KR101044491B1 - Making method of glove with dyed ultra high molecular weight polyethylene yarn - Google Patents

Making method of glove with dyed ultra high molecular weight polyethylene yarn Download PDF

Info

Publication number
KR101044491B1
KR101044491B1 KR1020090098948A KR20090098948A KR101044491B1 KR 101044491 B1 KR101044491 B1 KR 101044491B1 KR 1020090098948 A KR1020090098948 A KR 1020090098948A KR 20090098948 A KR20090098948 A KR 20090098948A KR 101044491 B1 KR101044491 B1 KR 101044491B1
Authority
KR
South Korea
Prior art keywords
molecular weight
high molecular
weight polyethylene
polyethylene yarn
ultra
Prior art date
Application number
KR1020090098948A
Other languages
Korean (ko)
Other versions
KR20110041918A (en
Inventor
강현서
Original Assignee
강현서
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 강현서 filed Critical 강현서
Priority to KR1020090098948A priority Critical patent/KR101044491B1/en
Publication of KR20110041918A publication Critical patent/KR20110041918A/en
Application granted granted Critical
Publication of KR101044491B1 publication Critical patent/KR101044491B1/en

Abstract

본 발명은 초고분자량 폴리에틸렌 사 염색 장갑의 제조방법에 관한 것이다.The present invention relates to a method for producing ultra high molecular weight polyethylene yarn dyed gloves.

본 발명의 초고분자량 폴리에틸렌 사 염색 장갑의 제조방법은, 초고분자량 폴리에틸렌 사의 표면에 윤활액을 도포하는 윤활액도포단계와; 컴프레셔와 연결된 에어공급관이 일측에 연결되어 있고, 원통형 관 형태로 형성되어 있는 타격관을 준비하여, 타격관 내부로 상기 초고분자량 폴리에틸렌 사를 통과시키면서, 에어공급관을 통해 압축 공기를 타격관 내부로 공급하여 타격관 내부를 통과하는 초고분자량 폴리에틸렌 사를 에어 타격하는 에어타격단계와; 상기 에어타격단계를 거친 초고분자량 폴리에틸렌 사에 염색약품을 공급하여 염색하는 염색단계와; 상기 염색된 초고분자량 폴리에틸렌 사를 장갑 형태로 직조하는 직조단계;를 포함하여 구성된다.Method for producing ultra-high molecular weight polyethylene yarn dyed gloves of the present invention, the lubricant application step of applying a lubricant to the surface of the ultra-high molecular weight polyethylene yarn; The air supply pipe connected to the compressor is connected to one side, and prepares a blow tube formed in the form of a cylindrical tube, and passes compressed ultra high molecular weight polyethylene yarn into the blow tube, and supplies compressed air into the blow tube through the air supply pipe. An air striking step of air striking the ultra high molecular weight polyethylene yarn passing through the blow tube; A dyeing step of dyeing by supplying a dyeing agent to the ultra-high molecular weight polyethylene yarn subjected to the air strike step; It is configured to include; weaving step of weaving the dyed ultra high molecular weight polyethylene yarn in the form of a glove.

본 발명에 의해, 초고분자량 폴리에틸렌 사의 표면에 윤활액을 도포한 후 타격관 내를 통과시키되 타격관을 통과하는 초고분자량 폴리에틸렌 사에 고압으로 공기를 공급하여 타격함으로써 표면에 미세한 홈을 다수 형성함으로써 염색이 용이해지도록 함으로써 색상을 표현하기 위해 별도의 이종 섬유를 혼방하지 않으면서 강도가 유지되는 초고분자량 폴리에틸렌 사 염색 장갑이 제공되며, 타격관 전 후로 각각 한 쌍 씩의 롤러를 설치하여 초고분자량 폴리에틸렌 사를 공급하되 후방측 롤러의 회전 속도와 전방측 롤러의 회전 속도를 조정하여 타격관 내부에서 초고분자량 폴리에틸렌사가 굴곡진 형태로 통과하도록 하여 압축 공기에 의한 타격이 섬유 의 여러 면에 골고루 이루어질 수 있게 되며, 고압의 에어로 초고분자량 폴리에틸렌 사를 타격함에 따라 섬유가 부드러워져 유연성이 개선되도록 하여 고강도이면서 부드러운 장갑이 제공된다.According to the present invention, by applying a lubricating liquid to the surface of the ultra high molecular weight polyethylene yarn and passing through the inside of the blow tube, but blows by supplying air at a high pressure to the ultra high molecular weight polyethylene yarn passing through the blow tube by forming a large number of fine grooves on the surface In order to facilitate color expression, ultra-high molecular weight polyethylene yarn dyed gloves are provided to maintain the strength without blending separate heterogeneous fibers, and a pair of rollers are installed before and after the blow tube to provide ultra high molecular weight polyethylene yarn. By supplying but adjusting the rotational speed of the rear roller and the rotational speed of the front roller to allow the ultra-high molecular weight polyethylene yarn to pass through the inside of the blow tube to be compressed by the compressed air can be evenly applied to various sides of the fiber, For hitting ultra high molecular weight polyethylene yarn with high pressure aero The softening of the fibers thus allows for improved flexibility, providing a high strength and soft glove.

초고분자량, 폴리에틸렌, 염색, 장갑 Ultra high molecular weight, polyethylene, dyeing, gloves

Description

초고분자량 폴리에틸렌 사 염색 장갑의 제조방법{Making method of glove with dyed ultra high molecular weight polyethylene yarn} Making method of glove with dyed ultra high molecular weight polyethylene yarn

본 발명은 내약품성이 높은 초고분자량 폴리에틸렌 사에 물리적 처리를 통해 일반 염색약품으로 염색 처리하여 직조하는, 초고분자량 폴리에틸렌 사 염색 장갑의 제조방법에 관한 것이다.The present invention relates to a manufacturing method of ultra-high molecular weight polyethylene yarn dyed gloves, which is dyed by a general dyeing chemicals through physical treatment to ultra high molecular weight polyethylene yarn having high chemical resistance.

