KR100808208B1 - Lusterless uv curing composition for writing board and lusterless film for writing board coated the composition - Google Patents
Lusterless uv curing composition for writing board and lusterless film for writing board coated the composition Download PDFInfo
- Publication number
- KR100808208B1 KR100808208B1 KR1020070029620A KR20070029620A KR100808208B1 KR 100808208 B1 KR100808208 B1 KR 100808208B1 KR 1020070029620 A KR1020070029620 A KR 1020070029620A KR 20070029620 A KR20070029620 A KR 20070029620A KR 100808208 B1 KR100808208 B1 KR 100808208B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- oligomer
- writing board
- film
- Prior art date
Abstract
Description
도 1 - 본 발명의 실시예에 따른 (a)필기보드용 무광 필름 및 (b)이형지가 제거된 필기보드에 대한 단면도.1-A cross-sectional view of (a) a matte film for the writing board and (b) a writing board from which the release paper is removed according to an embodiment of the present invention.
도 2 - 본 발명의 실시예에 따른 엠보 무늬가 형성된 이형지에 대한 사시도.Figure 2-a perspective view of a release paper formed with embossed pattern according to an embodiment of the present invention.
10 : 점착 대상물 100 : 폴리에틸렌 테레프탈레이트 필름10: adhesion object 100: polyethylene terephthalate film
200 : 코팅층 300 : 점착층200: coating layer 300: adhesive layer
400 : 이형지 410 : 엠보 무늬400: release paper 410: embossed pattern
본 발명은 필기보드용 무광 UV경화형 조성물 및 필기보드용 무광 필름에 관한 것으로, 무광으로 필기적성, 부착성, 내용제성과 내스크래치성이 우수하고 지움성이 우수한 필기보드용 무광 UV경화형 조성물 및 필기보드용 무광 필름에 관한 것이다.The present invention relates to a matte UV-curable composition for writing boards and a matte film for writing boards, the matte UV-curable composition and writing for writing boards excellent in writing, adhesiveness, solvent resistance and scratch resistance, It relates to a matte film for boards.
필기보드는 일반적으로 화이트 색상을 띄는 화이트보드가 널리 사용되며, 상 기 화이트보드는 표면이 유광층을 띄며, 흠집이 없는 백색보드로, 염료 잉크로 제조되어진 수성펜으로 그림을 그리고 글씨를 쓰고 지울 수 있도록 만들어진 제품이다. 이러한 화이트 보드는 종래 분필을 사용하는 칠판을 대신하여 분필에서 발생하는 미세한 분필가루를 발생시키지 않으며 사용의 편의성으로 인해 학교, 학원, 기업에서 많이 사용되고 있다.Writing boards are generally used for whiteboards with white color. The whiteboard is a whiteboard with a glossy surface and without scratches. It can be painted, written and erased with a water-based pen made of dye ink. It is a product made to be. Such a white board does not generate fine chalk powder generated from chalk instead of a blackboard using conventional chalk, and is widely used in schools, academies, and businesses because of its ease of use.
그러나 종래의 화이트보드는 수성펜을 사용하여 글씨를 쓰거나 그림을 그릴 때 필기 적성이 우수하며 환경적인 오염이 적다는 장점이 있는 반면에 화이트보드는 형광등이나 불빛 반사에 의해 시인성이 떨어지며 불빛이나 빛이 반사되는 부분의 글씨나 그림 등은 잘 보이지 않는다는 단점을 갖고 있다.However, the conventional whiteboard has the advantage of good writing ability and less environmental pollution when writing or drawing with a water-based pen, while the whiteboard is less visible due to fluorescent light or light reflection and reflects light or light. There is a disadvantage that the letters and pictures of the parts are not easily seen.
특히 야간에 형광등 아래에서 교육자가 화이트보드 표면에 수성펜으로 기재 하였을 때 화이트보드 표면에 형광등 불빛이 반사되거나 형광등 자체가 화이트보트 표면에 보이게 되는 현상을 볼 수 있다. 이러한 형상으로 인해 피교육자는 강의 내용을 신속하게 이해할 수 없을 뿐만 아니라 강의 내용을 노트에 기록하지 못하게 되는 어려움이 있어 불이익을 받게 되며, 장시간 반사되는 빛에 노출되면 시력을 약화시키는 문제를 발생한다. 표면에 무광화된 화이트보드에 대한 필요성과 인식이 날로 높아짐에 따라 국내 업체에서도 무광 화이트보드에 대한 개발을 가속화하고 있으며 몇몇 제품을 선보이고 있다.In particular, when the instructor writes a water-based pen on the surface of the whiteboard under the fluorescent lamp at night, the fluorescent light is reflected on the surface of the whiteboard or the fluorescent lamp itself is visible on the whiteboard surface. Due to this shape, the trainees are not able to quickly understand the contents of the lecture and have difficulty in not recording the contents of the lecture in the notebook, which is disadvantageous, and when exposed to the reflected light for a long time, the eyesight is weakened. As the need and awareness of matte whiteboards on the surface increases, domestic companies are also accelerating the development of matte whiteboards and introducing several products.
