KR101586274B1 - Wrap film composition for food and wrap film prepared therefrom - Google Patents
Wrap film composition for food and wrap film prepared therefrom Download PDFInfo
- Publication number
- KR101586274B1 KR101586274B1 KR1020130132118A KR20130132118A KR101586274B1 KR 101586274 B1 KR101586274 B1 KR 101586274B1 KR 1020130132118 A KR1020130132118 A KR 1020130132118A KR 20130132118 A KR20130132118 A KR 20130132118A KR 101586274 B1 KR101586274 B1 KR 101586274B1
- Authority
- KR
- South Korea
- Prior art keywords
- wrap film
- weight
- plasticizer
- value
- parts
- Prior art date
Abstract
본 발명은 염화비닐수지; 1차 가소제인 팜핵유로부터 추출한 아세틸화 모노글리세린; 2차 가소제인 에폭시화대두유; 지방산 에스테르 화합물; 및 열 안정제를 포함하는 염화비닐수지 랩 필름 조성물 및 이로부터 제조되는 랩 필름에 관한 것으로, 식물성 글리세린계 가소제를 사용하여, 풀림성과 신율이 향상된 식품 포장용 랩 필름을 제공할 수 있다.The present invention relates to a resin composition comprising a vinyl chloride resin; Acetylated monoglycerin extracted from the palm oil channel as the primary plasticizer; Epoxidized soybean oil as a secondary plasticizer; Fatty acid ester compounds; And a thermal stabilizer, and a wrap film produced therefrom, and can provide a wrap film for food wrapping which is improved in releasability and elongation by using a vegetable glycerin-based plasticizer.
Description
본 발명은 염화비닐수지 랩 필름 조성물 및 이로부터 제조되는 랩 필름에 관한 것으로, 구체적으로는 글리콜계 가소제 대신에 식물성 글리세린계 가소제를 사용하여, 제조된 랩 필름의 풀림성과 신율을 향상시킬 수 있으며, 특히 식물성 원료의 사용으로 인해 환경친화적이면서도 식품 포장용으로 매우 적합한 랩 필름 조성물 및 이로부터 제조되는 랩 필름에 관한 것이다.The present invention relates to a polyvinyl chloride resin wrap film composition and a wrap film produced therefrom. More specifically, it is possible to improve the releasability and elongation of the wrap film by using a vegetable glycerin plasticizer in place of the glycol plasticizer, And more particularly to a wrap film composition which is environmentally friendly and very suitable for food packaging due to the use of vegetable raw materials, and a wrap film produced therefrom.
식품 포장용 랩 필름은 일반적으로 두께가 12~15㎛ 정도의 투명성이 높은 필름으로, 포장방법이 간편하고, 이물질 유입 방지 기능과 습기 차단 등으로 식품의 신선도를 유지하기에 적합하여, 과일, 야채, 떡, 가공음식 및 배달음식 등과 같은 모든 종류의 식품의 보관 및 포장에 널리 이용되고 있다.Wrapping film for food packaging is generally a film with high transparency of 12 ~ 15㎛ in thickness. It is easy to be wrapped and is suitable for maintaining the freshness of food by preventing foreign matter inflow and blocking moisture, It is widely used for storage and packaging of all kinds of foods such as rice cake, processed food and delivery food.
랩 필름은 폴리염화비닐(Polyvinylchloride, PVC), 폴리염화비닐리덴(Polyvinylidene chloride, PVDC), 저밀도 폴리에틸렌(low density polyethylene, LDPE) 등과 같은 합성수지를 주재료로 한 것이 주류를 이루고 있으나, 식품 포장용 랩 필름은 일반적으로 투명성, 점착성, 방담성, 신율, 부드러움, 인열강도 등의 물성이 확보되어야 하는 특징 때문에, 이와 같은 물성이 우수한, 염화비닐수지가 주로 사용되고 있다. 폴리염화비닐리덴과 저밀도 폴리에틸렌은 염화비닐수지 대비 투명성, 신율, 점착성 및 방담성 등 랩 필름의 품질을 결정짓는 물성 등이 현저히 떨어져 식품 포장용 랩 필름 제조용으로는 적용에 한계가 있다.Wrap films are mainly made of synthetic resins such as polyvinylchloride (PVC), polyvinylidene chloride (PVDC), and low density polyethylene (LDPE), but wrap films for food packaging In general, vinyl chloride resins having excellent physical properties such as transparency, tackiness, antifogging property, elongation, softness and tear strength are required to be secured. The polyvinylidene chloride and low density polyethylene are remarkably reduced in properties such as transparency, elongation, tackiness and anti-fogging properties, which determine the quality of the wrap film, compared with the vinyl chloride resin, and the application thereof is limited.
염화비닐수지 랩 필름 조성물에는 랩 필름의 가공성 개선 및 연질성 부여 등의 목적으로 가소제가 필수적으로 첨가되는데, 가소제는 높은 기계적 물성을 가지는 디에틸헥실아디페이트(DOA) 또는 디에틸헥실프탈레이트(DOP)가 주로 사용되어 왔다. 그러나, 아디페이트계 및 프탈레이트계 가소제는 환경호르몬을 방출하는 주요 성분으로 추정되고 있거나, 미국 환경보호국 및 세계야생보호기금(WWF) 등에서 환경호르몬 관찰물질로 분류하고 있어, 현재는 내분비 교란물질이 분비되지 않는 글리세린계 가소제나 글리콜계 가소제가 널리 사용되고 있다.In the vinyl chloride resin wrap film composition, a plasticizer is essentially added for the purpose of improving processability and softness of the wrap film. The plasticizer is a diethylhexyl adipate (DOA) or diethylhexyl phthalate (DOP) having high mechanical properties. Has been mainly used. However, the adipate-based and phthalate-based plasticizers are presumed to be major components releasing environmental hormones, or classified as environmental hormone-observing substances by the US Environmental Protection Agency and the World Wildlife Fund (WWF), and are currently secreted by endocrine disruptors A glycerin-based plasticizer and a glycol-based plasticizer have been widely used.
글리콜계 가소제는 디에틸렌 글리콜계 가소제와 트리에틸렌 글리콜계 가소제가 주로 사용되는데, 글리콜계 가소제를 사용한 랩 필름은 점착성이 높고 투명도가 좋은 특징이 있으나, 필름 자체의 부드러움(Softness)이 떨어지고, 사용시 풀림성이 떨어진다. 또한, 랩 필름 사용시의 중요 물성인 신율은 모노 글리세린 가소제 대비 약간 떨어지는 특징이 있다. 글리콜계 가소제는 산과 알코올을 반응시켜 만든 석유계통의 가소제이기 때문에 식물성 원료를 사용한 글리세린 가소제에 비해서는 친환경성이 떨어진다. The glycol-based plasticizer and the triethylene glycol-based plasticizer are mainly used as the glycol-based plasticizer. The wrap film using the glycol-based plasticizer has high tackiness and good transparency. However, the softness of the film itself is low, The castle falls. In addition, the elongation, which is an important property of the wrap film, is slightly lower than that of the monoglycerin plasticizer. Since glycol-based plasticizers are petroleum-based plasticizers made by reacting acids and alcohols, they are less eco-friendly than glycerin plasticizers using plant-based ingredients.
