KR101100783B1 - Reusable Paper Cup - Google Patents
Reusable Paper Cup Download PDFInfo
- Publication number
- KR101100783B1 KR101100783B1 KR1020100001808A KR20100001808A KR101100783B1 KR 101100783 B1 KR101100783 B1 KR 101100783B1 KR 1020100001808 A KR1020100001808 A KR 1020100001808A KR 20100001808 A KR20100001808 A KR 20100001808A KR 101100783 B1 KR101100783 B1 KR 101100783B1
- Authority
- KR
- South Korea
- Prior art keywords
- paper
- cup
- paper cup
- coating layer
- silver
- Prior art date
Abstract
음료가 수용되는 종이컵에 있어서, 상기 음료가 수용되도록 컵 형상으로 형성되는 종이층; 상기 컵 형상의 하단으로부터 소정의 높이까지 상기 종이층의 내측 면에, 은 나노 입자를 포함하여 형성되는 제1 코팅층; 및 상기 제1 코팅층의 상단으로부터 상기 컵 형상의 상단까지 상기 종이층의 내측 면에 Al2O3을 포함하여 형성되는 제2 코팅층을 포함하는 재사용이 가능한 종이컵이 제공된다.
또한, 상기 종이층의 외측면의 상단에서 입술이 닿는 부위인 소정의 높이까지 Al2O3 재질로 코팅을 하는 제3코팅층으로 이루어지는 것을 특징으로 하는 재사용이 가능한 종이컵이 제공된다.A paper cup in which a beverage is accommodated, the paper layer being formed in a cup shape to accommodate the beverage; A first coating layer including silver nanoparticles on an inner surface of the paper layer from a lower end of the cup shape to a predetermined height; And a second coating layer including Al 2 O 3 on the inner side of the paper layer from the top of the first coating layer to the top of the cup shape.
In addition, there is provided a reusable paper cup comprising a third coating layer coated with an Al 2 O 3 material to a predetermined height, which is a part where the lips touch at the upper end of the outer surface of the paper layer.
Description
본 발명은 종이컵에 관한 것으로, 종이컵의 내부에 커피 등의 뜨거운 음료가 차지하는 부분은 항균제인 은 성분으로 코팅을 하고 입술이 닫는 상부에는 열전도율이 낮은 금속으로 코팅하여 인체에 유익하고 재사용이 가능한 종이컵 기술에 관한 것이다.The present invention relates to a paper cup, a portion occupied by hot beverages such as coffee in the paper cup is coated with a silver component of an antimicrobial agent, and the upper portion of the lips close is coated with a metal with low thermal conductivity, which is beneficial to the human body and is reusable. It is about.
1년에 우리나라 사람들이 사용하는 종이컵은 약 120억개 정도 된다고 한다. 이러한 120억개의 종이컵을 만들기 위해서는 20년생 나무 120만 그루를 매년 베어내야 한다. 때문에 종이컵을 몇 번만 재사용하여도 상당한 탄소배출량을 줄일 수 있게 된다.It is said that about 12 billion paper cups are used by Korean people in one year. To make these 12 billion paper cups, we need to cut 1.2 million 20-year-old trees every year. As a result, the paper cup can be reused only a few times, resulting in significant carbon emissions.
일반적으로 도 1에 도시된 바와 같이 종이컵은 인체 건강상 재생용 화학펄프는 사용하지 않고 고급 천연펄프로 제조되고 있다. 하지만, 종이컵이라고 해서 종이로만 만들면 수분이 금방 종이에 흡수되어 컵이 흐물거리며 컵으로서의 기능을 상실하게 된다.In general, as shown in Figure 1, the paper cup is made of high-quality natural pulp without using chemical pulp for regeneration for human health. However, if the paper cup is made of paper only, moisture is quickly absorbed by the paper, causing the cup to drift and lose its function as a cup.