이러한 제품을 비교해 볼 때 순수 국내 제품은 무광도가 떨어져 시인성의 문제를 여전히 갖고 있으며, 일부 제품은 무광 처리된 열가소성 불소 수지와 PET를 결합시켜 만든 제품으로 지움성과 내용제성이 우수하지만 이 제품은 수성펜으로 기 록이 불가능하며 유성 펜에서 사용이 가능하므로 엄격한 의미에서 화이트보드라 할 수 없다.Compared to these products, pure domestic products are still matte and still have visibility problems. Some products are made of a combination of matte-treated thermoplastic fluorocarbon resin and PET. As it is impossible to record and can be used in the oil pen, it is not a whiteboard in the strict sense.
본 발명은 상기 문제점을 해결하기 위해 안출된 것으로서, 무광을 발생시키는 UV경화형 조성물을 제공하는 것을 그 목적으로 하며, 이를 이용하여 무광으로 필기적성, 부착성, 내용제성과 내스크래치성이 우수하고 지움성이 우수한 필기보드용 무광 필름을 제공하는 것을 그 목적으로 한다.The present invention has been made to solve the above problems, the object of the present invention is to provide a UV-curable composition that generates a matte, by using this matte excellent writing and adhesiveness, solvent resistance and scratch resistance It is an object of the present invention to provide a matte film for writing board having excellent properties.
또한 점착성이 우수하여 점착 대상물과의 착탈이 용이하며, 칼라안료를 첨가하여 다양한 색상을 제공하며, 엠보 무늬의 이형지를 사용하여 점착시 기포가 발생하지 않도록 하는 필기보드용 무광 필름의 제공을 또 다른 목적으로 한다.In addition, it is easy to attach / detach with the adhesive object because of its excellent adhesiveness, and it is possible to provide a variety of colors by adding color pigments, and to provide a matte film for writing boards that prevents bubbles from forming by using embossed release paper. The purpose.
상술한 바와 같은 목적 달성을 위해 본 발명은, 3~30중량부의 소광제, 40~70중량부의 UV경화형 6관능기 올리고머, 3~20중량부의 UV경화형 1~3관능기 올리고머, 10~20중량부의 UV경화형 모노머, 0.2~1.5중량부의 UV경화형 표면조절제, 3~10중량부의 경화제를 포함하여 이루어진 것을 특징으로 하는 필기보드용 무광 UV경화형 조성물 및 상기 무광 UV경화형 조성물을 폴리에틸렌 테레프탈레이트 필름 상면에 3~40㎛ 두께로 코팅시킨 필기보드용 무광 필름을 기술적 요지로 한다.In order to achieve the above object, the present invention, 3 to 30 parts by weight of a matting agent, 40 to 70 parts by weight of UV curing type 6 functional oligomer, 3 to 20 parts by weight of UV curing type 1 to 3 functional group oligomer, 10 to 20 parts by weight of UV A curable monomer, 0.2 to 1.5 parts by weight of a UV curable surface control agent, 3 to 10 parts by weight of a matting UV curable composition for writing board and the matte UV curable composition comprising a 3 to 40 parts by weight on the polyethylene terephthalate film upper surface The matte film for writing boards coated with a thickness of μm is a technical subject matter.
또한, 상기 소광제는, 무기소광제, 유기소광제, 왁스소광제 중에 적어도 하나를 선택하여 사용하는 것이 바람직하며, 상기 올리고머는 지방족 아크릴레이트 올리고머이며, 3관능기 올리고머가 6관능기 올리고머에 대해 9~11중량비로 첨가되 는 것이 바람직하다.In addition, the quencher is preferably used by selecting at least one of an inorganic quencher, an organic quencher, a wax quencher, the oligomer is an aliphatic acrylate oligomer, the tri-functional oligomer is 9 ~ to the six-functional oligomer It is preferably added in an 11 weight ratio.
여기에서, 상기 폴리에틸렌 테레프탈레이트 필름 하면에는 백색 티탄 산화물과 아크릴계 점착제가 혼합된 점착조성물이 코팅되어 점착층이 형성되는 것이 바람직하며, 또한 상기 아크릴계 점착제에는 칼라안료가 더 첨가되어 필기용 칼라보드를 형성시키는 것이 바람직하다.Here, the lower surface of the polyethylene terephthalate film is preferably a pressure-sensitive adhesive layer is formed by coating a pressure-sensitive adhesive composition of a mixture of white titanium oxide and an acrylic pressure-sensitive adhesive, and furthermore, a color pigment is further added to the acrylic pressure-sensitive adhesive to form a writing color board. It is preferable to make it.
또한, 상기 점착층 하면에는 점착층 보호를 위한 이형지가 부착되는 것이 바람직하며, 상기 이형지 상면에는 기포 방지용 엠보 무늬가 더 형성되는 것이 더욱 바람직하다.In addition, it is preferable that a release paper for protecting the adhesive layer is attached to the lower surface of the adhesive layer, and an embossing pattern for preventing bubbles is further formed on the upper surface of the release paper.
