CN205601317U - A compound waterproofing membrane of polymer self -adhesion for exposing roofing - Google Patents
A compound waterproofing membrane of polymer self -adhesion for exposing roofing Download PDFInfo
- Publication number
- CN205601317U CN205601317U CN201620409393.6U CN201620409393U CN205601317U CN 205601317 U CN205601317 U CN 205601317U CN 201620409393 U CN201620409393 U CN 201620409393U CN 205601317 U CN205601317 U CN 205601317U
- Authority
- CN
- China
- Prior art keywords
- layer
- thickness
- exposing
- roofing
- self
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model provides a compound waterproofing membrane of polymer self -adhesion for exposing roofing, its from the top down of multilayer structure are protective layer, high score sublayer, barrier layer, high temperature resistant modified asphalt layer, enhancement layer, self -adhesive layer, isolation layer in proper order, and the protective layer is the chlorosulfonated polyethylene layer, is its thickness 0.3 0.7mm. The high score sublayer is the thermoplastic polyolefin TPO layer, is its thickness 0.7 1.0mm. High temperature resistant modified asphalt layer is high polymer APP modified asphalt self -adhesion glue film, is its thickness 0.5 1.0mm. The self -adhesive layer is high temperature resistant non -cured rubberized asphalt dope layer, is its thickness 0.5 1.0mm. The enhancement layer is glass fiber net check polyester cloth, the isolation layer be the aluminium foil barrier film. This coiled material has superstrong high temperature resistance and low -temperature flexibility, intensity is high, and the percentage elongation is high, self -healing nature is strong, bonds with the base face is full, it is simple and convenient, energy -concerving and environment -protective to be under construction. Can be used to the various type roof waterproof engineerings that expose.
Description
Technical field
The present invention relates to the waterproof roll in buildings waterproof field, be particularly suited for building the adhesive polymer composite water-proof coiled material for exposing roofing exposing roof waterproof engineering.
Background technology
APP modified-high polymer waterproof roll material is the earliest in exposed conveying appliance roof waterproof engineering, the most gradually finds that this coiled material hot melt application causes efficiency of construction low, is susceptible to fire, not energy-conserving and environment-protective.In order to overcome these defects, given full play to the material characteristicses such as chlorosulfonated polyethylene, TPO and uncured rubber asphalt waterproof coating by scientific design, invented this for exposing roofing adhesive polymer composite water-proof coiled material.
Utility model content
Cause efficiency of construction low to solve APP modified-high polymer waterproof roll material hot melt application in prior art, it is susceptible to fire, the technical barriers such as not energy-conserving and environment-protective, the invention provides that a kind of weatherability ozone strong, resistance to, elongation percentage be big, the adhesive polymer composite of water-proof coiled material for exposing roofing of length in service life.
Realize foregoing invention purpose by the following technical solutions:
A kind of adhesive polymer composite water-proof coiled material for exposing roofing; for multiple structure; described multiple structure its be followed successively by protective layer, macromolecule layer, barrier layer, heat resist modification bitumen layer, enhancement layer, self-adhesive layer, sealing coat from top to bottom; described protective layer is chlorosulfonated polyethylene layer, and its thickness is 0.3-0.7mm；Described macromolecule layer is TPO TPO layer, its thickness be the heat resist modification bitumen layer described in 0.7-1.0mm be high polymer APP modified pitch self-adhesive glue layer, its thickness is 0.5-1.0mm；Described self-adhesive layer is high temperature resistant uncured rubber-asphalt coating layer, its thickness be the enhancement layer described in 0.5-1.0mm be fiberglass mesh mylar；Described sealing coat is aluminium foil isolating membrane.
Preferably, described macromolecule layer thickness is 1.0mm,
Preferably, described barrier layer is multilamellar PA/PE co-extrusion film, and thickness is 0.1mm.
Preferably, described heat resist modification asphalt thickness is 0.8mm.
Preferably, described enhancement layer thickness is 0.3mm.
Preferably, described sealing coat is aluminum plated PET sealing coat.
