KR101603560B1 - Composition for Synthetic Fiber Fabric Reconstruction, and Reconstruction Method for Synthetic Fiber Fabric Reconstruction Using the Composition - Google Patents
Composition for Synthetic Fiber Fabric Reconstruction, and Reconstruction Method for Synthetic Fiber Fabric Reconstruction Using the Composition Download PDFInfo
- Publication number
- KR101603560B1 KR101603560B1 KR1020140042171A KR20140042171A KR101603560B1 KR 101603560 B1 KR101603560 B1 KR 101603560B1 KR 1020140042171 A KR1020140042171 A KR 1020140042171A KR 20140042171 A KR20140042171 A KR 20140042171A KR 101603560 B1 KR101603560 B1 KR 101603560B1
- Authority
- KR
- South Korea
- Prior art keywords
- synthetic fiber
- composition
- fiber fabric
- polyester
- reconstruction
- Prior art date
Abstract
합성 섬유 원단 강화용 조성물 및 이를 사용하는 합성 섬유 원단 강화 방법이 개시된다. 본 발명에서의 조성물은 고분자 물질 용해제와 평활제를 혼합함으로써 제조된다. 본 발명에 따르면, 폴리에스테르 원단 등의 합성 섬유 원단으로 제작된 모자 등의 착용구의 형상을 손쉽게 강화할 수 있게 된다. 아울러, 본 발명에 따르면, 폴리에스테르 원단 등의 합성 섬유 원단으로 제작된 모자 등의 착용구의 세탁 품질을 높일 수 있게 된다.A composition for reinforcing a synthetic fiber fabric and a synthetic fiber fabric reinforcing method using the composition are disclosed. The composition of the present invention is prepared by mixing a polymeric substance dissolvent and a smoothing agent. INDUSTRIAL APPLICABILITY According to the present invention, it is possible to easily enhance the shape of a wearing tool such as a hat made of a synthetic fiber fabric such as a polyester fabric. In addition, according to the present invention, it is possible to improve the washing quality of a wearing tool such as a hat made of a synthetic fiber fabric such as a polyester fabric.
Description
본 발명은 합성 섬유 원단 강화용 조성물 및 이를 사용하는 합성 섬유 원단 강화 방법에 관한 것으로, 더욱 상세하게는 폴리에스테르 원단 등의 합성 섬유 원단으로 제작된 모자 등의 착용구의 형상을 손쉽게 강화할 수 있을 뿐만 아니라, 폴리에스테르 원단 등의 합성 섬유 원단으로 제작된 모자 등의 착용구의 세탁 품질을 높일 수 있도록 하는 합성 섬유 원단 강화용 조성물 및 이를 사용하는 합성 섬유 원단 강화 방법에 관한 것이다. The present invention relates to a composition for reinforcing synthetic fiber fabrics and a method for reinforcing synthetic fiber fabrics using the same. More specifically, the present invention can easily enhance the shape of a wearer's hat made of a synthetic fiber fabric such as a polyester fabric, The present invention relates to a composition for reinforcing synthetic fiber fabrics and a method for reinforcing synthetic fiber fabrics using the same.
최근 대한민국의 모자 시장 규모가 연간 1조원에 달한다는 발표가 있었다. 이와 같이 엄청난 양의 모자가 판매되고 사용됨에도 불구하고, 기타의 의류, 운동화 등의 제품군과는 달리 모자에 대해서는 아직까지 적절한 유지 관리 방법이 없는 상황이다.Recently, there was an announcement that the market size of the Korean mother market reached 1 trillion won per year. Despite the huge amount of hats sold and used, there is still no proper maintenance method for hats, unlike other apparel and sneakers.
한편, 현재 생산되는 대부분의 모자들은 그 형태를 유지하기 위해 안감으로 폴리에스테르(polyester)를 사용한 원단을 사용하고 있다. 구체적으로, 메이저 리그 야구 모자, 국내 프로야구 모자, 골프 모자 등의 스포츠 모자들이 그러하며, 이들 모자는 비교적 고가에 판매되고 있다.On the other hand, most of the hats that are currently produced use polyester with polyester lining to maintain its shape. Specifically, such are sports hats such as Major League baseball caps, domestic professional baseball caps, and golf hats, and these hats are sold at relatively high prices.
