KR101656670B1 - Aerogel with hydrophilicity, and aerogel composition with both hydrophilicity and hydrophobicity and aerogel paste manufactured by the composition and manufacturing method of the aerogel and the composition - Google Patents

Aerogel with hydrophilicity, and aerogel composition with both hydrophilicity and hydrophobicity and aerogel paste manufactured by the composition and manufacturing method of the aerogel and the composition Download PDF

Info

Publication number
KR101656670B1
KR101656670B1 KR1020150146762A KR20150146762A KR101656670B1 KR 101656670 B1 KR101656670 B1 KR 101656670B1 KR 1020150146762 A KR1020150146762 A KR 1020150146762A KR 20150146762 A KR20150146762 A KR 20150146762A KR 101656670 B1 KR101656670 B1 KR 101656670B1
Authority
KR
South Korea
Prior art keywords
aerogel
aerogels
hydrophobic
hydrophilic
volume
Prior art date
Application number
KR1020150146762A
Other languages
Korean (ko)
Inventor
김태원
Original Assignee
한양대학교 산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한양대학교 산학협력단 filed Critical 한양대학교 산학협력단
Priority to KR1020150146762A priority Critical patent/KR101656670B1/en
Priority to PCT/KR2015/011619 priority patent/WO2017069315A1/en
Application granted granted Critical
Publication of KR101656670B1 publication Critical patent/KR101656670B1/en
Priority to CN201680068074.6A priority patent/CN108348447B/en
Priority to US15/769,581 priority patent/US11020325B2/en
Priority to EP16857805.2A priority patent/EP3366275B1/en
Priority to PCT/KR2016/011867 priority patent/WO2017069547A1/en

Abstract

According to an embodiment of the present invention, a manufacturing method of hydrophilic aerogel comprises the following steps: preparing hydrophobic aerogel; and sintering the hydrophobic aerogel to manufacture the hydrophilic aerogel. According to an embodiment of the present invention, the hydrophilic aerogel is manufactured with a mixed composition comprising hydrophilicity and hydrophobicity by a process of sintering the hydrophobic aerogel in a temperature-elevated state, thereby simplifying a manufacturing process.

Description

친수성 에어로겔, 친수성 및 소수성을 모두 포함한 혼합 조성물 및 그 조성물로 제조되는 에어로겔 페이스트 그리고 그 에어로겔 및 그 조성물의 제조 방법{Aerogel with hydrophilicity, and aerogel composition with both hydrophilicity and hydrophobicity and aerogel paste manufactured by the composition and manufacturing method of the aerogel and the composition}TECHNICAL FIELD [0001] The present invention relates to a mixed composition including both hydrophilic and hydrophobic, hydrophilic and hydrophobic, and an aerogel paste made from the composition, and an aerogel and a method for producing the composition method of the aerogel and the composition}

친수성 에어로겔, 친수성 및 소수성을 모두 포함한 혼합 조성물 및 그 조성물로 제조되는 에어로겔 페이스트 그리고 그 에어로겔 및 그 조성물의 제조 방법이 개시된다. 보다 상세하게는, 소수성 에어로겔을 승온 상태에서 소결하는 공정에 의해 친수성 및 소수성을 모두 포함한 혼합 조성물로 제작함으로써 제작 공정을 단순화할 수 있는, 친수성 에어로겔, 친수성 및 소수성을 모두 포함한 혼합 조성물 및 그 조성물로 제조되는 에어로겔 페이스트 그리고 그 에어로겔 및 그 조성물의 제조 방법이 개시된다.A hydrophilic aerogel, a mixed composition containing both hydrophilic and hydrophobic, and an aerogel paste made from the composition, and an aerogel and a method for producing the composition are disclosed. More particularly, the present invention relates to a hydrophilic aerogel, a mixed composition including both hydrophilic and hydrophobic, and a composition thereof, which can simplify a manufacturing process by producing a hydrophobic and a hydrophobic mixed composition by sintering a hydrophobic aerogel at a raised temperature An aerogel paste to be produced, an airgel thereof, and a process for producing the composition are disclosed.

에어로겔(aerogel)은 높은 미세 기공률을 갖는 나노 다공성 물질으로 열차폐 및 소음, 전자파 차폐 특성 등을 지님에 따라, 건설, 건축용 단열재를 비롯하여 음파 지연재와 같이 다양한 산업분야에 사용되고 있다. 이 뿐만 아니라 기능성 화장용품으로써 외부의 고열 및 자외선 등으로부터 피부를 보호할 수 있으며 특히 물질이 구성하고 있는 나노 다공질 구조로 인해 우수한 보습력을 발현할 수 있고 따라서 찜질방을 비롯한 고온 환경에서도 오랜 시간 동안 적절한 수분을 유지할 수 있다. 아울러 수많은 미세한 기공이 자체 크기보다 수배에 달하는 부피의 피지를 흡수할 수 있으며, 또한 빛의 반사를 통해 균일한 점착성 및 피부 주름 개선에 도움을 줄 수 있다.Aerogels are nanoporous materials with high microporosity and are used in various industrial fields such as sound insulation materials as well as construction and building insulation materials due to their heat shielding, noise and electromagnetic shielding properties. In addition, it can protect skin from external high heat and ultraviolet ray as a functional cosmetic product. Especially, due to the nanoporous structure composed of the substance, it can exhibit excellent moisture retention. Therefore, even in a high temperature environment including a jjimjilbang, Lt; / RTI > In addition, numerous fine pores can absorb volumetric volumes of several times larger than their size, and can also help to improve uniformity and wrinkles of skin through reflection of light.

이러한 에어로겔은 물과의 흡착 정도에 따라 친수성과 소수성으로 구분될 수 있다. 여기서, 화장품은 유분과 수분을 동시에 함유하고 있는 유탁액으로 소수성과 친수성을 동시에 지닐 수 있어야 한다. 소수성 에어로겔의 경우 물 흡수에 따른 미세 기공의 크기 및 부피의 변화가 없으므로 높은 열 차폐 성능을 갖지만, 수분을 함유할 수 없는 구조적 한계가 있다. 따라서 소수성 에어로겔을 친수성 에어로겔로 변환시킬 수 있는 물리적 또는 화학적 처리를 통해 적절한 수분을 함유할 수 있는 친수성-소수성 에어로겔을 동시에 구현할 필요가 있다.Such aerogels can be classified into hydrophilic and hydrophobic depending on the degree of adsorption to water. Here, cosmetics are emulsions that contain both oil and water at the same time, and should be able to have both hydrophobicity and hydrophilicity. In the case of hydrophobic aerogels, there is no change in the size and volume of micropores due to water absorption, so that they have a high heat shielding performance, but there are structural limitations that can not contain moisture. Therefore, there is a need to simultaneously realize hydrophilic-hydrophobic aerogels which may contain appropriate moisture through physical or chemical treatments that can convert hydrophobic aerogels to hydrophilic aerogels.

다만, 종래의 기술, 즉 친수성 에어로겔 변환 공정에 대한 연구는 어느 정도 진척되었으나, 에어로겔 기공률이 감소하는 문제점이 여전히 상존하고 특히 화장용 조성물로 사용 가능할 수 있도록 하는 최적화된 친수-소수성 에어로겔에 대한 연구가 필요한 실정이다.However, research on a hydrophilic aerogel conversion process has been progressed to some extent, but research on an optimized hydrophilic-hydrophobic aerogel which can still be used as a cosmetic composition still has a problem of decreasing the airgel porosity It is necessary.