그래서 일반적으로 종이컵은 그 내부(3)에 폴리에틸렌으로 코팅처리를 하게 된다. 그런데 커피를 탈 때, 통상 90도 이상의 끓는 물에 커피를 타야 맛있는 커피를 즐길 수 있으나, 상기와 같이 PE로 코팅(3)된 종이컵에 뜨거운 물을 붓게 되면 코팅재에서 소량의 톨루엔과 시안화수소 같은 환경 호르몬 물질이 녹아나오기 대문에 뜨거운 차의 원래의 맛과 향을 유지시키는 점에서는 금속제나 자기제의 컵보다는 품질면에서 떨어지게 된다.In general, the paper cup is then coated with polyethylene on its inside (3). By the way, when you take coffee, you can enjoy delicious coffee by pouring coffee in boiling water of 90 degrees or more, but if you pour hot water into paper cup coated with PE (3) as described above, a small amount of environment such as toluene and hydrogen cyanide in the coating material As the hormonal substance melts, the quality and flavor of the hot tea is lower than that of metal or porcelain cups.
또한, 상기와 같은 PE코팅은 뜨거운 커피를 한잔 따라 놓게 되면 곧 코팅부위(3)에 수분이 함유되어 컵이 흐물거려서 본인의 컵이라도 재사용하기가 곤란하게 된다. In addition, the PE coating as described above, as soon as a cup of hot coffee is contained therein, the
본 발명의 목적은 건강에 유해한 물질이 제거되고 뜨거운 차의 원래의 맛과 향을 유지시킬 수 있으면서 재사용이 가능한 종이컵을 제공하는 것에 있다.It is an object of the present invention to provide a paper cup that can be reused while being able to remove harmful substances and maintain the original taste and aroma of hot tea.
더 나아가 본 발명은 금속으로 코팅된 종이컵에 뜨거운 차를 마실 때 입술 부위가 데는 것을 방지할 수 있는 종이컵을 제공한다.The present invention further provides a paper cup that can prevent the lip area from burning when drinking hot tea in a metal cup coated with a metal cup.
상기와 같은 과제를 해결하기 위하여 음료가 수용되는 종이컵에 있어서, 종이 재질로 형성되는 종이층과, 상기 종이층의 내측면의 바닥면에서 80 ~ 90% 높이 까지 은 나노 입자가 함유된 금속으로 코팅을 하는 제1코팅층과 상기 종이층의 내측면의 상부에서 제1코팅층까지 ZrO2,또는 AL2O3 재질로 코팅을 하는 제2코팅층으로 이루어지는 것을 특징으로 하는 재사용이 가능한 종이컵이 제공된다.In order to solve the above problems, in a paper cup in which a beverage is accommodated, a paper layer formed of a paper material and coated with a metal containing silver nanoparticles up to 80 to 90% height from the bottom surface of the inner surface of the paper layer ZrO 2 , or AL 2 O 3 from the upper part of the first coating layer and the inner surface of the paper layer to the first coating layer Provided is a reusable paper cup comprising a second coating layer coated with a material.
일 실시예에서, 본 발명의 종이컵은 외측면 전제 또는 외측면의 상부에서 1 ~2 cm 범위의 높이 까지 ZrO2,또는 AL2O3 재질로 코팅을 하는 제3코팅층으로 이루어지는 것을 특징으로 한다.In one embodiment, the paper cup of the present invention is characterized by consisting of a third coating layer coated with a ZrO 2 , or AL 2 O 3 material to a height in the range of 1 ~ 2 cm from the top of the outer surface or the outer surface.
본 발명의 종이컵은 입술이 닫는 부분과 용액이 담겨져 있는 부분을 금속으로 코팅하였기 때문에 뜨거운 차를 수용하여도 컵이 원래의 형태를 유지할 수 있으며, 내부와 입술이 닫는 부위만 간단히 세척하여 건조시키면 원래의 형태로 재사용할 수 있는 효과가 있다.Since the paper cup of the present invention is coated with a metal part covering the lips and the part containing the solution, the cup can maintain its original shape even when the hot tea is accommodated. It can be reused in the form of.
용액을 수용하는 부분을 원적외선이 방출되고 항균력이 있는 은 나도 코팅을 함으로써, 건강에 유익하고 차의 맛과 향을 유지시킬 수 있는 효과가 있다.By coating the part containing the solution with far-infrared rays and antimicrobial silver, it is beneficial for health and maintains the taste and aroma of tea.
