KR100912006B1 - A method for manufacturing artificial sarira using bone - Google Patents
A method for manufacturing artificial sarira using bone Download PDFInfo
- Publication number
- KR100912006B1 KR100912006B1 KR20070102593A KR20070102593A KR100912006B1 KR 100912006 B1 KR100912006 B1 KR 100912006B1 KR 20070102593 A KR20070102593 A KR 20070102593A KR 20070102593 A KR20070102593 A KR 20070102593A KR 100912006 B1 KR100912006 B1 KR 100912006B1
- Authority
- KR
- South Korea
- Prior art keywords
- artificial
- sari
- raw material
- saree
- kiln
- Prior art date
Abstract
이 발명에 따른 인골을 이용한 인조 사리 제조방법의 해결 수단은, 인조 사리의 제조원료로서 망자의 인골가루 70%, 일라이트 3%, 맥반석 5%, 장석 2%, 고령토 20%의 부피비율로 이루어지는 혼합물을 만드는 단계(S10); 위에서 만들어진 인조 사리 제조 원료인 혼합물을 물과 90:10 내지 80:20의 부피비율로 섞어서 반죽한 뒤 원하는 모양을 만드는 단계(S20); 위에서 원하는 모양으로 만들어진 인조 사리 제조 원료를 전기로 밖에 위치한 전기곤로의 열판 위에서 수분을 제거하기 위해 100℃의 온도로 20분 동안 건조시키는 단계(S30); 위에서 건조된 제조원료를 전기가마에서 1200℃로 2시간 동안 굽는 단계(S40); 및 전기가마 온도를 800℃로 내린 뒤 가마문을 열고 사리로 완성된 제조원료를 꺼내는 단계(S50)를 구비하여 이루어지고, 위의 S20 단계에서 모양이 만들어진 인조 사리에 생기는 흉터를 최소화하기 위해 위 건조 단계(S30) 및 굽는 단계(S40)에서 인조 사리가 열판 위에 형성된 다수의 지지용 침 위에 올려진 뒤 건조되고 구워지며, 위에서 만들어지는 인조 사리의 색은 돌가루 안료를 사용하여 조절되는 것을 특징으로 한다.Means for solving the artificial sari manufacturing method using the human bone according to the invention, the raw material of artificial sari made of the volume ratio of 70% of the human bone ash of the dead, illite 3%, ganban stone 5%, feldspar 2%, kaolin 20% Making a mixture (S10); Mixing the mixture, which is a raw material for preparing artificial sari, prepared at a volume ratio of 90:10 to 80:20, and kneading to form a desired shape (S20); Drying the artificial sari manufacturing raw material made in the desired shape above for 20 minutes at a temperature of 100 ℃ to remove moisture on the hot plate of the electric furnace located outside the electric furnace (S30); Baking the dried raw material for 2 hours at 1200 ℃ in an electric kiln (S40); And lowering the electric kiln temperature to 800 ° C. and opening the kiln door and taking out the finished raw material into the saree (S50), and in order to minimize the scars on the artificial saree shaped in step S20 above. In the drying step (S30) and the baking step (S40), the artificial sari is placed on a plurality of supporting needles formed on the hot plate, dried and baked, and the color of the artificial sari made from the above is controlled by using a stone powder pigment. It is done.
이 발명에 따르면 유족이 화장장에서 사리제조를 의뢰하면 약 3시간 30분 정도의 시간 이내에 유족에게 고인의 인골이 주원료가 되는 인조 사리를 건내 줄 수 있다. 그리고 인조 사리는 보석처럼 영롱하여 혐오감이 전혀 없이 장소에 구애받지 않고 제사, 추도식에도 모실 수 있고 그리운 가신님과의 친견이 자유로우며, 유가족들에게 생기던 조상님들의 분골을 잘 못 모심으로 인한 근심걱정, 병고, 송사 등을 말끔히 덜어 주는 효과가 있다. 아울러 이 발명을 이용하여 망자의 분골을 인골 흉상으로 만들어 사용할 수도 있고, 목걸이, 반지, 브로치 등으로도 만들어 늘 몸에 지니고 다닐 수도 있다.According to the present invention, when a surviving family requests a saree production in a crematory, the surviving family can be handed out to the surviving family in which the deceased bones are the main raw materials. And the artificial sari is jeweled like a jewel and can be held at sacrifices and mourning ceremony without any disgust at all. Free friendship with the nostalgic trail, and anxiety due to mishandling of the ancestors of the ancestors. Efficacy in relieving illnesses, deaths, etc. In addition, by using the present invention, the bones of the dead can be used as a human skeleton, or they can be always carried with a necklace, ring, brooch, etc.
