KR101613970B1 - In-line Double-side Adhesive Coating Film - Google Patents
In-line Double-side Adhesive Coating Film Download PDFInfo
- Publication number
- KR101613970B1 KR101613970B1 KR1020090028821A KR20090028821A KR101613970B1 KR 101613970 B1 KR101613970 B1 KR 101613970B1 KR 1020090028821 A KR1020090028821 A KR 1020090028821A KR 20090028821 A KR20090028821 A KR 20090028821A KR 101613970 B1 KR101613970 B1 KR 101613970B1
- Authority
- KR
- South Korea
- Prior art keywords
- adhesive layer
- film
- sensitive adhesive
- pressure
- coating
- Prior art date
Abstract
본 발명은 인라인 양면 점착 필름에 관한 것으로서, 보다 상세하게는 적어도 1축으로 연신된 투명한 폴리에스테르 기재필름에 점착액을 동시에 양면 코팅하여, 이형성과 점착성을 동시에 구현하도록 하여 필름의 권취와 피딩(feeding)을 동시에 할 수 있고, 또한 투명한 폴리에스테르 필름의 제막과 동시에 코팅이 진행되기 때문에 필름의 생산시간을 줄일 수 있고, 생산량을 늘릴 수 있는 인라인 양면 점착 필름에 관한 것이다. 이를 위해 본 발명에 따른 인라인 양면 점착 필름은 적어도 1축 방향으로 연신된 투명한 폴리에스테르 기재필름의 한 면에 점착층1이, 그 반대 면에 점착층2가 인라인으로 코팅된 것을 특징으로 하고, 여기서 상기 점착층1과 상기 점착층2는 열경화에 의한 코팅 방법으로 형성된 것을 특징으로 하며, 바람직하게는, 상기 점착층1의 도포량은 0.03 ~ 5 g/m2, 상기 점착층2의 도포량은 0.03 ~ 10 g/m2 인 것을 특징으로 한다.The present invention relates to an in-line double-sided pressure-sensitive adhesive film, and more particularly, to an in-line double-sided pressure-sensitive adhesive film which is coated on both sides of a transparent polyester base film stretched at least in one axis, ) Can be performed at the same time, and since the coating proceeds simultaneously with the film formation of the transparent polyester film, the production time of the film can be reduced and the production amount can be increased. To this end, the in-line double-sided pressure-sensitive adhesive film according to the present invention is characterized in that the pressure-sensitive adhesive layer 1 is coated on one side of the transparent polyester base film stretched in at least one axial direction and the pressure- The pressure-sensitive adhesive layer 1 and the pressure-sensitive adhesive layer 2 are formed by a coating method by thermal curing. Preferably, the pressure-sensitive adhesive layer 1 is applied in an amount of 0.03 to 5 g / m 2 and the pressure-sensitive adhesive layer 2 is applied in an amount of 0.03 To 10 g / m < 2 & gt ;.
폴리에스테르, 자기점착, 양면점착, 인라인 양면 코팅 Polyester, self-adhesive, double-sided adhesive, inline double-sided coating
Description
본 발명은 인라인 양면 점착 필름에 관한 것으로서, 보다 상세하게는 적어도 1축으로 연신된 투명한 폴리에스테르 기재필름에 점착액을 동시에 양면 코팅하여, 이형성과 점착성을 동시에 구현하도록 하여 필름의 권취와 피딩(feeding)을 동시에 할 수 있고, 또한 투명한 폴리에스테르 필름의 제막과 동시에 코팅이 진행되기 때문에 필름의 생산시간을 줄일 수 있고, 생산량을 늘릴 수 있는 인라인 양면 점착 필름에 관한 것이다.The present invention relates to an in-line double-sided pressure-sensitive adhesive film, and more particularly, to an in-line double-sided pressure-sensitive adhesive film which is coated on both sides of a transparent polyester base film stretched at least in one axis, ) Can be performed at the same time, and since the coating proceeds simultaneously with the film formation of the transparent polyester film, the production time of the film can be reduced and the production amount can be increased.
