KR101178029B1 - Pattern formation method of original materials through press process - Google Patents
Pattern formation method of original materials through press process Download PDFInfo
- Publication number
- KR101178029B1 KR101178029B1 KR1020110132656A KR20110132656A KR101178029B1 KR 101178029 B1 KR101178029 B1 KR 101178029B1 KR 1020110132656 A KR1020110132656 A KR 1020110132656A KR 20110132656 A KR20110132656 A KR 20110132656A KR 101178029 B1 KR101178029 B1 KR 101178029B1
- Authority
- KR
- South Korea
- Prior art keywords
- pattern
- surface finishing
- raw material
- veneer
- finishing member
- Prior art date
Abstract
Description
본 발명은 프레스 공정을 통한 원재의 패턴 형성공법에 관한 것으로, 더욱 상세하게는 열프레스 공정을 통해 인테리어 재료 또는 가구 등의 원재에 일정한 패턴을 형성할 때 패턴의 성형이 원활하게 이루어지도록 한 것이다.The present invention relates to a pattern forming method of a raw material through a pressing process, and more particularly, to form a pattern when forming a predetermined pattern on the raw material, such as interior materials or furniture through a heat press process.
주지하다시피, 건축물을 시공함에 있어서 인테리어는 매우 중요하며, 인테리어가 고급스럽게 될 때 건물의 가치는 올라가게 된다.As is well known, the interior is very important in the construction of the building, and the value of the building increases when the interior becomes luxurious.
이와 같이, 인테리어의 고급 여부가 건물의 가치를 높이는 중요한 요인이 되기 때문에 업체에서는 인테리어재료를 고급화하기 위해 인테리어의 재료가 되는 패널의 표면에 다양한 패턴을 형성하여 그 가치를 높여주기 위한 노력을 기울이고 있다.As such, whether or not the quality of the interior is an important factor to increase the value of the building, the company is making efforts to increase the value by forming various patterns on the surface of the panel, which is the material of the interior, to enhance the interior material. .
또한, 가구 등을 제작할 때에도 가구의 표면에 다양한 패턴을 형성하여 가구의 가치를 높여주고 있다.In addition, when manufacturing furniture, etc., various patterns are formed on the surface of the furniture to increase the value of the furniture.
이를 위하여 종래에는 MDF 등으로 이루어진 원판 위에 무늬목과 같은 표면 마감부재를 부착하고, 이를 열프레스 기기에 투입하여 옆프레스의 높은 온도와 높은 압력에 의해 원재의 표면을 압착하여 일정한 패턴을 형성하고 있다.To this end, conventionally, a surface finishing member such as veneer is attached to a disc made of MDF, and put into a heat press machine, thereby compressing the surface of the raw material by high temperature and high pressure of the side press to form a predetermined pattern.
그러나, 상기의 열프레스에 의한 패턴 형성공법의 경우 원판이 얇은 경우에는 어느 정도의 패턴 형성이 가능하지만 원판의 두께가 두꺼워지는 경우 원판의 표면 밀도가 높아지게 되므로 원하는 만큼의 요철을 구현하지 못하여 결국 패턴의 볼륨감을 원활하게 표현하기 어려웠으며, 이를 극복하기 위하여 100℃ 이상의 높은 온도범위와 이탈리아, 독일 등 외국의 경우 30,000t 정도의 큰 규모를 갖는 프레스기기를 적용하였으므로 소비전력 및 설비비가 증가되는 문제가 있었다. 국내의 경우 현재에도 1,000t 이하의 소형 프레스 기기를 적용하고 있으므로 볼륨감 미비 등 상기한 문제점을 전혀 해결하지 못하고 있는 실정이다.However, in the case of the pattern forming method by the heat press, when the disc is thin, a certain amount of pattern can be formed, but when the thickness of the disc becomes thick, the surface density of the disc becomes high, so that the pattern cannot be realized as much as desired. It was difficult to express the sense of volume smoothly. In order to overcome this problem, the press equipment having a high temperature range of 100 ℃ or higher and a large scale of about 30,000t was applied in foreign countries such as Italy and Germany. there was. In the case of domestic, even a small press device of less than 1,000t is currently applied to the situation that does not solve the above problems, such as lack of volume sense.
