KR101388244B1 - Manhole consisting of manhole cover and manhole case - Google Patents
Manhole consisting of manhole cover and manhole case Download PDFInfo
- Publication number
- KR101388244B1 KR101388244B1 KR1020120079137A KR20120079137A KR101388244B1 KR 101388244 B1 KR101388244 B1 KR 101388244B1 KR 1020120079137 A KR1020120079137 A KR 1020120079137A KR 20120079137 A KR20120079137 A KR 20120079137A KR 101388244 B1 KR101388244 B1 KR 101388244B1
- Authority
- KR
- South Korea
- Prior art keywords
- manhole
- layer
- material layer
- manhole cover
- glass cloth
- Prior art date
Abstract
본 발명은 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀에 관한 것으로, 더욱 상세하게는 제1배합원료층, 상기 제1배합원료층의 상부면에 형성되는 제1유리천층, 상기 제1유리천층의 상부면에 형성되는 제2배합원료층, 상기 제2배합원료층의 상부면에 형성되는 철근층, 상기 철근층의 상부면에 형성되는 제3배합원료층 및 상기 제3배합원료층의 상부면에 형성되는 제2유리천층으로 이루어진다.
상기의 구조로 이루어지는 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀은 휘어짐과 비틀림 및 크랙 등과 같은 문제점을 극복하기 위해 별도의 공정을 거칠 필요가 없어 제조시간이 짧고, 제조비용이 저렴하다.
또한, 중량이 가벼워 맨홀 작업시에 작업자들의 편의성을 도모할 수 있고, 최근 금속재료의 가격상승으로 인해 문제가 되고 있는 도난의 위험을 방지할 수 있다.The present invention relates to a manhole made up of a manhole cover and a manhole support frame, and more particularly to a manhole comprising a first blend material layer, a first glass cloth layer formed on an upper surface of the first blend material layer, A reinforcing layer formed on the upper surface of the second compounding material layer, a third material mixture layer formed on the upper surface of the reinforcing layer, and a second material mixture layer formed on the upper surface of the third material mixture layer As shown in FIG.
The manhole having the above-described structure of the manhole cover and the manhole cover does not have to undergo a separate process in order to overcome the problems such as warping, twisting and cracking, and thus the manufacturing time is short and the manufacturing cost is low.
In addition, since the weight is light, it is possible to provide convenience to operators in manhole work, and it is possible to prevent the risk of stolen, which is a problem due to an increase in the price of metal materials in recent years.
Description
본 발명은 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀에 관한 것으로, 더욱 상세하게는 중량이 가볍고, 내충격성이 우수하며, 성형과정에서 휘어짐이나, 비틀림 및 크랙 등이 발생하지 않고, 도난의 위험성이 없는 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀에 관한 것이다.
More particularly, the present invention relates to a manhole comprising a manhole cover and a manhole support frame, and more particularly, to a manhole which is lightweight, has excellent impact resistance, is free from warping, twisting, cracking, A lid and a manhole cover.
본 발명은 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀에 관한 것으로, 더욱 상세하게는 중량이 가볍고, 내충격성이 우수하며, 성형과정에서 휘어짐이나, 비틀림 및 크랙 등이 발생하지 않고, 도난의 위험성이 없는 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀에 관한 것이다.More particularly, the present invention relates to a manhole comprising a manhole cover and a manhole support frame, and more particularly, to a manhole which is lightweight, has excellent impact resistance, is free from warping, twisting, cracking, A lid and a manhole cover.
일반적으로 차도변이나 보도 등에는 배수를 용이하게 하기 위해 맨홀이 설치되며, 상기 맨홀에는 물의 유입이 용이하도록 다수의 통공을 갖는 맨홀 뚜껑과 이러한 맨홀 뚜껑을 받치고 있는 맨홀 받침틀이 설치되는데, 이러한 맨홀뚜껑 및 맨홀 받침틀은 대부분 중량을 갖는 금속주물로 제작된다.Generally, a manhole is provided on a driveway or a sidewalk to facilitate drainage. A manhole cover having a plurality of holes to facilitate the inflow of water and a manhole receiver supporting the manhole cover are installed. And the manhole support frame are made of a metal casting having the most weight.
