(30a)를 나타낸 도면이며, 도 7은 다중 겹침 구조를 가지는 복합방수시트의 하단 부직포(30b)를 나타낸 도면이다.FIG. 5 is a view showing an entire enlarged view of the composite waterproof sheet having a multiple overlap structure, FIG. 6 is a view showing the upper nonwoven fabric 30a of the composite waterproof sheet having a multiple overlap structure, and FIG. And the lower nonwoven fabric 30b of the composite waterproof sheet.

도 5 내지 도 7을 참조하면, 다중 겹침 구조를 가지는 복합방수시트에서 도 4에서의 다중 겹침 구조와 동일하므로 이에 대한 설명은 생략하기로 한다.5 to 7, a composite waterproof sheet having a multi-layer structure is the same as the multi-layer structure shown in FIG. 4, so that a description thereof will be omitted.

다중 겹침 구조를 가지는 복합방수시트는 두 번 이상의 코팅 공정을 거쳐 다중의 겹침 구조로 형성될 수 있으며, 직접 분사하여 코팅하는 방식이 아닌 필름을 삽입하여 삽입된 필름의 양측면에 코팅제(20)를 압출부착하여 방수 성능을 향상시킬 뿐만 아니라, 코팅제(20)의 양측에 부직포(30)를 형성시켜 방수 기능 뿐만 아니라 단열 기능까지 제공할 수 있어 효과적이다.
The composite waterproof sheet having a multi-layered structure can be formed into a plurality of layered structures through two or more coating processes, and the film 20 is inserted into both sides of the inserted film by extrusion The waterproofing performance can be improved and the nonwoven fabric 30 can be formed on both sides of the coating agent 20 to provide not only a waterproof function but also an insulating function.

상술한 바와 같이, 본 발명은 비록 한정된 실시 예와 도면에 의해 설명되었으나, 본 발명은 상기 실시 예에 한정되는 것은 아니며, 이는 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 이러한 기재로부터 다양한 수정 및 변형이 가능하다. 따라서 본 발명의 사상은 아래에 기재된 특허청구범위에 의해서만 파악되어야 하고, 이의 균등 또는 등가적 변형 모두는 본 발명 사상의 범주에 속한다고 할 것이다.
Although the present invention has been described with reference to the exemplary embodiments and drawings, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, And variations are possible. Accordingly, it is intended that the scope of the invention be defined by the claims appended hereto, and that all equivalent or equivalent variations thereof fall within the scope of the present invention.

100 : 제1 부직포제공부
200 : 제1 코팅제공부
300 : 필름제공부
400 : 제1 압출부착부
500 : 제2 코팅제공부
600 : 제2 부직포제공부
700 : 제2 압출부착부
800 : 반제품수용부
900 : 반제품공급부
1000 : 완제품수용부
S100 : 제1 부직포를 제공하는 단계
S200 : 제1 코팅제를 제공하는 단계
S300 : 필름을 제공하는 단계
S400 : 반제품으로 생성하는 단계
S500 : 제2 코팅제를 제공하는 단계
S600 : 제2 부직포를 제공하는 단계
S700 : 완제품을 생성하는 단계
S800 : 반제품을 수용하는 단계
S900 : 반제품을 공급하는 단계
S1000 : 완제품을 수용하는 단계
10 : 필름
20 : 코팅제
30 : 부직포100: a first nonwoven fabric-
200: First coating agent study
300: film supply
400: first extrusion attachment portion
500: Study of second coating agent
600: second nonwoven fabric-provided
700: second extrusion attachment portion
800: semi-finished product receiving portion
900: Semifinished product supply section
1000: Finished product receiving portion
S100: Step of providing a first nonwoven fabric
S200: Step of providing the first coating
S300: Step of providing film
S400: Step of generating semi-finished product
S500: Step of providing a second coating
S600: Step of providing a second nonwoven fabric
S700: Steps to create finished product
S800: Steps to accept semi-finished products
S900: Steps to supply semi-finished products
S1000: Steps to accommodate the finished product
10: Film
20: Coating agent
30: Nonwoven fabric

