KR101182190B1 - Releasing paper manufactured by using environmentally friendly water based acrylic emulsion and manufacturing method the same - Google Patents
Releasing paper manufactured by using environmentally friendly water based acrylic emulsion and manufacturing method the same Download PDFInfo
- Publication number
- KR101182190B1 KR101182190B1 KR1020100074086A KR20100074086A KR101182190B1 KR 101182190 B1 KR101182190 B1 KR 101182190B1 KR 1020100074086 A KR1020100074086 A KR 1020100074086A KR 20100074086 A KR20100074086 A KR 20100074086A KR 101182190 B1 KR101182190 B1 KR 101182190B1
- Authority
- KR
- South Korea
- Prior art keywords
- acrylic emulsion
- aqueous acrylic
- release paper
- emulsion coating
- coating layer
- Prior art date
Abstract
본 발명은 수성 아크릴에멀젼 코팅제로 개선함으로서 기존 LDPE의 물성을 그대로 보전함과 동시에 폐기되는 이형지를 친환경적으로 리펄핑(repulping)하여 다시 종이원료로 재생할 수 있는 수성 아크릴 에멀젼을 이용한 이형지 및 그의 제조방법에 관한 것이다.
본 발명은, 점착면을 보호하며 사용할 때 벗겨지는 박리용 기지(基紙)류; 상기 기지류의 상부에 도포되며, 내용제성 및 내수성을 가지며 코팅성이 우수한 수성 아크릴에멀젼 코팅층; 및 상기 수성 아크릴 에멀젼 코팅층의 상부에 도포되며 점착층으로부터 쉽게 박리되도록 하는 실리콘층을 포함하는 수성 아크릴 에멀젼을 이용한 이형지를 제공한다.The present invention provides a release paper using a water-based acrylic emulsion that can be recycled as a paper raw material by repulping environmentally friendly waste paper, while maintaining the physical properties of the existing LDPE as it is improved by an aqueous acrylic emulsion coating agent, and a method for producing the same. It is about.
The present invention, the base for peeling off when used while protecting the adhesive surface; An aqueous acrylic emulsion coating layer coated on top of the matrix, having solvent resistance and water resistance, and having excellent coating properties; And a silicone layer applied on top of the aqueous acrylic emulsion coating layer and easily peeled off from the adhesive layer.
Description
본 발명은 점착테이프, 감압접착지, 라벨, 스티커 등의 점착면에 접촉시켜 면을 보호하는 이형지에 관한 것으로, 더욱 상세하게는 내열성과 내수성 및 내용제성이 있으며, 적은 함량으로도 코팅효과를 구현할 수 있는 수성 아크릴 에멀젼을 중간코팅재로 구성하여 폐기되는 이형지를 펄프로 재사용이 가능하도록 제조된 이형지 및 그의 제조방법에 관한 것이다.
The present invention relates to a release paper that protects the surface by contacting the adhesive surface such as adhesive tape, pressure-sensitive adhesive paper, label, sticker, more specifically, heat resistance, water resistance and solvent resistance, and can realize a coating effect with a small amount The present invention relates to a release paper and a method for producing the release paper, which can be reused as a pulp by forming an aqueous acrylic emulsion which may be formed of an intermediate coating material.
일반적으로, 이형지는 점착면에 접촉되어 면을 보호하고, 사용할 때에는 벗겨내어 목적을 달성할 수 있도록 표면가공되어 있는 것으로 정의되며, 이러한 이형지는 라벨, 스티커류, 인테리어용 점착필름(일명, PVC시트라 함) 및 각종 산업용 캐스팅용(합성피혁제조등) 등으로 광범위하게 사용되고 있다.In general, the release paper is defined as the surface is processed to contact the adhesive surface to protect the surface, peel off when used to achieve the purpose, such release paper is a label, stickers, interior adhesive film (aka, PVC sheet) And various industrial castings (synthetic leather manufacturing, etc.).
종래의 이형지는 크라프트지 또는 펄프함량이 많은 박리지를 최하부면으로 하되, 그 위에 저밀도 폴리에틸렌(Low density polyethylene)층과 실리콘층이 순차적으로 적층된 구성으로 되어 있다.Conventional release paper has a kraft paper or a release paper with a large amount of pulp as the bottom surface, and a low density polyethylene layer and a silicon layer are sequentially stacked thereon.
상기 이형지의 구성중에서 중간코팅층으로 사용되고 있는 물질인 LDPE는 석유화학레진이고 물에 용해되지 않기 때문에, 리사이클이 어렵고 사용후 폐기되어 소각 및 매립되고 있다. 특히, 이형지의 매립은 LDPE의 분해시간이 약 50년이상 소요되는 것에 기인하여 환경문제 발생요인중의 하나로 지적되고 있다.LDPE, which is a material used as an intermediate coating layer in the composition of the release paper, is a petrochemical resin and does not dissolve in water, so it is difficult to recycle and disposed of after incineration and landfill. In particular, the landfill of the release paper is pointed out as one of the causes of environmental problems due to the decomposition time of the LDPE takes about 50 years or more.