글리콜계 가소제와 더불어 랩 필름의 가소제로 널리 사용 중인 글리세린 가소제는 아세틸화된 모노글리세린, 아세틸화된 디글리세린 또는 그 혼합물이 주로 사용되는데, 아세틸화된 글리세린 가소제를 사용하게 되면 신율, 풀림성, 부드러움 등의 주요 물성이 향상되는 효과가 있으며 순식물성 원료를 사용하여 친환경적인 특징이 있다. 그러나 원하는 물성을 얻기 위해 다량 사용시에는 랩 필름의 표면에 가소제가 배어나는 블리딩(Bleeding) 현상이 심하게 발생하며, 이에 따라 점착성 및 투명성이 현저히 저하되고 염화비닐수지와의 상용성이 떨어져 외관 품질도 떨어지는 현상이 나타나게 된다. 이에 따라 1차 가소제로서 다량을 단독으로 사용하는 대신 글리콜계 가소제와 같은 다른 가소제를 일정 비율로 혼합하여 사용해야 하는 제약이 존재한다.The glycerin plasticizer widely used as a plasticizer of a wrap film together with a glycol plasticizer is mainly acetylated monoglycerin, acetylated diglycerin or a mixture thereof. When an acetylated glycerin plasticizer is used, the elongation, loosening and softness And it has an eco-friendly characteristic by using pure and raw materials. However, in order to obtain a desired physical property, a large amount of plasticizer causes a bleeding phenomenon in which a plasticizer is exuded on the surface of the wrap film, resulting in marked deterioration of tackiness and transparency, poor compatibility with vinyl chloride resin, A phenomenon appears. Accordingly, there is a restriction that other plasticizers such as glycol plasticizers should be mixed at a certain ratio instead of using a large amount alone as the primary plasticizers.
따라서 본 발명은 1차 가소제로 글리콜계 가소제를 함유시키지 않더라도 신율, 풀림성 및 부드러움을 향상시킬 수 있고, 염화비닐수지와의 상용성이 잘 유지되어 랩 표면에 가소제가 배어나거나 투명성이 저하되는 것과 같은 현상이 나타나지 않는 랩 필름용 조성물을 제공하는 것을 목적으로 한다.Accordingly, the present invention can improve the elongation, releasability and softness without containing a glycol-based plasticizer as a primary plasticizer, maintain compatibility with the vinyl chloride resin well and allow the plasticizer to permeate the surface of the wrap, It is an object of the present invention to provide a composition for a wrap film in which the same phenomenon does not occur.
또한 본 발명은 친환경성 소재를 기반으로 하여 식품 포장용으로 사용하기에 적합한 염화비닐수지 랩 필름을 제공하는 것을 목적으로 한다.It is another object of the present invention to provide a vinyl chloride resin wrap film suitable for use in food packaging based on environmentally friendly materials.
이와 같은 목적을 달성하기 위하여, 본 발명은 염화비닐 수지; 1차 가소제로 팜핵유로부터 추출한 아세틸화 모노글리세린; 2차 가소제로 에폭시화 대두유; 지방산 에스테르 화합물; 및 열 안정제를 포함하는 염화비닐수지 랩 필름 조성물을 제공한다.In order to achieve the above object, the present invention provides a resin composition comprising a vinyl chloride resin; Acetylated monoglycerin extracted from palm kernel oil with primary plasticizer; Epoxidized soybean oil as a secondary plasticizer; Fatty acid ester compounds; And a heat stabilizer.
본 발명의 일 구현예에 따르면, 염화비닐 수지 50 내지 75 중량부; 팜핵유로부터 추출한 아세틸화 모노글리세린 가소제 20 내지 30 중량부; 에폭시화 대두유 4 내지 10 중량부; 지방산 에스테르 화합물 0.5 내지 5 중량부; 및 열 안정제 0.5 내지 5 중량부를 포함하는 염화비닐수지 랩 필름 조성물이 제공될 수 있다. According to one embodiment of the present invention, a resin composition comprising 50 to 75 parts by weight of a vinyl chloride resin; 20 to 30 parts by weight of an acetylated monoglycerin plasticizer extracted from the palm oil channel; 4 to 10 parts by weight of epoxidized soybean oil; 0.5 to 5 parts by weight of a fatty acid ester compound; And 0.5 to 5 parts by weight of a heat stabilizer may be provided.
본 발명의 다른 일 구현예에 따르면, 팜핵유로부터 추출한 아세틸화 모노글리세린은 팜핵유로부터 추출한 글리세린 원료를 아세틸화 및 분자증류하여 얻은 것으로, 모노에스테르(Monoester)의 함량이 85중량% 이상인 것이 바람직하다. According to another embodiment of the present invention, the acetylated monoglycerin extracted from the palm kernel channel is obtained by acetylation and molecular distillation of the glycerin raw material extracted from the palm kernel channel, and the content of the monoester is preferably 85% by weight or more .
본 발명의 또 다른 일 구현예에 따르면, 팜핵유로부터 추출한 아세틸화 모노글리세린은 산 값(acid value)이 1 내지 3 KOH mg/g, 비누화 값(saponification value)이 425 내지 450, 수산기 값(hydroxyl value)이 10 내지 20이며, 그리고 요오드 값(Iodine value)이 10 내지 20인 것이 바람직하다.According to another embodiment of the present invention, the acetylated monoglycerin extracted from the palm kernel channel has an acid value of 1 to 3 KOH mg / g, a saponification value of 425 to 450, a hydroxyl value (hydroxyl value of 10 to 20, and an iodine value of 10 to 20 is preferable.
본 발명의 또 다른 일 구현예에 따르면, 염화비닐수지는 겉보기 비중이 0.50 내지 0.58 g/cm3 이며, 중합도는 950 내지 1050인 것이 바람직하다. According to another embodiment of the present invention, it is preferable that the vinyl chloride resin has an apparent specific gravity of 0.50 to 0.58 g / cm 3 and a degree of polymerization of 950 to 1050.
본 발명의 또 다른 일 구현예에 따르면, 에폭시화 대두유는 비중이 0.982 내지 1.002 이며, 산 값이 0.0001 내지 0.5 KOH mg/g, 분자량이 800 내지 1200, 및 요오드 값이 0.5 내지 3인 것이 바람직하다.According to another embodiment of the present invention, the epoxidized soybean oil preferably has a specific gravity of 0.982 to 1.002, an acid value of 0.0001 to 0.5 KOH mg / g, a molecular weight of 800 to 1200, and an iodine value of 0.5 to 3 .
