KR101191775B1 - Method for Preparing Single Jersey Knitting Fabrics without Skew - Google Patents

Method for Preparing Single Jersey Knitting Fabrics without Skew Download PDF

Info

Publication number
KR101191775B1
KR101191775B1 KR1020100097180A KR20100097180A KR101191775B1 KR 101191775 B1 KR101191775 B1 KR 101191775B1 KR 1020100097180 A KR1020100097180 A KR 1020100097180A KR 20100097180 A KR20100097180 A KR 20100097180A KR 101191775 B1 KR101191775 B1 KR 101191775B1
Authority
KR
South Korea
Prior art keywords
single jersey
fabric
cotton yarn
needle
knitted fabric
Prior art date
Application number
KR1020100097180A
Other languages
Korean (ko)
Other versions
KR20120035575A (en
Inventor
박찬호
Original Assignee
박찬호
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 박찬호 filed Critical 박찬호
Priority to KR1020100097180A priority Critical patent/KR101191775B1/en
Publication of KR20120035575A publication Critical patent/KR20120035575A/en
Application granted granted Critical
Publication of KR101191775B1 publication Critical patent/KR101191775B1/en

Abstract

본 발명은 뒤틀림 없는 싱글 져지 편물을 제조하는 방법에 관한 것으로서, 구체적으로는 80~160g/m2 내외의 가볍고 얇은 싱글 져지 편물에서 발생하는 스큐현상을 방지할 수 있는 싱글 져지 편물의 제조방법에 관한 것이다. 구체적으로는 100% 면으로 이루어진 싱글 져지 편물의 제조방법으로서 꼬임 방향이 서로 다른 2올의 실을 하나의 니들에 동시에 공급하여 제직하는 것을 특징으로 하는 싱글 져지 편물의 제조방법을 제공한다.The present invention relates to a method for manufacturing a single jersey knit without distortion, and more particularly, to a method for manufacturing a single jersey knitted fabric which can prevent the skew phenomenon occurring in a light and thin single jersey knitted fabric of about 80 ~ 160g / m 2 will be. Specifically, the method for producing a single jersey knit fabric made of 100% cotton provides a method for manufacturing a single jersey knit fabric, characterized in that weaving is performed by simultaneously supplying two needles with different twist directions to one needle.

Description

스큐현상이 없는 싱글 져지 편물의 제조방법{Method for Preparing Single Jersey Knitting Fabrics without Skew}Method for Preparing Single Jersey Knitting Fabrics without Skew}

본 발명은 100% 면으로 이루어진 싱글 져지 편물을 뒤틀림 없게 제조하는 방법에 관한 것으로서, 구체적으로는 80~160g/m2 내외의 가볍고 얇은 싱글져지 편물에서 발생하는 뒤틀림현상을 방지할 수 있는 싱글 져지 편물의 제조방법에 관한 것이다. The present invention relates to a method for producing a single jersey knitted fabric made of 100% cotton without distortion, specifically, a single jersey knitted fabric which can prevent the warpage phenomenon occurring in a light and thin single jersey knitted fabric of about 80 ~ 160g / m 2 It relates to a manufacturing method of.

여성용 상의에 사용되는 소재 중 니트(knit) 편물은 환편기를 이용하여 제조되는 원단으로서, 대표적인 것으로 싱글져지(single jersey)를 들 수 있다. 싱글 져지 편물의 제조공정에서 단위시간당 생산량을 높여 가격 경쟁력을 갖기 위하여 환편기의 직경이 커지게 되었고, 환편기에 캠(cam)과 피더(Feeder)를 많이 장착하는 기술이 발달하게 되었다. 캠(cam)을 많이 장착할 수 있다는 것은 많은 실(yarn)을 동시에 공급하는 피더(Feeder)를 많이 장착할 수 있다는 것을 의미하며, 피더(Feeder) 수가 많아진다는 것은 환편기의 실린더(cylinder)가 한 바퀴 회전할 때 피더(feeder) 수만큼 코스(course)가 편성되므로 단위 시간당 더 많은 원단을 생산할 수 있다는 것을 의미한다.Among the materials used for women's tops, the knitted fabric is a fabric manufactured using a circular knitting machine, and a representative single jersey is mentioned. In the manufacturing process of single jersey knitting, the diameter of the circular knitting machine has been increased in order to increase the output per unit time to have a price competitiveness, and the technology of attaching many cams and feeders to the circular knitting machine has been developed. Being able to mount a lot of cams means that a lot of feeders can be installed to supply a lot of yarns at the same time, and that a large number of feeders means that a cylinder of a circular knitting machine By rotating the wheels, courses are organized by the number of feeders, meaning more fabrics can be produced per unit time.