인조 사리, 분골, 도기파(일라이트), 맥반석, 장석, 고령토. Artificial fern, bone, porcelain (light), elvan, feldspar, kaolin.
Description
이 발명은 인골을 이용하여 인조 사리를 제조하는 방법에 대한 것이다. 특히 이 발명은 화장장에서 파쇄된 인골을 이동성을 갖춘 차량에 설치된 사리 제조장치를 이용하여 화장장 또는 화장장 인근에서 짧은 시간안에 사리 제조장치에 준비된 소정(所定)의 재료들과 혼합하여 제조하는 기술에 관한 것이다.The present invention relates to a method of manufacturing artificial sari using human bone. In particular, the present invention relates to a technique for producing a mixture of predetermined materials prepared in a saree manufacturing apparatus in a short time in the vicinity of the crematorium or crematorium using a saree manufacturing apparatus installed in a mobile vehicle having a fractured bone in the crematorium will be.
오늘날 지구상에는 적게 잡아도 60억이 넘는 인구가 살고 있다. 그리고 매일 수많은 아기들이 태어나고 동시에 수많은 사람들이 여러가지 원인으로 죽는다. 의료기술의 발달로 인류의 수명이 늘어난 것은 사실이지만 그럼에도 불구하고 인류가 영원히 살 수는 없는 것이 사실이어서 안타깝지만 사망하는 사람들의 수도 꾸준히 늘고 있다.Today, there are over 6 billion people living on the planet. And every day a lot of babies are born and at the same time many people die from various causes. It is true that the life span of human beings is increased by the development of medical technology, but it is unfortunate that human beings cannot live forever, but the number of people who die is increasing steadily.
하지만 이처럼 늘어나는 사망자들을 옛날 풍습에 따라 매장한다는 것은 현실적으로 불가능하게 되었다. 그것은 매장할 수 있는 장지의 확보가 불가능하기 때문 이다. 그래서 무덤 대신 납골당을 이용하는 추세이긴 하나 이것도 혐오시설로 인식되어 각 지자체에서 납골당용 부지 확보에 어려움을 겪고 있다. However, it was practically impossible to bury these growing deaths according to old customs. This is because it is impossible to secure a burial place. Therefore, the tendency to use the ossuary instead of the tomb is recognized as a loathing facility, and local governments are having difficulty securing sites for the ossuary.
뿐만 아니라 화장을 하고 나서 유골을 파쇄하여 납골함에 봉안한 뒤 납골당에 이를 모시더라도 납골당 등에서의 결로 현상으로 인한 악취, 해충 발생 및 분골의 변질, 이민이나 이사로 인해 분골을 옮겨야 하는 경우 유족들은 적지않은 곤란함을 겪고 있다. 심지어는 가장 공경해야할 조상님들과 망자 때문에 본의 아니게 스트레스를 받게 되는 일이 점차 증가하고 있다. 따라서 분골을 보석처럼 영구적으로 가까이에서 모실 수 있는 해결방법이 마련되어야 할 필요성이 크게 대두 되고 있다.In addition, even after the cremation, the ashes are broken and sealed in the ossuary, and they are brought to the ossuary. I am having trouble. Even the unintentional stress of the ancestors and the deceased to be most respected is increasing. Therefore, there is a great need for a solution that can be used to permanently close the bone like a gem.
위에서 언급한 바와 같이 매년 증가 일로에 있는 사망자의 분골을 위생적일 뿐만 아니라 제 3자에게 혐오감을 주지 않고 후손들이 늘 가까이에서 모실 수 있는 인조 사리로 만들어 보관할 수 있는 방법을 제공하는 것을 이 발명의 목적으로 한다.As mentioned above, it is an object of the present invention to provide a method in which the bones of the deceased who are increasing year after year are not only sanitary but also made into artificial ferns that can be kept close by by their offspring without disgusting them. It is done.
