KR100942387B1 - Method of manufacturing coated functional paper - Google Patents

Method of manufacturing coated functional paper Download PDF

Info

Publication number
KR100942387B1
KR100942387B1 KR1020070117629A KR20070117629A KR100942387B1 KR 100942387 B1 KR100942387 B1 KR 100942387B1 KR 1020070117629 A KR1020070117629 A KR 1020070117629A KR 20070117629 A KR20070117629 A KR 20070117629A KR 100942387 B1 KR100942387 B1 KR 100942387B1
Authority
KR
South Korea
Prior art keywords
paper
functional
silica
functional material
sap
Prior art date
Application number
KR1020070117629A
Other languages
Korean (ko)
Other versions
KR20090051304A (en
Inventor
이규주
Original Assignee
이규주
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이규주 filed Critical 이규주
Priority to KR1020070117629A priority Critical patent/KR100942387B1/en
Publication of KR20090051304A publication Critical patent/KR20090051304A/en
Application granted granted Critical
Publication of KR100942387B1 publication Critical patent/KR100942387B1/en

Abstract

본 발명은 코팅기능종이 제조방법에 관한 것으로 음이온, 원적외선이 방출되는 토르마린(Tourmaline) 원석에서 유해 중금속, 이물질을 제거시키고 실리카(SiO2)에 담지시켜 많은 기공을 구성시켜 비중을 줄이고 많은 량의 음이온, 원적외선을 방출시키도록 구성시킨 실리카 토르마린(SiO2-Tourmaline)과 항균력이 있는 은(Ag)을 실리카(SiO2) 표면에 도포시켜 은(Ag)의 표면을 확대시켜 많은 량의 항균력을 갖도록 구성시킨 실리카 은나노(SiO2-Ag-nano)를 구비시키고 한가지 이상을 수액에 혼합시켜 기능 물질 수액으로 만들고 기능 물질 수액을 분사기로 종이표면에 분사시켜 기능 물질 입자를 종이표면에 도포시킨 다음 그 위에 PE 피막으로 도포시키면서 냉각로라를 통과시켜 코팅기능종이로 구성시킨다.

Figure R1020070117629

실리카 토르마린, 실리카 은나노, 코팅, 분사기, 기능 물질 수액.

The present invention relates to a method for producing coated functional paper, which removes harmful heavy metals and foreign substances from tourmaline gemstones in which negative ions and far-infrared rays are released, and is supported on silica (SiO 2 ) to form many pores to reduce specific gravity and a large amount of anions. Silica tourmaline (SiO 2- Tourmaline) and antimicrobial silver (Ag), which are configured to emit far infrared rays, are applied to the surface of silica (SiO 2 ) to enlarge the surface of silver (Ag) to have a large amount of antimicrobial activity. Made of silica silver nano (SiO 2 -Ag-nano) and mixed at least one into the sap into a functional material sap, and sprays the functional material sap on the paper surface with a sprayer to apply the functional material particles on the paper surface and then PE It is composed of coated functional paper by passing through a cooling roller while applying a film.

Figure R1020070117629

Silica tourmaline, silica silver nano, coatings, sprays, sap of functional substances.

