KR101132816B1 - Waterproof and thermo-shield method for concrete surface - Google Patents

Waterproof and thermo-shield method for concrete surface Download PDF

Info

Publication number
KR101132816B1
KR101132816B1 KR1020080076210A KR20080076210A KR101132816B1 KR 101132816 B1 KR101132816 B1 KR 101132816B1 KR 1020080076210 A KR1020080076210 A KR 1020080076210A KR 20080076210 A KR20080076210 A KR 20080076210A KR 101132816 B1 KR101132816 B1 KR 101132816B1
Authority
KR
South Korea
Prior art keywords
layer
asphalt
weight
acrylic
waterproofing
Prior art date
Application number
KR1020080076210A
Other languages
Korean (ko)
Other versions
KR20100015252A (en
Inventor
서기빈
임성은
오성
Original Assignee
한국석유공업 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한국석유공업 주식회사 filed Critical 한국석유공업 주식회사
Priority to KR1020080076210A priority Critical patent/KR101132816B1/en
Publication of KR20100015252A publication Critical patent/KR20100015252A/en
Application granted granted Critical
Publication of KR101132816B1 publication Critical patent/KR101132816B1/en

Abstract

본 발명은 콘크리트 구조물(10)의 표면에 아스팔트 프라이머(20)를 도포하는 단계; 아스팔트 프라이머(20)의 도포층 위에 아스팔트 방수시트(100)를 부착하는 단계; 아스팔트 방수시트(100) 위에 아크릴계 프라이머(30)를 도포하는 단계; 아크릴계 프라이머(30)의 도포층 위에 아크릴계 차열도료(40)를 도포하는 단계;를 포함하는 콘크리트 표면의 방수 및 차열공법을 제시함으로써, 우수한 방수 성능을 보유할 뿐만 아니라, 차열 및 단열 성능이 우수하여 건물 옥상과 같이 태양열에 직접 노출되는 곳에 시공되더라도 내구성이 우수한 구조를 얻을 수 있으며, 외부 열을 차단함으로써 하절기 냉방효과 및 동절기 보온효과를 향상시켜 실내 냉방비 및 보온비 절감효과를 얻도록 한다.The present invention comprises the steps of applying the asphalt primer 20 on the surface of the concrete structure (10); Attaching the asphalt waterproof sheet 100 on the coating layer of the asphalt primer 20; Applying an acrylic primer 30 on the asphalt waterproof sheet 100; Applying the acrylic heat-shielding paint 40 on the coating layer of the acrylic primer 30; by presenting a waterproof and heat-shielding method of the concrete surface, including, not only retains excellent waterproof performance, but also excellent heat shielding and thermal insulation performance Therefore, even if the construction is directly exposed to the solar heat, such as the roof of the building can obtain a structure with excellent durability, by blocking the external heat to improve the cooling effect of the summer and the winter warming effect to obtain the indoor cooling cost and thermal insulation savings.

방수, 차열, 단열 Waterproof, heat shield, heat insulation

Description

콘크리트 표면의 방수 및 차열공법{WATERPROOF AND THERMO-SHIELD METHOD FOR CONCRETE SURFACE}WATERPROOF AND THERMO-SHIELD METHOD FOR CONCRETE SURFACE

본 발명은 건설 분야에 관한 것으로서, 상세하게는 콘크리트 구조물(10)의 방수 및 차열공법에 관한 것이다.The present invention relates to the field of construction, and more particularly, to a waterproof and thermal insulation method of the concrete structure (10).

콘크리트 건물의 바닥면, 벽면, 천정면 등 면으로부터의 누수를 방지하기 위한 방수공법은 크게 방수시트를 부착하는 방식(시트방수)과, 방수재를 도포하여 도막을 형성하는 방식(도막방수)으로 대별할 수 있다.The waterproofing method to prevent leakage from the floor, wall, and ceiling surface of concrete building is largely divided into a method of attaching a waterproof sheet (waterproof sheet) and a method of forming a coating film by applying a waterproofing material (film waterproof). can do.