종래와 같이 금속주물로 제조된 맨홀뚜껑 및 맨홀 받침틀은 대개 검정색의 금속판으로 만들어지므로 도시 미관이 어두워 질 뿐아니라 소재자체의 단가가 고가이므로 생산비용도 많이 소요된다.Since the manhole cover and the manhole support frame made of metal casting are made of a black metal plate as in the conventional art, not only the beauty of the city is darkened but also the cost of the material itself is high, so the production cost is high.
또한, 종래의 맨홀 뚜껑 및 맨홀 받침틀은 주물작업에 의해 제조됨에 따라 형틀에 채워진 주물사에 맨홀 뚜껑 및 맨홀 받침틀과 같은 주형을 뜨고 이에 용융된 주물을 부어 주입시킨 후 이를 식혀 맨홀 뚜껑 및 맨홀 받침틀을 얻은 후에, 이를 다시 연마공정하여 완전한 성형물로 제조한다.In addition, since the conventional manhole cover and manhole support frame are manufactured by casting operation, a mold such as a manhole cover and a manhole support frame is placed on a molding sand filled in a mold, the molten casting is poured into the casting mold, Thereafter, it is polished again to produce a complete molded product.
그러나, 주물작업을 통해 제조되는 맨홀 뚜껑 및 맨홀 받침틀은 휘어짐과 비틀림 및 크랙 등과 같은 문제점을 극복하기 위해 여러 공정을 거쳐야 하기 때문에, 제조비용이 증가하며, 중량이 무거워 맨홀 작업시에 작업자들이 불편을 겪고 있을 뿐만 아니라, 다양한 형태로 제조할 수 없는 문제점이 있었다.However, since the manhole cover and the manhole support frame manufactured through the casting work have to undergo various processes in order to overcome the problems such as warping, twisting and cracking, the manufacturing cost is increased, There is a problem that it can not be manufactured in various forms as well as suffering.
또한, 최근 금속재료의 가격상승으로 인해 맨홀 뚜껑이 도난되는 문제점이 발생하고 있다.
In recent years, there has been a problem that the manhole cover is stolen due to an increase in the price of metal materials.
본 발명의 목적은 휘어짐과 비틀림 및 크랙 등과 같은 문제점을 극복하기 위해 별도의 공정을 거칠 필요가 없어 제조시간이 짧고 제조비용이 저렴한 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀을 제공하는 것이다.It is an object of the present invention to provide a manhole made of a manhole cover and a manhole support frame, which does not have to undergo a separate process in order to overcome problems such as warping, twisting, cracks, etc.,
본 발명의 다른 목적은 중량이 가벼워 맨홀 작업시에 작업자들의 편의성을 도모하며, 도난의 위험성이 없는 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀을 제공하는 것이다.
It is another object of the present invention to provide a manhole made of a manhole cover and a manhole support frame which is light in weight and which provides convenience for operators in a manhole operation and is free from the risk of theft.
본 발명의 목적은 제1배합원료층, 상기 제1배합원료층의 상부면에 형성되는 제1유리천층, 상기 제1유리천층의 상부면에 형성되는 제2배합원료층, 상기 제2배합원료층의 상부면에 형성되는 철근층, 상기 철근층의 상부면에 형성되는 제3배합원료층 및 상기 제3배합원료층의 상부면에 형성되는 제2유리천층으로 이루어지는 것을 특징으로 하는 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀을 제공함에 의해 달성된다.An object of the present invention is to provide a process for producing a glass composition which comprises a first blending material layer, a first glass forming layer formed on an upper surface of the first blending material layer, a second blending material layer formed on an upper surface of the first glass forming layer, A reinforcing layer formed on the upper surface of the reinforcing layer, a third reinforcing layer formed on the upper surface of the reinforcing layer, and a second reinforcing layer formed on the upper surface of the third reinforcing layer. This is achieved by providing a manhole made up of a manhole support frame.