풀리에스테르 원단은 체온이나 햇빛 등의 약한 열에도 조직이 연화되는 특성을 갖고 있는데, 폴리에스테르 원단이 갖고 있는 이와 같은 특성은 모자를 착용한 사용자에게 우수한 착용감을 제공하는 장점 뿐만 아니라, 모자에 쉽게 주름이 생기게 하는 단점의 원인이 된다.The pulley ester fabric has a characteristic of softening the tissues even in weak heat such as body temperature and sunlight. The polyester fabric has such merits that it provides excellent wearing comfort to the user wearing the cap, Which is a cause of disadvantages.
즉, 폴리에스테르 원단을 안감으로 사용하는 모자들은 대부분 햇빛이나 비에 약하고, 특히 물 세탁을 하거나 비에 맞아 젖은 상태에서 햇빛에 노출하되게 되면 건조에 따라 폴리에스테르 원단의 균열에 따른 주름이 발생하게 된다.In other words, hats that use polyester fabric lining are most vulnerable to sunlight or rain. Especially when exposed to sunlight in wet or wet conditions, wrinkles may occur due to cracking of polyester fabric due to drying do.
한편, 이와 같이 모자 안감인 폴리에스테르 원단의 균열에 의해 발생된 주름을 제거하는 것을 실질적으로 불가능하였기에, 이들 대부분은 고가의 모자임에도 이를 복원하지 못하고 버려야 하는 경우가 많았다. On the other hand, since it was virtually impossible to remove the wrinkles generated by the cracks of the polyester fabric, which was the hat lining, most of them were expensive and could not be restored.
아울러, 이와 같은 이유에서 세탁업체 또한 의류, 운동화 등의 제품군과는 달리 모자에 대해서는 세탁 서비스를 제공하고 있지 않은 실정이다.Also, for this reason, the laundry companies do not provide laundry services for their hats, unlike clothing and sneakers.
따라서, 본 발명의 목적은, 폴리에스테르 원단 등의 합성 섬유 원단으로 제작된 모자 등의 착용구의 형상을 손쉽게 강화할 수 있을 뿐만 아니라, 폴리에스테르 원단 등의 합성 섬유 원단으로 제작된 모자 등의 착용구의 세탁 품질을 높일 수 있도록 하는 합성 섬유 원단 강화용 조성물 및 이를 사용하는 합성 섬유 원단 강화 방법을 제공함에 있다.Accordingly, it is an object of the present invention to provide a method of fabricating a cloth, such as a hat, made of a synthetic fiber such as a polyester fabric, And a method for reinforcing synthetic fiber fabrics using the same.
상기 목적을 달성하기 위한 본 발명에 따른 합성 섬유 원단 강화용 조성물은, 고분자 물질 용해제와 평활제를 혼합하여 제조되는 것을 특징으로 한다.In order to accomplish the above object, the present invention provides a composition for reinforcing a synthetic fiber fabric, which is prepared by mixing a polymeric substance dissolvent and a smoothing agent.
바람직하게는, 상기 고분자 물질은 폴리 에스테르인 것을 특징으로 한다.Preferably, the polymer material is polyester.
또한, 상기 고분자 물질 용해제는 아세톤인 것을 특징으로 한다.Further, the polymeric substance dissolving agent is characterized by being acetone.
또한, 상기 평활제는 부틸아세테이트인 것을 특징으로 한다.Further, the smoothing agent is characterized by being butyl acetate.
한편, 본 발명에 따른 합성 섬유 원단 강화 방법은, 합성 섬유 원단에, 고분자 물질 용해제와 평활제를 혼합하여 제조된 조성물을 도포하는 단계; 및 상기 합성 섬유 원단에 도포된 상기 조성물을 건조시키는 단계를 포함한다.Meanwhile, the method of reinforcing a synthetic fiber fabric according to the present invention comprises the steps of: applying a composition prepared by mixing a synthetic polymer fiber dissolvent with a smoothing agent; And drying the composition applied to the synthetic fiber fabric.
