KR100718441B1 - Antimicrobial flocking binder and process of flocking using thereof - Google Patents

Antimicrobial flocking binder and process of flocking using thereof Download PDF

Info

Publication number
KR100718441B1
KR100718441B1 KR1020060060259A KR20060060259A KR100718441B1 KR 100718441 B1 KR100718441 B1 KR 100718441B1 KR 1020060060259 A KR1020060060259 A KR 1020060060259A KR 20060060259 A KR20060060259 A KR 20060060259A KR 100718441 B1 KR100718441 B1 KR 100718441B1
Authority
KR
South Korea
Prior art keywords
flocking
weight
binder
antimicrobial
trichloro
Prior art date
Application number
KR1020060060259A
Other languages
Korean (ko)
Inventor
박성민
이기풍
김숙진
문두환
Original Assignee
한국염색기술연구소
갑을합섬(주)
손병철
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한국염색기술연구소, 갑을합섬(주), 손병철 filed Critical 한국염색기술연구소
Priority to KR1020060060259A priority Critical patent/KR100718441B1/en
Application granted granted Critical
Publication of KR100718441B1 publication Critical patent/KR100718441B1/en

Abstract

본 발명은 플로킹용 항균바인더 및 이를 이용한 플로킹방법에 관한 것으로서, 보다 상세하게는 아크릴레이트계 모노머 22~40 중량%, 아크릴산 1~3중량%, 계면활성제 1.9~5 중량%, 촉매 0.1~2 중량% 및 물 50~75중량%를 유화중합하여 얻은 바인더 90 ~ 95 중량%와 항균제로써 하기 화학식 1의 2,4,4-트리클로로-2-하이드록시디페닐 이써( 2,4,4-trichloro-2-hydroxydiphenyl ether)를 함유하는 유화액 5~10중량%를 포함하는 것을 특징으로 하는 플로킹용 항균바인더에 관한 것이다. 본 발명에 의해 외관이나 촉감이 개선될 뿐만 아니라 우수한 항균성을 가지는 고품질의 플로킹 제품을 제공할 수 있다.The present invention relates to a antibacterial binder for flocking and a flocking method using the same, and more specifically, 22 to 40% by weight of acrylate monomer, 1 to 3% by weight of acrylic acid, 1.9 to 5% by weight of surfactant, and 0.1 to 2% by weight of catalyst. % And 50 to 75% by weight of the binder 90-95% by weight of the binder obtained by the emulsion polymerization and 2,4,4-trichloro-2-hydroxydiphenyl ether of the formula (1) as an antibacterial agent (2,4,4-trichloro It relates to an antimicrobial binder for flocking comprising 5 to 10% by weight of an emulsion containing 2-hydroxydiphenyl ether). The present invention can provide a high quality flocking product having not only an appearance and feel but also excellent antibacterial properties.

플로킹, 항균성 Flocking, Antimicrobial

Description

플로킹용 항균바인더 및 이를 이용한 플로킹방법{Antimicrobial flocking binder and Process of Flocking using thereof} Antimicrobial binder for flocking and flocking method using the same

도 1은 본 발명의 플로킹용 항균바인더를 이용하여 제조된 플로킹제품의 KS K 0693 - 2001에 의한 직물의 항균성 시험 성적서의 사진이다.1 is a photograph of the antimicrobial test report of the fabric according to KS K 0693-2001 of the flocking product manufactured using the antibacterial binder for flocking of the present invention.

본 발명은 플로킹용 항균바인더 및 이를 이용한 플로킹방법에 관한 것으로서, 외관이나 촉감을 개선할 뿐만 아니라 항균성을 가지는 고품질의 플로킹 제품을 제조하기 위한 플로킹용 항균바인더에 관한 것이다.The present invention relates to an antibacterial binder for flocking and a method of flocking using the same, and relates to an antibacterial binder for flocking to produce a high quality flocking product having antibacterial properties as well as improving appearance and feel.

