KR101401639B1 - 새로운 유기전계발광소자용 화합물 및 그를 포함하는 유기전계발광소자 - Google Patents

새로운 유기전계발광소자용 화합물 및 그를 포함하는 유기전계발광소자 Download PDF

Info

Publication number
KR101401639B1
KR101401639B1 KR1020120082429A KR20120082429A KR101401639B1 KR 101401639 B1 KR101401639 B1 KR 101401639B1 KR 1020120082429 A KR1020120082429 A KR 1020120082429A KR 20120082429 A KR20120082429 A KR 20120082429A KR 101401639 B1 KR101401639 B1 KR 101401639B1
Authority
KR
South Korea
Prior art keywords
group
compound
substituted
electroluminescent device
organic electroluminescent
Prior art date
Application number
KR1020120082429A
Other languages
English (en)
Other versions
KR20140014959A (ko
Inventor
현서용
윤용호
송정한
Original Assignee
(주)피엔에이치테크
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)피엔에이치테크 filed Critical (주)피엔에이치테크
Priority to KR1020120082429A priority Critical patent/KR101401639B1/ko
Publication of KR20140014959A publication Critical patent/KR20140014959A/ko
Application granted granted Critical
Publication of KR101401639B1 publication Critical patent/KR101401639B1/ko

Abstract

하기 구조식 1로 표시되는 유기전계발광소자용 화합물이 개시된다.
[구조식 1]
Figure 112012060318184-pat00047

본 발명에 따르면, 전기적 안정성 및 전자와 홀 수송능력이 우수하며, 삼중항 상태 에너지가 높아 인광발광재료의 발광효율을 향상 시킬 수 있는 유기발광소자용 화합물 및 이를 포함하는 유기전계발광소자를 제공할 수 있다.