이에 따라, UV경화형 조성물을 코팅한 필기보드용 무광 필름의 표면은 형광등에 의한 불빛 반사가 극히 적어 눈부심이 없을 뿐만 아니라 필기성 및 내용제성, 내스크래치성이 우수하고 수성펜 지우개로 글씨나 그림을 지울 때 지움성이 뛰어나고, 또한, 필기보드용 무광 필름의 뒷면은 여러 가지 색깔의 안료가 첨가된, 재박리가 가능한 점착층을 형성시켜 눈의 피로감을 완화시키고, 쉽게 붙이고 뗄 수 있어 사용의 편리성을 강화하였으며, 또한, 필기보드용 무광 필름의 점착층을 보호하기 위한 엠보 무늬가 형성된 이형지를 부착시켜, 필기보드용 무광 필름과 점착 대상물 사이에 발생하는 기포의 발생을 억제하여 표면이 매끄럽고 우수한 품질의 필기보드를 제공할 수 있는 이점이 있다.Accordingly, the surface of the matting film for writing boards coated with the UV-curable composition has extremely low light reflection by fluorescent lamps, so that there is no glare, and writing and solvent resistance and scratch resistance are excellent. The backing of the matte film for writing board is excellent and it is easy to use because it forms a re-peelable adhesive layer with various colored pigments to relieve eye fatigue and can be easily attached and removed. In addition, by attaching an embossed patterned release paper to protect the adhesive layer of the matting film for writing board, by suppressing the generation of bubbles generated between the matting film for writing board and the adhesive object, the surface is smooth and excellent quality There is an advantage to provide a writing board.
이하에서는 본 발명에 대해 첨부된 도면을 참조하여 상세히 설명하고자 한다. 도 1 (a)는 본 발명의 실시예에 따른 필기보드용 무광 필름이고, 도 1(b)는 본 발명의 실시예에 따른 이형지가 제거된 필기보드에 대한 단면도이며, 도 2는 본 발명의 실시예에 따른 엠보 무늬가 형성된 이형지에 대한 사시도를 나타낸 것이다.Hereinafter, with reference to the accompanying drawings for the present invention will be described in detail. Figure 1 (a) is a matting film for writing board according to an embodiment of the present invention, Figure 1 (b) is a cross-sectional view of the writing board is removed from the release paper according to an embodiment of the present invention, Figure 2 It shows a perspective view of a release paper formed embossed pattern according to the embodiment.
본 발명은 필기보드용 무광 UV경화형 조성물 및 이를 코팅한 필기보드용 필름에 관한 것으로서, 상기 무광 UV경화형 조성물은 빛을 소광하기 위한 소광제로 총중량의 3~30중량부가 첨가되며, 40~70중량부의 UV경화형 6관능기 올리고머, 3~20중량부의 UV경화형 1~3관능기 올리고머, 10~20중량부의 UV경화형 모노머, 0.2~1.5중량부의 UV경화형 표면조절제, 3~10중량부의 경화제가 포함하여 이루어진다.The present invention relates to a matte UV-curable composition for writing board and a film for writing board coated with the same, wherein the matte UV-curable composition is added to 3 to 30 parts by weight of a total weight as a matting agent for quenching light, 40 to 70 parts by weight UV curable 6 functional group oligomer, 3 to 20 parts by weight of UV curable 1 to 3 functional group oligomer, 10 to 20 parts by weight of UV curable monomer, 0.2 to 1.5 parts by weight of UV curable surface control agent, 3 to 10 parts by weight of the curing agent.
그리고, 상기 무광 UV경화형 조성물을 폴리에틸렌 테레프탈레이트(PET) 필름(100) 상면에 3~40㎛ 두께로 코팅하므로써 필기보드용 무광 필름이 제조되게 된다.In addition, the matte UV-curable composition is coated on the upper surface of the polyethylene terephthalate (PET)
이러한 필기보드용 무광 필름의 하면에는 점착제가 코팅되며, 상기 점착제의 점착 조성물은 백색 티탄 산화물과 아크릴계 점착제로 이루어지고, 상기 필기보드용 무광 필름 하면에 코팅하여 점착층(300)을 형성하며, 이러한 점착층(300)을 보호하기 위해 이형지(400)가 별도로 부착되어 제공되게 된다.A pressure-sensitive adhesive is coated on the bottom surface of the matting film for writing board, and the pressure-sensitive adhesive composition of the pressure-sensitive adhesive composition is made of white titanium oxide and an acrylic pressure-sensitive adhesive, and is coated on the bottom surface of the matting film for writing board to form an
상기 이형지(400)를 박리하여 상기 점착 대상물(10) 상면에 필기보드용 무광 필름을 점착시키므로써 무광의 필기보드가 완성되게 되는 것이다.By peeling the
여기에서, 점착제에 별도의 칼라를 띄는 안료의 첨가여부에 따라 필기보드의 색상이 화이트, 녹색, 청색 등 다양한 색깔의 보드를 형성시킬 수 있는 것이다.Here, the color of the writing board may form a board of various colors such as white, green, and blue according to the addition of a pigment having a separate color to the adhesive.