Description

코팅기능종이 제조방법{omitted}Coating functional paper manufacturing method {omitted}

본 발명은 코팅기능종이 제조방법에 관한 것으로 음이온, 원적외선이 방출되는 토르마린(Tourmaline) 원석에서 유해 중금속, 이물질을 제거시키고 실리카(SiO2)(1)에 담지시켜 많은 기공(3)을 구성시켜 비중을 줄이고 많은 량의 음이온, 원적외선을 방출시키도록 도 1과 같이 구성시킨 실리카 토르마린(SiO2-Tourmaline)(4)(이하 기능 물질로 칭함)과 항균력이 높은 은(Ag)(5)의 표면을 확대시켜 항균력을 높이도록 도 2와 같이 구성시킨 실리카 은나노(SiO2-Ag-nano)(6)(이하 기능 물질로 칭함)를 구비시키고, 이와는 달리 도 3과 같은 기능 물질 수액 제조기(13)를 하단에 물배출구(11)를 설치시킨 물탱크(7)를 만들고 벽면에 0.25mm의 많은 구멍을 구성시킨 철망 원통(8)을 물탱크(7) 안에 설치시키고 모타(10)와 연결시킨 임페라(9)를 철망 원통(8) 안쪽에 설치시켜 구성시키고, 철망 원통(8) 안에 기능 물질 분말(16)을 담고 물탱크(7)에 수액을 담은후 임페라(9)를 회전시켜 기능 물질 분말이 0.25mm 이하의 것만 수액과 혼합되어 기능 물질 수액(12)으로 만들어지도록 하고 만들어진 기능 물질 수액(12)은 물탱크(7)의 물배출구(11)와 연결된 기능 물질 수액 배관을 통해 분사기(14)로 이송되어 로즐(15)에서 종이표면에 도 5 와 같이 분사되고 기능 물질 수액(12)에 포함되어 있던 기능 물질 분말(16)은 종이표면에 도포되어 도 6과 같이 기능종이가 구성된다 이렇게 구성된 기능종이 표면에 도 7과 같이 통상적인 코팅방법으로 PE 피막(20)을 도포시켜 도 8과 같은 코팅기능종이로 구성시킨다.The present invention relates to a method for producing coated functional paper, which removes harmful heavy metals and foreign substances from tourmaline gemstones in which negative ions and far-infrared rays are released, and is supported on silica (SiO 2 ) (1) to form many pores (3). The surface of silica tourmaline (SiO 2- Tourmaline) (4) (hereinafter referred to as a functional substance) and high antibacterial silver (5), which are configured as shown in FIG. 1 to reduce the amount of negative ions and emit far infrared rays, Silica silver nano (SiO 2 -Ag-nano) (6) (hereinafter referred to as a functional material) configured as shown in Figure 2 to enlarge and increase the antimicrobial power, and the functional material sap maker 13 as shown in FIG. Impeller connected to the motor (10) by installing the water tank (7) with the water outlet (11) installed at the bottom, and installing the wire mesh (8) in the water tank (7) with a large number of holes of 0.25 mm on the wall. 9) is installed inside the wire mesh cylinder (8), The functional material powder 16 is contained in the network cylinder 8 and the sap is contained in the water tank 7, and then the impeller 9 is rotated so that only the functional material powder is mixed with the sap of 0.25 mm or less, thereby the functional material sap 12. The functional material sap 12 which is made to be made and is transferred to the injector 14 through the functional material sap pipe connected to the water outlet 11 of the water tank 7, and the paper surface on the paper surface in the lobe 15 as shown in FIG. 5. The functional material powder 16 sprayed and contained in the functional material sap 12 is applied to the surface of the paper to form functional paper as shown in FIG. 6. The functional paper surface thus formed is coated with a conventional coating method as shown in FIG. (20) is applied to constitute a coating functional paper as shown in FIG.

종래의 코팅종이 제조방법은 원하는 기능 물질로 마스타 배치(MASTER BATCH)로 만든다음 종이위에 코팅시키는 방법을 사용하고 있다.Conventional coating paper manufacturing method uses a method of making a master batch (MASTER BATCH) with a desired functional material and then coating on a paper.

이러한 방법은 기능 물질이 코팅제(PE, PP)와 용해가 되는 물질인 경우(색소, 향로)에는 가능하지만 실리카 토르마린, 실리카 은나노, 게르마늄, 황토와 같은 광물질은 코팅제(PE, PP)와 용해되지 않을뿐만 아니라 용해시에 고 열로 인하여 타거나, 색이 변질되어 코팅표면에 미관상 원하지 않는 색의 점으로 나타나는 결점이 있고 기능도 파괴될수 있는 결점도 있다.This method is possible when the functional material is a dissolving material (pigment, incense) with the coating (PE, PP), but minerals such as silica tourmaline, silica silver nano, germanium and ocher will not dissolve with the coating (PE, PP). In addition, there is a defect that burns due to high heat or discolors due to high heat during dissolution, and the appearance of undesired color spots on the surface of the coating, and the function may be destroyed.