Description

새로운 유기전계발광소자용 화합물 및 그를 포함하는 유기전계발광소자{NOVEL COMPOUND FOR ORGANIC ELECTROLUMINESCENT DEVICE AND ORGANIC ELECTROLUMINESCENT DEVICE COMPRISING THE SAME}
본 발명은 유기전계발광소자용 화합물 및 그를 포함하는 유기전계발광소자에 관한 것으로, 보다 상세하게는 효율이 높고 구동전압이 낮은 유기전계발광소자용 화합물 및 그를 포함하는 유기전계발광소자에 관한 것이다.
정보화 사회로의 움직임이 가속화되면서 평판 디스플레이의 비중이 점차 증가하고 있다. 그 중 LCD(Liquid Crystal Display)가 현재 가장 많이 쓰이고 있지만 액정에 전압을 가해 백라이트로부터의 빛을 컬러필터로 통과시켜 삼원색을 얻음으로써 화면을 만드는 방식이며, 유기EL(OLED; Organic Light Emitting Diodes)은 자체발광 소자로써 시야각 및 대조비 등이 우수하고, 경량 및 박형이 가능하며 휘는 성질의 기판에도 사용할 수 있어, 투명, 플렉서블 디스플레이가 가능하여 차세대 표시소자로서 주목을 받고 있다.
유기EL은 유기물 박막에 음극과 양극을 통하여 주입된 전자와 정공이 재결합을 통해 여기자를 형성하고, 형성된 그 여기자로부터 특정한 파장의 빛이 발생하는 현상으로 1963년 Pope 등에 의해 안트라센(anthracene)의 단결정으로부터 처음으로 발견되었고 이후 이스트만 코닥사의 탕(C.W Tang)등에 의해 적층형의 유기EL 소자의 보고(C.W Tang, S.A Vanslyke, Applied physics Letters. 51권 913p, 1987) 된 이후 활발히 연구 되고 있다.
유기전계발광소자에 사용되는 유기물질은 크게 고분자와 저분자 형태로 나누어지며 저분자는 순 유기물질과 메탈과 킬레이트를 형성한 메탈 콤플렉스로 나뉘어 질 수 있다.
고분자 물질은 다양한 기능의 유닛을 고분자 체인에 결합하여 다기능의 물질을 만들어 낼 수 있으나, 합성물 정제시나 소자 형성시 어려움이 있고, 저분자 물질은 각 특성의 물질을 합성 할 수 있으나 다기능의 특성을 나타내는 물질 합성에는 한계가 있다.
한편 유기전계발광소자를 적층구조로 형성할 수 있다. 적층구조의 장점으로는 각 기능에 맞게끔 물질을 선택하여 사용할 수 있는 것인데, 일반적으로 소자구조는 양극과 음극 사이에 정공주입층, 정공수송층, 발광층, 전자수송층, 전자주입층을 형성하여 발광층에서 여기자 형성을 쉽게 하고, 발광 효율을 높이게 되어 있다.
발광물질은 호스트물질과 발광물질(도판트)물질로 크게 나눌 수 있고, 발광물질은 발광 기작에 따라 형광과 인광으로 구별된다.
화합물 내 전자의 여기 상태는 일중항 대 삼중항의 비율이 1:3으로 삼중항 상태가 3배 정도 더 생성된다. 따라서, 일중항 상태에서 기저상태로 떨어지는 형광의 내부양자효율이 25%에 그치는 반면 삼중항 상태에서 기저상태로 떨어지는 인광의 내부양자효율은 75%이다. 또한 일중항 상태에서 삼중항 상태로 계간전이가 일어날 경우 내부양자효율의 이론적 한계치는 100%에 달한다. 이러한 점을 이용해 발광효율을 개선한 발광재료가 인광 발광재료이다.
유기물의 특성상 인광 발광은 어려움이 있어, 인광 발광재료로는 전이금속(이리듐)을 이용한 유기금속화합물이 개발되고 있으며, 이를 보조하는 호스트 물질로 유기물질이 이용되고 있다. 인광발광물질을 보조하는 물질(호스트)는 밴드갭이 넓고 삼중항 상태 에너지가 높아야 한다. 전류효율과 발광효율이 우수한 인광물질이 각광을 받고 있으나 전자 수송능력과 홀 수송능력, 열적, 전기적으로 안정하고 특히 삼중항 상태에너지가 높은 호스트 물질이 아직 없어 개발이 시급하다.
본 발명은 전기적 안정성 및 전자와 홀 수송능력이 우수하며, 삼중항 상태 에너지가 높아 인광발광재료의 발광효율을 향상시킬 수 있는 호스트로서 발광층에 사용 될 수 있는 유기발광소자용 화합물 및 이를 포함하는 유기전기발광소자를 제공할 수 있다.
또한 본 발명은 유기전기발광소자의 전자수송재료나, 홀수송재료에 사용될 수 있는 유기발광소자용 화합물 및 이를 포함하는 유기전기 발광소자를 제공할 수 있다.
본 발명의 일 측면에 따르면, 하기 구조식 1로 표시되는 유기전계발광소자용 화합물이 제공될 수 있다.
[구조식 1]
Figure 112012060318184-pat00001
상기 구조식 1에서,
R1 및 R2는 서로 같거나 다를 수 있고, R1 및 R2는 각각 독립적으로 수소원자,
Figure 112012060318184-pat00002
치환 또는 비치환된 C1 내지 C30의 알킬기, 치환 또는 비치환된 C3 내지 C30 시클로알킬기, 치환 또는 비치환된 C6 내지 C30 아릴기, 또는 치환 또는 비치환된 C1 내지 C30 헤테로 아릴기이거나, 또는 R1 및 R2는 중 어느 하나는 그 어느 하나가 결합된 탄소원자의 이웃한 탄소원자와 추가로 결합하여 치환 또는 비치환된 융합된 C6 내지 C30 아릴기 또는 치환 또는 비치환된 융합된 C1 내지 C30 헤테로 아릴기를 형성할 수 있고,
Ar1 및 Ar2는 서로 같거나 다를 수 있고, Ar1 및 Ar2는 각각 독립적으로 치환 또는 비치환된 C6 내지 C30 아릴기, 치환 또는 비치환된 C1 내지 C30 헤테로아릴기, 또는 치환 또는 비치환된 C3 내지 C30 시클로알킬기이거나, 또는 Ar1 및 Ar2는 서로 결합되고 그들 사이의 질소원자와 함께 치환 또는 비치환된 C2 내지 C30 헤테로 아릴기 또는 치환 또는 비치환된 C3 내지 C30 시클로알킬기를 형성할 수 있고,
Ar3 내지 Ar5는 서로 같거나 다를 수 있고, Ar3 내지 Ar5는 각각 독립적으로 치환 또는 비치환된 C6 내지 C30 아릴기, 치환 또는 비치환된 C1 내지 C30 헤테로아릴기, 또는 치환 또는 비치환된 C3 내지 C30 시클로알킬기이고,
R9 내지 R31은 서로 같거나 다를 수 있고, R9 내지 R31은 각각 독립적으로 수소원자, 치환 또는 비치환된 C1 내지 C30 알킬기, 치환 또는 비치환된 C3 내지 C30 시클로알킬기, 치환 또는 비치환된 C6 내지 C30 아릴기, 또는 치환 또는 비치환된 C1 내지 C30 헤테로아릴기이거나, 또는 R9 내지 R31 중 어느 하나는 그 어느 하나가 결합된 탄소원자의 이웃한 탄소원자와 추가로 결합하여 치환 또는 비치환된 융합된 C6 내지 C30 아릴기 또는 치환 또는 비치환된 융합된 C2 내지 C30 헤테로 아릴기를 형성할 수 있고,
Y1 내지 Y3은 서로 같거나 다를 수 있고, Y1 내지 Y3은 각각 독립적으로 산소원자 또는 황원자이고,
m은 0 또는 1이고,
R3 내지 R8은 서로 같거나 다를 수 있고, R3 내지 R8은 각각 독립적으로 수소원자, 치환 또는 비치환된 C1 내지 C30의 알킬기, 치환 또는 비치환된 C3 내지 C30 시클로알킬기, 치환 또는 비치환된 C6 내지 C30 아릴기, 또는 치환 또는 비치환된 C1 내지 C30 헤테로 아릴기이거나, 또는 R3 내지 R8 중 어느 하나는 그 어느 하나가 결합된 탄소원자의 이웃한 탄소원자와 추가로 결합하여 치환 또는 비치환된 융합된 C6 내지 C30 아릴기 또는 치환 또는 비치환된 융합된 C1 내지 C30 헤테로 아릴기를 형성할 수 있다.
본 발명의 다른 측면에 따르면, 하기 구조식 1로 표시되는 유기전계발광소자용 화합물이 제공될 수 있다.
[구조식 1]
Figure 112012060318184-pat00003
상기 구조식 1에서,
R1 및 R2는 서로 같거나 다를 수 있고, 각각 독립적으로 아래 화학식 U1 내지 U58 중에서 선택된 어느 하나이고,
m은 0 또는 1이고,
R3 내지 R8은 서로 같거나 다를 수 있고, R3 내지 R8은 각각 독립적으로 수소원자, 치환 또는 비치환된 C1 내지 C30의 알킬기, 치환 또는 비치환된 C3 내지 C30 시클로알킬기, 치환 또는 비치환된 C6 내지 C30 아릴기, 또는 치환 또는 비치환된 C1 내지 C30 헤테로 아릴기이거나, 또는 R3 내지 R8 중 어느 하나는 그 어느 하나가 결합된 탄소원자의 이웃한 탄소원자와 추가로 결합하여 치환 또는 비치환된 융합된 C6 내지 C30 아릴기 또는 치환 또는 비치환된 융합된 C1 내지 C30 헤테로 아릴기를 형성할 수 있다.
Figure 112012060318184-pat00004
Figure 112012060318184-pat00006
본 발명의 다른 측면에 따르면, 하기 구조식 1 내지 38, 바람직하게는 1내지 22로 표시되는 화합물 중에서 선택된 어느 하나인 유기전계발광소자용 화합물이 제공될 수 있다.
Figure 112012060318184-pat00007
Figure 112012060318184-pat00008
Figure 112012060318184-pat00009
Figure 112012060318184-pat00010
Figure 112012060318184-pat00011