중량 평균 분자량이 약 100만 이상의 고밀도 폴리에틸렌을 가리켜, 초고분자량 폴리에틸렌(ultra high molecular weight polyethylene, UHMW -PE )이라고 부르며, 일반적으로 UPE라고 알려져 있다.The weight average molecular weight refers to high density polyethylene of about 1 million or more, and is called ultra high molecular weight polyethylene (UHMW-PE), and is generally known as UPE.

초고분자량 폴리에틸렌은 일반 열가소성 플라스틱 중 내충격성 및 내마모성이 매우 뛰어난 특징을 가져 반송기계의 가이드레일, 체인, 컨베이어, 롤러 등 저마찰 계수 및 내마모성 및 내충격성이 요구되는 용도에 주로 사용된다.Ultra high molecular weight polyethylene has excellent impact resistance and abrasion resistance among general thermoplastics and is mainly used for applications requiring low friction coefficient, wear resistance and impact resistance, such as guide rails, chains, conveyors, and rollers of conveying machines.

위와 같은 초고분자량 폴리에틸렌을 섬유화 하여 적용하기도 하는데 주로 방탄복이나 산업용 장갑 등에 사용된다.Ultra high molecular weight polyethylene as described above is also applied to the fiber, mainly used in body armor and industrial gloves.

그런데, 초고분자량 폴리에틸렌은 산, 알칼리용제 등 약 80여종의 약품에 견뎌 내는 내약품성을 갖는 것으로 알려져 있다.By the way, ultra high molecular weight polyethylene is known to have chemical resistance to withstand about 80 kinds of drugs such as acid, alkali solvents.

따라서, 초고분자량 폴리에틸렌사를 이용한 장갑은 내약품성으로 인해 염색성이 나쁘기 때문에 공지의 염료로는 착색이 곤란한 문제점이 있었다.Therefore, the gloves using the ultra high molecular weight polyethylene yarn has a problem that it is difficult to color with a known dye because the dyeability is bad due to chemical resistance.

또, 바인더에 안료를 분산시킨 도료를 접착하더라도 접착력이 약해 접착된 도료가 분리되는 문제점이 있었다.In addition, even when the paint is dispersed in the pigment to the binder there is a problem that the adhesive strength is weak and the adhered paint is separated.

이처럼 염색성이 나쁜 초고분자량 폴리에틸렌사를 염색이 가능하도록 하기 위한 기술로, 초고분자량 폴리에틸렌 필라멘트를 복수개 집속하여 제조된 야안에 있어, 그 야안의 표면에 폴리아미드 피복층을, 야안의 간극부에 침입된 상태로 형성시켜 제조하는 기술이 '초고분자량 폴리에틸렌제 야안 및 그 야안을 착색시켜 제조한 낚시줄'(한국 등록특허공보 제10-0226043호)에 공개된 바 있다.As a technology for dyeing ultra-high molecular weight polyethylene yarns having poor dyeability as described above, in a yarn manufactured by converging a plurality of ultra-high molecular weight polyethylene filaments, a polyamide coating layer penetrates into the gap portion of the yarn. The technique of forming by forming a wire has been disclosed in the 'ultra high molecular weight polyethylene yarn and the fishing line made by coloring the yarn' (Korea Patent Publication No. 10-0226043).

상기와 같은 기술은 초고분자량 폴리에틸렌사의 표면에 폴리아미드 피복층을 간극부에 침입된 상태로 형성하여 착색이 가능하도록 하였다.As described above, the polyamide coating layer is formed on the surface of the ultra-high molecular weight polyethylene yarn in a state of penetration into the gap to enable coloring.

그러나, 상기와 같은 화학적 처리 방식은 공정이 복잡하여 제조 비용이 상승하고, 폴리에틸렌사의 물성이 변화하는 문제점이 있었다.However, the chemical treatment method as described above has a problem that the manufacturing cost increases due to the complicated process, and the physical properties of polyethylene yarn are changed.

이에 최근에 사용되는 방법은 장갑을 제조할 때 초고분자량 폴리에틸렌사와 색상을 갖는 이종의 섬유를 합사하거나 직조할 때 혼합 직조하여 색상 또는 무늬를 형성하고 있는 실정이다.In recent years, the method is used to form a color or pattern by mixing weaving when weaving or weaving heterogeneous fibers having a color with ultra high molecular weight polyethylene yarn when manufacturing gloves.

그러나, 이 역시 초고분자량 폴리에틸렌 사에 이종의 색상 섬유를 혼방함에 따라 구조적 강도가 저하되는 문제점이 있었다.However, this also has a problem in that the structural strength is lowered by mixing heterogeneous color fibers in ultra high molecular weight polyethylene yarn.

본 발명의 초고분자량 폴리에틸렌 사 염색 장갑의 제조방법은 상기와 같은 종래 기술에서 발생되는 문제점을 해소하기 위한 것으로, 화학적 처리가 아닌 간단한 물리적 처리를 통해 초고분자량 폴리에틸렌 사의 표면을 처리하여 일반 염색 약품으로 염색한 후 직조하는 염색 장갑을 제공하려는 것이다.The manufacturing method of the ultra-high molecular weight polyethylene yarn dyed gloves of the present invention is to solve the problems caused in the prior art as described above, by treating the surface of the ultra-high molecular weight polyethylene yarn through a simple physical treatment rather than chemical treatment and dyed with general dyeing chemicals After that we are going to provide dyed gloves to weave.