그러나 종이를 만들때 기능 광물질을 펄프에 혼합시켜 기능 종이로 만든다음 종이위에 코팅을 시키는 방법은 있으나 이러한 방법은 기능 물질이 종이표면에만 있게되는 것이 아니고 종이부피 전체에 분포되기 때문에 많은 기능 물질이 소모되고 종이 비중이(무게) 커지게 되는 결점이 있으며 소량으로 제조할 수 없는 결점이 있다However, when making paper, there is a method of mixing functional minerals into pulp to make a functional paper and then coating it on paper. However, this method consumes many functional materials because the functional material is not only on the paper surface but is distributed throughout the paper volume. Defects that can increase the specific gravity of paper, and cannot be manufactured in small quantities

본 발명은 코팅기능종이 제조방법에 관한것으로 합성수지재(PE, PP, ABS)에 용해 되지 않는 광물질과 같은 물질을 마스타 배치(MASTE BATCH)로 만들어 종이표면에 코팅시키면 합성수지재가 용해되는 열에 의해 광물질 입자가 원하지 않는 색점으로 나타나는 결점이 있고, 광물질의 기능이 변질되는 결점이 있게된다.The present invention relates to a method for producing a coated functional paper, and to make a material such as a mineral material that does not dissolve in synthetic resin (PE, PP, ABS) to make a master batch (MASTE BATCH) coated on the surface of the mineral mineral particles by heat dissolving the synthetic resin material There is a defect that appears as an unwanted color point, and there is a defect that the function of the mineral is altered.

따라서 본 발명에서는 광물질의 분말을 수액에 혼합시켜 기능 물질 수액으로 만들고 종이표면에 분사시켜 기능 물질 입자를 종이표면에 접착시키고 접합시킨 다음 그 위에 PE 코팅을 시켜 종이표면에 기능성을 살리면서 광물질 입자의 색과 기능성을 변질시키지 않도록 함을 목적으로 한다Therefore, in the present invention, the powder of mineral material is mixed into the sap to make the functional material sap, and sprayed on the surface of the paper to bond the functional material particles to the paper surface, and then join the PE coating on the surface of the mineral particles while maintaining the functionality on the paper surface. The purpose is not to alter color and functionality

기능 물질 수액 제조기(13)를 도 3과 같이 구성시키고 접착력이 있는 수액을 담고 기능 물질 분말(16)을 투입시킨 후 임페라(9)를 회전시켜 0.25mm 이하의 기능 물질 입자만을 수액과 혼합시켜 기능 물질 수액(12)으로 만든다음 분사기(14)로 종이표면에 분사시켜 기능 물질 분말을 종이표면에 도포시키므로서 종이표면에 기능성을 만들어 주고 그위에 도 7과 같은 방법으로 코팅시켜 코팅기능종이로 제조 시킨다.The functional material sap maker 13 is configured as shown in FIG. 3 and contains the adhesive sap, the functional material powder 16 is added thereto, and the impeller 9 is rotated to mix only 0.25 mm or less of the functional material particles with the sap. It is made of the material sap 12 and then sprayed on the paper surface with the injector 14 to apply the functional material powder on the paper surface, thereby making the functionality on the paper surface coated on the surface as shown in FIG. Let's do it.

본 발명에서는 기능 물질 분말로 기능 물질 수액으로 만들고 종이표면에 분사시켜 기능 물질 분말을 종이표면에 도포시킨 다음 그 위에 PE 코팅 피막을 도포시켜 코팅시키므로서 기능 물질 분말 색이 변하지 않고 기능이 파괴되지 않는 효과가 있게된다.In the present invention, the functional material powder is made of the functional material sap and sprayed on the paper surface to apply the functional material powder on the paper surface and then coated by coating the PE coating film thereon so that the color of the functional material powder does not change and the function is not destroyed. Will be effective.

본 발명은 코팅기능종이 제조방법에 관한 것으로 첨부된 도면을 참조하여 설명하면 다음과 같다.The present invention is described with reference to the accompanying drawings as a functional paper coating method as follows.

음이온, 원적외선을 방출시키는 토르마린(Tourmaline) 원석에서 유해 중금속, 이물질을 제거시키고 실리카(SiO2)(1)에 담지시켜 많은 기공(3)을 만들고 비중을 줄이고 많은 량의 음이온 원적외선을 방출시키도록 구성시킨 도 1과 같은 실리카 토르마린(SiO2-Tourmaline)(4)과 항균력이 높은 은(Ag)(5)을 실리카(SiO2)(1)에 도포시켜 항균력을 높이도록 구성시킨 도 2와 같은 실리카 은나노(SiO2-Ag-nano)(6)를 구비시킨다.It removes harmful heavy metals and foreign substances from tourmaline ore that emits anions and far infrared rays, and is supported on silica (SiO 2 ) (1) to make many pores (3), reduce specific gravity and emit large amount of anion far infrared rays. Silica tourmaline (SiO 2 -Tourmaline) (4) and silver (Ag) (5) having high antimicrobial activity is applied to silica (SiO 2 ) (1) as shown in FIG. Silver nano (SiO 2 -Ag-nano) 6 is provided.