시트방수의 경우 시트 상호의 조인트 부분에 누수가 발생한다는 문제가 있고, 도막방수의 경우 콘크리트의 균열 발생시 도막에도 함께 균열이 발생한다는 점, 소정 두께의 형성을 위해 과다한 시간과 비용이 소요된다는 점 등의 문제가 있다.In the case of waterproofing sheet, there is a problem of water leakage at joints between sheets. In the case of waterproofing of coating film, cracking occurs in the coating film when concrete is cracked. Excessive time and cost are required to form a predetermined thickness. There is a problem.

따라서 이들 양자의 단점을 서로 보완하고자, 시트방수와 도막방수의 복합구조인 복합방수가 시도되고 있다.Therefore, in order to compensate for the disadvantages of both of them, a composite waterproof, which is a composite structure of sheet waterproofing and coating waterproofing, has been attempted.

복합방수에 사용되는 재료로서는, 고분자계 또는 아스팔트 방수시트(100)와 열공법 또는 냉공법에 의해 도포되는 도막방수재의 조합이 가장 일반적이다.As the material used for the composite waterproofing, the combination of the polymer-based or asphalt waterproofing sheet 100 and the coating waterproofing material applied by the hot or cold method is most common.

그런데, 종래의 복합방수공법은 방수시트의 표면에 도포되는 도막방수재의 차열 및 단열 성능이 취약하므로, 건물의 옥상과 같이 태양열에 직접적으로 노출되는 구조의 경우, 방수 구조의 성능 저하가 빠르게 진행된다는 점에서 문제로 지적되어 왔다.However, in the conventional composite waterproofing method, since the heat shielding and thermal insulation performance of the coating waterproofing material applied to the surface of the waterproof sheet is weak, in the case of a structure directly exposed to solar heat such as the roof of a building, the performance of the waterproof structure is rapidly progressed. It has been pointed out as a problem.

본 발명은 상기와 같은 문제점을 해결하기 위하여 도출된 것으로서, 우수한 방수 성능을 보유할 뿐만 아니라, 차열 및 단열 성능이 우수하여 건물 옥상과 같이 태양열에 직접 노출되는 곳에 시공되더라도 내구성이 우수한 구조를 얻을 수 있으며, 외부 열을 차단함으로써 하절기 냉방효과 및 동절기 보온효과를 향상시켜 실내 냉방비 및 보온비 절감효과를 얻도록 하는 콘크리트 표면의 방수 및 차열공법을 제시하는 것을 그 목적으로 한다.The present invention has been derived to solve the above problems, not only has excellent waterproof performance, but also excellent heat shielding and thermal insulation performance, even if the construction is directly exposed to solar heat, such as building roofs can be obtained a durable structure The purpose of the present invention is to provide a waterproofing and heat shielding method of concrete surface to improve indoor cooling effect and winter warming effect by blocking external heat to obtain indoor cooling cost and thermal insulation saving effect.

본 발명은 상술한 바와 같은 목적을 달성하기 위하여, 콘크리트 구조물(10)의 표면에 아스팔트 프라이머(20)를 도포하는 단계; 상기 아스팔트 프라이머(20)의 도포층 위에 아스팔트 방수시트(100)를 부착하는 단계; 상기 아스팔트 방수시트(100) 위에 아크릴계 프라이머(30)를 도포하는 단계; 상기 아크릴계 프라이머(30)의 도포층 위에 아크릴계 차열도료(40)를 도포하는 단계;를 포함하는 콘크리트 표면의 방수 및 차열공법을 제시한다.The present invention comprises the steps of applying the asphalt primer 20 to the surface of the concrete structure 10, in order to achieve the object as described above; Attaching the asphalt waterproof sheet 100 on the coating layer of the asphalt primer 20; Applying an acrylic primer (30) on the asphalt waterproof sheet (100); It proposes a waterproof and heat shielding method of the concrete surface, including; applying an acrylic heat-insulating paint 40 on the coating layer of the acrylic primer (30).

상기 아스팔트 프라이머(20)는 산화 아스팔트 40~60 중량%, 탄화수소계 용제 40~60중량%를 포함하는 것이 바람직하다.The asphalt primer 20 preferably comprises 40 to 60% by weight of the oxidized asphalt, 40 to 60% by weight of the hydrocarbon solvent.