본 발명에 있어 소광제로는 무기소광제, 유기소광제, 왁스소광제 등을 사용 할 수 있으며, 무기소광제로는 SiO2, Talc, CaCO3, MgO, Al2O3, ZnO, CaO, Zeolite 등이 있으며, 유기소광제로는 PMMA 파우더, 멜라민 파우더(Melamaine powder), 왁스소광제로는 PE, PP, Amide, 불소가 있다.In the present invention, as a quencher, an inorganic quencher, an organic quencher, a wax quencher, etc. may be used, and as an inorganic quencher, SiO 2 , Talc, CaCO 3 , MgO, Al 2 O 3 , ZnO, CaO, Zeolite, etc. There are, as the organic quencher PMMA powder, melamine powder (Melamaine powder), the wax quencher is PE, PP, Amide, fluorine.
만약 무기소광제인 실리카를 사용할 경우 실리카 표면이 유기물로 코팅된 실리카를 사용해야 하며, 실리카 표면에 유기물이 코팅되어 있지 않거나 실리카의 함유량이 크면 수성펜으로 글씨나 그림을 지울 때 표면에 얼룩이 남아 지움성에 악영향을 미친다. 또한 Talc나 CaCO3은 지움성에 악영향을 미치지는 않으나 무광을 나타내기 위하여 많은 양의 사용이 필요하며 사용량이 많음에 따라 필기보드 표면의 내마모성이 떨어지는 단점이 있다. 또한 왁스소광제를 단독으로 사용하면 소광성이 떨어지며, 무기 또는 유기소광제와 혼합하여 사용하는 경우 표면슬립성 및 내용제성이 좋아지나 많은 양을 사용했을 경우 칙소성이 증가하여 코팅에 어려움이 있으므로, 상기 소광제를 최적의 비율로 선택하여 사용하거나 종류에 따라 혼합하여 사용하는 것이 바람직하다.If you use silica as an inorganic quencher, you should use silica coated with organic material. If the organic material is not coated on silica surface or the silica content is large, stains remain on the surface when you erase letters or pictures with water-based pen. Crazy In addition, Talc or CaCO 3 does not adversely affect erase properties, but requires a large amount of matte to exhibit a matte effect, and has a disadvantage in that wear resistance of the writing board surface is inferior as the amount is high. In addition, when the wax quencher is used alone, the quenching property is decreased, and when used in combination with an inorganic or organic quencher, the surface slipperiness and solvent resistance are improved, but when a large amount is used, the coating is difficult due to an increase in the thixotropy. It is preferable to select and use the quencher in an optimum ratio or to mix according to the type.
그리고, 상기 UV 경화형 올리고머는 UV경화형 조성물의 바인더로써 사용되며, 장시간 외부의 노출이 되는 필기보드의 특성상 황변을 유발하는 방향족 우레탄 아크릴레이트나 비스페놀형 에폭시 아크릴레이트를 배제하고, 6관능기 이상의 순수 지방족 우레탄 아크릴레이트 올리고머와 점도 조절과 부착력 향상을 위하여 1관능기 이상 3관능기의 올리고머를 사용하였다.In addition, the UV-curable oligomer is used as a binder of the UV-curable composition, excluding aromatic urethane acrylate or bisphenol-type epoxy acrylate that causes yellowing due to the characteristics of the writing board that is exposed to the outside for a long time, pure aliphatic urethane of 6 or more functional groups An oligomer of at least one functional group and at least trifunctional group was used for acrylate oligomer and viscosity control and adhesion improvement.
만약 6관능기 이상의 올리고머만을 바인더로 사용하였을 경우 무광 필기보드 표면의 지움성은 증가하는 반면 기재인 폴리에틸렌 테레프탈레이드(PET)의 컬(curl) 현상으로 인하여 제품화할 수 없으며, 6관능기 이하의 관능기를 주로 사용하면 유연한 물성으로 인하여 컬(curl) 현상이 없어지고 편평도도 우수하였으나 수성펜 지우개로 필기보드 표면을 지울 때 지움성이 현저히 떨어지는 결과가 나왔다. 또한 에테르(Ether) 구조를 가지는 아크릴레이트 올리고머를 사용하였을 때는 표면 건조성은 월등히 나은 결과를 가지나 역시 잉크의 지움성에서 현저하게 성능이 떨어지는 결과를 보였다.If only oligomers of 6 or more functional groups are used as binders, the eraser on the surface of the matte writing board increases, but it cannot be commercialized due to the curl of the polyethylene terephthalate (PET), which is a substrate. When the physical properties of the pen (curl) is eliminated due to the flexible physical properties and the flatness was also excellent, but the eraser was significantly reduced when the surface of the writing board with the water-based pen eraser. In addition, when the acrylate oligomer having an ether structure is used, the surface dryness is much better but also the performance is significantly lower in the eraseability of the ink.
따라서, 본 발명에 있어서는 6관능기의 올리고머와 1~3관능기의 올리고머의 사용량을 1~3관능기 올리고머가 6관능기 올리고머에 대해 9~11중량비로 사용하는 것이 바람직하며, 더욱 바람직하게는 6관능기 올리고머에서 10중량비를 1~3관능기 올리고머로 대체하였을 때 컬(curl) 현상도 현저히 줄어들며 잉크 지움성도 우수하였다.Therefore, in the present invention, it is preferable that 1-3 functional group oligomers are used in a 9 to 11 weight ratio of the 6 functional group oligomer and the 1 to 3 functional group oligomer, more preferably in the 6 functional group oligomer. When the 10 weight ratio was replaced with 1-3 functional group oligomers, curling was also significantly reduced and ink eraseability was excellent.