본 발명의 또 다른 측면에 따르면, 본 발명에 따른 유기전계발광소자용 화합물을 포함하는 유기전계발광소자가 제공될 수 있다.
본 발명의 또 다른 측면에 따르면, 제1전극, 제2전극 및 제1전극과 제2전극 사이에 단수 또는 복수의 유기물층을 포함하는 유기전계발광소자에 있어서, 상기 단수 또는 복수의 유기물층 중에서 선택된 1종 이상의 유기물층은 본 발명에 따른 유기전계발광소자용 화합물을 포함하는 것을 특징으로 하는 유기전계발광소자가 제공될 수 있다.
본 발명에서 상기 복수의 유기물층은 발광층을 포함할 수 있고, 상기 복수의 유기물층은 전자주입층, 전자수송층, 정공차단층, 전자차단층, 정공수송층, 및 정공주입층 중에서 선택된 1종 이상을 추가로 포함할 수 있다.
본 발명에서 상기 정공수송층 및 정공주입층 중에서 선택된 1종 이상은 본 발명에 따른 유기전계발광소자용 화합물을 포함할 수 있다.
본 발명에서 상기 발광층은 호스트와 도펀트를 포함할 수 있고, 상기 호스트는 본 발명에 따른 유기전계발광소자용 화합물을 포함할 수 있다.
본 발명은 전기적 안정성 및 전자와 홀 수송능력이 우수하며, 삼중항 상태 에너지가 높아 인광발광재료의 발광효율을 향상시킬 수 있는 호스트로서 발광층에 사용 될 수 있는 유기발광소자용 화합물 및 이를 포함하는 유기전기발광소자를 제공할 수 있다.
또한 본 발명은 유기전기발광소자의 전자수송재료나, 홀수송 재료에 사용될 수 있는 유기발광소자용 화합물 및 이를 포함하는 유기전기 발광소자를 제공할 수 있다.
도 1은 본 발명의 일 실시예에 따른 유기전계발광소자의 단면을 나타낸 단면도이다.
도 2는 본 발명의 다른 일 실시예에 따른 유기전계발광소자의 단면을 나타낸 단면도이다.
본 발명은 다양한 변환을 가할 수 있고 여러 가지 실시예를 가질 수 있는 바, 특정 실시예들을 예시하고 상세한 설명에 상세하게 설명하고자 한다. 그러나, 이는 본 발명을 특정한 실시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변환, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다. 본 발명을 설명함에 있어서 관련된 공지 기술에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우 그 상세한 설명을 생략한다.
또한, 이하에서 사용될 제1, 제2 등과 같이 서수를 포함하는 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 상기 구성요소들은 상기 용어들에 의해 한정되지는 않는다. 상기 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다. 예를 들어, 본 발명의 권리 범위를 벗어나지 않으면서 제1 구성요소는 제2 구성요소로 명명될 수 있고, 유사하게 제2 구성요소도 제1 구성요소로 명명될 수 있다.
또한, 어떤 구성요소가 다른 구성요소 상에 "형성되어" 있다거나 "적층되어" 있다고 언급된 때에는, 그 다른 구성요소의 표면상의 전면 또는 일면에 직접 부착되어 형성되어 있거나 적층되어 있을 수도 있지만, 중간에 다른 구성요소가 더 존재할 수도 있다고 이해되어야 할 것이다.
단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 출원에서, "포함하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.
본 명세서에서 "치환"이란 별도의 정의가 없는 한, 치환기 또는 화합물 중의 적어도 하나의 수소가 중수소, 할로겐기, 히드록시기, 아미노기, C1 내지 C30 아민기, 니트로기, C1 내지 C30 실릴기, C1 내지 C30 알킬기, C1 내지 C30 알킬실릴기, C3 내지 C30 시클로알킬기, C1 내지 C30 헤테로시클로알킬기, C6 내지 C30 아릴기, C1 내지 C30 헤테로 아릴기, C1 내지 C20 알콕시기, C1 내지 C10 트리플루오로알킬기 또는 시아노기로 치환된 것을 의미한다.
또한 상기 치환된 할로겐기, 히드록시기, 아미노기, C1 내지 C30 아민기, C3 내지 C30 실릴기, C1 내지 C30 알킬기, C1 내지 C30 알킬실릴기, C3 내지 C30 시클로알킬기, C6 내지 C30 아릴기, C1 내지 C20 알콕시기, C1 내지 C10 트리플루오로알킬기 또는 시아노기 중 인접한 두 개의 치환기가 융합되어 고리를 형성할 수도 있다.
본 명세서에서 "헤테로"란 별도의 정의가 없는 한, 하나의 작용기 내에 N, O, S 및 P로 이루어진 군에서 선택되는 헤테로 원자를 1 내지 4개 함유하고, 나머지는 탄소인 것을 의미한다.
본 명세서에서 "이들의 조합"이란 별도의 정의가 없는 한, 둘 이상의 치환기가 연결기로 결합되어 있거나, 둘 이상의 치환기가 축합하여 결합되어 있는 것을 의미한다.
본 명세서에서 "알킬(alkyl)기"란 별도의 정의가 없는 한, 지방족 탄화수소기를 의미한다.
알킬기는 어떠한 이중결합이나 삼중결합을 포함하고 있지 않은 "포화 알킬(saturated alkyl)기" 일 수 있다.
알킬기는 적어도 하나의 이중결합 또는 삼중결합을 포함하고 있는 "불포화 알킬(unsaturated alkyl)기"일 수도 있다.
"알케닐렌(alkenylene)기"는 적어도 두 개의 탄소원자가 적어도 하나의 탄소-탄소 이중 결합으로 이루어진 작용기를 의미하며, "알키닐렌(alkynylene)기" 는 적어도 두 개의 탄소원자가 적어도 하나의 탄소-탄소 삼중 결합으로 이루어진 작용기를 의미한다. 포화이든 불포화이든 간에 알킬기는 분지형, 직쇄형 또는 환형일 수 있다.
알킬기는 C1 내지 C30 알킬기일 수 있다. 보다 구체적으로 알킬기는 C1 내지 C20 알킬기, C1 내지 C10 알킬기 또는 C1 내지 C6 알킬기일 수도 있다.
예를 들어, C1 내지 C4 알킬기는 알킬쇄에 1 내지 4 개의 탄소원자, 즉, 알킬쇄는 메틸, 에틸, 프로필, 이소-프로필, n-부틸, 이소-부틸, sec-부틸 및 t-부틸로 이루어진 군에서 선택됨을 나타낸다.
구체적인 예를 들어 상기 알킬기는 메틸기, 에틸기, 프로필기, 이소프로필기, 부틸기, 이소부틸기, t-부틸기, 펜틸기, 헥실기, 에테닐기, 프로페닐기, 부테닐기, 시클로프로필기, 시클로부틸기, 시클로펜틸기, 시클로헥실기 등을 의미한다.
"아민기"는 아릴아민기, 알킬아민기, 아릴알킬아민기, 또는 알킬아릴아민기를 포함한다.
"시클로알킬(cycloalkyl)기"는 모노시클릭 또는 융합고리 폴리시클릭(즉, 탄소원자들의 인접한 쌍들을 나눠 가지는 고리) 작용기를 포함한다.
"헤테로시클로알킬(heterocycloalkyl)기"는 시클로알킬기 내에 N, O, S 및 P로 이루어진 군에서 선택되는 헤테로원자를 1 내지 4개 함유하고, 나머지는 탄소인 것을 의미한다. 상기 헤테로시클로알킬기가 융합고리인 경우, 각각의 고리마다 상기 헤테로 원자를 1 내지 4개 포함할 수 있다.
"방향족(aromatic)기"는 고리 형태인 작용기의 모든 원소가 p-오비탈을 가지고 있으며, 이들 p-오비탈이 공액(conjugation)을 형성하고 있는 작용기를 의미한다. 구체적인 예로 아릴기와 헤테로아릴기가 있다.
"아릴(aryl)기"는 모노시클릭 또는 융합 고리 폴리시클릭(즉, 탄소원자들의 인접한 쌍들을 나눠 가지는 고리) 작용기를 포함한다.
"헤테로아릴(heteroaryl)기"는 아릴기 내에 N, O, S 및 P로 이루어진 군에서 선택되는 헤테로원자를 1 내지 4개 함유하고, 나머지는 탄소인 것을 의미한다. 상기 헤테로아릴기가 융합고리인 경우, 각각의 고리마다 상기 헤테로 원자를 1 내지 4개 포함할 수 있다.
아릴기 및 헤테로아릴기에서 고리의 원자수는 탄소수 및 비탄소원자수의 합이다.
"알킬아릴기" 또는 "아릴알킬기"와 같이 조합하여 사용할 때, 상기에 든 각각의 알킬 및 아릴의 용어는 상기 나타낸 의미와 내용을 가진다.
"아릴알킬기"이란 용어는 벤질과 같은 아릴 치환된 알킬 라디칼을 의미하며 알킬기에 포함된다.
"알킬아릴기"이란 용어는 알킬 치환된 아릴 라디칼을 의미하며 아릴기에 포함된다.
이하, 본 발명의 실시예를 첨부도면을 참조하여 설명하기로 하며, 첨부 도면을 참조하여 설명함에 있어, 동일하거나 대응하는 구성 요소는 동일한 도면번호를 부여하고 이에 대한 중복되는 설명은 생략하기로 한다.
이하 본 발명의 유기전계발광소자에 대해 설명하도록 한다.
도 1 및 2를 참고하면, 본 발명의 실시예에 따르면 본 발명에 따른 유기전계발광소자용 화합물을 포함하는 유기전계발광소자(1)가 제공될 수 있다.
또한 본 발명의 다른 실시예에 따르면, 제1전극(110), 제2전극(150) 및 제1전극(110)과 제2전극(150) 사이에 단수 또는 복수의 유기물층(130)을 포함하는 유기전계발광소자(1)에 있어서, 상기 단수 또는 복수의 유기물층(130) 중에서 선택된 1종 이상의 유기물층은 본 발명에 따른 유기전계발광소자용 화합물을 포함할 수 있다.