본 발명의 또 다른 일 구현예에 따르면, 지방산 에스테르 화합물은 산 값이 1 내지 3 KOH mg/g, 요오드 값이 30 내지 55, 비누화 값(saponification value)이 140 내지 160이며, 수분 함량은 수분을 포함하지 않거나 1.5 중량% 이하인 것이 바람직하다. According to another embodiment of the present invention, the fatty acid ester compound has an acid value of 1 to 3 KOH mg / g, an iodine value of 30 to 55, a saponification value of 140 to 160, Or not more than 1.5% by weight.
본 발명의 또 다른 일 구현예에 따르면, 지방산 에스테르 화합물은 바람직하게 폴리글리세린 모노올레이트(Polyglycerine Monooleate), 폴리글리세린 모노팔미테이트(Polyglycerine Monopalmitate) 또는 이들의 혼합물이 될 수 있다. According to another embodiment of the present invention, the fatty acid ester compound is preferably polyglycerine monooleate, polyglycerine monopalmitate or a mixture thereof.
본 발명의 또 다른 일 구현예에 따르면, 열 안정제는 칼슘 지방산염, 아연 지방산염, 디하이드로 아세트산(dehydroacetic acid), 에폭시화 대두유, 리시놀산(ricinolic acid), 및 노르말-파라핀(n-paraffin)(CH3(CH2) n CH3(n=11))으로 이루어지는 칼슘-아연계 조성물에 2,6-디-터셔리-부틸-파라-크레졸(2,6-Di-tert-butyl-P-Cresol)을 첨가한 것으로, 비중이 0.900 내지 0.960이며 점도가 1 내지 100 cps인 것이 바람직하다. According to another embodiment of the present invention, the heat stabilizer is selected from the group consisting of calcium fatty acid salts, zinc fatty acid salts, dehydroacetic acid, epoxidized soybean oil, ricinolic acid, and n-paraffin. Di-tert-butyl-p-cresol was added to a calcium-zinc-based composition consisting of (CH 3 (CH 2 ) n CH 3 -Cresol), and it is preferable that the specific gravity is 0.900 to 0.960 and the viscosity is 1 to 100 cps.
본 발명은 또한 그 두께가 9 내지 15 ㎛이며, 풀림성 및 신율이 향상된 염화비닐수지 랩 필름을 제공한다. The present invention also provides a vinyl chloride resin wrap film having a thickness of 9 to 15 탆 and improved releasability and elongation.
본 발명에 따른 랩 필름은 친환경성이 우수한 식물 유래 아세틸화 모노글리세린을 1차 가소제로 사용하여 식품 포장용으로 매우 적합하다.The wrap film according to the present invention is highly suitable for food packaging using plant-derived acetylated monoglycerin having excellent environment-friendliness as a primary plasticizer.
또한 본 발명에 따른 랩 필름은 염화비닐수지와의 상용성이 우수하여 랩 필름 사용시에 나타나는 문제점인 블리딩(bleeding)이 적은 동시에, 신율, 풀림성 및 부드러움이 우수하여, 사용자가 많은 힘을 들이지 않고 편리하게 포장 등에 사용할 수 있다.Further, the wrap film according to the present invention is excellent in compatibility with vinyl chloride resin, so that it is excellent in stretchability, releasability and softness, with little bleeding, which is a problem in use of wrap film, It can be conveniently used for packaging.
이하 본 발명의 염화비닐수지 랩 필름 조성물에 대하여 보다 상세히 설명한다.Hereinafter, the vinyl chloride resin wrap film composition of the present invention will be described in more detail.
본 명세서에서, 수치 범위를 기재함에 있어서 특별히 언급하지 않는 한, 수치의 하한은 그 값 이상을, 상한은 그 값 이하를 의미한다. In the present specification, unless otherwise stated in the description of the numerical range, the lower limit of the numerical value means more than the value and the upper limit means less than the value.
식품 포장용으로 널리 사용되는 랩 필름은 필름 자체가 부드럽고 필름이 쉽게 풀릴 수 있도록 풀림성이 좋으면, 사용자가 랩을 반복적으로 사용하더라도 적은 힘이 들어 사용하기에 편리하며 포장을 하기에도 수월하게 해 준다. 또한, 잘 늘어나는 성질을 뜻하는 신율이 향상되면, 불규칙한 형태를 가지고 있거나 혹은 크기가 큰 용기 등을 포장할 경우에도 사용자가 피포장체의 크기 이상으로 필름을 늘려서 포장을 하기에 용이하며, 또한 필름 자체의 탄성으로 인해 필름이 잘 찢어지지 않고 필름끼리 점착을 하여도 잘 풀리지 않는 특성을 가지게 된다.Wrap films widely used for food packaging are easy to use and easy to package even if the user repeatedly uses the wrap because the film itself is soft and the film is easy to loosen so that the film can be easily unwound. In addition, when the elongation rate, which means a good stretching property, is improved, even when a container having an irregular shape or a large size is packed, it is easy for the user to stretch the film more than the size of the packed body, The film is not easily torn due to the elasticity of the film itself, and even if the films adhere to each other, the film is not easily broken.
본 발명자들은 특정 소재로부터 추출한 아세틸화 모노글리세린을 1차 가소제로 사용하면, 글리콜계 가소제처럼 투명도 및 점착력이 높으면서도 염화비닐수지(이하, 'PVC'로 표기한 곳도 있다.)와의 상용성이 우수하여 블리딩(bleeding)이 적은 동시에, 신율 및 풀림성이 우수하며, 친환경적인 글리세린 가소제의 장점을 동시에 구현할 수 있는 것을 발견하고 본 발명을 완성하였다. The present inventors have found that when acetylated monoglycerin extracted from a specific material is used as a primary plasticizer, compatibility with vinyl chloride resin (hereinafter also referred to as " PVC ") is high as well as transparency and adhesiveness Which is superior in elongation and releasability and is environmentally friendly, can be realized at the same time. The present invention has been completed based on this discovery.
랩 필름 조성물의 일 성분인 가소제는 염화비닐수지에 유연성을 부여하고 가공성을 원활하게 하는 원료이다. A plasticizer which is one component of the wrap film composition is a raw material which imparts flexibility to the vinyl chloride resin and smoothes the processability.
가소제의 가소화 효율이 높으면 염화비닐수지의 분자 사이에 침투한 가소제가 염화비닐수지 분자 사이의 직접 끌어당기는 힘을 약하게 하고 윤활유와 같은 역할을 하여 잘 휘게 할 수 있는 연성을 부여하며, 신율, 인장강도와 같은 기계적 물성도 향상시킬 수 있다. 또한, 가소제는 PVC와의 상용성이 우수할수록 염화비닐수지 분자 사이에 잘 섞일 수 있으며, 특정 환경에서 혹은 시간이 지나면서 수지와 분리되어 표면으로 가소제가 배어나는 현상이 없어 안정적이다.When the plasticizing efficiency of the plasticizer is high, the plasticizer penetrating between the molecules of the vinyl chloride resin weakens the direct pulling force between the vinyl chloride resin molecules, gives the softener the ability to bend well by acting as a lubricant, Mechanical properties such as strength can also be improved. In addition, plasticizers can be well mixed with vinyl chloride resin molecules as they are more compatible with PVC, and are stable because they are separated from the resin in a specific environment or over time and have no swelling of the plasticizer on the surface.
