KR101473158B1 - Lacquer applied sheets manufacturing method - Google Patents

Lacquer applied sheets manufacturing method Download PDF

Info

Publication number
KR101473158B1
KR101473158B1 KR1020140128918A KR20140128918A KR101473158B1 KR 101473158 B1 KR101473158 B1 KR 101473158B1 KR 1020140128918 A KR1020140128918 A KR 1020140128918A KR 20140128918 A KR20140128918 A KR 20140128918A KR 101473158 B1 KR101473158 B1 KR 101473158B1
Authority
KR
South Korea
Prior art keywords
lacquer
layer
opaque
transparent
reinforcing
Prior art date
Application number
KR1020140128918A
Other languages
Korean (ko)
Inventor
전종선
Original Assignee
전종선
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 전종선 filed Critical 전종선
Priority to KR1020140128918A priority Critical patent/KR101473158B1/en
Application granted granted Critical
Publication of KR101473158B1 publication Critical patent/KR101473158B1/en

Abstract

The present invention provides a method for manufacturing a paperboard with a lacquer applied pattern, the method being characterized by comprising: drying a pattern frame plate having a surface unevenness after thinly applying transparent lacquer; drying after thinly re-applying opaque lacquer; installing a reinforcing layer formed of aqueous adhesive; applying adhesive to the reinforcing layer; attaching a reinforcing paperboard; and taking off from the pattern frame plate. Thus clothes, bags or the like can be manufactured by attaching the lacquer pattern paperboards to a backing cloth, leather or the like.

Description

옻칠 문양 판지의 제조 방법{Lacquer applied sheets manufacturing method} {Lacquer applied sheets manufacturing method}

본 발명은 가방이나 구두를 제조하기 위한 가죽판, 겉옷을 만들기 위한 옷감, 모자나 장갑을 만들기 위한 포지 등으로 두루 사용할 수 있게 하는 판지에 관한 것으로 특히, 요철 모양이 형성된 옻칠 문양을 가지는 판지와 그 제조 방법을 제공하기 위한 것이다.The present invention relates to a cardboard which can be used as a leather plate for manufacturing a bag or a shoe, a cloth for making a jacket, a forge for making a hat or gloves and the like, and more particularly to a cardboard having a lacquer pattern And a method for manufacturing the same.

옻칠은 옻나무에서 채취한 생옻칠과 이를 가공한 것으로 진한 검은 색을 띄는 흑칠 및 붉은 색의 주합이 있는 바, 이러한 옻칠은 주로 가구의 칠 재료로 사용되어 왔다. 옻칠은 내염성, 내열성, 방수성, 방부성, 방충성 및 절연성이 우수할 뿐 아니라 그 광택이 고와서 고품위 가구용 칠 재료로 사용되어 왔으나, 굳은 후의 경도가 커서 깨지기 쉬우므로 구부러지는 가죽이나 천과 같은 판지에의 코팅재로 사용되기에는 적합하지 못한 결점이 있다.Lacquer is a raw lacquer sampled from lacquer and processed with it. The lacquer has been used mainly as a lacquer for furniture since it has dark blackish black and red colored lacquer. Lacquer has excellent resistance to salt, heat, waterproof, antiseptic, insecticide and insulation, and has been used as a high-quality material for furniture since its luster is high. However, since it has a hardness after hardening, it is fragile. It is not suitable for use as a coating material.

특허제100334293호는, 옻(Lacquer) 성분을, 상용화되어 있는 기존의 합성수지, 특히 폴리에틸렌에 혼합한(blending) 기능성 합성수지 및 그 제조 방법을 개시하고 있다. 그러나, 이는 옻 성분과 합성수지를 혼합한 것일 뿐이어서, 판지에의 칠재료로 사용될 수는 없었다. 결국, 과거에는 마른 상태에서의 경도가 큰 옻칠을 어떠한 형태로던 포지 등의 구부러지는 판지 표면에 피복시킬 수는 없었던 것이다.Patent No. 100334293 discloses a functional synthetic resin blending a conventional lacquer component with a conventional synthetic resin, particularly polyethylene, and a method for producing the same. However, this was a mixture of lacquer and synthetic resin, so it could not be used as a primer for cardboard. As a result, in the past, lacquer having a large hardness in a dry state could not be coated on the surface of a curled cardboard such as porcelain in any form.