일반적으로, 인라인 코팅기술이란 폴리에스테르 필름의 제막과정에서 적어도 1축 이상의 연신과 동시에 코팅을 행하여, 폴리에스테르 필름에 새로운 기능을 부여하는 기술로서, 코팅 기술의 발전과 함께 양면 동시 코팅도 가능하게 되었다. 이러한 코팅기술을 이용하여, 필름의 양면에 점착 또는 이형 코팅을 행하면서, 광학용, 포장용 등의 기능을 갖는 폴리에스터 필름의 개발이 진행되고 있다. 그러나 제막과 동시에 양면에 점착 코팅을 하게 되면, 권취 시에도 문제가 될 뿐만 아니라, 생산을 한다 하더라도 양면 점착이기 때문에 피딩(feeding) 공정에 어려움이 많이 따르게 된다. 이러한 양면 점착 필름은 그 동안 반대면에 이형필름을 합지하는 형 태로 진행이 되어 왔다.In general, the in-line coating technology is a technology for imparting a new function to a polyester film by coating at the same time as at least one or more axes of stretching in the course of film formation of a polyester film, . With the use of such a coating technique, development of a polyester film having functions such as optics and packaging while advancing or sticking to both sides of the film has been progressed. However, if the adhesive coating is applied on both sides simultaneously with the film formation, it is a problem not only in winding but also in feeding process because it is a double-sided adhesive even if it is produced. This double-sided adhesive film has been in the form of laminating a release film on the opposite side.
도 1은 종래 양면점착필름의 단면도를 도시한 것으로서, 점착코팅(2)을 기재 필름(1) 위에 코팅한 후, 피착제나 이형필름(3)이나 이형지를 합지하여 생산이 이루어지게 되어 있으며, 사용시에 이형필름이나 이형지를 제거해야만 한다. 종래의 기술은 이형코팅층만을 가지는 것으로 한국특허공개 제2007-0084347호와 한국특허공개 제2005-0118821호에 잘 명시되어 있다.FIG. 1 is a cross-sectional view of a conventional double-sided pressure-sensitive adhesive film. The pressure-sensitive
그러나, 이러한 필름의 경우는 기재필름을 생산하고 난 후, 권취되어 있는 필름의 피딩, 점착코팅, 건조, 이형필름이나 이형지 합지 및 권취의 순으로 생산되며, 그 과정 또한 복잡하고 생산 시간이 많이 소요된다는 단점이 있다.However, in the case of such a film, after the base film is produced, it is produced in the order of feeding of the wound film, adhesion coating, drying, releasing film, releasing film, .
본 발명은 상기와 같은 문제점을 해결하기 위해 안출한 것으로서, 본 발명의 목적은 투명한 폴리에스테르 기재필름에 점착액을 동시에 양면 코팅하고, 일면은 실리콘계 점착제를 사용하여 반대면의 점착층에 대한 이형성을 가지게 하는 것과 동시에 기타 다른 피착제에는 점착력을 가지도록 하여, 필름의 권취와 피딩(feeding)을 동시에 할 수 있고, 또한 필름의 생산시간을 줄일 수 있고 생산량을 늘릴 수 있는 인라인 양면 점착 필름을 제공하고자 하는 것이다.DISCLOSURE OF THE INVENTION The present invention has been made in order to solve the above problems, and an object of the present invention is to provide a transparent polyester base film which is coated on both sides with a tacky liquid at the same time, To provide an inline double-sided pressure-sensitive adhesive film capable of simultaneous winding and feeding of the film, and also capable of reducing the production time of the film and increasing the production amount, .
본 발명의 상기 및 다른 목적과 이점은 바람직한 실시예를 설명한 하기의 설명으로부터 보다 분명해 질 것이다.These and other objects and advantages of the present invention will become more apparent from the following description of a preferred embodiment thereof.
상기 목적은, 적어도 1축 방향으로 연신된 투명한 폴리에스테르 기재필름의 한 면에 점착층1이, 그 반대 면에 점착층2가 인라인으로 코팅된 것을 특징으로 하는 인라인 양면점착 코팅필름에 의해 달성된다.The above object is achieved by an in-line double-sided pressure-sensitive adhesive coating film characterized in that the pressure-sensitive
여기서, 상기 점착층1과 상기 점착층2는 열경화에 의한 코팅 방법으로 형성된 것을 특징으로 한다.Here, the
바람직하게는, 상기 점착층1의 도포량은 0.03 ~ 5 g/m2, 상기 점착층2의 도포량은 0.03 ~ 10 g/m2 인 것을 특징으로 한다.Preferably, the application amount of the
바람직하게는, 상기 점착층2는 고형분10~40%의 수성 아크릴계, 천연 고무계, 실리콘계 에멀전, 솔벤리스 실리콘 점착액 중 적어도 하나의 경화형 점착액이 도포되어 형성된 것을 특징으로 한다.Preferably, the
삭제delete
바람직하게는, 상기 투명한 폴리에스테르 기재필름의 한 면 혹은 양면에 대전방지층을 더 포함하는 것을 특징으로 한다.Preferably, the transparent polyester base film further comprises an antistatic layer on one side or both sides of the transparent polyester base film.