환편기에서 편성되는 싱글 져지 편물의 편성 원리를 살펴보면, 환편기의 캠은 고정되어 있고 실린더가 회전하면서 니트 편물이 편성되는데, 실린더의 지름은 용도에 따라 다르다. 환편기는 인체의 둘레와 직경이 같은 10", 12", 14" 등의 봉제선이 없는 원통형(seamless)용 환편기가 있고, 직경이 26", 30", 32", 36"인치 등 직경이 큰 환편기들도 있다. 직경이 큰 환편기는 폭이 넓은 편물의 편성에 사용되는데, 폭이 넓은 원단은 원단을 재단한 후 봉제하는 절차를 거쳐 사용되게 된다.Looking at the knitting principle of a single jersey knitted in a circular knitting machine, the cam of the circular knitting machine is fixed and the knitted knitting is knitted as the cylinder rotates, the diameter of the cylinder varies depending on the application. The circular knitting machine has a seamless circular knitting machine, such as 10 ", 12", 14 ", which has the same diameter as the circumference of the human body, and has a large diameter circular knitting machine, such as 26", 30 ", 32", and 36 "inches. Large diameter circular knitting machines are used to knit wide knitted fabrics, which are used to cut and sew fabrics.

그런데 환편기에서 생산된 원단들은 환편기의 기계적 구조로 인하여 연속적인 나선형 모양으로 편성된다. 따라서 편성 중에 코오스(course)가 수평을 이루지 못하고 연속적으로 편성되어 원형 형태의 원단을 개폭하면 원단의 한쪽이 수평보다 기울어진 원단이 생산되게 된다. 이렇게 기울어진 원단은 염색 전처리, 염색, 후처리 등의 공정을 거치는 동안 원단의 결이 바르지 않은 상태에서 연속적으로 처리되는 문제점이 있다. However, the fabrics produced in the circular knitting machine are knitted in a continuous spiral shape due to the mechanical structure of the circular knitting machine. Therefore, during knitting, the course is not horizontal but is knitted continuously to open a circular shaped fabric so that one side of the fabric is inclined than horizontal. This inclined fabric has a problem in that it is continuously processed in the state that the texture of the fabric during the process of dyeing pre-treatment, dyeing, post-treatment, and the like.

또한 편성하면서 웨일 방향이 기울어지게 생산되어 원단을 재단할 때 웨일과 코오스를 정확하게 맞추기가 어렵기 때문에 기울어진 상태에서 그대로 재단되는 경우가 대부분이다. 따라서 최종적으로 생산된 의류는 웨일 방향이 틀어지게 되고 따라서 코오스가 기울어져 전체적으로 뒤틀어지게 된다. 이렇게 뒤틀어진 의류는 착용 후 세탁하는 과정에서도 옆 솔기, 어깨, 목둘레 등에서 뒤틀림 현상이 나타나게 된다.In addition, the wale direction is inclined while knitting, so it is difficult to accurately match the wales and the coarse when cutting the fabric, so it is often cut in the inclined state. Therefore, the final garment produced is the wale direction is distorted and thus the coarse tilted overall warp. Such warped clothing may be warped in side seams, shoulders, and neck circumference even after washing.

이러한 문제점을 해결하기 위해서 여러 가지 시도가 이루어지고 있다. Various attempts have been made to solve this problem.

그중 한 방법으로는 편성할 때 개폭선을 만들지 않고 편성한 후 튜브 상태의 편물을 수세(water wash)하여 개폭하는 방법이 있다. 이 방법은 재단시 결 방향을 완전히 무시하고 재단하여 옷을 만들어서 뒤틀림 현상을 감소시키는 방법이다. 하지만, 이 경우에는 웨일과 코스가 수직 및 수평으로 놓이지 않으므로 옷을 착용한 경우에 착용자가 기울어져 보이는 현상이 나타나 품질을 매우 떨어뜨리는 문제점이 있다.One of the methods is to open the tube in the form of a water wash and then open it without forming an opening line when knitting. This method is to completely disregard the direction of the grain when cutting, to make clothes by cutting to reduce the distortion. However, in this case, since the wale and the course are not placed vertically and horizontally, there is a problem in that the wearer is inclined when the clothes are worn, which greatly degrades the quality.