이에 본 발명자는 가방이나 구두를 제조하기 위한 가죽판, 겉옷을 만들기 위한 옷감, 모자나 장갑을 만들기 위한 포지 등으로 두루 사용할 수 있게 하는 판지를 제공함에 있어서, 옻칠로 표면 처리된 판지를 제공하게 함으로서 고 품위의 판지를 제공하여야 한다는 과제를 해결하고자 한다. 나아가, 본 발명은 위와 같은 판지의 옻칠 표면이 요철 및 농담(濃淡; 진하고 옅음)의 문양을 가지는 판지를 제공하여야 한다는 과제를 해결하고자 한다. Accordingly, the present inventors have found that it is possible to provide a cardboard which can be used as a leather plate for manufacturing a bag or a shoe, a cloth for making a jacket, a forge for making a hat or gloves, etc., And to provide a high quality paperboard. Further, the present invention aims to provide a cardboard in which the lacquer surface of the above-mentioned cardboard has a pattern of concave and convex and dark and light.

위와 같은 과제를 해결하기 위하여, 본 발명은, 표면에 0.3~1mm의 높이차를 가지는 요철부를 가지는 문양틀판을 마련하는 문양틀판 마련단계와, 테레핀유에 희석된 옻칠을 마련하되 옅은색 투명 옻칠과 불투명한 옻칠의 두가지 옻칠을 마련하는 옻칠단계와, 상기 문양틀판에 상기 투명 옻칠을 0.05~0.1mm 바람직하게는 0.07mm의 두께로 피복시키는 투명 옻칠 도포단계와, 상기 투명 옻칠을 습도 60~80% 온도 섭씨25도의 조건에서 12~36시간, 바람직하게는 24시간 건조시키어 투명 옻칠층을 형성시키는 투명 옻칠 건조 단계와, 건조된 투명 옻칠층 위에 불투명인 옻칠을 0.05~0.1mm 바람직하게는 0.07mm 두께로 도포하는 불투명 옻칠 도포 단계와, 도포된 불투명 옻칠층을 습도 60~80% 온도 섭씨 25도의 조건에서 12~36시간 바람직하게는 24시간 건조시키는 불투명 옻칠층 건조단계와, 불투명 옻칠층 위에, 불투명 옻칠층의 표면에 문양틀판의 요철에 대응하여 형성된 요철 중 높은 봉우리 위로 0.05~0.5mm 바람직하게는 0.2mm 높도록 또, 불투명 옻칠층의 모든 요철의 위 보강층 표면부가 평평하도록, 보강층을 설치하는 보강층 설치단계와, 상기 보강층에 접착제를 도포하고 보강판지를 부착하는 보강판지 설치 단계와, 상기 문양틀판으로부터 투명 옻칠층과 불투명 옻칠층과 보강층과 보강판 및 보강판지로 되는 옻칠 문양 판지를 분리하는 문양틀판 분리 단계로 구성되는 옻칠 문양 판지의 제조 방법을 제공한다. According to an aspect of the present invention, there is provided a method for manufacturing a lacquer, comprising the steps of: providing a pattern plate having a surface having a concavo-convex portion having a height difference of 0.3 to 1 mm; A transparent lacquer coating step in which the transparent lacquer is coated to a thickness of 0.05 to 0.1 mm, preferably 0.07 mm; and a transparent lacquer coating step in which the transparent lacquer is coated with a transparent lacquer having a humidity of 60 to 80% A transparent lacquer layer is formed by drying at a temperature of 25 DEG C for 12 to 36 hours, preferably 24 hours, to form a transparent lacquer layer; and a step of lacquer opaque on the dried transparent lacquer layer in a thickness of 0.05 to 0.1 mm, preferably 0.07 mm And an opaque lacquer layer is applied to the opaque lacquer layer to dry the opaque lacquer layer at a temperature of 60 to 80% at a temperature of 25 DEG C for 12 to 36 hours, preferably 24 hours On the opaque lacquer layer, on the surface of the opaque lacquer layer, 0.05 to 0.5 mm, preferably 0.2 mm above the high peak of the unevenness formed in correspondence to the concave and the convex of the pattern plate, A step of installing a reinforcing layer for providing a reinforcing layer so that the reinforcing layer is attached to the reinforcing layer, a step of installing a reinforcing layer for installing the reinforcing layer, a step of applying a glue to the reinforcing layer and attaching a reinforcing cardboard, A step of separating the lacquer pattern paper from the lacquer pattern cardboard.

