KR101176036B1 - The composition of toothbrush and toothbrush manufactured thereby - Google Patents
The composition of toothbrush and toothbrush manufactured thereby Download PDFInfo
- Publication number
- KR101176036B1 KR101176036B1 KR20100060988A KR20100060988A KR101176036B1 KR 101176036 B1 KR101176036 B1 KR 101176036B1 KR 20100060988 A KR20100060988 A KR 20100060988A KR 20100060988 A KR20100060988 A KR 20100060988A KR 101176036 B1 KR101176036 B1 KR 101176036B1
- Authority
- KR
- South Korea
- Prior art keywords
- powder
- weight
- parts
- bristles
- toothbrush
- Prior art date
Abstract
본 발명은 칫솔모 조성물, 이를 이용한 칫솔모 및 치솔에 관한 것으로로 폴리프로필렌, 폴리에스테르, 폴리에틸렌, 폴리스틸렌, 폴리에틸렌테레프탈라이트, 폴리부틸렌테레프탈레이트, 폴리염화비닐, 폴리카보네이트, 폴리페닐렌 옥사이드, 폴리우레탄, 아크릴로니트릴, 실리콘 중 어느 하나 또는 둘 이상의 조합으로 구성되는 합성수지 레진에 매실 분말, 호두나무(잎 및 껍질) 분말, 상추 분말 및 은(Ag)을 함유하는 다공성 실리카 복합체 분말을 함유함을 특징으로 한다.The present invention relates to bristle compositions, bristles and toothbrushes using the same, polypropylene, polyester, polyethylene, polystyrene, polyethylene terephthalate, polybutylene terephthalate, polyvinyl chloride, polycarbonate, polyphenylene oxide, polyurethane, A resin composition composed of acrylonitrile, silicon, any one or a combination of two or more of them contains a porous silica composite powder containing plum powder, walnut (leaf and shell) powder, lettuce powder and silver (Ag). do.
Description
본 발명은 칫솔모 조성물에 관한 것으로 로 폴리프로필렌, 폴리에스테르, 폴리에틸렌, 폴리스틸렌, 폴리에틸렌테레프탈라이트, 폴리부틸렌테레프탈레이트, 폴리염화비닐, 폴리카보네이트, 폴리페닐렌 옥사이드, 폴리우레탄, 아크릴로니트릴, 실리콘 중 어느 하나 또는 둘 이상의 조합으로 구성되는 합성수지 레진에 매실 분말, 호두나무(잎 및 껍질) 분말, 상추 분말 및 은(Ag)을 함유하는 다공성 실리카 복합체 분말을 함유한 칫솔모용 수지 조성물 및 이를 이용한 칫솔모에 관한 발명이다.
The present invention relates to bristle compositions comprising polypropylene, polyester, polyethylene, polystyrene, polyethylene terephthalite, polybutylene terephthalate, polyvinyl chloride, polycarbonate, polyphenylene oxide, polyurethane, acrylonitrile, silicone Resin composition for bristles containing a porous silica composite powder containing plum powder, walnut tree (leaves and bark) powder, lettuce powder and silver (Ag) in a synthetic resin composed of any one or two or more combinations and bristles using the same Invention.
일반적으로 칫솔모는 나일론(나일론 612)이 주류를 이루고 있고, 일부 폴리부틸테레프탈레이트(PBT)가 이용되기도 한다. 그러나 지금까지 칫솔모를 위한 수지 조성물은 개발된 바 없었다.In general, bristles are mainly made of nylon (nylon 612), and some polybutyl terephthalate (PBT) is also used. However, until now, a resin composition for bristles has not been developed.
그 이유는 칫솔모의 재질 보다는 칫솔모의 가공 상태 즉, 칫솔모의 라운딩 정도에 따라 잇몸의 손상이나 치아의 건강 및 칫솔모의 수명이 결정되는 것으로 인식되고 있기 때문이다.This is because it is recognized that the damage of the gums, the health of the teeth and the life of the bristles are determined by the processing state of the bristles, that is, the degree of rounding of the bristles, rather than the material of the bristles.
