KR101440222B1 - Preparing method for cotton gloves using natural rubber and synthetic rubber - Google Patents
Preparing method for cotton gloves using natural rubber and synthetic rubber Download PDFInfo
- Publication number
- KR101440222B1 KR101440222B1 KR1020130027020A KR20130027020A KR101440222B1 KR 101440222 B1 KR101440222 B1 KR 101440222B1 KR 1020130027020 A KR1020130027020 A KR 1020130027020A KR 20130027020 A KR20130027020 A KR 20130027020A KR 101440222 B1 KR101440222 B1 KR 101440222B1
- Authority
- KR
- South Korea
- Prior art keywords
- coating
- cotton
- coating liquid
- latex
- glove
- Prior art date
Abstract
Description
본 발명은 천연고무와 합성고무를 이용한 면장갑의 제조방법에 대한 것으로, 특히 천연고무에 의해 내마모성과 인장력이 우수하면서, 합성고무에 의해 내유성과 그립성이 우수한 코팅층을 가지는 면 장갑에 대한 것이다.
The present invention relates to a method for producing a cotton glove made of natural rubber and synthetic rubber, and more particularly to a cotton glove having a coating layer excellent in wear resistance and tensile strength by natural rubber and excellent in oil resistance and gripability by synthetic rubber.
일반적으로 장업용 장갑에는 면으로 된 장갑과 나일론으로 된 장갑이 주종을 이루고 있다.In general, business gloves consist of cotton gloves and nylon gloves.
상기 면으로 된 장갑은 장갑의 재질이 면으로 직조되어 있기 때문에 장갑의 바닥면이나 손가락부에 수지를 코팅할 경우 수지가 면에 잘 묻음으로서 용이하게 코팅할수가 있으나 장갑이 면으로 된 특성으로 인하여 장갑을 이루고있는 면과 코팅부가 두껍고 투박하며, 이로 인하여 장갑을 끼고 물건을 집으로 경우 감각을 느낄 수가 없는 문제점이 있었다. 또한, 면에 수지가 코팅된 면장갑은 수지가 견고하기 때문에 장갑을 장기간 착용할 경우 손에 통증을 느끼게 됨으로서 작업자가 장갑의 착용을 기피하게 되는 단점이 있으며 이로 인하여 작업자가 맨손으로 작업을 하게 됨으로서 미끄럼이 잘생되어 안전사고가 일어나게 되는 단점이 있으며, 장갑의 사용을 기피함으로서 손이 트거나 사고가 일어 날 경우 작업자가 크게 다치게 되는 문제점이 있었다. 그리고, 면으로 된 장갑은 장갑을 직조할때 실이 굵으므로 인하여 직조시 장갑에 형성되는 실과 실사이의 간격이 크므로 보기가 흉한 단점이 있으며, 이로 인하여 면 장갑에 수지를 코팅할 경우 미관상 보기가 흉한 문제점이 있었다.Since the glove made of the above-mentioned face is woven with the surface of the glove, when the resin is coated on the bottom face or the finger portion of the glove, the resin can be easily coated because it is easily coated on the face. There is a problem that the face and the coating part forming the gloves are thick and tough, and the sense of feeling can not be felt when the object is put on the glove with the glove. In addition, the cotton gloves coated with resin on the face have a disadvantage that the workers feel pain in the hands when wearing the gloves for a long period of time because the resin is robust, thereby avoiding wearing of the gloves. As a result, There is a disadvantage that a safety accident occurs, and there is a problem that a worker is severely injured when a hand or an accident occurs by avoiding the use of gloves. In addition, the cotton gloves have a disadvantage in that the gap between the yarn and the yarn formed on the gloves is large due to the thick yarn when weaving the gloves, and therefore, when the resin is coated on the cotton gloves, There was a nasty problem.
또한, 나일론 장갑을 사용할 경우 나일론 자체가 미끄러운 재질이기 때문에 작업용으로 사용하기에는 곤란한 문제점이 있었다. 상기와 같은 문제점을 해결하기 위하여 나일론 장갑에 수지를 코팅할 경우 나일론의 미끄러운 성질에 의하여 수지가 묻지 않아 코팅이 되지 않는 단점이 있었다. 상기와 같이 종래에는 나일론의 장갑은 미끄러운 성질로 인하여 작업용으로는 사용하지 않게 되는 단점이 있으며, 이로 인하여 각종 행사장에서 일회용으로 착용하는 것으로 만족하여야 하므로서 고가의 장갑을 낭비하게 되는 문제점이 있었다.
Further, when nylon gloves are used, nylon itself is a slippery material, so that it is difficult to use it as a workpiece. When the resin is coated on the nylon glove to solve the above-mentioned problem, there is a drawback that the resin is not coated due to the slippery nature of the nylon and the coating is not performed. As described above, conventionally, the nylon glove is disadvantageous in that it is not used for a work because of its slippery nature, and therefore it is required to be worn as disposable at various events so that expensive gloves are wasted.
한편, 종래의 라텍스 코팅 장갑에는 천연 라텍스(natural latex)가 주로 사용되었는 데, 천연 라텍스에 함유된 단백질은 일부 사용자에게 통증이나 발진 등의 알러지 반응을 일으키는 문제점이 있었다. 그리고, 천연 라텍스는 원산지에 따라 물성이 달라 품질이 균일하지 않고, 최근 고무나무의 재배면적 감소로 인해 가격이 급등하고 있다. 또한, 천연 고무 라텍스는 장갑에 코팅되더라도 기름에 의해 쉽게 녹아내리고, 물체를 잡았을 때 매우 미끄러워서 그립성이 없기 때문에, 작업 능률이 떨어지고 일회용으로 사용하고 버려야하는 문제점이 있었다.On the other hand, natural latex is mainly used for conventional latex-coated gloves. Proteins contained in natural latex have a problem that some users cause allergic reaction such as pain and rash. In addition, the quality of natural latex is not uniform due to the different properties depending on the place of origin, and the price has soared due to the recent decrease in the cultivation area of the rubber tree. Further, the natural rubber latex is easily melted by oil even when it is coated on the glove, and when the object is gripped, it is very slippery and there is no grip, so that the work efficiency is lowered and it is used for disposable use.