위와 같은 본 발명은, 가죽이나 포지와 같은 판지에, 문양틀판에 새겨진 문양에 따르는 문양을 가지는 옻칠층을 형성시킬 수 있으며, 이러한 옻칠층은, 일반적인 옻칠층이 구부러지면 쉽게 부러져 깨지는 것과 달리, 쉽게 굴신하여, 상기 옻칠층을 구비한 판지는 이를 가방이나 구두의 소재로 적절히 사용할 수 있으며, 특히, 그 표면의 광택이 고와 가구에 접합하는 경우 품격 높은 가구가 제공된다. According to the present invention as described above, it is possible to form a lacquer layer having a pattern according to a pattern engraved on a pattern plate on a cardboard such as a leather or a forge. Such a lacquer layer is easily broken when a general lacquer layer is bent, The cardboard having the lacquer layer can be suitably used as a material for a bag or a shoe. Especially, when the surface of the cardboard has a glossy surface, it is furnished with high quality furniture.

본 발명은, 표면에 0.3~1mm의 높이차를 가지는 요철부를 가지는 문양틀판을 마련하는 문양틀판 마련단계와, 테레핀유에 희석된 옻칠을 마련하되 옅은색 투명 옻칠과 불투명한 옻칠의 두가지 옻칠을 마련하는 옻칠단계와, 상기 문양틀판에 상기 투명 옻칠을 0.05~0.1mm 바람직하게는 0.07mm의 두께로 피복시키는 투명 옻칠 도포단계와, 상기 투명 옻칠을 습도 60~80% 온도 섭씨25도의 조건에서 12~36시간, 바람직하게는 24시간 건조시키어 투명 옻칠층을 형성시키는 투명 옻칠 건조 단계와, 건조된 투명 옻칠층 위에 불투명인 옻칠을 0.05~0.1mm 바람직하게는 0.07mm 두께로 도포하는 불투명 옻칠 도포 단계와, 도포된 불투명 옻칠층을 습도 60~80% 온도 섭씨25도의 조건에서 12~36시간 바람직하게는 24시간 건조시키는 불투명 옻칠층 건조단계와, 불투명 옻칠층의 표면에 문양틀판의 요철에 대응하여 형성된 요철 중 높은 봉우리 위로 0.05~0.5mm 바람직하게는 0.2mm 높도록 또, 불투명 옻칠층의 모든 요철의 위 보강층 표면부가 평평하도록, 보강층을 설치하는 보강층 설치단계와, 상기 보강층에 접착제를 도포하고 보강판지를 부착하는 보강판지 설치 단계와, 상기 문양틀판으로부터 투명 옻칠층과 불투명 옻칠층과 보강층과 보강판 및 보강판지로 되는 옻칠 문양 판지를 분리하는 문양틀판 분리 단계로 구성되는 옻칠 문양 판지의 제조 방법을 제공한다.The present invention relates to a method for manufacturing a lacquer, comprising the steps of providing a pattern plate having a surface having a concavo-convex portion having a height difference of 0.3 to 1 mm, and lacquer diluted in terpinene oil, wherein the lacquer is made of light transparent lacquer and opaque lacquer A transparent lacquer coating step of coating the transparent lacquer with a thickness of 0.05 to 0.1 mm, preferably 0.07 mm, on the patterned plate, and applying the transparent lacquer to the transparent lacquer at a temperature of 25 to 120 deg. C under a humidity of 60 to 80% Drying the transparent lacquer layer to form a transparent lacquer layer by drying the transparent lacquer layer for 36 hours, preferably 24 hours, and applying opaque lacquer on the dried transparent lacquer layer in a thickness of 0.05 to 0.1 mm, preferably 0.07 mm, , Drying the opaque lacquer layer on the surface of the opaque lacquer layer by drying the applied opaque lacquer layer under the conditions of 60 to 80% humidity and 25 DEG C for 12 to 36 hours, preferably 24 hours; A reinforcing layer providing step of providing a reinforcing layer such that the surface of the reinforcing layer above all the concavities and convexities of the opaque lacquer layer is flat so that it is 0.05 to 0.5 mm, preferably 0.2 mm higher than the high peak of the concavities and convexities formed in correspondence to the concavities and convexities of the plate, Separating the transparent lacquer layer, the opaque lacquer layer, the reinforcing layer, the reinforcing plate, and the lacquer cardboard made of the reinforcing cardboard from the patterned plate, A method for manufacturing a lacquered cardboard is provided.