이 발명에 따른 인골을 이용한 인조 사리 제조방법의 해결 수단은,
인조 사리의 제조원료로서 망자의 인골가루 70%, 일라이트 3%, 맥반석 5%, 장석 2%, 고령토 20%의 부피비율로 이루어지는 혼합물을 만드는 단계(S10);
위에서 만들어진 인조 사리 제조 원료인 혼합물을 물과 90:10 내지 80:20의 부피비율로 섞어서 반죽한 뒤 원하는 모양을 만드는 단계(S20);
위에서 원하는 모양으로 만들어진 인조 사리 제조 원료를 전기로 밖에 위치한 전기곤로의 열판 위에서 수분을 제거하기 위해 100℃의 온도로 20분 동안 건조시키는 단계(S30);
위에서 건조된 제조원료를 전기가마에서 1200℃로 2시간 동안 굽는 단계(S40); 및
전기가마 온도를 800℃로 내린 뒤 가마문을 열고 사리로 완성된 제조원료를 꺼내는 단계(S50)를 구비하여 이루어지고,
위의 S20 단계에서 모양이 만들어진 인조 사리에 생기는 흉터를 최소화하기 위해 위 건조 단계(S30) 및 굽는 단계(S40)에서 인조 사리가 열판 위에 형성된 다수의 지지용 침 위에 올려진 뒤 건조되고 구워지며,
위에서 만들어지는 인조 사리의 색은 돌가루 안료를 사용하여 조절되는 것을 특징으로 한다.Means for solving the artificial sari manufacturing method using the bone according to the present invention,
Step (S10) to prepare a mixture consisting of the volume ratio of the artificial bones 70%, elite 3%, ganban stone 5%, feldspar 2%, kaolin 20% as the raw material of artificial sari (S10);
Mixing the mixture, which is a raw material for preparing artificial sari, prepared at a volume ratio of 90:10 to 80:20, and kneading to form a desired shape (S20);
Drying the artificial sari manufacturing raw material made in the desired shape above for 20 minutes at a temperature of 100 ℃ to remove moisture on the hot plate of the electric furnace located outside the electric furnace (S30);
Baking the dried raw material for 2 hours at 1200 ℃ in an electric kiln (S40); And
Lowering the electric kiln temperature to 800 ℃ and open the kiln door and take out the finished raw material of the saree (S50) is made,
In order to minimize the scar on the artificial sari formed in the step S20 above, the artificial sari is dried and baked after being placed on a plurality of supporting needles formed on the hot plate in the above drying step (S30) and the baking step (S40),
The color of the artificial fern produced from the above is characterized by using a stone powder pigment.
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
이 발명을 이용하여 만들어진 인조 사리는 보석처럼 영롱하여 혐오감이 전혀 없이 옛날 조상님들이 가정에 신주단지 모셨듯이 장소에 구애받지 않고 제사, 추도식에도 모실 수 있고 그리운 가신님과의 친견이 자유롭다. 그리고 유가족들에게 생긴 조상님들의 분골을 잘 못 모심으로 인한 근심걱정, 병고, 송사 등을 말끔히 덜어 주는 효과가 있다.The artificial sari made by using this invention is jeweled like a jewel, so there is no disgust at all. It can be held at sacrifices and mourning ceremonies, as if the ancient ancestors had a sacred complex in their homes. And it is effective to relieve anxiety, sickness, death, etc. caused by mishandling the bones of ancestors caused by bereaved families.
이 발명을 이용하여 망자의 분골을 인골 흉상으로 만들어 사용할 수도 있고, 목걸이, 반지, 브로치 등으로도 만들어 늘 몸에 지니고 다닐 수도 있다.By using this invention, the bones of the dead can be made into a human bust, or they can be made into necklaces, rings, broaches, etc.
이 발명에 따른 인골을 이용한 인조 사리 제조방법의 실시를 위한 구체적인 내용을 첨부된 도면을 참조하여 설명하면 다음과 같다. 도 1은 이 발명에 따른 인조 사리 제조방법의 바람직한 일 실시예의 흐름도를 나타낸다. 그리고 도 2는 도 1의 방법에 따라 만들어진 인조 사리의 모습을 보여준다.Referring to the accompanying drawings, the specific content for the implementation of the artificial sari manufacturing method using the bone according to the invention as follows. Figure 1 shows a flow chart of a preferred embodiment of the artificial sari manufacturing method according to the present invention. And Figure 2 shows the appearance of the artificial sari made according to the method of FIG.