그리고, 무광 화이트보드를 제조하기 위하여 사용된 유, 무기 소광제의 함량이 늘어남에 따라 점도가 상승되고 이러한 상승된 점도는 코팅의 어려움을 가져오게 된다. 따라서, 적당한 점도를 유지하기 위한 방법으로 1관능기보다 크고 6관능기보다 작은 모노머를 사용한다. 모노머의 함량이 많아지면 코팅시 표면의 레벨링이 좋아지나 잉크 지움성이 떨어지며 UV 건조 속도가 떨어지므로 적절한 량을 사용한다.In addition, as the content of the organic and inorganic matting agents used to manufacture the matte whiteboard increases, the viscosity is increased, and this increased viscosity causes difficulty in coating. Therefore, as a method for maintaining a moderate viscosity Monomers larger than monofunctional and smaller than 6 functional groups are used. If the content of the monomer is increased, the leveling of the surface is improved during coating, but ink eraseability is decreased and UV drying speed is decreased. Therefore, use an appropriate amount.
그리고, UV경화형 표면조절제의 경우 폴리 디메틸 실록산 또는 실리콘 폴리에테르 아크릴레이트 형태를 주로 사용하였으며, 여기에 표면 기포와 내마모성을 향상시키기 위하여 실리콘 아크릴레이트를 소량 첨가하였다. 표면조절제의 경우 첨가량이 많으면 실리콘의 영향으로 수성펜의 습윤력이 나빠지며, 첨가량이 적으면 지움성이 나빠져 화이트보드 표면에 얼룩이 남게 된다. 또한 UV경화형이 아닌 실리콘 표면 조절제를 사용한 경우는 글씨의 지움성은 우수하나 수성펜 지우개로 글씨를 지우고 난 뒤 필기보드 표면에 유광의 글씨 흔적이 나타나며, 실리콘이 서서히 화이트보드 표면으로 이행하는 현상으로 인해 효과의 지속성을 기대할 수 없게 된다. 따라서, UV경화형의 표면조절제를 사용하는 것이 바람직하다.In the case of the UV-curable surface control agent, polydimethyl siloxane or silicone polyether acrylate form was mainly used, and a small amount of silicone acrylate was added thereto to improve surface bubbles and wear resistance. In the case of the surface control agent, the amount of the additive is high, so that the wetting power of the aqueous pen is deteriorated due to the influence of silicone, and when the amount of the additive is small, the eraser becomes poor and stains remain on the surface of the whiteboard. In addition, the use of non-UV curing silicone surface control agent is excellent in erasing of the text, but after erasing the text with an aqueous pen eraser, the writing trace appears on the surface of the writing board. You will not be able to expect continuity. Therefore, it is preferable to use a UV curing surface control agent.
그리고, 경화제로서는 자외선을 흡수하여 자유 라디칼을 생성하는 광개시제를 사용한다. 이러한 자유 라디칼이 반응을 개시하며 광개시제의 함량이 낮아지면 부착력은 좋아지나 표면의 건조가 늦어져 잉크 지움성이 떨어지며, 함량이 높아지면 표면 건조성이 빨라 지움성은 좋아지나 폴리에틸렌 테레프탈레이트(PET) 필름(100) 기재와의 부착이 떨어진다.And as a hardening | curing agent, the photoinitiator which absorbs an ultraviolet-ray and produces | generates a free radical is used. The free radicals initiate the reaction and the lower the content of the photoinitiator, the better the adhesion, but the lower the dryness of the surface, the lower the ink eraseability, and the higher the content, the faster the surface dryability, the better the eraseability, but the polyethylene terephthalate (PET) film (100) Adhesion with a base material falls.