상기 문양틀판 마련단계에서의 문양틀판은 알루미늄 호일(Foil)로 제조 될 수 있다. 그러나 알루미늄 호일로 제조될 경우, 알루미늄 호일로부터 옻칠 문양판지를 분리할 때 문양틀판이 파손되어 재사용이 불가능한 결점이 있다. 그리고 문양틀판을 스테인레스스틸과 같은 금속으로 형성시킬 경우 내구성은 우수하나 문양틀판으로부터 옻칠 문양 판지를 분리하기가 용이하지 아니하므로, 박리 용이성을 위하여 문양틀판에 수성 이형제를 도포한 후 옻칠을 도포함이 바람직하다. 수성 이형제를 도포할 경우, 그 위에 도포되는 옻칠이 고르게 펴지도록 이형제는 건조되는 것이 바람직하다. 그러나, 상기의 문양틀판은 표면 점착력이 약한 연질의 합성수지로 제조되는 것이 더욱 바람직하다. 상기의 문양틀판을 제조하기 위한 연질의 합성수지는 라텍스, 연질 에폭시, 연질의 폴리우레탄, 실리콘 등으로부터 선택될 수 있다. The pattern plate in the step of preparing the pattern plate may be made of aluminum foil. However, when it is made of aluminum foil, there is a drawback that when the lacquer pattern paperboard is detached from the aluminum foil, the pattern plate is damaged and reusable. However, since it is not easy to separate the lacquered cardboard from the pattern plate, it is coated with a water-based releasing agent on the pattern plate for easy peeling, and then coated with lacquer desirable. When the aqueous release agent is applied, the release agent is preferably dried so that the lacquer applied thereon is evenly spread. However, it is more preferable that the above-mentioned pattern plate is made of a soft synthetic resin having a weak surface adhesion. The soft synthetic resin for making the above-mentioned patterned plate may be selected from latex, soft epoxy, flexible polyurethane, silicone and the like.

옅은색 투명 옻칠은 옅은색 투명 옻칠 1중량부에 테레핀유 0.5~1.5중량부를 혼합하여 유동성을 높인다. 일반적인 옻칠에 있어서는 옻칠에 혼합하는 테레핀유와 옻칠의 혼합비가 옻칠1: 테레핀유0.3~0.4(중량부)인 것이 보통이나 본 발명에 있어서는 옻칠의 유동성을 향상시켜 문양틀판의 미세 요철부에 이르기까지 옻칠이 충전되도록 테레핀유의 함량을 높였다. Light colored transparent lacquer is prepared by mixing 0.5 to 1.5 parts by weight of terpine oil with 1 part by weight of light transparent lacquer to improve fluidity. In general lacquering, it is common that the mixture ratio of lacquer and lacquer mixed in lacquer is lacquer 1: 0.3 to 0.4 (parts by weight). However, in the present invention, since the fluidity of lacquer is improved, The content of terfenin oil was increased so that lacquer was filled.