본 발명의 바람직한 특징에 따르면, 상기 제1배합원료층, 상기 제2배합원료층 및 상기 제3배합원료층은 합성수지 18 내지 20 중량부, 유리섬유 촙 0.05 내지 0.15 중량부, 백운석 70 내지 75 중량부 및 경화제 0.05 내지 0.15 중량부로 이루어지는 것으로 한다.According to a preferred feature of the present invention, the first blend material layer, the second blend material layer and the third blend material layer contain 18 to 20 parts by weight of synthetic resin, 0.05 to 0.15 parts by weight of glass fibers, 70 to 75 parts by weight of dolomite And 0.05 to 0.15 parts by weight of a curing agent.
본 발명의 더 바람직한 특징에 따르면, 상기 합성수지는 불포화폴리에스터로 이루어지는 것으로 한다.According to a further preferred feature of the present invention, the synthetic resin is made of an unsaturated polyester.
본 발명의 더욱 바람직한 특징에 따르면, 상기 경화제는 터셔리-부틸퍼록시벤조에이트로 이루어지는 것으로 한다.According to a further preferred feature of the present invention, the curing agent is composed of tertiary-butyl peroxybenzoate.
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 맨홀은 상기 제1배합원료층, 제1유리천층, 제2배합원료층, 철근층, 제3배합원료층 및 제2유리천층으로 형성되는 맨홀 뚜껑 및 상기 제1배합원료층, 제1유리천층, 제2배합원료층, 철근층, 제3배합원료층 및 제2유리천층으로 형성되는 맨홀 받침들로 이루어지는 것으로 한다.According to an even more preferred feature of the present invention, the manhole is provided with a manhole cover formed of the first blended raw material layer, the first glass cloth layer, the second blended raw material layer, the reinforcing bar layer, the third blended raw material layer and the second glass cloth layer, And manhole bases formed of the first blended raw material layer, the first glass cloth layer, the second blended raw material layer, the reinforcing bar layer, the third blended raw material layer and the second glass cloth layer.
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 맨홀 뚜껑의 철근층은 격자구조의 철근으로 이루어지는 것으로 한다.According to a further preferred feature of the present invention, the reinforcing layer of the manhole cover is made of reinforcing bars having a lattice structure.
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 맨홀 받침틀의 철근층은 2겹의 테두리 철근 및 상기 2겹의 테두리 철근의 모서리 부위에 사선방향으로 연결되는 연결철근으로 이루어지는 것으로 한다.
According to a further preferred feature of the present invention, the reinforcing layer of the manhole support frame is composed of a double-layered reinforcing bar and a connecting reinforcing bar connected in an oblique direction to a corner portion of the double reinforcing reinforcing bar.
본 발명에 따른 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀은 휘어짐과 비틀림 및 크랙 등과 같은 문제점을 극복하기 위해 별도의 공정을 거칠 필요가 없어 제조시간이 짧고, 제조비용이 저렴한 맨홀 뚜껑 또는 맨홀 받침틀로 이루어진 맨홀을 제공하는 탁월한 효과를 나타낸다.The manhole made up of the manhole cover and the manhole support frame according to the present invention does not have to undergo a separate process in order to overcome the problems such as warping, twisting and cracking, ≪ / RTI >
또한, 중량이 가벼워 맨홀 작업시에 작업자들의 편의성을 도모하며, 도난의 위험성이 없는 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀을 제공하는 탁월한 효과를 나타낸다.
In addition, it is light in weight, which provides an operator's convenience during manhole work, and provides an excellent effect of providing a manhole made of a manhole cover and a manhole support frame without the risk of theft.
도 1은 본 발명에 따른 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀의 맨홀 뚜껑을 나타낸 분해사시도이다.
도 2는 본 발명에 따른 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀의 맨홀 받침틀을 나타낸 분해사시도이다.
도 3은 본 발명에 따른 맨홀 뚜껑의 제조시에 사용되는 철근을 나타낸 사진이다.
도 4는 본 발명에 따른 맨홀 받침틀의 제조시에 사용되는 철근을 나타낸 사진이다.
도 5는 본 발명에 의해 제조된 맨홀 뚜껑을 나타낸 사진이다.
도 6은 본 발명에 의해 제조된 맨홀 받침틀을 나타낸 사진이다.
도 7은 본 발명에 의해 맨홀 뚜껑 및 맨홀 받침틀을 제조하는데 사용되는 금형을 나타낸 사진이다.