본 발명의 종이컵은 입술이 닿는 부위를 열전도율이 낮은 금속으로 코팅하였기 때문에 뜨거운 차를 마실 때에도 입술을 데일 염려가 없으며 상대적으로 열에 약한 입술을 보호할 수 있게 된다.Since the paper cup of the present invention is coated with a metal having low thermal conductivity on the area where the lips touch, there is no fear of having a lip even when drinking hot tea, and it is possible to protect the lips which are relatively weak to heat.
또한, 제3코팅층을 외부 전체에 실시하여 열전도율이 낮은 ZrO2,또는 AL2O3 재질로 코팅을 하게 되면 열전도율이 낮은 ZrO2,또는 AL2O3 재질의 특징과 제1코팅층, 종이층 제3코팅층으로 형성된 단열 작용에 의하여 종이컵 내부에 뜨거운 차를 넣더라도 외부의 손잡는 부위에서는 뜨거운 감을 보다 적게 느끼게 되는 효과를 가지게 된다.In addition, when the third coating layer is applied to the entire outside to coat with ZrO 2 or AL 2 O 3 material having low thermal conductivity, the characteristics of the ZrO 2 or AL 2 O 3 material with low thermal conductivity and the first coating layer and paper layer are made. Even if hot tea is put into the paper cup by the heat insulation action formed by the three coating layers, the hot hand feels less at the outside.
도 1 은 종래의 종이컵에 대한 구성도이다.
도 2 및 3은 본 발명의 일 실시에 의한 금속 코팅 종이컵을 설명하기 위한 개략도이다.1 is a block diagram of a conventional paper cup.
2 and 3 is a schematic view for explaining a metal coated paper cup according to an embodiment of the present invention.
본 발명은 다양한 변경을 가할 수 있고 여러 가지 실시예들을 가질 수 있는바, 특정 실시예들을 도면에 예시하고 이를 상세한 설명을 통해 상세히 설명하고자 한다. 그러나 이는 본 발명을 특정한 실시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다.As the present invention allows for various changes and numerous embodiments, particular embodiments will be illustrated in the drawings and described in detail in the written description. However, this is not intended to limit the present invention to specific embodiments, it should be understood to include all changes, equivalents, and substitutes included in the spirit and scope of the present invention.
본 발명을 설명함에 있어서, 관련된 공지 기술에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우 그 상세한 설명을 생략한다. 또한, 본 명세서의 설명 과정에서 이용되는 숫자(예를 들어, 제1, 제2 등)는 하나의 구성요소를 다른 구성요소와 구분하기 위한 식별기호에 불과하다.In describing the present invention, when it is determined that the detailed description of the related known technology may unnecessarily obscure the subject matter of the present invention, the detailed description thereof will be omitted. In addition, numerals (eg, first, second, etc.) used in the description process of the present specification are merely identification symbols for distinguishing one component from another component.
이하, 첨부된 도면들을 참조하여 본 발명의 실시예에 따른 재사용이 가능한 종이컵에 관하여 상세히 설명하기로 한다.Hereinafter, with reference to the accompanying drawings will be described in detail with respect to the reusable paper cup according to an embodiment of the present invention.
도 2는 본 발명의 일 실시예에 의한 종이컵을 설명하기 위한 개략도이다.Figure 2 is a schematic diagram for explaining the paper cup according to an embodiment of the present invention.
도 2에 도시된 바와 같이 종이층(10)의 내측면의 바닥면에서 80 ~ 90% 높이 까지는 은 나노 입자가 함유된 금속으로 코팅을 하는 제1코팅층(11)이 형성된다.As shown in FIG. 2, a
은은 비중이 10~12, 모스 경도는 2.5 ~3, 용융점은 960이다. 은의 효능은 고대로부터 몸에 착용하고 있으면 신체의 컨디션에 따라 광택이나 컬러가 변하여 자신이 느끼지 못하는 신체의 불균형을 검사할 수 있는 도구 또는 음식물에 독극물이 함유되었을 때, 은의 색이 변하는 점을 이용하여 이를 식별하는 도구로 사용되기도 하였다.Silver has a specific gravity of 10 to 12, a Mohs hardness of 2.5 to 3, and a melting point of 960. The effect of silver is that the color of the silver changes when the body contains poisons in tools or foods that can be used to check the body's imbalance. It was also used as a tool to identify it.