본 발명은 소광제를 포함하여, UV경화형 실리콘 표면조절제를 첨가하여 이루어진 UV 경화형 조성물에 관한 것이다. 이 조성물은 6관능기 이상의 올리고머에 1 내지 3관능기의 올리고머를 첨가하여 이루어지고, 사용된 소광제가 수성펜의 지움성에 영향을 주지 않으며, 실리콘 표면조절제는 폴리에틸렌 테레프탈레이트(PET) 필름(100) 기재와의 부착력 및 필기성에 영향을 주지 않는 범위의 0.2~1.5%를 사용하였다.The present invention relates to a UV curable composition made by adding a UV curing silicone surface control agent, including a matting agent. The composition is made by adding oligomers of 1 to 3 functional groups to oligomers of 6 or more functional groups, the quencher used does not affect the eraseability of the aqueous pen, and the silicone surface modifier with the polyethylene terephthalate (PET)
본 발명에 의한 UV 경화형 조성물을 기재인 폴리에틸렌 테레프탈레이트(PET) 필름(100) 위에 도포하는 코팅 방법은 그라비아(gravure), 마이크로 그라비 아(micro gravure), 콤마(cimma), 에어나이프(air nife), 롤 코팅(roll coating) 방법 등이 있으며 코팅층(200)의 두께나 조성물의 점도 상태에 따라 코팅 방법은 임의로 선정할 수 있다.The coating method of applying the UV curable composition according to the present invention on a polyethylene terephthalate (PET)
코팅층(200)의 두께는 3~40㎛가 적당하며 더욱 바람직하게는 5~30㎛가 좋다. 3㎛이하에서는 충분한 무광도를 내기 어렵고 40㎛ 이상에서는 코팅층(200)의 두께로 인하여 부착력 저하 및 컬(curl) 현상을 발생시키게 된다.The thickness of the
폴리에틸렌 테레프탈레이트(PET) 필름(100)의 하면에는 재박리(removal)가 가능한 아크릴 코 폴리머 점착제를 처리하여 점착층(300)을 형성시켜 쉽게 붙이고 뗄 수 있도록 되어 있으며, 점착층(300)의 두께는 20~25㎛ 정도가 적당하다. 상기 점착층(300)을 보호하기 위해 이형지(400)를 부착하며, 상기 이형지(400) 상면에는 엠보(embo) 무늬(410)를 가공하여 형성시킨다. 여기에서 엠보 무늬(410)는 PE 재질로 형성되며, 엠보 무늬(410)가 형성된 롤을 이형지(400)에 라미네이션시켜 이형지(400) 상면에 엠보(embo) 무늬(410)가 형성되도록 한다.The lower surface of the polyethylene terephthalate (PET)
도 2는 이형지(400) 상면에 형성된 육각형 형상의 엠보 무늬(410)에 대한 일실시예를 도시하였으며, 폴리에틸렌 테레프탈레이트 필름(100)과의 이형지(400)와의 접착시 엠보 무늬(410)가 필름 하면에 일부 투영되어, 폴리에틸렌 테레프탈레이트 필름(100)을 점착 대상물(10)에 점착시 점착 대상물(10)과의 사이에 발생하는 기포의 발생을 억제하여 표면이 매끄럽고 우수한 품질의 필기보드를 제조할 수 있도록 한 것이다.Figure 2 shows an embodiment for the hexagonal
이하에서는 본 발명의 바람직한 실시예와 그에 대한 비교예를 나타내었으며, 이러한 실시예 및 비교예에 대한 물성을 측정하였다. 아래의 조성을 가지는 UV경화형 조성물은 어플리케이터를 이용하여 170㎛ 두께의 폴리에틸렌 테레프탈레이트 필름(100) 상면에 도포하고 80℃에서 1분간 건조 후 자외선 조사장치에서 UV경화를 실시하였으며, 코팅층(200)의 두께는 25㎛를 유지하였다. 실시예에 따라 제조된 UV경화형 조성물을 이용하여 필기보드를 제작하였으며, 이에 대한 물성은 표 1에 나타내었다. 여기에서는 화이트 색상의 화이트보드를 제작하였다. 그리고 각 조성물 간의 분산성을 좋게 하기 위하여 분산제를 더 첨가하였다.Hereinafter, preferred examples of the present invention and comparative examples thereof are shown, and physical properties of the examples and the comparative examples were measured. The UV-curable composition having the following composition was applied to the upper surface of the
<< 실시예Example 1> 1>
CaCO3(무기소광제) 10중량%CaCO 3 (Inorganic quencher) 10% by weight
CERAFLOUR 995(왁스소광제) 5중량%5% by weight of CERAFLOUR 995 (wax quencher)
6관능기 올리고머 SU522 61중량%6 functional group oligomer SU522 61% by weight
3관능기 올리고머 SU5260 6중량%Trifunctional oligomer SU5260 6% by weight
1,6-헥산디올 디아크릴레이트(모노머) 10중량%10% by weight of 1,6-hexanediol diacrylate (monomer)
RAD 2250(표면슬립제) 1중량%RAD 2250 (surface slipper) 1% by weight
Chivacure 184(경화제) 6중량%Chivacure 184 (hardener) 6% by weight
BYK 168(분산제) 1중량%BYK 168 (dispersant) 1% by weight
<< 실시예Example 2> 2>
WN 1135(왁스소광제) 5중량%5 wt% of WN 1135 (wax quencher)
PMMA powder(유기소광제) 5중량%PMMA powder 5% by weight
6관능기 올리고머 SU571 64중량%64% by weight of 6 functional group oligomer SU571
3관능기 올리고머 SU594 6중량%Trifunctional oligomer SU594 6% by weight
2-하이드록시 프로필 아크릴레이트(모노머) 13중량%13% by weight of 2-hydroxypropyl acrylate (monomer)
UV 3500(표면슬립제) 1중량%UV 3500 (surface slipper) 1% by weight
Chivacure 184(경화제) 5중량%5% by weight of Chivacure 184 (hardener)
BYK 168(분산제) 1중량%BYK 168 (dispersant) 1% by weight
<< 실시예Example 3> 3>