바람직하게는, 상기 고분자 물질은 폴리 에스테르인 것을 특징으로 한다.Preferably, the polymer material is polyester.
또한, 상기 고분자 물질 용해제는 아세톤인 것을 특징으로 한다.Further, the polymeric substance dissolving agent is characterized by being acetone.
또한, 상기 평활제는 부틸아세테이트인 것을 특징으로 한다.Further, the smoothing agent is characterized by being butyl acetate.
본 발명에 따르면, 폴리에스테르 원단 등의 합성 섬유 원단으로 제작된 모자 등의 착용구의 형상을 손쉽게 강화할 수 있게 된다.INDUSTRIAL APPLICABILITY According to the present invention, it is possible to easily enhance the shape of a wearing tool such as a hat made of a synthetic fiber fabric such as a polyester fabric.
아울러, 본 발명에 따르면, 폴리에스테르 원단 등의 합성 섬유 원단으로 제작된 모자 등의 착용구의 세탁 품질을 높일 수 있게 된다.In addition, according to the present invention, it is possible to improve the washing quality of a wearing tool such as a hat made of a synthetic fiber fabric such as a polyester fabric.
도 1은 본 발명의 일 실시예에 따른 합성 섬유 원단 강화용 조성물을 이용한 합성 섬유 원단 강화 방법을 설명하는 절차 흐름도, 및
도 2는 본 발명의 일 실시예에 따른 합성 섬유 원단 강화용 조성물을 모자에 도포하는 장면을 나타낸 도면이다. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a flow chart illustrating a method for reinforcing synthetic fiber fabrics using a composition for reinforcing synthetic fiber fabrics according to an embodiment of the present invention; and FIG.
2 is a view showing a state in which a synthetic fiber reinforcing composition according to an embodiment of the present invention is applied to a cap.
이하에서는 도면을 참조하여 본 발명을 보다 상세하게 설명한다. 도면들 중 동일한 구성요소들은 가능한 한 어느 곳에서든지 동일한 부호들로 나타내고 있음에 유의해야 한다. 또한 본 발명의 요지를 불필요하게 흐릴 수 있는 공지 기능 및 구성에 대한 상세한 설명은 생략한다.Hereinafter, the present invention will be described in detail with reference to the drawings. It is to be noted that the same elements among the drawings are denoted by the same reference numerals whenever possible. In the following description, well-known functions or constructions are not described in detail since they would obscure the invention in unnecessary detail.
도 1은 본 발명의 일 실시예에 따른 합성 섬유 원단 강화용 조성물을 이용한 합성 섬유 원단 강화 방법을 설명하는 절차 흐름도이다. 도 1 내지 도 2를 참조하여, 본 발명의 일 실시예에 따른 합성 섬유 원단 강화용 조성물을 이용한 합성 섬유 원단 강화 방법을 설명하면, 먼저, 작업자는 휘발성을 갖는 고분자 물질 용해제와 평활제를 혼합하여, 혼합 조성물을 제조한다(S110).FIG. 1 is a flowchart illustrating a method of reinforcing synthetic fiber fabrics using a synthetic fiber reinforcing composition according to an embodiment of the present invention. Referring to FIG. Referring to FIGS. 1 and 2, a method for reinforcing synthetic fiber fabrics using a composition for reinforcing synthetic fiber fabrics according to an embodiment of the present invention will be described. First, an operator mixes a volatile polymer material dissolver and a smoothing agent , And a mixed composition is prepared (S110).