본 발명은 1차 가소제로, 기름야자나무(oil palm)의 과실 속에 있는 핵인 팜핵으로부터 채취한 팜핵유를 아세틸화 과정을 거치게 하여 얻어진 아세틸화된 모노글리세린을 적용하였다. 팜핵유에는 올레인산 및 팔미트산 등의 지방산이 많이 함유되어 있는데 이 중 특히, 올레인산은 불포화 지방산으로서 가소제 내 함량이 높을수록 가소화 효율이 높고, PVC와의 상용성이 우수한 특징이 있다. 본 발명에 따라, 올레인산 함량이 높은 팜핵유로부터 추출한 아세틸화 모노글리세린을 1차 가소제로 사용한 염화비닐수지 랩 필름은 부드러움 및 풀림성 등이 향상되었으며, 투명성과 신율도 개선할 수 있었으며, 특히 가소제가 PVC와의 상용성이 우수하여 다량을 적용하여도 랩 필름 표면에 배어나는 현상이 없음을 확인하였다. 여기서 '다량'은 랩 필름으로서 갖추어야 하는 물성은 만족시킬 수 있으면서, 1차 가소제로서 사용할 수 있는 최대량까지를 의미한다. The present invention employs acetylated monoglycerin obtained by subjecting palm kernel oil collected from a palm kernel in a fruit palm of oil palm to acetylation as a primary plasticizer. The palm kernel oil contains a lot of fatty acids such as oleic acid and palmitic acid. Of these, oleic acid is an unsaturated fatty acid, and the higher the content in the plasticizer, the higher the plasticizing efficiency and the excellent compatibility with PVC. According to the present invention, a vinyl chloride resin wrap film using acetylated monoglycerin as a primary plasticizer extracted from a palm kernel channel having a high content of oleic acid has improved softness and releasability, and has also been able to improve transparency and elongation, It is confirmed that there is no phenomenon of swelling on the surface of wrap film even when a large amount of PVC is applied. Here, 'large amount' refers to the maximum amount that can be used as the primary plasticizer while satisfying the physical properties to be provided as the wrap film.
본 발명의 염화비닐수지 랩 필름 조성물은 염화비닐 수지; 1차 가소제로 팜핵유로부터 추출한 아세틸화 모노글리세린; 2차 가소제로 에폭시화 대두유; 지방산 에스테르 화합물; 및 열 안정제를 포함한다.The vinyl chloride resin wrap film composition of the present invention comprises a vinyl chloride resin; Acetylated monoglycerin extracted from palm kernel oil with primary plasticizer; Epoxidized soybean oil as a secondary plasticizer; Fatty acid ester compounds; And heat stabilizers.
염화비닐수지(Polyvinyl chloride, PVC)는 기본 중합체(Base polymer) 중 염화비닐의 함유율이 50% 이상인 합성수지로서, 열안정성 및 가공성이 취약하다는 단점이 있다. 반면에 염화비닐수지는 PVC에 가소제(Plasticizer), 안정제(Stabilizer), 방담제(anti-fogging agent) 등의 여러 가지 첨가제를 적절하게 사용하면 다양한 특성 및 물성을 부여할 수 있는 저가의 범용 수지라는 장점이 있다. 염화비닐수지는 범용 수지로서 가격이 저렴하고 다양한 첨가제의 배합이 가능하며, 투명도, 점착력 및 신율이 우수한 특성 때문에 랩 필름의 주재료로 사용되어 왔다.Polyvinyl chloride (PVC) is a synthetic resin having a content of vinyl chloride in a base polymer of 50% or more, which is disadvantageous in terms of heat stability and processability. On the other hand, vinyl chloride resin is a low-cost general-purpose resin that can give various properties and properties by using various additives such as plasticizers, stabilizers and anti-fogging agents to PVC There are advantages. Vinyl chloride resin is a general-purpose resin and its price is low, various additives can be mixed, and it has been used as a main material of a wrap film because of its excellent transparency, adhesive strength and elongation.
PVC는 고분자 수지로 다양한 중합도를 가질 수 있으나, 중중합도 PVC는 연질의 필름용으로 제조되어 투명성 및 신율 등이 뛰어난 특징이 있어 랩 필름의 원료로 가장 적합하다. 중합도가 중중합도 이하이면 랩의 기계적 강도 측면에서 물성이 저하되고, 중중합도 이상의 고중합도 PVC의 경우에는 기계적 물성은 높은 분자량으로 인해 뛰어나나 필름이 뻣뻣하고 부드러움이 떨어져 사용감이 떨어지는 점이 취약하다. 따라서 본 발명은 중합도가 950 내지 1050인 중중합도의 염화비닐수지로서, 겉보기 비중이 0.50 내지 0.58 g/cm3인 것을 사용한다. 이 경우 랩 필름으로서의 기계적 강도는 물론 부드러움을 갖춘 랩 필름을 얻을 수 있다. PVC is a polymer resin, which can have various degrees of polymerization, but PVC with medium degree of polymerization is manufactured for a flexible film and has excellent transparency and elongation, making it the most suitable raw material for a wrap film. When the degree of polymerization is lower than the degree of polymerization, the physical properties are lowered in terms of the mechanical strength of the wraps. In the case of PVC having a high degree of polymerization, the mechanical properties are excellent due to high molecular weight. Accordingly, the present invention employs a vinyl chloride resin having a degree of polymerization of 950 to 1050 and an apparent specific gravity of 0.50 to 0.58 g / cm < 3 & gt ;. In this case, a wrap film having softness as well as mechanical strength as a wrap film can be obtained.
염화비닐수지는 랩 필름 조성물 총 100 중량부에 대하여 50 내지 75 중량부로 포함되는 것이, 랩 필름으로서의 기본 물성 확보를 위해서 바람직하다.It is preferable that the vinyl chloride resin is contained in an amount of 50 to 75 parts by weight based on 100 parts by weight of the total amount of the wrap film composition in order to secure basic physical properties as a wrap film.
팜핵유로부터 추출한 아세틸화 모노글리세린은 팜핵유로부터 추출한 글리세린을 아세틸화시킨 후 분자증류하여 만들어진 순식물성 가소제로서, 환경친화적이며 글리콜계의 석유계 가소제보다 인체에 무해하여 식품포장용으로 매우 적합하게 사용될 수 있다. 또한, 통상 사용되어 오던 야자유로부터 추출하여 만든 범용적인 글리세린 가소제보다 불포화 지방산인 올레인산의 함량이 높아 신율 등의 기계적 물성이 우수한 특징이 있으며 PVC와의 상용성에 영향을 미치는 주물질인 모노에스테르(Monoester)의 함량이 85중량% 이상으로 높아서, 랩 필름 성형시 필름 표면에 가소제가 배어나는 현상이 없고 안정적인 장점이 있다. Acetylated monoglycerin extracted from palm kernel oil is a pure synthetic plasticizer made by acetylation of glycerin extracted from palm kernel oil and molecular distillation. It is more environmentally friendly and harmless to the human body than glycol based petroleum plasticizer, . Also, it is characterized by superior mechanical properties such as elongation due to high content of oleic acid, which is an unsaturated fatty acid, rather than general purpose glycerin plasticizer extracted from palm oil which is usually used. Monoester, which is a main material affecting compatibility with PVC The content is as high as 85% by weight or more, and there is no phenomenon that the plasticizer is exuded on the surface of the film during the formation of the wrap film, and there is a stable advantage.