이러한 단점을 보완하기 위하여, 합성고무로서 내유성인 니트릴 부타디엔 고무(NBR: nitrilebutadiene rubber) 라텍스를 코팅하기도 하지만, 물 세척이 없는 건식 타입으로 코팅할 경우 면장갑 내피 사이로 NBR LATEX가 침투되는 특수성 때문에 제품화할 수가 없었다. In order to compensate for these drawbacks, nitrile butadiene rubber latex (NBR) may be coated as a synthetic rubber, but when coated with a dry type without water washing, the NBR LATEX penetrates into the inner side of the armor There was no.
이와 관련하여, 대한민국 공개특허 2002-0086801에서는 나일론 장갑을 먼저 알콜(침투방지제)로 전처리하고, NBR 등을 포함하는 1차 및 2차 코팅제에 연속적으로 딥핑(dipping)하며, 건조, 세척 및 재건조의 과정을 거치는 특수합성고무 코팅제가 코팅된 나일론 작업용 장갑의 코팅방법이 기재되어 있으나, 이것은 기본적으로 나일론 장갑을 대상으로 하는 것이고, 침투방지제를 이용한 전처리와 1차 및 2차의 연속 코팅 과정 및 세척과 재건조 과정과 같은 복잡한 과정을 거쳐야 하는 단점이 있다.
In this connection, Korean Patent Laid-Open Publication No. 2002-0086801 discloses a method wherein the nylon gloves are first pre-treated with an alcohol (an anti-penetration agent), dipped continuously into primary and secondary coating agents including NBR, The present invention relates to a method of coating a nylon glove coated with a special synthetic rubber coating agent which is applied to a nylon glove, It is a complicated process such as a re-drying process.
본 발명은 상기한 문제점을 해결하기 위한 것으로, 내마모성과 인장력이 우수하면서, 동시에 내유성과 그립성도 우수한 코팅층을 가지는 면 장갑을 제조하는 것이 목적이다. Disclosure of Invention Technical Problem [8] Accordingly, the present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to provide a cotton glove having a coating layer excellent in wear resistance and tensile strength and also excellent in oil resistance and gripability.
또한, 본 발명은 별도의 방수제나 발수제(응고제)에 의한 전처리 코팅 없이도, 우수한 땀 흡수성과, 내유성, 그립성, 굴곡성 등을 고르게 만족시킬 수 있는 라텍스 코팅 면 장갑을 간단하고 용이하게 제조하기 위한 것이다.
The present invention is also intended to easily and easily produce a latex coated cotton glove which can satisfactorily satisfy superior sweat absorbability, oil resistance, gripability, flexibility and the like even without pretreatment with a waterproofing agent or a water repellent agent .
상기한 목적을 달성하기 위한 본 발명은, 천연고무 라텍스를 주성분으로 하는 제1코팅액과, 합성고무 라텍스를 주성분으로 하는 제2코팅액을 준비하는 단계; 면 장갑에 상기 제1코팅액을 코팅하고, 상기 제1코팅액이 코팅된 코팅층에 상기 제2코팅액을 코팅하는 단계; 및 상기 제2코팅액이 코팅된 면 장갑을 건조시키는 단계;를 포함하는 면 장갑의 제조방법이다. According to an aspect of the present invention, there is provided a method of preparing a rubber composition, comprising: preparing a first coating solution containing a natural rubber latex as a main component; and a second coating solution containing a synthetic rubber latex as a main component; Coating the first coating liquid on the cotton glove, and coating the second coating liquid on the coating layer coated with the first coating liquid; And drying the cotton glove coated with the second coating liquid.
여기서, 상기 코팅층은 겔 상태인 것이 바람직하다. Here, the coating layer is preferably in a gel state.
그리고, 상기 코팅하는 단계는, 몰드에 장착된 면 장갑에 상기 제1코팅액을 코팅하는 단계; 상기 몰드의 온도를 20~60℃ 범위 내로 하고, 상기 제1코팅액이 코팅된 면 장갑을 3~10분간 건조시키는 단계; 및 상기 건조에 의해 형성된 코팅층에 상기 제2코팅액을 코팅하는 단계;를 포함하는 것이 가능하다.
The coating step may include coating the first coating liquid on a face glove mounted on the mold; Drying the face glove coated with the first coating liquid for 3 to 10 minutes while setting the temperature of the mold within a range of 20 to 60 ° C; And coating the second coating liquid on the coating layer formed by the drying.
한편, 본 발명의 다른 실시형태는, 상기한 제조방법에 의해 제조되어, 면 장갑 표면에 천연고무 라텍스를 주성분으로 하는 제1코팅층과, 합성고무 라텍스를 주성분으로 하는 제2코팅층이 순차적으로 형성된 것을 특징으로 하는 면 장갑일 수 있다.
On the other hand, another embodiment of the present invention is a manufacturing method of a cotton glove, which is produced by the above-described manufacturing method, comprising a first coating layer comprising a natural rubber latex as a main component and a second coating layer comprising a synthetic rubber latex as a main component sequentially formed on the surface of the cotton glove It can be a cotton glove featured.
기타 실시예들의 구체적인 사항들은 상세한 설명 및 도면들에 포함되어 있다.
The details of other embodiments are included in the detailed description and drawings.
이러한 본 발명에 의하면, 천연고무에 의해 내마모성과 인장력이 우수하면서, 합성고무에 의해 내유성과 그립성이 우수한 코팅층을 가지는 면 장갑을 제조할 수 있다. According to the present invention, it is possible to produce a cotton glove having a coating layer excellent in oil resistance and gripability by synthetic rubber while having excellent abrasion resistance and tensile strength by natural rubber.
또한, 본 발명은 별도의 방수제나 발수제(응고제)에 의한 전처리 코팅 없이도, 우수한 땀 흡수성과, 내유성, 그립성, 굴곡성 등을 고르게 만족시킬 수 있는 라텍스 코팅 면 장갑을 간단하고 용이하게 제조할 수 있는 것이다.