다른 방법으로, MDF 등으로 이루어진 원판 위에 반죽 목분(이하 곤죽이라 칭함)을 도포하고 건조한 후 열프레스 기기에 투입하여 건조된 곤죽의 열변형 특성을 이용하여 패턴을 형성하고, 후공정에서 무늬목과 같은 표면 마감부재를 패턴이 형성된 부위에 맞게 부착시켜주는 방법이 있는데, 이럴 경우 표면 마감부재가 합성수지재 시트와 같이 늘어나는 성질을 갖는 것이면 표면 마감부재를 패턴이 형성되어 있는 원재의 표면 굴곡을 따라 표면 마감부재의 부착이 가능하지만 표면 마감부재가 무늬목, 종이 등과 같이 늘어나는 성질이 없는 경우에는 패턴이 형성되어 있는 원재의 표면 굴곡을 따라 표면 마감부재를 세밀하게 부착할 수 없어 최종 제품의 가치가 떨어지는 단점이 있게 된다. 즉, 상기한 공법의 경우 후공정에서 표면 마감부재를 패턴 형성위치를 따라 부착시켜주는 공정이 매우 어렵고, 다양한 표면 마감부재를 사용할 수 없는 단점이 있는 것이었다.Alternatively, apply dough wood powder (hereinafter referred to as konjac) on a disc made of MDF, and dry it, and then put it into a heat press machine to form a pattern by using the heat deformation characteristics of the dried konjac, There is a method of attaching the surface finishing member to the patterned part. In this case, if the surface finishing member has the property of stretching like a synthetic resin sheet, the surface finishing member is finished along the surface curvature of the patterned raw material. If the member can be attached but the surface finishing member is not stretched like veneer or paper, it is impossible to attach the surface finishing member finely along the surface curvature of the raw material on which the pattern is formed. Will be. That is, in the case of the above method, the process of attaching the surface finishing member along the pattern forming position in the post process is very difficult, and various surface finishing members cannot be used.
본 발명은 이러한 점을 감안하여 제안된 것으로, 열프레스 공정을 통해 인테리어 재료 또는 가구 등의 원재에 일정한 패턴을 형성할 때 패턴의 성형이 원활하게 이루어지도록 한 프레스 공정을 통한 원재의 패턴 형성공법을 제공하고자 하는 것이다.The present invention has been proposed in view of this point, and when forming a predetermined pattern on a raw material such as interior materials or furniture through a heat press process, the pattern forming method of the raw material through the press process to make the pattern is smoothly It is to provide.
이러한 과제를 해결하기 위해 본 발명은, 목재 원판의 표면에 성형부재를 피복하는 단계; 상기 성형부재의 표면에 표면 마감부재를 부착하는 단계; 및 상기 표면 마감부재가 부착된 원판을 패턴 금형이 형성되어 있는 열프레스 기기에 투입하여 원재의 표면에 패턴을 성형하는 단계를 포함한다.The present invention to solve this problem, the step of coating a molding member on the surface of the wooden disc; Attaching a surface finishing member to the surface of the molding member; And forming a pattern on the surface of the raw material by inserting the original plate having the surface finishing member attached to the heat press machine having the pattern mold formed thereon.
바람직하게는, 상기 성형부재는 반죽 목분으로 이루어지며, 상기 원판의 표면에 상기 반죽 목분을 피복한 후 건조하는 단계를 더 거칠 수 있다.Preferably, the molding member is made of dough wood powder, it may be more rough to the step of coating the dough wood powder on the surface of the disc and then drying.