또한, 동의보감에서는 간질과 경기 등 정신질환과 부인병의 예방과 치료에 효험이 있다고 하고 은을 분말 화하여 복용하는 한약재로서 역할도 하였고, 은은 몸에 지니고 있으면 오장이 편안하고 심신이 안정되며, 사기를 내 쫓고 몸을 가볍게 하여 명을 길게 한다고 본초강목에서 기록하고 있다. In addition, Dongbogam said that it is effective in the prevention and treatment of mental disorders and women's diseases such as epilepsy and game, and played a role as a herbal medicine powdered with silver. It is written in the main tree that they chased me and lightened their body to lengthen their lives.
또한, 중세에 흑사병이 만연했을 때는 은 식기나 은 집기류를 많이 갖고 있었던 귀족이나 왕족들에게는 흑사병이 걸리지 않았는데 이는 은에서 발생하는 음이온이 흑사병 균을 살균할 정도로 방출되어 전염병으로부터 상대적으로 안전할 수 있었다고 하며 왕실이나 국빈을 모시는 자리에는 빠짐없이 은제품이 애용되고 있었다고 한다.Also, when the Black Plague prevailed in the Middle Ages, nobility of the black aristocrats and royals, who had many silverware and silver utensils, did not have black plague, which released silver to the extent that it was able to sterilize the Black Plague bacteria, making it relatively safe from infectious diseases. In the place where the royal family and the state guests were served, silver products were used habitually.
은의 원자량은 107.87 amu 이고 은이 살균력을 지녔다는 건 동서고금을 막론하고 이미 오래전부터 알려져 왔다. The atomic weight of silver is 107.87 amu, and it has been known for a long time that silver has sterilizing power.
이러한 은 나노 기술로 코팅된 금속은 강력한 항균 및 살균 기능, 전자파 차단 우수한 전기 전도성의 메커니즘을 가지게 되어 이러한 금속으로 만든 용기 내에서는 세균이 내성을 갖지 못한 것으로 밝혀 졌으며, 현재까지의 실험결과 지상의 거의 모든 단세포 병균을 짧은 시간에 살균하는 것으로 확인되었다. 은 나노의 주요 항균 메커니즘은 유해균의 세포막을 녹여서 세포 내의 효소와 작용하여 영양 물질의 대사기능 즉 영양물질유입 및 배출을 차단하고 유해균의 호흡기능과 생성을 막아 유해 균의 생육정지 및 재생 능력을 파괴하여 유해 균을 사멸한다. 은 나노는 일반 화학 항균제나 염소계 살균제와는 다르게 순수한 SILVER의 초미립자이므로, 고온에서도 탁월한 항균/제균력을 가지고 있으며 인체에 무독성, 무 자극성이며 세균이나 대장균 바이러스 곰팡이 균은 은 나노 물질과 5분 이상 접촉하여 살 수 없다는 결과가 보고되어 있다.Metals coated with this silver nanotechnology have a strong antibacterial and bactericidal function and a good electrical conductivity mechanism, which has proved that bacteria are not resistant in containers made of these metals. All unicellular pathogens were found to sterilize in a short time. The main antimicrobial mechanism of silver nano dissolves harmful cell membranes and interacts with enzymes in cells to block the metabolic function of nutrients, ie, the influx and discharge of nutrients, and to prevent the respiratory function and production of harmful bacteria, thereby destroying the growth and regeneration of harmful bacteria. To kill harmful bacteria. Unlike general chemical antibacterial and chlorine disinfectants, silver nanoparticles are pure SILVER's ultra-fine particles, so they have excellent antibacterial and antibacterial properties even at high temperatures, are nontoxic and non-irritating to humans. It has been reported that it cannot live.