먼저 인조 사리의 제조원료로서 망자의 분골 70%, 도기파(일라이트라고도 함. 일종의 돌가루임.) 3%, 맥반석 5%, 장석 2%, 고령토 20%의 부피비율로 이루어지는 혼합물을 만든다(S10). 도기파는 점력을 향상시키는 매개물질이며 균열을 방지하는 광물질이다. 인조 사리의 제조 공정에서 도기파를 사용함으로써 인조 사리의 제조시간을 획기적으로 줄일 수 있다. 그 이유에 대해서는 뒤에서 다시 설명한다.First, as a raw material of artificial sari, a mixture consisting of 70% of dead man's bone, pottery (also called illite, a kind of stone powder), 3% of elvanite, 5% of feldspar, 2% of kaolin and 20% of kaolin is made. S10). Pottery waves are mediators that enhance viscosity and minerals that prevent cracking. The use of ceramic waves in the manufacturing process of artificial sari can drastically reduce the manufacturing time of artificial sari. The reason for this will be described later.
위에서 만들어진 인조 사리 제조 원료 혼합물과 물을 90:10 내지 80:20의 부 피비율로 섞어서 반죽한 뒤 원하는 모양을 만든다(S20). 이때 원하는 모양을 만들 때 일반 사리, 목걸이, 반지, 브로치, 흉상 등의 모양을 만드는 것이 바람직하다. 도 3은 도 1의 방법에서 여러가지 모양으로 만들어진 인조사리 반죽을 뾰족한 침 모양의 열판 위에 올려놓은 모습을 보여주고 있다. 이렇게 뾰족한 침 모양으로 된 열판 위에 사리 반죽을 얹는 이유는 인조 사리가 완성되었을 때 사리와 열판 사이의 접촉면에 생기는 흉터를 최소화 하기 위해서이다. The artificial sari manufacturing raw material mixture and water prepared above are mixed at a volume ratio of 90:10 to 80:20, kneaded to form a desired shape (S20). At this time, it is desirable to make a general sari, a necklace, a ring, a brooch, a bust or the like when creating a desired shape. FIG. 3 shows a state in which the phosphorus dough made of various shapes in the method of FIG. 1 is placed on a pointed needle-shaped hot plate. The reason for placing saree dough on the pointed needle-shaped hotplate is to minimize the scar on the contact surface between the saree and the hotplate when the artificial saree is completed.
그리고 위에서 구워진 제조원료를 전기로 밖에 위치한 전기곤로의 열판 위에서 수분을 제거하기 위해 100℃의 온도에서 20분 동안 건조시킨다(S30). And the raw material baked above is dried for 20 minutes at a temperature of 100 ℃ to remove moisture on the hot plate of the electric stove located outside the electric furnace (S30).
건조된 제조원료를 전기가마에서 1200℃로 2시간 동안 굽는다계(S40).The dried raw material is baked in an electric kiln at 1200 ° C. for 2 hours (S40).
전기가마의 온도를 800℃로 내린 뒤 가마문을 열고 완성된 사리를 꺼낸다(S50). 일반적으로 도자기 제조 공정에서는 도자기를 가마에서 꺼낼 때 가마의 온도를 100℃로 낮춘 상태에서 꺼내야 한다. 그렇지 않고 높은 온도에서 꺼낼 경우에는 도자기가 다 터지게 된다. 300℃에서도 도자기는 가마문을 열지 못한다. 그래서 도자기를 굽는 과정은 매우 오랜 시간이 소요된다. 하지만 이 발명에서는 약 3시간 반 이내의 시간이면 인조 사리를 제조가 가능하다. 그것은 가마를 완전히 냉각시키지 않고 800℃에서도 가마문을 열고 사리를 꺼낼 수 있기 때문이다. 이 발명에 의하면 이러한 고온에서 가마문을 열어도 사리가 터지지 않는다. 그러한 이유는 인조사리의 성분 가운데 포함되어 있는 도기파 때문이다. 도기파는 점력을 향상시키는 성질이 있을 뿐만 아니라 균열을 방지하는 효과도 뛰어나기 때문이다. After lowering the temperature of the electric kiln to 800 ℃ open the kiln door and take out the finished saree (S50). In general, in the pottery manufacturing process, when the pottery is taken out of the kiln, the temperature of the kiln should be lowered to 100 ° C. Otherwise, when taken out at high temperatures, the ceramic will break. Even at 300 ℃, pottery can't open kiln. So the process of baking pottery takes a very long time. However, in this invention, it is possible to manufacture artificial sari within a time of about three and a half hours. This is because the kiln door can be opened and the saree can be taken out even at 800 ° C without completely cooling the kiln. According to the present invention, even when the kiln door is opened at such a high temperature, the sari does not burst. The reason for this is due to the presence of porcelain in the composition of the phosphorus. This is because the ceramic wave not only improves the viscosity, but also prevents cracking.