본 발명에 따르면, 적어도 1축으로 연신된 투명한 폴리에스테르 기재필름에 점착액을 동시에 양면 코팅하여, 이형성과 점착성을 동시에 구현하도록 하여 필름의 권취와 피딩(feeding)을 동시에 할 수 있고, 또한 투명한 폴리에스테르 필름의 제막과 동시에 코팅이 진행되기 때문에 필름의 생산시간을 줄일 수 있고, 생산량을 늘릴 수 있는 등의 효과를 가진다.According to the present invention, a transparent polyester base film stretched on at least one axis can be simultaneously coated on both surfaces of a pressure-sensitive adhesive liquid so as to realize both releasing and sticking properties, thereby enabling simultaneous winding and feeding of the film, Since the coating proceeds simultaneously with the film formation of the ester film, the production time of the film can be reduced and the production amount can be increased.
이하, 본 발명의 실시예와 도면을 참조하여 본 발명을 상세히 설명한다. 이들 실시예는 오로지 본 발명을 보다 구체적으로 설명하기 위해 예시적으로 제시한 것일 뿐, 본 발명의 범위가 이들 실시예에 의해 제한되지 않는다는 것은 당업계에서 통상의 지식을 가지는 자에 있어서 자명할 것이다.Hereinafter, the present invention will be described in detail with reference to embodiments and drawings of the present invention. It will be apparent to those skilled in the art that these embodiments are provided by way of illustration only for the purpose of more particularly illustrating the present invention and that the scope of the present invention is not limited by these embodiments .
본 발명은 종래 점착필름의 제반 문제들을 해결하기 위해, 투명한 폴리에스테르 필름의 제막단계부터 점착층2를 코팅하고, 그 반대 면에 점착층1을 동시에 형성함으로써 양면 점착필름의 제작에 관한 것이다.The present invention relates to the production of a double-sided pressure-sensitive adhesive film by coating the pressure-sensitive
본 발명자는 이러한 기능성 양면 점착필름을 이용하여 기존 점착 필름이 가지고 있던 생산과정의 단계를 줄이고, 보호필름이나 점착필름의 대량생산이 가능하도록 함으로써 본 발명을 완성하였다.The present inventors have completed the present invention by using such a functional double-sided adhesive film to reduce the production steps of existing adhesive films and to mass-produce protective films or adhesive films.
도 2는 본 발명에 따른 인라인 양면 점착 필름의 단면도를 도시한 것으로서, 기재필름(1)의 일면에 점착층1(4)을, 반대면에 점착층2(2)를 동시에 도포하여 만든 필름이다. 즉, 본 발명은 투명한 폴리에스테르 기재필름에 인라인 코팅으로 점착층 1 및 2를 동시에 코팅하여 새로운 기능을 부여하는 양면점착 코팅필름에 관한 것으로서, 보다 상세하게는 기재필름의 한 면에 실리콘계 도포액을 도포하고, 반대 면에 점착액을 도포하여 점착층1과 점착층2를 동시에 형성한 필름으로 생산시의 권취와 가공시의 피딩(feeding)를 가능하게 하는 양면점착 코팅필름에 관한 것이다.2 is a cross-sectional view of an in-line double-sided pressure-sensitive adhesive film according to the present invention, which is a film formed by applying an adhesive layer 1 (4) to one surface of a
본 발명에 따른 양면점착 코팅필름의 상기 점착층1과 상기 점착층2는 열경화에 의한 코팅 방법으로 형성된 것을 특징으로 한다. 또한 점착층1의 특성은 실리콘계 수지의 도포량에 따라서 조절이 가능하도록 설계 한 것이다.The pressure-sensitive
본 발명에 따른 투명한 폴리에스테르 기재필름(1)은 양면에 코로나 처리 또는 플라즈마 처리를 하여 양면 코팅이 가능하도록 한 후 사용할 수 있다. The transparent polyester base film (1) according to the present invention can be used after being subjected to corona treatment or plasma treatment on both sides so that double-side coating is possible.