그러나 최근에는 칫솔모의 재질이 치아의 건강이나 잇몸의 손상에 큰 영향을 미치는 연구결과들이 발표됨으로써 칫솔모의 재질에 대한 관심이 높아지고 있다.However, recently, research results in which the material of the bristles have a great influence on the health of the teeth and the damage of the gums have been published, and the interest in the materials of the bristles has increased.
국내특허 제352542호에는 항균성과 조습, 탈취 그리고 정화 등을 목적으로 숯분말을 혼합한 칫솔모에 관한 기술이 개시되어 있다. 상기의 기술은 항균성 등을 목적으로 하는 칫솔모의 재질에 관한 특허의 한 예일 뿐이다.
Korean Patent No. 352542 discloses a technique for bristle mixed with charcoal powder for the purpose of antibacterial, humidity control, deodorization and purification. The above technique is only one example of a patent relating to the material of the bristles for the purpose of antibacterial activity and the like.
이에 본 발명자는 로 폴리프로필렌, 폴리에스테르, 폴리에틸렌, 폴리스틸렌, 폴리에틸렌테레프탈라이트, 폴리부틸렌테레프탈레이트, 폴리염화비닐, 폴리카보네이트, 폴리페닐렌 옥사이드, 폴리우레탄, 아크릴로니트릴, 실리콘 중 어느 하나 또는 둘 이상의 조합으로 구성되는 합성수지 레진에 매실 분말, 호두나무잎 껍질 분말, 상추 분말 및 은(Ag)을 함유하는 다공성 실리카 복합체 분말을 함유한 칫솔모용 수지 조성물에 관한 것으로 상기의 수지 조성물을 이용한 칫솔모는 항균활성에 의해 구강염증을 예방할 수 있음은 물론, 이에 더해서 충치예방, 치아미백에 효과가 우수한 칫솔모 조성물 및 이들 이용한 칫솔모의 제조방법을 제공하는 데 있다.Accordingly, the inventors of the present invention any one or two of low polypropylene, polyester, polyethylene, polystyrene, polyethylene terephthalate, polybutylene terephthalate, polyvinyl chloride, polycarbonate, polyphenylene oxide, polyurethane, acrylonitrile, silicone It relates to a bristle resin composition containing a porous silica composite powder containing plum powder, walnut tree bark powder, lettuce powder and silver (Ag) in a synthetic resin composed of the above combination, the bristles using the resin composition is antibacterial In addition to preventing oral inflammation by activity, in addition to providing a bristle composition excellent in the prevention of tooth decay, tooth whitening, and a method for producing the bristles using these.
상기와 같은 목적을 달성하기 위하여 본 발명자는 오랫동안 연구한 결과, 매실에는 각종 비타민과 무기질이 풍부하게 들어있고 특히, 해독 및 살균력이 뛰어난 피크린산과 카네킨산을 다량 함유하고 있으며, 호두나무잎 껍질의 유글론은 살균작용이 뛰어나며, 상추는 치아미백에 가장 대표적인 식품으로는 상추에 함유되어 있는 섬유질 성분이 일종의 자정작용으로 치아에 붙어있는 플라그를 없애는 역할을 하고 치아미백 효과를 가지며, 은(Ag)을 함유하는 다공성 실리카 복합체는 항균성에 효과가 있다는 것은 이미 잘 알려진 사실이다.In order to achieve the above object, the present inventors have studied for a long time, and the plums are rich in various vitamins and minerals, and especially, they contain large amounts of picric acid and canine acid, which are excellent in detoxification and sterilization. Glon has excellent bactericidal action. Lettuce is the most representative food for tooth whitening. The fiber component of lettuce is a kind of self-cleaning action to remove plaque attached to teeth, and it has silver whitening effect. It is well known that the containing porous silica composite is effective in antimicrobial activity.
이에 본 발명자는 이들 성분들과 폴리프로필렌, 폴리에스테르, 폴리스틸렌 및 실리콘 중 어느 하나 또는 둘 이상의 조합으로 구성되는 칫솔모용 합성수지 조성물을 개발하게 되었다.Accordingly, the present inventors have developed a bristle synthetic resin composition composed of any one or two or more of these components and polypropylene, polyester, polystyrene and silicone.
