CN108552650A - A kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric - Google Patents

A kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric Download PDF

Info

Publication number
CN108552650A
CN108552650A CN201810299096.4A CN201810299096A CN108552650A CN 108552650 A CN108552650 A CN 108552650A CN 201810299096 A CN201810299096 A CN 201810299096A CN 108552650 A CN108552650 A CN 108552650A
Authority
CN
China
Prior art keywords
acid fiber
polylactic
fiber
moisture absorbing
sweat releasing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810299096.4A
Other languages
Chinese (zh)
Inventor
陈东进
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan Lianzhou Intellectual Property Operation and Management Co Ltd
Original Assignee
Dongguan Lianzhou Intellectual Property Operation and Management Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongguan Lianzhou Intellectual Property Operation and Management Co Ltd filed Critical Dongguan Lianzhou Intellectual Property Operation and Management Co Ltd
Priority to CN201810299096.4A priority Critical patent/CN108552650A/en
Publication of CN108552650A publication Critical patent/CN108552650A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric, detailed process is:First using acrylic monomer as modified monomer, modified polylactic acid fiber is made using the method for in-situ polymerization;Then one layer of nano silicon oxide is deposited on modified polylactic acid fiber surface;The blended obtained fabric of modified polylactic acid fiber and polyester fiber that finally nano silicon oxide obtained is coated, fabric sucting wet air permeability made from this method is good, soft comfortable, and prepare it is simple, it is at low cost.