본 발명의 실시예에 따른 목적은, 소수성 에어로겔을 승온 상태에서 소결하는 공정에 의해 친수성 및 소수성을 모두 포함한 혼합 조성물로 제작함으로써 제작 공정을 단순화할 수 있는, 친수성 에어로겔, 친수성 및 소수성을 모두 포함한 혼합 조성물 및 그 조성물로 제조되는 에어로겔 페이스트 그리고 그 에어로겔 및 그 조성물의 제조 방법을 제공하는 것이다.An object of an embodiment of the present invention is to provide a hydrophilic aerogel which can be manufactured by a mixed composition including both a hydrophilic and a hydrophobic by a process of sintering a hydrophobic aerogel at an elevated temperature, And an aerogel paste prepared from the composition, and an aerogel and a method for producing the composition.

또한 본 발명의 실시예에 따른 다른 목적은, 친수성 및 소수성을 모두 포함한 혼합 조성물로 제조되는 에어로겔 페이스트가 우수한 에어로겔 기공률을 가짐으로써 가령 화장용 제품 등으로 제조되는 경우 높은 열차폐 성능을 가지면서도 유분과 수분을 함께 함유할 수 있어 품질 좋은 화장용 제품 등을 제조할 수 있는, 친수성 에어로겔, 친수성 및 소수성을 모두 포함한 혼합 조성물 및 그 조성물로 제조되는 에어로겔 페이스트 그리고 그 에어로겔 및 그 조성물의 제조 방법을 제공하는 것이다.Another object of the present invention is to provide an aerogel paste, which is produced from a mixed composition containing both hydrophilic and hydrophobic properties, has excellent airgel porosity, and thus has a high heat- A hydrophilic airgel, a hydrophilic and hydrophobic mixed composition capable of producing a cosmetic product and the like which can contain water together, and an aerogel paste made from the composition, and an aerogel and a method for producing the composition will be.

본 발명의 실시예에 따른 친수성 에어로겔은, 하기 [화학식 1]로 표시될 수 있다.The hydrophilic aerogels according to the embodiment of the present invention can be represented by the following formula (1).

[화학식 1][Chemical Formula 1]

≡ Si - OH≡ Si - OH

일측에 따르면, 상기 친수성 에어로겔은 소수성 에어로겔의 소결을 통해 작용기가 알킬기에서 수산화기로 변환되면서 제조된 것인, 상기 친수성 에어로겔은 소수성 에어로겔의 소결을 통하여 제조될 수 있다.According to one aspect, the hydrophilic aerogels may be prepared by sintering a hydrophobic aerogel, wherein the hydrophilic aerogels are prepared by sintering hydrophobic aerogels and converting functional groups from alkyl groups to hydroxyl groups.

일측에 따르면, 상기 친수성 에어로겔은 소수성 에어로겔의 소결을 통하여 제조될 수 있다.According to one aspect, the hydrophilic aerogels can be prepared through sintering of hydrophobic aerogels.

본 발명의 실시예에 따른 혼합 조성물은, 하기 [화학식 1]로 표시되는 친수성 에어로겔 및 하기 [화학식 2]로 표시되는 소수성 에어로겔을 포함할 수 있다.The mixed composition according to an embodiment of the present invention may include a hydrophilic aerogel represented by the following formula (1) and a hydrophobic aerogel represented by the following formula (2).

[화학식 1][Chemical Formula 1]

≡ Si - OH,≡ Si - OH,

[화학식 2](2)

≡ Si - R Si-R

(상기 R은 수소원자 또는 탄소수 1 내지 8의 알킬기임).(Wherein R is a hydrogen atom or an alkyl group having 1 to 8 carbon atoms).

일측에 따르면, 상기 혼합 조성물 중, 상기 친수성 에어로겔 및 상기 소수성 에어로겔의 부피비는 3:7 내지 7:3 일 수 있다.According to one aspect, in the mixed composition, the volume ratio of the hydrophilic aerogels and the hydrophobic aerogels may be 3: 7 to 7: 3.

한편, 본 발명의 실시예에 따른 에어로겔 페이스트는, 하기 [화학식 1]로 표시되는 친수성 에어로겔; 하기 [화학식 2]로 표시되는 소수성 에어로겔; 및 용매;를 포함할 수 있다.On the other hand, the aerogel paste according to the embodiment of the present invention is a hydrophilic aerogel represented by the following formula (1); A hydrophobic aerogel represented by the following formula (2); And a solvent.

[화학식 1][Chemical Formula 1]

≡ Si - OH,≡ Si - OH,

[화학식 2](2)

≡ Si - RSi-R

(상기 R은 수소원자 또는 탄소수 1 내지 8의 알킬기임).(Wherein R is a hydrogen atom or an alkyl group having 1 to 8 carbon atoms).

일측에 따르면, 상기 친수성 에어로겔 및 상기 소수성 에어로겔의 혼합 부피는 상기 에어로겔 페이스트 중 0.001 부피% 내지 10 부피%이고, 상기 친수성 에어로겔 및 상기 소수성 에어로겔의 부피비는 3:7 내지 7:3 일 수 있다.According to one aspect, the mixed volume of the hydrophilic aerogels and the hydrophobic aerogels may be 0.001 to 10 volume% of the aerogel paste, and the volume ratio of the hydrophilic aerogels and the hydrophobic aerogels may be 3: 7 to 7: 3.

일측에 따르면, 상기 용매는, 정제수, 알코올, 이소프로판올, 에틸 카보네이트, 에틸 아세테이트, 벤질 알코올, 벤질 벤조에이트, 프로필렌글리콜, 1,3-부틸글리콜 오일, 글리세롤 지방족 에스테르, 폴리에틸렌 글리콜, 소르비탄의 지방산 에스테르로 이루어진 군에서 선택되는 적어도 어느 하나를 포함할 수 있다.According to one aspect, the solvent is selected from the group consisting of purified water, alcohols, isopropanol, ethyl carbonate, ethyl acetate, benzyl alcohol, benzyl benzoate, propylene glycol, 1,3-butyl glycol oil, glycerol aliphatic ester, polyethylene glycol, fatty acid esters of sorbitan And at least one selected from the group consisting of

일측에 따르면, 상기 용매가, 상기 에어로겔 페이스트 중 40 부피% 내지 60 부피%일 수 있다.According to one aspect, the solvent may be from 40% by volume to 60% by volume of the aerogel paste.

일측에 따르면, 상기 에어로겔 페이스트는, 점증제를 더 포함할 수 있다.According to one aspect, the aerogel paste may further comprise an agglomerating agent.

일측에 따르면, 상기 점증제는 셀룰로오스, 히드록시프로필셀룰로오스, 젤라틴, 메칠셀룰로오스, 카보머, 소듐 카르복시 메틸 셀룰로오스, 구아검, 스테아린산, 폴리비닐알코올, 콜라겐, 만난 및 카라기난으로 이루어진 군으로부터 선택되는 적어도 어느 하나를 포함할 수 있다.According to one aspect, the thickener may be at least one selected from the group consisting of cellulose, hydroxypropyl cellulose, gelatin, methylcellulose, carbomer, sodium carboxymethylcellulose, guar gum, stearic acid, polyvinyl alcohol, collagen, mannan and carrageenan One can be included.

일측에 따르면, 상기 점증제는, 상기 에어로겔 페이스트 중 1 부피% 내지 25 부피%일 수 있다.According to one aspect, the thickener may be from 1 volume% to 25 volume% of the aerogel paste.

일측에 따르면, 보습제, 계면활성제 및 방부제 중 적어도 어느 하나를 더 포함할 수 있다.According to one aspect, it may further include at least one of a moisturizing agent, a surfactant, and an antiseptic agent.