한편 도 3과 같이 하단에 물배출구(11)를 구성시킨 물탱크(7)를 만들고 0.25mm의 많은 구멍을 구성시킨 철망 원통(8)을 만들어 원통안에 설치시키고 그 안쪽에 임페라(9)를 설치시키고 모타(10)에 연결시켜 회전시키도록 구성시킨 기능 물질 수액 제조기(13)를 도 3과 같이 구성시킨 다음 기능 물질 분말(16)을 철망 원통(8)에 담고 물탱크(7)에 약간의 접착력이 있는 수액을 담은 다음 임페라(9)를 회전시키면 0.25mm 이하의 기능 물질 분말 입자만이 수액과 혼합되어 기능 물질 수액(12)으로 만들어진다. 이렇게 만들어진 기능 물질 수액(12)을 분사기(14)로 종이표면에 도 5와 같이 분사시켜 기능 물질 분말 입자를 종이표면에 도포시켜 도 6과 같은 기능 종이로 구성시키고 그 위에 도 7과 같은 공정으로 PE 피막(20)을 도포시키고 냉각로라(21)에 통과시켜 도 8과 같은 구성의 코팅기능종이(19)로 구성시킨다.Meanwhile, as shown in FIG. 3, a water tank 7 having a water outlet 11 is formed at the bottom, and a wire mesh cylinder 8 having a large number of holes of 0.25 mm is formed and installed in the cylinder, and an impeller 9 is installed therein. And the functional material sap maker 13 configured to be rotated by being connected to the motor 10 is configured as shown in FIG. 3, and then the functional material powder 16 is placed in the wire mesh cylinder 8, and the water tank 7 is slightly After containing the adhesive sap and rotating the impeller 9, only 0.25 mm or less of the functional material powder particles are mixed with the sap to make the functional material sap 12. The functional material sap 12 thus made is sprayed on the paper surface with the injector 14 as shown in FIG. 5 to apply the functional material powder particles to the paper surface, and then composed of the functional paper as shown in FIG. PE film 20 is applied and passed through the cooling roller 21 to form a coating functional paper 19 of the configuration as shown in FIG.

도 1 - 실리카 토르마린(SiO2-Tourmaline) 구성도.1-Silica tourmaline (SiO 2- Tourmaline) configuration diagram.

도 2 - 실리카 은나노(SiO2-Ag-nano) 구성도Figure 2-Silica silver nano (SiO 2 -Ag-nano) configuration diagram

도 3 - 기능 물질 수액 제조기 구성도3-Functional substance sap maker configuration diagram

도 4 - 분사기 도Figure 4-Injector Diagram

도 5 - 기능 물질 수액 분사도5-Functional material sap injection diagram

도 6 - 기능종이 단면도Figure 6-Cross section of functional paper

도 7 - 코팅기능종이 제조 공정도7-Coating function paper manufacturing process diagram

도 8 - 코팅기능종이 구성도8-Coated Functional Paper Structure

도 9 - 항균시험 성적서Figure 9-Antimicrobial Test Report

도 9-1 - 항균시험사진(1, 2)Figure 9-1-Antimicrobial test pictures (1, 2)

도 9-2 - 항균시험사진(3, 4)Figure 9-2-Antimicrobial test pictures (3, 4)

도 10 - 원적외선 시험 성적서Figure 10-Far Infrared Test Report

도 10-1,2 원적외선 방출 그래프10-1,2 Far Infrared Emission Graph

도 11 - 음이온 시험 성적서11-Anion test report

( 도면의 주요 부분에 대한 부호 설명 )(Symbol description of main part of drawing)

1. 실리카(SiO2)Silica (SiO 2 )