상기 아스팔트 방수시트(100)는 접착층(110); 상기 접착층(110) 위에 형성된 제1 개질 아스팔트층(120); 상기 제1 개질 아스팔트층(120) 위에 형성된 중심재층(130); 상기 중심재층(130) 위에 형성된 제2 개질 아스팔트층(140);을 포함하는 것이 바람직하다.The asphalt waterproof sheet 100 is an adhesive layer 110; A first modified asphalt layer 120 formed on the adhesive layer 110; A core material layer 130 formed on the first modified asphalt layer 120; It is preferable to include; a second modified asphalt layer 140 formed on the center material layer 130.

상기 접착층(110)은 폴리에틸렌, 폴리에스테르 또는 폴리프로필렌을 포함하는 재질에 의한 필름에 의해 형성된 것이 바람직하다.The adhesive layer 110 is preferably formed of a film made of a material containing polyethylene, polyester or polypropylene.

상기 제1 개질 아스팔트층(120) 및 제2 개질 아스팔트층(140)을 형성하는 개질 아스팔트층은 스트레이트 아스팔트 50~60 중량%, SBS계 또는 TPO 개질제 10~20 중량%, 탄산칼슘 20~30 중량%, 기타 첨가제 5~15 중량%를 포함하는 재질에 의해 형성된 것이 바람직하다.The modified asphalt layer forming the first modified asphalt layer 120 and the second modified asphalt layer 140 is 50 to 60% by weight of straight asphalt, 10 to 20% by weight SBS-based or TPO modifier, 20 to 30% by weight calcium carbonate It is preferably formed of a material containing%, other additives 5 to 15% by weight.

상기 중심재층(130)은 폴리에스터, 폴리프로필렌 또는 유리섬유 재질에 의한 부직포 또는 직포로 형성된 것이 바람직하다.The core material layer 130 is preferably formed of a nonwoven fabric or woven fabric made of polyester, polypropylene or glass fiber material.

상기 제2 개질 아스팔트층(140)의 위에 규사(150)가 살포된 것이 바람직하다.It is preferable that the silica sand 150 is sprayed on the second modified asphalt layer 140.

상기 아크릴계 프라이머(30)는 아크릴 에멀젼 30~50 중량%와 물에 의해 형성된 것이 바람직하다.The acrylic primer 30 is preferably formed of 30 to 50% by weight of acrylic emulsion and water.

상기 아크릴계 차열도료(40)는 아크릴 에멀젼 40~60 중량%, 붕규산계 세라믹 20~40 중량%, 기타 첨가제 10~30 중량%를 포함하는 것이 바람직하다.The acrylic heat insulating paint 40 preferably contains 40 to 60% by weight of acrylic emulsion, 20 to 40% by weight of borosilicate ceramic, and 10 to 30% by weight of other additives.

상기 아크릴계 차열도료(40)의 도포층 위에 표면 보호재(50)를 도포하는 단계를 더 포함하는 것이 바람직하다.It is preferable to further include the step of applying a surface protective material 50 on the coating layer of the acrylic heat-insulating paint (40).

상기 표면 보호재(50)는 아크릴 에멀젼 30~50 중량%와 물에 의해 형성된 것이 바람직하다.The surface protective material 50 is preferably formed of 30 to 50% by weight of acrylic emulsion and water.

본 발명은 우수한 방수 성능을 보유할 뿐만 아니라, 차열 및 단열 성능이 우수하여 건물 옥상과 같이 태양열에 직접 노출되는 곳에 시공되더라도 내구성이 우수한 구조를 얻을 수 있으며, 외부 열을 차단함으로써 하절기 냉방효과 및 동절기 보온효과를 향상시켜 실내 냉방비 및 보온비 절감효과를 얻도록 하는 콘크리트 표면의 방수 및 차열공법을 제시한다.The present invention not only has excellent waterproof performance, but also has excellent heat shielding and thermal insulation performance, so that even if the construction is directly exposed to solar heat such as a roof of a building, a durable structure can be obtained. We propose the waterproofing and heat shielding method of the concrete surface to improve the warming effect and to obtain the effect of reducing the indoor cooling cost and warming cost.