다른 한 가지 방법으로는 편성할 때 웨일 방향에 개폭선을 형성하는 것이다. 개폭 시 웨일 방향을 기준으로 편환이 이루어지지 않은 개폭선을 따라 절단하고, 텐터 공정 전에 코스(course) 방향이 수평이 되도록 보정한다. 하지만, 이 경우에도 완성된 옷을 세탁하면 다시 옆 솔기가 뒤틀리는 현상이 발생하는 문제점이 있다. Another method is to form an open line in the wale direction when knitting. When opening, cut along the open line, which is not deflected relative to the wale direction, and correct the course direction to be horizontal before the tenter process. However, even in this case, there is a problem in that the side seam is twisted again when the finished clothes are washed.

본 발명은 100% 면으로 이루어진 싱글 져지 편물에 있어서 형태안정성을 유지하는 방법을 제공하는 것을 목적으로 하며, 특히 싱글 져지 편물의 편성 과정에서 발생하는 뒤틀림 현상을 없애거나 최소화할 수 있는 방법을 제공하는 것을 목적으로 한다.An object of the present invention is to provide a method for maintaining morphological stability in a single jersey knitted fabric made of 100% cotton, and in particular, to provide a method for eliminating or minimizing the distortion occurring during the knitting process of a single jersey knitted fabric. For the purpose of

본 발명의 적절한 실시 형태에 따르면, 100% 면으로 이루어진 싱글저지편물의 제조방법으로서 꼬임방향이 서로 다른 면사를 환편기의 하나의 니들에 동시에 공급하여 편성하는 것을 특징으로 하는 싱글 져지 편물의 제조방법을 제공한다.According to a preferred embodiment of the present invention, a method for producing a single jersey knitted fabric made of 100% cotton, characterized in that the knitting of the single jersey knitting, characterized in that the knitting by feeding the cotton yarn of different twisting direction to one needle of the circular knitting machine at the same time to provide.

본 발명의 다른 적절한 실시 형태에 따르면, 상기 면사는 꼬임 방향이 우연 또는 좌연인 것을 특징으로 한다.According to another suitable embodiment of the present invention, the cotton yarn is characterized in that the twist direction is a coincidence or a left margin.

본 발명의 또 다른 적절한 실시 형태에 따르면, 상기 면사는 연계수(TM)가 2.5 내지 4.0 인 것을 특징으로 한다.According to another suitable embodiment of the present invention, the cotton thread is characterized in that the linkage (TM) of 2.5 to 4.0.

본 발명의 또 다른 적절한 실시 형태에 따르면, 연계수가 2.5 내지 4.0인 우연 및 좌연 면사를 동시에 이용하여 편성되고, 편물의 무게가 80 내지 160g/m2인 싱글 져지 편물을 제공한다.According to another suitable embodiment of the present invention, there is provided a single jersey knit fabric which is knitted using both the right and left edge yarns having a linkage of 2.5 to 4.0 at the same time, and has a weight of 80 to 160 g / m 2 .

본 발명에서 제조된 싱글 져지 편물은 염색 및 재단 후에 뒤틀림이 거의 발생하지 않으며, 세탁 후 의류의 형태가 뒤틀림 없이 그대로 유지된다.The single jersey knitted fabric produced in the present invention hardly causes distortion after dyeing and cutting, and the shape of the garment is maintained without distortion after washing.

도 1은 본 발명에서 꼬임 방향이 다른 두 올의 면사가 하나의 니들에 공급되는 것을 개략적으로 도시한 것이다.
도 2는 본 발명에서 편성된 직물의 정면도이다.FIG. 1 schematically shows that cotton yarns of two rows having different twisting directions are supplied to one needle in the present invention.
2 is a front view of the fabric knitted in the present invention.

싱글 져지 편물은 주로 여성용 상의에 사용되는 원단으로, 본 발명에서는 100% 면으로 이루어지고 80 내지 160g/m2 내외의 가볍고 얇은 직물을 의미한다. Single jersey knit is a fabric mainly used for women's tops, in the present invention means a light and thin fabric made of 100% cotton and around 80 to 160g / m 2 .