한편, 종래에는 리사이클이 가능한 방습지(공개번호 특2001-0029768/출원명:방습지)가 제안된 바 있다. 이는 합성고무계 라텍스와 아크릴계 에멀젼을 함유하는 수지조성물을 기지(基紙)상에 도포하여 방습층을 형성함으로써 방습지의 기본성능을 유지하고, 종이는 재생이 가능하도록 한 것이다. On the other hand, conventionally, a moisture-proof paper (public number 2001-0029768 / application name: moisture-proof paper) which can be recycled has been proposed. This is to apply a resin composition containing a synthetic rubber latex and an acrylic emulsion on a substrate to form a moisture barrier layer to maintain the basic performance of the moisture barrier paper, and to allow paper to be recycled.
상기한 구조는 합성고무계 라텍스와 아크릴계 에멀젼이 함유된 수지 조성물이 혼합물로 이루어져 있어 공정이 복잡하며, 코팅층 위에 실리콘처리가 되지 않은 방습지 상태로서 이형지와는 다른 유형의 제품이다.The above-described structure is a complex of the resin composition containing a synthetic rubber latex and an acrylic emulsion, the process is complicated, and is a type of product different from the release paper as a moisture-proof paper that is not siliconized on the coating layer.
이 밖에, 아크릴에멀젼을 이용한 방습지(공개번호 특2002-0012815/출원명:종이용 방습피막재의 제조방법및 그 피막재를 이용한 방습지) 기술이 제안되어 있으나, 이는 1차, 2차에 걸친 합성단계로 나뉘어져 있어 제조가 복잡한 단점이 있다. 즉, 1차로 합성수지를 합성한 다음, 1차로 합성된 합성수지와 또 다른 모노머를 반응시켜 2차 합성을 완성하며 2차합성제품에 왁스에멀젼을 혼합하여 피막제를 만들고 종이에 코팅하는 것으로 공정이 복잡한 문제점이 있다. In addition, a moisture-proof paper using an acrylic emulsion (Publication No. 2002-0012815 / Application Name: a method of manufacturing a moisture-proof film material for paper and a moisture-proof paper using the film material) has been proposed, but this is a synthesis step for the first and second It is divided into complex manufacturing disadvantages. In other words, the first step is to synthesize the synthetic resin first, and then react the first synthetic resin with another monomer to complete the second synthesis. There is this.
한편, 유성아크릴접착제를 석유계용제인 메탄올에 희석하여 종이에 코팅한 종이코팅공정과 그위에 실리콘액을 도포후 건조한 유사한 이형지(공개번호 10-2005-011949/출원명: 생리대용 실리콘 이형지 제조방법 및 실리콘이형지)가 제시되어 있으나, 이는 유성아크릴을 이용하고 있기 때문에 리펄핑(repulping)이 어려우며, 솔벤트인 메탄올을 사용하고 있기 때문에 진정한 친환경적 수성제품이라 하기가 어렵다.Meanwhile, a paper coating process in which oil-based acrylic adhesive is diluted in methanol, a petroleum solvent, and coated on paper, and a similar release paper dried after application of a silicone solution thereon (Publication No. 10-2005-011949 / And silicone release paper), but since it uses oily acrylic, it is difficult to repulping, and since it uses methanol as a solvent, it is difficult to say that it is a truly eco-friendly aqueous product.
따라서, 본 발명은 상기와 같은 제반 문제점을 해결하기 위해 제안된 것으로서, 이형지를 이루는 중간코팅층을 LDPE 대신에 내열성과 내수성 및 내용제성이 있으며, 적은 함량으로도 코팅효과를 구현할 수 있는 수성 아크릴에멀젼 코팅제로 개선함으로서 기존 LDPE의 물성을 그대로 보전함과 동시에 폐기되는 이형지를 친환경적으로 리펄핑(repulping)하여 다시 종이원료로 재생할 수 있는 수성 아크릴 에멀젼을 이용한 이형지 및 그의 제조방법을 제공함에 그 목적이 있다.
Therefore, the present invention has been proposed to solve the above problems, the heat-resistant, water-resistant and solvent-resistant instead of the LDPE intermediate coating layer forming a release paper, an aqueous acrylic emulsion coating agent that can realize a coating effect with a small amount The purpose of the present invention is to provide a release paper using a water-based acrylic emulsion that can be recycled as a paper material by repulping environmentally friendly waste paper and at the same time retaining the properties of the existing LDPE as it is improved.
상기 목적을 달성하기 위하여 본 발명은, 점착면을 보호하며 사용할 때 벗겨지는 박리용 기지(基紙)류; 상기 기지류의 상부에 도포되며, 내용제성 및 내수성을 가지며 코팅성이 우수한 수성 아크릴에멀젼 코팅층; 및 상기 수성 아크릴 에멀젼 코팅층의 상부에 도포되며 점착층으로부터 쉽게 박리되도록 하는 실리콘층을 포함하는 수성 아크릴 에멀젼을 이용한 이형지를 제공한다.In order to achieve the above object, the present invention, the base for peeling off when used to protect the adhesive surface; An aqueous acrylic emulsion coating layer coated on top of the matrix, having solvent resistance and water resistance, and having excellent coating properties; And a silicone layer applied on top of the aqueous acrylic emulsion coating layer and easily peeled off from the adhesive layer.