도 8은 본 발명에 의해 제조된 맨홀 뚜껑 및 맨홀 받침틀의 결합상태를 나타낸 사진이다.1 is an exploded perspective view showing a manhole cover of a manhole made up of a manhole cover and a manhole cover according to the present invention.
2 is an exploded perspective view showing a manhole support frame of a manhole made up of a manhole cover and a manhole support frame according to the present invention.
3 is a photograph showing a reinforcing bar used in manufacturing a manhole cover according to the present invention.
4 is a photograph showing a reinforcing bar used in manufacturing the manhole cover according to the present invention.
5 is a photograph showing a manhole cover manufactured by the present invention.
6 is a photograph showing a manhole cover manufactured by the present invention.
7 is a photograph showing a mold used for manufacturing a manhole cover and a manhole support frame according to the present invention.
FIG. 8 is a photograph showing the mating state of the manhole cover and the manhole support frame manufactured by the present invention.
이하에는, 본 발명의 바람직한 실시예와 각 성분의 물성을 상세하게 설명하되, 이는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 발명을 용이하게 실시할 수 있을 정도로 상세하게 설명하기 위한 것이지, 이로 인해 본 발명의 기술적인 사상 및 범주가 한정되는 것을 의미하지는 않는다.
Hereinafter, preferred embodiments of the present invention and physical properties of the respective components will be described in detail with reference to the accompanying drawings. However, the present invention is not limited thereto, And this does not mean that the technical idea and scope of the present invention are limited.
본 발명에 따른 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀은 제1배합원료층(10), 상기 제1배합원료층(10)의 상부면에 형성되는 제1유리천층(20), 상기 제1유리천층(20)의 상부면에 형성되는 제2배합원료층(30), 상기 제2배합원료층(30)의 상부면에 형성되는 철근층(40), 상기 철근층(40)의 상부면에 형성되는 제3배합원료층(50) 및 상기 제3배합원료층(50)의 상부면에 형성되는 제2유리천층(60)으로 이루어진다.The manhole made up of the manhole cover and the manhole support frame according to the present invention comprises a first
또한, 상기의 구조로 이루어진 맨홀은 상기 제1배합원료층(10), 제1유리천층(20), 제2배합원료층(30), 철근층(40), 제3배합원료층(50) 및 제2유리천층(60)으로 형성되는 맨홀 뚜껑 및 상기 제1배합원료층(10), 제1유리천층(20), 제2배합원료층(30), 철근층(40), 제3배합원료층(50) 및 제2유리천층(60)으로 형성되는 맨홀 받침틀로 이루어진다.
The manhole having the above structure is provided with the first
상기 제1배합원료층(10)은 합성수지, 유리섬유 촙, 백운석 및 경화제로 이루어지며, 합성수지 18 내지 20 중량부, 유리섬유 촙 0.05 내지 0.15 중량부, 백운석 70 내지 75 중량부 및 경화제 0.05 내지 0.15 중량부로 이루어지는데, 맨홀 제조용 금형 내부가 1/3 정도 충전되도록 배합원료를 투입하여 형성된다.The first compounding
이때, 배합원료를 맨홀 제조용 금형 내부에 투입하기 전에 금형 내부에 왁스칠을 해주는 것이 바람직한데, 이는 배합원료 성분이 금형으로부터 쉽게 이탈될 수 있도록 하기 위함이다.At this time, it is preferable to wax the inside of the mold before the compounding material is injected into the mold for manhole production, in order to allow the ingredients of the ingredients to be easily separated from the mold.
상기 합성수지는 18 내지 20 중량부가 첨가되며, 18.5 중량부로 첨가되는 것이 바람직하다.18 to 20 parts by weight of the synthetic resin is added, and 18.5 parts by weight of the synthetic resin is added.
또한, 상기 합성수지는 불포화 이염기산 및 글리콜의 종류에 따라 다양한 조합으로 생성되고, 수지의 점도가 낮아 함침이 잘되며, 증점공정에서는 적절하게 점도가 상승하며 증점이 완료후에는 시간에 따른 점도변화가 없는 수지인 불포화폴리에스터가 바람직하다.In addition, the synthetic resin is produced in various combinations depending on the kinds of unsaturated dibasic acids and glycols, the viscosity of the resin is low and the impregnation is good. In the thickening step, the viscosity is appropriately increased. Unsaturated polyester which is a resin which is free from the above is preferable.