100% 면으로 이루어진 싱글 져지 편물은 일반적으로 60 내지 120 피더(feeder)가 장착된 환편기를 이용하여 편성되는데, 최근에는 200 피더가 장착된 환편기도 이용되고 있다. 환편기의 피더가 120개인 경우, 환편기의 실린더가 한바퀴 회전할 때마다 120가닥의 실이 동시에 편성되어 120 코스(course)가 그룹으로 생산되고, 이들 그룹이 반복되는 나선형의 모양의 편물이 생산된다. 이렇게 생산된 편물은 튜브 상태이므로, 재단을 위하여 이를 개폭하여 평면 상태로 만들게 된다. 이때 피더 수에 따라 원단의 경사도(skew)가 달라지는데, 전체 피더의 갯수에 루프 장을 곱한 만큼 한쪽 변이 올라가거나 내려가는 기울어짐이 발생하게 된다. Single jersey knitted fabric made of 100% cotton is generally knitted using a circular knitting machine equipped with 60 to 120 feeders, and recently, circular knitting machines equipped with 200 feeders have also been used. When the circular knitting machine has 120 feeders, each time the cylinder of the circular knitting machine rotates one round, 120 threads are simultaneously knitted to produce 120 courses in groups, and a spiral-shaped knitted fabric in which these groups are repeated is produced. The knitted fabric thus produced is in the form of a tube, so it is opened for cutting and made flat. At this time, the skew of the fabric varies depending on the number of feeders. As the number of feeders is multiplied by the loop length, one side rises or falls down.

한편, 싱글 져지 편물의 뒤틀림은 상기한 환편기의 기계적인 문제에 더하여 원사인 면사의 특성에 의해서도 발생한다. 일반적으로 사용되는 면사는 일정한 꼬임이 부여되어 있는데, 실의 단위길이 당 꼬임 수는 단섬유의 길이, 실의 굵기, 요구되는 실의 강력, 촉감 등에 따라 달라진다. On the other hand, warping of the single jersey knitted fabric is also caused by the characteristics of the cotton yarn as a yarn in addition to the mechanical problem of the circular knitting machine described above. Generally used cotton yarn is given a certain twist, the number of twists per unit length of the yarn depends on the length of the short fiber, the thickness of the yarn, the strength of the yarn required, the touch.

연계수는 꼬임수와 번수의 제곱근의 비를 의미하는데, 연계수(TM:Twist multiples)가 4.0~5.0인 경우에 강력이 가장 커지게 되므로 일반적으로 연계수가 4.0 정도의 면사가 싱글 져지 편물의 제조에 많이 사용되고 있다. 최근에는 꼬임이 22TPI(twist per inch)인 30's의 면사, 25TPI인 40's의 면사, 28TPI인 50's의 면사 그리고 31TPI인 60's의 면사가 주로 사용되고 있다. 이들 각각의 연계수를 환산하여 보면, 30's는 4.02TM, 40's는 3.95TM, 50's는 3.96TM, 60's는 4.0TM이 되므로, 번수는 각각 다르지만, 연계수는 4.0 정도로 거의 동일한 것을 알 수 있다.The linkage is the ratio of the square root of the twist and the number of times.In general, when the linkage (TM) is multiple between 4.0 and 5.0, the strength is greatest. Cotton yarns of about 4.0 are frequently used for the production of single jersey knit fabrics. Recently, 30's cotton yarn with twist of 22TPI (twist per inch), 40's cotton yarn with 25TPI, 50's cotton yarn with 28TPI and 60's cotton yarn with 31TPI are mainly used. In terms of the number of linkages, the 30's are 4.02TM, the 40's are 3.95TM, the 50's are 3.96TM, and the 60's are 4.0TM.

그러나 꼬임이 형성된 실은 장력이 제거되면 저절로 서로 말리는 스날(snal) 현상이 발생하게 된다. 상기에서 스날이란, 꼬임이 형성된 실에 발생하는 현상으로서, 실에 가해진 장력이 제거되면 실이 저절로 말리는 현상을 말한다. 이는 면사가 천연섬유인 셀룰로오스로 이루어져 있기 때문인데, 셀룰로오스는 결정화도가 높아서 가연(twist)이 되면 섬유가 꼬인 상태에서 쉽게 안정되지 않는데 이러한 현상은 잔류응력(residual stress)이 작용하기 때문이다. 이러한 면사의 스날현상으로 인하여 편성된 후에 편물이 틀어지는 현상이 발생하게 된다. However, the twisted yarns are caused to have a snal phenomenon in which they spontaneously dry when tension is removed. In the above description, the term "snare" is a phenomenon occurring in a thread having a twist formed, and refers to a phenomenon in which the thread is spontaneously dried when the tension applied to the thread is removed. This is because cotton yarn is made of cellulose which is a natural fiber. The cellulose has high crystallinity and is not easily stabilized in the twisted state when twisted. This phenomenon is caused by residual stress. Due to the phenomena of the yarn of cotton yarn, a knitting phenomenon occurs after being knitted.