본 발명의 실시예에서, 상기 수성 아크릴 에멀젼 코팅층은 유리전이온도 -10℃ ~ 30℃를 가지며, 점도 100 ~ 200cps, 고형분45%으로 이루어진 것을 특징으로 한다. 또한, 상기 수성 아크릴에멀젼 코팅층은 유리전이온도가 낮은 접착성부여 단량체 55 ~70중량%에 유리전이온도가 높은 강도 부여 단량체 20 ~ 40중량%, 가교성 아크릴단량체 5~ 10중량%로 이루어지는 단량체혼합물을 제조하고, 상기 단량체혼합물 100중량부에 대하여 라디칼 중합반응개시제 0.5 ~ 1중량부 및 반응성 유화제 1 ~ 3중량부를 혼합한 후, 80℃ ~ 85℃의 온도로 유지되는 이온교환수에 3 ～ 5시간동안 적하하여 중합제조되는 것을 특징으로 한다.In an embodiment of the present invention, the aqueous acrylic emulsion coating layer has a glass transition temperature of -10 ℃ ~ 30 ℃, it characterized in that the viscosity consists of 100 ~ 200cps, solid content 45%. In addition, the aqueous acrylic emulsion coating layer is a monomer mixture consisting of 20 to 40% by weight of the high strength transition monomer, 20 to 40% by weight, crosslinkable acrylic monomer, 55 to 70% by weight of the adhesion-providing monomer having a low glass transition temperature To prepare 100 parts by weight of the monomer mixture, 0.5 to 1 parts by weight of the radical polymerization initiator and 1 to 3 parts by weight of the reactive emulsifier were mixed, and then 3 to 5 in ion-exchanged water maintained at a temperature of 80 ℃ to 85 ℃ It is dropwise added for a time, characterized in that the polymerization is produced.
또한, 본 발명은 상하로 접촉하며 그라비아 롤러로 이루어진 제1 롤러기구를 수성 아크릴에멀젼 코팅액 용기에 일부 함침시켜 회전하는 제1 단계; 상기 제1 롤러기구의 상부롤러에 기지류를 접촉한 상태로 이송하여 상기 기지류에 수성 아크릴에멀젼 코팅액을 그라비아코팅하는 제2 단계; 수성 아크릴에멀젼 코팅액이 도포된 기지류를 공정라인 상에 구비된 약 90℃ ~ 150℃의 제1 드라이어에 통과시켜 1차 아크릴 에멀젼 코팅층을 완성하는 제3 단계; 상하로 접촉하는 한쌍의 그라비아롤러 또는 일반 원형롤러중 어느 하나로 이루어진 구조의 제2 롤러기구를 실리콘액 용기에 일부 함침시키고, 상기 1차 수성 아크릴 에멀젼 코팅층이 형성된 기지류를 회전하는 제2 롤러기구의 상부롤러에 접촉하여 1차 수성 아크릴 에멀젼 코팅층면에 실리콘층을 도포하는 제4 단계; 및 상기 제3 단계의 1차 아크릴에멀젼 코팅공정과 동일한 온도의 제2 드라이어에 기지류를 통과시켜 실리콘 이형지를 완성하는 제5 단계를 특징으로 하는 수성 아크릴 에멀젼을 이용한 이형지의 제조방법을 제공한다.
In addition, the present invention is a first step of rotating by impregnating the first roller mechanism consisting of a gravure roller in contact with the top and bottom part of the aqueous acrylic emulsion coating liquid container; A second step of gravure coating an aqueous acrylic emulsion coating liquid on the matrix by transferring the matrix to the upper roller of the first roller mechanism; A third step of passing the matrix having the aqueous acrylic emulsion coating liquid applied thereto through a first dryer at about 90 ° C. to 150 ° C. provided on the process line to complete the primary acrylic emulsion coating layer; A second roller mechanism having a structure consisting of either a pair of gravure rollers or a general circular roller which is in contact with each other up and down is partially impregnated in the silicone liquid container, and the second roller mechanism for rotating the matrix having the primary aqueous acrylic emulsion coating layer formed thereon. A fourth step of applying a silicon layer on the surface of the primary aqueous acrylic emulsion coating layer in contact with the upper roller; And a fifth step of completing a silicone release paper by passing a known stream through a second dryer having the same temperature as the primary acrylic emulsion coating process of the third step.
전술한 바와 같이 본 발명의 특징에 따르면, 다음과 같은 효과가 있다.As described above, according to the features of the present invention, the following effects are obtained.
첫째, 본 발명의 이형지를 이루는 중간코팅층을 기존의 합성수지계인 LDPE 코팅층 대신에 친환경적이면서 내용제성 및 내수성이 있고, 얇은 코팅두께로 코팅효과를 낼 수 있는 특성을 가지는 수성 아크릴 에멀젼 코팅층으로 구성한다. 상기 수성 아크릴에멀젼이 코팅된 기지류는 물속에 담구었을 때 빠르게 용해됨으로써 이형지를 리펄핑하여 종이원료로 재사용이 가능하다.First, instead of the conventional synthetic resin-based LDPE coating layer, the intermediate coating layer forming the release paper of the present invention is composed of an aqueous acrylic emulsion coating layer having characteristics of being environmentally friendly, solvent resistant and water resistant, and having a coating effect with a thin coating thickness. The aqueous acrylic emulsion-coated matrix is rapidly dissolved when immersed in water, thereby repulsing a release paper and reused as a paper material.