또한 팜핵유로부터 추출한 아세틸화 모노 글리세린은 산 값(acid value)이 1 내지 3 KOH mg/g이고, 비누화 값(saponification value)이 425 내지 450이고, 수산기 값(hydroxyl value)이 10 내지 20, 요오드 값(iodine value)이 10 내지 20인 것이 PVC와의 상용성 확보 및 물성개선에 바람직하다. 본 발명의 아세틸화 모노 글리세린은 팜핵유를 원료로 사용하여 올레일(Oleyl)기의 함량이 높으면서 가소제 내 모노에스테르 함량이 85중량% 이상이며, 옅은 황색 계열의 오일상 에스테르계 글리세린이다. 이러한 아세틸화 모노글리세린 상품으로는 일본 리켄 비타민(Riken Vitamin)사의 바이오사이저(Biocizer)와 같은 제품이 있으며, 본 발명에서 바람직하게 사용될 수 있다.Also, the acetylated monoglycerin extracted from the palm oil channel has an acid value of 1 to 3 KOH mg / g, a saponification value of 425 to 450, a hydroxyl value of 10 to 20, An iodine value of 10 to 20 is preferable for securing compatibility with PVC and improving physical properties. The acetylated monoglycerin of the present invention is palm kernel oil as a raw material and has a high oleyl group content and a monoester content of 85 wt% or more in the plasticizer and is a pale yellow oily ester type glycerin. Examples of such acetylated monoglycerin products include products such as Biocizer from Riken Vitamin Co., Ltd., which can be preferably used in the present invention.
팜핵유에서 추출한 아세틸화 모노글리세린은 랩 필름 조성물 총 100 중량부에 대하여 20 내지 30 중량부로 포함되는 것이 바람직하다. 그 함량이 20 중량부 미만일 경우에는 기존 야자유 기반의 글리세린 가소제와 글리콜계 가소제를 혼용하여 사용한 것에 대비하여 신율 및 부드러움이 우수하지 않을 수 있으며 신율 및 풀림성 등에 있어서 본 발명에서 목적하는 물성을 나타내지 않을 수 있다. 30 중량부를 초과할 경우에는 신율 및 터치감 등은 우수해지나, 랩 필름의 투명성이 양호하지 않고 생산성이 떨어질 수 있다.The acetylated monoglycerin extracted from palm kernel oil is preferably contained in an amount of 20 to 30 parts by weight based on 100 parts by weight of the total amount of the wrap film composition. When the content is less than 20 parts by weight, it may not be excellent in elongation and softness as compared with the conventional coconut oil-based glycerin plasticizer and glycol plasticizer used in combination, and does not exhibit desired physical properties in terms of elongation and releasability . When the content is more than 30 parts by weight, the elongation and touch feeling are excellent, but the transparency of the wrap film is not good and the productivity may be deteriorated.
팜핵유로부터 추출한 아세틸화 모노글리세린은 단독으로 사용하는 것보다는 2차 가소제로 에폭시화 대두유(epoxidized soybean oil, ESO) 및 방담제로 지방산 에스테르 화합물을 함께 사용할 경우 신율, 풀림성 및 부드러움 등의 물성을 더욱 효율적으로 향상시킬 수 있는 효과가 있다. The acetylated monoglycerin extracted from the palm oil channel is used as a secondary plasticizer rather than by itself, but when the epoxidized soybean oil (ESO) and anti-fogging agent are used together with the fatty acid ester compound, the properties such as elongation, There is an effect that it can be efficiently improved.
에폭시화 대두유(ESO)는 분자량이 800 내지 1200이며, 산 값이 0.0001 내지 0.5 KOH mg/g, 요오드 값(Iodine value)이 0.5 내지 3이고, 비중이 0.982 내지 1.002인 것이 열 안정성 및 PVC와의 상용성 측면에서 우수하다. 본 발명에 있어서, 에폭시화 대두유는 가소제의 역할뿐만 아니라 복합 금속계 안정제와 함께 열 안정제의 역할을 동시에 수행한다. 이러한 에폭시화 대두유의 상품으로는 중국소재 장춘석유화학의 O-130 및 한국소재 사조해표의 SDB Cizer E-03 등의 제품이 있으며, 본 발명에서 바람직하게 사용될 수 있다.Epoxidized soybean oil (ESO) has a molecular weight of 800 to 1200, an acid value of 0.0001 to 0.5 KOH mg / g, an iodine value of 0.5 to 3 and a specific gravity of 0.982 to 1.002, It is excellent in terms of sex. In the present invention, the epoxidized soybean oil plays a role of a heat stabilizer together with a composite metal stabilizer as well as a role of a plasticizer. Products of such epoxidized soybean oil include O-130 of Changchun Petrochemical in China and SDB Cizer E-03 of Sajo Haepyo in Korea, and they can be preferably used in the present invention.
에폭시화 대두유는 랩 필름 조성물 총 100 중량부에 대하여 4 내지 10 중량부로 포함되는 것이 바람직하다. 그 함량이 4 중량부 미만일 경우에는 가공시의 열 안정성이 떨어질 가능성이 있으며, 함량이 10 중량부를 초과하는 경우에는 PVC와의 상용성이 저하되어 투명성이 떨어지거나 신율 및 풀림성 등에 있어서 본 발명에서 목적하는 물성이 제대로 나타나지 않을 수 있다.The epoxidized soybean oil is preferably included in an amount of 4 to 10 parts by weight based on 100 parts by weight of the total amount of the wrap film composition. When the content is less than 4 parts by weight, there is a possibility that the thermal stability at the time of processing is lowered. When the content exceeds 10 parts by weight, compatibility with PVC is lowered and the transparency is lowered. May not be properly displayed.