본 발명에 따른 코팅에 사용되는 점착 수지는 수성 에멀전이 아니어도 상관없으나 친환경 필름의 생산에 있어서는 용제형 수지보다 유리하다. 점착액의 경우, 아크릴계, 실리콘계, 천연고무계 등의 수지를 사용할 수 있으며, 에멀전의 경우 두 가지 이상의 에멀전을 단독 또는 혼합하여 사용 할 수 있다. The adhesive resin used in the coating according to the present invention may be an aqueous emulsion, but it is more advantageous than the solvent type resin in the production of environmentally friendly films. In the case of the adhesive liquid, resins such as acrylic, silicone, and natural rubber may be used. In the case of emulsion, two or more emulsions may be used alone or in combination.
본 발명에 따른 인라인 양면점착 코팅필름에 있어서 상기 인라인으로 코팅되는 상기 점착층은 고형분 10~40%의 수성 아크릴계, 천연 고무계, 실리콘계 에멀전, 솔벤리스 실리콘 점착액 중 적어도 하나의 경화형 점착액이 도포되어 형성된 것이 바람직하다.In the in-line double-sided pressure-sensitive adhesive coating film according to the present invention, the pressure-sensitive adhesive layer coated with the inline is coated with at least one curable adhesive liquid of an aqueous acrylic, natural rubber, silicone emulsion or sorbent silicone adhesive liquid having a solid content of 10 to 40% Is preferably formed.
삭제delete
본 발명에서 사용되는 수지들은 모두 수성 에멀전 수지를 사용하여 코팅을 진행하였다. 수성이기 때문에 환경적으로도 문제가 없으며, 분자량이나 경화 정도에 관계없이 대부분의 수지를 사용할 수 있다.All resins used in the present invention were coated using an aqueous emulsion resin. Since it is water-soluble, there is no environmental problem, and most resins can be used regardless of the molecular weight or degree of curing.
본 발명에 따른 양면점착 코팅필름에서 투명한 기재필름 상에 도포액을 도포하는 방식은 특별히 제한되지 않고 사용할 수 있으나, 바람직하게는 바 도포, 나이프 도포, 그라비아 전이 도포, 리버스 롤 도포 방식을 사용할 수 있다. 또한 코팅 후 기재필름의 1축 이상의 연신을 진행해도 관계가 없다.The method of applying the coating liquid on the transparent substrate film in the double-sided pressure-sensitive adhesive coating film according to the present invention is not particularly limited and may be used. Preferably, the coating method is bar coating, knife coating, gravure transfer coating or reverse roll coating . It is also irrelevant to stretching more than one axis of the substrate film after coating.
본 발명에 따른 인라인 양면점착 코팅필름의 도포량은 상기 점착층1의 경우에는 0.03 ~ 5 g/m2 , 상기 점착층2의 경우에는 0.03 ~ 10 g/m2인 것을 특징으로 한다.The application amount of the in-line double-sided pressure-sensitive adhesive coating film according to the present invention is 0.03 to 5 g / m 2 for the pressure-sensitive
본 발명에 따른 양면점착 코팅필름에서 점착층2(2)의 점착력은 경화 정도와 두께에 의해서 조절되는데, 일액형의 수성 조액의 경우는 경화제의 함량이 결정되기 때문에, 두께에 의해 점착력을 조절하게 되고, 점착/이액형의 경우에는 경화제의 함량과 두께로 점착력을 조절하기 때문에 인라인에서의 코팅 방법에 따라 점착력을 조절해야 한다.In the double-sided pressure-sensitive adhesive coating film according to the present invention, the adhesive strength of the pressure-sensitive adhesive layer 2 (2) is controlled by the degree of curing and the thickness thereof. In the case of the single- In the case of the adhesive / two-component type, the adhesive force is controlled by the content and thickness of the curing agent. Therefore, the adhesive force should be adjusted according to the coating method in the inline.
또한, 본 발명에 따른 양면점착 코팅필름은 투명한 폴리에스테르 기재필름의 한 면 혹은 양면에, 대전방지층을 형성할 수도 있는데, 이는 제단 및 조립 작업시 발생하는 스크래치를 억제하고 이물 혼입을 방지하기 위함이다.In addition, the antireflection layer may be formed on one side or both sides of the transparent polyester base film according to the present invention in order to suppress scratches during the altar and assembling operations and to prevent foreign matter from entering the antireflection layer .
