KR100848575B1 - Joint filler tape and waterproof layer protection member manufacturing method - Google Patents

Joint filler tape and waterproof layer protection member manufacturing method Download PDF

Info

Publication number
KR100848575B1
KR100848575B1 KR1020070107607A KR20070107607A KR100848575B1 KR 100848575 B1 KR100848575 B1 KR 100848575B1 KR 1020070107607 A KR1020070107607 A KR 1020070107607A KR 20070107607 A KR20070107607 A KR 20070107607A KR 100848575 B1 KR100848575 B1 KR 100848575B1
Authority
KR
South Korea
Prior art keywords
tape
resin foam
waterproof layer
manufacturing
adhesives
Prior art date
Application number
KR1020070107607A
Other languages
Korean (ko)
Inventor
김재민
장억수
Original Assignee
김재민
장억수
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김재민, 장억수 filed Critical 김재민
Priority to KR1020070107607A priority Critical patent/KR100848575B1/en
Application granted granted Critical
Publication of KR100848575B1 publication Critical patent/KR100848575B1/en

Abstract

A manufacturing method of a windproof tape and a waterproof layer protection material is provided to reduce the cost of materials required for construction and to make post management easy and convenient by manufacturing a windproof tape and a waterproof layer protection material having strong adhesive property, not causing inferiority caused by adhesives of resin foam attached partially to a protection sheet when stripping off a protection sheet from resin foam for using a windproof tape and a waterproof layer protection material. A manufacturing method of a windproof tape and a waterproof layer protection material for manufacturing a windproof tape for increasing the function of interlayer noise and vibration absorption as well as thermal insulation of an apartment house, and separating a protection sheet and attaching resin foam to a wall by adhesive property of adhesives to construct floor concrete evenly or a waterproof layer protection material for cutting off moisture permeated from the bottom comprises the steps of: manufacturing adhesives at 250°C in an industrial mixer capable of mixing materials of adhesives for manufacturing a windproof tape and a waterproof layer protection material, and heating and melting, and then keeping at the fixed temperature; cooling down the adhesives supplied from the industrial mixer to a liquid receiver at 70~80°C; applying the adhesives cooled in the liquid receiver directly to a resin foam; and coupling the resin foam applied with the adhesives with a protection sheet.

Description

방통 테이프 및 방수층 보호재 제조방법{Joint filler tape and waterproof layer protection member manufacturing method}Joint filler tape and waterproof layer protection member manufacturing method

본 발명은 방통 테이프 및 방수층 보호재 제조방법에 관한 것으로서, 더욱 상세하게는 아파트 등과 같은 공동 주택 등의 층간 소음과 진동 흡수 및 단열 기능을 강화함과 아울러 바닥 콘크리트를 균일한 상태로 시공하기 위해 제작된 방통 테이프나, 바닥면으로부터 올라오는 습기를 차단시키기 위해 시공되는 방수층 보호재를 사용하기 위해 발포 수지폼으로부터 보호 쉬트를 분리하기 위해 벗겨낼 때 발포 수지폼에 도포된 점착제가 보호 쉬트에 일부 달라붙어서 사용할 수 없는 불량이 발생되는 현상을 완벽하게 방지할 수 있음은 물론, 강력한 점착력을 갖는 방통 테이프 및 방수층 보호재를 제조할 수 있도록 한 것이다.The present invention relates to a method for manufacturing a barrier tape and a waterproof layer protective material, and more specifically, a barrier that is manufactured to uniformly install floor concrete while reinforcing the noise and vibration absorption and insulation function between floors, such as apartment houses. When peeled off to separate the protective sheet from the foamed foam to use a tape or a waterproofing layer protective material to block moisture from the floor, the adhesive applied to the foamed foam may stick to the protective sheet. It is possible to completely prevent the phenomenon that no defect occurs, as well as to produce a waterproof tape and a waterproof layer protective material having a strong adhesive force.

일반적으로, 복층으로 시공되는 아파트나 다세대 주택 등과 같은 형태의 공동 주택은 점차 사람들의 가치관이 다양해지고 의식 수준이 향상됨에 따라 물질적인 측면뿐만 아니라, 정신적인 측면도 고려하여 시공되고 있는 데, 특히 이러한 공 동 주택은 한정된 두께의 벽과 바닥을 인접 세대와 공유해야 하는 특성상 윗집 아이들의 뛰노는 소리, 피아노 소리 등과 같은 상하층간의 바닥 충격음은 피할 수 없으며, 이로 인한 위축된 생활과 이웃 세대와의 분쟁 등은 실제로 공동 주택에서 가장 많은 민원이 제기되는 심각한 사회 문제화되고 있는 실정이다.In general, multi-family apartments, such as apartments and multi-family houses, are being constructed in consideration of not only the material aspects but also the mental aspects as people's values are gradually diversified and the level of consciousness is improved. As the house has to share a limited thickness of walls and floors with neighboring generations, floor impact noises such as children's playing and piano sounds of upper-class children cannot be avoided. This is actually a serious social problem, with most complaints in multi-family housing.

상기와 같은 바닥 충격음 즉, 층간 전달소음을 최소화하기 위해 현재 국내에서 보편적으로 사용하는 시공 방법은 콘크리트 바닥 슬래브 위에 충격음 저감 및 완충을 목적으로 완충 부재를 설치하고, 이 완충 부재의 상부에 기포 콘크리트와 시멘트 몰탈을 시공함으로써 콘크리트 바닥 슬래브로부터 기포 콘크리트와 시멘트 몰탈을 분리시키는 뜬바닥 공법이 사용되고 있다.The construction method currently commonly used in Korea to minimize the floor impact noise, that is, interlayer transfer noise, is installed on the concrete floor slab for the purpose of reducing the impact sound and cushioning, and the foam concrete and Floating bottom method is used to separate bubble concrete and cement mortar from concrete floor slab by constructing cement mortar.