은 나노의 추출방법은 증류수에 은(Ag 99.9%)을 투입하고 저온에서 저 전류를 발생시켜 은이 포함된 화합물을 전기 분해하여 각 분자가 가지고 있는 +, - 극을 이용한 전기영동을 실시한 후 은(Ag 99.9%)을 모을 수 있으며 그 밖에도 액상 환원법, 그라인딩 등의 물리적인 방법으로 제조할 수 있으며 안정적인 은 나노 물질을 얻기 위해서는 상기의 전기 분해법을 많이 사용하고 있다.The extraction method of silver nano is made by adding silver (Ag 99.9%) to distilled water and generating a low current at low temperature to electrolyze the compound containing silver, followed by electrophoresis using + and-poles of each molecule. Ag 99.9%) can be collected and can also be manufactured by physical methods such as liquid reduction and grinding. In order to obtain stable silver nanomaterials, the above electrolysis method is used a lot.
일 실시예에서는 은 이온 발생 제조기로부터 전기분해에 의하여 순수한 은 이온수 용액을 만든 후 일정시간 종이컵을 침전시키고, 그 후 건조과정을 거치면 종이컵에 은 나노 물질이 코팅되는 방법을 사용하였다.In one embodiment, a pure silver ionized water solution was prepared by electrolysis from a silver ion generator, and then a paper cup was precipitated for a predetermined time, and then, the drying process was followed by coating a silver nanomaterial on the paper cup.
또 다른 방법으로는 많은 음이온, 원적외선 방출 효과가 있도록 하기 위하여 항균력이 있는 은을 실리카에 도포시켜 실리카 은 나노를 형성한 후 종이컵 내부에 코팅시킨다. In another method, in order to have a large number of anion and far-infrared emission effects, antimicrobial silver is applied to silica to form silica silver nano and then coated inside the paper cup.
상기와 같이 은 나노 물질을 코팅하여 수차례에 걸쳐 실험을 한 결과 최소한 종이층의 0.05중량% 이상 코팅막이 형성되면 뜨거운 용액을 30분 동안 담아두어도 수분이 종이층으로 침투하지 않았으며, 형태가 변하지 않고 재사용이 가능하게 되었다. As a result of several experiments by coating the silver nanomaterial as described above, when at least 0.05% by weight of the coating layer was formed, the moisture did not penetrate into the paper layer even if the hot solution was kept for 30 minutes, and the shape did not change. It is possible to reuse without.
또한, 은 나노 물질은 많이 코팅될수록 효과는 좋다고 할 것이나, 종이층의 10중량% 또는 종이층의 10중량% 을 초과한 상태에서는 뜨거운 용액을 30분 동안 담아둔 상태에서 몇 번을 사용하여도 전혀 수분이 침투되지 않았으며 그 형상이 변하지 않았다. 즉, 은 함량이 종이층의 10중량% 가 초과한 상태에서는 더 많이 코팅을 하여도 더 이상 상승된 효과는 나타나지 않았다.In addition, the more the silver nanomaterial is coated, the better the effect. However, in a state where more than 10% by weight of the paper layer or 10% by weight of the paper layer, the hot solution is soaked for 30 minutes. Moisture did not penetrate and its shape did not change. That is, in the state where the silver content is more than 10% by weight of the paper layer, even if more coatings did not show an increased effect anymore.
따라서 본 발명의 목적과 경제적인 면을 고려할 때, 상기 은 나노 물질은 종이층의 0.05중량% 이상에서 10중량% 이하로 코팅하는 것이 바람직한 것으로 실험되었다.
Therefore, in consideration of the object and economic aspects of the present invention, it has been experimented that the silver nanomaterial is preferably coated in less than 10% by weight from 0.05% by weight of the paper layer.
그러나 종이컵의 내부를 모두 은 나노 물질인 제1코팅층으로 할 경우, 은의 열전도성이 높기 때문에 섭씨 90도의 차의 온도가 그대로 코팅층을 통하여 전달되기 때문에, 차를 마시기 위하여 종이컵을 입술에 닿는 순간 민감한 입술에 상당한 고통을 느끼게 되며 또 다른 불편을 초래하게 된다.However, when the inside of the paper cup is made of the first coating layer made of all silver nanomaterials, since the thermal conductivity of silver is high, the temperature of 90 degrees Celsius is transmitted through the coating layer. You will feel a lot of pain and cause another inconvenience.
그렇다고 입술이 닿는 부위만 남겨두고 코팅을 하게 되면 종이컵의 가장 중요한 입구부분이 수분의 침투에 의하여 컵이 흐물거리며 컵으로서의 기능을 상실하게 되어 재사용을 할 수 없게 된다.