일측에 따르면, 상기 보습제는 글리세린, 프로필렌글리콜, 에틸렌글리콜, 부틸렌글리콜, 디프로필렌글리콜, 펜틸렌글리콜, 헥실렌글리콜 및 소르비톨로 이루어진 군으로부터 선택되는 적어도 어느 하나를 포함할 수 있다.According to one aspect, the humectant may include at least one selected from the group consisting of glycerin, propylene glycol, ethylene glycol, butylene glycol, dipropylene glycol, pentylene glycol, hexylene glycol and sorbitol.

일측에 따르면, 상기 보습제는, 상기 에어로겔 페이스트 중 1 부피% 내지 20 부피%일 수 있다.According to one aspect, the humectant may be between 1% and 20% by volume of the aerogel paste.

일측에 따르면, 상기 방부제는 페녹시에탄올, 메칠파라벤, 에칠파라벤, 미네랄오일, 이소프로필알코올 및 천연방부제로 이루어진 군으로부터 선택되는 적어도 어느 하나를 포함할 수 있다.According to one aspect, the preservative may include at least one selected from the group consisting of phenoxyethanol, methylparaben, ethylparaben, mineral oil, isopropyl alcohol, and natural preservatives.

일측에 따르면, 상기 방부제는, 상기 에어로겔 페이스트 중 0.01 부피% 내지 3 부피%일 수 있다.According to one aspect, the preservative may be from 0.01% to 3% by volume of the aerogel paste.

일측에 따르면, 상기 계면활성제는 코코베타인, 레시틴, 잔탄검, 올리브유화왁스 및 LES로 이루어진 군으로부터 선택되는 적어도 어느 하나를 포함할 수 있다.According to one aspect, the surfactant may include at least one selected from the group consisting of coco betaine, lecithin, xanthan gum, olive oil wax, and LES.

일측에 따르면, 상기 계면활성제는, 상기 에어로겔 페이스트 중 0.01 부피% 내지 10 부피%일 수 있다.According to one aspect, the surfactant may be from 0.01% by volume to 10% by volume of the aerogel paste.

한편, 본 발명의 실시예에 따른 친수성 에어로겔의 제조 방법은, 소수성 에어로겔을 준비하는 단계; 및 상기 소수성 에어로겔을 소결하여 친수성 에어로겔을 제조하는 단계;를 포함할 수 있다.Meanwhile, a method of manufacturing a hydrophilic aerogel according to an embodiment of the present invention includes: preparing a hydrophobic aerogel; And sintering the hydrophobic aerogels to produce a hydrophilic aerogel.

일측에 따르면, 상기 소결은, 300℃ 내지 500℃의 온도에서 1 시간 내지 24 시간 동안 수행될 수 있다.According to one aspect, the sintering may be performed at a temperature of 300 ° C to 500 ° C for 1 hour to 24 hours.

일측에 따르면, 상기 소결을 통하여, 하기의 [화학식 2]로 표시되는 소수성 에어로겔의 알킬기(-CH3)가 제거되어, 하기의 [화학식1]로 표시되는 친수성 에어로겔이 형성될 수 있다.According to one aspect, the hydrophobic aerogel represented by the following formula (1) can be formed through removal of the alkyl group (-CH 3 ) of the hydrophobic aerogel represented by the following formula (2) through the above sintering.

[화학식 1][Chemical Formula 1]

≡ Si - OH,≡ Si - OH,

[화학식 2](2)

≡ Si - R Si-R

(상기 R은 수소원자 또는 탄소수 1 내지 8의 알킬기임).(Wherein R is a hydrogen atom or an alkyl group having 1 to 8 carbon atoms).

한편, 본 발명의 실시예에 따른 친수성 에어로겔 및 소수성 에어로겔을 포함하는 혼합 조성물의 제조 방법은, 소수성 에어로겔을 준비하는 단계; 및 상기 소수성 에어로겔을 소결하여 친수성 에어로겔을 제조하는 단계;를 포함하고, 상기 소수성 에어로겔의 전부가 친수성 에어로겔로 전환된 경우에는 소수성 에어로겔을 추가하는 단계를 더 포함할 수 있다.Meanwhile, a method for preparing a mixed composition comprising a hydrophilic aerogel and a hydrophobic aerogel according to an embodiment of the present invention includes: preparing a hydrophobic aerogel; And sintering the hydrophobic aerogels to produce a hydrophilic aerogel. When the entire hydrophobic aerogels are converted to hydrophilic aerogels, the method may further include adding hydrophobic aerogels.

일측에 따르면, 상기 소결을 통하여, 하기의 [화학식 2]로 표시되는 소수성 에어로겔의 알킬기(-CH3)가 제거되어, 하기의 [화학식1]로 표시되는 친수성 에어로겔이 형성될 수 있다. According to one aspect, the hydrophobic aerogel represented by the following formula (1) can be formed through removal of the alkyl group (-CH 3 ) of the hydrophobic aerogel represented by the following formula (2) through the above sintering.

[화학식 1][Chemical Formula 1]

≡ Si - OH,≡ Si - OH,

[화학식 2](2)

≡ Si - RSi-R

(상기 R은 수소원자 또는 탄소수 1 내지 8의 알킬기임).(Wherein R is a hydrogen atom or an alkyl group having 1 to 8 carbon atoms).

본 발명의 실시예에 따르면, 소수성 에어로겔을 승온 상태에서 소결하는 공정에 의해 친수성 및 소수성을 모두 포함한 혼합 조성물로 제작함으로써 제작 공정을 단순화할 수 있다.According to the embodiment of the present invention, the manufacturing process can be simplified by manufacturing a mixed composition including both hydrophilic and hydrophobic by a process of sintering the hydrophobic aerogels at an elevated temperature.

또한 본 발명의 실시예에 따르면, 혼합 조성물로 제조되는 에어로겔 페이스트가 우수한 에어로겔 기공률을 가짐으로써 가령 화장용 제품 등으로 제조되는 경우 높은 열차폐 성능을 가지면서도 유분과 수분을 함께 함유할 수 있어 품질 좋은 화장용 제품 등을 제조할 수 있다.Further, according to the embodiment of the present invention, since the aerogel paste made of the mixed composition has an excellent airgel porosity, when it is made of a cosmetic product or the like, it can contain both oil and moisture with high heat- Cosmetics, and the like can be produced.

도 1은 본 발명의 일 실시예에 따른 혼합 조성물의 제조 방법 및 이를 통한 화장용 제품의 제조 방법의 순서도이다.
도 2는 도 1에 도시된 혼합 조성물의 제조 과정 및 이를 통한 에어로겔 페이스트 그리고 화장용 제품을 제조하는 과정을 개략적으로 도시한 블록도이다.
도 3은 본 발명의 다른 실시예에 따른 혼합 조성물의 제조 방법 및 이를 통한 화장용 제품의 제조 방법의 순서도이다.
도 4는 도 3에 도시된 혼합 조성물의 제조 과정 및 이를 통한 에어로겔 페이스트 그리고 화장용 제품을 제조하는 과정을 개략적으로 도시한 블록도이다.
도 5는 승온, 소결 시간에 따른 에어로겔의 소수성 및 친수성의 변화 경향을 나타낸 그래프이다.
도 6은 일반 수분 크림과 본 실시예의 에어로겔 페이스트를 혼합한 수분 크림의 수분 증발량을 비교한 그래프이다. 1 is a flow chart of a method of manufacturing a mixed composition according to an embodiment of the present invention and a method of manufacturing a cosmetic product using the same.
FIG. 2 is a block diagram schematically showing a process of manufacturing the mixed composition shown in FIG. 1, and a process of manufacturing aerogel paste and cosmetic product therewith.
3 is a flow chart of a method of manufacturing a mixed composition according to another embodiment of the present invention and a method of manufacturing a cosmetic product using the same.
FIG. 4 is a block diagram schematically illustrating a process of manufacturing the mixed composition shown in FIG. 3, and a process of manufacturing the aerogel paste and cosmetic product therefrom.
FIG. 5 is a graph showing changes in the hydrophobicity and hydrophilicity of the aerogels according to the temperature rise and sintering time.
6 is a graph comparing moisture evaporation amounts of a moisture cream mixed with a general moisture cream and an airgel paste of this embodiment.