보다 구체적으로, 초고분자량 폴리에틸렌 사의 표면에 윤활액을 도포한 후 타격관 내를 통과시키되 타격관을 통과하는 초고분자량 폴리에틸렌 사에 고압으로 공기를 공급하여 타격함으로써 표면에 미세한 홈을 다수 형성함으로써 염색이 용이해지도록 함으로써 색상을 표현하기 위해 별도의 이종 섬유를 혼방하지 않으면서 강도가 유지되는 초고분자량 폴리에틸렌 사 염색 장갑을 제공하려는 것이다.More specifically, after applying a lubricating liquid to the surface of the ultra high molecular weight polyethylene yarn to pass through the blow tube, but blows by supplying air at a high pressure to the ultra high molecular weight polyethylene yarn passing through the blow tube to form a large number of fine grooves on the surface for easy dyeing It is intended to provide an ultra high molecular weight polyethylene yarn dyed glove that maintains strength without blending separate dissimilar fibers in order to render color.

이때, 타격관 전 후로 각각 한 쌍 씩의 롤러를 설치하여 초고분자량 폴리에틸렌 사를 공급하되 후방측 롤러의 회전 속도와 전방측 롤러의 회전 속도를 조정하여 타격관 내부에서 초고분자량 폴리에틸렌사가 굴곡진 형태로 통과하도록 하여 압축 공기에 의한 타격이 섬유의 여러 면에 골고루 이루어질 수 있게 하려는 것이다.At this time, a pair of rollers are installed before and after the blow tube to supply the ultra high molecular weight polyethylene yarn, but the ultra high molecular weight polyethylene yarn is curved in the inside of the blow tube by adjusting the rotation speed of the rear roller and the rotation speed of the front roller. It is intended to pass through so that blows by compressed air can be evenly distributed on different sides of the fiber.

결국, 상기와 같이 비교적 단순한 물리적 처리를 통해 초고분자량 폴리에틸렌 사에 염색 약품이 잘 부착되어 저렴한 비용으로 초고분자량 폴리에틸렌 사에 염색을 실시할 수 있게 되고, 이로 인해 다양한 색상을 갖는 장갑을 제공하려는 것이다.As a result, the dyeing agent is well attached to the ultra-high molecular weight polyethylene yarn through the relatively simple physical treatment as described above, and the dyeing can be performed on the ultra-high molecular weight polyethylene yarn at low cost, thereby providing a glove having various colors.

또한, 고압의 에어로 초고분자량 폴리에틸렌 사를 타격함에 따라 섬유가 부 드러워져 유연성이 개선되도록 하여 고강도이면서 부드러운 장갑을 제공하려는 것이다.In addition, by hitting the ultra-high molecular weight polyethylene yarn with a high-pressure air it is to provide a high-strength and soft gloves by softening the fiber to improve the flexibility.

본 발명의 초고분자량 폴리에틸렌 사 염색 장갑의 제조방법은 상기와 같은 기술적 과제를 해결하기 위하여, 초고분자량 폴리에틸렌 사의 표면에 윤활액을 도포하는 윤활액도포단계와; 컴프레셔와 연결된 에어공급관이 일측에 연결되어 있고, 원통형 관 형태로 형성되어 있는 타격관을 준비하여, 타격관 내부로 상기 초고분자량 폴리에틸렌 사를 통과시키면서, 에어공급관을 통해 압축 공기를 타격관 내부로 공급하여 타격관 내부를 통과하는 초고분자량 폴리에틸렌 사를 에어 타격하는 에어타격단계와; 상기 에어타격단계를 거친 초고분자량 폴리에틸렌 사에 염색약품을 공급하여 염색하는 염색단계와; 상기 염색된 초고분자량 폴리에틸렌 사를 장갑 형태로 직조하는 직조단계;를 포함하여 구성된다.Method for producing ultra-high molecular weight polyethylene yarn dyed gloves of the present invention, in order to solve the above technical problem, the lubricant coating step of applying a lubricant to the surface of the ultra-high molecular weight polyethylene yarn; The air supply pipe connected to the compressor is connected to one side, and prepares a blow tube formed in the form of a cylindrical tube, and passes compressed ultra high molecular weight polyethylene yarn into the blow tube, and supplies compressed air into the blow tube through the air supply pipe. An air striking step of air striking the ultra high molecular weight polyethylene yarn passing through the blow tube; A dyeing step of dyeing by supplying a dyeing agent to the ultra-high molecular weight polyethylene yarn subjected to the air strike step; It is configured to include; weaving step of weaving the dyed ultra high molecular weight polyethylene yarn in the form of a glove.

이때, 상기 에어타격단계에서, 타격관 앞에 서로 맞물려 회전하는 한 쌍의 전방롤러를 설치하고, 타격관 뒤에 서로 맞물려 회전하는 한 쌍의 후방롤러를 설치한 후 초고분자량 폴리에틸렌 사는 전방롤러와 후방롤러의 구동에 의해 타격관 내부로 삽입된 후 배출되도록 하는 것을 특징으로 한다.At this time, in the air striking step, after installing a pair of front rollers interlocking with each other in front of the impact pipe, and a pair of rear rollers interlocking with each other behind the impact pipe, the ultra high molecular weight polyethylene yarn of the front roller and the rear roller It is characterized in that it is discharged after being inserted into the blow tube by the drive.