본 발명의 칫솔모용 합성수지 조성물은 천연성분의 첨가제를 사용함으로써 인체에 무독하면서도 치주질환 예방 및 치아미백에 뛰어난 효과를 가지고 있다.Synthetic resin composition for brush head of the present invention by using an additive of the natural ingredient is harmless to the human body and has an excellent effect on the prevention of periodontal disease and teeth whitening.
본 발명에 따른 칫솔모용 합성수지 조성물은 폴리프로필렌, 폴리에스테르, 폴리스틸렌 및 실리콘 중 어느 하나 또는 둘 이상의 조합으로 구성되는 합성수지 레진 100중량부에 대하여 매실 분말 3~5중량부, 호두나무(잎 및 껍질 )분말 2~6중량부, 상추 분말 1~3중량부 및 나노 은(Ag) 다공성 실리카 복합체 분말 0.5 내지 5중량부로 구성된다.Synthetic resin composition for bristles according to the present invention 3 to 5 parts by weight of plum powder, walnut tree (leaves and shells) based on 100 parts by weight of synthetic resin composed of any one or two or more of polypropylene, polyester, polystyrene and silicone. 2 to 6 parts by weight of powder, 1-3 parts by weight of lettuce powder, and 0.5 to 5 parts by weight of nano silver (Ag) porous silica composite powder.
상기의 성분 중 매실 분말의 조성비가 5중량부를 초과할 경우 약산성을 띄어 치아가 시릴 염려가 있고, 3중량부 미만인 살균 및 해독 능력이 떨어질 우려가 있다.When the composition ratio of the plum powder in the above components exceeds 5 parts by weight, there is a concern that the tooth may be cyring due to weak acidity, and the sterilization and detoxification ability of less than 3 parts by weight may be deteriorated.
상기의 성분 중 호두나무잎 껍질 분말의 조성비가 6중량부를 초과할 경우 칫솔모의 탄력성이 떨어질 우려가 있고, 2중량부 이하일 경우 살균력이 떨어질 우려가 있다.When the composition ratio of the walnut tree bark powder of the above components exceeds 6 parts by weight, there is a fear that the elasticity of the bristles are lowered, and when less than 2 parts by weight, the sterilization power may be reduced.
상기의 성분 중 상추 분말의 경우 1중량부 미만을 함유할 경우 치아 미백의 효과가 떨어지고 3중량부를 초과할 경우 칫솔모의 탄력성이 떨어질 우려가 있다.In the case of the above-mentioned ingredients, the lettuce powder may contain less than 1 part by weight of the tooth whitening effect, and if it exceeds 3 parts by weight, the bristles may have poor elasticity.
또한, 본 발명에서 사용하는 항균제는 나노 은(Ag) 0.1~5중량%와 다공성 실리카 95~99.9중량%로 이루어진 나노 은(Ag) 다공성 실리카 복합체 분말로 첨가량을 0.5중량부 미만으로 첨가하면 항균효과가 미비하며, 5중량부를 초과할 경우 제조원가의 상승의 요인이 된다.In addition, the antimicrobial agent used in the present invention is a nano silver (Ag) porous silica composite powder consisting of 0.1 to 5% by weight of nano silver (Ag) and 95 to 99.9% by weight of porous silica, and when the added amount is less than 0.5 parts by weight, antibacterial effect It is insufficient, and if it exceeds 5 parts by weight, it will be a factor of the increase of manufacturing cost.
이하에서 실시예를 들어서 본 발명을 더욱 상세하게 설명하지만, 본 발명은 이들 실시예에 한정되는 것은 아니다.Although an Example is given to the following and this invention is demonstrated to it in more detail, this invention is not limited to these Examples.
<실시예1>≪ Example 1 >
중합도 1,300의 폴리프로필렌 레진 93중량%, 첨가제로 매실 분말 2중량%, 호두나무분말 분말 2중량%, 상추 분말 2중량% 및 나노 은(Ag) 다공성 실리카 복합체 분말 1중량%로 조성된 칫솔모용 수지 조성물을 제조하였다.93% by weight of polypropylene resin of 1,300 degree of polymerization, 2% by weight of plum powder, 2% by weight of walnut powder, 2% by weight of lettuce powder, and 1% by weight of nano silver (Ag) porous silica composite powder The composition was prepared.