혼합 조성물에 포함된 고분자 물질 용해제는 모자(10)의 안감으로 사용되는 폴리 에스테르 등의 고분자 물질을 용해시키는 기능을 수행하며, 평활제는 고분자 물질 용해제에 의해 용해된 물질이 폴리 에스테르 원단에서 용이하게 확산되도록 하는 기능을 수행한다.The polymeric substance dissolving agent contained in the mixed composition functions to dissolve a polymer substance such as polyester used as a lining of the
본 발명을 실시함에 있어서, 고분자 물질 용해제로는 아세톤이 사용될 수 있을 것이며, 평활제로는 부틸아세테이트가 사용될 수 있을 것이다. 아울러, 0.5 내지 1.5 부피비의 아세톤과 1 내지 3 부피비의 부틸아세테이트를 혼합함이 바람직할 것이다.In practicing the present invention, acetone may be used as a polymer substance dissolving agent, and butyl acetate may be used as a smoothing agent. In addition, it may be preferable to mix acetone of 0.5 to 1.5 volume ratio and butyl acetate of 1 to 3 volume ratio.
또한, 본 발명을 실시함에 있어서는 에틸 알코올 2.5 내지 7.5 부피비를 추가로 혼합함으로써, 살균, 소독 등의 추가의 성질을 갖도록 할 수도 있을 것이다.Further, in the practice of the present invention, it may be possible to have additional properties such as sterilization and disinfection by further mixing 2.5 to 7.5 volume parts of ethyl alcohol.
한편, 본 발명에 따라 제조된 조성물을 이용한 폴리 에스테르 원단의 강화를 시험함에 있어서는, 아세톤과 부틸아세테이트를 1:2의 부피비로 혼합하였으며, 에틸 알코올 5 부피비를 추가로 혼합하였다.On the other hand, when the polyester fabric was tested using the composition prepared according to the present invention, acetone and butyl acetate were mixed at a volume ratio of 1: 2, and 5 parts by volume of ethyl alcohol was further mixed.
참고로, 아세톤(aceton: CH3COCH3)은 56.5℃의 끓는점을 가지며, 부틸아세테이트(Butyl Acetate): C6H12O2)는 126℃의 끓는점을 가지고, 에틸알코올(ethyl alcohol: C2H5OH)은 78℃의 끓는점을 가지며, 실험을 위해 상술한 바와 같은 부피비로 제조된 혼합 조성물은 대략 56.5℃에서부터 126℃까지의 온도 구간에서 기화되는 것으로 확인되었다.For reference, the acetone (aceton: CH 3 COCH 3) has a boiling point of 56.5 ℃, butyl acetate (Butyl Acetate): C 6 H 12 O 2) has a boiling point of 126 ℃, ethanol (ethyl alcohol: C 2 H 5 OH) had a boiling point of 78 ° C. and it was confirmed that the mixed composition prepared at the volume ratio as described above for the experiment was vaporized at a temperature range from about 56.5 ° C. to 126 ° C.
한편, 이와 같이 제조된 혼합 조성물을 도 2에서와 같이 모자(10) 안감 등의 폴리 에스테르 원단에 분무기(50)를 이용하여 도포하였다(S130). 그에 따라, 혼합 조성물에 포함된 아세톤에 의해 폴리 에스테르의 부분적 용해가 시작되었으며, 혼합 조성물에 포함된 부틸아세테이트에 의해 용해된 폴리 에스테르의 평활 및 확산이 촉진되었다.Meanwhile, the mixed composition thus prepared was applied to a polyester fabric such as a cap lining or the like using an
한편, 혼합 조성물을 폴리 에스테르 원단에 도포함에 따른 상술한 용해 및 확산 현상이 진행됨과 동시에, 휘발성 액체인 아세톤과 부틸아세테이트의 증발에 의한 폴리 에스테르 원단의 건조가 시작된다(S150).On the other hand, the above-described dissolution and diffusion phenomenon caused by the application of the mixed composition to the polyester fabric proceeds and at the same time, drying of the polyester fabric by evaporation of volatile liquid acetone and butyl acetate starts (S150).
이와 같이 폴리 에스테르 원단을 건조시킴에 있어서는 자연 건조가 바람직하지만, 폴리 에스테르 원단의 용해 및 확산의 정도를 제어하기 위해, 작업자는 열풍을 이용한 고속 건조 방법을 사용할 수도 있을 것이다.In this way, drying of the polyester fabric is preferably natural drying, but in order to control the degree of dissolution and diffusion of the polyester fabric, the operator may use a high-speed drying method using hot air.