일반적으로 실의 꼬임방향은 좌연(Z twist)과 우연(S twist)으로 나눌 수 있는데, 현재 환편기를 이용한 편직과정에서는 일반적으로 동일한 꼬임을 가진 하나의 면사를 하나의 니들에 공급하고 있다. 이때 면사의 스날 현상으로 인하여 편물이 틀어지게 된다.In general, the twisting direction of the yarn can be divided into Z twist and S twist. Currently, in the knitting process using a circular knitting machine, one cotton yarn having the same twist is generally supplied to one needle. At this time, the knitted fabric is twisted due to the yarn phenomenon of cotton yarn.

본 발명은 싱글 져지 편물의 뒤틀림 현상을 해결하기 위하여 환편기에 한 가닥의 면사 대신에 꼬임방향이 다른 2종의 면사를 하나의 니들에 공급하는 것을 특징으로 한다. 구체적으로는 실의 꼬임이 우연(S twist)인 면사 1올과 실의 꼬임이 좌연(Z twist)인 면사 한 올을 환편기 상의 하나의 니들에 공급한다. 이때 공급되는 실은 서로 꼬이지 않도록 공급하는 것이 바람직하다. The present invention is characterized by supplying two needles of different yarns in different twisting directions to one needle in order to solve the warping phenomenon of the single jersey knitted fabric. Specifically, one thread of cotton yarn with twist of thread and one thread of yarn twist with twist of thread is supplied to one needle on the circular knitting machine. At this time, it is preferable to supply the yarns so as not to twist each other.

이때 하나의 니들에 공급된 2올의 면사는 꼬임 방향이 서로 반대이기 때문에, 편성과정에서 서로의 꼬임 특성을 상쇄하게 된다. 그 결과 면사에 꾜임에 의해 발생하는 편물의 뒤틀림 현상 즉 스큐현상을 방지할 수 있다. 본 발명에서 제조된 싱글져지 편물은 세탁시에도 뒤틀림이 거의 발생하지 않는다.
In this case, since the yarns of the 2-ol supplied to one needle are twisted in opposite directions, the twisting properties of the two oles cancel each other's twisting characteristics in the knitting process. As a result, it is possible to prevent the warping phenomenon, that is, the skew phenomenon, of the knitted fabric caused by the pinching of the cotton yarn. The single jersey knit fabric produced in the present invention hardly causes distortion even during washing.

본 발명에서는 편물의 뒤틀림 현상을 최소화하기 위하여 추가적으로 면사의 적절한 연계수를 선택하는 것이 바람직하다. 본 발명에서 사용되는 면사는 연계수가 2.5TM 내지 4.0TM인 것이 바람직하다. 연계수가 2.5TM 미만인 경우에는 개별섬유의 뭉친 상태가 엉성하여 강력이 약해지게 되고, 연계수가 4.0TM 이상인 경우에는 면사의 잔류응력이 크기 때문에 스날 현상이 심하게 발생한다. 이러한 틀어짐 현상을 최소화하기 위하여 본 발명에서는 연계수가 2.5TM 내지 4.0TM인 것을 사용하는 것이 바람직하다.In the present invention, it is preferable to additionally select an appropriate number of yarns in order to minimize warping of the knitted fabric. The cotton yarn used in the present invention preferably has a linked number of 2.5 TM to 4.0 TM. If the number of joints is less than 2.5TM, the aggregated state of individual fibers is poor, and the strength is weakened. If the number of links is more than 4.0TM, a sharp phenomenon occurs due to the large residual stress of cotton yarn. In order to minimize this distortion, it is preferable to use a linkage of 2.5 TM to 4.0 TM in the present invention.