하지만, 이는 바닥면을 통한 충격 및 소음 진동을 해소하기 위한 공법일 뿐이며, 벽체를 통한 층간 소음을 해소하기 위해서는 완충 부재의 상부로 타설되는 기포 콘크리트 및 시멘트 몰탈층과 그들과 맞닿는 벽체 사이에 차음 및 흡수성을 갖는 방통 테이프(Joint fillar tape)를 부착하여 이를 통해 벽체를 타고 하부층으로 전달되는 충격 및 소음 진동을 해소하고 있다.However, this is only a method for solving the impact and noise vibration through the floor surface, and in order to eliminate the interlayer noise through the wall, the sound insulation and the wall between the foam concrete and cement mortar layer which is placed on top of the cushioning member and the wall in contact with them Joint fillar tape with absorbency is attached to remove shocks and noise vibrations transmitted to the lower layer through the wall.

즉, 상기와 같은 뜬바닥 공법은 도 1 및 도 2에 도시한 바와 같이, 바닥층에 가해지는 충격 에너지가 직접적으로 구조체인 콘크리트 바닥 슬래브(1)와 벽체(2)에 전달되지 않도록 하기 위해 상기 콘크리트 바닥 슬래브(1) 상부에 완충 부재(3)를 깔고, 이 완충 부재(3) 상의 벽체(2)를 따라 방통 테이프(10)를 부착시킨 후, 상기 완충 부재(3)의 상부에 순차적으로 온돌층 역할을 하는 기포 콘크리트층(4)과 마감재 역할을 하는 시멘트 몰탈층(5)을 타설하거나, 다른 방식으로 상기 콘크리트 바닥 슬래브(1)의 상부에 완충 부재(3)와 기포 콘크리트층(4)을 시공한 다음, 이 기포 콘크리트층(4) 상부의 벽체(2)를 따라 방통 테이프(10)를 부착시킨 후, 상기 기포 콘크리트층(4)의 상부에 시멘트 몰탈층(5)을 타설하는 방식이다.That is, the floating floor method as described above, as shown in Figures 1 and 2, in order to prevent the impact energy applied to the floor layer is directly transmitted to the concrete floor slab 1 and the wall (2), which is a structure. The cushioning member 3 is laid on the bottom slab 1, and the barrier tape 10 is attached along the wall 2 on the cushioning member 3, and then the ondol is sequentially on top of the cushioning member 3. A foamed concrete layer 4 serving as a layer and a cement mortar layer 5 serving as a finishing material are cast, or alternatively, the cushioning member 3 and the foamed concrete layer 4 on top of the concrete floor slab 1. After the construction, after attaching the barrier tape 10 along the wall (2) above the foamed concrete layer (4), the method of pouring cement mortar layer (5) on top of the foamed concrete layer (4) to be.

그리고, 도 3은 일반적인 방수층 보호재(100)를 나타낸 사시도로서, 적어도 하나 이상 다중 결합된 발포 수지폼(12)의 일단면에는 점착제(14)에 의해 이형지인 보호 쉬트(16)가 부착되고, 상기 발포 수지폼(12)의 타단면에는 우븐 크로스(woven cross) 등과 같은 조밀한 원단인 직물지(18)가 부착된 구조로서, 상기한 방통 테이프(10)와 동일하게 시공시 발포 수지폼(12)으로부터 보호 쉬트(16)를 벗긴 상태로 사용한다.And, Figure 3 is a perspective view of a general waterproof layer protective material 100, at least one end surface of the at least one multi-bonded foamed resin foam 12 is attached to the protective sheet 16, which is a release paper by the adhesive 14, the The other end surface of the foamed resin foam 12 is a structure in which a woven paper 18, which is a dense fabric such as a woven cross, is attached to the foamed resin foam 12. It is used in a state where the protective sheet 16 is peeled off.

한편, 종래의 방통 테이프(10) 및 방수층 보호재(100)를 제조할 때에는 먼저, 롤 형상의 이형지인 보호 쉬트를 장치 일단 하부의 보호 쉬트 공급부에 셋팅시킨 후, 상기 보호 쉬트의 단부를 전방으로 밀어주면 보호 쉬트가 전진하면서 산업용 믹서로부터 공급되는 점착제가 담겨져 있는 액받이 내부의 상부 및 하부에 장착된 제 1,2 히팅 로울러는 상호 역방향으로 회전하면서 이 점착제 도포용 로울러가 상기 액받이 내의 점착제를 제 1 히팅 로울러에 묻혀줌과 동시에, 이 히팅 로울러의 표면에 보호 쉬트가 접촉하면서 상승함에 따라 보호 쉬트에 점착제가 도포된다.On the other hand, when manufacturing the conventional waterproof tape 10 and the waterproof layer protective material 100, first, the protective sheet, which is a roll-shaped release paper, is set in the protective sheet supply unit at the lower end of the device, and then the end of the protective sheet is pushed forward. The first and second heating rollers mounted on the upper and lower portions of the drip tray containing the pressure-sensitive adhesive supplied from the industrial mixer while the main surface protection sheet is advanced rotated in opposite directions, and the roller for applying the pressure-sensitive adhesive removes the pressure-sensitive adhesive in the drip tray. 1 It is buried in the heating roller, and an adhesive is applied to the protective sheet as the protective sheet rises in contact with the surface of the heating roller.