상기 유리섬유 촙은 0.05 내지 0.15 중량부가 첨가되며, 0.1 중량부가 첨가되는 것이 바람직하다.0.05 to 0.15 parts by weight of the glass fiber glass is added, and 0.1 part by weight of the glass fiber glass is preferably added.
상기 유리섬유 촙은 경량이면서도 금속과 같은 강성을 갖는 맨홀뚜껑을 제조할 수 있도록 배합원료에 강성을 부여하는 역할을 하여, 작업성과 운반이 용이한 맨홀뚜껑을 제공하는 역할을 한다.The glass fiber rods serve to provide a manhole cover having a rigidity similar to that of a metal with a light weight, and to provide a manhole cover with workability and ease of transportation.
유리섬유 촙은 유리섬유사를 잘게 절단하여 형성되는데, 더욱 상세하게는 750 내지 4400 TEX의 유리섬유사를 20 내지 25밀리미터의 단위로 잘게 절단하여 형성되며, 750 TEX를 사용하며, 20밀미미터 단위로 절단하는 것이 더욱 바람직하다.The glass fiber is formed by finely cutting a glass fiber yarn, and more specifically, it is formed by finely cutting glass fiber yarn of 750 to 4400 TEX into 20 to 25 millimeters, using 750 TEX, Is more preferable.
상기 백운석은 70 내지 75 중량부가 첨가되며, 71 중량부가 첨가되는 것이 바람직하다.70 to 75 parts by weight of dolomite is added, and 71 parts by weight of dolomite is preferably added.
상기 백운석은 석회석과 규석이 3:7 내지 4:6의 중량비율로 배합된 것이 바람직한데, 석회석은 배합원료의 응집성을 향상시키고, 규석은 배합원료의 기계적 강성을 향상시키는 역할을 한다.The dolomite is preferably blended with limestone and silica in a weight ratio of 3: 7 to 4: 6. Limestone improves the cohesion of the blended raw material, and the silica serves to improve the mechanical rigidity of the blended raw material.
또한, 상기 백운석은 0.7 내지 6 밀리미터의 입경을 갖도록 미분쇄된 분말을 사용하는 것이 바람직한데, 입경의 차이가 나는 백운석 분말을 사용함으로 인해 배합원료의 기계적 강도를 향상시킬 수 있다.It is preferable that the dolomite is pulverized to have a particle diameter of 0.7 to 6 millimeters. By using dolomite powder having a different particle diameter, the mechanical strength of the blended raw material can be improved.
상기 경화제는 0.05 내지 0.15 중량부가 첨가되며, 상기 합성수지의 경화를 향상시켜 기계적 강도가 향상된 맨홀 뚜껑을 제공하는 역할을 한다.The curing agent is added in an amount of 0.05 to 0.15 parts by weight to provide a manhole cover having improved mechanical strength by improving the hardening of the synthetic resin.
상기 경화제 성분은 상기 합성수지 성분인 불포화 폴리에스터를 경화시킬 수 있는 성분이면 특별히 한정되지 않지만, 터셔리-부틸퍼록시벤조에이트로 이루어지는 것이 바람직하다.The curing agent component is not particularly limited as long as it is a component capable of curing the unsaturated polyester as the synthetic resin component, but it is preferably composed of tertiary-butylperoxybenzoate.
상기의 성분들로 이루어진 배합원료는 교반기에서 50 내지 200rpm의 교반속도로 10 내지 30분 동안 교반한 후에 사용하는 것이 바람직하다.
It is preferable to use the compounding materials composed of the above-mentioned components after stirring for 10 to 30 minutes at a stirring speed of 50 to 200 rpm in a stirrer.