이하, 첨부도면을 참조하여 본 발명의 실시예에 관하여 상세히 설명한다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1 이하에 도시된 바와 같이, 본 발명에 의한 콘크리트 표면의 방수 및 차열공법 기본적으로, 콘크리트 구조물(10)의 표면에 아스팔트 프라이머(20)를 도포하는 단계; 아스팔트 프라이머(20)의 도포층 위에 아스팔트 방수시트(100)를 부착하는 단계; 아스팔트 방수시트(100) 위에 아크릴계 프라이머(30)를 도포하는 단계; 아크릴계 프라이머(30)의 도포층 위에 아크릴계 차열도료(40)를 도포하는 단계;를 포함하여 구성된다.As shown in Figure 1, the waterproof and heat shielding method of the concrete surface according to the present invention, basically, applying the asphalt primer 20 to the surface of the concrete structure 10; Attaching the asphalt waterproof sheet 100 on the coating layer of the asphalt primer 20; Applying an acrylic primer 30 on the asphalt waterproof sheet 100; And applying an acrylic heat shield coating 40 on the coating layer of the acrylic primer 30.

즉, 아스팔트 방수시트(100)에 의한 시트방수와 아크릴계 차열도료(40)에 의한 도막방수의 복합방수 및 차열공법으로서, 아스팔트 방수시트(100)의 우수한 방수성능과 아크릴계 차열도료(40)의 우수한 차열 및 단열 성능이 동시에 발휘되도록 한 것이다.That is, as a composite waterproofing and heat shielding method of the sheet waterproofing by the asphalt waterproof sheet 100 and the waterproofing of the coating film by the acrylic thermal barrier coating 40, the excellent waterproofing performance of the asphalt waterproof sheet 100 and the acrylic thermal barrier coating (40) Excellent heat shielding and thermal insulation performance to be exhibited at the same time.

아스팔트 프라이머(20)는 산화 아스팔트 40~60 중량%, 탄화수소계 용제 40~60중량%를 포함하여 구성되는 것이 바람직하다.Asphalt primer 20 is preferably composed of 40 to 60% by weight of oxidized asphalt, 40 to 60% by weight of hydrocarbon solvent.

산화 아스팔트는 브로운 아스팔트라고도 하는데, 이는 석유 아스팔트를 주원 료로 220~250℃의 고온에서 공기를 불어 넣어 산화반응 및 중,축합반응에 의해 탄성력이 큰 아스팔트로 만든 것으로서, 스트레이트 아스팔트에 비해 아스팔텐의 함유량이 많고 페트로렌(Petrolene)의 함유량이 적어 내열성이 우수하며 충격 저항력이 강하고 감온성이 적다는 특징이 있다.Oxidized asphalt is also called blown asphalt. It is made of asphalt which has high elasticity by oxidizing reaction and polycondensation reaction by blowing air from petroleum asphalt at the high temperature of 220 ~ 250 ℃ as the main raw material. It has high content and low content of Petrolene, so it has excellent heat resistance, strong impact resistance and low temperature sensitivity.

아스팔트 방수시트(100)는 아스팔트 재질에 의해 형성된 방수시트를 의미하는데, 구체적으로는 도 2에 도시된 바와 같이, 접착층(110); 접착층(110) 위에 형성된 제1 개질 아스팔트층(120); 제1 개질 아스팔트층(120) 위에 형성된 중심재층(130); 중심재층(130) 위에 형성된 제2 개질 아스팔트층(140);을 포함하는 층상구조를 취하는 것이 바람직하다.Asphalt waterproof sheet 100 means a waterproof sheet formed by the asphalt material, specifically, as shown in Figure 2, the adhesive layer 110; A first modified asphalt layer 120 formed on the adhesive layer 110; A core material layer 130 formed on the first modified asphalt layer 120; It is preferable to take a layered structure including a second modified asphalt layer 140 formed on the core material layer 130.

접착층(110)은 부직포 등의 구성을 취함으로써 접착재에 의해 방수시트(100)를 콘크리트 구조물(10)의 표면에 접착하는 구성을 취할 수 있는데, 폴리에틸렌, 폴리에스테르 또는 폴리프로필렌을 포함하는 재질에 의한 필름의 구조를 취하는 경우, 접착면을 토치 등에 의해 가열한 후 접착함으로써 방수시트(100)를 쉽게 안정적으로 시공할 수 있다는 장점이 있다.The adhesive layer 110 may be configured to adhere the waterproof sheet 100 to the surface of the concrete structure 10 by an adhesive by taking a nonwoven fabric or the like, and may be formed of a material including polyethylene, polyester, or polypropylene. When taking the structure of the film, there is an advantage that the waterproof sheet 100 can be easily and stably constructed by heating the adhesive surface with a torch or the like and then adhering.