In addition, the present invention can easily and easily produce a latex coated cotton glove which can satisfactorily satisfy superior sweat absorbability, oil resistance, gripability, flexibility and the like without pretreatment with a waterproofing agent or a water repellent agent will be.
본 발명은 다양한 변환을 가할 수 있고 여러 가지 실시 예를 가질 수 있는 바, 특정 실시 예들을 도면에 예시하고 상세한 설명에서 상세하게 설명하고자 한다. 그러나, 이는 본 발명을 특정한 실시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변환, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다. 본 발명을 설명함에 있어서 관련된 공지 기술에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우 그 상세한 설명을 생략한다.BRIEF DESCRIPTION OF THE DRAWINGS The present invention is capable of various modifications and various embodiments, and specific embodiments are illustrated in the drawings and will be described in detail in the detailed description. It is to be understood, however, that the invention is not to be limited to the specific embodiments, but includes all modifications, equivalents, and alternatives falling within the spirit and scope of the invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.
본 출원에서 사용한 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 출원에서, "포함하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.The terminology used in this application is used only to describe a specific embodiment and is not intended to limit the invention. The singular expressions include plural expressions unless the context clearly dictates otherwise. In the present application, the terms "comprises" or "having" and the like are used to specify that there is a feature, a number, a step, an operation, an element, a component or a combination thereof described in the specification, But do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, or combinations thereof.
제1, 제2 등의 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 상기 구성요소들은 상기 용어들에 의해 한정되어서는 안 된다. 상기 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다.
The terms first, second, etc. may be used to describe various components, but the components should not be limited by the terms. The terms are used only for the purpose of distinguishing one component from another.
본 발명은 면 장갑의 제조방법에 대한 것으로, 주로 면이나 또는 나일론 등으로 이루어진 장갑에 라텍스 수지 조성물을 코팅하는 방법이며, 바람직하게는 면으로 이루어진 면 장갑을 코팅하는 방법이다. The present invention relates to a method for producing cotton gloves, and is a method of coating a latex resin composition on a glove mainly made of cotton, nylon or the like, and is preferably a method of coating cotton gloves made of cotton.
기본적으로, 본 발명에 따른 면 장갑 제조방법은 면 장갑을 코팅하기 위한 코팅액을 준비하고, 상기 준비한 코팅액을 면 장갑에 코팅하며, 상기 코팅액이 코팅된 면 장갑을 건조하는 과정을 포함한다. Basically, the method for manufacturing cotton gloves according to the present invention comprises preparing a coating liquid for coating cotton gloves, coating the prepared coating liquid on cotton gloves, and drying the cotton gloves coated with the coating liquid.
특히, 본 발명자는 면 장갑에 천연고무 라텍스를 주성분으로 하는 제1코팅액을 코팅하고, 이어서 합성고무 라텍스를 주성분으로 하는 제2코팅액을 코팅한 후, 건조시키면, 천연고무에 의해 내마모성과 인장력이 우수하면서, 합성고무에 의해 내유성과 그립성이 우수한 코팅층을 가지는 면 장갑을 제조할 수 있음을 확인한 후, 본 발명을 완성하였다. Particularly, the inventors of the present invention have found that when a first coating liquid containing a natural rubber latex as a main component is coated on a cotton glove and then a second coating liquid containing a synthetic rubber latex as a main component is coated and dried, natural abrasion resistance and tensile strength , The present inventors completed the present invention after confirming that it is possible to produce cotton gloves having a coating layer excellent in oil resistance and gripability by synthetic rubber.
이를 위하여, 본 발명에 따른 면 장갑 제조방법은, 먼저 천연고무 라텍스를 주성분으로 하는 제1코팅액과, 합성고무 라텍스를 주성분으로 하는 제2코팅액을 준비하는 것이다. To this end, the method for manufacturing cotton gloves according to the present invention comprises preparing a first coating liquid containing a natural rubber latex as a main component and a second coating liquid containing a synthetic rubber latex as a main component.
상기 제1코팅액과 제2코팅액 각각이 천연고무 라텍스와 합성고무 라텍스를 주성분으로 하는 것은, 각각의 코팅액 조성물 전체에서 상기 천연고무 라텍스와 합성고무 라텍스가 각각 절반 이상, 즉 50 중량% 이상 함유되는 것을 의미한다. 상기 제1코팅액과 제2코팅액을 준비하는 것은 순서에 상관없이, 연속적으로 또는 동시에 준비될 수 있다. The first coating liquid and the second coating liquid each contain a natural rubber latex and a synthetic rubber latex as a main component in such a manner that the natural rubber latex and the synthetic rubber latex are each contained in an amount of not less than 50% it means. The preparation of the first coating liquid and the second coating liquid can be prepared continuously or simultaneously, regardless of the order.
상기 천연고무 라텍스는 이 기술분야에 알려진 다양한 것을 모두 포함하고, 예를 들면 NR(natural rubber) 라텍스인 것이 바람직하다. 그리고, 상기 합성고무 라텍스 역시 특별히 제한되지 않으며 예를 들면 니트릴 부타디엔 고무(NBR: nitrilebutadiene rubber) 라텍스, 스티렌-부타디엔 라텍스(SB 라텍스), 스티렌-부타디엔 고무 라텍스(SBR latex) 등일 수 있고, 그 중에서도 NBR 라텍스인 것이 더욱 바람직하다. The natural rubber latex includes various ones known in the art, for example, natural rubber (NR) latex. The synthetic rubber latex is also not particularly limited and may be, for example, nitrile butadiene rubber latex, styrene-butadiene latex (SB latex), styrene-butadiene rubber latex (SBR latex) More preferably, it is latex.