이하, 첨부 도면을 참조하여 본 발명의 실시예에 따른 구성 및 적용에 관하여 상세히 설명한다. 이하의 설명은 특허 청구 가능한 본 발명의 여러 태양(aspects) 중 하나이며, 하기의 기술(description)은 본 발명에 대한 상세한 기술(detailed description)의 일부를 이룬다. Hereinafter, configurations and applications according to embodiments of the present invention will be described in detail with reference to the accompanying drawings. DETAILED DESCRIPTION OF THE INVENTION The following description is one of many aspects of the claimed invention and the following description forms part of a detailed description of the present invention.

다만, 본 발명을 설명함에 있어서, 공지된 기능 혹은 구성에 관한 구체적인 설명은 본 발명의 요지를 명료하게 하기 위하여 생략하기로 한다.In the following description, well-known functions or constructions are not described in detail for the sake of clarity and conciseness.

이하에서 설명되는 소수성 에어로겔, 친수성 에어로겔 및 혼합 조성물은 분말 형태를 가질 수 있다. 다만, 이에 한정되는 것은 아니다.The hydrophobic aerogels, hydrophilic aerogels and mixed compositions described below may have a powder form. However, the present invention is not limited thereto.

도 1은 본 발명의 일 실시예에 따른 친수성 및 소수성을 모두 구비한 혼합 조성물의 제조 방법 및 이를 통한 화장용 제품의 제조 방법의 순서도이고, 도 2는 도 1에 도시된 친수성 및 소수성을 모두 구비한 혼합 조성물의 제조 과정 및 이를 통한 에어로겔 페이스트 그리고 화장용 제품을 제조하는 과정을 개략적으로 도시한 블록도이다.FIG. 1 is a flow chart of a method for producing a mixed composition having both hydrophilic and hydrophobic properties and a method for manufacturing a cosmetic product according to an embodiment of the present invention, and FIG. 2 is a view showing the hydrophilic and hydrophobic properties FIG. 2 is a block diagram schematically showing a process of manufacturing a mixed composition and a process of manufacturing aerogel paste and cosmetic product therewith. FIG.

도 1 및 도 2를 참조하면, 본 발명의 일 실시예에 따른 친수성 및 소수성을 모두 구비한 혼합 조성물의 제조 방법 및 이를 통한 에어로겔 페이스트 그리고 화장용 제품의 제조 방법은, 소수성 에어로겔(110)을 준비한 후 준비된 소수성 에어로겔(110) 중 소결하여 친수성 에어로겔(120)을 제조하는 친수성 에어로겔 제조 단계(S110)와, 제조된 친수성 에어로겔(120)에 소수성 에어로겔(110a)을 혼합하여 혼합 조성물(100)을 제조하는 혼합 조성물 제조 단계(S120)와, 제조된 혼합 조성물(100)에 용매, 점증제를 혼합하여 에어로겔 페이스트(130)를 제조하는 에어로겔 페이스트 제조 단계(S130)와, 에어로겔 페이스트(130)를 화장용 제품(150)으로 제조하는 화장용 제품 제조 단계(S140)를 포함할 수 있다.1 and 2, a method for producing a mixed composition having both hydrophilic and hydrophobic properties according to an embodiment of the present invention, a method for producing an aerogel paste and a cosmetic product using the same, comprises the steps of preparing a hydrophobic aerogel 110 A hydrophilic aerogel manufacturing step S110 of producing a hydrophilic aerogel 120 by sintering the prepared hydrophobic aerogels 110 and a hydrophobic aerogel 110a mixing the prepared hydrophilic aerogels 120 to manufacture a mixed composition 100 (S130) for producing an aerogel paste 130 by mixing a solvent and a thickening agent in the prepared mixed composition 100, and a step S130 for preparing an aerogel paste 130, And a cosmetic product manufacturing step (S140) of manufacturing the product (150).

각각의 단계에 대해 설명하면, 먼저 본 실시예의 친수성 에어로겔 제조 단계(S110)는, 도 1 및 도 2에 도시된 것처럼, 소결 장치(미도시)를 이용하여 소수성 에어로겔(110)을 소결함으로써 친수성 특성이 부여된 친수성 에어로겔(120)을 제조하는 단계이다. 1 and 2, the hydrophilic aerogels 110 of the present embodiment are prepared by sintering the hydrophobic aerogels 110 using a sintering apparatus (not shown) as shown in FIGS. 1 and 2, To thereby produce the hydrophilic aerogel 120 to which the hydrophilic aerogels 120 are attached.

소수성 에어로겔(110)은 알킬기(CH3)를 포함한다. 따라서 소수성 에어로겔(110)을 친수성 에어로겔에 비해 입자 크기가 크고 기공 부피는 작으며 기공 표면적 역시 작다. 부연하면, 알킬기(CH3)가 산화되면서 수산화기가 생기고 반응기의 크기가 작아지면서 에어로겔 입자의 크기가 작아지고 기공 부피 및 기공의 표면적인 넓어진다. 따라서 수분을 흡수할 수 있는 공간이 증가하여 친수성이 증가된다.Hydrophobic airgel 110 includes an alkyl group (CH 3). Accordingly, the hydrophobic aerogel 110 has a larger particle size, smaller pore volume, and smaller pore surface area than a hydrophilic aerogel. Further, as the alkyl group (CH 3 ) is oxidized, hydroxyl groups are formed and the size of the reactor becomes smaller, the size of the airgel particles becomes smaller, and the surface area of the pore volume and pore becomes wider. Therefore, the space capable of absorbing moisture is increased and the hydrophilicity is increased.

친수성 에어로겔 제조 단계(S110) 시, 소결 과정이 승온 상태에서 이루어짐으로써 소수성 에어로겔(110)로부터 알킬기를 제거하여 친수성 에어로겔(120)로 표면특성을 개질할 수 있다. In the hydrophilic aerogel production step (S110), the sintering process is carried out at a temperature elevated temperature to remove the alkyl groups from the hydrophobic aerogels 110, thereby modifying the surface characteristics with the hydrophilic aerogels 120.

이러한 친수성 에어로겔 제조 단계(S110)는, 소수성 에어로겔(110)을 승온 상태에서 있도록 하는 승온 단계와, 소수성 에어로겔(110)을 소결시켜 친수성 에어로겔(120)로 제조하는 소결 단계를 포함할 수 있다. The hydrophilic aerogel manufacturing step S110 may include a temperature raising step of raising the hydrophobic aerogels 110 and a sintering step of sintering the hydrophobic aerogels 110 to produce the hydrophilic aerogels 120. [

여기서 승온 단계 시, 전기로(미도시)를 이용해 300 내지 500℃의 온도로 승온시킬 수 있으며 이 온도 상태 하에 소수성 에어로겔(110)이 있을 수 있도록 한다. 그러면, 소수성 에어로겔(110)로부터 알킬기 및 잔여 수분이 제거되어 친수성 에어로겔(120)로 표면특성이 개질되는데, 이 친수성 에어로겔(120)은 소수성 에어로겔(110)에 비해 입자의 크기가 작아진다. At this time, the temperature can be raised to 300 to 500 ° C by using an electric furnace (not shown), and the hydrophobic aerogels 110 can be present under the temperature condition. Then, the alkyl group and the residual moisture are removed from the hydrophobic aerogels 110 to modify the surface characteristics of the hydrophilic aerogels 120. The hydrophilic aerogels 120 have smaller particle sizes than the hydrophobic aerogels 110.