바람직하게는, 상기 표면 마감부재는 무늬목, 종이, 천 중 선택된 재질로 이루어질 수 있다.Preferably, the surface finishing member may be made of a selected material of veneer, paper, cloth.
바람직하게는, 상기 열프레스 기기는 1000t 이하 규모의 열프레스 기기가 적용되며, 상기 열프레스 기기를 통해 가해지는 온도는 50~100℃ 범위일 수 있다.Preferably, the heat press device is a heat press device of a scale of 1000t or less is applied, the temperature applied through the heat press device may be in the range of 50 ~ 100 ℃.
바람직하게는, 상기 성형부재는 0.5㎜ ~ 5㎜의 두께로 이루어진 단판 무늬목으로 이루어지고, 상기 표면 마감부재는 0.15㎜ ~ 0.2㎜의 두께로 이루어진 표면 외장 무늬목으로 이루어질 수 있다.Preferably, the molding member is made of a veneer veneer made of a thickness of 0.5mm ~ 5mm, the surface finishing member may be made of a surface facing veneer made of a thickness of 0.15mm ~ 0.2mm.
본 발명은 목재 원판 위에 반죽 목분과 같은 성형부재를 도포하고, 성형부재 위에 무늬목과 같은 표면 마감부재를 부착한 상태에서 열프레스 기기에 투입하게 되므로 열프레스 기기의 열에 의해 성형부재가 열성 변형되면서 그 압력에 의해 열프레스 기기의 패턴 금형에 따라 성형부재와 표면 마감부재가 같이 함몰이 이루어지게 되어 패턴 형성이 원활히 이루어질 수 있는 것이며, 패턴 형성 후 별도의 마감공정없이 원재의 생산이 완료되는 것이다.The present invention is applied to a heat press machine while applying a molding member such as dough wood powder on a wooden disc, and attached a surface finishing member such as veneer on the molding member, so that the molding member is thermally deformed by the heat of the heat press machine. According to the pattern mold of the heat press machine by the pressure, the molding member and the surface finishing member are formed together, so that the pattern formation can be made smoothly, and after the pattern formation, the production of raw materials is completed without a separate finishing process.
따라서, 패턴의 성형이 이루어질 때 표면 마감부재가 성형부재의 함몰된 위치까지 정확하게 같이 함몰될 수 있어 패턴의 볼륨감을 살릴 수 있으며, 보다 작은 규모의 열플레스 기기를 사용하더라도 보다 원활하게 패턴을 성형할 수 있고, 표면 마감부재로서 무늬목, 종이, 천과 같이 늘어나지 않는 성질의 표면 마감부재를 적용하면서도 원활한 패턴 형성이 가능해지는 이점도 있게 된다.Therefore, when the pattern is formed, the surface finishing member can be accurately recessed to the recessed position of the molding member, thereby making it possible to save the volume of the pattern, and to form the pattern more smoothly even when using a smaller scale heatless device. It can be, while also applying a surface finishing member having a property that does not stretch, such as veneer, paper, cloth as the surface finishing member has the advantage that the seamless pattern can be formed.
또한, 종래 기술과 비교할 때 훨씬 작은 규모의 열프레스 기기를 적용할 수 있으므로 설비비가 적게 소요됨은 물론 설비가 차지하는 공간 역시 작아질 수 있으며, 동일 규모의 열프레스 기기를 적용하게 되면 생산성을 크게 증대시킬 수 있는 이점도 있는 것이다.In addition, compared to the prior art, it is possible to apply a much smaller scale of the heat press equipment, which requires less equipment costs, and also the space occupied by the equipment can be reduced. There is also an advantage.
도 1은 본 발명에 따른 프레스 공정을 통한 원재의 패턴 형성 공정도.
도 2는 본 발명에 따른 프레스 공정을 통한 원재의 패턴 형성 순서도.1 is a pattern forming process of the raw material through the pressing process according to the present invention.
Figure 2 is a flow chart of the pattern of the raw material through the pressing process according to the present invention.