이와 동시에, 상기 점착제가 도포된 보호 쉬트가 상승하여 자연 건조를 하기 위해 장치 상부의 보호 쉬트 이송부에서 일정 시간에 걸쳐 이송하여 장치 타단 하부의 결합부에 도달함과 동시에, 발포 수지폼 공급부에서 공급되는 발포 수지폼이 전진하여 결합부에 도달하면서 상기 점착제가 도포된 보호 쉬트와 발포 수지폼이 동시에 결합부에 설치되어 회전하는 제 3 히팅 로울러를 통과하여 가압되면서 결합된 상태로 전진하여 권취부에서 롤 형태로 권취하는 공정을 반복함으로써 방통 테이프 및 방수층 보호재를 제조하게 된다.At the same time, the protective sheet coated with the adhesive is raised to be transported over a predetermined time in the protective sheet conveying portion of the upper portion of the apparatus for natural drying to reach the coupling portion of the lower end of the apparatus, and is supplied from the foamed resin foam supply portion. As the foamed resin foam moves forward to reach the joining portion, the protective sheet coated with the pressure-sensitive adhesive and the foamed resin foam are simultaneously installed in the joining portion and pressurized through the rotating third heating roller to move forward in the combined state and roll on the winding portion. By repeating the step of winding in the form, it is possible to produce a barrier tape and a waterproof layer protective material.

이때, 상기한 점착제를 보호 쉬트에 도포할 때 상기 액받이와 제 1,2 히팅 로울러는 전원이 공급된 히팅된 상태를 유지하게 되고, 또한 상기 산업용 믹서에서 250℃로 제조된 점착제는 상기 액받이에 공급되어 200℃의 상태를 유지하여 도포시키게 되는 데, 상기 제 1,2 히팅 로울러가 히팅된 상태를 유지하도록 하는 이유는 점착제의 온도가 낮을 경우 과도하게 보호 쉬트에 점착제가 도포되는 것을 방지하여 점착제의 사용량을 효율적으로 절감시키도록 하기 위함이다.At this time, when the adhesive is applied to the protective sheet, the drip tray and the first and second heating rollers are maintained in a heated state in which power is supplied, and the adhesive prepared at 250 ° C. in the industrial mixer is the drip tray. The first and second heating rollers are kept in a heated state to be applied to the coating sheet. The reason for maintaining the heated state of the first and second heating rollers is to prevent the adhesive from being applied to the protective sheet excessively. This is to effectively reduce the amount of the pressure-sensitive adhesive used.

또한, 상기 점착제가 도포된 보호 쉬트를 발포 수지폼과 곧바로 결합시키지 않고 자연 건조시키는 이유는 보호 쉬트에 점착제가 충분히 접착된 상태를 유지하도록 하기 위함이다.In addition, the reason why the pressure-sensitive adhesive is applied to the protective sheet is naturally dried without bonding the foam directly to the foamed foam is to maintain a state that the adhesive is sufficiently adhered to the protective sheet.

또한, 상기 점착제가 도포된 보호 쉬트와 발포 수지폼의 결합시 제 3 히팅 로울러를 점착제가 180℃를 유지하도록 하기 위해 히팅시키게 되는 데, 그 이유는 상기 보호 쉬트에 도포된 자연 건조된 점착제를 녹여 발포 수지폼에 점착제를 효율적으로 전사시킬 수 있도록 하기 위함이다.In addition, when the pressure-sensitive adhesive is applied to the protective sheet and the foamed foam foam is bonded to the third heating roller to maintain the pressure-sensitive adhesive 180 ℃, because the melted naturally dried pressure-sensitive adhesive applied to the protective sheet This is to allow the pressure-sensitive adhesive to be efficiently transferred onto the foamed resin foam.

그리고, 상기 보호 쉬트(16)에 고온의 점착제(14)를 도포하는 이유는 발포 수지폼(12)에 고온의 점착제를 도포할 경우 재질의 특성상 발포 수지폼이 고온을 견디지 못하고 녹아버리기 때문이다.The reason why the high temperature adhesive 14 is applied to the protective sheet 16 is that the foamed resin foam does not endure high temperature and melts when the high temperature adhesive is applied to the foamed resin foam 12.

그러나, 실제 시공 현장에서 방통 테이프(10)나 방수층 보호재(100)를 시공 하기 위해 발포 수지폼(12)으로부터 보호 쉬트(16)를 분리하기 위해 벗겨낼 때 보호 쉬트(16)에 도포된 점착제(14)가 발포 수지폼(12)에만 전사되어 있어야만 벽체(2) 등에 부착된 상태에서 결합력을 유지할 수 있으나, 종래의 방식으로 제작된 방통 테이프(10)나 방수층 보호재(100)는 보호 쉬트(16)와 점착제(14)의 점착력이 점착제(14)와 발포 수지폼(12)의 점착력보다 강하기 때문에 점착제(14)가 보호 쉬트(16)에 일부 달라붙어서 사용할 수 없는 치명적인 불량이 빈번하게 발생하기 때문에 방통 테이프(10) 및 방수층 보호재(100)의 시공시 자재 비용이 많이 소요되고, 방통 테이프(10) 및 방수층 보호재(100)의 빈번한 불량 발생에 따른 시공 시간이 많이 걸리게 되므로 인해 시공 생산성이 저하되는 등의 많은 문제점이 있었다.However, the adhesive applied to the protective sheet 16 when peeled off to separate the protective sheet 16 from the foamed resin foam 12 in order to construct the barrier tape 10 or the waterproofing layer protective material 100 at the actual construction site ( 14 must be transferred only to the foamed resin foam 12 to maintain the bonding force in the state attached to the wall 2, etc., but the barrier tape 10 or the waterproofing layer protective material 100 manufactured in a conventional manner is a protective sheet 16 Since the adhesive force of the adhesive and the adhesive 14 is stronger than that of the adhesive 14 and the foamed resin foam 12, a fatal defect that the adhesive 14 is stuck to the protective sheet 16 frequently and cannot be used frequently occurs. When the construction of the barrier tape 10 and the waterproofing layer protection material 100 takes a lot of material costs, and the construction time is reduced due to the frequent construction failure of the barrier tape 10 and the waterproofing layer protection material 100. There were many problems such as.