또, 상기 에어공급관은 타격관 외주면에 다수 개가 각기 다른 각도로 연결되어 초고분자량 폴리에틸렌 사 둘레의 여러 각도에서 에어 타격하는 것을 특징으로 한다.In addition, the air supply pipe is characterized in that the air blow from a plurality of angles around the ultra high molecular weight polyethylene yarn is connected to a plurality of different angles on the outer peripheral surface of the blow pipe.

아울러, 타격관은 직경 0.1 내지 5 mm인 것을 특징으로 한다.In addition, the blow tube is characterized in that the diameter of 0.1 to 5 mm.

또한, 상기 직조단계에서 이종의 섬유를 혼합하여 직조하는 것을 특징으로 한다.In addition, the weaving step is characterized in that the weaving by mixing the different types of fibers.

본 발명에 의해, 화학적 처리가 아닌 간단한 물리적 처리를 통해 초고분자량 폴리에틸렌 사의 표면을 처리하여 일반 염색 약품으로 염색한 후 직조하는 염색 장갑이 제공된다.According to the present invention, there is provided a dyed glove which weaves the surface of the ultra high molecular weight polyethylene yarn through a simple physical treatment rather than a chemical treatment and dyes it with a general dyeing agent.

보다 구체적으로, 초고분자량 폴리에틸렌 사의 표면에 윤활액을 도포한 후 타격관 내를 통과시키되 타격관을 통과하는 초고분자량 폴리에틸렌 사에 고압으로 공기를 공급하여 타격함으로써 표면에 미세한 홈을 다수 형성함으로써 염색이 용이해지도록 함으로써 색상을 표현하기 위해 별도의 이종 섬유를 혼방하지 않으면서 강도가 유지되는 초고분자량 폴리에틸렌 사 염색 장갑이 제공된다.More specifically, after applying a lubricating liquid to the surface of the ultra high molecular weight polyethylene yarn to pass through the blow tube, but blows by supplying air at a high pressure to the ultra high molecular weight polyethylene yarn passing through the blow tube to form a large number of fine grooves on the surface for easy dyeing The ultra high molecular weight polyethylene yarn dyed glove is provided to maintain strength without blending separate dissimilar fibers in order to render color.

이때, 타격관 전 후로 각각 한 쌍 씩의 롤러를 설치하여 초고분자량 폴리에틸렌 사를 공급하되 후방측 롤러의 회전 속도와 전방측 롤러의 회전 속도를 조정하여 타격관 내부에서 초고분자량 폴리에틸렌사가 굴곡진 형태로 통과하도록 하여 압축 공기에 의한 타격이 섬유의 여러 면에 골고루 이루어질 수 있게 된다.At this time, a pair of rollers are installed before and after the blow tube to supply the ultra high molecular weight polyethylene yarn, but the ultra high molecular weight polyethylene yarn is curved in the inside of the blow tube by adjusting the rotation speed of the rear roller and the rotation speed of the front roller. Passage allows compressed air to evenly spread on different sides of the fiber.

결국, 상기와 같이 비교적 단순한 물리적 처리를 통해 초고분자량 폴리에틸렌 사에 염색 약품이 잘 부착되어 저렴한 비용으로 초고분자량 폴리에틸렌 사에 염색을 실시할 수 있게 되고, 이로 인해 다양한 색상을 갖는 장갑이 제공된다.As a result, the dyeing agent is well adhered to the ultra high molecular weight polyethylene yarn through the relatively simple physical treatment as described above, so that the dye can be dyed to the ultra high molecular weight polyethylene yarn at low cost, thereby providing gloves having various colors.

또한, 고압의 에어로 초고분자량 폴리에틸렌 사를 타격함에 따라 섬유가 부드러워져 유연성이 개선되도록 하여 고강도이면서 부드러운 장갑이 제공된다.In addition, by hitting the ultra-high molecular weight polyethylene yarn with high pressure air, the fiber is softened to improve the flexibility to provide a high-strength and soft gloves.

초고분자량 폴리에틸렌은 한 방향으로 초연신할 경우, 고분자 사슬의 배향도가 높아져 기계적 물성이 탁월하게 나타난다. When ultra-high molecular weight polyethylene is super-stretched in one direction, the degree of orientation of the polymer chain is increased, the mechanical properties are excellent.

이 섬유는 지금까지 상업적으로 시판되고 있는 고기능성 섬유인 아라미드 섬유(케블라), 탄소섬유, 특수 유리섬유, 보론 섬유 등에 비하여 비강도(단위 중량당 강도)가 높고, 비탄성율도 고탄성 탄소 섬유와 비슷하여 사용온도가 비교적 낮으면서 고강도가 요구되는 분야에서 수요가 증가하고 있다.This fiber has a higher specific strength (strength per unit weight) and higher inelasticity than high elastic carbon fiber compared to commercially available high-performance fibers such as aramid fiber (Kevlar), carbon fiber, special glass fiber and boron fiber. The demand is increasing in the field where the use temperature is relatively low and high strength is required.

고강도 기능이 요구되는 분야 중의 하나로 산업용 장갑이나 레저용 장갑 등이 있다.One of the fields requiring high strength is industrial gloves or leisure gloves.

이러한 초고분자량 폴리에틸렌은 내약품성이 강해 염색이 매우 어려워 색상을 표현하기 위한 의류나 장갑의 표면재료로는 사용되지 못하고 있는 실정이다.Such ultra-high molecular weight polyethylene has a strong chemical resistance, which is very difficult to dye, and thus it is not used as a surface material of clothing or gloves to express color.