불투명 옻칠층 위에 형성시키는 상기 보강층은 옻칠층의 강성을 보강할 뿐 아니라 투명 옻칠층의 외면에 형성되는 요철이 일그러지지 아니하도록 요철 상태를 보호한다. 보강층의 표면을 평탄하게 하는 이유이다. 이러한 보강층을 형성시키는 물질은 수성 접착제인 것이 바람직하다. 보강층의 두께는 0.05~1.5mm인 것이 바람직하다. 굴신이 용이하여 부드러운 감촉을 제공하게 하기 위함이다. 그러나, 불투명 옻칠층의 표면에 문양틀판의 요철에 대응하여 형성된 요철 중 높은 봉우리 위로 0.2mm 이상 보강층을 형성시키므로서 강성을 보강할 수 있다. 보강층을 형성시키기 위해 불투명 옻칠층 위에 수성접착제를 도포하는 경우, 도포되는 풀의 두께에 따라 차이가 있을 수 있으나, 적어도 2시간 이상의 건조 공정이 필요하다. The reinforcing layer formed on the opaque lacquer layer not only reinforces the rigidity of the lacquer layer but also protects the unevenness state so that irregularities formed on the outer surface of the transparent lacquer layer are not distorted. This is why the surface of the reinforcing layer is made flat. The material forming such a reinforcing layer is preferably an aqueous adhesive. The thickness of the reinforcing layer is preferably 0.05 to 1.5 mm. So that it is easy to bend and provide soft touch. However, rigidity can be reinforced by forming a reinforcing layer of 0.2 mm or more on a high peak of the unevenness formed on the surface of the opaque lacquer layer in correspondence to the concavity and convexity of the pattern plate. When an aqueous adhesive is applied on the opaque lacquer layer to form a reinforcing layer, there is a difference depending on the thickness of the applied paste, but a drying process of at least 2 hours is required.

보강층 위에 설치되는 보강판지는 얇은 천이나 종이인 것이 바람직하다. The reinforcing cardboard provided on the reinforcing layer is preferably a thin cloth or paper.

위와 같은 본 발명의 방법으로 제조된 옻칠 문양 판지는, 옻칠 자체가 7% 이상의 고무성분을 포함하고 있어 어느 정도 유연성을 가지는데다가, 옻칠의 두께가 워낙 얇고 접착제로 되는 보강층으로 인하여 굴신이 가능하며, 표면의 투명 옻칠층은 요철로 인하여 입체적인 문양을 제공하고, 그러한 문양은 그 이면의 불투명 옻칠층으로 인하여 두드러진 모양으로 표현되게 하고, 특히, 이면의 보강층은 표면의 투명 옻칠층이 가지는 요철 상태가 일그러지지 아니하게 보호하여 옻칠층의 우수한 질감과 옻칠층에 형성된 요철 문양으로 고 품위의 판지를 제공하게 된다. The lacquer-coated cardboard produced by the method of the present invention as described above has flexibility to some extent because the lacquer itself contains 7% or more of rubber components, and the lacquer can be bent due to the thin layer of the lacquer being made of an adhesive, The transparent lacquer layer on the surface provides a three-dimensional pattern due to the unevenness, and such a pattern is expressed in a prominent shape due to the opaque lacquer layer on the back surface. Particularly, in the reinforcing layer on the back surface, The lacquer layer protects the lacquer layer and provides a high-quality cardboard with a good texture of the lacquer layer and a relief pattern formed on the lacquer layer.

그리고 상기 보강판지는 문양틀판으로부터 옻칠 문양 판지를 분리할 때, 또 보관과 운반 시의 옻칠 문양 판지의 손상을 방지하게 된다. The reinforced cardboard prevents damage to the lacquered cardboard when separating the lacquered cardboard from the pattern plate and also during storage and transportation.