However, if the coating is applied leaving only the area where the lips touch, the most important inlet of the paper cup is the cup's function due to the infiltration of water and the cup loses its function and cannot be reused.
이러한 문제를 해결하기 위하여 일 실시예에서는 도 2에 도시된 바와 같이 상기 컵 형상의 하단으로부터 소정의 높이까지 상기 종이층의 내측 면에 은 나노 입자를 포함하여 형성되는 제1 코팅층(11)을 형성하고 상기 제1 코팅층의 상단으로부터 상기 컵 형상의 상단까지 상기 종이층의 내측 면에는 열전도율이 낮은 ZrO2 또는 Al2O3 로 코팅한 제2코팅(12)층을 형성하였다.In order to solve this problem, in one embodiment, as shown in FIG. 2, the
구체적으로는 종이층의 내측면의 바닥면에서 80 ~ 90% 높이 까지는 은 나노 입자가 함유된 금속으로 코팅을 하는 제1코팅층(11)을 형성시키고, 입술이 닿는 부분인 상부 내측의 10~20%는 열전도율이 낮은 Al2O3 재질로 코팅을 하는 제2코팅층(12)을 형성하였다. 상기 제2코팅층(12)에 의하여 뜨거운 차를 마실 때에도 입술에 별다른 고통을 느끼지 않고 마실 수 있게 된다.Specifically, the
또 다른 일 실시예에서는 입술이 닿는 부분인 상부 내측 외에 상부 외측의 10~20%에 해당하는 1~2 Cm를 열전도율이 낮은 Al2O3재질로 코팅을 하는 제3코팅층(13)을 형성하여 바깥쪽에서 입술이 닿는 부위의 종이층이 수분에 의하여 침투되는 것을 방지하도록 하였다.
In another embodiment, the
또 다른 실시에서는 도 2에 도시된 바와 같이 제3코팅층을 외부 전체에 걸쳐서 열전도율이 낮은 ZrO2,또는 AL2O3 재질로 코팅을 하여 외부코팅층(14)을 형성하게 되면, 제1코팅층, 종이층, 그리고 열전도율이 낮은 ZrO2, 또는 AL2O3 재질의 특징으로 하는 외부코팅층(14)으로 형성된 단열 작용에 의하여 종이컵 내부에 뜨거운 차를 넣더라도 외부의 손잡는 부위에서는 뜨거운 감을 보다 적게 느끼게 되는 효과를 가지게 된다.
In another embodiment, as shown in FIG. 2, when the third coating layer is coated with ZrO 2 or AL 2 O 3 having low thermal conductivity over the entire exterior to form the
위와 같이, 본 발명의 종이컵은 내부를 수분이 쉽게 침투되지 않는 금속으로 코팅하였기 때문에 한번 사용 후 쉽게 형태가 쉽게 변형되지 않고 또한 종이컵 내부에 세척이 가능하여 사용 후 수차례에 걸쳐 재사용이 가능하게 된다.
As described above, since the paper cup of the present invention is coated with a metal which does not easily penetrate moisture inside, the paper cup is not easily deformed after one use and can be washed inside the paper cup to be reused several times after use. .
또한, 종래의 PE로 코팅된 종이컵의 재활용을 위해서는 내부의 PE 코팅을 기계적으로 벗겨내야 하기 때문에 재활용을 하기 위해 코팅을 벗기려면 종이컵이 원 모양대로 구겨지지 않아야 하기 때문에 종이컵을 수거한 양에 비하여 그 재활용률은 상대적으로 낮게 된다.In addition, in order to recycle a conventional PE coated paper cup, the internal PE coating must be peeled off mechanically. Therefore, to remove the coating for recycling, the paper cup must not be wrinkled in a circular shape. Recycling rates are relatively low.
이러한 이유는 종이컵을 구겨버리면 코팅을 기계적으로 벗기기 어렵게 되기 때문에 종이컵을 수거하여도 재활용률을 할 수 없게 되나, 본 발명은 금속재질로 코팅하였기 때문에 전기분해에 의하여 간단히 코팅층을 분리할 수가 있어서 재활용 비율을 높일 수 있는 효과가 있다.