이에, 본 발명의 출원인이 연구하던 중 압축 공기를 이용하여 타격이 가해졌을 때 마치 스크래치 작업을 할 때처럼 표면에 미세한 다수의 홈이 형성되고 이로 인해 염료가 표면에 잘 부착되는 것을 알게 되었다.Thus, when the applicant of the present invention while studying the impact is applied to the compressed air using a lot of fine grooves are formed on the surface as if scratching, it is found that the dye adheres well to the surface.

본 발명은 이러한 연구 결과에 의한 것으로 이하, 본 발명의 초고분자량 폴리에틸렌 사 염색 장갑의 제조방법에 대하여 보다 상세히 설명하기로 한다.The present invention is based on the results of this study, and will be described in more detail with respect to the manufacturing method of ultra-high molecular weight polyethylene yarn dyed gloves of the present invention.

본 발명의 초고분자량 폴리에틸렌 사 염색 장갑의 제조방법은 초고분자량 폴리에틸렌 사(60)의 표면에 윤활액을 도포하는 윤활액도포단계와, 초고분자량 폴리에틸렌 사(60)의 표면을 압축공기로 타격하는 에어타격단계와, 에어타격단계를 거친 초고분자량 폴리에틸렌 사를 염색하는 염색단계 및 염색된 초고분자량 폴리에틸렌 사를 장갑 형태로 직조하는 직조단계;를 포함하여 구성된다.Method for producing ultra-high molecular weight polyethylene yarn dyed gloves of the present invention is a lubricating liquid applying step of applying a lubricating liquid to the surface of the ultra-high molecular weight polyethylene yarn (60), and an air striking step of hitting the surface of the ultra-high molecular weight polyethylene yarn (60) with compressed air And a dyeing step of dyeing the ultra high molecular weight polyethylene yarns subjected to the air striking step, and a weaving step of weaving the dyed ultra high molecular weight polyethylene yarns in the form of gloves.

상술한 바와 같이 본 발명의 출원인은 압축 공기로 초고분자량 폴리에틸렌 사(60)를 타격하게 된 후 초고분자량 폴리에틸렌 사(60)에 염료를 피복시킬 경우 염료가 초고분자량 폴리에틸렌 사(60)의 표면에 부착되는 것을 알게 되었다.As described above, the applicant of the present invention, when hitting the ultra-high molecular weight polyethylene yarn (60) with compressed air and then coating the dye on the ultra-high molecular weight polyethylene yarn (60), the dye adheres to the surface of the ultra-high molecular weight polyethylene yarn (60) I found out.

그런데, 본 발명의 출원인이 수차례 실험 결과 압축 공기에 의해 초고분자량 폴리에틸렌 사(60)가 타격을 받게 되면서 타격관(10)을 통과한 초고분자량 폴리에틸렌 사(60)가 마치 실타래 엉키는 풀어지고 꼬여 엉킨 섬유를 풀어줘야 하는 불편함이 있는 것을 알게 되었다.However, the applicant of the present invention several times as a result of the experiment, the ultra high molecular weight polyethylene yarn (60) is hit by the compressed air, the ultra high molecular weight polyethylene yarn (60) passed through the blow tube (10) as if the thread is tangled loose and twisted I noticed the inconvenience of having to release the fibers.

윤활액도포단계는 이처럼 초고분자량 폴리에틸렌 사(60)가 압축공기에 의해 타격을 받기 전 액상의 윤활액을 도포함으로써 풀어지고 엉키게 되는 현상을 방지하기 위한 것이다.The lubricating liquid applying step is to prevent the phenomenon that the ultra-high molecular weight polyethylene yarn 60 is released and entangled by applying a liquid lubricating liquid before being hit by compressed air.

사용되는 윤활액은 대표적으로 물이나 오일 등을 사용할 수 있으며, 섬유유연제, 정전기방지제 등을 단독 또는 상기 물이나 오일에 혼합하여 사용할 수 있다.As the lubricating liquid to be used, water or oil may be typically used, and a fiber softener, an antistatic agent, or the like may be used alone or in combination with the water or oil.

윤활액의 공급 방식은 도시된 바와 같이 타격관(10)의 전방에 윤활액을 공급하는 윤활액공급관(30)을 설치하고 윤활액공급관(30) 선단에 노즐을 설치하여 공급할 수 있다.As shown in the drawing, the lubricating liquid may be supplied by installing a lubricating liquid supplying pipe 30 for supplying a lubricating liquid in front of the striking pipe 10 and installing a nozzle at the tip of the lubricating liquid supplying pipe 30.

또다른 방식으로는 도시하지는 않았으나 에어공급관(20)의 일측에 윤활액공급관(30)을 연결하여 에어와 함께 초고분자량 폴리에틸렌 사(60)에 공급되도록 할 수도 있다.Although not shown in another manner, the lubricant supply pipe 30 may be connected to one side of the air supply pipe 20 so as to be supplied to the ultra high molecular weight polyethylene yarn 60 together with the air.

에어타격단계는 도 1에 도시되어 있는 바와 같이 원통형 관 형태로 형성되어 있고, 컴프레셔와 연결된 에어공급관(20)이 일측에 연결되어 있는 타격관(10)을 준비한 후 타격관(10) 내부로 초고분자량 폴리에틸렌 사(60)를 통과시키면서 에어공급관(20)을 통해 타격관(10) 내부로 압축공기를 공급하여 타격관(10) 내부를 통과하는 초고분자량 폴리에틸렌 사(60)를 타격하도록 구성되어 있다.The air striking step is formed in the shape of a cylindrical tube, as shown in Figure 1, after preparing the blow pipe 10 is connected to the air supply pipe 20 connected to the compressor is very high inside the blow pipe (10) While passing through the molecular weight polyethylene yarn (60) it is configured to blow the ultra-high molecular weight polyethylene yarn (60) passing through the blow tube (10) by supplying compressed air into the blow tube (10) through the air supply pipe (20). .