이와 같이 혼합 조성물의 증발에 따른 폴리 에스테르 원단의 건조 과정이 완료되면, 부분적 용해 및 평활이 진행되었던 폴리 에스테르 원단의 경화가 이루어진다. When the drying of the polyester fabric by the evaporation of the mixed composition is completed, the polyester fabric that has undergone partial dissolution and smoothing is cured.
한편, 아세톤과 부틸아세테이트는 이와 같이 공기 중으로 증발됨으로써, 폴리 에스테르 원단을 제외한 나머지 원단(면, 모, 실크 등)에는 물리적, 화학적 영향을 전혀 주지 않게 된다.On the other hand, acetone and butyl acetate are evaporated into air in this way, so that no physical and chemical influences are imparted to the other fabrics (cotton, wool, silk, etc.) except for the polyester fabric.
즉, 폴리 에스테르의 부분적 용해, 평활, 경화의 과정을 통해 폴리 에스테르 원단은 제품 출시 당시의 강도를 회복할 수 있게 된다.In other words, through the process of partial melting, smoothing and curing of the polyester, the polyester fabric can recover the strength at the time of product release.
뿐만 아니라, 폴리 에스테르의 부분적 용해, 평활, 경화의 과정을 통해 폴리 에스테르 원단과 함께 사용되는 인접 원단과의 밀착 정도 및 부착 강도를 높일 수 있게 되며, 그에 따라 인접 원단에서의 주름을 효과적으로 개선할 수 있을 뿐만 아니라, 향후 주름의 발생을 방지할 수 있게 된다.In addition, through the process of partial dissolution, smoothing and hardening of the polyester, it is possible to increase the degree of close contact with the adjacent fabric used together with the polyester fabric and the adhesion strength thereof, thereby effectively improving the wrinkles in the adjacent fabric In addition, it is possible to prevent the occurrence of wrinkles in the future.
이와 같이, 본 발명에 따른 조성물을 이용하면 폴리 에스테르 원단이 사용된 모자(10) 등의 다양한 착용구의 다림 작업, 및 세탁 작업에서뿐만 아니라, 모자(10) 등의 제작 과정에서도 해당 제품에 구조적 강성을 부여할 수 있게 된다.As described above, when the composition according to the present invention is used, not only in the ironing operation and the laundry operation of various wearing areas such as the
한편, 본 발명에서의 혼합 조성물의 끓는점이 56.5℃ 미만인 경우에는, 폴리 에스테르의 부분적 용해 및 평활이 충분히 진행되기 전에 혼합 조성물이 조기에 증발되어 버리는 문제가 있고, 혼합 조성물의 끓는점이 126℃를 초과하는 경우에는, 혼합 조성물의 증발에 비교적 장시간이 소요되는 결과, 폴리 에스테르의 과도한 용해가 진행되어 폴리 에스테르의 기본 구조가 완전히 소멸되는 문제가 있다.On the other hand, when the boiling point of the mixed composition in the present invention is less than 56.5 ° C, there is a problem that the mixed composition is evaporated prematurely before the partial dissolution and smoothing of the polyester sufficiently progress. When the boiling point of the mixed composition exceeds 126 ° C , It takes a relatively long time to evaporate the mixed composition, resulting in excessive dissolution of the polyester, resulting in the complete disappearance of the basic structure of the polyester.
따라서, 본 발명에서의 혼합 조성물의 끓는점은 56.5℃ 내지 126℃가 되도록 함이 바람직하다. Therefore, the boiling point of the mixed composition in the present invention is preferably 56.5 ° C to 126 ° C.
구체적으로, 56.5℃의 끓는점을 가지는 아세톤은 저온에서 폴리 에스테르를 용해시키는 역할을 하며, 126℃의 끓는점을 가지는 부틸아세테이트는 조성물의 휘발을 지연시켜 혼합물에 의한 폴리 에스테르의 용해 및 평활이 충분히 진행되도록 한다.Specifically, acetone having a boiling point of 56.5 캜 serves to dissolve the polyester at a low temperature, and butyl acetate having a boiling point of 126 캜 serves to retard the volatilization of the composition and sufficiently dissolve and smooth the polyester by the mixture do.