둘째, 기존의 LDPE를 사용하는 박리지의 경우 천연펄프량을 많이 사용하는 반면에, 본 발명에서의 박리지는 기존 대비 약 20%만큼 펄프량이 적으며 가격도 저렴한 백상지를 기재류로 사용하기 때문에 친환경적이면서 경제적이다.Second, in the case of the release paper using the conventional LDPE, the amount of natural pulp is used a lot, while the release paper in the present invention uses about 100% less pulp and cheaper white paper as the base material. And economical.
셋째, 본 발명의 이형지 제조시 반응성유화제를 사용하여 내수성을 보강한 수성제품의 아크릴에멀젼 코팅제를 사용함으로써 공장에서의 화재위험이 적으며, 본 발명의 이형지를 이용한 제품제조시, 예를들어 PVC쉬트지를 제조시 정전기 발생이 적어 화재의 위험성을 줄일 수 있다.Third, the use of an acrylic emulsion coating agent of an aqueous product reinforced with water resistance using a reactive emulsifier in the manufacture of the release paper of the present invention has a low risk of fire in the factory, when manufacturing a product using the release paper of the present invention, for example, PVC sheet The production of paper makes the generation of static electricity less, reducing the risk of fire.
넷째, 중간코팅층인 수성 아크릴에멀젼층의 코팅두께가 기존 LDPE에 비해 1/3 ~ 1/2정도로 얇게 할 수 있으므로, 이형지제조 또는 이형지를 이용한 제품 제조시 롤의 두께가 얇아져 취급이 용이하며, 운송비 절감효과가 있다.Fourth, since the coating thickness of the aqueous acrylic emulsion layer, which is an intermediate coating layer, can be made thinner by 1/3 to 1/2 than that of the existing LDPE, the roll thickness is thin when manufacturing a release paper or a product using a release paper, and handling is easy. There is a saving effect.
다섯째, 백상지에 코팅되는 수성 아크릴에멀젼 코팅액의 경제적인 도포량을 통하여 이형지 제조단가를 낮춤으로써 사용고객들의 경제적인 이익에 기여할 수 있다.
Fifth, it is possible to contribute to the economic benefit of the customer by reducing the release paper manufacturing cost through the economical coating amount of the aqueous acrylic emulsion coating liquid coated on the white paper.
도1은 본 발명에 의한 이형지 제조장치의 구성을 나타낸 개략적인 공정도이다.1 is a schematic process diagram showing the configuration of a release paper manufacturing apparatus according to the present invention.
상술한 목적, 특징들 및 장점은 첨부된 도면과 관련한 다음의 상세한 설명을 통하여 보다 분명해 질 것이다. 이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 상세히 설명한다.The above-mentioned objects, features and advantages will become more apparent from the following detailed description in conjunction with the accompanying drawings. Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.
본 발명에 의한 수성 아크릴 에멀젼을 이용하여 제조된 이형지 및 그의 제조방법은 이형지를 구성하는 중간코팅층을 수성 아크릴에멀젼으로 개선하여 기존의 LDPE의 물성을 보존하면서 폐기되는 이형지를 재생하여 종이원료로 재사용이 가능하도록 구현한 것이다.The release paper produced using the aqueous acrylic emulsion according to the present invention and a manufacturing method thereof are improved by the intermediate coating layer constituting the release paper into an aqueous acrylic emulsion to recycle the release paper discarded while preserving the properties of the existing LDPE to reuse as a paper material. It is implemented to be possible.
본 발명에 따른 이형지는 점착면을 보호하며 사용할 때 벗겨지는 박리용 기지(基紙)류와; 상기 기지류의 상부에 도포되며, 내용제성 및 내수성을 가지는 수성 아크릴에멀젼 코팅층; 및 상기 수성 아크릴에멀젼 코팅층의 상부에 적층되며 점착층으로부터 쉽게 박리되도록 하는 실리콘층을 포함한다.Release paper according to the present invention protects the adhesive surface and peels off the base when used (base); An aqueous acrylic emulsion coating layer coated on top of the matrix and having solvent resistance and water resistance; And a silicon layer laminated on top of the aqueous acrylic emulsion coating layer and easily peeled off from the adhesive layer.
상기한 구성을 포함하는 본 발명에서, 실리콘 이형지를 만들기 위해서는 2차공정인 실리콘코팅층의 표면균열이나 변형현상을 방지하기 위한 전처리공정인 종이상단의 중간코팅공정이 필수적이다.In the present invention including the above-described configuration, in order to make the silicone release paper, an intermediate coating step of the upper end of the paper, which is a pretreatment step for preventing surface cracking or deformation of the silicon coating layer, which is a secondary process, is essential.
이형지의 중간코팅층으로 도포되는 수성 아크릴 에멀젼 코팅층은 종래의 합성수지계인 LDPE 코팅층을 대신하는 것으로서 액상으로 제조되며, 친환경적이면서 내용제성 및 내수성이 있고, 얇은 코팅두께로 코팅효과를 구현할 수 있는 특성을 가진다. The aqueous acrylic emulsion coating layer applied as the intermediate coating layer of the release paper is manufactured in liquid form as a substitute for the LDPE coating layer, which is a conventional synthetic resin, and is environmentally friendly, has solvent resistance and water resistance, and has a characteristic of implementing a coating effect with a thin coating thickness.