2. 토르마린(Tourmaline)2. Tourmaline

3. 기공3. Pore

4. 실리카 토르마린(SiO2-Tourmaline)4. Silica tourmaline (SiO 2 -Tourmaline)

5. 은(Ag)5. Silver (Ag)

6. 실리카 은나노(SiO2-Ag-nano)6. Silica silver nano (SiO 2 -Ag-nano)

7. 물탱크7. Water tank

8. 철망원통8. Wire mesh

9. 임페라9. Impera

10. 모타10. Motor

11. 물배출구11. Water outlet

12. 기능 물질 수액12. Sap of functional substance

13. 기능 물질 수액 제조기13. Functional substance sap maker

14. 분사기14. Sandblast

15. 로즐15. Lodz

16. 기능 물질 분말16. Functional substance powder

17. 배관17. Piping

18. 종이18. Paper

19. 코팅기능종이19. Coating function paper

20. PE 피막20. PE film

21. 냉각로라21. Cooling roller

Claims (2)

코팅종이 제조방법에 있어서In the coated paper manufacturing method 종이 표면에 나타내고자 하는 기능물질(실리카 토르마린, 실리카 은나노) 분말을 구비하고 물을 담을 물탱크(7)를 만들어 하단 측면에 물배출구(11)를 구성시키며 물탱크(7) 안쪽 아래쪽에 0.25mm의 구멍을 다수 구성시킨 철망 원통(8)을 구성시키고 철망 원통 안쪽에 임페라(9)를 설치시켜 기능물질 수액 제조기(13)를 구성시킨 다음 철망 원통(8) 안쪽에 기능물질 분말(실리카 토르마린 실리카 은나노)를 내장시키고 물탱크에 물을 담고 임페라(9)를 회전시켜 철망 원통(8) 안쪽에 있는 0.25mm 이하의 기능물질 분말(16)만이 철망 구멍을 통해 빠저나와 물과 혼합되어 기능물질 수액(12)이 만들어 지며 기능물질 수액(12)을 물탱크 하단 측면에 구성시킨 물배출구(11)를 통해 분사기(14) 쪽으로 배출시켜 분사기를 통해 종이 표면에 분사시켜 기능물질 분말(16)이 종이 표면에 도포되고 종이에 도포된 기능물질 분말(16) 이탈을 막기위해 종이위에 도포된 기능물질 분말 위에 통상적인 PE 코팅방법으로 PE 피막을 접합시킴을 특징으로 하는 코팅기능종이 제조방법.A water tank (7) containing water (silica tourmaline, silica silver nano) powder to be displayed on the surface of the paper is formed, and a water outlet 11 is formed at the bottom side, and 0.25 mm in the bottom of the water tank (7). A wire mesh cylinder (8) consisting of a large number of holes is formed, and an impeller (9) is installed inside the wire mesh cylinder to configure a functional fluid sap maker (13), and then a functional material powder (silica tourmaline silica inside the wire mesh cylinder (8). Silver nano), containing water in the water tank, and rotating the impeller (9), only the functional material powder (16) of 0.25 mm or less inside the wire mesh cylinder (8) is mixed with water through the wire mesh hole and mixed with water (12) is made and the functional material sap 12 is discharged toward the injector 14 through the water outlet 11 formed on the bottom side of the water tank and sprayed on the surface of the paper through the injector to the functional material powder (16) paper table Applied and the functional material powder 16 is coated with functional paper production method characterized by Sikkim bonded to PE film in a conventional PE-coating on the functional material powder is applied onto a piece of paper to prevent the release coating to the paper. 청구항 1에 있어서The method according to claim 1 기능물질(실리카 토르마린, 실리카 은나노) 분말을 종이 표면에 접합시키고 PE 피막을 접합시켜 종이 표면에서 기능물질 분말의 이탈을 방지시켜 기능성이 감소되거나 소멸됨이 없이 음이온 원적외선이 방출되고 항균 살균력이 발생되는 복합적 기능 효과를 갖게함을 특징으로 하는 코팅기능종이 제조방법.Combined functional material (silica tourmaline, silica silver nano) powder to paper surface and PE film is bonded to prevent separation of functional material powder from paper surface. Method of producing a coated functional paper, characterized in that it has a functional effect.
KR1020070117629A 2007-11-19 2007-11-19 Method of manufacturing coated functional paper KR100942387B1 (en)