컴프레셔는 일반 산업용 컴프레셔를 이용하면 되며, 단지 에어공급관(20)의 내경이 0.1 ~ 1.5mm 정도 되도록 하거나 에어공급관(20) 끝단의 내경이 상기와 같은 크기가 되도록 하여 압축공기가 공급되도록 하면 된다.The compressor may be a general industrial compressor, and only the inner diameter of the air supply pipe 20 is about 0.1 to 1.5 mm or the inner diameter of the end of the air supply pipe 20 is the same size as described above to supply compressed air.

이때, 일측 방향에서만 압축공기를 공급하게 되면 초고분자량 폴리에틸렌 사(60)의 일측 면만 압축공기에 의한 미세 홈이 형성되어 타측면은 염료가 잘 부착되지 않게 된다.At this time, when compressed air is supplied only in one side, only one side of the ultra high molecular weight polyethylene yarn 60 is formed with fine grooves by compressed air, so that the other side is not easily attached to the dye.

이에 에어타격단계에서 초고분자량 폴리에틸렌 사(60)의 표면 둘레 전체 내지 둘레 전체에는 못 미치더라도 전체적으로 염색되었을 정도가 되기 위해서는 도 3에 도시된 바와 같이 상, 하, 좌, 우에 다수 개의 에어공급관(20)을 연결하여 전체 둘레가 압축공기에 의해 타격되도록 하는 것이 바람직하다.Thus, in order to be totally dyed even if less than the entire surface circumference to the entire circumference of the ultra-high molecular weight polyethylene yarn 60 in the air strike step, as shown in Figure 3 a plurality of air supply pipe 20 in the upper, lower, left, right ) So that the entire circumference is hit by compressed air.

이처럼 상,하, 좌, 우에서 각각 압축공기로 골고루 타격이 이루어지게 되면 초고분자량 폴리에틸렌 사(60)의 전체 표면에 골고루 미세 홈이 형성되면서 염색이 가능한 재질로 변경되게 된다.When hitting evenly with compressed air in each of the upper, lower, left, and right as described above, fine grooves are evenly formed on the entire surface of the ultra-high molecular weight polyethylene yarn 60, thereby changing to a dyeable material.

그런데, 상기와 같이 여러 개의 에어공급관(20)을 타격관(10)에 연결할 경우 여러 개의 컴프레셔 및 에어공급관(20)을 설치해야 하므로 생산성이 떨어지는 단점이 발생할 수 있다.By the way, when connecting a plurality of air supply pipe 20 to the blow tube 10 as described above, it is necessary to install a plurality of compressors and air supply pipe 20, there may be a disadvantage that the productivity is low.

도 1은 이러한 문제점을 해소하여 보다 생산성을 향상시키기 위한 예를 도시한 것으로 타격관(10)을 통과하는 초고분자량 폴리에틸렌 사(60)를 상하 지그재그 형상 또는 상하좌우 지그재그 형상으로 퍼져 이동하도록 하고, 1 내지 2 개의 에어공급관(20)만을 타격관(10)에 연결하여 최소한의 에어공급관(20)을 설치하면서 초고분자량 폴리에틸렌 사(60)의 표면에 골고루 미세 홈이 형성되도록 한 것이다.FIG. 1 illustrates an example for solving such a problem and improving productivity. The ultra high molecular weight polyethylene yarn 60 passing through the blow tube 10 is spread and moved in a vertical zigzag shape or a vertical zigzag shape. By connecting only two air supply pipe 20 to the blow tube 10 to install a minimum air supply pipe 20 is to form a fine groove evenly on the surface of the ultra-high molecular weight polyethylene yarn (60).

이처럼 타격관(10) 내부에서 초고분자량 폴리에틸렌 사(60)가 유동성을 갖도록 하기 위한 조건으로 타격관(10)의 직경 즉 내경은 0.1 내지 5 mm인 것이 바람직하다.As such, the diameter of the blow tube 10, that is, the inner diameter of the blow tube 10 is preferably 0.1 to 5 mm in order to allow the ultra high molecular weight polyethylene yarn 60 to have fluidity within the blow tube 10.

만약, 5 mm를 초과할 경우 타격관(10) 내부에서의 유동성이 너무 커져 비록 윤활액을 도포하더라도 섬유가 엉킬 가능성이 높아지며, 0.1mm 미만일 경우에는 유동성이 너무 작아 섬유 표면에 전체적으로 미세 홈이 형성되지 않아 표면적 대비 염색 비율이 저하되게 된다.If it exceeds 5 mm, the fluidity inside the blow tube 10 becomes too large, so even if lubricating liquid is applied, the fiber is more likely to be entangled. If it is less than 0.1 mm, the fluidity is so small that fine grooves are not formed entirely on the fiber surface. As a result, the ratio of dyeing to surface area is reduced.

상기와 같이 초고분자량 폴리에틸렌 사(60) 외경보다 크게 타격관(10)을 형성하게 되면 컴프레셔에 의해 압축공기가 타격관(10) 내부로 유입되면서 초고분자량 폴리에틸렌 사(60)를 타격하게 되므로 섬유는 자연스럽게 지그재그 형태로 이동하게 된다.When the blow tube 10 is formed larger than the outer diameter of the ultra high molecular weight polyethylene yarn 60 as described above, the compressed air is blown into the blow tube 10 by the compressor, and thus the fiber is blown by the ultra high molecular weight polyethylene yarn 60. It naturally moves in a zigzag form.