여기서, 상기 복수의 유기물층(130)은 발광층(134)을 포함하고, 상기 복수의 유기물층은 전자주입층(131), 전자수송층(132), 정공차단층(133), 전자차단층(135), 정공수송층(136) 및 정공주입층(137) 중에서 선택된 1종 이상을 추가로 포함할 수 있다.
또한 전자주입층(131), 전자수송층(132), 정공차단층(133), 전자차단층(135), 정공수송층(136) 및 정공주입층(137) 중에서 선택된 1종 이상은 본 발명의 유기전계발광소자용 화합물을 포함할 수 있다.
또한 바람직하게는 상기 정공수송층(136) 및 정공주입층(137) 중에서 선택된 1종 이상은 본 발명에 따른 유기전계발광소자용 화합물을 포함할 수 있다.
또한 상기 발광층(134)은 호스트와 도펀트를 포함하고, 상기 호스트는 본 발명에 따른 유기전계발광소자용 화합물을 포함할 수 있다.
상기 유기전계발광소자는 바람직하게는 투명기판에 의하여 지지된다. 투명기판의 재료로는 양호한 기계적 강도, 열안정성 및 투명성을 갖는 한 특별한 제한은 없다. 구체적인 예를 들면, 유리, 투명 플라스틱 필름 등을 사용할 수 있다.
본 발명의 유기전계발광소자의 양극재료로서는 4eV 이상의 일함수를 갖는 금속, 합금, 전기전도성 화합물 또는 이의 혼합물을 사용할 수 있다. 구체적으로는 금속인 Au 또는 CuI, ITO(인듐 주석 산화물), SnO2 및 ZnO와 같은 투명 전도성 재료를 들 수 있다. 양극 필름의 두께는 10 내지 200nm 가 바람직하다.
본 발명의 유기전계발광소자의 음극 재료로서는 4eV 미만의 일함수를 갖는 금속, 합금, 전기 전도성 화합물 또는 이의 혼합물을 사용할 수 있다. 구체적으로는, Na, Na-K 합금, 칼슘, 마그네슘, 리튬, 리튬 합금, 인듐, 알루미늄, 마그네슘 합금, 알루미늄 합금을 들 수 있다. 이외에, 알루미늄/AlO2, 알루미늄/리튬, 마그네슘/은 또는 마그네슘/인듐 등도 사용될 수 있다. 음극필름의 두께는 10 내지 200nm 가 바람직하다.
유기 EL 소자의 발광효율을 높이기 위해서는 하나 이상의 전극은 바람직하게는 10% 이상의 광투과율을 가지는 것이 바람직하다. 전극의 쉬트저항은 바람직하게는 수백 Ω/mm 이하이다. 전극의 두께는 10nm 내지 1㎛, 보다 바람직하게는 10 내지 400nm 이다. 이러한 전극은 화학적 기상증착(CVD), 물리적 기상증착(PVD) 등의 기상증착법 또는 스퍼터링법을 통하여 상기한 전극 재료를 박막으로 형성하여 제조할 수 있다.
또한 본 발명의 목적에 적합하게 본 발명의 유기전계발광소자용 화합물이 사용될 때, 공지된 정공수송 물질, 정공주입 물질, 발광층 물질, 발광층의 호스트 물질, 전자수송 물질, 및 전자주입 물질이 상기 각각의 유기물층에서 단독으로 사용되거나 또는 본 발명의 유기전계발광소자용 화합물과 선택적으로 병행하여 사용될 수 있다.
정공 수송 물질로서 N,N-dicarbazolyl-3,5-benzene(mCP), poly(3,4-ethylenedioxythiophene):polystyrenesulfonate (PEDOT:PSS), N, N’-di(1-naphthyl)-N,N’-diphenylbenzidine(NPD), N,N'-디페닐-N,N'-디(3-메틸페닐)-4,4'-디아미노비페닐(TPD), N,N'-디페닐-N,N'-디나프틸-4,4'-디아미노비페닐, N,N,N'N'-테트라-p-톨릴-4,4'-디아미노비페닐, N,N,N'N'-테트라페닐-4,4'-디아미노비페닐, 코퍼(II)1,10,15,20-테트라페닐-21H,23H-포피린 등과 같은 포피린(porphyrin)화합물 유도체, 주쇄 또는 측쇄내에 방향족 3차아민을 갖는 중합체, 1,1-비스(4-디-p-톨릴아미노페닐)시클로헥산, N,N,N-트리(p-톨릴)아민, 4, 4', 4'-트리스[N-(3-메틸페닐)-N-페닐아미노]트리페닐아민과 같은 트리아릴아민 유도체, N-페닐카르바졸 및 폴리비닐카르바졸과 같은 카르바졸 유도체, 무금속 프탈로시아닌, 구리프탈로시아닌과 같은 프탈로시아닌 유도체, 스타버스트 아민 유도체, 엔아민스틸벤계 유도체, 방향족 삼급아민과 스티릴 아민 화합물의 유도체, 및 폴리실란 등을 들 수 있다.
전자 수송 물질로서 diphenylphosphine oxide-4-(triphenylsilyl)phenyl (TSPO1), Alq3, 2,5-디아릴 실롤 유도체(PyPySPyPy), 퍼플루오리네이티드 화합물(PF-6P), Octasubstituted cyclooctatetraene 화합물(COTs)을 들 수 있다.
본 발명의 유기전계발광소자에 있어서, 전자 주입층, 전자 수송층, 정공 수송층 및 정공 주입층은 상기한 화합물의 하나 이상의 종류를 함유하는 단일 층으로 형성되거나, 또는 상호 적층된, 상이한 종류의 화합물을 함유하는 복수의 층으로 구성될 수 있다.
발광재료로서 예를 들면 축광 형광재료, 형광증백제, 레이저 색소, 유기 신틸레이터 및 형광 분석용 시약을 들 수 있다. 구체적으로는, 카바졸계 화합물, 포스핀옥사이드계 화합물, 카바졸계 포스핀옥사이드 화합물, bis((3,5-difluoro-4-cyanophenyl)pyridine) iridium picolinate(FCNIrpic), tris(8-hydroxyquinoline) aluminum(Alq3), 안트라센, 페난트렌, 피렌, 크리센, 페릴렌, 코로넨, 루브렌 및 퀴나크리돈과 같은 폴리아로마틱 화합물, 퀴터페닐과 같은 올리고페닐렌 화합물, 1,4-비스 (2-메틸스티릴)벤젠, 1,4-비스(4-메틸스티릴)벤젠, 1,4-비스(4-메틸-5-페닐-2-옥사졸릴)벤젠, 1,4-비스(5-페닐-2-옥사졸릴)벤젠, 2,5-비스(5-t-부틸-2-벤즈옥사졸릴)사이오펜, 1,4-디페닐-1,3-부타디엔, 1,6-디페닐-1,3,5-헥사트리엔,1,1,4,4-테트라페닐-1,3-부타디엔과 같은 액체신틸레이션용 신틸레이터, 옥신 유도체의 금속착체, 쿠마린 색소, 디시아노메틸렌피란 색소, 디시아노메틸렌사이오피란 색소, 폴리메틴 색소, 옥소벤즈안트라센 색소, 크산텐 색소, 카르보스티릴 색소, 페릴렌 색소, 옥사진 화합물, 스틸벤 유도체, 스피로 화합물, 옥사디아졸 화합물 등을 들 수 있다.
본 발명의 유기 EL 소자를 구성하는 각 층은 진공 증착, 스핀 코팅 또는 캐스팅과 같은 공지된 방법을 통하여 박막으로 형성시키거나, 각 층에서 사용되는 재료를 이용하여 제조할 수 있다. 이들 각층의 막 두께에 대해서는 특별한 제한은 없으며, 재료의 특성에 따라 알맞게 선택할 수 있으나, 보통 2nm 내지 5,000nm의 범위에서 결정될 수 있다.
본 발명의 따른 유기전계발광소자용 화합물은 진공 증착법에 의하여 형성될 수 있으므로, 박막 형성 공정이 간편하고, 핀홀(pin hole)이 거의 없는 균질한 박막으로 용이하게 얻을 수 있는 장점이 있다.
[실시예]
이하, 실시예를 통하여 본 발명에 따른 유기전계발광소자용 화합물 및 이를 포함하는 유기전계발광소자의 제조방법을 더욱 구체적으로 설명한다. 그러나 이는 예시를 위한 것으로서 이에 의하여 본 발명의 범위가 한정되는 것이 아니다.
실시예 1: 화합물 1의 합성
(1) 제조예 1-1 : 중간체 1-1 합성
Figure 112012060318184-pat00012
9-bromo-9-phenyl-9H-fluorene(15.13g, 0.0471mol/시그마알드리치)을 정제된 THF용액 500ml에 녹인 후 질소 환류 하에서 -78℃로 낮추고, n-BuLi (3.02g, 0.047mol)을 적가한 후 2시간 동안 교반시켜 주었다. 그 후 트리메틸보레이트(8.31g, 0.08mol/시그마알드리치)를 저온에서 천천히 넣어 준 후 온도를 상승시켜 상온에서 24시간 교반하여 반응시켰다. 염산(10M)을 넣어(리트머스 종이로 확인) 중화 후 반응을 종료 하였다. 디클로로메탄으로 추출한 후 헥산으로 재결정 하여 중간체 1-1을 5.39g수득하였다. (수율: 40%)
(2) 제조예 1-2 : 중간체 1-2 합성
Figure 112012060318184-pat00013
중간체 1-1 (18.65g, 0.0652mol), 2,4-dibromo-1,3,5-triazine (7.78g, 0.0326mol)에 Pd2(PPh3)4 (1.1g, 0.000978mol), Toluene 400ml를 넣고 교반 후 Na2CO3 13.8g(4당량, 0.130mol)을 수용액 상으로 투입하여 80℃로 승온하여 6시간 반응시켰다. 반응 종료 후 물과 MC로 추출한 후 MeOH로 Washing 하고 칼럼 정제(n-Hexane : methylene chloride)하여 중간체 1-2를 14.65g 수득하였다.(수율: 80%)
(3) 제조예 1-3 : 화합물 1 합성
Figure 112012060318184-pat00014