따라서, 본 발명의 수성 아크릴 에멀젼 코팅층을 기지류와 실리콘층 중간에 도포함으로써 제지사에서 이형지용으로 사용되는 펄프함량이 많은 박리지를 배제하고 펄프함량이 적은 일반 백상지를 사용하여 이형지를 제조할 수 있게 된다.Accordingly, by applying the aqueous acrylic emulsion coating layer of the present invention in the middle of the base and the silicone layer, it is possible to exclude the release paper with a lot of pulp content used for release paper in papermaking paper, and to produce a release paper using a normal white paper with a low pulp content. do.
본 발명의 실리콘 이형지에서 1차 코팅층으로 도포되는 수성 아크릴에멀젼 코팅액의 제조과정을 설명한다.A process for preparing an aqueous acrylic emulsion coating liquid applied as a primary coating layer on a silicone release paper of the present invention will be described.
상기 수성 아크릴에멀젼 코팅액은 유화중합시 반응성유화제를 사용하고 가교아크릴단량체로 중합공정을 완성하여 내수성, 내용제성, 코팅성이 우수한 특성을 가지도록 제조되는 것이다. The aqueous acrylic emulsion coating liquid is prepared to have excellent water resistance, solvent resistance and coating property by using a reactive emulsifier during emulsion polymerization and completing a polymerization process with a crosslinked acrylic monomer.
상기 수성 아크릴에멀젼 코팅액의 제조과정에서는 유리전이온도가 -10℃ ~ 30℃되도록 하는 것이 중요하며, 유리전이온도가 낮은 아크릴단량체, 유리전이온가 높은 아크릴단량체, 가교성 아크릴단량체의 적절한 선택 및 배합이 중요하다.In the manufacturing process of the aqueous acrylic emulsion coating liquid, it is important to make the glass transition temperature is -10 ℃ ~ 30 ℃, and the appropriate selection and blending of the acrylic monomer with a low glass transition temperature, the acrylic monomer with a high glass ion, the crosslinkable acrylic monomer It is important.
상기 수성 아크릴에멀젼 코팅액의 제조는 상기한 단량체들을 유화중합(계면활성제 존재하에 반응)하여 이루어지는데, 본 발명의 실시예에서는 코팅액 자체에 우수한 내수성을 부과하는 특성을 가진 반응성유화제를 사용하였다.The aqueous acrylic emulsion coating liquid is prepared by emulsion polymerization of the monomers (react in the presence of a surfactant). In the embodiment of the present invention, a reactive emulsifier having a property of imparting excellent water resistance to the coating liquid itself is used.
상기 반응성 유화제는 자체의 분자구조중에 불포화 결합을 갖고 있으며, 중합체의 연속상인 물에 용해되는 표면활성 모노머이다. 일반 에멀젼중합에 있어서는 보통 단량체총량의 1 내지 6중량%에 해당하는 비이온성 또는 음이온성유화제를 사용하나, 이러한 범용유화제는 기포발생, 코팅면의 밀착성과 내수성을 손상시키므로 이를 극복하기 위한 대안으로 최근에는 반응성유화제를 사용하는 방법이 널리 알려져 있다. The reactive emulsifier is a surface active monomer having an unsaturated bond in its molecular structure and dissolved in water, which is a continuous phase of the polymer. In general emulsion polymerization, nonionic or anionic emulsifiers are generally used in an amount of 1 to 6% by weight of the total amount of monomers. However, these general emulsifiers may cause foaming, impaired adhesion and water resistance of the coated surface, and as an alternative to overcome these problems, The method of using a reactive emulsifier is widely known.
상기 반응성유화제로는 소듐 비닐 설포네이트(sodium vinyl sulfonate), 소듐 파라 스티렌 설포네이트(sodium p-styrene sulfonate), 암모늄 폴리옥시에틸렌 알킬 설페이트(ammonium polyoxyethylene alkyl sulfate), 하기의 [구조식1]을 갖는 제품중 하나를 선택하여 사용한다.As the reactive emulsifier, sodium vinyl sulfonate, sodium p-styrene sulfonate, ammonium polyoxyethylene alkyl sulfate, a product having the following [formula 1] Select one and use it.
[구조식 1][Structural formula 1]
구체적으로, 상기 수성 아크릴 에멀젼 코팅액은 유리전이온도가 낮은 접착성부여 단량체 55 ~70중량%에 유리전이온도가 높은 강도 부여 단량체 20 ~ 40중량%, 가교성 아크릴단량체 5~ 10중량%로 이루어지는 단량체혼합물과, 상기 단량체혼합물 총 중량부에 대하여 0.5 ~ 1중량부의 라디칼 중합반응개시제 및 1 ~ 3중량부의 반응성 유화제를 혼합하고, 이를 80℃ ~ 85℃의 온도로 유지되는 이온교환수에 3 ～ 5시간동안 적하한 후, 2 ~ 3시간 동안 추가교반작업을 통하여 합성을 완성한다.Specifically, the aqueous acrylic emulsion coating liquid is a monomer consisting of 20 to 40% by weight of the strength-providing monomer 20 to 40% by weight, high cross-linking acrylic monomer, 55 to 70% by weight of the adhesion-providing monomer having a low glass transition temperature The mixture and 0.5 to 1 parts by weight of a radical polymerization initiator and 1 to 3 parts by weight of a reactive emulsifier are mixed with respect to the total weight of the monomer mixture, which is then mixed with ion exchanged water maintained at a temperature of 80 ° C to 85 ° C. After dropping for an hour, the synthesis is completed by additional stirring for 2-3 hours.