종래에 장갑용 코팅 조성물로서 사용되던 천연고무 라텍스는 장갑에 코팅되더라도 기름에 의해 쉽게 녹아내리고, 물체를 잡았을 때 매우 미끄러워서 그립성이 없다는 단점이 있었다. 또한, 종래에 합성고무 라텍스를 면 장갑에 코팅하면, 면장갑 내피 사이로 NBR LATEX가 침투되어 제품화할 수가 없었다. 이에 본 발명에서는 천연고무 라텍스와 합성고무 라텍스를 함께 이용하여, NR LATEX와 NBR LATEX의 장점만을 결합하고자 하였으며, 이를 위하여 천연고무 라텍스와 합성고무 라텍스를 각각 별도로 준비한 다음, 후술하는 바와 같이 서로 다른층으로 코팅하는 것이 특징이다. Conventionally, natural rubber latex used as a coating composition for a glove has a disadvantage that it is easily melted by oil even when it is coated on gloves, and is very slippery when gripping an object, so that there is no grip. In addition, when conventional synthetic rubber latex was coated on cotton gloves, NBR LATEX penetrated into the inner surface of cotton gloves and could not be commercialized. Therefore, in the present invention, only the advantages of NR LATEX and NBR LATEX are combined using natural rubber latex and synthetic rubber latex. For this purpose, natural rubber latex and synthetic rubber latex are separately prepared, and then, .
이와 함께, 본 발명에 따른 상기 제1코팅액과 제2코팅액에는 라텍스 수지 조성물의 물성을 보다 향상시키기 위한 각종 첨가제가 포함될 수 있다. 상기 첨가제는 당업계에서 통상적으로 사용되는 각 첨가제의 종류를 통상의 함량으로 사용할 수 있으므로, 그 종류 및 함량을 특별히 한정하지 않는다. In addition, the first coating liquid and the second coating liquid according to the present invention may contain various additives for further improving the physical properties of the latex resin composition. The kind of the additive usually used in the art can be used in a usual amount, and therefore the kind and content thereof are not particularly limited.
이때 바람직하게는, 상기 첨가제로서 pH 조절을 위한 수산화칼륨(KOH), 합성고무 라텍스를 가황시키기 위한 황, 가황 촉진제를 비롯한, 산화아연, 염료, 무기 충진제, 분산제 및 촉진제로 이루어진 군에서 선택된 하나 이상이 포함될 수 있다. 예를 들어, 상기 제1코팅액과 제2코팅액은 각각 NR 라텍스(NR:Natrul Rubber Latex)와 합성고무 라텍스인 니트릴 부타디엔 고무(NBR: nitrilebutadiene rubber latex)를 주원료로 하고, 여기에 가교제인 황, 가황 촉진제인 산화아연, 가류 촉진제, 분산제, 안정제인 수산화칼륨, 증점제, 안료 등을 포함할 수 있다. 즉, 상기 제1코팅액은 NR LATEX에 KOH, 유황, 아연화, 분산제, 촉진제, 안료 등을 혼합, 교반하여 숙성시키는 과정을 통하여 준비될 수 있고, 상기 제2코팅액은 NBR LATEX에 KOH, 유황, 아연화, 분산제, 촉진제, 증점제, 안료 등를 혼합, 교반하여 숙성시키는 과정으로 준비될 수 있다. 구체적으로, 상기 제1코팅액은 NR LATEX 원액에 유황,아연화, 분산제, 촉진제, 물로 볼밀된 약품을 투입, 교반하면서 안료를 투입하고, 8시간~48시간 이상 숙성시켜서 준비하는 것이 가능하며, 상기 제2코팅액은 NBR LATEX 원액에 KOH(3%수용액)을 가하여 PH를 9~11로 조정한 다음, 유황, 아연화, 분산제, 촉진제, 물로 볼밀된 약품을 투입, 교반하면서 증점제와 안료를 순차적으로 또는 한번에 투입한 후 8시간~48시간 이상 숙성시켜서 준비할 수 있다. 더욱 바람직하게는, 천연고무 라텍스 또는 합성고무 라텍스 100 중량부에 대하여, 산화아연 0.45~0.9 중량부, 황 0.28~0.56 중량부, 분산제 0.12~0.24 중량부, 촉진제 0.26~0.52 중량부, 물 1.2~2.4 중량부가 포함될 수 있다. Preferably, the additive is at least one selected from the group consisting of zinc oxide, a dye, an inorganic filler, a dispersing agent and an accelerator, such as potassium hydroxide (KOH) for controlling the pH, sulfur for vulcanizing the synthetic rubber latex, May be included. For example, the first coating liquid and the second coating liquid are prepared by using NR latex (Natrul Rubber latex) and nitrile butadiene rubber latex (NBR), which are synthetic rubber latex, as main raw materials, Zinc oxide as an accelerator, a vulcanization accelerator, a dispersant, a stabilizer such as potassium hydroxide, a thickener, a pigment, and the like. That is, the first coating liquid may be prepared by mixing and stirring the NR LATEX with KOH, sulfur, zinc, a dispersant, an accelerator, a pigment, etc., and aging the second coating liquid. The second coating liquid may contain KOH, sulfur, , A dispersing agent, an accelerator, a thickener, a pigment, and the like, followed by aging and aging. Specifically, the first coating liquid can be prepared by adding sulfur, zinc, a dispersant, an accelerator, a ball milled with water to a stock solution of NR LATEX and stirring the mixture for 8 hours to 48 hours or more, 2 The coating solution is prepared by adding KOH (3% aqueous solution) to the NBR LATEX stock solution to adjust the pH to 9-11, then adding the ball milled chemicals with sulfur, zinc, dispersant, accelerator and water and stirring the thickener and pigment sequentially After the addition, it can be prepared by aging for 8 hours to 48 hours or more. More preferably, 0.45 to 0.9 parts by weight of zinc oxide, 0.28 to 0.56 parts by weight of sulfur, 0.12 to 0.24 parts by weight of a dispersing agent, 0.26 to 0.52 parts by weight of an accelerator, and 1.2 to 0.52 parts by weight of a rubber are mixed with 100 parts by weight of natural rubber latex or synthetic rubber latex. 2.4 parts by weight may be included.