중간체 1-2 (13.2g, 0.0235mol)에 2-(4-bromophenyl)triphenylene (9g, 0.0235mol/TCI)과 촉매 Copper(II) (0.15g, 0.00235mol)과 Sodium hydride (0.6g, 0.0235mol), n-Hexane 750ml를 넣고 상온에서 반응시켰다. 반응 혼합물을 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 1을 12.18g 수득하였다.(수율: 60%)
H-NMR(200MHz, CDCl3): δ ppm, 1H (9.15/S, 8.04/D, 8.18/D) 2H 7.26/M, 7.85/D, 7.25/D, 8.93/D, 7.88/M, 7.82/M, 8.12/D) 4H (7.55/D, 7.28/M, 7.38/M, 7.87/D, 7.11/D, 7.33/M)
LC/Mass [M+H]+: 863.04
실시예 2: 화합물 2의 합성
Figure 112012060318184-pat00015
중간체 1-2 (13.2g, 0.0235mol)에 2-(4-bromophenyl)-1-phenyl-1H-benzo[d]imidazole (8.2g, 0.0235mol/시그마알드리치)과 촉매 Copper(II) (0.15g, 0.00235mol)과 Sodium hydride (0.6g, 0.0235mol)을 n-Hexane 700ml를 넣고 상온에서 반응한다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 2을 10.92g수득하였다.(수율 56%)
H-NMR(200MHz, CDCl3): δ ppm, 1H (7.45/M, 8.56/D, 7.59/D) 2H (7.26/M, 7.58/M, 7.50/D, 7.22/M) 4H (7.55/D, 7.28/M, 7.38/M, 7.87/D, 7.33/M, 7.11/D, 7.85/D)
LC/Mass [M+H]+: 828.99
실시예 3: 화합물 3의 합성
Figure 112012060318184-pat00016
중간체 1-2 (13.2g, 0.0235mol)에 3-(4-bromophenyl)dibenzo[b,d]thiophene (7.97g, 0.0235mol/중국)과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride (0.6g, 0.0235mol), n-Hexane 700ml를 넣고 상온에서 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 3을 9.63g 수득하였다.(수율: 50%)
H-NMR(200MHz, CDCl3): δ ppm, 1H (8.08/S, 8.05/D, 8.11/D, 7.98/D, 7.50/M, 7.52/M, 8.45/D) 2H (7.85/D, 7.25/D, 7.26/M) 4H(7.55/D, 7.28/M, 7.38/M, 7.87/D, 7.11/D, 7.33/M)
LC/Mass [M+H]+: 819.01
실시예 4: 화합물 4의 합성
Figure 112012060318184-pat00017
중간체 1-2 (13.2g, 0.0235mol)에 N-(4-bromophenyl)-N-phenyldibenzo[b,d]thiophen-4-amine (10.11g, 0.0235mol/시안(중국))과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride (0.6g, 0.0235mol), n-Hexane 1000ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 4를 7.06g 수득하였다.(수율: 33%)
H-NMR(200MHz, CDCl3): δ ppm, 1H (6.81/M, 6.86/D, 7.27/M, 7.81/D, 7.98/D, 7.50/M, 7.52/M, 8.45/D) 2H (7.26/M, 7.90/D, 6.69/D, 6.63/D, 7.20/M) 4H (7.55/D, 7.28/M, 7.38/M, 7.87/D, 7.11/D, 7.33/M)
LC/Mass [M+H]+: 910.12
실시예 5: 화합물 5의 합성
Figure 112012060318184-pat00018
중간체 1-2 (13.2g, 0.0235mol)에 4-(3-bromophenyl)dibenzo[b,d]thiophene (7.97g, 0.0235mol/시그마알드리치)과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride (0.6g, 0.0235mol), n-Hexane 700ml을 넣고 상온에서 4시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 5를 11.75g 수득하였다.(수율: 61%)
H-NMR(200MHz, CDCl3): δ ppm, 1H (8.24/D, 7.57/M, 7.48/D, 7.70/S, 8.20/D, 7.58/M, 8.41/D, 7.98/D, 7.50/M, 7.52/M, 8.45/D) 2H (7.26/M) 4H (7.55/D, 7.28/M, 7.38/M, 7.87/D, 7.11/D, 7.33/M)
LC/Mass [M+H]+: 819.01
실시예 6: 화합물 6의 합성
Figure 112012060318184-pat00019
중간체 1-2 (13.2g, 0.0235mol)에 N-(4-bromophenyl)-N-phenyl-(dipyrole)thiophen(9.24g, 0.0235mol/중국)과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride (0.6g, 0.0235mol), n-Hexane 1000ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 6을 14.38g 수득하였다.(수율: 70%)
H-NMR(200MHz, CDCl3): δ ppm, 2H (7.26/M, 7.79/D, 7.68/D, 7.26/D, 6.19/D, 7.50/D, 7.58/M, 7.45/M) 4H (7.55/D, 7.28/M, 7.38/M, 7.87/D, 7.11/D, 7.33/M)
LC/Mass [M+H]+: 873.06
실시예 7: 화합물 7의 합성
Figure 112012060318184-pat00020
중간체 1-2 (13.2g, 0.0235mol)에 N-(biphenyl-4-yl)-N-(4-bromophenyl)-9,9-dimethyl-9H-fluoren-2-amine(12.14g, 0.0235mol/시안(중국))과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride (0.6g, 0.0235mol), n-Hexane 1000ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 7을 16.64g 수득하였다.(수율: 71%)
H-NMR(200MHz, CDCl3): δ ppm, 1H (6.58/D, 7.62/D, 6.75/S, 1.72/S) 2H (7.26/M, 7.90/D, 7.54/D, 7.52/D, 7.51/M, 7.41/M) 4H (6.69/D, 7.11/D, 7.33/M) 5H (7.55/D, 7.28/M, 7.38/M, 7.87/D)
LC/Mass [M+H]+: 996.23
실시예 8: 화합물 8의 합성
Figure 112012060318184-pat00021
중간체 1-2 (13.2g, 0.0235mol)에 N-(4-bromophenyl)-N-(dibenzo[b,d]thiophen-4-yl)dibenzo[b,d]thiophen-4-amine(12.6g, 0.0235mol/중국)과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride (0.6g, 0.0235mol), n-Hexane 1000ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 7을 12.67g 수득하였다.(수율: 53%)
H-NMR(200MHz, CDCl3): δ ppm, 2H (7.26/M, 7.90/D, 6.69/D, 6.86/D, 7.27/M, 7.81/D, 8.45/D, 7.52/M, 7.50/M, 7.98/D) 4H (7.55/D, 7.28/M, 7.38/M, 7.87/D, 7.11/D, 7.33/M)
LC/Mass [M+H]+: 1016.27
실시예 9: 화합물 9의 합성
Figure 112012060318184-pat00022
중간체 1-2 (13.2g, 0.0235mol)에 2-(4-bromophenyl)-1-phenyl-1H-dibenzo[e,g]indole(10.53g, 0.0235mol/중국)과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride(0.6g, 0.0235mol), n-Hexane 1000ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 9를 10.91g 수득하였다.(수율: 50%)