이하, 본 발명을 실시예와 비교예를 통해 상세히 설명한다.Hereinafter, the present invention will be described in detail with reference to examples and comparative examples.
[실시예 1-4][Example 1-4]
투명 폴리에스테르 필름(도레이새한㈜ XG210, 50㎛)의 일면에 하기 조성을 가진 도포액 1과 그 반대면에 하기 조성을 가진 도포액 2를 인라인으로 코팅하여, 180℃에서 30초간 건조하여 필름을 제조하였다. 제조된 필름은 80℃에서 3시간 30분간 에이징(aging)하였다.On one side of a transparent polyester film (XG210, 50 占 퐉, made by Toray Saehan Co., Ltd.), a
도포액 1의 조성Composition of coating liquid 1
- 순수 : 70 중량%- pure water: 70 wt%
- 실리콘 에멀전 수지 : 26.1중량%- Silicone emulsion resin: 26.1 wt%
- 실리콘 촉매 수지 : 2.8 중량%- Silicon catalyst resin: 2.8 wt%
- leveling제 : 0.5 중량%- leveling agent: 0.5 weight%
- wetting제 : 0.6 중량%- wetting agent: 0.6 wt%
도포액 2의 조성Composition of
- 순수 : 80 중량%- pure water: 80 wt%
- 실리콘 에멀전 수지 : 18 중량%Silicone emulsion resin: 18 wt%
- 실리콘 촉매 수지 : 1.2 중량%- Silicon catalyst resin: 1.2 wt%
- leveling제 : 0.4 중량%- leveling agent: 0.4 wt%
- wetting제 : 0.4 중량%- wetting agent: 0.4 wt%
실시예 1에서 4는 상기 도포액 1, 2에서 다음의 표1에 있는 점착 에멀전의 두께를 조절하면서 코로나 처리된 폴리에스테르 필름 위에 코팅하여 양면코팅 필름을 제조하였다. In Examples 1 to 4, a double-side coated film was prepared by coating the corona-treated polyester film with the thickness of the adhesive emulsion shown in the following Table 1 in the
[표 1] [Table 1]
* 바 선수에 따라 도포량의 차이가 있으며, 점착층2에 대해서만 바 선수를 변화 시킴.* There is a difference in the application amount depending on the player of the bar, and only the bar player is changed for the
* 반대면의 점착층1의 경우는 한가지의 두께의 조건만 사용함*
* 실시예 1~4의 조액의 제조는 순수로 점도를 조절한 것으로 도포액 조성 범위 내에서 점도를 맞추어 제조함.* The preparation of the crude liquids of Examples 1 to 4 was prepared by adjusting the viscosity to pure water and adjusting the viscosity within the coating liquid composition range.
[비교예 1, 2] [Comparative Examples 1 and 2]
상기 실시예와 같은 투명 폴리에스테르 필름(도레이새한㈜ XG210, 50㎛)의 일 면에 하기 조성을 가진 도포액 3 또는 4를 사용하여 양면코팅 점착필름을 오프라인 공정을 통해 제조하는 것 이외에 상기 실시예와 동일하게 수행하여 필름을 제조하였다.In addition to manufacturing the double-side coated adhesive film through the off-line process using the
도포액 3의 조성Composition of
- 순수 : 80 중량%- pure water: 80 wt%
- 실리콘 에멀전 수지 : 18.5중량%Silicone emulsion resin: 18.5 wt%
- 실리콘 촉매 수지 : 1.0 중량%- Silicon catalyst resin: 1.0 wt%
- wetting제 : 0.5 중량%- wetting agent: 0.5 wt%
도포액 4의 조성Composition of coating liquid 4
- 순수 : 80 중량%- pure water: 80 wt%
- 실리콘 에멀전 수지 : 18 중량%Silicone emulsion resin: 18 wt%
- 실리콘 촉매 수지 : 1.2 중량%- Silicon catalyst resin: 1.2 wt%
- wetting제 : 0.8 중량%- wetting agent: 0.8 wt%
비교예 1 및 2는 상기 도포액 3, 4에서 다음의 표2에 있는 점착 에멀전의 두께를 조절하면서 코로나 처리된 폴리에스테르 필름 위에 코팅하여 양면코팅 필름을 제조하였다.Comparative Examples 1 and 2 were coated on a corona-treated polyester film while adjusting the thickness of the adhesive emulsion shown in Table 2 below in
[표 2][Table 2]
[실험예][Experimental Example]
상기 실시예 1 ~ 4 및 비교예 1, 2 에서 제조된 필름에 대하여 하기와 같이 물성을 측정하여 표 3에 기재하였다.The properties of the films prepared in Examples 1 to 4 and Comparative Examples 1 and 2 were measured as described below and are shown in Table 3.