Use technique scheme, compared with prior art, the chlorosulfonated polyethylene layer being used for exposing roofing adhesive polymer composite water-proof coiled material of this utility model offer has superpower ageing-resistant, against weather, uviolresistance, can need to be prepared as multiple color according to beautifying city, white appearance can reflected sunlight, and then play building energy-saving effect.TPO layer is that the roof waterpoof material that leaks outside is first-selected, has intensity high, and elongation percentage is high, ageing-resistant feature, and it, with inherently to have superpower thermostability APP high-polymer modified pitch layer the most waterproof, is greatly improved the service life of material.High temperature resistant uncured rubber asphalt waterproof coating layer has stronger cementability, full with basal plane bonding, it is achieved skin-type is waterproof.This coiled material has stronger weatherability, ageing-resistant, substantially prolongs coiled material service life；White appearance reflected sunlight plays energy-saving effect, and colorful outward appearance has beautified city；This coiled material has stronger cementability, it is achieved full bonding；It is applied to leak outside in roofworks and can play waterproof, energy-conservation and environment protecting.It plays chlorosulfonated polyethylene layer weatherability ozone strong, resistance to, can add pigment and make it have different colours, beautify the environment；Have that TPO waterproof roll intensity is high, elongation percentage big, length in service life and energy-conserving and environment-protective advantage；There is uncured asphalt rubber asphalt waterproofing paint to do bottom more waterproof, realize with basal plane full bonding；And APP polymer modified bituminous waterproof sheet material itself has the most high temperature resistant and weatherability, above-mentioned multiple material feature combines and makes waterproof roll and will have good weatherability properties, substantially exceeds tradition APP modified-high polymer waterproof roll material service life.The cold construction of self-adhesive layer, improves efficiency, has saved the energy.This coiled material of white appearance can not reflected sunlight, accomplish building green energy conservation, environmental protection.
Accompanying drawing explanation
Accompanying drawing 1 is structural representation of the present utility model.
Labelling in figure, protective layer 1, macromolecule layer 2, barrier layer 3, heat resist modification bitumen layer 4, enhancement layer 5, self-adhesive layer 6, sealing coat 7.
Detailed description of the invention
Present embodiment discloses a kind of for exposing roofing adhesive polymer composite water-proof coiled material; the structure of this coiled material is as it is shown in figure 1, its cross-sectional configuration is followed successively by protective layer 1, macromolecule layer 2, barrier layer 3, heat resist modification bitumen layer 4, enhancement layer 5, self-adhesive layer 6, sealing coat 7 from top to bottom.Protective layer 1 is chlorosulfonated polyethylene layer, thickness 0.5mm, itself just has stronger weatherability, uvioresistant, adds pigment and can be made into multiple color beautifying city.Macromolecule layer 2 is TPO TPO layer, and thickness is 1.0mm, and it is high that it has intensity, and elongation percentage is big, and the most ageing-resistant, service life is long.Barrier layer 3 is multilamellar PA/PE co-extrusion film, and thickness is 0.1mm, and it can effectively intercept oil point in heat resist modification bitumen layer 4 and migrate, and protects macromolecule layer.Heat resist modification bitumen layer 4 is APP high-polymer modified pitch cementitious matter, and thickness is 0.8mm, and it is high temperature resistant, uvioresistant, the most waterproof with TPO layer is greatly prolonged coiled material service life.Enhancement layer 5 is fiberglass mesh mylar, and thickness is 0.3mm.Self-adhesive layer 6 is high temperature resistant uncured rubber-asphalt coating layer, and thickness is 0.5-1.0mm, has stronger cementability, full with basal plane bonding, it is achieved skin-type is waterproof.Sealing coat 7 is aluminum plated PET sealing coat.
This coiled material has stronger weatherability, ageing-resistant, substantially prolongs coiled material service life；White appearance reflected sunlight plays energy-saving effect, and colorful outward appearance has beautified city；This coiled material has stronger cementability, it is achieved full bonding；It is applied to leak outside in roofworks and can play waterproof, energy-conservation and environment protecting.
Claims (6)
1. the adhesive polymer composite water-proof coiled material being used for exposing roofing; for multiple structure; it is characterized in that; described multiple structure its be followed successively by protective layer, macromolecule layer, barrier layer, heat resist modification bitumen layer, enhancement layer, self-adhesive layer, sealing coat from top to bottom; described protective layer is chlorosulfonated polyethylene layer, and its thickness is 0.3-0.7mm；Described macromolecule layer is TPO TPO layer, and its thickness is 0.7-1.0mm, and described heat resist modification bitumen layer is high polymer APP modified pitch self-adhesive glue layer, and its thickness is 0.5-1.0mm；Described self-adhesive layer is high temperature resistant uncured rubber-asphalt coating layer, and its thickness is 0.5-1.0mm, and described enhancement layer is fiberglass mesh mylar；Described sealing coat is aluminium foil isolating membrane.
Adhesive polymer composite water-proof coiled material for exposing roofing the most according to claim 1, it is characterised in that described macromolecule layer thickness is 1.0mm.
Adhesive polymer composite water-proof coiled material for exposing roofing the most according to claim 1, it is characterised in that described barrier layer is multilamellar PA/PE co-extrusion film, thickness is 0.1mm.
Adhesive polymer composite water-proof coiled material for exposing roofing the most according to claim 1, it is characterised in that described heat resist modification asphalt thickness is 0.8mm.
Adhesive polymer composite water-proof coiled material for exposing roofing the most according to claim 1, it is characterised in that described enhancement layer thickness is 0.3mm.
Adhesive polymer composite water-proof coiled material for exposing roofing the most according to claim 1, it is characterised in that described sealing coat is aluminum plated PET isolating membrane.