플로킹(Flocking) 가공은 면, 레이온, 기타 화학섬유를 일정한 길이로 짧게 절단한 파일을 접착제를 입힌 직물 표면 위에 전기적으로 고정시켜 인조가죽과 같은 효과를 주는 공정이다. 따라서 직물 위에 부착된 파일과의 사이에 공기층이 생겨 부드러운 촉감 및 유연한 외관뿐만 아니라 보온, 방음의 기능적 특성을 가지고 있으며, 주용도는 의류제품, 운동화, 카펫, 의자 커버, 벽지 등 인테리어용, 자동차 내부, 가구 및 포장재에서부터 전기제품, 기계류까지 다양하게 적용되고 있다. 이러한 플로킹 가공에 의한 제품은 촉감, 유연한 외관, 보온성 및 방음성이 우수한 장점을 가지고 있으나, 플로킹제품의 특성상 세탁이 불가능하여, 각종 미생물이나, 진드기의 서식처가 될 수 있어 위생상의 문제점을 가지고 있다.Flocking is a process in which cotton, rayon, and other chemical fibers are shortened to a certain length and electrically fixed on an adhesive fabric surface to give them the effect of artificial leather. Therefore, the air layer is formed between the pile attached to the fabric, so it has not only soft touch and flexible appearance but also functional properties of heat insulation and sound insulation.The main uses are for interior goods such as clothing products, sneakers, carpets, chair covers, wallpaper, interior of cars, It is applied in various ways from furniture and packaging materials to electrical appliances and machinery. The product by the flocking process has the advantages of excellent touch, flexible appearance, warmth and sound insulation, but because of the nature of the flocking product can not be washed, it can be a habitat for a variety of microorganisms and ticks have a hygienic problem.

이러한 미생물에 대한 플로킹제품의 저항력은 종류에 따라 약간의 차이는 있지만, 일반적으로 제품 표면에 번식하는 미생물을 제거하거나 발생을 억제하기 위하여 과산화수소, 이산화염소, 칼슘이온, 알콜스프레이 등의 살균제가 현재까지 주로 사용되어 왔다. 그러나 이와 같은 기존 살균제는 효과는 우수하지만 잘못 사용할 경우에는 인체에 피해를 입히거나, 그 효과가 지속적이지 못한 것이 단점으로 지적되어 왔다. The resistance of flocking products to these microorganisms varies slightly depending on the type, but generally, disinfectants such as hydrogen peroxide, chlorine dioxide, calcium ions and alcohol sprays have been used to remove or suppress microorganisms that propagate on the surface of products. Mainly used. However, such conventional fungicides have excellent effects, but have been pointed out that if used incorrectly, they cause damage to the human body or the effect is not sustained.

플로킹 제품에 번식하는 미생물의 오염을 궁극적으로 제거하고 살균제를 사용함으로서 야기되는 기존 살균방법의 단점을 개선할 수 있는 방법으로는 파일섬유를 항균성을 가지는 합성섬유를 사용하는 것도 한 방법이 될 수 있으나, 부분적인 항균성능만을 가질 뿐 플로킹 제품에서는 파일섬유와 기재의 접촉부위에는 항균성을 부여하기가 어려운 점이 있었다.One way to improve the shortcomings of the existing sterilization methods caused by ultimately removing the contamination of the microorganisms propagated in the flocking product and using a disinfectant may be to use synthetic fibers having antimicrobial properties. In the case of flocking products, it was difficult to give antimicrobial properties to the contact area between the pile fiber and the substrate.

플로킹 제품의 제조에 있어서는 바인더에 항균제를 첨가하는 것이 항균성 부여에 효과적인데, 상기 항균제로는 크게 유기계항균제 및 무기계항균제가 사용될 수 있다. In the manufacture of flocking products, adding an antimicrobial agent to the binder is effective for imparting antimicrobial activity. As the antimicrobial agent, organic antimicrobial agents and inorganic antimicrobial agents may be used.

유기계 항균제는 무기계 항균에 비하여 비교적 가공이 쉽고 최종 제품의 기계적 물성, 투명도, 색상 등에 큰 영향을 끼치지 않는다는 점에서 현재까지 많이 사용되어 왔으나, 유기계 항균제는 제품 표면으로 약제가 비교적 쉽게 용출되므로 일시적 효력은 뛰어나지만 효능의 지속성이 결여되고, 특히 내열성이 열등하다는 점에서 문제점을 가진다. 유기계 항균제 중에는 피부자극성, 등의 문제를 일으키는 것도 있다. 또 장기적으로 사용하면 내성균이 발생될 수 있으며 폐기물에서 다이옥신이 생성된다는 보고도 있다. 현재 사용되는 유기계 항균제로는 유기수은 화합물, 유기크롬산 구리화합물, 유기구리 화합물, 유기아연 화합물, 염소페닐에테르계, 유기질소계 화합물, 유기실리콘 제4급 암모늄 등으로 대별된다.Organic antimicrobials have been used to date because they are relatively easy to process and do not significantly affect the mechanical properties, transparency, or color of the final product. Is excellent but lacks the persistence of efficacy, and particularly has a problem in that heat resistance is inferior. Some organic antimicrobial agents cause skin irritation and the like. Long-term use may result in resistant bacteria and dioxin is produced in the waste. Organic antimicrobial agents currently used include organic mercury compounds, copper organic chromium compounds, organic copper compounds, organic zinc compounds, chlorine phenyl ethers, organic nitrogen compounds, and organosilicon quaternary ammonium.