본 발명에서는 하나의 니들에 2올의 면사가 공급되기 때문에 면사의 굵기는 20~30's인 것이 바람직하다. 하나의 니들에 일반적인 굵기의 면사가 2올이 공급되는 경우 편성되는 직물의 두께는 두꺼워지게 된다. 이를 해결하기 위하여, 40~60's인 면사를 사용하는 것이 바람직하다. 굵기가 40's인 면사를 2올 사용하여 20's 한 올을 사용하는 경우와 유사한 두께와 중량을 나타내게 되고, 굵기가 60's인 면사를 2올 사용하여 30's를 한 올을 사용하는 경우와 유사한 효과를 나타낼 수 있다.
In the present invention, since two yarns of cotton yarn are supplied to one needle, the thickness of the cotton yarn is preferably 20 to 30's. If two needles of a general thickness of cotton thread are supplied to one needle, the thickness of the fabric to be knitted becomes thick. In order to solve this problem, it is preferable to use cotton yarn of 40 to 60's. It has a thickness and weight similar to that of using 20's single cotton with 2's of 40's cotton yarn, and shows similar effects to those of 30's using 2's of 60's cotton yarn. have.

이하에서는 첨부된 도면을 참조하여 본 발명을 상세하게 설명한다.Hereinafter, with reference to the accompanying drawings will be described in detail the present invention.

도 1은 본 발명에서 싱글편물을 제직하기 위하여 환편기의 니들에 면사를 공급하는 공정을 개략적으로 도시한 것이다.Figure 1 schematically shows a process for supplying cotton yarn to the needle of the circular knitting machine to weave a single knitted fabric in the present invention.

먼저 좌연(Z twist)을 갖는 제1 면사(11)와 우연(S twist)을 갖는 제2 면사(12)를 각각 준비한다. 이를 각각의 실공급기에 장착한 후, 제1가이드 장치(13)의 2개의 홀에 각각 통과시킨 후, 제2 가이드 장치(14)로 연속적으로 공급하여 2가닥의 실이 합사되게 한다. 제2 가이드장치(14)를 통과한 제1면사(11) 및 제2 면사(12)는 합사된 상태로 환편기의 니들(15)에 공급된다. 상기 제2 가이드 장치(14)는 환편기의 니들(15)에서 2올의 실이 합쳐져서 공급될 수 있도록 한다. 이때 공급된 각 실은 서로 꼬이지 않고 공급되도록 한다.First, a first cotton yarn 11 having a Z twist and a second cotton yarn 12 having a S twist are prepared. It is mounted on each thread feeder, and then passed through two holes of the first guide device 13, respectively, and then continuously supplied to the second guide device 14 so that the two strands of yarn are spun together. The first cotton yarn 11 and the second cotton yarn 12 that have passed through the second guide device 14 are supplied to the needle 15 of the circular knitting machine in a plyed state. The second guide device 14 allows the two balls of thread to be fed together from the needle 15 of the circular knitting machine. In this case, the supplied yarns are supplied without being twisted with each other.

니들(15)에 공급된 2올의 면사는 환편기를 통해 하나의 싱글 져지 편물로 편성된다. 이렇게 제조된 싱글져지 편물은 한올의 면사만을 사용한 경우와 비교하여, 꼬임방향이 상쇄되기 때문에 사행도(skewness)가 낮고 뒤틀림이 거의 발생하지 않는다.
The 2-ol cotton yarn supplied to the needle 15 is knitted into a single jersey knitted fabric through a circular knitting machine. The single jersey knitted fabric thus produced is low in skewness and hardly distorted because the twisting direction is canceled compared with the case of using only one cotton yarn.

이하에서는 구체적인 실시 예를 들어서 본 발명을 설명하지만, 실시예의 기재에 의해서 권리범위가 제한되어 해석되어서는 안 된다. Hereinafter, the present invention will be described with reference to specific examples, but the scope of the present invention should not be construed as being limited by the description of the embodiments.

실시예 1Example 1

좌연 3.5TM을 가진 면사 60's와 우연 3.5TM을 가진 면사 60's가 제1 가이드장치 및 제2 가이드장치를 통과하여 니들에 동시에 공급되도록 하여 싱글져지 편물을 제조하였다. 환편기는 (주)금용에서 제작한 싱글 져지 환편기를 사용하였다. 상기 환편기는 실린더 직경이 76cm(30인치), 게이지가 28(1인치당 바늘이 28개)이다. 따라서 니들 수는 2,640개이며 72피더를 사용하여 원통형 싱글져지 편물을 제조하였다. 제조된 싱글져지 편물은 세탁 후 140g/m2이었다. 제조된 편물을 개폭하고, 개폭선을 기준으로 편물의 사행도(skewness)를 측정하였다. A single jersey knit fabric was prepared by allowing a cotton yarn 60's with a left edge 3.5TM and a cotton yarn 60's with a chance 3.5TM to be fed simultaneously through the first guide device and the second guide device to the needle. Circular knitting machine used a single jersey circular knitting machine manufactured by Geumyong Co., Ltd. The circular knitting machine has a cylinder diameter of 76 cm (30 inches) and a gauge of 28 (28 needles per inch). Accordingly, the number of needles was 2,640 and a cylindrical single jersey knit fabric was prepared using 72 feeders. The single jersey knit fabric produced was 140 g / m 2 after washing. The knitted fabric was opened and the skewness of the knitted fabric was measured based on the opening line.