또한, 상기 증점제는 도포되는 수지의 두께, 함침의 정도, 착색의 정도에 따라 점도를 조절 및 유지시키는 역할을 하는데, 이때 증점제로는 아크릴계 증점제, 아마이드계증점제, 우레탄계 증점제 및 셀룰로즈계 증점제 등을 이용할 수 있고, 그 중에서도 아크릴 에멀젼 점증제를 사용하는 것이 바람직하다. 나아가, 상기 아크릴 에멀젼 점증제와 함께 알긴산나트륨, 메틸셀룰로오스, 규산나트륨, PVA, 폴리아크릴산나트륨 및 벤토니트로 등의 다양한 첨가제를 이용할 수 있으며, 더욱 바람직하게는 아크릴 에멀젼과 폴리아크릴산나트륨을 함께 이용하는 것이 적합하다. In addition, the thickener serves to control and maintain the viscosity according to the thickness of the applied resin, the degree of impregnation, and the degree of coloring. Examples of the thickener include an acrylic thickener, an amide thickener, a urethane thickener, and a cellulose thickener Among them, it is preferable to use an acrylic emulsion thickener. Further, various additives such as sodium alginate, methylcellulose, sodium silicate, PVA, sodium polyacrylate and bentonitro may be used together with the above acrylic emulsion thickener, more preferably acrylic emulsion and sodium polyacrylate are used together Do.
이어서, 본 발명에 따른 면 장갑 제조방법은 면 장갑에 상기 제1코팅액을 코팅하고, 상기 제1코팅액이 코팅된 코팅층에 상기 제2코팅액을 코팅하는 단계를 거친다. Next, the method for manufacturing a cotton glove according to the present invention includes the step of coating the first coating liquid on a cotton glove, and coating the second coating liquid on the coating layer coated with the first coating liquid.
즉, 별도로 준비된 면 장갑에 먼저 상기 제1코팅액으로 제1코팅층을 형성하고, 상기 형성된 제1코팅층 위에 상기 제2코팅액으로 제2코팅층을 형성하는 것이다. 예를 들어, 상기 교반, 숙성된 코팅액에 직조된 면장갑이 끼워진 몰드를 딥핑(dipping)하여 코팅시킬 수 있다. 다시 말해서, 장갑이 직조되고 1,2차 코팅액이 준비되면 상기 코팅액을 별도의 1차, 2차 용기에 투입하고, 직조된 장갑을 몰드에 끼운 다음, 상기 몰드를 1차로 NR라텍스 조성물이 담겨진 1차 용기에 디핑한 후, 이어서 2차 NBR라텍스 조성물이 담겨진 2차 용기에 디핑하는 것이다. 이러한 본 발명은 면장갑에 침투방지제(응고제)의 사전 전처리 없이 코팅액을 코팅시키는 것이 가능하다. That is, a first coating layer is first formed of the first coating liquid in a separately prepared cotton glove, and a second coating layer is formed of the second coating liquid on the formed first coating layer. For example, the aged coating solution may be coated by dipping a mold with woven cotton gloves into the aged coating solution. In other words, when the gloves are woven and the first and second coating liquids are prepared, the coating liquid is put into separate primary and secondary containers, and the woven gloves are sandwiched between the molds. Then, the mold is immersed in a solution containing the NR latex composition Dipping into a secondary vessel followed by dipping into a secondary vessel containing the secondary NBR latex composition. The present invention makes it possible to coat a coating liquid on a cotton glove without pre-treating the penetration inhibitor (coagulant).
그래서, 본 발명에 따른 코팅 단계는, NR LATEX가 교반, 숙성된 제1코팅액에 면장갑이 끼워진 몰드를 딥핑하여 NR 라텍스 조성물을 1차로 코팅시키는 제1코팅 단계와; NBR LATEX가 교반, 숙성된 제2코팅액에 상기 NR 라텍스 조성물이 1차로 코팅된 면 장갑이 끼워진 몰드를 딥핑하여 NBR 라텍스 조성물을 2차로 코팅시키는 제2코팅 단계;를 포함할 수 있다.Thus, the coating step according to the present invention comprises: a first coating step in which the NR latex composition is first coated by dipping a mold in which the NR LATEX is agitated and the aged first coating solution has a cotton glove; And a second coating step in which the NBR latex composition is coated with the NBR latex composition by dipping in a second coating liquid in which the NBR LATEX is aged and aged, by dipping a mold having a face glove on the first coating the NR latex composition.
상기 제1코팅액과 제2코팅액은 각각 면 장갑의 전체 또는 일부(손바닥 및/또는 손등 부분)에 코팅될 수 있고, 바람직하게는 상기 제2코팅액이 면 장갑에 직접 스며들지 않도록, 상기 제2코팅액은 제1코팅액에 의해 형성된 제1코팅층 상에 코팅되는 것이 적합하다. The first coating liquid and the second coating liquid may be coated on all or a part of the cotton glove (the palm and / or the back of the hand), preferably the second coating liquid does not directly impregnate the cotton glove, Is suitably coated on the first coating layer formed by the first coating liquid.
이러한 본 발명은 1차로 면장갑에 NR 라텍스(NR:Natrul Rubber Latex)조성물을 코팅하고, 2차로 합성고무 라텍스인 니트릴 부타디엔 고무(NBR: nitrilebutadiene rubber latex) 코팅용 조성물을 코팅하는 것이 특징이고, 이에 따르면 NBR이 면 장갑에 직접 침투되지 않아 면의 땀 흡수성을 유지할 수 있을 뿐만 아니라, 천연고무에 의해 내마모성과 인장력이 우수하면서, 합성고무에 의해 내유성과 그립성이 우수한 코팅층을 가지는 면 장갑을 제조할 수 있다. The present invention is characterized in that a nitrile butadiene rubber (NBR) coating composition is coated on a cotton knit glove in the first place by coating a NR rubber latex composition and a second synthetic rubber latex, NBR is not directly penetrated to the cotton gloves, and cotton gloves having a coating layer excellent in oil resistance and gripability by synthetic rubber can be produced, while maintaining the sweat absorbency of the cotton as well as being excellent in abrasion resistance and tensile strength by natural rubber have.