아울러 감소된 입자의 크기로 인해 공간이 생기게 되고 이로 인해 기공 부피 및 기공 표면적이 증가하여 최종적으로 친수성이 증가될 수 있다. In addition, due to the reduced size of the particles, space is created, which increases the pore volume and pore surface area, and ultimately increases the hydrophilicity.

알킬기를 포함한 소수성 에어로겔(110)의 [화학식 1] 및 그로부터 알킬기가 제거(CH3-free)된 친수성 에어로겔(120)의 [화학식 2]는 다음과 같다. [Formula 1] of the hydrophobic aerogel 110 containing an alkyl group and the hydrophilic aerogel 120 in which the alkyl group is removed (CH 3 -free) from the formula 1 is as follows.

[화학식 1][Chemical Formula 1]

≡ Si - RSi-R

[화학식 2](2)

≡ Si - OH≡ Si - OH

(상기 R은 수소원자 또는 탄소수 1 내지 8의 알킬기임)(Wherein R is a hydrogen atom or an alkyl group having 1 to 8 carbon atoms)

부연하면, 친수성 에어로겔(120)을 소수성 에어로겔(110)의 소결을 통해 작용기가 알킬기에서 수산화기로 변환되면서도 제조될 수 있다.In addition, the hydrophilic aerogels 120 can be produced while the functional groups are converted from an alkyl group to a hydroxyl group through sintering of the hydrophobic aerogels 110.

한편, 소결 단계 시, 전술한 온도 상태를 1시간 내지 24시간 동안 유지하면서 소결 장치(미도시)에 의해 소수성 에어로겔(110)을 친수성 에어로겔(120)로 표면특성을 개질할 수 있다.On the other hand, at the sintering step, the hydrophobic aerogels 110 can be modified with the hydrophilic aerogels 120 by a sintering apparatus (not shown) while maintaining the above-mentioned temperature state for 1 hour to 24 hours.

한편, 본 실시예의 혼합 조성물 제조 단계(S120)는, 도 2에 도시된 것처럼, 친수성 에어로겔 제조 단계(S110)에 의해 제조된 친수성 에어로겔(120)에 소수성 에어로겔(110a)을 혼합하여 혼합 장치(미도시)에 의해 친수성 및 소수성이 모두 구비된 혼합 조성물(100)을 제조하는 것이다. 부연하면, 소수성 에어로겔(110) 중 일부는 전술한 친수성 에어로겔 제조 단계(S110) 시 소결에 의해 친수성 에어로겔(120)로 표면특성이 개질될 수 있으며, 소수성 에어로겔(110a) 중 다른 일부는 제조된 친수성 에어로겔(120)에 혼합될 수 있다. 2, the hydrophilic aerogels 110a are mixed with the hydrophilic aerogels 120 produced by the hydrophilic aerogel manufacturing step S110, and then mixed with the hydrophilic aerogels 110a, (100) having both hydrophilicity and hydrophobicity. In addition, some of the hydrophobic aerogels 110 may be modified in their hydrophilic aerogels 120 by sintering in the hydrophilic aerogel preparation step (S110) described above, and other hydrophobic aerogels 110a may have hydrophilic Can be mixed with the airgel 120.

여기서, 친수성 에어로겔(120) 및 소수성 에어로겔(110)은 설정된 부피비로 제조될 수 있다. 예를 들면, 친수성 에어로겔(120) 및 소수성 에어로겔(110)의 부피비는 3:7 내지 7:3일 수 있으며, 이 부피비 범위 내에서 선택적인 조절에 의해 친수성 및 소수성 중 원하는 특성이 더 부여될 수 있다. 상기 비율의 전자의 경우, 혼합 조성물(100)에서 소수성이 더 부여될 수 있는 것이고, 후자의 경우 친수성이 더 부여될 수 있을 것이다. 아울러, 혼합 장치에 의해 대략 1 내지 2분 동안 혼합되어 혼합 조성물(100)을 제조할 수 있다.Here, the hydrophilic aerogels 120 and the hydrophobic aerogels 110 may be manufactured in a predetermined volume ratio. For example, the volume ratio of the hydrophilic aerogels 120 and the hydrophobic aerogels 110 can be from 3: 7 to 7: 3, and by selective control within this volume ratio, more hydrophilic and hydrophobic properties can be imparted have. In the case of the former ratio, hydrophobicity can be further imparted to the mixed composition 100, and in the latter case, more hydrophilicity can be imparted. In addition, the mixed composition 100 can be prepared by mixing by a mixing apparatus for about 1 to 2 minutes.

한편, 본 실시예의 에어로겔 페이스트 제조 단계(S130)는, 도 2에 도시된 바와 같이, 혼합 조성물 제조 단계(S120) 시 제조된 혼합 조성물(100)에 용매, 점증제를 섞어 에어로겔 페이스트(130)를 제조하는 단계이다. 여기서 혼합 조성물(100)에 용매, 점증제는 설정된 비율로 혼합될 수 있는데, 이 때 용매, 점증제의 결합 비율 또는 혼합 시간은 혼합 조성물(100)의 양과 제조되는 제품의 용도에 따라 선택적으로 설정될 수 있다.2, the aerogel paste production step (S130) of the present embodiment is performed by mixing the solvent composition and the thickening agent in the mixed composition 100 produced in the mixed composition production step (S120) . In this case, the solvent and the thickening agent may be mixed in a predetermined ratio in the mixed composition 100. In this case, the mixing ratio or mixing time of the solvent, the thickener may be selectively set according to the amount of the mixed composition 100 and the use of the product to be manufactured .

부연하면, 혼합 조성물(100)에 혼합되는 용매는 물(정제수) 또는 에탄올과 같은 알코올이거나 이들이 혼합된 혼합물일 수 있으며, 혼합 조성물(100)에 설정된 비율로 혼합될 수 있다. In addition, the solvent to be mixed with the mixed composition 100 may be water (purified water) or an alcohol such as ethanol or a mixture thereof, and may be mixed in the mixing ratio set in the mixing composition 100.

혼합 조성물(100)에 점증제 역시 설정된 비율로 혼합되어 제조되는 에어로겔 페이스트(130)의 점도를 조절할 수 있다. 즉, 점증재의 혼합 비율에 따라 에어로겔 페이스트(130)의 점도를 선택적으로 조절할 수 있는 것이다. 다만, 점도 조절을 위해, 점증제가 아닌 결합재가 적용될 수도 있다. 결합재는 응집력 및 접착력이 있어 물질을 결합하는 데 적합하므로 점증제 대신 사용될 수 있다.The viscosity of the aerogel paste 130, which is prepared by mixing the admixture composition 100 with the admixture in a predetermined ratio, can be adjusted. That is, the viscosity of the aerogel paste 130 can be selectively controlled according to the mixing ratio of the incremental material. However, for control of viscosity, non-agglomerating binders may be applied. Binders may be used in place of incremental agents as they are suitable for bonding materials with cohesive and adhesive forces.

예를 들면, 에어로겔 페이스트(130) 제조를 위해, 혼합 조성물(100)은 0.001 ~ 10 부피%를 차지할 수 있다. 그리고 용매는 40 내지 60 부피%를 차지할 수 있다. 또한 점증제는 1 내지 25 부피%를 차지할 수 있다. 이 외에도 보습제가 1 내지 20 부피%를 차지할 수 있고, 방부제가 0.01 내지 3 부피%를 차지할 수 있고, 계면활성제가 0.01 내지 10 부피%를 차지할 수 있다. 다만, 전술한 용매, 점증제, 보습제, 방부제 또는 계면활성제의 함유 비율이 이에 한정되는 것은 아니며, 다른 비율로 혼합될 수 있음은 당연하다.For example, for the production of aerogel paste 130, the blend composition 100 may comprise from 0.001 to 10% by volume. And the solvent may comprise from 40 to 60% by volume. The thickener may also comprise from 1 to 25% by volume. In addition, the humectant may comprise from 1 to 20% by volume, the preservative from 0.01 to 3% by volume, and the surfactant from 0.01 to 10% by volume. However, the content ratio of the above-mentioned solvents, thickeners, moisturizers, preservatives or surfactants is not limited to these, and it is natural that they can be mixed at different ratios.