이들 가운데 유기금속 화합물은 전체적으로 살균성이 강하지만 유기수은 화합물, 유기크롬산 구리화합물 등은 독성이 크기 때문에 사용이 금지되어 왔다. 따라서 현재 일반적으로 많이 쓰이는 유기계 항균제는 염소페닐 에테르계, 유기실리콘 제4급 암모늄염계, 유기질소계화합물, 브로모시안알데하이드(bromocinnaldehyde)와 피리미딘(pyrimidine)계를 병용한 제품, 양이온 활성을 가진 유기실린 화합물 등인데, 이러한 유기계 항균제는 독성이 있어 안정성에 문제점을 가지고 있다. Of these, organometallic compounds are generally sterilizable, but organic mercury compounds and organochromate copper compounds are toxic, and thus their use is prohibited. Therefore, currently used organic antimicrobial agents are commonly used chlorine phenyl ether, organosilicon quaternary ammonium salts, organic nitrogen-based compounds, bromocinnaldehyde and pyrimidine-based products, organic having a cationic activity Although it is a silin compound, such an organic antimicrobial agent is toxic and has a problem in stability.

무기계 항균제는 제오라이트, 실리카알루미나 등의 무기담체에 은, 구리, 아연 등과 같이 항균성이 뛰어난 금속이온을 치환시킨 것을 사용하고 있는데, 이는 미세한 기공을 가진 3차원의 골격구조를 지니기 때문에 비표면적이 크고 내열성이 우수하다. 무기계 항균제는 종래의 유기계 항균제와 비교하여 내열성이 높고 휘발, 분해 등을 일으키지 않는 등 안정성이 높기 때문에 넓은 용도로 응용할 수 있다. 무기계 항균제의 항균효과는 활성산소이온에 의해 발현되기 때문에 유기계 항균제에는 볼 수 없는 뛰어난 장점을 많이 가지고 있다. 예를 들면 약제의 용출에 의한 즉효성은 없지만 지속성이 길고 내성균을 발생시키지 않는다. 그러나 은, 구리, 아연 등의 금속이온은 수지를 열화시키거나 황변현상을 야기시키고, 수지의 접착력을 약화시켜 상품가치를 현저하게 저하시킬 우려가 있는 문제점이 있다. Inorganic antimicrobial agent is used to substitute metal ions such as silver, copper and zinc with inorganic carriers such as zeolite and silica alumina.They have a three-dimensional skeletal structure with fine pores. This is excellent. Inorganic antimicrobial agents have high heat resistance compared to conventional organic antimicrobial agents and have high stability, such as not causing volatilization or decomposition, and thus can be applied to a wide range of applications. Since the antimicrobial effect of the inorganic antimicrobial agent is expressed by active oxygen ions, it has many excellent advantages not found in the organic antimicrobial agent. For example, there is no immediate effect by dissolution of the drug, but it is long lasting and does not generate resistant bacteria. However, metal ions such as silver, copper, and zinc have a problem of deteriorating the resin or causing yellowing, weakening the adhesive strength of the resin, and significantly lowering the product value.

그러므로 본 발명에 의하면, 상기 종래기술의 문제점을 해결하여 외관이나 촉감을 개선할 뿐만 아니라 항균성을 가지는 고품질의 플로킹 제품을 제공하는 것을 기술적 과제로 한다.Therefore, according to the present invention, to solve the problems of the prior art to improve the appearance and feel, as well as to provide a high-quality flocking product having antibacterial as a technical problem.