H-NMR(200MHz, CDCl3): δ ppm, 1H (6.60/S, 7.45/M) 2H (7.26/M, 7.85/D, 8.30/D, 7.50/D, 7.58/M, 7.88/M, 8.93/D, 7.82/M, 8.12/D) 4H (7.55/D, 7.28/M, 7.38/M, 7.87/D, 7.11/D, 7.33/M)
LC/Mass [M+H]+: 928.11
실시예 10: 화합물 10의 합성
Figure 112012060318184-pat00023
중간체 1-2 (13.2g, 0.0235mol)에 6-(4-bromophenyl)-5-phenyl-5H-pyrrolo[3,2-f][1,10]phenanthroline(10.58g, 0.0235mol/중국)과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride(0.6g, 0.0235mol), n-Hexane 1000ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 10을 9.85g 수득하였다.(수율: 45%)
H-NMR(200MHz, CDCl3): δ ppm, 1H (6.60/S, 7.45/M) 2H (7.26/M, 7.85/D, 8.30/D, 7.50/D, 8.83/D, 8.38/D) 4H (7.55/D, 7.28/M, 7.38/M, 7.87/D, 7.11/D, 7.33/M, 7.58/M)
LC/Mass [M+H]+: 930.09
실시예 11: 화합물 11의 합성
Figure 112012060318184-pat00024
중간체 1-2 (13.2g, 0.0235mol)에 4-bromobiphenyl(D:중수소)(5.6g, 0.0235mol/중국)과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride (0.6g, 0.0235mol), n-Hexane 1000ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 11을 13.48g 수득하였다.(수율 75%)
H-NMR(200MHz, CDCl3): δ ppm, 2H (7.26/M, 7.85/D, 7.25/D) 4H (7.55/D, 7.28/M, 7.38/M, 7.87/D, 7.11/D, 7.33/M)
LC/Mass [M+H]+: 717.90
실시예 12: 화합물 12의 합성
Figure 112012060318184-pat00025
중간체 1-2 (13.2g, 0.0235mol)에 2-(4-bromophenyl)pyrido[2,3-f][1,7]phenanthroline(9.07g, 0.0235mol/시그마알드리치)과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride (0.6g, 0.0235mol), n-Hexane 700ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 12를 12.22g 수득하였다.(수율: 55%)
H-NMR(200MHz, CDCl3): δ ppm, 1H (7.35/D, 8.10/D) 2H 7.26/M, 7.88/D, 8.81/D, 8.38/D, 8.83/D, 7.58/M) 4H (7.11/D, 7.28/M, 7.38/M, 7.33/M, 7.55/D, 7.87/D)
LC/Mass [M+H]+: 866.01
실시예 13: 화합물 13의 합성
Figure 112012060318184-pat00026
중간체 1-2 (13.2g, 0.0235mol)에 N-(4-bromophenyl)-N-(pyridin-3-yl)pyridin-3-amine(7.66g, 0.0235mol/시그마알드리치)과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride (0.6g, 0.0235mol), n-Hexane 700ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 13을 18.96g 수득하였다.(수율: 60%)
H-NMR(200MHz, CDCl3): δ ppm, 2H (7.26/M, 7.90/D, 6.69/D, 8.04/S, 8.09/D, 7.27/D, 7.36/M) 4H (7.11/D, 7.28/M, 7.33/M, 7.38/M, 7.55/D, 7.87/D)
LC/Mass [M+H]+: 805.95
실시예 14: 화합물 14의 합성
Figure 112012060318184-pat00027
중간체 1-2 (13.2g, 0.0235mol)에 N-(2,3'-bipyridin-5-yl)-N-(4-bromophenyl)-2,3'-bipyridin-5-amine(11.29g, 0.0235mol/시그마알드리치)과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride (0.6g, 0.0235mol), n-Hexane 700ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 14를 13.55g 수득하였다.(수율: 60%)
H-NMR(200MHz, CDCl3): δ ppm, 2H (7.26/D, 7.90/D, 6.69/D, 7.71/S, 9.75/S, 8.76/D, 7.60/M, 8.93/D, 8.05/D, 7.16/D) 4H (7.11/D, 7.28/M, 7.38/M, 7.33/M, 7.55/D, 7.87/D)
LC/Mass [M+H]+: 960.12
실시예 15: 화합물 15의 합성
Figure 112012060318184-pat00028
중간체 1-2 (13.2g, 0.0235mol)에 (4-bromophenyl)(bipyridin-3-yl)-4-thiopen(8.01g, 0.0235mol/중국)과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride (0.6g, 0.0235mol), n-Hexane 700ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 15를 11.59g 수득하였다.(수율: 60%)
H-NMR(200MHz, CDCl3): δ ppm, 1H (7.38/D, 8.43/D, 9.51/S, 8.98/S, 9.24/S) 2H (7.26/M, 7.85/D, 7.25/D) 4H (7.11/D, 7.28/M, 7.38/M, 7.33/M, 7.55/D, 7.87/D)
LC/Mass [M+H]+: 820.99
실시예 16: 화합물 16의 합성
Figure 112012060318184-pat00029
중간체 1-2 (13.2g, 0.0235mol)에 N-(4-bromophenyl)(dipyrimidine)-pyrole(7.66g, 0.0235mol/중국)과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride (0.6g, 0.0235mol), n-Hexane 700ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 16을 10.43g 수득하였다.(수율: 55%)
H-NMR(200MHz, CDCl3): δ ppm, 2H (7.26/M, 7.79/D, 7.68/D, 8.78/S, 9.26/S) 4H (7.11/D, 7.28/M, 7.38/M, 7.33/M, 7.55/D, 7.87/D)
LC/Mass [M+H]+: 805.91
실시예 17: 화합물 17의 합성
Figure 112012060318184-pat00030
중간체 1-2 (13.2g, 0.0235mol)에 2-(4-bromophenyl)-4,6-diphenyl-1,3,5-triazine(9.12g, 0.0235mol/중국)과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride (0.6g, 0.0235mol), n-Hexane 700ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 17을 11.23g 수득하였다.(수율: 55%)
H-NMR(200MHz, CDCl3): δ ppm, 2H (7.26/M, 7.41/M) 4H (7.11/D, 7.28/M, 7.38/M, 7.33/M, 7.55/D, 7.87/D, 7.85/D, 8.28/D, 7.51/M)
LC/Mass [M+H]+: 868.02
실시예 18: 화합물 18의 합성
Figure 112012060318184-pat00031
중간체 1-2 (13.2g, 0.0235mol)에 4-(4-bromophenyl)-3,5-diphenyl-4H-1,2,4-triazole(8.83g, 0.0235mol/아크로스)과 촉매 Copper(II) (0.15g, 0.00235mol)과 Sodium hydride (0.6g, 0.0235mol), n-Hexane 700ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 18을 11.07g 수득하였다.(수율: 55%)