지방산 에스테르 화합물은 방담제로서, 김서림을 방지하여 랩 필름 표면의 투명성을 유지할 수 있게 한다. 본 발명에서는 지방산 에스테르 화합물의 산 값(acid value)이 1 내지 3 KOH mg/g이고, 비누화 값(saponification value)이 140 내지 160이고, 요오드 값(Iodine value)이 30 내지 55이며, 수분 함량이 0 내지 1.5중량%인 것이 바람직하게 사용될 수 있다. 수분함량이 높을 경우, 필름 성형시 기포가 발생할 수 있으며, 산 값이 높다면 특유의 냄새가 나거나 물성에 좋지 않은 영향을 미칠 수도 있다. Fatty acid ester compounds are antifogging agents, which prevent fogging and maintain the transparency of the wrap film surface. In the present invention, the fatty acid ester compound has an acid value of 1 to 3 KOH mg / g, a saponification value of 140 to 160, an iodine value of 30 to 55, 0 to 1.5% by weight can be preferably used. When the moisture content is high, air bubbles may be formed during the film molding, and if the acid value is high, there may be a characteristic odor or a bad influence on the physical properties.
이러한 지방산 에스테르 화합물로는 상술한 물성을 만족하면 특별히 제한되지 않으나, 폴리글리세린 모노올레이트(Polyglycerine Monooleate), 폴리글리세린 모노팔미테이트(Polyglycerine Monopalmitate) 또는 이들의 혼합물이 바람직하게 사용될 수 있다. 지방산 에스테르 화합물 방담제 상품으로는 일본 리켄 비타민(Riken Vitamin)사의 KA-901, KA-904, 한국 CSC의 HK-505, HK507, 한국 일신웰스의 Almax-9280L 등의 제품이 있으며, 본 발명에서 바람직하게 사용될 수 있다.Such fatty acid ester compounds are not particularly limited as long as the above-mentioned physical properties are satisfied, but polyglycerine monooleate, polyglycerine monopalmitate or a mixture thereof can be preferably used. Examples of fatty acid ester compound anti-fogging agents include KA-901 and KA-904 of Riken Vitamin, HK-505 and HK507 of Korea CSC, and Almax-9280L of Korea Ilshin Wells. Lt; / RTI >
지방산 에스테르 화합물은 랩 필름 조성물 총 100 중량부에 대하여 0.5 내지 5 중량부로 포함되는 것이 바람직하다. 그 함량이 0.5 중량부 미만일 경우에는 기본적인 성능인 방담성이 크게 떨어질 수 있으며, 5 중량부를 초과할 경우에는 방담성은 우수해지나, 랩 필름 표면에 방담제가 지속적으로 배어나서 투명성이 현저하게 떨어질 수 있다.The fatty acid ester compound is preferably contained in an amount of 0.5 to 5 parts by weight based on 100 parts by weight of the total amount of the wrap film composition. If the content is less than 0.5 parts by weight, the antifogging property as a basic performance may be significantly deteriorated. If the content is more than 5 parts by weight, the antifogging property is excellent, but the antifogging agent may continuously infiltrate on the surface of the wrap film, .
열 안정제는 바륨-아연계, 칼슘-아연계 조성물 등을 사용할 수 있으나, 식품 포장용으로 인체에 무독한 조건을 충족시키기 위해서는 칼슘-아연계 조성물을 사용하는 것이 좀 더 바람직하다. 칼슘-아연계 조성물은 칼슘 지방산염, 아연 지방산염, 디하이드로 아세트산(dehydroacetic acid), 에폭시화 대두유, 리시놀산(ricinolic acid), 노르말-파라핀(n-paraffin)(CH3(CH2) n CH3(n=11))을 포함한다. 더 바람직하게는 칼슘-아연계 조성물에 2,6-디-터셔리-부틸-파라-크레졸(2,6-di-tert-butyl-para-cresol)이 첨가한 것을 사용하는 것으로, 경시에 따른 투명성 저하를 방지할 수 있다. 2,6-디-터셔리-부틸-파라-크레졸(2,6-di-tert-butyl-para-cresol)은 칼슘-아연계 화합물에 대하여 0.5 내지 5 중량부의 소량이 함유되면, 경시에 따른 랩 필름의 투명성 저하를 방지할 수 있다. 칼슘-아연계 조성물은 비중이 0.900 내지 0.960이며, 점도가 1 내지 100 cps 이하인 것이 성형 가공시의 부하가 적고 상용성이 좋은 특징이 있다. 이러한 열 안정제의 상품으로는 ㈜한국대협에서 제조, 판매되고 있는 LTX-630P와 우창실업의 KCZ-03 제품이 있으며, 본 발명에서 바람직하게 사용될 수 있다.The thermal stabilizer may be a barium-zinc or a calcium-zinc-based composition, but it is more preferable to use a calcium-zinc-based composition for food packaging in order to satisfy human health. Calcium-zinc-based composition is calcium fatty acid salt, zinc fatty acid salts, dihydro acetic acid (dehydroacetic acid), epoxidized soybean oil, ricinoleic acid (ricinolic acid), n-paraffin (n-paraffin) (CH 3 (CH 2) n CH 3 (n = 11)). It is more preferable to use 2,6-di-tert-butyl-para-cresol added to the calcium-zinc-based composition, And deterioration of transparency can be prevented. When 2,6-di-tert-butyl-para-cresol is contained in a small amount of 0.5 to 5 parts by weight based on the calcium-zinc compound, the 2,6-di- The transparency of the wrap film can be prevented from deteriorating. The calcium-zinc-based composition has a specific gravity of 0.900 to 0.960 and a viscosity of 1 to 100 cps or less. Examples of such heat stabilizers include LTX-630P, which is manufactured and sold by Daehan KOREA, and KCZ-03, Woochang Industrial Co., Ltd., and can be preferably used in the present invention.
열 안정제는 랩 필름 조성물 총 100 중량부에 대하여 0.5 내지 5 중량부로 사용하는 것이 좋다. 그 함량이 0.5 중량부 미만일 경우에는 압출기 내부에서 필름 성형시 필름이 탄화될 수 있고, 가공 안정성이 확보되지 않을 가능성이 높으며, 5 중량부를 초과하여 사용하는 경우에는 열 안정제 자체의 활성이 높아 랩 필름 내부로 열 안정제가 배어나서 투명성이 저하될 수 있다.The heat stabilizer is preferably used in an amount of 0.5 to 5 parts by weight based on 100 parts by weight of the total amount of the wrap film composition. When the content is less than 0.5 part by weight, the film may be carbonized during film forming in the extruder, and there is a high possibility that the processing stability is not ensured. When the content is more than 5 parts by weight, the activity of the heat stabilizer itself is high, The heat stabilizer may penetrate into the inside and the transparency may be lowered.
본 발명은 또한 상술한 바와 같은 염화비닐수지 랩 필름 조성물을 사용하여, 각종 과일, 야채, 배달음식, 생육 등의 식품 포장을 위한 랩 필름을 제공할 수 있다. 랩 필름은 본 발명에 따른 염화비닐수지 랩 필름 조성물을 압출하여 필름을 성형하는 방법, 구체적으로 T-다이 익스트루더법(T-die Extruder)으로 제조될 수 있다. 본 발명에 따른 염화비닐수지 랩은 두께가 9 내지 15 ㎛로, 신율 및 풀림성에서 개선이 이루어져 매우 얇게도 성형 가능하며, 식품 포장용으로 적합하며, 풀림성 및 신율이 우수하다.