Description

A kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric
Technical field:
The present invention relates to textile preparation fields, are specifically related to a kind of acid fiber by polylactic/blend polyester of moisture absorbing and sweat releasing The preparation method of fabric.
Background technology:
With the quickening of human civilization process, the change of the progress and people's consumption idea of science and technology, people are to influencing the mankind The requirement of the various aspects such as the food, clothing, housing and transportation of quality of life is higher and higher.For dress, requirement of the people to clothes, Through from initial screening body, it is warming, protection etc. practicabilities diversion functionality, both effectiveness, comfort.Wherein, especially to garment surface More stringent requirements are proposed in terms of the comfort of material.Recently, an investigation display of the U.S. to consumer, 81% consumer's handle The comfort of clothes has fallen back on relatively secondary position as main selection, the Design modelling of clothes.In China, consumer Comfort alternatively clothes an important factor for one of.Therefore, the comfort of clothes and functionality have become garment production enterprise The key point that industry obtains market advantage.Clothes and the theme of textile prevalence from simple moulding style progressively towards Direction transfer centered on Thermo-Wet Comfort, tactile comfort.Comfortable features of clothing has become the common demands of people's dressing, convex Show the life new concept in 2l centuries --- it is green and comfortable.
Human body is ceaselessly generating heat.Even if being seated, human body about generates 55-60kcal/m2The heat of h.Still more One day most of the time of human body is kept in motion.Either normal walking, or carry out indoor and outdoor movement, human body Always perspire.When perspiring, then good Thermo-Wet Comfort, the i.e. performance of moisture absorbing and sweat releasing quick-drying are required to clothes." moisture absorption Perspiring quick-drying " property refers to when being worn under hygrothermal environment, fabric can absorb the sweat of skin surface rapidly, and quickly be conducted It to fabric exterior and then evaporates, so that skin surface is kept dry and comfortable, human body sensory is comfortable." moisture absorption quick-drying fabric " is that have simultaneously There is the fabric of two kinds of characteristics of moisture absorption and quick-drying.In general, largely being perspired due to movement in the season of high temperature and humidity and human body In the case of, all it is difficult to have both water imbibition and quick-drying both property in untreated preceding either natural fiber or synthetic fibers Energy.
Invention content:
The invention discloses a kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric, party's legal systems Acid fiber by polylactic/blend polyester fabric the soft comfortable obtained, moisture absorbing and sweat releasing property is good, and has certain anti-microbial property, mechanical property It can be good.
To achieve the above object, the present invention uses following technical scheme:
A kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric, includes the following steps:
(1) acrylic monomer and deionized water are uniformly mixed, are then added emulsifier, ultrasonic disperse 30min, then Acid fiber by polylactic is added, is to slowly warm up to 60-80 DEG C, initiator is added dropwise, reacts 10-40min, after reaction, filters, precipitation It is washed using absolute ethyl alcohol, it is dry, modified polylactic acid fiber is made;
(2) modified polylactic acid fiber obtained above is placed in absolute ethyl alcohol, ethyl orthosilicate is then added dropwise, stirring is mixed After conjunction, the nitrogen with water is passed through under conditions of 50-60 DEG C, back flow reaction 10-20h is cooled to room temperature, mistake after reflux Filter, precipitation are washed with ethyl alcohol, dry, and the modified polylactic acid fiber of nano silicon oxide cladding is made;
(3) the blended obtained fabric of modified polylactic acid fiber and polyester fiber coated nano silicon oxide obtained above.
As a preferred embodiment of the above technical solution, in step (1), the acrylic monomer is ethyl acrylate, acrylic acid One or more mixing in methyl esters, methyl methacrylate, butyl acrylate.
As a preferred embodiment of the above technical solution, in step (1), the emulsifier is polyethenoxy sorbitan list oleic acid It is one or more in ester, neopelex, dimethyl silicone polymer, lauryl sodium sulfate, esters of silicon acis coupling agent Mixing.
As a preferred embodiment of the above technical solution, in step (1), the initiator is cumyl peroxide.
As a preferred embodiment of the above technical solution, in step (1), the dosage of each component is respectively in parts by weight:Acrylic acid 30-60 parts of class monomer, 20-40 parts of deionized water, 2-4 parts of emulsifier, 15-33 parts of acid fiber by polylactic, 4-7 parts of initiator.
As a preferred embodiment of the above technical solution, in step (2), the modified polylactic acid fiber, ethyl orthosilicate quality Than for (5-11):0.3.
As a preferred embodiment of the above technical solution, in step (3), the modified polylactic acid fiber of nano silicon oxide cladding and The mass ratio of polyester fiber is 1:(3-5).
As a preferred embodiment of the above technical solution, in step (3), the PET fiber surface is also wrapped on one layer of kapok fibre Dimension.
Compared with prior art, the present invention has the following advantages:
The base stock that the present invention is prepared using acid fiber by polylactic, polyester fiber as fabric, in order to improve the moisture absorption of fabric Perspiration discharging performance, the present invention are first modified polylactic acid fiber surface by the way of acrylic monomer in-situ polymerization, have Effect improves the moisture pick-up properties of acid fiber by polylactic, and in order to further improve the performance of acid fiber by polylactic, the present invention is after modification Polylactic acid fiber surface in-situ deposition nano silicon oxide, be evenly distributed in modified polylactic acid fiber surface, do not changing Become outside the original excellent properties of fiber, effectively improves the intensity of fiber;
The present invention is using polyester fiber and modified acid fiber by polylactic is blended prepares fabric, and polyester fiber is hydrophobic, modified Acid fiber by polylactic there is excellent hydrophily so that fabric obtained can effective moisture absorbing and sweat releasing, and PET fiber surface packet It is covered with bombax cotton, effectively increases the comfort of fabric.
Specific implementation mode:
For a better understanding of the present invention, below by embodiment, the present invention is further described, and embodiment is served only for solving The present invention is released, any restriction will not be constituted to the present invention.
Embodiment 1
A kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric, includes the following steps:
(1) acrylic monomer and deionized water are uniformly mixed, are then added emulsifier, ultrasonic disperse 30min, then Acid fiber by polylactic is added, is to slowly warm up to 60 DEG C, initiator is added dropwise, reacts 10min, after reaction, filtering, precipitation uses nothing Water-ethanol washs, dry, and modified polylactic acid fiber is made;Wherein, the dosage of each component is respectively in parts by weight:Acrylic compounds 30 parts of monomer, 20 parts of deionized water, 2 parts of emulsifier, 15 parts of acid fiber by polylactic, 4 parts of initiator;