H-NMR(200MHz, CDCl3): δ ppm, 2H (7.79/D, 7.68/D, 7.41/M, 7.26/M) 4H (7.11/D, 7.28/M, 7.38/M, 7.33/M, 7.55/D, 7.87/D, 8.28/D, 7.51/M)
LC/Mass [M+H]+: 856.01
실시예 19: 화합물 19의 합성
Figure 112012060318184-pat00032
중간체 1-2 (13.2g, 0.0235mol)에 2,2'-(4'-bromobiphenyl-3,5-diyl)bis(1-phenyl-1H-benzo[d]imidazole)(14.5g, 0.0235mol/중국)과 촉매 Copper(II) (0.15g, 0.00235mol)과 Sodium hydride (0.6g, 0.0235mol), n-Hexane 700ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 19를 14.19g 수득하였다.(수율: 55%)
H-NMR(200MHz, CDCl3): δ ppm, 2H (7.26/M, 7.85/D, 7.25/D, 8.56/D, 7.59/D, 7.45/M) 3H (7.66/S) 4H(7.11/D, 7.28/M, 7.38/M, 7.33/M, 7.55/D, 7.87/D, 7.50/D, 7.22/M, 7.58/M)
LC/Mass [M+H]+: 1097.30
실시예 20: 화합물 20의 합성
Figure 112012060318184-pat00033
중간체 1-2 (13.2g, 0.0235mol)에 6-(4-bromophenyl)-2,3-diphenylquinoxaline(10.27g, 0.0235mol/중국)과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride (0.6g, 0.0235mol), n-Hexane 700ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 20을 11g 수득하였다.(수율: 51%)
H-NMR(200MHz, CDCl3): δ ppm, 1H (8.30/S, 7.90/D, 7.73/D) 2H (7.26/M, 7.85/D, 7.25/D, 7.41/M) 4H (7.11/D, 7.28/M, 7.38/M, 7.33/M, 7.55/D, 7.87/D, 7.47/D, 7.51/M)
LC/Mass [M+H]+: 917.09
실시예 21: 화합물 21의 합성
Figure 112012060318184-pat00034
중간체 1-2 (13.2g, 0.0235mol)에 9-(4-bromophenyl)-9H-indolo[3,2-f][1,10]phenanthroline(9.97g, 0.0235mol/중국)과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride (0.6g, 0.0235mol), n-Hexane 700ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 21을 11.69g 수득하였다.(수율: 55%)
H-NMR(200MHz, CDCl3): δ ppm, 1H (7.94/D, 7.25/M, 8.55/D) 2H (7.26/M, 7.79/D, 7.68/D, 7.58/M, 8.83/D, 8.38/D) 4H (7.11/D, 7.28/M, 7.38/M, 7.33/M, 7.55/D, 7.87/D)
LC/Mass [M+H]+: 904.05
실시예 22: 화합물 22의 합성
Figure 112012060318184-pat00035
중간체 1-2 (13.2g, 0.0235mol)에 5-(4-bromophenyl)-2,3,7-triphenylthieno[3,4-b]pyrazine(12.2g, 0.0235mol/중국)과 촉매 Copper(II) (0.15g, 0.00235mol)와 Sodium hydride (0.6g, 0.0235mol), n-Hexane 700ml를 넣고 상온에서 8시간 반응시켰다. 반응 혼합물을 상온으로 냉각시킨 후 물을 반응 용매량 만큼 첨가하여 추출 후 칼럼 정제(n-Hexane : methylene chloride)하여 화합물 22를 10.57g 수득하였다.(수율: 45%)
H-NMR(200MHz, CDCl3): δ ppm, 2H (7.26/M, 7.79/D) 3H (7.41/M) 4H (7.11/D, 7.28/M, 7.38/M, 7.33/M, 7.55/D, 7.87/D, 7.85/D, 7.47/D) 6H (7.51/M)
LC/Mass [M+H]+: 999.22
본 발명의 시험예에서 쓰이는 약어는 아래와 같다.
NPB: N,N'-Bis(naphthalen-1-yl)-N,N'-bis(phenyl)benzidine
Ir(ppy)3: Iridium, tris(2-phenylpyidine)
Balq: Bis(2-methyl-8-quinolinolato-N1,O8)-(1,1'-Biphenyl-4-olato)aluminum
Alq3: tris(8-quinolinolato)-aluminium(III)
CBP: (4,4-N,N-dicarbazole)biphenyl
시험예 1
ITO로 코팅된 유리기판 위에 NPB를 증착하여 120nm 두께의 정공수송층을 형성하였으며, 이어서 Ir(ppy)3을 도펀트로 하여 화합물 1의 증착속도를 0.1nm/sec, Ir(ppy)3 증착속도를 0.009nm/sec로 증착하여 증착속도 비율이 9%가 되도록 Ir(ppy)3을 도핑하여 정공수송층 상에 발광층을 30nm 두께로 형성하였다. 그 위에 Balq를 10nm 두께로 증착하여 정공이 발광층을 지나 전자수송층으로 이동하는 것을 방지하는 정공차단층을 형성하고, 그 위에 Alq3를 증착하여 40nm 두께의 전자수송층을 형성하였으며, 그 위에 불화리튬을 증착하여 1nm두께의 전자주입층을 형성하였다. 전자주입층 상에 알루미늄을 증착하여 120nm 두께의 음극을 형성하여 유기전계발광소자를 제조하였다.
이때, 각 물질의 증착속도는 유기물질인, 화합물 1, NPB, Alq3, Balq는 0.1 nm/sec의 속도로 증착하였고, 불화리튬은 0.01 nm/sec, 알루미늄은 0.5 nm/sec의 속도로 증착하였다.
시험예 2 내지 22
화합물 1 대신에 표 1에 기재된 발광재료를 사용한 것을 제외하고는 시험예 1과 동일한 방법으로 시험예 2 내지 22의 유기전계발광소자를 제조하였다.
비교시험예 1
상기 화합물 1 대신 (4,4 -N,N -dicarbazole)biphenyl (CBP)를 사용한 것을 제외하고는 실시예 1과 동일한 방법으로 유기전계발광소자를 제조하였다.
이하, 상기 시험예와 비교시험예에 따라 제조된 유기전계발광소자의 특성을 비교한 결과를 하기 표 1에 나타내었다.
호스트물질 구동전압(V)
(At 1000cd/m2)		 발광효율
cd/A		 색(CIE (x,y))
시험예 1 화합물 1 5.1 35 0.29, 0.61
시험예 2 화합물 2 4.0 30 0.30, 0.62
시험예 3 화합물 3 5.2 25 0.27, 0.60
시험예 4 화합물 4 5.4 22 0.31, 0.60
시험예 5 화합물 5 4.5 39 0.33, 0.63
시험예 6 화합물 6 5.9 26 0.30, 0.60
시험예 7 화합물 7 5.2 27 0.29, 0.62
시험예 8 화합물 8 5.5 31 0.30, 0.59
시험예 9 화합물 9 5.4 29 0.29, 0.63
시험예 10 화합물 10 5.5 22 0.29, 0.67
시험예 11 화합물 11 5.0 34 0.33, 0.62
시험예 12 화합물 12 4.9 30 0.30, 0.61
시험예 13 화합물 13 5.2 20 0.31, 0.60
시험예 14 화합물 14 5.1 27 0.29, 0.64
시험예 15 화합물 15 4.5 31 0.28, 0.64
시험예 16 화합물 16 5.2 29 0.33, 0.63
시험예 17 화합물 17 5.5 35 0.33, 0.62
시험예 18 화합물 18 4.4 41 0.29, 0.62
시험예 19 화합물 19 4.8 39 0.31, 0.62
시험예 20 화합물 20 4.7 44 0.33, 0.62
시험예 21 화합물 21 5.4 39 0.30, 0.63
시험예 22 화합물 22 5.8 27 0.31, 0.62
비교시험예 1 CBP 6.5 19 0.33, 0.63
유기전계발광소자 특성분석
위에서 만든 유기발광소자(기판크기:25×25mm2/증착면적:2×2mm2)를 IVL 측정셋트(CS-2000+지그+IVL프로그램)에 고정한 후 전류를 1mA/m2씩 상승시키며 증착면의 발광 휘도(cd/m2), 구동전압(V), 전류밀도(A/m2), 발광효율(cd/A)를 측정하여 휘도가 1000cd/m2 일 때 구동전압과 발광효율을 표 1에 나타내었다.
표 1을 참고하면, 본 발명에 따른 유기전계발광소자용 화합물이 유기전계발광소자의 발광층의 호스트 물질로 사용될 때 종래의 CBP를 사용할 때보다 구동전압이 상당히 떨어지고, 발광효율이 상당히 우수함을 보여주고 있다.