여기서, 본 발명의 다른 특징은 상기 코팅층이 겔 상태인 것이 바람직하다. 즉, 제1코팅액을 코팅한 후, 제2코팅액을 코팅하는 시점에 있어서, 상기 제1코팅액에 의해 형성된 코팅층이 약간 습한 미가류의 겔링 상태일 때 제2코팅액을 코팅하는 것이 제1코팅층과 제2코팅층 간의 층분리를 없게 해 준다는 점에서 바람직하다. 상기 겔 상태라 함은 제1코팅액에 포함된 수분이 승화하기 전의 젤 상태와 상기 수분이 거의 모두 증발한 고체 상태의 중간 단계로써, 구체적으로는 상기 제1코팅액에 포함된 가소성 물질이 탄성물질로 변화되기 전 또는 상기 제1코팅액에 포함된 황 성분이 가류되기 전의 단계를 의미한다. In another aspect of the present invention, it is preferable that the coating layer is in a gel state. That is, when the first coating liquid is coated and then the second coating liquid is coated, coating the second coating liquid when the coating layer formed by the first coating liquid is in the gelled state of the slightly wetted unvulcanized state, 2 < / RTI > coating layer. The gel state is an intermediate state between a gel state before the sublimation of the water contained in the first coating liquid and a solid state in which the water is almost completely evaporated. Specifically, the plastic state contained in the first coating liquid is an elastic substance Means a step before the sulfur component contained in the first coating liquid is changed or before the sulfur component is vulcanized.
이를 위하여, 면 장갑이 장착된 몰드(금형)의 온도는 20~60℃ 범위 내인 것이 바람직하고, 상기 제1코팅액이 코팅된 다음 약 3~10분간(바람직하게는 4~8분간)의 시간 동안 건조시킨 다음, 제2코팅액을 코팅하는 것이 더욱 바람직하다. 만약, 상기 몰드의 온도와 시간이 상기 범위를 벗어나면, 제1코팅층이 젤 상태 또는 고체 상태를 가져서, 제1코팅층과 제2코팅층의 층 분리가 일어날 수 있다. For this, the temperature of the mold (mold) equipped with the cotton gloves is preferably in the range of 20 to 60 ° C., and after the coating of the first coating liquid is performed for about 3 to 10 minutes (preferably 4 to 8 minutes) It is more preferable to coat the second coating liquid after drying. If the temperature and time of the mold are out of the above range, the first coating layer may have a gel state or a solid state, so that the layer separation of the first coating layer and the second coating layer may occur.
이에 따르면, 본 발명에 따른 상기 코팅하는 단계는, 먼저 몰드에 장착된 면 장갑에 상기 제1코팅액을 코팅하는 단계; 상기 몰드의 온도를 20~60℃ 범위 내로 하고, 상기 제1코팅액이 코팅된 면 장갑을 3~10분간 건조시키는 단계; 및 상기 건조에 의해 형성된 코팅층에 상기 제2코팅액을 코팅하는 단계;를 포함할 수 있다. According to the present invention, the coating step may include coating the first coating liquid on a cotton glove mounted on a mold; Drying the face glove coated with the first coating liquid for 3 to 10 minutes while setting the temperature of the mold within a range of 20 to 60 ° C; And coating the second coating liquid on the coating layer formed by the drying.
상기 제1코팅액과 제2코팅액의 사용량은 특별히 제한되지 않지만, 상기 제1코팅액 1 중량부에 대하여 제2코팅액은 0.2~2.0중량부인 것이 바람직하고, 0.5~1.5중량부인 것이 더욱 바람직하다. 즉, 천연고무 라텍스와 합성고무 라텍스를 이용함에 따른 최소한도의 효과가 발현될 수 있도록 하기 위하여, 상기 제1코팅액과 제2코팅액 각각은 고형분 함량을 기준으로 상기 제1코팅액 1 중량부에 대하여 제2코팅액이 0.2 중량부 이상 포함되는 것이 바람직하다. 또한, 상기 제2코팅액을 필요 이상으로 첨가할 경우 합성고무 라텍스에 의한 코팅층의 특성(탄성, 유연성 등)이 저하될 수 있는데, 이를 방지하기 위하여 상기 제1코팅액과 제2코팅액의 사용량은 상기 제1코팅액 1 중량부에 대하여 제2코팅액이 2.0 중량부 이하인 것이 바람직하다.The amount of the first coating liquid and the second coating liquid is not particularly limited, but is preferably 0.2-2.0 parts by weight, and more preferably 0.5-1.5 parts by weight based on 1 part by weight of the first coating liquid. That is, in order to minimize the effect of using the natural rubber latex and the synthetic rubber latex, each of the first coating solution and the second coating solution may be prepared by mixing, based on the solid content, 1 part by weight of the first coating solution 2 coating liquid is preferably contained in an amount of 0.2 part by weight or more. In addition, when the second coating solution is added in an excessive amount, the properties (elasticity, flexibility, etc.) of the coating layer due to the synthetic rubber latex may be deteriorated. To prevent this, the amount of the first coating solution and the second coating solution, 1 coating liquid is 2.0 parts by weight or less based on 1 part by weight of the coating liquid.
그런 다음, 본 발명은 상기 제2코팅액이 코팅된 면 장갑을 건조시키는 단계;를 거친다. Then, the present invention is carried out by drying the cotton glove coated with the second coating liquid.
즉, 상기 디핑 단계를 거친 코팅 장갑은 건조단계를 거칠 수 있고, 열을 가하여 소정시간 동안 진행할 수 있으며, 이러한 건조, 경화 단계를 거치게 되면 코팅장갑의 수분은 증발됨과 동시에 코팅액이 가류, 경화된다. 이러한 본 발명은 코팅된 장갑을 세척과정을 거치지 않고 바로 건조로에서 건조, 가류, 경화시키는 것이 특징이다. That is, the coating glove having passed through the dipping step can be subjected to a drying step and can proceed for a predetermined time by applying heat. When the drying and curing steps are performed, moisture of the coating glove is evaporated and the coating liquid is cured and hardened. The present invention is characterized in that the coated gloves are dried, vulcanized and cured immediately in a drying furnace without being subjected to a washing process.
나아가, 본 발명은 상기 건조 가류 경화된 코팅장갑을 몰드에서 탈피시키는 탈피단계;를 더 포함할 수도 있다. Further, the present invention may further include a removing step of removing the dry vulcanized cured coating glove from the mold.