CAB-O-SIL TS-610(무기소광제) 5중량%CAB-O-SIL TS-610 (Inorganic quencher) 5% by weight
WN 1135(유기소광제) 5중량%5 wt% of WN 1135 (organic quencher)
6관능기 올리고머 SU522B 60중량%6 functional group oligomer SU522B 60% by weight
3관능기 올리고머 SU564 7중량%Trifunctional oligomer SU564 7% by weight
이소보닐 아크릴레이트(모노머) 16중량%16% by weight of isobornyl acrylate (monomer)
UV 3500(표면슬립제) 0.5중량%UV 3500 (Surface Slipper) 0.5% by weight
UV 3510(표면슬립제) 0.5중량%UV 3510 (Surface Slipper) 0.5% by weight
Chivacure 184(경화제) 5중량%5% by weight of Chivacure 184 (hardener)
BYK 168(분산제) 1중량%BYK 168 (dispersant) 1% by weight
<< 실시예Example 4> 4>
Dusil WM 1200(무기소광제) 5중량%Dusil WM 1200 (Inorganic quencher) 5% by weight
WN 1000(왁스소광제) 5중량%5 wt% of WN 1000 (wax quencher)
6관능기 올리고머 SU522 62중량%6 functional group oligomer SU522 62% by weight
3관능기 올리고머 SU564 6중량%Trifunctional oligomer SU564 6% by weight
트리메틸올 프로판 트리아크릴레이트(모노머) 15중량%15% by weight of trimethylol propane triacrylate (monomer)
RAD 2500(표면슬립제) 1중량%1 weight% of RAD 2500 (surface slip agent)
Chivacure 184(경화제) 5중량%5% by weight of Chivacure 184 (hardener)
BYK 168(분산제) 1중량%BYK 168 (dispersant) 1% by weight
<비교예 1>Comparative Example 1
CaCO3(무기소광제) 10중량%CaCO3 (inorganic quencher) 10% by weight
WN 1135(왁스소광제) 5중량%5 wt% of WN 1135 (wax quencher)
9관능기 올리고머 SU5039 63중량%9 functional group oligomer SU5039 63% by weight
1,6-헥산디올 디아크릴레이트(모노머) 15중량%15% by weight of 1,6-hexanediol diacrylate (monomer)
RAD 2500(표면슬립제) 1중량%1 weight% of RAD 2500 (surface slip agent)
Chivacure 184(경화제) 5중량%5% by weight of Chivacure 184 (hardener)
BYK 168(분산제) 1중량%BYK 168 (dispersant) 1% by weight
<비교예 2>Comparative Example 2
E 220A(무기소광제) 5중량%E 220A (Inorganic quencher) 5% by weight
6관능기 올리고머 SU522 70중량%70 wt% of 6 functional group oligomer SU522
3관능기 올리고머 SU5260 7중량%Trifunctional oligomer SU5260 7% by weight
1,6-헥산디올디 아크릴레이트(모노머) 10중량%10% by weight of 1,6-hexanediol diacrylate (monomer)
RAD 2500(표면슬립제) 1중량%1 weight% of RAD 2500 (surface slip agent)
Chivacure 184(경화제) 6중량%Chivacure 184 (hardener) 6% by weight
BYK 168(분산제) 1중량%BYK 168 (dispersant) 1% by weight
<비교예 3>Comparative Example 3
CaCO3(무기소광제) 10중량%CaCO 3 (Inorganic quencher) 10% by weight
WN 1000(왁스소광제) 5중량%5 wt% of WN 1000 (wax quencher)
6관능기 올리고머 SU522 60중량%6 functional group oligomer SU522 60% by weight
3관능기 올리고머 SU564 7중량%Trifunctional oligomer SU564 7% by weight
트리메틸올 프로판 아크릴레이트(모노머) 10중량%10% by weight of trimethylol propane acrylate (monomer)
RAD 2500(표면슬립제) 2중량%2% by weight of RAD 2500 (surface slip agent)
Chivacure 184(경화제) 5중량%5% by weight of Chivacure 184 (hardener)
BYK 168(분산제) 1중량%BYK 168 (dispersant) 1% by weight
하기의 실시예에 있어 제조된 필름의 물성 평가는 아래와 같은 방법으로 실시하였다.Evaluation of physical properties of the film produced in the following Examples was carried out by the following method.
1)경도계1) Hardness meter
연필경도계(Mitsubishi pencil, 750g)를 사용하여 표면 경도를 측정하였다.Surface hardness was measured using a pencil hardness meter (Mitsubishi pencil, 750g).
2)내용제성2) solvent resistance
이소프로필 알콜, 톨루엔, 아세톤에 24시간 침적시킨 후 도막의 물성을 관찰하였다.After immersion in isopropyl alcohol, toluene, acetone for 24 hours, the physical properties of the coating film were observed.
3)필기성3) Handwriting
수성펜으로 필기를 한 다음 1시간 방치 후 글씨의 상태를 관찰하였다.After writing with a water-based pen, left for 1 hour, the state of the writing was observed.
4)지움성4) Erase
수성펜으로 필기를 한 후 7일 후에 수성펜 지우개로 지울 때 깨끗이 지워지는가를 판단하였다.After 7 days of writing with a water-based pen, it was judged whether it was erased with a water-based pen eraser after 7 days.
5)표면상태5) Surface condition
화이트보드 표면 상태의 curl 여부를 관찰하였다.The curl of the whiteboard surface state was observed.