또한, 방통 테이프나 방수층 보호재를 제조할 때 자연 건조공정 및 제 3 히팅 로울러를 히팅시키는 공정에서 발포 수지폼(12)과 점착제(14)의 점착력이 약화되므로 인해 설령 상기와 같은 불량이 발생하지 않고 벽면에 부착된다 하더라도 시공 현장의 온도가 고온 다습한 경우 일정 시간이 지나면 벽면에 점착제만 붙고, 발포 수지폼(12)은 떨어지는 불량이 발생하게 되는 등의 문제점이 있었다.In addition, since the adhesive strength of the foamed resin foam 12 and the pressure-sensitive adhesive 14 in the process of heating the natural drying process and the third heating roller when the barrier tape or waterproof layer protective material is manufactured, the above-mentioned defects do not occur. Even if it is attached to the wall surface, when the temperature of the construction site is high temperature and high humidity after a certain time, only the adhesive on the wall surface, the foamed resin foam 12 had a problem such that the falling defect occurs.

따라서, 본 발명은 상기한 종래의 제반 문제점을 해결하기 위해 안출한 것으로서, 본 발명은 방통 테이프 및 방수층 보호재를 제조할 때 발포 수지폼에 직접 점착제를 도포할 수 있어서 방통 테이프 및 방수층 보호재를 사용하기 위해 발포 수지폼으로부터 보호 쉬트를 분리하기 위해 벗겨낼 때 발포 수지폼에 전사된 점착제가 보호 쉬트에 일부 달라붙어서 사용할 수 없는 불량이 발생되는 현상을 완벽하게 방지할 수 있도록 방통 테이프 및 방수층 보호재를 제조할 수 있어서 시공시 소요되는 자재 비용을 대폭 절감시킬 수 있을 뿐만 아니라, 시공면에 부착된 상태에서 현장의 온도나 습도 등과 같은 조건에 따라 시공면에 점착제만 붙고 발포 수지폼은 떨어지는 시공 불량이 발생되지 않는 강력한 점착력을 갖는 방통 테이프 및 방수층 보호재를 제조할 수 있어서 시공후 사후 관리가 용이하고 편리한 방통 테이프 및 방수층 보호재 제조방법을 제공하는 데 그 목적이 있다.Therefore, the present invention has been made to solve the above-mentioned conventional problems, the present invention can be applied to the pressure-sensitive adhesive directly on the foamed resin foam when manufacturing the barrier tape and waterproof layer protective material to use the barrier tape and waterproof layer protective material In order to completely remove the protective sheet from the foamed foam, the adhesives transferred to the foamed foam will stick to the protective sheet to prevent the occurrence of unusable defects. Not only can it greatly reduce the material cost required during construction, but it also causes adhesive failures in which only the adhesive is attached to the construction surface and foamed resin foam falls on the construction surface, depending on conditions such as temperature and humidity of the site while attached to the construction surface. Manufactures breathable tape and waterproof layer protective material with strong adhesive strength It is an object number according to the follow-up after construction easily and provides a convenient method for producing protective materials Broadcasting & Telecommunications tape and a waterproof layer.

본 발명의 다른 목적은 방통 테이프 및 방수층 보호재의 시공 작업시 작업 불량이 발생됨이 없이 신속하고 용이하여 작업 시간의 단축에 의한 작업 능률을 효율적으로 증대시킬 수 있는 방통 테이프 및 방수층 보호재 제조방법을 제공하는 데 있다.Another object of the present invention is to provide a method for manufacturing a waterproof tape and a waterproof layer protective material which can quickly and easily increase the efficiency of work by shortening the working time without a bad work during construction of the waterproof tape and the waterproof layer protective material. There is.

본 발명의 또 다른 목적은 방통 테이프 및 방수층 보호재를 제조할 때 점착제를 도포한 후 자연 건조공정을 진행하지 않고 곧바로 신속하게 후공정을 진행할 수 있어서 생산성을 효율적으로 증대시킬 수 있음과 아울러, 방통 테이프 및 방수층 보호재를 제조하기 위한 장치의 히팅 시간을 크게 줄일 수 있어서 장치의 구동시 소요되는 히팅을 위한 소비 전력을 대폭 절감시킬 수 있는 방통 테이프 및 방수층 보호재 제조방법을 제공하는 데 있다.Still another object of the present invention is to manufacture a fireproof tape and a waterproofing layer protective material, and then to apply the pressure-sensitive adhesive immediately after the natural drying process, so that the post-process can be promptly carried out to increase productivity efficiently, and also provide a fireproof tape. And it is possible to significantly reduce the heating time of the device for manufacturing the waterproof layer protective material to provide a method of manufacturing a waterproof tape and waterproof layer protective material that can significantly reduce the power consumption for the heating required when the device is driven.