(2) modified polylactic acid fiber obtained above is placed in absolute ethyl alcohol, ethyl orthosilicate is then added dropwise, stirring is mixed After conjunction, the nitrogen with water is passed through under conditions of 50-60 DEG C, back flow reaction 10h is cooled to room temperature after reflux, is filtered, and is sunk Shallow lake is washed with ethyl alcohol, dry, and the modified polylactic acid fiber of nano silicon oxide cladding is made;Wherein, the modified polylactic acid fiber, The mass ratio of ethyl orthosilicate is 5:0.3;
(3) the blended obtained fabric of modified polylactic acid fiber and polyester fiber coated nano silicon oxide obtained above; Wherein, the modified polylactic acid fiber of the nano silicon oxide cladding and the mass ratio of polyester fiber are 1:3.
Embodiment 2
A kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric, includes the following steps:
(1) acrylic monomer and deionized water are uniformly mixed, are then added emulsifier, ultrasonic disperse 30min, then Acid fiber by polylactic is added, is to slowly warm up to 80 DEG C, initiator is added dropwise, reacts 40min, after reaction, filtering, precipitation uses nothing Water-ethanol washs, dry, and modified polylactic acid fiber is made;Wherein, the dosage of each component is respectively in parts by weight:Acrylic compounds 60 parts of monomer, 40 parts of deionized water, 4 parts of emulsifier, 33 parts of acid fiber by polylactic, 7 parts of initiator;
(2) modified polylactic acid fiber obtained above is placed in absolute ethyl alcohol, ethyl orthosilicate is then added dropwise, stirring is mixed After conjunction, the nitrogen with water is passed through under conditions of 50-60 DEG C, back flow reaction 20h is cooled to room temperature after reflux, is filtered, and is sunk Shallow lake is washed with ethyl alcohol, dry, and the modified polylactic acid fiber of nano silicon oxide cladding is made;Wherein, the modified polylactic acid fiber, The mass ratio of ethyl orthosilicate is 11:0.3;
(3) the blended obtained fabric of modified polylactic acid fiber and polyester fiber coated nano silicon oxide obtained above; Wherein, the modified polylactic acid fiber of the nano silicon oxide cladding and the mass ratio of polyester fiber are 1:5.
Embodiment 3
A kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric, includes the following steps:
(1) acrylic monomer and deionized water are uniformly mixed, are then added emulsifier, ultrasonic disperse 30min, then Acid fiber by polylactic is added, is to slowly warm up to 65 DEG C, initiator is added dropwise, reacts 20min, after reaction, filtering, precipitation uses nothing Water-ethanol washs, dry, and modified polylactic acid fiber is made;Wherein, the dosage of each component is respectively in parts by weight:Acrylic compounds 40 parts of monomer, 25 parts of deionized water, 2.5 parts of emulsifier, 18 parts of acid fiber by polylactic, 5 parts of initiator;
(2) modified polylactic acid fiber obtained above is placed in absolute ethyl alcohol, ethyl orthosilicate is then added dropwise, stirring is mixed After conjunction, the nitrogen with water is passed through under conditions of 50-60 DEG C, back flow reaction 12h is cooled to room temperature after reflux, is filtered, and is sunk Shallow lake is washed with ethyl alcohol, dry, and the modified polylactic acid fiber of nano silicon oxide cladding is made;Wherein, the modified polylactic acid fiber, The mass ratio of ethyl orthosilicate is 7:0.3;
(3) the blended obtained fabric of modified polylactic acid fiber and polyester fiber coated nano silicon oxide obtained above; Wherein, the modified polylactic acid fiber of the nano silicon oxide cladding and the mass ratio of polyester fiber are 1:3.5.
Embodiment 4
A kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric, includes the following steps:
(1) acrylic monomer and deionized water are uniformly mixed, are then added emulsifier, ultrasonic disperse 30min, then Acid fiber by polylactic is added, is to slowly warm up to 70 DEG C, initiator is added dropwise, reacts 30min, after reaction, filtering, precipitation uses nothing Water-ethanol washs, dry, and modified polylactic acid fiber is made;Wherein, the dosage of each component is respectively in parts by weight:Acrylic compounds 45 parts of monomer, 30 parts of deionized water, 3 parts of emulsifier, 21 parts of acid fiber by polylactic, 6 parts of initiator;
(2) modified polylactic acid fiber obtained above is placed in absolute ethyl alcohol, ethyl orthosilicate is then added dropwise, stirring is mixed After conjunction, the nitrogen with water is passed through under conditions of 50-60 DEG C, back flow reaction 14h is cooled to room temperature after reflux, is filtered, and is sunk Shallow lake is washed with ethyl alcohol, dry, and the modified polylactic acid fiber of nano silicon oxide cladding is made;Wherein, the modified polylactic acid fiber, The mass ratio of ethyl orthosilicate is 8:0.3;
(3) the blended obtained fabric of modified polylactic acid fiber and polyester fiber coated nano silicon oxide obtained above; Wherein, the modified polylactic acid fiber of the nano silicon oxide cladding and the mass ratio of polyester fiber are 1:4.
Embodiment 5
A kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric, includes the following steps:
(1) acrylic monomer and deionized water are uniformly mixed, are then added emulsifier, ultrasonic disperse 30min, then Acid fiber by polylactic is added, is to slowly warm up to 70 DEG C, initiator is added dropwise, reacts 35min, after reaction, filtering, precipitation uses nothing Water-ethanol washs, dry, and modified polylactic acid fiber is made;Wherein, the dosage of each component is respectively in parts by weight:Acrylic compounds 50 parts of monomer, 35 parts of deionized water, 3.5 parts of emulsifier, 25 parts of acid fiber by polylactic, 6 parts of initiator;
(2) modified polylactic acid fiber obtained above is placed in absolute ethyl alcohol, ethyl orthosilicate is then added dropwise, stirring is mixed After conjunction, the nitrogen with water is passed through under conditions of 50-60 DEG C, back flow reaction 16h is cooled to room temperature after reflux, is filtered, and is sunk Shallow lake is washed with ethyl alcohol, dry, and the modified polylactic acid fiber of nano silicon oxide cladding is made;Wherein, the modified polylactic acid fiber, The mass ratio of ethyl orthosilicate is 9:0.3;
(3) the blended obtained fabric of modified polylactic acid fiber and polyester fiber coated nano silicon oxide obtained above; Wherein, the modified polylactic acid fiber of the nano silicon oxide cladding and the mass ratio of polyester fiber are 1:4.
Embodiment 6
A kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric, includes the following steps:
(1) acrylic monomer and deionized water are uniformly mixed, are then added emulsifier, ultrasonic disperse 30min, then Acid fiber by polylactic is added, is to slowly warm up to 75 DEG C, initiator is added dropwise, reacts 35min, after reaction, filtering, precipitation uses nothing Water-ethanol washs, dry, and modified polylactic acid fiber is made;Wherein, the dosage of each component is respectively in parts by weight:Acrylic compounds 55 parts of monomer, 38 parts of deionized water, 3.5 parts of emulsifier, 30 parts of acid fiber by polylactic, 6.5 parts of initiator;
(2) modified polylactic acid fiber obtained above is placed in absolute ethyl alcohol, ethyl orthosilicate is then added dropwise, stirring is mixed After conjunction, the nitrogen with water is passed through under conditions of 50-60 DEG C, back flow reaction 18h is cooled to room temperature after reflux, is filtered, and is sunk Shallow lake is washed with ethyl alcohol, dry, and the modified polylactic acid fiber of nano silicon oxide cladding is made;Wherein, the modified polylactic acid fiber, The mass ratio of ethyl orthosilicate is 10:0.3;
(3) the blended obtained fabric of modified polylactic acid fiber and polyester fiber coated nano silicon oxide obtained above; Wherein, the modified polylactic acid fiber of the nano silicon oxide cladding and the mass ratio of polyester fiber are 1:4.5.