시트의 본체를 이루는 중심재층(130)은 폴리에스터, 폴리프로필렌 또는 유리섬유 재질에 의한 부직포 또는 직포로 형성되는 것이 바람직하다.The core material layer 130 constituting the main body of the sheet is preferably formed of a nonwoven or woven fabric made of polyester, polypropylene or glass fiber material.

제1 개질 아스팔트층(120) 및 제2 개질 아스팔트층(140)을 형성하는 개질 아스팔트층은 스트레이트 아스팔트 50~60 중량%, SBS계 또는 TPO 개질제 10~20 중량%, 탄산칼슘 20~30 중량%, 기타 첨가제(산화방지제, 분산제 등) 5~15 중량%를 포함하는 재질에 의해 형성되는 것이 바람직하다.The modified asphalt layer forming the first modified asphalt layer 120 and the second modified asphalt layer 140 is 50 to 60% by weight of straight asphalt, 10 to 20% by weight of SBS-based or TPO modifier, and 20 to 30% by weight of calcium carbonate. It is preferably formed of a material containing 5 to 15% by weight of other additives (antioxidants, dispersants, etc.).

이러한 구성을 취하는 아스팔트 방수시트(100)는 다층막 구조를 취하므로 방수성능이 우수하고, 타 방수재와 친화력이 우수하며, 방수층 전체에 고르게 신장력이 분포되어 있어 유해한 건물의 거동에 견딜 수 있고, 자외선 및 오존에 대한 저항성이 우수하며, 시공이 용이하고, 경제적이며, 연기, 악취의 발생이 적고 용제 사용이 적어 악취발생이 없다는 장점이 있다.Asphalt waterproof sheet 100 having such a configuration has a multi-layered structure, so it has excellent waterproofing performance, excellent affinity with other waterproofing materials, and evenly distributed stretching force throughout the waterproofing layer, capable of withstanding harmful building behavior, ultraviolet rays and Excellent resistance to ozone, easy to install, economical, there is little smoke, odor generation and less solvent use has the advantage of no odor generation.

제2 개질 아스팔트층(140)의 위에는 규사(150)가 살포되는 것이 타 재료와의 부착력을 강화한다는 측면에서 바람직하다.The silica sand 150 is preferably sprayed on the second modified asphalt layer 140 in view of enhancing adhesion to other materials.

아크릴계 프라이머(30)는 아크릴 에멀젼 30~50 중량%와 물에 의해 형성되는 것이 적절하다.Acrylic primer 30 is preferably formed by 30 to 50% by weight of the acrylic emulsion and water.

아크릴계 차열도료(40)는 아크릴 에멀젼 40~60 중량%, 붕규산계 세라믹 20~40 중량%, 기타 첨가제(산화방지제, 분산제 등) 10~30 중량%를 포함하는 구성을 취하는 경우, 차열 및 단열 성능이 우수할 뿐만 아니라, 외부 습기의 내부 침투를 막고 내부의 습기 발생을 방지하는 특성이 있으므로 방수성이 우수하고, 열에 대한 안정성이 우수하며, 재료의 강도 및 신장율이 뛰어나 균열발생을 방지할 수 있고, 곰팡이 등의 발생을 억제하는 방균 기능이 있어 친환경적이라는 장점이 있다.When the acrylic heat insulating paint 40 has a composition including 40 to 60% by weight of an acrylic emulsion, 20 to 40% by weight of a borosilicate ceramic, and 10 to 30% by weight of other additives (antioxidants, dispersants, etc.), Not only is it excellent, it has the property of preventing the internal penetration of external moisture and preventing the generation of internal moisture, so it is excellent in waterproofness, excellent in heat stability, and excellent in strength and elongation of the material to prevent cracking, It has the advantage of being eco-friendly because it has an antibacterial function that suppresses the occurrence of mold.