최종 편성된 원단은 개폭하여, 도 2와 같이 도시하였다. 개폭선을 기준선으로 하여 수평선(a)은 65인치이고, 원단이 올라간 부분(b)은 1.5인치이다. 이를 근거로 하여 편물의 사행도 (skewness)를 아래와 같이 계산하였다.The final knitted fabric was opened, as shown in FIG. The horizontal line (a) is 65 inches and the portion (b) where the fabric is raised is 1.5 inches based on the opening line. On the basis of this, the skewness of the knitted fabric was calculated as follows.

1.5"(b) / 65"(a) x 100 = 2.3%1.5 "(b) / 65" (a) x 100 = 2.3%

본 발명의 방법으로 제조된 편물의 사행도(코오스 스큐, 코오스 방향의 경사 진 각도)는 3%이내인 것을 알 수 있다.
It can be seen that the meandering degree (coarse skew, inclination angle in the coarse direction) of the knitted fabric produced by the method of the present invention is within 3%.

비교예 1Comparative Example 1

좌연 4.0TM을 가진 면사 30's 한올을 환편기의 니들에 공급한 것 이외에는 실시예 1과 동일한 방법으로 원통형 싱글 져지 편물을 제조하였다. 제조된 싱글져지 편물은 136g/cm2이다. A cylindrical single jersey knitted fabric was prepared in the same manner as in Example 1 except that a 30's hanol with a strand 4.0TM was supplied to the needle of the circular knitting machine. The single jersey knit fabric produced was 136 g / cm 2 .

상기 실시예 1과 동일한 방법으로 편물의 사행도(skewness)를 측정하였다.개폭선을 기준선으로 하여 수평선(a)은 65인치이고, 원단이 올라간 부분(b)은 20인치이다. 이를 이용하여 편물의 사행도 (skewness)는 아래의 식으로 계산하였다.The skewness of the knitted fabric was measured in the same manner as in Example 1. The horizontal line (a) was 65 inches and the portion (b) where the fabric was raised was 20 inches with the opening line as a reference line. Using this, the skewness of the knitted fabric was calculated by the following equation.

20"(b) / 65"(a) x 100 = 30.7%
20 "(b) / 65" (a) x 100 = 30.7%

Claims (4)

100% 면으로 이루어진 싱글 져지 편물의 제조방법에 있어서,
꼬임방향이 서로 다른 2올의 면사를 환편기의 하나의 니들에 동시에 공급하여 편성하고,
상기 서로 다른 2올의 면사는 각각 우연 또는 좌연인 것을 특징으로 하는 싱글 져지 편물의 제조방법.In the method of manufacturing a single jersey knitted of 100% cotton,
The two yarns of different twisting directions are fed to one needle of the circular knitting machine at the same time,
The cotton yarn of the two different olol is characterized in that the single jersey knit fabric, characterized in that each of the right or left edge. 삭제delete 청구항 1에 있어서,
상기 면사는 연계수(TM)가 2.5 내지 4.0인 것을 특징으로 하는 싱글 져지 편물의 제조방법.The method according to claim 1,
The cotton yarn manufacturing method of the single jersey knit, characterized in that the linkage (TM) is 2.5 to 4.0. 연계수(TM)가 2.5 내지 4.0인 우연 및 좌연 면사를 하나의 니들에 동시에 공급하여 편성되고, 편물의 무게가 80 내지 160g/m2인 싱글 져지 편물.A single jersey knit fabric having a joint number (TM) of 2.5 to 4.0 and a needle and a left margin cotton yarn simultaneously supplied to one needle, and having a weight of 80 to 160 g / m 2 .
KR1020100097180A 2010-10-06 2010-10-06 Method for Preparing Single Jersey Knitting Fabrics without Skew KR101191775B1 (en)