이러한 본 발명의 옻칠 문양 판지는 이를 가죽에 접합하여 가방, 신발 등의 소재로 사용할 수 있으며, 포지에 접합하여 옷감이나 가방 등의 소재로 사용될 수 있다. 본 발명의 옻칠 문양 판지를 가구에 접합하는 경우 품격 높은 가구가 제공된다. Such a lacquered cardboard according to the present invention can be used as a material for bags, shoes, and the like by bonding it to leather, and it can be bonded to a forge and used as a material such as cloth or bag. When the lacquered cardboard of the present invention is bonded to furniture, highly furnished furniture is provided.

Claims (2)

표면에 0.3~1mm의 높이차를 가지는 요철부를 가지는 문양틀판을 마련하는 문양틀판 마련단계와,
테레핀유에 희석된 옻칠을 마련하되 옅은색 투명 옻칠과 불투명한 옻칠의 두가지 옻칠을 마련하는 옻칠단계와,
상기 문양틀판에 상기 투명 옻칠을 피복시키는 투명 옻칠 도포단계와,
상기 투명 옻칠을 건조시키어 투명 옻칠층을 형성시키는 투명 옻칠 건조 단계와, 건조된 투명 옻칠층 위에 불투명인 옻칠을 도포하는 불투명 옻칠 도포 단계와,
도포된 불투명 옻칠층을 건조시키는 불투명 옻칠층 건조단계와,
불투명 옻칠층 위에, 표면부가 평평하게, 보강층을 설치하는 보강층 설치단계와, 상기 보강층에 접착제를 도포하고 보강판지를 부착하는 보강판지 설치 단계와,
상기 문양틀판으로부터 투명 옻칠층과 불투명 옻칠층과 보강층과 보강판지로 되는 옻칠 문양 판지를 분리하는 문양틀판 분리 단계로 구성되는 것을 특징으로 하는 옻칠 문양 판지의 제조 방법.A step of preparing a pattern mold plate having a surface having a concavo-convex portion having a height difference of 0.3 to 1 mm,
Lacquered lacquer is prepared in diluted lacquer oil, and lacquering step is carried out to prepare two lacquer of light transparent lacquer and opaque lacquer,
A transparent lacquer applying step of coating the transparent lacquer on the pattern plate,
A transparent lacquer drying step of drying the transparent lacquer to form a transparent lacquer layer, an opaque lacquer applying step of applying opaque lacquer on the dried transparent lacquer layer,
Drying the opaque lacquer layer to dry the coated opaque lacquer layer,
A reinforcing layer mounting step of providing a reinforcing layer on the opaque lacquer layer so as to have a flat surface, a reinforcing cardboard mounting step of applying an adhesive to the reinforcing layer and attaching a reinforcing cardboard,
And separating the transparent lacquer layer, the opaque lacquer layer, the reinforcing layer, and the lacquer patterned cardboard from the patterned plate, from the patterned plate. 제1항에 있어서, 투명 옻칠 도포 단계는 상기 투명 옻칠을 0.05~0.1mm의 두께로 피복시키는 것이며, 불투명 옻칠 도포 단계는 불투명인 옻칠을 0.05~0.1mm 두께로 도포하는 것이며, 보강층 설치 단계는 보강층이 문양틀판의 요철에 대응하여 불투명 옻칠층에 형성된 요철 중 높은 봉우리 위로 0.05~0.5mm 높게 형성되게 하는 것이고, 보강층을 형성하는 물질은 수성접착제인 것을 특징으로 하는 옻칠 문양 판지의 제조 방법.[2] The method of claim 1, wherein the transparent lacquer coating step comprises coating the transparent lacquer with a thickness of 0.05-0.1 mm, the opaque lacquer applying step applying opaque lacquer with a thickness of 0.05-0.1 mm, Wherein the reinforcing layer is formed of a water-based adhesive, wherein the reinforcing layer is formed to have a thickness of 0.05 to 0.5 mm above the high peaks of the unevenness formed in the opaque lacquer layer in correspondence to the concavities and convexities of the pattern plate.
KR1020140128918A 2014-09-26 2014-09-26 Lacquer applied sheets manufacturing method KR101473158B1 (en)