상기한 조성으로 제조되는 수성 아크릴에멀젼 코팅액은 유리전이온도 -10℃ ~ 30℃를 가지며, 점도 100 ~ 200cps, 고형분45%으로 이루어진다. 상기에서 얻어진 수성 아크릴에멀젼 코팅액 조성물에 코팅성을 좋게 하기 위하여 증점제를 사용하여 점도조정이 가능하다.The aqueous acrylic emulsion coating liquid prepared with the above composition has a glass transition temperature of -10 ° C to 30 ° C, and has a viscosity of 100 to 200cps and a solid content of 45%. Viscosity adjustment is possible using a thickener in order to improve the coatability in the aqueous acrylic emulsion coating liquid composition obtained above.
본 발명의 수성 아크릴에멀젼 코팅액 조성물에서, 유리전이온도가 낮은 접착성 부여 단량체로는 부틸 크릴레이트(n-Butylacrylate ), 2-에틸핵실아크릴레이트(2-Ethylhexylacrylate), 라우릴메타아크릴레이트(Laurylmethacrylate), 에틸아크릴레이트(Ethylacrylate )로 구성되는 그룹에서 선택된 적어도 1종 이상이 사용된다. In the aqueous acrylic emulsion coating solution composition of the present invention, the adhesion imparting monomer having a low glass transition temperature is butyl acrylate (n-Butylacrylate), 2-ethylnuclear acrylate (2-Ethylhexylacrylate), laurylmethacrylate (Laurylmethacrylate) , At least one selected from the group consisting of ethylacrylate is used.
유리전이온도가 높은 강도 부여 단량체로는 메틸메타아크릴레이트(Methylmethacrylate ), 에틸메타아크릴레이트(Ethylmethacrylate), 스티렌(Styrene), 터셔리 부틸 메타아크릴레이트(t-Butylmethacrylate)으로 구성되는 그룹에서 선택된 적어도 1종 이상이 사용된다. At least one selected from the group consisting of methyl methacrylate, ethyl methacrylate, styrene, and tertiary butyl methacrylate as a monomer having high glass transition temperature. More than one species are used.
가교성 아크릴 단량체로는 메타크릴산(Methacrylic acid), 2-하이드록시에틸 메타크릴레이트(2-Hydroxyethyl methacrylate), 이타콘산(Itaconic acid ), 아크릴아마이드(Acrylamide)로 구성되는 그룹에서 선택된 적어도 1종 이상이 사용된다.Crosslinkable acrylic monomers include at least one selected from the group consisting of methacrylic acid, 2-hydroxyethyl methacrylate, itaconic acid, and acrylamide The above is used.
본 발명의 실리콘 이형지는 단면이형지의 경우, 기재(백상지)/아크릴코팅층/실리콘층으로 구성되며, 양면이형지의 경우 기재의 양면에 단면과 같은 코팅작업을 수행함으로써 실리콘층/아크릴코팅층/기재/아크릴코팅층/실리콘층의 구조를 갖는다.In the case of the cross-sectional release paper, the silicone release paper of the present invention is composed of a substrate (white paper) / acrylic coating layer / silicone layer, and in the case of double-sided release paper, a silicone layer / acrylic coating layer / substrate / acrylic is performed by performing the same coating operation on both sides of the substrate. It has a structure of coating layer / silicon layer.
상기 실리콘 이형지의 주요부인 수성 아크릴 에멀젼 코팅액은 내용제성 및 내수성 외에도 우수한 내열성, 방습성을 나타낸다.The aqueous acrylic emulsion coating liquid, which is a main part of the silicone release paper, exhibits excellent heat resistance and moisture resistance in addition to solvent resistance and water resistance.
따라서, 본 발명의 실리콘 이형지는 합성피혁 또는 기타 필름캐스팅용으로 사용될 경우, 상기 수성 아크릴 에멀젼 코팅층이 가지고 있는 내열, 내용제 특성을 활용하여 내열성 이형지로 사용될 수 있다.Therefore, when the silicone release paper of the present invention is used for synthetic leather or other film casting, it can be used as a heat-resistant release paper utilizing the heat and solvent properties of the aqueous acrylic emulsion coating layer.
또한, 종이제품 포장지인 방습용 포장재로 사용할 경우에도, 상기 수성 아크릴 에멀젼 코팅층이 가지고 있는 방습성을 활용하여 수분에 민감한 인쇄용 평판종이제품등의 최종 포장재로 사용될 수 있다.In addition, even when used as a moisture-proof packaging material that is a paper product packaging paper, it can be used as a final packaging material such as printing plate paper products sensitive to moisture by utilizing the moisture resistance of the aqueous acrylic emulsion coating layer.