Claims (8)

  1. 하기 구조식 1로 표시되는 유기전계발광소자용 화합물.
    [구조식 1]
    Figure 112014017128491-pat00036

    상기 구조식 1에서,
    R1은 수소원자,
    Figure 112014017128491-pat00050
    , 치환 또는 비치환된 C6 내지 C30 아릴기, 또는 치환 또는 비치환된 C1 내지 C30 헤테로 아릴기이고,
    R2는 수소원자이고,
    m은 1이고,
    Ar1 및 Ar2는 서로 같거나 다를 수 있고, Ar1 및 Ar2는 각각 독립적으로 치환 또는 비치환된 C6 내지 C30 아릴기, 또는 치환 또는 비치환된 C1 내지 C30 헤테로아릴기이고,
    R3 내지 R8은 서로 같거나 다를 수 있고, R3 내지 R8은 각각 독립적으로 수소원자, 치환 또는 비치환된 C1 내지 C30의 알킬기, 또는 치환 또는 비치환된 C6 내지 C30 아릴기이고,
    상기 "치환된"이란 상기 화합물의 적어도 하나의 수소가 중수소, 할로겐기, 히드록시기, 아미노기, C1 내지 C30 아민기, 니트로기, C1 내지 C30 실릴기, C1 내지 C30 알킬기, C1 내지 C30 알킬실릴기, C3 내지 C30 시클로알킬기, C1 내지 C30 헤테로시클로알킬기, C6 내지 C30 아릴기, C1 내지 C30 헤테로 아릴기, C1 내지 C20 알콕시기, C1 내지 C10 트리플루오로알킬기 또는 시아노기로 치환된 것을 의미한다.
  2. 제1항에 있어서,
    R1은 수소원자, 또는
    Figure 112014017128491-pat00051
    이고,
    Ar1 및 Ar2는 서로 같거나 다를 수 있고, Ar1 및 Ar2는 각각 독립적으로 치환 또는 비치환된 C6 내지 C30 아릴기, 또는 치환 또는 비치환된 C1 내지 C30 헤테로아릴기인 것을 특징으로 하는 유기전계발광소자용 화합물.
  3. 제1항에 있어서,
    상기 유기전계발광소자용 화합물은 하기 구조식으로 표시되는 화합물 중에서 선택된 어느 하나인 것을 특징으로 하는 유기전계발광소자용 화합물.
    Figure 112014017128491-pat00042

    Figure 112014017128491-pat00043

    Figure 112014017128491-pat00044

    Figure 112014017128491-pat00045

    Figure 112014017128491-pat00046
  4. 제1항 내지 제3항 중 어느 한 항에 따른 유기전계발광소자용 화합물을 포함하는 유기전계발광소자.
  5. 제1전극, 제2전극 및 제1전극과 제2전극 사이에 단수 또는 복수의 유기물층을 포함하는 유기전계발광소자에 있어서,
    상기 단수 또는 복수의 유기물층 중에서 선택된 1종 이상의 유기물층은 제1항 내지 제3항 중 어느 한 항에 따른 유기전계발광소자용 화합물을 포함하는 것을 특징으로 하는 유기전계발광소자.
  6. 제5항에 있어서,
    상기 복수의 유기물층은 발광층을 포함하는 것을 특징으로 하는 유기전계발광소자.
  7. 제6항에 있어서,
    상기 복수의 유기물층은 전자주입층, 전자수송층, 정공차단층, 전자차단층, 정공수송층, 및 정공주입층 중에서 선택된 1종 이상을 추가로 포함하는 것을 특징으로 하는 유기전계발광소자.
  8. 제6항에 있어서,
    상기 발광층은 호스트와 도펀트를 포함하는 것을 특징으로 하는 유기전계발광소자.
KR1020120082429A 2012-07-27 2012-07-27 새로운 유기전계발광소자용 화합물 및 그를 포함하는 유기전계발광소자 KR101401639B1 (ko)