이러한, 본 발명은 별도의 방수제나 발수제(응고제)에 의한 전처리 코팅 없이도, 우수한 땀 흡수성과, 내유성, 그립성, 굴곡성 등을 고르게 만족시킬 수 있는 라텍스 코팅 면 장갑을 간단하고 용이하게 제조할 수 있는 효과가 있다. 또한, 본 발명은 내유성, 굴곡성, 내구성 및 내슬립성이 모두 우수한 NR LATEX와 NBR LATEX 면 2중코팅 장갑을 건식 방법으로도 제조할 수 있고, 이를 통해 기존의 일반화된 NR 코팅장갑기계를 이용해서도 NR 및 NBR 면 코팅 장갑을 생산하는 것이 가능하다.
The present invention can easily and easily produce a latex coated cotton glove which can satisfactorily satisfy superior sweat absorbability, oil resistance, gripability, flexibility and the like even without pretreatment with a waterproofing agent or a water repellent agent It is effective. Further, the present invention can also produce NR LATEX and NBR LATEX double coated gloves, which are excellent in oil resistance, flexibility, durability and slip resistance, by a dry method, and by using the conventional generalized NR coated glove machine It is also possible to produce NR and NBR cotton coated gloves.
한편, 본 발명의 다른 실시형태는, 상기한 제조방법에 의해 제조되어, 면 장갑 표면에 천연고무 라텍스를 주성분으로 하는 제1코팅층과, 합성고무 라텍스를 주성분으로 하는 제2코팅층이 순차적으로 형성된 것을 특징으로 하는 면 장갑일 수 있다. On the other hand, another embodiment of the present invention is characterized in that a first coating layer mainly composed of a natural rubber latex and a second coating layer mainly composed of a synthetic rubber latex are sequentially formed on the surface of the cotton glove, It can be a cotton glove featured.
본 발명에 따른 조성물은 나일론 장갑에 적용되는 것도 가능하지만, 나일론 보다는 면 장갑에 코팅되는 접착력이 우수하고, 종래에 합성고무 라텍스가 면 직물에 침투되는 것을 방지하기 위한 것이라는 점에서, 면 장갑 코팅용으로 적용되는 것이 적합하다. The composition according to the present invention can be applied to nylon gloves, but it has excellent adhesion strength to be coated on cotton gloves rather than nylon, and in order to prevent penetration of synthetic rubber latex into cotton fabric in the past, .
상기 제1코팅층과 제2코팅층 각각은 용도별로 0.1~2.0mm 범위 내의 두께를 가질 수 있다. Each of the first coating layer and the second coating layer may have a thickness within a range of 0.1 to 2.0 mm for each application.
이러한 본 발명에 따른 면장갑은 우수한 땀 흡수성과 함께, NR의 우수한 인장력과 NBR의 내유성을 가질 뿐만 아니라, NR라텍스와 NBR라텍스의 장점만을 살릴 수 있기 때문에, 접지력과 착용감이 우수하고 내구성도 뛰어나다.
The cotton glove according to the present invention has superior sweat absorbability, excellent tensile strength of NR and oil resistance of NBR, as well as merits of NR latex and NBR latex, so that it has good gripping force and excellent durability.
본 발명은 하기의 실시예에 의하여 보다 더 잘 이해 될 수 있으며, 하기의 실시예는 본 발명의 예시 목적을 위한 것이며, 첨부된 특허청구범위에 의하여 한정되는 보호범위를 제한하고자 하는 것은 아니다.
The present invention may be better understood by the following examples, which are for the purpose of illustrating the invention and are not intended to limit the scope of protection defined by the appended claims.
실시예Example
1: 1차 코팅 후, 1: After the first coating,
미가류Micheal
겔링Gelling
상태에서 2차 코팅하는 방법 Method of secondary coating in state
1차 NR 라텍스 코팅 조성물은 NR 라텍스 100KG(60% 고형분 하이 암모니아)에 산화아연(0.6~1.2KG), 황(0.37~0.75KG), 분산제(0.16~0.33KG), 촉진제(0.34~0.68KG)와 물(1.5~3KG)을 24~48시간이상 미세 볼밀한 볼밀액을 투입 교반하고, 8~48시간 동안 숙성시켰다.The primary NR latex coating compositions were prepared by adding zinc oxide (0.6-1.2KG), sulfur (0.37-0.75KG), dispersant (0.16-0.33KG), accelerator (0.34-0.68KG) And water (1.5 to 3 Kg) were agitated for 8 to 48 hours by agitating a ball mill solution having a fine ball mill for 24 to 48 hours or longer.
2차 NBR 라텍스 코팅 조성물은 NBR 라텍스 100KG(45% 고형분)에 KOH(3%) 수용액을 가하여 PH를 9~11로 조절 후, 산화아연(0.45~0.9KG), 황(0.28~0.56KG), 분산제(0.12~0.24KG), 촉진제(0.26~0.52KG)와 물(1.2~2.4KG)을 24~48시간 이상 미세 볼밀한 볼밀액을 투입 교반 하고, 아크릴 점증제(30%고형분 0~1.2KG)를 추가 투입 교반한 후, 8~48시간 동안 숙성시켰다.The secondary NBR latex coating composition was prepared by adding an aqueous solution of KOH (3%) to 100 kg of NBR latex (45% solids) and adjusting pH to 9-11, adding zinc oxide (0.45-0.9 Kg), sulfur (0.28-0.56 Kg) A ball mill solution having a fine ball mill for 24 to 48 hours or more was charged and stirred with a dispersant (0.12 to 0.24 Kg), an accelerator (0.26 to 0.52 Kg) and water (1.2 to 2.4 KG), and an acrylic thickener (30% ) Was further added and agitated, followed by aging for 8 to 48 hours.
기르고, 면장갑을 금형에 끼운 후 상기 1차 코팅액을 디핑한 다음, 1차코팅액의 수분이 승화함으로써 미가류 상태인 1차 코팅 표면이 약간 습한 겔링 상태(금형온도를 20~60도에서 4~10분 가류)를 유지한 상태에서, 2차 코팅액을 디핑한 다음, 건조 및 가류 하였다.
And the cotton glove is dipped in the mold. After dipping the primary coating solution, the water in the primary coating solution sublimes and the uncooled primary coating surface is gelled in a slightly wet state (mold temperature is 20 to 60 degrees and 4 to 10 Minute), the secondary coating solution was dipped, followed by drying and vulcanization.