이하, 본 발명을 제시되는 실시예 및 첨부된 도면에 따라 상세히 설명한다.Hereinafter, the present invention will be described in detail with reference to the embodiments shown in the attached drawings.
본 발명은 프레스 공정을 통해 원재에 일정한 패턴을 형성하기 위한 것으로, 도면상에 도시한 바와 같이 MDF와 같은 목재로 된 원판(1)의 표면에 성형부재(2)를 피복하고, 성형부재(2)의 표면에 표면 마감부재(3)를 부착하게 된다.The present invention is to form a predetermined pattern on the raw material through the pressing process, as shown in the figure coating the
이때, 원판(1)의 두께는 원재의 규격에 따라 3㎜ ~ 18㎜의 범위내에서 선택될 수 있으며, 성형부재(2)는 열성변형의 특성을 갖는 반죽 목분(이하, 곤죽이라 칭함)으로 구성함이 바람직하다. 이러한 곤죽은 목분에 접착제를 일정한 비율로 혼합한 것을 뜻하며, 시중에 유통되고 있는 곤죽을 적용하면 되므로 특별하게 그 함량, 목분의 종류, 접착제의 종류를 제한하지는 않는다.At this time, the thickness of the
곤죽을 원판(1)의 표면에 도포한 후 일정한 시간 동안 상온에서 건조하고, 표면 마감부재(3)의 이면에 접착제를 칠한 상태에서 상기 건조된 곤죽의 표면에 표면 마감부재(3)를 부착하게 된다.After applying the clay on the surface of the disc (1), and dried at room temperature for a predetermined time, and attaching the surface finishing member (3) to the surface of the dried clay in the state of applying an adhesive on the back surface of the surface finishing member (3) do.
표면 마감부재(3)는 후공정인 열프레스 공정에서의 열성 변형이 방지할 수 있도록 늘어나지 않는 성질을 갖는 무늬목, 종이, 천 등으로 구성함이 바람직하다.
이후, 성형부재(2)와 표면 마감부재(3)가 부착된 원판(1)을 패턴 금형이 형성되어 있는 열프레스 기기에 투입하게 되며, 열프레스 기기의 프레스금형이 내려와 성형부재(2)와 표면 마감부재(3)가 부착된 원판(1)과 접촉하게 되면 그 열기가 건조되어 있는 성형부재(2)를 이루는 곤죽에 가해지면서 곤죽이 연한 상태로 열성 변형되고, 이와 동시에 프레스금형의 압력에 의해 곤죽과 표면 마감부재(3)가 같이 눌리면서 일정한 패턴이 성형될 수 있는 것이다.Subsequently, the
도면상의 미설명 부호 4는 패턴 형성부위를 나타낸 것이다.Reference numeral 4 in the drawings indicates a pattern formation portion.
이와 같이 하면, 곤죽은 열프레스 기기의 열기에 의해 연한 상태로 열성 변형이 이루어짐과 동시에 프레스 금형에 의해 눌리게 되므로 이러한 곤죽 위에 부착되어 있는 표면 마감부재(3)가 찢어지지 않고 곤죽의 요철을 따라 같이 눌려지면서 보다 볼륨감있는 고품격의 패턴 성형이 이루어질 수 있게 된다.In this way, since the brittle is thermally deformed in the soft state by the heat of the heat press machine and is pressed by the press mold, the
또한, 본 발명에 적용되는 열프레스 기기는 1000t 이하 정도로 작은 규모의 열프레스 기기를 적용하여도 충분하며, 곤죽의 열성 변형 온도를 감안하여 열프레스 기기를 통해 가해지는 온도 역시 50~100℃ 범위로 낮게 설정할 수 있음은 자명하다.In addition, the heat press device to be applied to the present invention is sufficient to apply a heat press device of a small scale of about 1000t or less, the temperature applied through the heat press device in the range of 50 ~ 100 ℃ in consideration of the thermal deformation temperature of the gruel. It is obvious that it can be set low.