본 발명자는 상기 기술적 과제를 해결하기 위하여 본 발명의 항균제를 바인더에 함유시켜 플로킹 작업을 하게 되면 플로킹 제품의 고유 물성을 저하시키지 않고도 높은 항균성을 부여할 수 있다는 것을 알게 되어 본 발명을 완성하게 된 것이다.In order to solve the above technical problem, the present inventors have realized that the antimicrobial agent of the present invention can be incorporated into a binder to achieve high antimicrobial properties without reducing the inherent physical properties of the flocking product. .

그러므로 본 발명에 의하면, 아크릴레이트계 모노머 22~40 중량%, 아크릴산 1~3중량%, 계면활성제 1.9~5 중량%, 촉매 0.1~2 중량% 및 물 50~75중량%를 유화중합하여 얻은 바인더 90 ~ 95 중량%와 항균제로써 하기 화학식 1의 2,4,4-트리클로로-2-하이드록시디페닐 이써( 2,4,4-trichloro-2-hydroxydiphenyl ether)를 함유하는 유화액 5~10중량%를 포함하는 것을 특징으로 하는 플로킹용 항균바인더가 제공된다.Therefore, according to the present invention, a binder obtained by emulsion polymerization of 22 to 40% by weight of acrylate monomer, 1 to 3% by weight of acrylic acid, 1.9 to 5% by weight of surfactant, 0.1 to 2% by weight of catalyst and 50 to 75% by weight of water 5 to 10 weight percent emulsion containing 90 to 95 weight% and 2,4,4-trichloro-2-hydroxydiphenyl ether of formula 1 Flocking antimicrobial binder, characterized in that it comprises a% is provided.

[화학식 1][Formula 1]

Figure 112006047050792-pat00001
Figure 112006047050792-pat00001

본 발명의 플로킹용 항균바인더의 상기 유화액은 화학식 1의 2,4,4-트리클로로-2-하이드록시디페닐 이써( 2,4,4-trichloro-2-hydroxydiphenyl ether) 0.1~2중량%, 유화제 4.9~13중량% 및 접착제 85~95중량%로 이루어진 것을 특징으로 한다.The emulsion of the antibacterial binder for flocking of the present invention is 0.1 to 2% by weight of 2,4,4-trichloro-2-hydroxydiphenyl ether (2,4,4-trichloro-2-hydroxydiphenyl ether) of Formula 1, It is characterized by consisting of 4.9 to 13% by weight of the emulsifier and 85 to 95% by weight of the adhesive.

또한, 본 발명에 의하면, a) 부직포 또는 직물로 이루어진 기재상에 상기 제 1항 또는 제 2항 기재의 플로킹용 항균바인더를 도포하는 공정, b) 상기 바인더가 도포된 기재상에 직류의 고압전기를 이용하여 파일섬유를 부착시키고 컷팅한 후 텐터에 의해 건조시키는 플로킹 공정, c) 상기 플로킹 공정에 의한 플로킹 원단의 접착성 및 표면질감을 개선하기 위한 캘린더링 공정, d) 상기 캘린더링 공정 후, 건조, 열처리 및 브러싱공정을 포함하는 것을 특징으로 하는 플로킹 방법이 제공된다.In addition, according to the present invention, a) a step of applying the antimicrobial binder for flocking according to claim 1 or 2 on a substrate made of a non-woven fabric or fabric, b) a direct current high voltage Flocking step of attaching and cutting the pile fiber using a tenter and then dried by a tenter, c) Calendering process for improving the adhesion and surface texture of the flocking fabric by the flocking process, d) After the calendering process, A flocking method is provided comprising a drying, heat treatment and brushing process.

또한, 본 발명의 플로킹 방법에서는 상기 c)캘린더링 공정 후 제2차 항균바인더를 도포하고 제2차 플로킹공정을 더 행할 수 있다.In addition, in the flocking method of the present invention, after the c) calendaring step, the second antibacterial binder may be applied and the second flocking step may be further performed.

이하, 본 발명을 보다 상세히 설명하기로 한다.Hereinafter, the present invention will be described in more detail.

본 발명의 플로킹용 항균바인더는 플로킹 공정에서 기재상에 직류의 고압전 기를 이용하여 파일섬유를 부착하기 위하여 사용되는 것으로서, 바인더와 항균제를 함유하는 유화액을 포함하여 이루어진다.The antimicrobial binder for flocking of the present invention is used to attach a pile fiber by using a high pressure electric current of DC on a substrate in a flocking process, and comprises an emulsion containing a binder and an antimicrobial agent.