상기한 목적을 달성하기 위해 본 발명은 아파트 등과 같은 공동 주택 등의 층간 소음과 진동 흡수 및 단열 기능을 강화함과 아울러 바닥 콘크리트를 균일한 상태로 시공하기 위해 이형지인 보호 쉬트를 분리하여 점착제의 점착력에 의해 발포 수지폼을 벽면에 부착하기 위한 방통 테이프나 바닥면으로부터 올라오는 습기를 차단시키기 위해 시공되는 방수층 보호재를 제조하기 위한 방통 테이프 및 방수층 보호재 제조방법에 있어서, 상기한 방통 테이프 및 방수층 보호재를 제조하기 위해 점착제의 원료들을 혼합한 후 가열하여 용융 및 일정 온도를 유지시킬 수 있는 산업용 믹서에서 250℃의 온도로 점착제를 제조하는 단계와, 상기 산업용 믹서에서 액받이로 공급된 점착제(14)의 온도를 70~80℃로 냉각시키는 단계와, 상기 액받이에서 냉각된 점착제를 발포 수지폼에 직접 도포하는 단계와, 상기 점착제가 도포된 발포 수지폼을 보호 쉬트와 결합시켜 방통 테이프 및 방수층 보호재를 제조하는 단계를 진행하는 것을 특징으로 하는 방통 테이프 및 방수층 보호재 제조방법이 제공된다.In order to achieve the above object, the present invention is to strengthen the inter-floor noise and vibration absorption and insulation function of apartment houses such as apartments, etc., and to separate the protective sheet, which is a release paper, in order to construct the floor concrete uniformly to the adhesive force of the adhesive. In the method for manufacturing a waterproof tape and a waterproof layer protective material for manufacturing a waterproof tape for attaching the foamed resin foam to a wall surface or a waterproof layer protective material which is constructed to block moisture from the bottom surface, the above-described waterproof tape and a waterproof layer protective material are manufactured. To prepare a pressure-sensitive adhesive at a temperature of 250 ° C. in an industrial mixer capable of mixing the raw materials of the pressure-sensitive adhesive and heating it to maintain melting and a constant temperature, and the temperature of the pressure-sensitive adhesive 14 supplied from the industrial mixer to the liquid receiver. Cooling to 70 ~ 80 ℃ and the pressure-sensitive adhesive cooled in the drip tray There is provided a method for producing a waterproof tape and a waterproof layer protective material, characterized in that the step of applying directly to the foam resin foam, and the step of manufacturing the waterproof tape and the waterproof layer protective material by combining the foamed resin foam coated with the adhesive with a protective sheet. .

삭제delete

이상에서 상술한 바와 같이, 본 발명은 방통 테이프 및 방수층 보호재를 제조할 때 발포 수지폼에 직접 점착제를 도포할 수 있음으로써 방통 테이프 및 방수층 보호재를 사용하기 위해 발포 수지폼으로부터 보호 쉬트를 분리하기 위해 벗겨낼 때 발포 수지폼에 전사된 점착제가 보호 쉬트에 일부 달라붙어서 사용할 수 없는 불량이 발생되는 현상을 완벽하게 방지할 수 있도록 방통 테이프 및 방수층 보 호재를 제조할 수 있어서 시공시 소요되는 자재 비용을 대폭 절감시킬 수 있게 된다.As described above, the present invention can apply a pressure-sensitive adhesive directly to the foamed resin foam when manufacturing the barrier tape and the waterproof layer protective material to separate the protective sheet from the foamed resin foam for use of the barrier tape and the waterproof layer protective material When peeled off, the adhesive transferred to the foamed foam is stuck to the protective sheet to prevent the unusable defects from occurring. It will be able to greatly reduce.

또한, 방통 테이프나 방수층 보호재가 시공면에 부착된 상태에서 현장의 온도나 습도 등과 같은 조건에 따라 시공면에 점착제만 붙고 발포 수지폼은 떨어지는 시공 불량이 발생되지 않는 강력한 점착력을 갖는 방통 테이프 및 방수층 보호재를 제조할 수 있어서 시공후 사후 관리가 용이하고, 이에 따른 시공 작업시의 작업 불량이 발생됨이 없이 신속하고 용이하여 작업 시간의 단축에 의한 작업 능률을 효율적으로 증대시킬 수 있게 된다.In addition, when the waterproof tape or waterproof layer protective material is attached to the construction surface, only the adhesive is attached to the construction surface according to conditions such as temperature and humidity in the field, and the foamed resin foam has a strong adhesive force that does not cause poor construction failure. Since the protective material can be manufactured, it is easy to follow-up management after construction, and accordingly, it is possible to quickly and easily increase the work efficiency by shortening the working time without generating a work defect during construction work.

특히, 방통 테이프 및 방수층 보호재를 제조할 때 점착제를 도포한 후 자연 건조공정을 진행하지 않고 곧바로 신속하게 후공정을 진행할 수 있어서 생산성을 효율적으로 증대시킬 수 있을 뿐만 아니라, 방통 테이프 및 방수층 보호재를 제조하기 위한 장치의 히팅 시간을 크게 줄일 수 있어서 장치의 구동시 소요되는 히팅을 위한 소비 전력을 대폭 절감시킬 수 있는 등의 많은 장점이 구비된 매우 유용한 발명이다.In particular, when manufacturing the barrier tape and the waterproofing layer protective material, after the adhesive is applied, the post-process can be promptly performed immediately without performing the natural drying process, thereby increasing productivity efficiently, and manufacturing the barrier tape and the waterproofing layer protective material. It is a very useful invention with many advantages, such as to significantly reduce the heating time of the device for reducing the power consumption for the heating required when the device is driven.

이하, 상기한 목적을 달성하기 위한 본 발명의 바람직한 실시예를 첨부된 도면을 참조하여 상세히 설명하면 다음과 같다. Hereinafter, with reference to the accompanying drawings, preferred embodiments of the present invention for achieving the above object will be described in detail.

도 4는 본 발명에 따른 방통 테이프 및 방수층 보호재 제조장치를 개략적으로 나타낸 구성도이며, 도 5는 본 발명에 따른 방통 테이프 및 방수층 보호재 제조 공정을 나타낸 흐름도이다.Figure 4 is a schematic view showing a manufacturing apparatus for manufacturing a waterproof tape and waterproof layer protective material according to the present invention, Figure 5 is a flow chart showing a manufacturing process of the waterproof tape and waterproof layer protective material according to the present invention.