Claims (11)

제1 부직포를 제공하는 제1 부직포제공부;
상기 제1 부직포제공부로부터 제공되는 제1 부직포를 코팅하기 위한 제1 코팅제를 제공하는 제1 코팅제공부;
상기 제1 코팅제공부로부터 제공되는 제1 코팅제에 필름을 제공하기 위한 필름제공부;
상기 제1 부직포제공부로부터 제공받은 제1 부직포와 상기 제1 코팅제공부로부터 제공받은 제1 코팅제와 상기 필름제공부에서 제공받은 필름을 압출부착하여 반제품으로 생성하는 제1 압출부착부;
상기 제1 압출부착부로부터 생성된 반제품을 코팅하기 위한 제2 코팅제를 제공하는 제2 코팅제공부;
상기 제2 코팅제공부로부터 제공되는 제2 코팅제에 제2 부직포를 제공하는 제2 부직포제공부;
상기 제1 압출부착부로부터 생성된 반제품과 상기 제2 코팅제공부로부터 제공받은 제2 코팅제와 상기 제2 부직포제공부로부터 제공받은 제2 부직포를 압출부착하여 완제품으로 생성하기 위한 제2 압출부착부;
상기 제1 압출부착부로부터 생성된 반제품을 수용하는 반제품수용부; 및
상기 반제품수용부에서 수용된 반제품을 상기 제2 코팅제공부로 공급하는 반제품공급부를 포함하되,
상기 필름은, 메탈로센 LLDPE 31~33중량%, LDPE 31~33중량%, 부텐 LLDPE 31~33중량%, 산화방지제 1~3중량%, 슬립제 1~3중량%의 함량으로 혼합되는 다중 겹침 구조를 가지는 복합방수시트 제조장치.
A first nonwoven fabric providing unit for providing a first nonwoven fabric;
A first coating agent providing a first coating agent for coating the first nonwoven fabric provided from the first nonwoven fabricator;
A film supplier for providing a film to the first coating agent provided from the first coating agent study;
A first extrusion attachment unit for extruding and attaching a first coating material supplied from the first nonwoven fabric supply unit, a first coating material supplied from the first coating material supply unit, and a film supplied from the film supply unit to produce a semi-finished product;
A second coating agent providing a second coating agent for coating the semi-finished product produced from the first extrusion attachment portion;
A second nonwoven fabric providing unit for providing a second nonwoven fabric to a second coating material provided from the second coating material study;
A second extrusion attachment unit for extruding and attaching the semi-finished product produced from the first extruded attachment unit, the second coating material supplied from the second coating material application and the second nonwoven fabric supplied from the second nonwoven material supply unit to produce a finished product;
A semi-finished product receiving portion for receiving the semi-finished product generated from the first extruded attachment portion; And
And a semi-finished product supply unit for supplying the semi-finished product stored in the semi-finished product storage unit to the second coating material study unit,
The film may comprise a mixture of 31 to 33% by weight of metallocene LLDPE, 31 to 33% by weight of LDPE, 31 to 33% by weight of butene LLDPE, 1 to 3% by weight of an antioxidant and 1 to 3% A composite waterproof sheet manufacturing apparatus having an overlapping structure.
삭제delete 삭제delete 제1항에 있어서,
상기 제2 압출부착부에서 생성된 완제품을 서로 감아서 수용하는 완제품수용부를 더 포함하는 것을 특징으로 하는 다중 겹침 구조를 가지는 복합방수시트 제조장치.
The method according to claim 1,
Further comprising a finished article receiving part for winding and holding the articles produced by the second extrusion attachment part to each other.
제1 부직포제공부가 제1 부직포를 제공하는 단계;
제1 코팅제공부가 상기 제1 부직포를 코팅하는 제1 코팅제를 제공하는 단계;
필름제공부가 상기 제1 코팅제에 필름을 제공하는 단계;
제1 압출부착부가 상기 제1 부직포와 상기 제1 코팅제와 상기 필름을 압출부착하여 반제품으로 생성하는 단계;