아울러, 아세톤과 부틸아세테이트의 혼합비를 결정함에 있어서, 아세톤을 0.5 부피비 미만으로 혼합하는 경우에는, 아세톤에 의한 폴리 에스테르의 용해 작용을 충분히 기대할 수 없으며, 1.5 부피비 이상으로 혼합하는 경우에는 폴리 에스테르의 과도한 용해가 이루어지므로, 본 발명을 실시함에 있어서, 아세톤의 혼합 부피비는 0.5 내지 1.5 부피비로 결정하였다.Further, in the case of mixing acetone and butyl acetate at a mixing ratio of less than 0.5 volume ratio, it is impossible to sufficiently expect the polyester to dissolve by acetone. When the mixing ratio is more than 1.5 volume ratio, excessive polyester In carrying out the present invention, the mixing volume ratio of acetone was determined to be 0.5 to 1.5 volume ratio.
또한, 부틸아세테이트를 1 부피비 미만으로 혼합하는 경우에는, 용해된 폴리 에스테르의 충분한 평활 작용을 기대할 수 없으며, 3 부피비를 초과하여 혼합하는 경우에는 용해된 폴리에스테르가 과도하게 확산되는 문제가 있으므로, 본 발명을 실시함에 있어서, 부틸아세테이트의 혼합 부피비는 1 내지 3 부피비로 결정하였다.In addition, when butyl acetate is mixed at a volume ratio of less than 1 part by volume, a sufficient smoothing action of the dissolved polyester can not be expected. When the mixing ratio exceeds 3 volume ratio, there is a problem that the dissolved polyester is excessively diffused. In carrying out the invention, the mixing volume ratio of butyl acetate was determined to be 1 to 3 volume ratio.
이상에서는 본 발명의 바람직한 실시예 및 응용예에 대하여 도시하고 설명하였지만, 본 발명은 상술한 특정의 실시예 및 응용예에 한정되지 아니하며, 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 발명이 속하는 기술분야에서 통상의 지식을 가진자에 의해 다양한 변형실시가 가능한 것은 물론이고, 이러한 변형실시들은 본 발명의 기술적 사상이나 전망으로부터 개별적으로 이해되어져서는 안될 것이다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, It will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the present invention.
또한, 본 발명에서 사용한 용어는 단지 특정한 실시 예를 설명하기 위해 사용된 것으로 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 출원에서, "포함하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.
Furthermore, the terms used in the present invention are used only to describe specific embodiments and are not intended to limit the present invention. The singular expressions include plural expressions unless the context clearly dictates otherwise. In the present application, the terms "comprises" or "having" and the like are used to specify that there is a feature, a number, a step, an operation, an element, a component or a combination thereof described in the specification, But do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, or combinations thereof.
10: 모자, 50: 분무기.10: hat, 50: atomizer.
Claims (8)
상기 고분자 물질 용해제는 아세톤이고,
상기 평활제는 부틸아세테이트인 것인 합성 섬유 원단 강화용 조성물.
A polymer material dissolver and a smoothing agent,
Wherein the polymeric substance dissolving agent is acetone,
Wherein the smoothing agent is butyl acetate.
상기 고분자 물질은 폴리 에스테르인 것인 합성 섬유 원단 강화용 조성물.
The method according to claim 1,
Wherein the polymeric material is a polyester.
상기 합성 섬유 원단에 도포된 상기 조성물을 건조시키는 단계
를 포함하며,
상기 고분자 물질 용해제는 아세톤이고,
상기 평활제는 부틸아세테이트인 것인 합성 섬유 원단 강화 방법.
Applying a composition prepared by mixing a polymeric substance-dissolving agent and a smoothing agent to a synthetic fiber fabric; And
Drying said composition applied to said synthetic fiber fabric
/ RTI >
Wherein the polymeric substance dissolving agent is acetone,
Wherein the smoothing agent is butyl acetate.
상기 고분자 물질은 폴리 에스테르인 것인 합성 섬유 원단 강화 방법.
6. The method of claim 5,
Wherein the polymeric material is a polyester.