그리고 이 실시예에 있어서, 위 인조 사리용 제조 원료 모양은 사리에 생기는 흉터를 최소화 하기 위해 열판 위에 형성된 다수의 지지용 침 위에 올려진 뒤 구워지는 것이 바람직하다.And in this embodiment, the shape of the manufacturing raw material for the artificial yarn is preferably baked after being placed on a plurality of support needles formed on the hot plate to minimize scarring in the saree.
또한 위 인조 사리 제조용 장치들은 이동이 가능한 차량에 설치되며, 이 차량을 화장장 인근에 주차한 뒤 유족의 의뢰가 있으면 바로 현장에서 화장장에서 화장후 파쇄한 고인의 분골과 차량에 미리 준비되어 있는 도기파, 맥반석, 장석, 고령토를 이용하여 인조 사리를 제조하는 것이 바람직하다.In addition, the devices for manufacturing artificial sari are installed in a mobile vehicle, and when the vehicle is parked near the crematorium, the bead of the deceased who has been crushed after cremation at the crematorium at the scene and the porcelain are prepared in advance. It is preferable to prepare artificial fern using elvan, feldspar and kaolin.
그리고 위 혼합물을 만들기 위해 인골과 다른 재료를 섞을 때 시신에 쇠가 닿으면 안된다는 풍습을 고려하여 교반장치 가운데 혼합물과 직접 닿는 부분에 쇠를 사용하지 않는 것이 바람직하다.In addition, it is desirable to avoid the use of iron in the direct contact with the mixture in the stirrer, taking into account the custom that iron should not touch the body when mixing bone and other materials to make the above mixture.
그리고 위에서 만들어지는 인조 사리는 돌가루 안료를 사용하여 사리의 색을 조절할 수 있다.And artificial sari made from above can adjust color of sari using stone powder pigment.
그리고 위에서 만들어진 사리를 유골함에 넣은 뒤 납골당, 사당, 수목장, 성당, 교회, 절 또는 유가족이 원하는 곳에 안치하거나, 인조 사리를 목걸이, 귀걸이, 반지 등의 장신구 형태로 만들어 유족이 평소 몸에 지니고 다니도록 하는 것이 바람직하다.Place the sari made above in the ashes and place it in the ossuary, shrine, ranch, cathedral, church, temple, or where your bereaved family wants, or make the artificial sari in the form of necklaces, earrings, rings, etc. It is desirable to.
이 발명에 의해 만들어진 인조 사리를 납골당, 수목장, 사리탑, 사찰, 성당, 교회, 자택, 정원 등에 안치할 수 있다. 무엇보다 분골을 보석처럼 영구적으로 가 까이서 모실 수 있어서 이의 산업상 이용 가능성은 매우 높다고 할 수 있다.The artificial sari made by this invention can be enclosed in a ossuary, a grove, a stupa, a temple, a cathedral, a church, a house, a garden, and the like. Above all, the bones can be taken permanently close to each other like jewels, so its industrial application is very high.
도 1은 이 발명에 따른 인골을 이용한 인조 사리 제조방법을 나타내는 흐름도.1 is a flow chart showing a method of manufacturing artificial yarn using the bone according to the present invention.
도 2는 이 발명에 따른 인골을 이용한 인조 사리 제조방법에 의해 만들어진 인조 사리의 실시예 사진.Figure 2 is an embodiment photograph of the artificial sari made by the artificial sari manufacturing method using the bone according to the present invention.
도 3은 도 1의 방법에서 여러가지 모양으로 만들어진 인조사리 반죽을 뾰족한 침모양의 열판 위에 올려놓은 모습을 보여주는 사진.Figure 3 is a photograph showing the appearance on the pointed needle-shaped hot plate dough made of various shapes in the method of Figure 1;
Claims (6)