한편, 본 발명에서는 성형부재(2)로서 곤죽 대신 밀도가 MDF와 같은 원판(1)에 비해 상대적으로 낮은 단판 무늬목을 적용할 수도 있으며, 이러한 단판 무늬목은 패턴의 성형 두께를 감안하여 0.5㎜ ~ 5㎜의 두께로 이루어진 것을 선택하여 사용할 수 있다.On the other hand, in the present invention, as the
또한, 표면 마감부재(3)로는 0.15㎜ ~ 0.2㎜의 두께로 이루어진 표면 외장 무늬목으로 구성하여 열프레스의 압력에 의해 단판 무늬목과 표면 외장 무늬목이 한꺼번에 눌리면서 원활하게 패턴이 성형되게 할 수도 있다.In addition, the
그리고, 본 발명에서 설명하지는 않았지만 성형부재(2)로서 열프레스의 열기와 압력에 의해 쉽게 성형이 이루어질 수 있는 재질이면 무엇이든 적용할 수 있음은 자명하다.And, although not described in the present invention, it is obvious that the
1 : 원판 2 : 성형부재
3 : 표면 마감부재 4 : 패턴 형성부위1: disc 2: forming member
3: surface finishing member 4: pattern forming part
Claims (5)
상기 성형부재의 표면에 표면 마감부재를 부착하는 단계; 및
상기 표면 마감부재가 부착된 원판을 패턴 금형이 형성되어 있는 열프레스 기기에 투입하여 원재의 표면에 패턴을 성형하는 단계를 포함하여서 된 프레스 공정을 통한 원재의 패턴 형성공법.Coating a molding member on a surface of a wooden disc;
Attaching a surface finishing member to the surface of the molding member; And
The pattern forming method of the raw material through the pressing process comprising the step of forming a pattern on the surface of the raw material by inserting the disk with the surface finishing member is attached to the heat press machine with the pattern mold is formed.
상기 성형부재는 반죽 목분으로 이루어지며, 상기 원판의 표면에 상기 반죽 목분을 피복한 후 건조하는 단계를 더 거치는 것을 특징으로 하는 프레스 공정을 통한 원재의 패턴 형성공법.The method of claim 1,
The molding member is made of dough wood powder, the pattern forming method of the raw material through the pressing process, characterized in that further comprising the step of drying after coating the dough wood powder on the surface of the disc.
상기 표면 마감부재는 무늬목, 종이, 천 중 선택된 재질로 이루어진 것을 특징으로 하는 프레스 공정을 통한 원재의 패턴 형성공법.The method of claim 1,
The surface finishing member is a pattern forming method of the raw material through the pressing process, characterized in that made of a material selected from veneer, paper, cloth.
상기 열프레스 기기는 1000t 이하 규모의 열프레스 기기가 적용되며, 상기 열프레스 기기를 통해 가해지는 온도는 50~100℃ 범위인 것을 특징으로 하는 프레스 공정을 통한 원재의 패턴 형성공법.The method of claim 1,
The heat press device is a heat press device of a scale of 1000t or less is applied, the temperature forming method of the raw material through the pressing process, characterized in that the temperature applied through the heat press device ranges from 50 ~ 100 ℃.
상기 성형부재는 0.5㎜ ~ 5㎜의 두께로 이루어진 단판 무늬목으로 이루어지고, 상기 표면 마감부재는 0.15㎜ ~ 0.2㎜의 두께로 이루어진 표면 외장 무늬목으로 이루어진 것을 특징으로 하는 프레스 공정을 통한 원재의 패턴 형성공법.
The method of claim 1,
The molding member is made of a veneer veneer made of a thickness of 0.5mm ~ 5mm, the surface finishing member is formed of a pattern of the raw material through the pressing process, characterized in that made of a surface facing veneer made of a thickness of 0.15mm ~ 0.2mm Method.