Claims (8)

1. a kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric, which is characterized in that including following step Suddenly:
(1) acrylic monomer and deionized water are uniformly mixed, emulsifier is then added, then ultrasonic disperse 30min is added Acid fiber by polylactic is to slowly warm up to 60-80 DEG C, and initiator is added dropwise, and reacts 10-40min, and after reaction, filtering, precipitation uses Absolute ethyl alcohol washs, dry, and modified polylactic acid fiber is made;
(2) modified polylactic acid fiber obtained above is placed in absolute ethyl alcohol, ethyl orthosilicate is then added dropwise, be stirred Afterwards, the nitrogen with water is passed through under conditions of 50-60 DEG C, back flow reaction 10-20h is cooled to room temperature after reflux, filtering, Precipitation is washed with ethyl alcohol, dry, and the modified polylactic acid fiber of nano silicon oxide cladding is made;
(3) the blended obtained fabric of modified polylactic acid fiber and polyester fiber coated nano silicon oxide obtained above.
2. a kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric as described in claim 1, feature It is:In step (1), the acrylic monomer is ethyl acrylate, methyl acrylate, methyl methacrylate, acrylic acid One or more mixing in butyl ester.
3. a kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric as described in claim 1, feature It is:In step (1), the emulsifier is polyoxyethylene sorbitan monooleate, neopelex, poly- diformazan One or more mixing in radical siloxane, lauryl sodium sulfate, esters of silicon acis coupling agent.
4. a kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric as described in claim 1, feature It is:In step (1), the initiator is cumyl peroxide.
5. a kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric as described in claim 1, feature It is:In step (1), the dosage of each component is respectively in parts by weight:30-60 parts of acrylic monomer, deionized water 20-40 Part, 2-4 parts of emulsifier, 15-33 parts of acid fiber by polylactic, 4-7 parts of initiator.
6. a kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric as described in claim 1, feature It is:In step (2), the modified polylactic acid fiber, ethyl orthosilicate mass ratio be (5-11):0.3.
7. a kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric as described in claim 1, feature It is:In step (3), the modified polylactic acid fiber of the nano silicon oxide cladding and the mass ratio of polyester fiber are 1:(3-5).
8. a kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric as described in claim 1, feature It is:In step (3), the PET fiber surface is also wrapped on one layer of bombax cotton.
CN201810299096.4A 2018-04-04 2018-04-04 A kind of preparation method of the acid fiber by polylactic of moisture absorbing and sweat releasing/blend polyester fabric Withdrawn CN108552650A (en)