The present invention can also provide a wrap film for food packaging such as various fruits, vegetables, delivery foods, growing, etc., using the above-described vinyl chloride resin wrap film composition. The wrap film can be produced by a method of extruding a vinyl chloride resin wrap film composition according to the present invention to form a film, specifically, a T-die extruder. The vinyl chloride resin wraps according to the present invention have a thickness of 9 to 15 占 퐉 and are improved in elongation and releasability so that they can be formed very thinly and are suitable for food packaging and have excellent releasability and elongation.
이하, 본 발명의 이해를 돕기 위해 실시예를 들어 본 발명을 상세하게 설명한다. 그러나, 하기 실시예들은 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 하기 실시예들에 한정되는 것으로 해석되어서는 안 된다. 본 발명의 실시예는 이 기술분야에서 통상의 지식을 가진 자에게 본 발명을 보다 자세하게 설명하기 위해 제공되는 것이다.
BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in detail by way of examples to facilitate understanding of the present invention. However, the following examples can be modified in various other forms, and the scope of the present invention should not be construed as being limited to the following examples. The embodiments of the present invention are provided to explain the present invention to a person having ordinary skill in the art in more detail.
실시예Example
염화비닐수지 랩 필름을, 하기 표 1에 나타낸 바와 같은 성분 및 함량의 PVC 랩 필름 조성물을 사용하여, T-다이 익스트루더(T-die Extruder)를 이용하여 일반적인 랩 필름의 두께인 13㎛의 두께로 제조하였다. 제조된 랩 필름의 물성을 평가하고 그 결과를 표 2에 나타내었다. A polyvinyl chloride resin wrap film was laminated using a T-die extruder using a component and a content of a PVC wrap film composition as shown in the following Table 1, Thick. The physical properties of the produced wrap film were evaluated, and the results are shown in Table 2.
이때, 중중합도 PVC 수지로 LG화학의 PVC수지 제품 LS 100S, 1차 가소제로 팜핵유에서 추출한 아세틸화 모노글리세린 가소제로 리켄 비타민사(Riken Vitamin)의 바이오사이저(Biocizer), 2차 가소제로 에폭시화 대두유(ESO)(제품명 알려주세요), 방담제로 폴리글리세린 모노올레이트(Poly Glycerine Monooleate, PGMO)를 주요 원료로 사용한 복합 지방산 에스테르 계통의 방담제인 일신웰스의 Almax-9280L을 사용하였으며, 열 안정제로 칼슘 지방산염과 아연 지방산염으로 이루어진 케이디켐의 LTX-630P를 사용하였다.At this time, the resin of medium polymerization degree PVC resin LS 100S of LG Chemical, the biocide of Riken Vitamin (acetylated monoglycerin plasticizer) extracted from palm kernel oil as the primary plasticizer, the epoxy resin Almax-9280L of Ilshinweels, a complex fatty acid ester-based anti-fogging agent using polyglycerol monooleate (PGMO) as an anti-fogging agent, was used as a heat stabilizer. LTX-630P of K-DECEM, made of calcium fatty acid salt and zinc fatty acid salt, was used.
(중량부)Example
(Parts by weight)
(팜핵유 추출
아세틸화 모노글리세린)Primary plasticizer
(Palm kernel oil extraction
Acetylated monoglycerin)
(야자유 추출
아세틸화 모노글리세린)Primary plasticizer
(Palm oil extraction
Acetylated monoglycerin)
(디에틸렌 글리콜/트리에틸렌 글리콜 혼합 가소제)Primary plasticizer
(Diethylene glycol / triethylene glycol mixed plasticizer)
(에폭시화 대두유)Secondary plasticizer
(Epoxidized soybean oil)
(케이디켐, LTX-630P)Heat stabilizer
(K-DECEM, LTX-630P)
(복합 지방산 에스테르, Almax-9280L)Antifog agent
(Complex fatty acid ester, Almax-9280L)
비교예Comparative Example 1 One
상기 표 1에 나타낸 바와 같이, 1차 가소제로 야자유에서 추출한 아세틸화 모노글리세린 가소제를 전량 사용하였으며, 그 이외의 것은 실시예에 따라서 랩 필름을 제조하였다. 제조된 랩 필름의 물성을 평가하고 그 결과를 표 2에 나타내었다.
As shown in Table 1, the entire amount of the acetylated monoglycerin plasticizer extracted from palm oil was used as the primary plasticizer, and a wrap film was produced according to the examples except for the above. The physical properties of the produced wrap film were evaluated, and the results are shown in Table 2.
비교예Comparative Example 2 2
상기 표 1에 나타낸 바와 같이, 1차 가소제로 디에틸렌 글리콜과 트리 에틸렌 글리콜을 혼합한 가소제를 전량 사용하였으며, 실시예에 따라서 랩 필름을 제조하였다. 제조된 랩 필름의 물성을 평가하고 그 결과를 표 2에 나타내었다.
As shown in Table 1, a total amount of a plasticizer in which diethylene glycol and triethylene glycol were mixed as a primary plasticizer was used, and a wrap film was produced according to the examples. The physical properties of the produced wrap film were evaluated, and the results are shown in Table 2.
평가예Evaluation example
실시예 및 비교예에 따라서 제조된 랩 필름에 대하여 아래와 같은 방법으로 물성을 측정하였으며, 그 결과를 하기 표 2에 종합하여 나타내었다.
The properties of the wrap films prepared according to Examples and Comparative Examples were measured in the following manner, and the results are summarized in Table 2 below.
인장강도The tensile strength // 인열강도Phosphorus strength
만능 재료 시험기(UTM)를 이용하여 랩 필름에 대한 인장/인열 강도를 측정하였다. 하기 표 2에서 인장강도는 높을수록 필름이 끊어질 때의 최대강도가 높다는 것을 의미하며, 인열강도는 높을수록 필름 자체의 찢어짐에 대한 저항성이 우수함을 나타낸다.
The tensile / tear strength of the wrap film was measured using a universal material testing machine (UTM). In Table 2, the higher the tensile strength, the higher the maximum strength at breaking of the film, and the higher the tear strength, the better the film itself is resistant to tearing.
점착력 및 Adhesion and 풀림성Loose property
만능 재료 시험기(UTM)를 이용하여 랩 필름에 대한 풀림성을 측정하였으며, 점착력은 필름 2개를 180mm ×100mm 크기로 각각 취하여 필름끼리 접촉할 시에 점착력 정도가 양호한 경우에 5점, 비슷한 경우 3점, 열악한 경우에 1점을 부여하였다. 하기 표2에서 점착력은 클수록, 풀림성은 작을수록 잘 풀림을 의미한다.
The peelability of the wrap film was measured using a universal material tester (UTM). The adhesion was measured as 180 mm × 100 mm in two films. The adhesion was evaluated as 5 points when adhesion was good, and 3 cases And 1 point in the case of poor. In Table 2, the larger the cohesive force and the smaller the releasability, the better the releasing.