전술한 점증제는 셀룰로오스, 히드록시프로필셀룰로오스, 젤라틴, 메칠셀룰로오스, 카보머, 소듐 카르복시 메틸 셀룰로오스, 구아검, 스테아린산, 폴리비닐알코올, 콜라겐, 만난 및 카라기난 등의 성분을 가질 수 있다.The aforementioned thickening agent may have a component such as cellulose, hydroxypropyl cellulose, gelatin, methyl cellulose, carbomer, sodium carboxymethyl cellulose, guar gum, stearic acid, polyvinyl alcohol, collagen, mannan and carageenan.

전술한 보습제는 글리세린, 프로필렌글리콜, 에틸렌글리콜, 부틸렌글리콜, 디프로필렌글리콜, 펜틸렌글리콜, 헥실렌글리콜 또는 소르비톨로 중 1종 이상으로 이루어질 수 있다.The above-mentioned moisturizing agent may be composed of at least one of glycerin, propylene glycol, ethylene glycol, butylene glycol, dipropylene glycol, pentylene glycol, hexylene glycol or sorbitol.

그리고 기능성 첨가제로서의 방부제는 페녹시에탄올, 메칠파라벤, 에칠파라벤, 미네랄오일, 이소프로필알코올 또는 천연방부제 중 1종 이상으로 이루어질 수 있다. And the preservative as a functional additive may be at least one of phenoxyethanol, methylparaben, ethylparaben, mineral oil, isopropyl alcohol or a natural preservative.

또한 계면활성제는 코코베타인, 레시틴, 잔탄검, 올리브유화왁스 또는 LES 중 1종 이상으로 이루어질 수 있다.Further, the surfactant may be composed of at least one of cocobetaine, lecithin, xanthan gum, olive oil wax or LES.

한편, 본 실시예의 화장용 제품 제조 단계(S140)는, 도 2에 도시된 바와 같이, 에어로겔 페이스트 제조 단계(S130) 시 제조된 에어로겔 페이스트(130)를 얇고 유연한 소재에 도포하여 팩 형태의 화장용 제품(150)으로 제조하거나 피부에 직접 바르는 화장용 제품(150)으로 제조하는 단계이다. 얇고 유연한 소재로는 종이, 비닐, 부직포 등이 적용될 수 있으나 이에 한정되는 것은 아니다.2, the aerosol paste 130 produced in the aerogel paste production step (S130) is applied to a thin and flexible material to form a packaged cosmetic product Or a cosmetic product (150) which is manufactured by the product (150) or applied directly to the skin. As the thin and flexible material, paper, vinyl, nonwoven fabric and the like can be applied, but the present invention is not limited thereto.

화장용 제품 제조 단계(S140)에 의해 제조되는 화장용 제품(150)의 경우, 에어로겔 기공률이 우수한 에어로겔 페이스트(130)로 제조되는 것이기 때문에 높은 열차폐성을 기대할 수 있으면서도 유분 및 수분을 함께 함유할 수 있다.Since the cosmetic product 150 manufactured by the cosmetic product manufacturing step S140 is manufactured from the aerogel paste 130 having an excellent airgel porosity, it can be expected to have a high heat shielding property and can contain both oil and moisture have.

이와 같이, 본 발명의 일 실시예에 따르면, 소수성 에어로겔(110)을 승온 및 소결하는 단일의 공정에 의해 혼합 조성물(100)로 제작함으로써 제작 공정을 단순화할 수 있는 장점이 있다.As described above, according to one embodiment of the present invention, the manufacturing process can be simplified by fabricating the mixed composition 100 by a single process of heating and sintering the hydrophobic aerogels 110.

아울러, 혼합 조성물(100)로 제조되는 에어로겔 페이스트(130)가 우수한 에어로겔 기공률을 가짐으로써 가령 화장용 제품(150) 등으로 제조되는 경우 높은 열차폐 성능을 가지면서도 유분과 수분을 함께 함유할 수 있어 품질 좋은 화장용 제품(150) 등을 제조할 수 있는 장점이 있다.In addition, since the aerogel paste 130 made of the mixed composition 100 has excellent airgel porosity, when it is made of a cosmetic product 150 or the like, it can contain both oil and moisture with high heat-shielding performance And a cosmetic product 150 having good quality can be manufactured.

이하에서는, 본 발명의 다른 실시예에 따른 혼합 조성물의 제조 방법 및 이를 통한 화장용 제품의 제조 방법에 대해 설명하되 전술한 일 실시예의 구성과 실질적으로 동일한 부분에 대해서는 그 설명을 생략하기로 한다.Hereinafter, a method of manufacturing a mixed composition according to another embodiment of the present invention and a method of manufacturing a cosmetic product using the same will be described with reference to portions substantially the same as those of the above-described embodiment.

도 3은 본 발명의 다른 실시예에 따른 혼합 조성물의 제조 방법 및 이를 통한 화장용 제품의 제조 방법의 순서도이고, 도 4는 도 3에 도시된 혼합 조성물의 제조 과정 및 이를 통한 에어로겔 페이스트 그리고 화장용 제품을 제조하는 과정을 개략적으로 도시한 블록도이다.FIG. 3 is a flow chart of a method for producing a mixed composition according to another embodiment of the present invention and a method for manufacturing a cosmetic product using the same, and FIG. 4 is a flowchart illustrating a process for producing the mixed composition shown in FIG. 3, Fig. 2 is a block diagram schematically showing a process of manufacturing a product.

도 3및 도 4에 도시된 것처럼, 본 발명의 다른 실시예에 따른 혼합 조성물의 제조 방법 및 이를 통한 에어로겔 페이스트 그리고 화장용 제품의 제조 방법은, 전술한 일 실시예와 마찬가지로, 혼합 조성물 제조 단계(S210)와, 에어로겔 페이스트 제조 단계(S220)와, 화장용 제품 제조 단계(S230)를 포함할 수 있다. 그런데, 전술한 일 실시예와 다른 단계에서는 실질적으로 동일하지만, 혼합 조성물 제조 단계(S210)에 있어서는 차이가 있다.As shown in FIGS. 3 and 4, the method for producing a mixed composition according to another embodiment of the present invention, and the method for producing an aerogel paste and a cosmetic product according to another embodiment of the present invention, S210), an aerogel paste manufacturing step S220, and a cosmetic product manufacturing step S230. However, the steps are substantially the same as those in the above-described one embodiment, but differ in the mixed composition production step (S210).

도 3 및 도 4를 참조하면, 본 실시예의 혼합 조성물 제조 단계(S210)는, 전체의 소수성 에어로겔(210) 중 일부의 소수성 에어로겔만을 소결하여 친수성 및 소수성이 모두 부여된 혼합 조성물(200)을 제조하는 단계이다. 3 and 4, the mixed composition manufacturing step (S210) of this embodiment sinters only a part of the hydrophobic aerogels of the entire hydrophobic aerogels 210 to manufacture the mixed composition 200 imparted both hydrophilicity and hydrophobicity .