상기 제1유리천층(20)은 상기 제1배합원료층(10)의 상부면에 형성되며, 유리섬유사를 직조하여 형성된 유리천으로 이루어지는데, 배합원료를 맨홀 제조용 금형 내부에 1/3정도 충전하여 형성된 배합원료층(10)의 상부면에 유리섬유를 직조하여 이루어진 유리천을 개재하고 다져서 형성된다.The first
이때, 상기 유리천은 750 내지 4400 TEX의 유리섬유사를 직조하여 형성하는 것이 바람직하다.At this time, it is preferable that the glass cloth is formed by woven glass fiber yarn of 750 to 4400 TEX.
이러한 제1유리천층(20)의 형성을 통해 상기 제1배합원료층(20) 및 상기 제2배합원료층(30)의 배합원료들의 결속력이 향상되어, 기계적 강성이 보강된 맨홀을 제공할 수 있다.
Through the formation of the first
상기 제2배합원료층(30)은 상기 제1유리천층(20)의 상부면에 형성되며, 상기 제1유리천층(20)의 상부면에 배합원료를 충전하여 형성되는데, 맨홀 제조용 금형 내부가 2/3 정도 충전되도록 배합원료를 투입하는 형성된다.The second
이러한 제2배합원료층(30)은 성분과 역할이 상기 제1배합원료층(10)과 동일함으로 이에 대한 설명은 생략하기로 한다.
Since the components and the role of the second
상기 철근층(40)은 상기 제2배합원료층(30)의 상부면에 형성되며, 상기 제2배합원료층(30)의 상부면에 철근을 개재하고 다지는 과정을 통해 형성된다.The reinforcing
상기 철근층(40)은 배합원료의 기계적 강성을 향상시킬 뿐만 아니라, 본 발명에 따른 맨홀의 형태안정성을 향상시키는 역할을 한다.The reinforcing
상기 철근층(40)은 직경이 0.1 내지 10 밀리미터인 철근을 사용하는 것이 바람직한데, 철근의 직경이 0.1밀리미터 미만이면 본 발명에 따른 맨홀의 형태안정성이 저하되며, 10 밀리미터를 초과하게 되면, 맨홀의 중량이 증가하게 된다.When the diameter of the reinforcing bar is less than 0.1 millimeter, the shape stability of the manhole according to the present invention is deteriorated. When the diameter of the
상기 철근층(40)은 맨홀 뚜껑에 적용될 경우에는 격자구조의 철근(도 3)으로 이루어지며, 맨홀 받침틀에 적용될 경우에는 2겹의 테두리 철근 및 상기 2겹의 테두리 철근의 모서리 부위에 사선방향으로 연결되는 연결철근(도 4)으로 이루어진다.The reinforcing
또한, 상기 철근층(40)은 철근과 철근이 접하는 부위를 용접 등의 방법으로 결속하여 형태안정성이 유지되도록 하는 것이 바람직하다.
In addition, it is preferable that the reinforcing layer (40) binds the portion where the reinforcing bar and the reinforcing bar are in contact with each other by welding or the like so that the shape stability is maintained.
상기 제3배합원료층(50)은 상기 철근층(40)의 상부면에 형성되며, 상기 철근층의 상부면에 배합원료를 충전하되, 금형 내에 배합원료가 꽉 차도록 충전하여 형성되는데, 이러한 제3배합원료층(50)은 성분과 역할이 상기 제1배합원료층(10)과 동일함으로 이에 대한 설명은 생략하기로 한다.
The third
상기 제2유리천층(60)은 상기 제3배합원료층(50)의 상부면에 형성되며, 상기 제3배합원료층(50)의 상부면에 유리섬유사를 직조하여 형성된 유리천을 개재하고 다져서 형성되는데, 상기 제1유리천층(20)과 성분 및 역할이 동일함으로 이에 대한 설명은 생략하기로 한다.
The second
상기 제2유리천층(60)이 형성되면, 맨홀 제조용 금형 내에 충전된 배합원료, 유리천 및 철근을 압축하여 맨홀 모양으로 성형하는데, 맨홀 제조용 금형을 유압프레스로 15 내지 25분 동안 압축하여 맨홀 형태의 성형물을 성형한다.When the second
상기 성형물은 맨홀의 형태를 가짐과 동시에 1차적인 경화가 진행되며, 1차적인 경화가 진행된 성형물은 상온에서 45 내지 50 시간 동안 서서히 경화되어 휘어짐이나 비틀림이 없는 맨홀로 제조된다.