투명도transparency
투명도는 헤이즈미터(Hazemeter)를 이용하여 측정하였으며, 하기 표 2에서 헤이즈미터 측정값이 작을수록 투명도가 우수함을 나타낸다.
The transparency was measured using a hazemeter. The smaller the haze meter value in Table 2, the better the transparency.
신율Elongation
신율은 만능 재료 시험기(UTM)를 이용하여 측정하였으며, 값이 높을수록 신율이 우수하고 필름이 잘 늘어남을 나타낸다.
The elongation was measured using a universal testing machine (UTM). The higher the value, the better the elongation and the better the film is stretched.
경시안정성Stability over time
경시안정성은 45℃ 항온기에서 5일 이상 경시하였을 때, 랩 필름 표면으로 가소제 등의 첨가제가 배어나는 현상)이 발생하는지 사이드 컷팅면에 단차가 생기지 않고 안정적인지를 나타낸다.Stability with respect to time is a stable phenomenon, such as a phenomenon in which additives such as a plasticizer are introduced into the surface of the wrap film when the temperature is lowered by more than 5 days in a 45 ° C thermostat) or no side step is formed on the side cutting surface.
상기 표 2에 나타낸 바와 같이, 본 발명의 실시예에 따른 랩 필름은 비교예 1에 비하여 점착력이 우수하게 나타났으며, 비교예 2에 비해서도 크게 떨어지지 않는 점착력을 나타냈다. 특히 실시예는 풀림성 및 신율 등은 가장 우수하며 외관 품질이 뛰어났다. 또한 부드러움성 및 터치감이 향상되었고, 특히 MD방향의 인장강도가 개선되어 사용자들이 랩 필름을 사용할 때 적은 힘으로도 용이하게 랩 필름을 풀어 사용할 수 있게 되었다. 비교예 1 및 2의 랩 필름에 대비하여 실시예의 랩 필름의 기계적 물성은 전체적으로 향상되면서, 경시안정성은 우수하여 글리세린 가소제를 다량 처방할 때 나타나는 블리딩 현상도 발생하지 않았다.As shown in Table 2, the wrap film according to the example of the present invention exhibited excellent adhesive strength as compared with Comparative Example 1, and exhibited an adhesive strength that was not much lower than Comparative Example 2. Particularly, the examples were excellent in peelability and elongation and excellent in appearance quality. In addition, the softness and touch feeling are improved, and in particular, the tensile strength in the MD direction is improved, so that when the user uses the wrap film, the wrap film can be easily loosened with less force. Compared to the wrap films of Comparative Examples 1 and 2, the mechanical properties of the wrap film of the Examples were improved as a whole, and the stability with time was excellent, so that no bleeding phenomenon occurred when a large amount of glycerin plasticizer was prescribed.
Claims (10)
팜핵유로부터 추출한 모노에스테르(Monoester)의 함량이 85중량% 이상인 아세틸화 모노글리세린 20 내지 30 중량부;
에폭시화대두유 4 내지 10 중량부;
폴리글리세린 모노올레이트(Polyglycerine Monooleate), 폴리글리세린 모노팔미테이트(Polyglycerine Monopalmitate) 또는 이들의 혼합물인 지방산 에스테르 화합물 0.5 내지 5중량부; 및
열 안정제 0.5 내지 5 중량부를 포함하는 염화비닐수지 랩 필름 조성물.
50 to 75 parts by weight of a vinyl chloride resin having a degree of polymerization of 950 to 1050;
20 to 30 parts by weight of acetylated monoglycerin having a monoester content of 85% by weight or more extracted from the palm oil channel;
4 to 10 parts by weight of epoxidized soybean oil;
0.5 to 5 parts by weight of a fatty acid ester compound which is polyglycerine monooleate, polyglycerine monopalmitate or a mixture thereof; And
And 0.5 to 5 parts by weight of a heat stabilizer.
상기 팜핵유로부터 추출한 아세틸화 모노글리세린은 산 값(acid value) 1 내지 3 KOH mg/g, 비누화 값(saponification value) 425 내지 450, 수산기 값(hydroxyl value) 10 내지 20, 및 요오드 값(Iodine value) 10 내지 20인 것을 특징으로 하는 랩 필름 조성물.
The method according to claim 1,
The acetylated monoglycerin extracted from the palm kernel channel has an acid value of 1 to 3 KOH mg / g, a saponification value of 425 to 450, a hydroxyl value of 10 to 20, and an iodine value Lt; RTI ID = 0.0 > 10-20. ≪ / RTI >
상기 염화비닐수지는 겉보기 비중이 0.50 내지 0.58 g/cm3 인 것을 특징으로 하는 랩 필름 조성물.
The method according to claim 1,
Wherein the vinyl chloride resin has an apparent specific gravity of 0.50 to 0.58 g / cm < 3 & gt ;.
상기 에폭시화 대두유는 비중 0.982 내지 1.002, 산 값 0.0001 내지 0.5 KOH mg/g, 분자량 800 내지 1200, 및 요오드 값 0.5 내지 3인 것을 특징으로 하는 랩 필름 조성물.
The method according to claim 1,
Wherein the epoxidized soybean oil has a specific gravity of 0.982 to 1.002, an acid value of 0.0001 to 0.5 KOH mg / g, a molecular weight of 800 to 1200, and an iodine value of 0.5 to 3.
상기 지방산 에스테르 화합물은 산 값 1 내지 3 KOH mg/g, 요오드 값 30 내지 55, 비누화 값(saponification value) 140 내지 160이며, 수분 함량은 수분을 포함하지 않거나 1.5 중량% 이하인 것을 특징으로 하는 랩 필름 조성물.
The method according to claim 1,
Wherein the fatty acid ester compound has an acid value of 1 to 3 KOH mg / g, an iodine value of 30 to 55, a saponification value of 140 to 160, and a moisture content of no more than 1.5% Composition.
상기 열 안정제는 칼슘 지방산염, 아연 지방산염, 디하이드로 아세트산(dehydroacetic acid), 에폭시화 대두유, 리시놀산(ricinolic acid), 및 노르말-파라핀(n-paraffin)(CH3(CH2) n CH3(n=11))으로 이루어지는 칼슘-아연계 조성물에 2,6-디-터셔리-부틸-파라-크레졸(2,6-Di-tert-butyl-P-Cresol)이 첨가된 것으로, 비중이 0.900 내지 0.960이며 점도가 1 내지 100 cps인 것을 특징으로 하는 랩 필름 조성물.
The method according to claim 1,
The heat stabilizer may be selected from the group consisting of calcium fatty acid salts, zinc fatty acid salts, dehydroacetic acid, epoxidized soybean oil, ricinolic acid, and n-paraffin (CH 3 (CH 2 ) n CH 3 2,6-di-tert-butyl-P-cresol was added to a calcium-zinc based composition comprising a mixture of n-butanol and n-butanol (n = 0.900 to 0.960 and a viscosity of 1 to 100 cps.