본 발명의 방통 테이프 제조방법을 설명하기 전에 통상적인 방통 테이프(10) 및 방수층 보호재(100)의 발포 수지폼(12)은 충격을 흡수하는 완충 재질을 사용, 즉 폴리에틸렌(polyethylene; PE) 또는 에틸렌비닐아세테이트(ethylene vinylacetate; EVA)를 화학가교 및 발포시킨 시트 상태의 반경질 발포체로서, 단열성, 내수성, 완충성 및 내약품성 등이 우수하고, 친환경적임은 물론 가볍기 때문에 작업이 편리하며, 인체에 해가 없고, 반영구적이면서 내구성을 지닌 환경친화적인 특성을 갖는 단열재이다.Before describing the manufacturing method of the present invention, the foamed resin foam 12 of the conventional waterproofing tape 10 and the waterproofing layer protective material 100 uses a shock absorbing buffer material, that is, polyethylene (PE) or ethylene This semi-rigid foam is made of ethylene vinylacetate (EVA), chemically cross-linked and foamed, and has excellent thermal insulation, water resistance, cushioning, and chemical resistance, and is environmentally friendly and light. It is a heat insulating material having no environmentally friendly and durable properties.

또한, 방통 테이프(10) 및 방수층 보호재(100)의 상기 발포 수지폼(12)에 직접 도포되는 점착제(14)는 점착제 원료들을 혼합한 후 가열하여 용융 및 일정 온도를 유지시킬 수 있는 통상적인 산업용 믹서의 내부에 폴리우레탄, 저밀도 폴리에틸렌, 에틸렌아세테이트 등과 같은 합성 고무 또는 합성 수지 성분의 점착제 원료들을 혼합하여 용해시키는 것으로, 신나 등과 같은 용제(flux)를 사용하지 않으면서도 접착한 후에 고분자화하는 핫멜트(hot melt) 방식에 의해 제조된다.In addition, the pressure-sensitive adhesive 14 directly applied to the foamed resin foam 12 of the barrier tape 10 and the waterproofing layer protective material 100 may be mixed with adhesive raw materials and then heated to maintain melting and a constant temperature. Hot melt that is polymerized after bonding without dissolving the adhesive raw materials of synthetic rubber or synthetic resin components such as polyurethane, low density polyethylene, ethylene acetate, etc. It is manufactured by hot melt method.

본 발명의 방통 테이프 및 방수층 보호재 제조방법을 구체적으로 설명하면 도 4 및 도 5에 도시한 바와 같이, 먼저 방통 테이프(10) 및 방수층 보호재(100)의 롤 형상의 발포 수지폼(12)을 장치 일단 하부의 발포 수지폼 공급부(20)에 셋팅시킨 후, 장치를 작동시킨 상태에서 상기 발포 수지폼(12)의 단부를 전방으로 밀어주면 발포 수지폼(12)이 전진하면서 산업용 믹서(30)로부터 공급되는 점착제(14)가 담겨져 있는 액받이(40) 내의 상부 및 하부에 장착된 히팅 로울러(44) 및 점착제 도포용 로울러(42)는 상호 역방향으로 회전하면서 히팅 로울러(44)가 상기 액받이(40) 내의 점착제(14)를 점착제 도포용 로울러(42)에 묻혀줌과 동시에, 이 점착제 도포용 로울러(42)의 표면에 발포 수지폼(12)이 접촉하면서 상승함에 따라 발포 수지폼(12)에 직접 점착제(14)가 도포된다.Referring to the manufacturing method of the waterproofing tape and the waterproofing layer protective material of the present invention in detail, as shown in FIGS. 4 and 5, first, the roll-shaped foamed resin foam 12 of the waterproofing tape 10 and the waterproofing layer protective material 100 is provided. Once the lower foamed resin foam supply unit 20 is set, the end of the foamed resin foam 12 is pushed forward while the apparatus is in operation, and the foamed resin foam 12 moves forward from the industrial mixer 30. The heating roller 44 and the roller for applying pressure-sensitive adhesive 42 mounted on the upper and lower portions in the liquid receiver 40 containing the supplied pressure-sensitive adhesive 14 rotate in opposite directions, while the heating roller 44 is connected to the liquid receiver ( The pressure-sensitive adhesive 14 in the 40 is buried in the pressure-sensitive adhesive roller 42, and the foamed resin foam 12 is raised as the foamed resin foam 12 comes into contact with the surface of the pressure-sensitive adhesive roller 42. The adhesive 14 is apply | coated directly to it.

이와 동시에, 상기 점착제가 도포된 발포 수지폼(12)이 상승하여 장치 상부의 발포 수지폼 이송부(50)를 통과하여 장치 타단 하부의 결합부에 도달함과 동시에, 보호 쉬트 공급부(70)에서 공급되는 보호 쉬트(16)가 전진하여 결합부(60)에 도달하면서 상기 점착제(14)가 도포된 발포 수지폼(12)과 보호 쉬트(16)가 동시에 결합부(60)에 설치되어 회전하는 가압 로울러를 통과하여 결합된 상태로 전진하여 권취부(80)에서 롤 형태로 권취하는 공정을 반복함으로써 방통 테이프(10) 및 방수층 보호재(100)를 제조할 수 있게 된다.At the same time, the foamed resin foam 12 coated with the pressure-sensitive adhesive is raised to pass through the foamed resin foam transfer part 50 at the upper part of the device to reach the engaging part at the lower end of the device, and is supplied from the protective sheet supply part 70. When the protective sheet 16 is advanced to reach the coupling portion 60, the pressure-sensitive foam foam 12 and the protective sheet 16 to which the pressure-sensitive adhesive 14 is applied are simultaneously installed on the coupling portion 60 and rotated. By passing through the rollers in a combined state and repeating the winding process in the form of a roll in the winding unit 80 it is possible to manufacture the barrier tape 10 and the waterproof layer protective material 100.