The molded product has a shape of a manhole and a primary hardening is proceeded. The primary hardened molded product is slowly hardened at room temperature for 45 to 50 hours to produce a manhole without warping or twisting.
상기 제1배합원료층(10), 제1유리천층(20), 제2배합원료층(30), 철근층(40), 제3배합원료층(50) 및 제2유리천층(60)으로 이루어지는 맨홀은 휘어짐, 비틀림 및 크랙 등과 같은 문제점을 극복하기 위해 별도의 공정을 거칠 필요가 없어 제조시간이 짧고, 제조비용이 저렴하며, 중량이 가벼워 맨홀 작업시에 작업자들의 편의성을 도모할 뿐만 아니라, 도난의 위험성이 없다.
The first
10 ; 제1배합원료층
20 ; 제1유리천층
30 ; 제2배합원료층
40 ; 철근층
50 ; 제3배합원료층
60 ; 제2유리천층10; The first compounding raw material layer
20; The first glass cloth layer
30; The second blend material layer
40; Reinforcing layer
50; The third compounding raw material layer
60; The second glass layer
Claims (8)
상기 제1배합원료층의 상부면에 형성되는 제1유리천층;
상기 제1유리천층의 상부면에 형성되는 제2배합원료층;
상기 제2배합원료층의 상부면에 형성되는 철근층;
상기 철근층의 상부면에 형성되는 제3배합원료층; 및
상기 제3배합원료층의 상부면에 형성되는 제2유리천층으로 이루어지는 것을 특징으로 하는 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀에 있어서,
상기 맨홀 뚜껑과 상기 맨홀 받침틀은 각각 상기 제1배합원료층, 제1유리천층, 제2배합원료층, 철근층, 제3배합원료층 및 제2유리천층으로 이루어지는 것을 특징으로 하고,
상기 제1배합원료층, 상기 제2배합원료층 및 상기 제3배합원료층은 합성수지 18 내지 20 중량부, 유리섬유 촙 0.05 내지 0.15 중량부, 백운석 70 내지 75 중량부 및 경화제 0.05 내지 0.15 중량부로 이루어지는 것을 특징으로 하고,
상기 맨홀 받침틀의 상기 철근층은 2겹의 테두리 철근; 및
상기 2겹의 테두리 철근의 모서리 부위에 사선방향으로 연결되는 연결철근;으로 이루어지는 것을 특징으로 하는 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀.
A first compounding raw material layer;
A first glass cloth layer formed on an upper surface of the first blend material layer;
A second blend material layer formed on an upper surface of the first glass cloth layer;
A reinforcing layer formed on an upper surface of the second blend material layer;
A third blend material layer formed on the upper surface of the reinforcing layer; And
And a second glass cloth layer formed on an upper surface of the third blend material layer. The manhole cover according to claim 1,
Wherein the manhole cover and the manhole support frame are formed of the first blended raw material layer, the first glass cloth layer, the second blended raw material layer, the reinforcing bar layer, the third blended raw material layer and the second glass cloth layer,
Wherein the first blend material layer, the second blend material layer and the third blend material layer contain 18 to 20 parts by weight of synthetic resin, 0.05 to 0.15 parts by weight of glass fibers, 70 to 75 parts by weight of dolomite and 0.05 to 0.15 parts by weight of a hardener .
The reinforcing layer of the manhole support frame comprises a double-layered reinforcing bar; And
And a connection reinforcing bar connected to a corner portion of the two-ply reinforcing bar in an oblique direction.
상기 합성수지는 불포화폴리에스터로 이루어지는 것을 특징으로 하는 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀.
The method according to claim 1,
Wherein the synthetic resin is made of an unsaturated polyester. The manhole comprises a manhole cover and a manhole cover.
상기 경화제는 터셔리-부틸퍼록시벤조에이트로 이루어지는 것을 특징으로 하는 맨홀 뚜껑 및 맨홀 받침틀로 이루어진 맨홀.
3. The method according to claim 1 or 2,
Wherein the hardener is made of tertiary-butyl peroxybenzoate. The manhole comprises a manhole cover and a manhole cover.