본 발명의 플로킹용 항균바인더의 항균제는 하기 화학식 1의 2,4,4-트리클로로-2-하이드록시디페닐 이써( 2,4,4-trichloro-2-hydroxydiphenyl ether)로서 유화액에 포함되어 바인더와 혼합된다.The antimicrobial agent of the antimicrobial binder for flocking of the present invention is contained in an emulsion as 2,4,4-trichloro-2-hydroxydiphenyl ether (2,4,4-trichloro-2-hydroxydiphenyl ether) of Chemical Formula 1 Mixed with

[화학식 1][Formula 1]

Figure 112006047050792-pat00002
Figure 112006047050792-pat00002

상기 유화액은 화학식 1의 2,4,4-트리클로로-2-하이드록시디페닐 이써( 2,4,4-trichloro-2-hydroxydiphenyl ether) 0.1~2중량%, 유화제 4.9~13중량% 및 접착제 85~95중량%로 이루어지는 것이 바람직하다. 상기 접착제는 아크릴바인더를 사용하는 것이 바람직하며, 유화제는 분자량 30~500인 알킬폴리에틸렌옥사이드와 같은 비이온계면활성제가 바람직하다.The emulsion is 0.1 to 2% by weight of 2,4,4-trichloro-2-hydroxydiphenyl ether (2,4,4-trichloro-2-hydroxydiphenyl ether) of Formula 1, 4.9 to 13% by weight of the emulsifier and adhesive It is preferable that it consists of 85 to 95 weight%. It is preferable to use an acrylic binder for the adhesive, and an emulsifier is preferably a nonionic surfactant such as alkyl polyethylene oxide having a molecular weight of 30 to 500.

상기 2,4,4-트리클로로-2-하이드록시디페닐 이써( 2,4,4-trichloro-2-hydroxydiphenyl ether)는 우수한 항균력을 가져 상기 접착제 및 유화제와 함께 유화액상태로 만들어 사용하게 되면 바인더와 잘 혼합되어 플로킹 공정에서 우수한 항균 효과를 가지면서 접착성이 좋고 유연한 플로킹 제품을 제조할 수 있게 된다.The 2,4,4-trichloro-2-hydroxydiphenyl ether (2,4,4-trichloro-2-hydroxydiphenyl ether) has excellent antimicrobial activity and is used as a binder when the emulsion is used together with the adhesive and the emulsifier. It can be mixed well with and have an excellent antimicrobial effect in the flocking process and can produce an adhesive good and flexible flocking product.

상기 2,4,4-트리클로로-2-하이드록시디페닐 이써(2,4,4-trichloro-2-hydroxydiphenyl ether)를 함유하는 유화액은 전체 플로킹용 바인더의 5~10중량% 포함되는 것이 바람직한데, 5중량%미만인 경우에는 항균효과가 저하되며, 10중량%를 초과하는 경우에는 바인더의 접착력을 저하시키는 문제점이 있다.The emulsion containing 2,4,4-trichloro-2-hydroxydiphenyl ether (2,4,4-trichloro-2-hydroxydiphenyl ether) is preferably contained 5 to 10% by weight of the total flocking binder. However, when less than 5% by weight, the antimicrobial effect is lowered, and when it exceeds 10% by weight, there is a problem of lowering the adhesive strength of the binder.

본 발명의 바인더는 아크릴레이트계 모노머, 아크릴산, 계면활성제, 촉매 및 물을 중합하여 형성되는데, 아크릴레이트계 모노머 22~40 중량%, 아크릴산 1~3중량%, 계면활성제 1.9~5 중량%, 촉매 0.1~2 중량% 및 물 50~75중량%를 혼합, 분산시켜 유화중합하여 바인더를 얻게 된다.The binder of the present invention is formed by polymerizing an acrylate monomer, acrylic acid, a surfactant, a catalyst, and water, and 22 to 40 wt% of an acrylate monomer, 1 to 3 wt% of an acrylic acid, 1.9 to 5 wt% of a surfactant, and a catalyst. 0.1-2 wt% and 50-75 wt% of water are mixed and dispersed to emulsify to obtain a binder.