한편, 상기와 같이 타격관(10) 내부에서 지그재그로 유동성 있게 이동이 가능하도록 하기 위해 타격관(10)의 전방과 후방에는 각각 초고분자량 폴리에틸렌 사(60)를 견인할 수 있도록 롤러를 설치하는 것이 바람직하다.On the other hand, in order to be able to move in a zigzag fluid within the impact tube 10 as described above it is to install a roller to pull the ultra-high molecular weight polyethylene yarn 60 in front and rear of the impact tube 10, respectively. desirable.

이를 위해 도시된 바와 같이 타격관(10) 앞에 서로 맞물려 회전하는 한 쌍의 전방롤러(50)를 설치하고, 타격관(10) 뒤에 서로 맞물려 회전하는 한 쌍의 후방롤러(40)를 설치한 후 초고분자량 폴리에틸렌 사(60)는 전방롤러(50)와 후방롤러(40)의 구동에 의해 타격관(10) 내부로 삽입된 후 배출되도록 하는 것이 바람직하다.To this end, a pair of front rollers 50 are engaged with each other and rotated in front of the impact pipe 10 as shown, and a pair of rear rollers 40 are engaged with each other and rotated behind the impact pipe 10. Ultra high molecular weight polyethylene yarn 60 is preferably discharged after being inserted into the blow tube 10 by the drive of the front roller 50 and the rear roller 40.

이때, 전방롤러(50)와 후방롤러(40)의 회전 속도는 일정하게 진행하되, 일정 시점에서 후방롤러(40)의 회전속도를 빠르게 하면서 전방롤러(50)의 회전속도를 느리게 하여 타격관(10) 내부에서 초고분자량 폴리에틸렌 사(60)가 지그재그로 유동성을 가질 수 있게 할 수 있다.At this time, the rotational speed of the front roller 50 and the rear roller 40 proceeds uniformly, while at a certain time to increase the rotational speed of the rear roller 40 to slow down the rotational speed of the front roller (50) ( 10) it is possible to make the ultra high molecular weight polyethylene yarn 60 zigzag fluidity inside.

아울러, 상기와 같은 구성에서 타격관(10)은 도시된 것처럼 후방측에 직경이 넓은 확장부(11)를 형성하여 초고분자량 폴리에틸렌 사(60)의 유입이 용이하도록 하는 것이 바람직하다.In addition, in the configuration as described above, the impact tube 10 is preferably formed to expand the wide diameter portion 11 on the rear side as shown to facilitate the introduction of ultra-high molecular weight polyethylene yarn (60).

상기와 같이 윤활액도포단계 및 에어타격단계를 거친 후 초고분자량 폴리에틸렌 사(60)에 염색약품을 공급하여 염색을 실시한다.After the lubricating liquid application step and the air striking step as described above, the dye is supplied to the ultra-high molecular weight polyethylene yarn (60) by dyeing.

이때, 에어타격단계를 거친 후 초고분자량 폴리에틸렌 사(60) 표면에 묻은 수분을 제거한 후 염색을 한다.At this time, after the air striking step is removed after staining the ultra-high molecular weight polyethylene yarn (60) surface.

염색단계는 공지의 다양한 염료를 적용하여 염료가 저장된 용기에 초고분자량 폴리에틸렌 사(60)를 담구거나 통과시키는 방법으로 진행한다.The dyeing step proceeds by applying various known dyes to immerse or pass the ultra high molecular weight polyethylene yarn 60 in a container in which the dye is stored.

염색이 끝난 초고분자량 폴리에틸렌 사(60)는 장갑 형태로 직조하기 위한 공지의 다양한 직조기에 투입하여 장갑 형태로 직조한다. Dyeing ultra high molecular weight polyethylene yarn 60 is put into a variety of known weaving machines for weaving in the form of gloves to weave in the form of gloves.

최종 완성된 형태는 도 4에 도시된 바와 같이 다양한 색상으로 염색된 것을 알 수 있다.The final finished form can be seen that it is dyed in various colors as shown in FIG.

이때, 장갑 제조시에는 초고분자량 폴리에틸렌 사(60) 외 다양한 기능성 섬유를 혼합하여 직조할 수도 있다.At this time, when manufacturing gloves, ultra-high molecular weight polyethylene yarn 60 and other functional fibers may be mixed and woven.

도 2는 전처리된 초고분자량 폴리에틸렌 사(60)의 표면에 염색약품을 공급했을 때의 상태를 도시한 것으로 초고분자량 폴리에틸렌 사(60)의 표면에는 쐐기형태의 미세한 홈이 다수 형성되어 있으며 이로 인해 염색층(70)이 섬유 표면에 잘 부착되어 있음을 확인할 수 있다.Figure 2 shows the state when the dye is supplied to the surface of the pre-treated ultra-high molecular weight polyethylene yarn (60), the surface of the ultra-high molecular weight polyethylene yarn (60) is formed with a number of wedge-shaped fine grooves due to the dyeing It can be seen that layer 70 adheres well to the fiber surface.

아울러, 고압의 에어로 초고분자량 폴리에틸렌 사를 타격함에 따라 섬유가 부드러워져 유연성이 개선되도록 하여 고강도이면서도 부드러운 장갑이 제조됨을 확인할 수 있었다.In addition, by hitting the ultra-high molecular weight polyethylene yarn with a high-pressure air it was confirmed that the fiber is softened to improve the flexibility to produce a high-strength yet soft gloves.

도 1은 본 발명에서 윤활액도포단계 및 에어타격단계를 나타낸 개략도.1 is a schematic view showing a lubricating liquid applying step and the air blow step in the present invention.