본 발명에 의한 실리콘 이형지의 제조과정을 도1을 참조하여 설명하면 다음과 같다.Referring to Figure 1 describes the manufacturing process of the silicone release paper according to the present invention.
도면에 도시한 바와 같이, 상하로 접촉하며 그라비아 롤러로 이루어진 제1 롤러기구(2)가 수용성 아크릴에멀젼 코팅액 용기(4)에 일부 함침된 채로 회전하고, 상기 제1 롤러기구(2)의 상부롤러(2a)에 기지류(백상지)(6)를 접촉한 상태로 이송하여 상기 기지류(6)에 수성 아크릴에멀젼 코팅액을 그라비아 코팅한다. 그리고, 수성 아크릴에멀젼 코팅액이 도포된 기지류(6)를 공정라인 상에 구비된 약 90℃ ~ 150℃의 제1 드라이어(dryer)(8)에 10 ~ 20초간 통과시켜 코팅두께가 5 ~ 15u가 되는 1차 아크릴 에멀젼 코팅층을 완성한다.As shown in the figure, the
다음, 상하로 접촉하는 한쌍의 그라비아 롤러나 일반 원형롤러로 이루어진 구조의 제2 롤러기구(10)를 실리콘액 용기(12)에 일부 함침시키고, 상기 1차 수성 아크릴 에멀젼 코팅층이 형성된 기지류(2)를 회전하는 제2 롤러기구(10)의 상부롤러(10a)에 접촉하여 1차 수성 아크릴 에멀젼 코팅층면에 실리콘층을 도포한다. 그리고, 1차 수성 아크릴에멀젼 코팅공정과 동일한 온도의 제2 드라이어(14)에 통과시켜 실리콘 이형지를 완성한 후, 권취기(winding)(16)에서 감아 제품화한다. 상기 2차 실리콘 코팅공정에서 실리콘용액의 제조는 유효성분의 함량이 30중량%인 실리콘 폴리머100중량부에 유기용제 톨루엔을 300 ~ 700중량부를 희석하고, 경화제 1중량부를 첨가하여 제조한다.Next, the
상기한 공정으로 이루어진 실리콘 이형지의 제조과정에서, 공정단축과 연속작업을 위하여 고형분100%의 실리콘폴리머를 사용하고 경화제 4 ~5중량%를 혼합한 실리콘용액을 사용할 수도 있음은 주지의 사실이다.In the manufacturing process of the silicone release paper made of the above-described process, it is well known that a silicone solution of 100% solids and a mixture of 4 to 5% by weight of a curing agent may be used for process shortening and continuous operation.
이상에서 설명한 본 발명은 전술한 실시예 및 첨부된 도면에 의해 한정되는 것이 아니고, 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 통상의 지식을 가진자에게 있어 명백할 것이다.
The present invention described above is not limited to the above-described embodiment and the accompanying drawings, and will be apparent to those skilled in the art without departing from the technical spirit of the present invention.
2: 제1 롤러기구 4: 아크릴에멀젼 코팅액 용기
6: 기지류 8: 제1 드라이어
10: 제2 롤러기구 12: 실리콘액 용기
14: 제2 드라이어 16: 권취기2: first roller mechanism 4: acrylic emulsion coating liquid container
6: Base stream 8: 1st dryer
10: second roller mechanism 12: silicone liquid container
14: 2nd dryer 16: winder
Claims (5)
상기 기지류의 상부에 도포되며, 내용제성 및 내수성을 가지며 코팅성이 우수한 수성 아크릴에멀젼 코팅층; 및
상기 수성 아크릴 에멀젼 코팅층의 상부에 도포되며 점착층으로부터 쉽게 박리되도록 하는 실리콘층
을 포함하는 수성 아크릴 에멀젼을 이용하여 제조된 이형지.
Peeling bases that protect the adhesive surface and are peeled off when used;
An aqueous acrylic emulsion coating layer coated on top of the matrix, having solvent resistance and water resistance, and having excellent coating properties; And
A silicone layer applied on top of the aqueous acrylic emulsion coating layer and easily peeled off from the adhesive layer
Release paper produced using an aqueous acrylic emulsion comprising a.
상기 수성 아크릴에멀젼 코팅층은 유리전이온도 -10℃ ~ 30℃를 가지며, 점도 100 ~ 200cps, 고형분45%으로 이루어진 것을 특징으로 하는 수성 아크릴 에멀젼을 이용하여 제조된 이형지.
The method of claim 1,
The aqueous acrylic emulsion coating layer has a glass transition temperature -10 ℃ ~ 30 ℃, the release paper produced using an aqueous acrylic emulsion, characterized in that the viscosity consists of 100 ~ 200cps, solid content 45%.
상기 수성 아크릴에멀젼 코팅층은 접착성부여 단량체 55 ~70중량%에 강도 부여 단량체 20 ~ 40중량%, 가교성 아크릴단량체 5~ 10중량%을 혼합한 단량체혼합물을 제조하고, 상기 단량체혼합물 100중량부에 대하여 라디칼 중합반응개시제 0.5 ~ 1중량부 및 반응성 유화제 1 ~ 3중량부를 혼합한 후, 80℃ ~ 85℃의 온도로 유지되는 이온교환수에 3 ～ 5시간동안 적하하여 제조된 것을 특징으로 하는 수성 아크릴 에멀젼을 이용하여 제조된 이형지.