6)부착력6) adhesion
화이트보드 표면에 셀로판테이프를 부착한 후 박리를 시킬 때 표면을 확인한 후 코팅층에 대한 양호, 불량으로 판단하였다.After attaching the cellophane tape to the surface of the whiteboard, when the surface was peeled off, the surface was checked and judged as good or poor for the coating layer.
7)무광도7) Matte
Sheen사 광택계를 사용하여 표면의 60°광도(glossiness)를 측정하였다.60 ° glossiness of the surface was measured using a Sheen glossmeter.
<표 1>TABLE 1
상기 표 1에서 나타낸 바와 같이, 비교예 1에서와 같이 6관능기 이상의 올리고머만을 바인더로 사용하였을 경우에는 화이트보드 표면의 지움성은 증가하는 반면 기재인 폴리에틸렌 테레프탈레이트(PET) 필름의 컬(curl) 현상으로 인하여 제품화할 수 없으며, 비교예 2에서와 같이 6관능기 이하의 관능기를 주로 사용하면 유연한 물성으로 인하여 컬(curl) 현상이 없어지고 편평도는 우수하였으나 수성펜 지우개로 필기보드 표면을 지울 때 지움성이 현저히 떨어지는 결과가 나왔다.As shown in Table 1, when only oligomers having 6 or more functional groups were used as the binders as in Comparative Example 1, the eraseability of the surface of the whiteboard was increased while the curl phenomenon of the polyethylene terephthalate (PET) film as a substrate was increased. Due to the flexible properties, curling is eliminated and flatness is excellent, but the eraseability is remarkably clear when the surface of the writing board is erased with an aqueous pen eraser. The falling result came out.
그리고, 비교예 3에서와 같이 UV경화형 실리콘 표면조절제의 첨가량을 많이 하였을 경우에는 폴리에틸렌 테레프탈레이트(PET) 기재와 코팅층(200)의 부착력이 떨어지는 것을 확인할 수 있었고 필기성 또한 떨어졌었다.In addition, when a large amount of the UV-curable silicone surface control agent was added, as in Comparative Example 3, it was confirmed that the adhesion of the polyethylene terephthalate (PET) substrate and the
따라서, 본 발명을 바람직하게 실시하기 위해서는 유, 무기, 왁스소광제를 적절한 량으로 혼합하여 사용하고, 6관능기의 올리고머에 대해 1~3관능기의 올리고머의 량을 적절하게 사용하며, 사용된 소광제가 수성펜의 지움성에 영향을 주지 않도록 하고, UV경화형 실리콘 표면조절제는 폴리에틸렌 테레프탈레이트(PET) 필름 기재와의 부착력 및 필기성에 영향을 주지 않는 범위를 사용하여야 한다.Therefore, in order to implement the present invention preferably, an oil, an inorganic, and a wax quencher are mixed and used in an appropriate amount, and an amount of an oligomer of 1 to 3 functional groups is suitably used with respect to the oligomer of 6 functional groups. In order not to affect the eraseability of the water-based pen, the UV-curable silicone surface modifier should be used in a range that does not affect the adhesion and handwriting with the polyethylene terephthalate (PET) film substrate.
상기 구성에 의한 본 발명은, UV경화형 조성물을 폴리에틸렌 테레프탈레이트 필름에 코팅한 후 UV를 조사하여 필기보드용 무광 필름을 제조할 수 있으며, 상기 필기보드용 무광 필름의 표면은 형광등에 의한 불빛 반사가 극히 적어 눈부심이 없을 뿐만 아니라 필기성 및 내용제성, 내스크래치성이 우수하고 수성펜 지우개로 글씨나 그림을 지울 때 지움성이 뛰어난 효과가 있다.According to the present invention, the UV curable composition is coated on a polyethylene terephthalate film and then irradiated with UV to produce a matting film for writing board, and the surface of the matting film for writing board is light reflective by fluorescent lamps. It has very little glare and is excellent in writing, solvent resistance, scratch resistance, and erasing effect when erasing letters and pictures with a water-based pen eraser.
또한, 필기보드용 무광 필름의 뒷면은 여러 가지 색깔의 안료가 첨가된, 재박리가 가능한 점착층을 형성시켜 눈의 피로감을 완화시키고, 쉽게 붙이고 뗄 수 있어 사용의 편리성을 강화한 효과가 있다.In addition, the back surface of the matte film for writing board to form a re-peelable adhesive layer is added to a variety of pigments, relieve eye fatigue, can be easily attached and detached has the effect of enhancing the ease of use.
또한, 필기보드용 무광 필름의 점착층 하면에는 점착층을 보호하고 상면에 엠보 무늬가 형성된 이형지를 부착시켜, 필기보드용 무광 필름을 점착 대상물에 점착시 필기보드용 무광 필름과 점착 대상물 사이에 발생하는 기포의 발생을 억제하 여 표면이 매끄럽고 우수한 품질의 필기보드를 제공할 수 있는 효과가 있다.In addition, the adhesive layer on the bottom of the adhesive film for writing board protects the adhesive layer and attaches a release paper having an embossed pattern on the upper surface, and is generated between the writing board matting film and the adhesive object when the writing board is adhered to the adhesive object. By suppressing the occurrence of bubbles, the surface is smooth and has the effect of providing a writing board of excellent quality.
Claims (12)