도 2는 본 발명에서 염색이 완료된 상태에서 초고분자량 폴리에틸렌 사의 섬유 단면을 나타낸 단면 개략도.Figure 2 is a schematic cross-sectional view showing a fiber cross section of ultra high molecular weight polyethylene yarn in the dyeing is completed in the present invention.

도 3은 본 발명에서 사용되는 타격관의 또다른 예를 나타낸 사시도.Figure 3 is a perspective view showing another example of the blow tube used in the present invention.

도 4는 본 발명의 제조방법에 의해 제조된 장갑의 예를 나타낸 사진.Figure 4 is a photograph showing an example of a glove manufactured by the manufacturing method of the present invention.

<도면의 주요 부호에 대한 상세한 설명><Detailed Description of Major Symbols in Drawing>

10 : 타격관 11 : 확장부10: blow tube 11: extension portion

20 : 에어공급관 30 : 윤활액공급관20: air supply pipe 30: lubricating liquid supply pipe

40 : 후방롤러 50 : 전방롤러40: rear roller 50: front roller

60 : 초고분자량 폴리에틸렌 사 70 : 염색층60: ultra high molecular weight polyethylene yarn 70: dyed layer

Claims (5)

염색 장갑의 제조방법에 있어서,In the manufacturing method of the dyed gloves, 초고분자량 폴리에틸렌 사의 표면에 윤활액을 도포하는 윤활액도포단계와;A lubricating liquid applying step of applying a lubricating liquid to the surface of the ultra high molecular weight polyethylene yarn; 컴프레셔와 연결된 에어공급관(20)이 일측에 연결되어 있고, 원통형 관 형태로 형성되어 있는 타격관(10)을 준비하여, 타격관(10) 내부로 상기 초고분자량 폴리에틸렌 사(60)를 통과시키면서, 에어공급관(20)을 통해 압축 공기를 타격관(10) 내부로 공급하여 타격관(10) 내부를 통과하는 초고분자량 폴리에틸렌 사(60)를 에어 타격하는 에어타격단계와;The air supply pipe 20 connected to the compressor is connected to one side, and prepares a blow tube 10 formed in a cylindrical tube shape, while passing the ultra high molecular weight polyethylene yarn 60 into the blow tube 10, An air striking step of supplying compressed air into the blow tube 10 through the air supply pipe 20 to blow the ultra high molecular weight polyethylene yarn 60 passing through the blow tube 10; 상기 에어타격단계를 거친 초고분자량 폴리에틸렌 사에 염색약품을 공급하여 염색하는 염색단계와;A dyeing step of dyeing by supplying a dyeing agent to the ultra-high molecular weight polyethylene yarn subjected to the air strike step; 상기 염색된 초고분자량 폴리에틸렌 사를 장갑 형태로 직조하는 직조단계;를 포함하여 구성된,Weaving step of weaving the dyed ultra-high molecular weight polyethylene yarn in the form of a glove; 초고분자량 폴리에틸렌 사 염색 장갑의 제조방법.Method for producing ultra-high molecular weight polyethylene yarn dyed gloves. 제 1항에 있어서,The method of claim 1, 상기 에어타격단계에서,In the air strike step, 타격관(10) 앞에 서로 맞물려 회전하는 한 쌍의 전방롤러(50)를 설치하고, 타격관(10) 뒤에 서로 맞물려 회전하는 한 쌍의 후방롤러(40)를 설치한 후 초고분 자량 폴리에틸렌 사(60)는 전방롤러(50)와 후방롤러(40)의 구동에 의해 타격관(10) 내부로 삽입된 후 배출되도록 하는 것을 특징으로 하는,After installing a pair of front rollers 50 to be engaged with each other to rotate in front of the impact pipe (10), and after installing a pair of rear rollers (40) rotated to interlock with each other behind the impact pipe (10) ultra high molecular weight polyethylene yarn ( 60 is characterized in that to be discharged after being inserted into the impact tube 10 by the drive of the front roller 50 and the rear roller 40, 초고분자량 폴리에틸렌 사 염색 장갑의 제조방법.Method for producing ultra-high molecular weight polyethylene yarn dyed gloves. 제 1항에 있어서,The method of claim 1, 상기 에어공급관(20)은 타격관(10) 외주면에 다수 개가 각기 다른 각도로 연결되어 초고분자량 폴리에틸렌 사(60) 둘레의 여러 각도에서 에어 타격하는 것을 특징으로 하는,The air supply pipe 20 is connected to a plurality of different angles on the outer circumferential surface of the blow pipe 10, characterized in that the air blow at various angles around the ultra-high molecular weight polyethylene yarn 60, 초고분자량 폴리에틸렌 사 염색 장갑의 제조방법.Method for producing ultra-high molecular weight polyethylene yarn dyed gloves. 제 2항 내지 제 3항 중 어느 한 항에 있어서,The method according to any one of claims 2 to 3, 상기 타격관(10)은 직경 0.1 내지 5 mm인 것을 특징으로 하는,The blow tube 10 is characterized in that the diameter of 0.1 to 5 mm, 초고분자량 폴리에틸렌 사 염색 장갑의 제조방법.Method for producing ultra-high molecular weight polyethylene yarn dyed gloves. 제 4항에 있어서,The method of claim 4, wherein 상기 직조단계에서 이종의 섬유를 혼합하여 직조하는 것을 특징으로 하는,In the weaving step, characterized in that weaving by mixing different kinds of fibers, 초고분자량 폴리에틸렌 사 염색 장갑의 제조방법.Method for producing ultra-high molecular weight polyethylene yarn dyed gloves.
KR1020090098948A 2009-10-16 2009-10-16 Making method of glove with dyed ultra high molecular weight polyethylene yarn KR101044491B1 (en)