이러한 아크릴계 차열도료(40)의 도포층 위에는 표면 보호재(50)를 도포하는 것이 더욱 바람직하고, 이러한 표면 보호재(50)는 위 아크릴계 프라이머(30)와 마찬가지로 아크릴 에멀젼 30~50 중량%와 물에 의해 형성되는 것이 바람직하다.It is more preferable to apply the surface protective material 50 on the coating layer of the acrylic heat-insulating paint 40, this surface protective material 50, like the acrylic primer 30, by 30 to 50% by weight of the acrylic emulsion and water It is preferably formed.

이상은 본 발명에 의해 구현될 수 있는 바람직한 실시예의 일부에 관하여 설명한 것에 불과하므로, 주지된 바와 같이 본 발명의 범위는 위의 실시예에 한정되 어 해석되어서는 안 될 것이며, 위에서 설명된 본 발명의 기술적 사상과 그 근본을 함께 하는 기술적 사상은 모두 본 발명의 범위에 포함된다고 할 것이다.Since the above has just been described with respect to some of the preferred embodiments that can be implemented by the present invention, as is well known the scope of the present invention should not be construed as limited to the above embodiments, the present invention described above All of the technical ideas together with the technical idea of the base will be included in the scope of the present invention.

도 1 이하는 본 발명에 의한 방수 및 차열공법을 설명하기 위한 것으로서,1 is for explaining the waterproofing and heat shielding method according to the present invention,

도 1은 제1실시예에 의해 시공된 방수구조의 단면도.1 is a cross-sectional view of the waterproof structure constructed by the first embodiment.

도 2는 방수시트의 상세 단면도.Figure 2 is a detailed cross-sectional view of the waterproof sheet.

도 3은 제2실시예에 의해 시공된 방수구조의 단면도.3 is a cross-sectional view of the waterproof structure constructed by the second embodiment.

**도면의 주요부분에 대한 부호의 설명**DESCRIPTION OF REFERENCE NUMERALS

10 : 콘크리트 구조물 20 : 아스팔트 프라이머10: concrete structure 20: asphalt primer

30 : 아크릴계 프라이머 40 : 아크릴계 차열도료30: acrylic primer 40: acrylic heat insulating paint

50 : 표면 보호재 100 : 아스팔트 방수시트50: surface protection material 100: asphalt waterproof sheet

110 : 접착층 120 : 제1 개질 아스팔트층110: adhesive layer 120: first modified asphalt layer

130 : 중심재층 140 : 제2 개질 아스팔트층130: core material layer 140: second modified asphalt layer

150 : 규사150: silica sand

Claims (11)