상기의 실시예1, 2, 3, 4 및 5의 수지 조성물로 제조한 칫솔모와 일반적으로 시판되고 있는 나일론 칫솔모(대조시료1) 및 PBT 칫솔모(대조시료2)를 준비하였다.
The bristles prepared with the resin compositions of Examples 1, 2, 3, 4, and 5 described above, and nylon bristles (control sample 1) and PBT bristle (control sample 2) generally available on the market were prepared.
〈항균실험〉〈Antibacterial test〉
상기의 실시예1, 2, 3, 4 및 5의 시료와 대조시료1 및 2에 시험균주를 접종하여 1주일간 배양한 다음, 각 시료별 균체의 성장 정도를 관찰하여 균 성장을 억제하는 최소농도를 판정하였다. 상기 시험에 사용된 균주는 facultative anaerobic 균을 사용하였다. Inoculate the test strain to the samples of Examples 1, 2, 3, 4 and 5 and the control samples 1 and 2 and incubated for 1 week, and then observed the growth of the cells for each sample to minimize the growth of bacteria Was determined. The strain used in the test was facultative anaerobic bacteria.
각 시료들의 facultative anaerobic 균에 대한 [표 2]의 MIC 측정결과에서 알 수 있듯이 본 발명의 실시예1, 2 및 3의 칫솔모는 항균력에 큰 차이가 없이 모두 우수하였고 나노 은(Ag) 다공성 실리카 복합체 분말을 함유하지 아니한 실시예4의 칫솔모는 실시예1, 2 및 3에 비해 항균력이 떨어졌으나 대조시료1 및 2에 비하여는 항균력이 뛰어난 것으로 확인되었다.
As can be seen from the MIC measurement results of [Table 2] for the facultative anaerobic bacteria of each sample, the bristles of Examples 1, 2 and 3 of the present invention were excellent without any significant difference in the antimicrobial activity and nano silver (Ag) porous silica composites. The bristles of Example 4, which did not contain powder, were found to have lower antimicrobial activity compared to Examples 1, 2 and 3, but were superior to the control samples 1 and 2.
〈치아 미백 실험〉〈Tooth Whitening Experiment〉
본 발명에 대한 치아 미백 효과를 측정하기 위하여, 성인 남자 30명을 표본으로 5개 조로 선정하고 각 조에 대하여 실시예1, 실시예2, 실시예5, 대조시료1 및 대조시료2의 칫솔모로 1일 3회 이를 닦은 후 2주가 경과한 시점에서 치아미백 정도를 측정한 결과 각각의 칫솔모의 미백효과는 하기 [표 3(2주 후의 치아 미백 효과 측정 결과)]과 같다.In order to measure the tooth whitening effect on the present invention, 30 adult males were selected as 5 sets of samples, and the brush heads of Examples 1, 2, 5, Control Sample 1 and Control Sample 2 were used for each group. After brushing teeth three times a day, the result of measuring tooth whitening at the point of two weeks passed is as shown in [Table 3 (result of tooth whitening effect after two weeks)].
상기의 [표 3]에서 알 수 있듯이 본 발명의 실시예1 및 2의 수지 조성물을 함유하는 칫솔모는 통상의 일반적인 칫솔모인 대조시료1 및 2의 칫솔모에 비하여 미백효과가 뛰어남을 알 수 있다. 그리고 상추 분말을 함유하지 아니한 본 발명의 실시예5의 조성물의 칫솔모는 실시예1 및 2 칫솔모에 비하여 미백효과가 떨지는 것으로 확인되었다. 상기의 실험 결과에 의하면 상추분말이 미백효과가 뛰어난 것으로 판명되었다.As can be seen in Table 3 above, the bristles containing the resin compositions of Examples 1 and 2 of the present invention are superior to the bristles of the control samples 1 and 2, which are common general bristles. And it was confirmed that the bristles of the composition of Example 5 of the present invention, which does not contain lettuce powder, have a whitening effect as compared to Examples 1 and 2 bristles. According to the above experimental results, the lettuce powder was found to be excellent in the whitening effect.
Claims (4)
합성수지 레진은 폴리프로필렌과 실리콘을 조합한 것을 특징으로 하는 칫솔모용 수지 조성물The method of claim 1,
Synthetic resin is a resin composition for bristles, characterized in that a combination of polypropylene and silicone