한편, 본 발명에 의해 방통 테이프(10) 및 방수층 보호재(100)를 제조하기 위해 상기 발포 수지폼(12)에 직접 점착제(14)를 도포할 때 상기 원료들을 혼합한 후 가열하여 용융 및 일정 온도를 유지시킬 수 있는 산업용 믹서(30)에서 제조된 250℃ 정도의 점착제(14)는 상기 산업용 믹서(30)에서 액받이(40)로 공급된 점착제(14)의 온도가 70~80℃를 유지하도록 온도를 냉각시킨 상태에서 상기 발포 수지폼(12)에 도포하게 된다.
이때, 상기 발포 수지폼(12)에 직접 점착제(14)를 도포할 때의 온도를 70~80℃로 유지하는 이유는 70℃ 이하인 경우 과도한 점착제가 도포되고, 80℃ 이상인 경우 발포 수지폼이 녹게 되므로 인해 직접 발포 수지폼에 도포시의 최적의 온도 조건임을 파악할 수 있었다.
한편, 상기 산업용 믹서(30)에서 액받이(40)로 공급되는 점착제(14)의 온도를 냉각시키는 방법은 필요에 따라 통상적으로 산업용 믹서(30)에서 제조된 점착제(14)를 액받이(40)로 공급하여 이 액받이(40)에서 대기중에 자연 냉각시키는 자연 냉각방식이나, 상기 액받이(40) 근처에 송풍기 등을 설치하여 강제 냉각시키는 강제 냉각방식 등과 같이 제작 물량이나 공장의 여건 등을 고려하여 냉각 방식을 채택하여 사용할 수 있으며, 상기 액받이(40)에는 작업자가 도포 작업에 적합한 점착제의 온도를 정확하게 감지하여 인식하기 위한 온도 감지센서를 부착하는 것이 바람직하다. On the other hand, when the pressure-sensitive adhesive 14 is applied directly to the foamed resin foam 12 in order to manufacture the barrier tape 10 and the waterproof layer protective material 100 according to the present invention, the raw materials are mixed and heated to melt and a predetermined temperature. 250 ° C. of pressure-sensitive adhesive 14 manufactured in the industrial mixer 30 capable of maintaining the temperature of the pressure-sensitive adhesive 14 supplied from the industrial mixer 30 to the liquid receiver 40 maintains 70 to 80 ° C. It is applied to the foamed resin foam 12 while the temperature is cooled.
At this time, the reason for maintaining the temperature when the pressure-sensitive adhesive 14 is directly applied to the foamed resin foam 12 at 70 ~ 80 ℃ is that the excessive adhesive is applied when the temperature is 70 ℃ or less, and the foamed resin foam is melted at 80 ℃ or more Therefore, it could be understood that the optimum temperature condition when directly applied to the foamed foam.
On the other hand, the method of cooling the temperature of the pressure-sensitive adhesive 14 supplied from the industrial mixer 30 to the liquid receiver 40, the liquid receiver 40 is usually prepared by the industrial mixer 30, if necessary. The amount of production or factory conditions, such as a natural cooling method to naturally cool the atmosphere in the drip tray 40 and a forced cooling method by installing a blower or the like near the drip tray 40 for forced cooling. In consideration of the cooling method may be adopted, it is preferable that the drip tray 40 is attached with a temperature sensor for the operator to accurately detect and recognize the temperature of the adhesive suitable for the coating operation.

또한, 본 발명과 같이 점착제(14)의 온도를 70~80℃로 강하하여 발포 수지폼(12)에 직접 도포할 경우 종래의 기술과 비교할 때 점착제(14)가 과도하게 도포될 것으로 예상되지만, 실제로 발포 수지폼(12)의 표면에는 무수히 많은 미세한 발포홈이 형성되어 있으므로 인해 종래 기술에서 보호 쉬트(16)의 단면적 전체 100%에 도포하는 것보다 발포 수지폼(12)의 단면적이 상기한 발포홈에 의해 작아지기 때문에 실제로 도포되는 점착제(14)의 사용량을 종래 기술에 비해 효과적으로 절감시킬 수 있게 된다.In addition, when dropping the temperature of the pressure-sensitive adhesive 14 to 70 ~ 80 ℃ as in the present invention directly applied to the foamed resin foam 12, it is expected that the pressure-sensitive adhesive 14 is excessively applied in comparison with the prior art, In fact, since a myriad of fine foamed grooves are formed on the surface of the foamed resin foam 12, the cross-sectional area of the foamed resin foam 12 is higher than that in the prior art applied to 100% of the total cross-sectional area of the protective sheet 16. Since the grooves are reduced by the grooves, the amount of the adhesive 14 actually applied can be effectively reduced compared to the prior art.

또한, 상기 점착제(14)를 온도가 강하된 70~80℃로 발포 수지폼(12)에 도포한다고 하여도 발포 수지폼의 특성상 70~80℃의 점착제를 발포 수지폼에 도포하는 과정에서 발포 수지폼의 표면이 열에 의해 녹으면서 거칠어지기 때문에 발포 수지폼과 점착제 사이에 강력한 접착력이 발생하게 된다.In addition, even if the pressure-sensitive adhesive 14 is applied to the foamed resin foam 12 at a temperature of 70 to 80 ° C., the foamed resin in the process of applying the pressure-sensitive adhesive of 70 to 80 ° C. to the foamed resin foam due to the characteristics of the foamed resin foam. Since the surface of the foam becomes rough as it melts by heat, a strong adhesive force is generated between the foamed resin foam and the pressure-sensitive adhesive.