The reason for this is that if the paper cup is crumpled, the coating is difficult to peel off mechanically, and thus the recycling rate cannot be obtained even when the paper cup is collected. It can increase the effect.
또한, 본 발명의 종이컵은 입술이 닫는 부분과 용액이 담겨져 있는 부분을 금속으로 코팅하였기 때문에 뜨거운 차를 수용하여도 컵이 원래의 형태를 유지할 수 있으며, 내부와 입술이 닫는 부위만 간단히 세척하여 건조시키면 원래의 형태로 재사용할 수 있는 효과가 있다.In addition, since the paper cup of the present invention is coated with a metal part covering the lips and the part containing the solution, the cup can maintain its original shape even when the hot tea is accommodated. This can be reused in its original form.
또한, 본 발명의 종이컵은 차의 용액이 수용되는 부분을 원적외선이 방출되고 항균력이 있는 은 나도 코팅을 함으로써, 종래의 종이컵에 비하여 건강에 유익하고 차의 맛과 향을 유지시킬 수 있는 효과가 있다.In addition, the paper cup of the present invention by coating the portion containing the solution of tea is far-infrared and antibacterial silver silver, it is beneficial to health and maintain the taste and aroma of tea compared to the conventional paper cup .
본 발명의 종이컵은 입술이 닿는 부위를 열전도율이 낮은 금속으로 코팅하였기 때문에 뜨거운 차를 마실 때에도 입술에 고통을 느끼거나 데일 염려가 없으며 상대적으로 열에 약한 입술을 보호할 수 있게 된다.
Since the paper cup of the present invention is coated with a metal with low thermal conductivity on the area where the lips touch, there is no fear of pain or lip even when drinking hot tea, and it is possible to protect the lips which are relatively heat-sensitive.
이상에서는 본 발명의 실시예들을 참조하여 설명하였지만, 해당 기술 분야에서 통상의 지식을 가진 자라면 하기의 특허청구범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 쉽게 이해할 수 있을 것이다.
Although the above has been described with reference to embodiments of the present invention, those skilled in the art may variously modify and modify the present invention without departing from the spirit and scope of the present invention as set forth in the claims below. It will be easy to understand that it can be changed.
<도면의 주요부분에 대한 부호의 설명>
1.: 종이컵
2: 종이컵 상부
3: 종이컵 내부의 코팅 부위
10: 종이층
11: 제1코팅층
12: 제2코팅층
13: 제3코팅층
14: 외부 코팅층<Description of the symbols for the main parts of the drawings>
1 .: paper cup
2: paper cup top
3: coating area inside the paper cup
10: paper layer
11: first coating layer
12: second coating layer
13: 3rd coating layer
14: outer coating layer
Claims (7)
상기 음료가 수용되도록 컵 형상으로 형성되는 종이층;
상기 종이컵 내측면의 하단으로부터 전체의 높이의 80% ~ 90% 높이까지 은 나노 입자가 함유된 금속으로 상기 종이층의 0.05중량% 이상에서 10중량% 이하의 비율로 코팅되는 제1 코팅층; 상기 제1 코팅층의 상단으로부터 상기 컵 형상의 상단까지 상기 종이층의 내측 면에 Al2O3 재질로 코팅되는 제2 코팅층: 및 상기 종이층의 외측면의 상단으로부터 1 ~ 2 Cm 범위에 Al2O3 재질로 코팅되는 제3 코팅층을 포함하는 재사용이 가능한 종이컵.
A paper cup in which drinks are accommodated,
A paper layer formed in a cup shape to accommodate the beverage;
A first coating layer coated with a metal containing silver nanoparticles from a lower end of the inner surface of the paper cup to a height of 80% to 90% of the total height at a ratio of 0.05% by weight or more to 10% by weight or less of the paper layer; A second coating layer coated with an Al 2 O 3 material on an inner surface of the paper layer from an upper end of the first coating layer to an upper end of the cup shape: and an Al 2 in a range of 1 to 2 Cm from an upper end of the outer surface of the paper layer. A reusable paper cup comprising a third coating layer coated with O 3 material.