1. 코팅층의 두께측정1. Measurement of thickness of coating layer
상기 실시예 1 ~ 4 및 비교예 1, 2에서 제조된 시트의 코팅층 두께는 마이크로메터를 이용한 침압식 측정기[미쯔토요사, 모델명: ID-Ff125]를 사용하여 측정하였으며, 시트의 총 두께 측정 값에서 투명한 기재필름의 두께를 뺀 값으로 산출하였다.The thicknesses of the coating layers of the sheets prepared in Examples 1 to 4 and Comparative Examples 1 and 2 were measured using a pressure-sensitive meter (Mitsutoyo, Model: ID-Ff125) using a micrometer, Minus the thickness of the transparent base film.
2. 점착력 측정2. Adhesion measurement
상기 실시예 1 ~ 4 및 비교예 1, 2에서 제조된 시트의 점착력은 AR-1000(Cheminstruments)장비를 이용하여 180도 peel을 측정하였다.The adhesive strength of the sheets prepared in Examples 1 to 4 and Comparative Examples 1 and 2 was measured with a 180 degree peel using AR-1000 (Cheminstruments) equipment.
3. 외관 확인3. Appearance check
상기 실시예 1 ~ 4 및 비교예 1, 2에서 제조된 시트를 삼파장 램프 밑에서 투과로 검사하였다.The sheets prepared in Examples 1 to 4 and Comparative Examples 1 and 2 were inspected under the condition of a three-wavelength lamp by transmission.
4. 수성 조액의 점도 측정4. Viscosity measurement of aqueous solution
상기 실시예 1 ~ 4 및 비교예 1, 2에서 사용된 조액은 Brookfield 점도계 spindle No. 00로 측정하였다.The crude liquid used in Examples 1 to 4 and Comparative Examples 1 and 2 was measured with a Brookfield viscometer spindle No. 1. 00.
[표 3][Table 3]
(g/inch)Initial adhesion
(g / inch)
(g/inch)Final adhesion
(g / inch)
O : 양호, Δ : 보통, X : 불량O: Good, Δ: Normal, X: Bad
* 최종 점착력은 에이징 후의 점착력을 말함* Final adhesion refers to adhesion after aging.
상기 표 3에서 보는 바와 같이, 일액형 수성 아크릴 에멀전을 이용하여, 보호필름용 미점착 양면 필름의 제조가 가능한 것을 알 수 있다. 그리고 보호필름의 경우에는 요구되는 물성이, 미점착이라는 점과 헤이즈가 낮아야 한다는 것이다. 따라서 본 발명에 따른 양면점착 코팅필름은 보호필름 용도로 사용할 수도 있게 된다.As shown in Table 3, it can be seen that the unfixed double-sided film for a protective film can be produced by using the one-pack type aqueous acrylic emulsion. In the case of a protective film, the required physical properties are that it is not tacky and that the haze is low. Therefore, the double-sided pressure-sensitive adhesive coating film according to the present invention can also be used as a protective film.
이상에서 본 발명은 기재된 구체예에 대해서만 상세히 설명되었지만 본 발명의 범위 내에서 다양한 변형 및 수정이 가능함은 당업자에게 명백한 것이며, 이러한 변형 및 수정이 첨부된 특허청구범위에 속함은 당연한 것이다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is evident that many alternatives, modifications and variations will be apparent to those skilled in the art.
도 1은 종래 점착필름의 단면도.1 is a sectional view of a conventional adhesive film.
도 2는 본 발명에 따른 인라인 양면점착 코팅필름의 모식적 단면도.2 is a schematic cross-sectional view of an in-line double-sided pressure-sensitive adhesive coating film according to the present invention.
<도면의 주요부분에 대한 부호의 간단한 설명> BRIEF DESCRIPTION OF THE DRAWINGS FIG.
1 : 폴리에스테르 기재 필름 2 : 점착층21: polyester base film 2:
3 : 이형필름 4 : 점착층13: Release film 4:
Claims (6)