The method according to claim 1 or 2,
The aqueous acrylic emulsion coating layer prepared a monomer mixture of 55 to 70% by weight of the adhesion-providing monomer to 20 to 40% by weight of the strength imparting monomer, 5 to 10% by weight of the crosslinkable acrylic monomer, to 100 parts by weight of the monomer mixture. Aqueous 0.5 to 1 part by weight of a radical polymerization initiator and 1 to 3 parts by weight of a reactive emulsifier are mixed, and then dropwise added to ion-exchanged water maintained at a temperature of 80 ° C. to 85 ° C. for 3 to 5 hours. Release paper made using acrylic emulsion.
상기 접착성 부여 단량체는 부틸 크릴레이트(n-Butylacrylate ), 2-에틸핵실아크릴레이트(2-Ethylhexylacrylate), 라우릴메타아크릴레이트(Laurylmethacrylate), 에틸아크릴레이트(Ethylacrylate )로 구성되는 그룹에서 선택된 적어도 1종 이상이 사용되고;
상기 강도 부여 단량체는 메틸메타아크릴레이트(Methylmethacrylate ), 에틸메타아크릴레이트(Ethylmethacrylate), 스티렌(Styrene), 터셔리 부틸 메타아크릴레이트(t-Butylmethacrylate)으로 구성되는 그룹에서 선택된 적어도 1종이상이 사용되며;
상기 가교성 아크릴 단량체는 메타크릴산(Methacrylic acid), 2-하이드록시에틸 메타크릴레이트(2-Hydroxyethyl methacrylate), 이타콘산( Itaconic acid ), 아크릴아마이드(Acrylamide)으로 구성되는 그룹에서 선택된 적어도 1종이상이 사용되는 것을 특징으로 하는 수성 아크릴 에멀젼을 이용하여 제조된 이형지.
The method of claim 3, wherein
The adhesion-providing monomer is at least one selected from the group consisting of butyl acrylate (n-Butylacrylate), 2-ethylhexylacrylate, 2-laurylmethacrylate, Laurylmethacrylate, and ethylacrylate. More than one species are used;
The strength-providing monomer is at least one selected from the group consisting of methyl methacrylate (Methylmethacrylate), ethyl methacrylate (Ethylmethacrylate), styrene (styrene), tertiary butyl methacrylate (t-Butylmethacrylate) is used ;
The crosslinkable acrylic monomer is at least one selected from the group consisting of methacrylic acid, 2-hydroxyethyl methacrylate, itaconic acid, and acrylamide. Release paper produced using an aqueous acrylic emulsion, characterized in that the above is used.
상기 제1 롤러기구의 상부롤러에 기지류를 접촉한 상태로 이송하여 상기 기지류에 수성 아크릴에멀젼 코팅액을 그라비아 코팅하는 제2 단계;
수성 아크릴에멀젼 코팅액이 도포된 기지류를 공정라인 상에 구비된 90℃ ~ 150℃의 제1 드라이어에 통과시켜 1차 수성 아크릴 에멀젼 코팅층을 완성하는 제3 단계;
상하로 접촉하는 한쌍의 그라비아롤러 또는 일반 원형롤러중 어느 하나로 이루어진 구조의 제2 롤러기구를 실리콘액 용기에 일부 함침시키고, 상기 1차 수성 아크릴 에멀젼 코팅층이 형성된 기지류를 회전하는 제2 롤러기구의 상부롤러에 접촉하여 1차 수성 아크릴 에멀젼 코팅층면에 실리콘층을 도포하는 제4 단계; 및
상기 제3 단계의 1차 수성 아크릴 에멀젼 코팅공정과 동일한 온도의 제2 드라이어에 기지류를 통과시켜 실리콘 이형지를 완성하는 제5 단계
를 특징으로 하는 수성 아크릴 에멀젼을 이용하여 제조된 이형지의 제조방법.A first step of rotating the first roller mechanism in contact with the top and bottom by partially impregnating the first roller mechanism of the gravure roller in the aqueous acrylic emulsion coating liquid container;
A second step of gravure coating the aqueous acrylic emulsion coating liquid on the matrix by transferring the matrix to the upper roller of the first roller mechanism;
A third step of passing the matrix having the aqueous acrylic emulsion coating solution applied thereto through a first dryer at 90 ° C. to 150 ° C. provided on the process line to complete the primary aqueous acrylic emulsion coating layer;
A second roller mechanism having a structure consisting of either a pair of gravure rollers or a general circular roller which is in contact with each other up and down is partially impregnated in the silicone liquid container, and the second roller mechanism for rotating the matrix having the primary aqueous acrylic emulsion coating layer formed thereon. A fourth step of applying a silicon layer on the surface of the primary aqueous acrylic emulsion coating layer in contact with the upper roller; And
A fifth step of completing the silicone release paper by passing a known stream through the second dryer at the same temperature as the first aqueous acrylic emulsion coating process of the third step
Method for producing a release paper produced using an aqueous acrylic emulsion characterized in that.