따라서, 상기한 발포 수지폼과 점착제 사이에 강력한 접착력과 아울러 발포 수지폼(12)에 직접 점착제(14)가 도포되어 완벽하게 전사된 상태이기 때문에 방통 테이프(10) 및 방수층 보호재(100)를 시공하기 위해 발포 수지폼(12)으로부터 보호 쉬트(16)를 급하게 분리하여 벗겨낸다고 하더라도 점착제(14)가 보호 쉬트(16)에 달라붙어서 사용할 수 없는 불량이 발생되는 현상을 완벽하게 방지할 수 있어서 방통 테이프의 시공시 소요되는 자재 비용을 대폭 절감시킬 수 있음은 물론, 방통 테이프의 시공 작업시 작업 불량이 발생됨이 없이 신속하고 용이하여 작업 시간의 단 축에 의한 시공 생산성을 효율적으로 증대시킬 수 있게 된다.Therefore, since the adhesive 14 is applied directly to the foamed resin foam 12 and is completely transferred to the foamed resin foam and the pressure-sensitive adhesive, the barrier tape 10 and the waterproof layer protective material 100 are constructed. Even if the protective sheet 16 is urgently separated and peeled off from the foamed resin foam 12, the adhesive 14 adheres to the protective sheet 16 to completely prevent the occurrence of unusable defects. Not only can the material cost required for the construction of tapes can be greatly reduced, but also the construction productivity can be efficiently and efficiently increased due to the shortening of the working time without the occurrence of work defects during the construction of the barrier tape. .

도 1은 일반적인 방통 테이프를 나타낸 사시도 Figure 1 is a perspective view showing a general penetration tape

도 2는 일반적인 방통 테이프의 사용 상태를 나타낸 종단면도 Figure 2 is a longitudinal cross-sectional view showing a state of use of the general barrier tape.

도 3은 일반적인 방수층 보호재를 나타낸 사시도 3 is a perspective view showing a general waterproof layer protective material

도 4는 본 발명에 따른 방통 테이프 및 방수층 보호재 제조장치를 개략적으로 나타낸 구성도 Figure 4 is a schematic view showing a manufacturing apparatus for manufacturing a waterproof tape and waterproof layer protective material according to the present invention

도 5는 본 발명에 따른 방통 테이프 및 방수층 보호재 제조 공정을 나타낸 흐름도 5 is a flow chart showing a manufacturing process of the waterproofing tape and the waterproofing layer protective material according to the present invention.

* 도면의 주요 부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings

10; 방통 테이프 12; 발포 수지폼 10; Bulletproof tape 12; Foam Resin Foam

14; 점착제 16; 보호 쉬트 14; Adhesive 16; Protection sheet

18; 직물지 20; 발포 수지폼 공급부 18; Tissue paper 20; Foam Resin Foam Supply

30; 산업용 믹서 40; 액받이 30; Industrial mixer 40; Drip tray

42; 점착제 도포용 로울러 44; 히팅 로울러 42; Roller 44 for pressure-sensitive adhesive application; Heating roller

50; 발포 수지폼 이송부 60; 결합부 50; Foamed resin foam transfer unit 60; Joint

70; 보호 쉬트 공급부 80; 권취부 70; Protective sheet supply 80; Winding

100; 방수층 보호재 100; Waterproof layer protective material

Claims (2)

아파트 등과 같은 공동 주택 등의 층간 소음과 진동 흡수 및 단열 기능을 강화함과 아울러 바닥 콘크리트를 균일한 상태로 시공하기 위해 이형지인 보호 쉬트를 분리하여 점착제의 점착력에 의해 발포 수지폼을 벽면에 부착하기 위한 방통 테이프나 바닥면으로부터 올라오는 습기를 차단시키기 위해 시공되는 방수층 보호재를 제조하기 위한 방통 테이프 및 방수층 보호재 제조방법에 있어서, It is designed to attach foamed resin foam to the wall by adhesive force by separating the protective sheet, which is a release paper, in order to strengthen the inter-floor noise and vibration absorption and insulation function of apartment houses such as apartments. In the manufacturing method of the waterproofing tape and waterproofing layer protective material for manufacturing the waterproofing layer protective material which is constructed to block moisture rising from the waterproofing tape or the bottom surface, 상기한 방통 테이프(10) 및 방수층 보호재(100)를 제조하기 위해 점착제의 원료들을 혼합한 후 가열하여 용융 및 일정 온도를 유지시킬 수 있는 산업용 믹서(30)에서 250℃의 온도로 점착제(14)를 제조하는 단계와, The pressure-sensitive adhesive 14 at a temperature of 250 ° C. in an industrial mixer 30 which can mix and heat the raw materials of the pressure-sensitive adhesive to manufacture the above-mentioned barrier-proof tape 10 and the waterproof layer protective material 100 and then melt and maintain a constant temperature. Manufacturing the step; 상기 산업용 믹서(30)에서 액받이(40)로 공급된 점착제(14)의 온도를 70~80℃로 냉각시키는 단계와, Cooling the temperature of the pressure-sensitive adhesive 14 supplied from the industrial mixer 30 to the liquid receiver 40 at 70 to 80 ° C .; 상기 액받이(40)에서 냉각된 점착제(14)를 발포 수지폼(12)에 직접 도포하는 단계와, Directly applying the adhesive 14 cooled in the drip tray 40 to the foamed resin foam 12; 상기 점착제(14)가 도포된 발포 수지폼(12)을 보호 쉬트(16)와 결합시켜 방통 테이프 및 방수층 보호재를 제조하는 단계를 진행하는 것을 특징으로 하는 방통 테이프 및 방수층 보호재 제조방법.The method of manufacturing a fireproof tape and a waterproof layer protective material, characterized in that the pressure-sensitive adhesive (14) is applied to the foamed resin foam (12) is combined with a protective sheet (16) to produce a waterproof tape and a waterproof layer protective material. 삭제delete
KR1020070107607A 2007-10-25 2007-10-25 Joint filler tape and waterproof layer protection member manufacturing method KR100848575B1 (en)