콘크리트 구조물(10)의 표면에, 산화 아스팔트 40~60 중량%, 탄화수소계 용제 40~60중량%를 포함하는 아스팔트 프라이머(20)를 도포하는 단계;Applying to the surface of the concrete structure 10, an asphalt primer 20 including 40 to 60% by weight of oxidized asphalt and 40 to 60% by weight of a hydrocarbon solvent; 상기 아스팔트 프라이머(20)의 도포층 위에 아스팔트 방수시트(100)를 부착하는 단계;Attaching the asphalt waterproof sheet 100 on the coating layer of the asphalt primer 20; 상기 아스팔트 방수시트(100) 위에 아크릴계 프라이머(30)를 도포하는 단계;Applying an acrylic primer (30) on the asphalt waterproof sheet (100); 상기 아크릴계 프라이머(30)의 도포층 위에 아크릴계 차열도료(40)를 도포하는 단계;를Applying an acrylic thermal barrier coating (40) on an application layer of the acrylic primer (30); 포함하는 콘크리트 표면의 방수 및 차열공법.Waterproofing and thermal insulation of concrete surfaces, including. 삭제delete 제1항에 있어서,The method of claim 1, 상기 아스팔트 방수시트(100)는The asphalt waterproof sheet 100 접착층(110);Adhesive layer 110; 상기 접착층(110) 위에 형성된 제1 개질 아스팔트층(120);A first modified asphalt layer 120 formed on the adhesive layer 110; 상기 제1 개질 아스팔트층(120) 위에 형성된 중심재층(130);A core material layer 130 formed on the first modified asphalt layer 120; 상기 중심재층(130) 위에 형성된 제2 개질 아스팔트층(140);을A second modified asphalt layer 140 formed on the center material layer 130; 포함하는 것을 특징으로 하는 콘크리트 표면의 방수 및 차열공법.Waterproofing and heat shielding method of the concrete surface comprising a. 제3항에 있어서,The method of claim 3, 상기 접착층(110)은 The adhesive layer 110 폴리에틸렌, 폴리에스테르 또는 폴리프로필렌을 포함하는 재질에 의한 필름에 의해 형성된 것을 특징으로 하는 콘크리트 표면의 방수 및 차열공법.Waterproofing and heat shielding method of the concrete surface, characterized in that formed by a film made of a material containing polyethylene, polyester or polypropylene. 제3항에 있어서,The method of claim 3, 상기 제1 개질 아스팔트층(120) 및 제2 개질 아스팔트층(140)을 형성하는 개질 아스팔트층은The modified asphalt layer forming the first modified asphalt layer 120 and the second modified asphalt layer 140 is 스트레이트 아스팔트 50~60 중량%, SBS계 또는 TPO 개질제 10~20 중량%, 탄산칼슘 20~30 중량%, 기타 첨가제 5~15 중량%를 포함하는 재질에 의해 형성된 것을 특징으로 하는 콘크리트 표면의 방수 및 차열공법.Waterproofing of the concrete surface, characterized in that formed by the material comprising 50 to 60% by weight of straight asphalt, 10 to 20% by weight of SBS-based or TPO modifier, 20 to 30% by weight of calcium carbonate, and 5 to 15% by weight of other additives. Thermal insulation method. 제3항에 있어서,The method of claim 3, 상기 중심재층(130)은The central material layer 130 is 폴리에스터, 폴리프로필렌 또는 유리섬유 재질에 의한 부직포 또는 직포로 형성된 것을 특징으로 하는 콘크리트 표면의 방수 및 차열공법.Waterproofing and heat shielding method of the concrete surface, characterized in that formed of non-woven or woven fabric made of polyester, polypropylene or glass fiber material. 제3항에 있어서,The method of claim 3, 상기 제2 개질 아스팔트층(140)의 위에 규사(150)가 살포된 것을 특징으로 하는 콘크리트 표면의 방수 및 차열공법.Waterproofing and heat shielding method of the concrete surface, characterized in that the silica sand 150 is sprayed on the second modified asphalt layer 140. 제1항에 있어서,The method of claim 1, 상기 아크릴계 프라이머(30)는 아크릴 에멀젼 30~50 중량%와 물에 의해 형성된 것을 특징으로 하는 콘크리트 표면의 방수 및 차열공법.The acrylic primer 30 is waterproof and heat shielding method of the concrete surface, characterized in that formed by the acrylic emulsion 30 ~ 50% by weight and water. 제1항에 있어서,The method of claim 1, 상기 아크릴계 차열도료(40)는 The acrylic heat shield paint 40 아크릴 에멀젼 40~60 중량%, 붕규산계 세라믹 20~40 중량%, 기타 첨가제 10~30 중량%를 포함하는 것을 특징으로 하는 콘크리트 표면의 방수 및 차열공법.Waterproofing and heat shielding method of the concrete surface, characterized in that it comprises 40 to 60% by weight of acrylic emulsion, 20 to 40% by weight of borosilicate ceramic, and 10 to 30% by weight of other additives. 제1항에 있어서,The method of claim 1, 상기 아크릴계 차열도료(40)의 도포층 위에 표면 보호재(50)를 도포하는 단계를 더 포함하는 것을 특징으로 하는 콘크리트 표면의 방수 및 차열공법.Waterproofing and heat shielding method of the concrete surface, characterized in that it further comprises the step of applying a surface protective material (50) on the coating layer of the acrylic insulating paint (40). 제10항에 있어서,The method of claim 10, 상기 표면 보호재(50)는 아크릴 에멀젼 30~50 중량%와 물에 의해 형성된 것을 특징으로 하는 콘크리트 표면의 방수 및 차열공법.The surface protective material 50 is waterproof and heat shielding method of the concrete surface, characterized in that formed by 30 to 50% by weight of acrylic emulsion and water.
KR1020080076210A 2008-08-04 2008-08-04 Waterproof and thermo-shield method for concrete surface KR101132816B1 (en)