도 1을 참조하면, 전술한 일 실시예의 친수성 에어로겔 제조 단계(S110) 및 혼합 조성물 제조 단계(S120)가, 소수성 에어로겔(110)을 소결하여 친수성 에어로겔(120)을 만든 후 여기에 소수성 에어로겔(110a)을 혼합하여 혼합 조성물(100)을 제조하는 데 반해, 본 실시예에서는 전체의 소수성 에어로겔(210) 중 일부만을 소결하여 바로 혼합 조성물(200)을 제조한다. Referring to FIG. 1, the hydrophilic aerogels 110 and 120 are prepared by sintering the hydrophobic aerogels 110 and 120, respectively, in the hydrophilic aerogels manufacturing step (S110) and the mixed composition manufacturing step (S120) ) Are mixed to prepare the mixed composition 100. In this embodiment, however, only a part of the entire hydrophobic aerogels 210 is sintered to prepare the mixed composition 200 directly.

여기서, 전기로를 이용해 300 내지 500℃의 온도로 승온한 상태에서 1시간 내지 24시간 동안 소결 장치에 의해 소수성 에어로겔(210)을 소결함으로써 소수성 에어로겔(210) 내의 알킬기 및 잔여 수분을 부분적으로 제거할 수 있으며, 이를 통해 혼합 조성물(200)을 제조할 수 있다.Herein, the hydrophobic aerogels 210 are sintered by the sintering apparatus for 1 hour to 24 hours in the state where the temperature is raised to 300 to 500 ° C. by using an electric furnace to partially remove the alkyl groups and residual moisture in the hydrophobic aerogels 210 , Whereby the mixed composition (200) can be prepared.

부연하면, 알킬기를 포함하고 는 복수개의 소수성 에어로겔(210)어도 일부의 알킬기가 제거되어 수산화기를 포함하고 있는 친수성 에어로겔로 표면특성이 개질되는 것이다.In other words, the surface characteristics of the hydrophobic aerogels 210 including the alkyl group are modified by the hydrophilic aerogels containing some hydroxyl groups.

이처럼 소수성 에어로겔(210)들 중 일부만이 친수성으로 표면특성이 개질되고 다른 일부는 소수성 에어로겔로 남아 있기 때문에 친수성 및 소수성을 모두 포함한 혼합 조성물(200)이 제조될 수 있는 것이다. Since only a part of the hydrophobic aerogels 210 is hydrophilic and the surface characteristics are modified and the other hydrophobic aerogels 210 remain hydrophobic airgel, the mixed composition 200 including both hydrophilic and hydrophobic can be produced.

이렇게 제조된 혼합 조성물(200)은, 전술한 일 실시예와 마찬가지로, 에어로겔 페이스트 제조 단계(S220)에 의해 에어로겔 페이스트(230)로 제조될 수 있고, 아울러 화장용 제품 제조 단계(S230)에 의해 화장용 제품(250)으로 제조될 수 있다.The mixed composition 200 thus manufactured can be manufactured into the aerogel paste 230 by the aerogel paste manufacturing step S220 as in the above embodiment and can be manufactured by the cosmetic product manufacturing step S230 (250). ≪ / RTI >

한편, 도 5를 통해 소결 시간에 따른 친수성 또는 소수성 정도를 파악할 수 있다. 소결 시간이 길어질수록 소수성은 감소되고 친수성이 증가함을 알 수 있다. 이러한 원리를 이용하여 전술한 일 실시예의 친수성 에어로겔 제조 단계(S110)에서 소수성 에어로겔(110)을 승온 상태에서 소결하는 경우 친수성 에어로겔(120)을 제조할 수 있는 것이다. Meanwhile, the degree of hydrophilicity or hydrophobicity according to the sintering time can be grasped through FIG. As the sintering time becomes longer, the hydrophobicity decreases and the hydrophilicity increases. Using this principle, the hydrophilic aerogel 120 can be manufactured when the hydrophobic aerogel 110 is sintered at a temperature elevated state in the hydrophilic aerogel manufacturing step (S110) of the above-described embodiment.

한편, 전술한 다른 실시예의 혼합 조성물 제조 단계(S210)에서 소결 장치에 의해 전체의 소수성 에어로겔(210) 중 일부만을 소결하는 경우 친수성과 소수성을 모두 갖는 혼합 조성물을 제조할 수 있는 것이다.On the other hand, when only a part of the entire hydrophobic aerogels 210 is sintered by the sintering apparatus in the mixed composition manufacturing step S210 of the other embodiment described above, a mixed composition having both hydrophilic and hydrophobic properties can be produced.

한편, 도 6은 일반 수분 크림과 본 실시예의 에어로겔 페이스트를 혼합한 수분 크림의 수분 증발량을 비교한 그래프이다. On the other hand, FIG. 6 is a graph comparing moisture evaporation amounts of the moisture cream mixed with the ordinary moisture cream and the airgel paste of this embodiment.

이에 도시된 것처럼, 본 실시예의 혼합 조성물(100, 200)로 제조된 에어로겔 페이스트(130, 230)를 이용하여 제조된 화장용 제품(150, 250), 예를 들면 수분 크림이 일반 수분 크림에 비해 낮은 수분 증발량을 가짐을 확인할 수 있으며 이를 통해 혼합 조성물(100, 200)로 제조되는 화장용 제품(150, 250)의 경우 우수한 수분 유지 성능을 가질 수 있음을 알 수 있다.As shown therein, the cosmetic products 150, 250 made using the aerogel paste 130, 230 made of the mixed composition 100, 200 of this embodiment, for example, the water cream, It can be seen that the cosmetic products (150, 250) made of the mixed composition (100, 200) have excellent water retention performance.

전술한 실시예에서는, 혼합 조성물이 에어로겔 페이스트로 제조되고 이 에어로겔 페이스트가 팩 또는 크림 등과 같은 화장용 제품으로 제조되는 경우에 대해 상술하였으나, 혼합 조성물의 적용 분야가 이에 한정되는 것은 아니다.In the above-described embodiment, the case where the mixed composition is made of an aerogel paste and the aerogel paste is made of a cosmetic product such as a pack or cream has been described above, but the application field of the mixed composition is not limited thereto.

한편, 본 발명은 기재된 실시예에 한정되는 것이 아니고, 본 발명의 사상 및 범위를 벗어나지 않고 다양하게 수정 및 변형할 수 있음은 이 기술의 분야에서 통상의 지식을 가진 자에게 자명하다. 따라서 그러한 수정예 또는 변형예들은 본 발명의 특허청구범위에 속한다 하여야 할 것이다.It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit and scope of the invention. Accordingly, such modifications or variations are intended to fall within the scope of the appended claims.

100, 200 : 혼합 조성물
110, 210 : 소수성 에어로겔
120 : 친수성 에어로겔
130, 230 : 에어로겔 페이스트
150, 250 : 화장용 제품100, 200: mixed composition
110, 210: Hydrophobic aerogels
120: Hydrophilic aerogels
130 and 230: Aerogel paste
150, 250: cosmetic products

Claims (27)

삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 하기 화학식 1로 표시되는 수산화기와 하기 화학식 2로 표시되는 알킬기를 모두 갖는 표면을 구비하는 에어로겔을 함유하는 친수성 에어로겔;
하기 화학식 2로 표시되는 표면으로 이루어진 소수성 에어로겔;
점증제;
보습제, 계면활성제 및 방부제 중 적어도 어느 하나; 및
용매를 함유하는 에어로겔 페이스트이고,
상기 친수성 에어로겔 및 상기 소수성 에어로겔의 혼합 부피는 상기 에어로겔 페이스트 중 0.001 부피% 내지 10 부피%이고,
상기 친수성 에어로겔 및 상기 소수성 에어로겔의 부피비는 3:7내지 7:3인 화장용 제품:
[화학식 1]
≡ Si - OH,
[화학식 2]
≡ Si - R
(상기 R은 수소원자 또는 탄소수 1 내지 8의 알킬기임).1. A hydrophilic airgel comprising an aerogel having a surface having both a hydroxyl group represented by the following formula (1) and an alkyl group represented by the following formula (2);
A hydrophobic aerogel having a surface represented by the following formula (2);
Increasing agent;
At least one of a moisturizing agent, a surfactant, and an antiseptic agent; And
A solvent-containing airgel paste,
The mixed volume of the hydrophilic aerogels and the hydrophobic aerogels is 0.001 to 10 volume% of the aerogel paste,
Wherein the volume ratio of the hydrophilic aerogels to the hydrophobic aerogels is from 3: 7 to 7: 3.
[Chemical Formula 1]
≡ Si - OH,
(2)
Si-R
(Wherein R is a hydrogen atom or an alkyl group having 1 to 8 carbon atoms). 제6항에 있어서,
상기 친수성 에어로겔은 소수성 에어로겔의 소결을 통해 표면 작용기의 일부가 알킬기에서 수산화기로 변환되면서 제조된 것인, 화장용 제품. The method according to claim 6,
Wherein said hydrophilic aerogels are made by sintering hydrophobic aerogels while converting part of the surface functional groups from alkyl groups to hydroxyl groups. 삭제delete 제6항에 있어서,
상기 용매는, 정제수, 알코올, 이소프로판올, 에틸 카보네이트, 에틸 아세테이트, 벤질 알코올, 벤질 벤조에이트, 프로필렌글리콜, 1,3-부틸글리콜 오일, 글리세롤 지방족 에스테르, 폴리에틸렌 글리콜, 소르비탄의 지방산 에스테르로 이루어진 군에서 선택되는 적어도 어느 하나를 포함하는, 화장용 제품.The method according to claim 6,
The solvent is selected from the group consisting of purified water, alcohols, isopropanol, ethyl carbonate, ethyl acetate, benzyl alcohol, benzyl benzoate, propylene glycol, 1,3-butyl glycol oil, glycerol aliphatic ester, polyethylene glycol, sorbitan fatty acid esters And at least one selected from the group consisting of: 제6항에 있어서,
상기 용매가, 상기 에어로겔 페이스트 중 40 부피% 내지 60 부피%인, 화장용 제품.The method according to claim 6,
Wherein the solvent is from 40% by volume to 60% by volume of the aerogel paste. 삭제delete 제6항에 있어서,
상기 점증제는 셀룰로오스, 히드록시프로필셀룰로오스, 젤라틴, 메칠셀룰로오스, 카보머, 소듐 카르복시 메틸 셀룰로오스, 구아검, 스테아린산, 폴리비닐알코올, 콜라겐, 만난 및 카라기난으로 이루어진 군으로부터 선택되는 적어도 어느 하나를 포함하는 화장용 제품.The method according to claim 6,
Wherein the thickener comprises at least one selected from the group consisting of cellulose, hydroxypropylcellulose, gelatin, methylcellulose, carbomer, sodium carboxymethylcellulose, guar gum, stearic acid, polyvinyl alcohol, collagen, mannan and carrageenan Cosmetic products. 제6항에 있어서,
상기 점증제는, 상기 에어로겔 페이스트 중 1 부피% 내지 25 부피%인 것인, 화장용 제품.The method according to claim 6,
Wherein the thickener is from 1 volume% to 25 volume% of the aerogel paste. 삭제delete 제6항에 있어서,
상기 보습제는 글리세린, 프로필렌글리콜, 에틸렌글리콜, 부틸렌글리콜, 디프로필렌글리콜, 펜틸렌글리콜, 헥실렌글리콜 및 소르비톨로 이루어진 군으로부터 선택되는 적어도 어느 하나를 포함하는, 화장용 제품.The method according to claim 6,
Wherein the moisturizing agent comprises at least one selected from the group consisting of glycerin, propylene glycol, ethylene glycol, butylene glycol, dipropylene glycol, pentylene glycol, hexylene glycol and sorbitol. 제6항에 있어서,
상기 보습제는, 상기 에어로겔 페이스트 중 1 부피% 내지 20 부피%인 것인, 화장용 제품.The method according to claim 6,
Wherein the humectant is from 1 vol.% To 20 vol.% Of the aerogel paste. 제6항에 있어서,
상기 방부제는 페녹시에탄올, 메칠파라벤, 에칠파라벤, 미네랄오일, 이소프로필알코올 및 천연방부제로 이루어진 군으로부터 선택되는 적어도 어느 하나를 포함하는 것인, 화장용 제품.The method according to claim 6,
Wherein the preservative comprises at least one selected from the group consisting of phenoxyethanol, methylparaben, ethylparaben, mineral oil, isopropyl alcohol and natural preservatives. 제6항에 있어서,
상기 방부제는, 상기 에어로겔 페이스트 중 0.01 부피% 내지 3 부피%인 것인, 화장용 제품.The method according to claim 6,
Wherein the preservative is present in an amount of from 0.01% to 3% by volume of the aerogel paste. 제6항에 있어서,
상기 계면활성제는 코코베타인, 레시틴, 잔탄검, 올리브유화왁스 및 LES로 이루어진 군으로부터 선택되는 적어도 어느 하나를 포함하는 것인, 화장용 제품.The method according to claim 6,
Wherein the surfactant comprises at least one selected from the group consisting of coco betaine, lecithin, xanthan gum, olive oil wax and LES. 제6항에 있어서,
상기 계면활성제는, 상기 에어로겔 페이스트 중 0.01 부피% 내지 10 부피%인 것인, 화장용 제품.The method according to claim 6,
Wherein the surfactant is present in an amount of from 0.01% by volume to 10% by volume of the aerogel paste. 삭제delete 삭제delete 삭제delete 삭제delete 소수성 에어로겔들을 준비하는 단계; 및
상기 소수성 에어로겔들을 일부 소결하여, 상기 소수성 에어로겔들 중 일부를 수산화기와 알킬기를 모두 갖는 표면을 구비하는 에어로겔을 함유하는 친수성 에어로겔로 변환시켜, 나머지 일부의 소수성 에어로겔과 상기 친수성 에어로겔의 혼합물을 제조하는 단계; 및
보습제, 계면활성제 및 방부제 중 적어도 어느 하나, 상기 에어로겔 혼합물, 점증제, 및 용매를 혼합하여 에어로겔 페이스트를 제조하는 단계를 포함하고,
상기 에어로겔 혼합물은 상기 에어로겔 페이스트 중 0.001부피% 내지 10부피%로 함유되고,
상기 친수성 에어로겔 및 상기 소수성 에어로겔의 부피비는 3:7내지 7:3인 화장용 제품 제조방법.Preparing hydrophobic aerogels; And
Sintering the hydrophobic aerogels to convert some of the hydrophobic aerogels to hydrophilic aerogels containing an aerogel having surfaces having both hydroxyl groups and alkyl groups to produce a mixture of hydrophobic aerogels and hydrophilic aerogels of the rest of the hydrophobic aerogels ; And
Mixing at least one of a humectant, a surfactant, and an antiseptic agent, the airgel mixture, the thickener, and a solvent to prepare an airgel paste,
Wherein the aerogel mixture is contained in an amount of from 0.001% by volume to 10% by volume of the aerogel paste,
Wherein the hydrophilic aerogels and the hydrophobic aerogels have a volume ratio of 3: 7 to 7: 3. 삭제delete 삭제delete
KR1020150146762A 2015-10-21 2015-10-21 Aerogel with hydrophilicity, and aerogel composition with both hydrophilicity and hydrophobicity and aerogel paste manufactured by the composition and manufacturing method of the aerogel and the composition KR101656670B1 (en)