제2 코팅제공부가 상기 반제품을 코팅하기 위한 제2 코팅제를 제공하는 단계;
제2 부직포제공부가 상기 제2 코팅제에 제2 부직포를 제공하는 단계;
제2 압출부착부가 상기 반제품과 상기 제2 코팅제와 상기 제2 부직포를 압출부착하여 완제품으로 생성하는 단계;
반제품수용부가 상기 반제품을 수용하는 단계; 및
반제품공급부가 상기 반제품을 상기 제2 코팅제공부로 공급하는 단계를 포함하되,
상기 필름은, 메탈로센 LLDPE 31~33중량%, LDPE 31~33중량%, 부텐 LLDPE 31~33중량%, 산화방지제 1~3중량%, 슬립제 1~3중량%의 함량으로 혼합되는 다중 겹침 구조를 가지는 복합방수시트 제조방법.
Providing the first nonwoven fabric providing section with the first nonwoven fabric;
Providing a first coating for coating the first nonwoven fabric with a first coating material;
Providing a film to the first coating agent;
Forming a first extruded and adhered portion by extrusion bonding the first nonwoven fabric, the first coating agent, and the film to produce a semi-finished product;
Providing a second coating agent for coating the semi-finished article;
Providing a second nonwoven fabric to the second coating material;
The second extrusion attachment unit extruding the semi-finished product, the second coating material, and the second nonwoven fabric to produce a finished product;
Receiving the semi-finished product; And
Wherein the semi-finished product supply unit supplies the semi-finished product to the second coating material study,
The film may comprise a mixture of 31 to 33% by weight of metallocene LLDPE, 31 to 33% by weight of LDPE, 31 to 33% by weight of butene LLDPE, 1 to 3% by weight of an antioxidant and 1 to 3% A method for manufacturing a composite waterproof sheet having an overlapping structure.
삭제delete 삭제delete 제5항에 있어서,
완제품수용부가 상기 완제품을 수용하는 단계를 더 포함하는 것을 특징으로 하는 다중 겹침 구조를 가지는 복합방수시트 제조방법.
6. The method of claim 5,
The method of claim 1, further comprising the step of accommodating the finished article in a finished product receiving section.
제5항 또는 제8항 중 어느 한 항의 복합방수시트 제조방법에 의해 제조된 다중 겹침 구조를 가지는 복합방수시트.
A composite waterproof sheet having a multi-layer structure produced by the method for manufacturing a composite waterproof sheet according to any one of claims 5 to 8.
방수층을 이루는 필름;
상기 필름의 양측에 각각 형성되어, 상기 필름을 코팅하여 방수막을 이루는 코팅제; 및
상기 코팅제의 양측에 각각 형성되어, 상기 필름 및 상기 코팅제를 보강하기 위한 부직포를 포함하되,
상기 필름은, 메탈로센 LLDPE 31~33중량%, LDPE 31~33중량%, 부텐 LLDPE 31~33중량%, 산화방지제 1~3중량%, 슬립제 1~3중량%의 함량으로 혼합되는 다중 겹침 구조를 가지는 복합방수시트. A film constituting a waterproof layer;
A coating agent formed on both sides of the film to form a waterproof film by coating the film; And
A nonwoven fabric formed on both sides of the coating agent for reinforcing the film and the coating agent,
The film may comprise a mixture of 31 to 33% by weight of metallocene LLDPE, 31 to 33% by weight of LDPE, 31 to 33% by weight of butene LLDPE, 1 to 3% by weight of an antioxidant and 1 to 3% Composite waterproof sheet with overlapping structure. 삭제delete
KR1020140148607A 2014-10-29 2014-10-29 Apparatus for and Method of manufacturing Complex waterproof sheet with multiple overlap construction and Complex waterproof sheet with multiple overlap construction manufactured thereby KR101667263B1 (en)