비교예Comparative Example
1: 1차 코팅 후, 바로 2차 코팅하는 방법 1: First coating, second coating immediately
면장갑을 금형에 끼우고, 상기 1차 코팅액에 디핑한 후, 1차코팅액의 수분이 승화하기 전(금형 온도 20~60도)에 바로 상기 2차 코팅액을 디핑한 다음, 건조, 가류 하였다.
The cotton gloves were put into a mold, dipped in the primary coating solution, and then dipped in the secondary coating solution before the water of the primary coating solution sublimated (mold temperature 20 to 60 degrees), followed by drying and curing.
비교예Comparative Example
2: 장시간 건조에 의한 일부 가류 상태에서 2차 코팅하는 방법 2: A method of secondary coating in a partial vulcanization state by drying for a long time
면장갑을 금형에 끼우고, 상기 1차 코팅액을 디핑한 후, 건조(금형 온도 20~60도에서 10~20분 이상 가류)하여 1차 코팅액 표면이 일부 가류가 이루어진 상태에서 상기 2차 코팅액을 디핑한 다음, 건조,가류 하였다.
The second coating solution was dipped in a state where the surface of the first coating solution was partially vulcanized by drying (dipping at 20 to 60 degrees at a mold temperature of 10 to 20 minutes or more) after dipping the primary coating solution into the mold, Followed by drying and curing.
비교예Comparative Example
3: 고온 건조에 의한 일부 가류 상태에서 2차 코팅하는 방법 3: Method of secondary coating in a state of partial vulcanization by high temperature drying
면장갑을 금형에 끼우고, 상기 1차 코팅액을 디핑한 후, 건조(금형 온도 60도 이상 4~10분 가류)하여 1차 코팅액 표면이 일부 가류가 이루어진 상태에서 상기 2차 코팅액을 디핑한 다음, 건조,가류 하였다.
The second coating solution was dipped in a state that the surface of the first coating solution was partially vulcanized by drying (mold temperature of 60 DEG C or higher for 4 to 10 minutes) after the first coating solution was dipped in the mold, Dried, and vulcanized.
실험예Experimental Example
1: 가류 전, 후의 박리현상 확인 1: Confirmation of peeling phenomenon before and after vulcanization
상기 실시예 1과 비교예 1~3을 통해 각각 제조한 코팅 면 장갑에 대하여, 가류 전과 가류 후에 1차 코팅층과 2차 코팅층이 분리되는 박리현상을 확인하였고, 그 결과를 하기 표 1에 나타내었다.The peeling phenomenon in which the primary coating layer and the secondary coating layer were separated from each other before and after vulcanization was confirmed for the coated cotton gloves manufactured through Example 1 and Comparative Examples 1 to 3 and the results are shown in Table 1 .
상기 표 1에 나타난 바와 같이, 실시예 1의 경우만 가류 전과 후에 박리현상이 없는 것으로 조사되었다. As shown in Table 1, only the case of Example 1 was found to have no peeling phenomenon before and after vulcanization.
즉, 1차 코팅 조성물과 2차 코팅 조성물의 층 분리 현상이 없도록 하기 위해서는, 1차 NR 라텍스 조성물에 의한 1차 코팅 표면이 약간 습한 겔링(미가류) 상태를 가질 때, 2차 NBR 라텍스 조성물로 2차 코팅하는 것이 바람직함을 확인할 수 있다.
That is, in order to avoid the layer separation phenomenon between the primary coating composition and the secondary coating composition, when the primary coating surface by the primary NR latex composition has a slightly wet gelled (unvulcanized) state, the secondary NBR latex composition It can be confirmed that secondary coating is preferable.
한편, 상기에서는 본 발명을 특정의 바람직한 실시예에 관련하여 도시하고 설명하였지만, 이하의 특허청구범위에 의해 마련되는 본 발명의 기술적 특징이나 분야를 이탈하지 않는 한도 내에서 본 발명이 다양하게 개조 및 변화될 수 있다는 것은 당업계에서 통상의 지식을 가진 자에게 명백한 것이다.
While the present invention has been particularly shown and described with reference to preferred embodiments thereof, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, It will be apparent to those skilled in the art that changes may be made.
Claims (4)
면 장갑에 상기 제1코팅액을 코팅하고, 상기 제1코팅액이 코팅된 코팅층에 상기 제2코팅액을 코팅하는 단계; 및
상기 제2코팅액이 코팅된 면 장갑을 건조시키는 단계;를 포함하는 면 장갑의 제조방법.
Preparing a first coating solution containing at least 50% by weight of natural rubber latex and a second coating solution containing at least 50% by weight synthetic rubber latex;
Coating the first coating liquid on the cotton glove, and coating the second coating liquid on the coating layer coated with the first coating liquid; And
And drying the face glove coated with the second coating liquid.
상기 코팅층은 겔 상태인 것을 특징으로 하는 면 장갑의 제조방법.
The method according to claim 1,
Wherein the coating layer is in a gel state.
상기 코팅하는 단계는,
몰드에 장착된 면 장갑에 상기 제1코팅액을 코팅하는 단계;
상기 몰드의 온도를 20~60℃ 범위 내로 하고, 상기 제1코팅액이 코팅된 면 장갑을 3~10분간 건조시키는 단계; 및
상기 건조에 의해 형성된 코팅층에 상기 제2코팅액을 코팅하는 단계;를 포함하는 것을 특징으로 하는 면 장갑의 제조방법.
The method according to claim 1,
Wherein the coating step comprises:
Coating the first coating liquid on a cotton glove mounted on a mold;
Drying the face glove coated with the first coating liquid for 3 to 10 minutes while setting the temperature of the mold within a range of 20 to 60 ° C; And
And coating the second coating liquid on the coating layer formed by the drying.
A process for producing a synthetic rubber latex, comprising the steps of: preparing a first coating layer containing at least 50% by weight of a natural rubber latex on the surface of cotton gloves, and a second coating layer containing at least 50% 2 < / RTI > coating layer are sequentially formed.