상기 아크릴레이트계 모노머는 메틸아크릴레이트, 에틸아크릴레이트, 부틸아크릴레이트, N-메틸아크릴레이트 및 메틸메타아크릴레이트로 이루어진 군으로부터 선택되는 어느 하나이상의 모노머를 사용하는 것이 바람직하며, 촉매는 암모늄퍼설페이트가 좋으며, 계면활성제는 소디움설포석시네이트와 같은 음이온계 계면활성제가 바람직하다. The acrylate monomer is preferably at least one monomer selected from the group consisting of methyl acrylate, ethyl acrylate, butyl acrylate, N-methyl acrylate and methyl methacrylate, the catalyst is ammonium persulfate The surfactant is preferably an anionic surfactant such as sodium sulfosuccinate.

본 발명의 플로킹용 항균바인더를 사용하여 플로킹제품을 제조하는 방법은 다음과 같다.Method for producing a flocking product using the antibacterial binder for flocking of the present invention is as follows.

a) 부직포 또는 직물로 이루어진 기재상에 상기 제 1항 또는 제 2항 기재의 플로킹용 항균바인더를 도포하는 공정, b) 상기 바인더가 도포된 기재상에 직류의 고압전기를 이용하여 파일섬유를 부착시키고 컷팅한 후 텐터에 의해 건조시키는 플로킹 공정, c) 상기 플로킹 공정에 의한 플로킹 원단의 접착성 및 표면질감을 개선하기 위한 캘린더링 공정, d) 상기 캘린더링 공정 후, 건조, 열처리 및 브러싱공정에 의하여 플로킹제품을 제조할 수 있다. a) applying the antibacterial binder for flocking according to claim 1 or 2 on a substrate made of a nonwoven fabric or fabric; b) attaching pile fibers using direct current high voltage electricity on the binder-coated substrate. After the cutting and drying by a tenter, c) a calendering process for improving the adhesion and surface texture of the flocking fabric by the flocking process, d) after the calendering process, drying, heat treatment and brushing process Flocking products can be produced.

또한, 상기 c)캘린더링 공정 후에 제2차 항균바인더를 도포하고 제2차 플로킹공정을 행할 수 있는데, 이 공정은 필요에 따라 수회반복할 수 있다. In addition, after the c) calendaring process, the second antimicrobial binder may be applied and the second flocking process may be performed. This process may be repeated several times as necessary.

이하 본 발명을 실시예에 의거 상세히 설명하나, 본 발명이 실시예에 의해 한정되는 것은 아니다.Hereinafter, the present invention will be described in detail with reference to Examples, but the present invention is not limited by Examples.

[실시예 1]Example 1

표 1과 같은 비율에 의하여 원료를 배합하여 130℃에서 4시간동안 교반하여 유화중합한 바인더 93g과, 표 2의 2,4,4-트리클로로-2-하이드록시디페닐 이써( 2,4,4-trichloro-2-hydroxydiphenyl ether)를 함유하는 유화액 7g을 호모믹서기로 혼합하여 본 발명의 플로킹용 항균바인더를 제조하였다. The raw materials were mixed according to the ratios shown in Table 1 and stirred for 2 hours at 130 ° C. for 93 g of the binder, and the 2,4,4-trichloro-2-hydroxydiphenyl ether of Table 2 (2,4, 7 g of an emulsion containing 4-trichloro-2-hydroxydiphenyl ether) was mixed with a homomixer to prepare an antibacterial binder for flocking of the present invention.

원료명Raw material name 함량(g)Content (g) 비고Remarks EAMEAM 180180 에틸아크릴레이트 모노머Ethylacrylate monomer BAMBAM 8080 부틸아크릴레이트 모노머Butyl acrylate monomer AACAAC 1515 아크릴산Acrylic acid N-MAMN-MAM 2020 N-메틸아크릴레이트 모노머N-methylacrylate monomer MMAMMA 6060 메틸메타아크릴레이트Methyl methacrylate 계면활성제(음이온)Surfactant (anion) 2525 소디움설포석시네이트Sodium sulfosuccinate 촉매catalyst 2.22.2 암모늄퍼설페이트Ammonium persulfate H2OH 2 O 617.8617.8 총합total 10001000

원료명Raw material name 함량(g)Content (g) 비 고Remarks 2,4,4-트리클로로-2-하이드록시디페닐 이써2,4,4-trichloro-2-hydroxydiphenyl ether 0.50.5 유화제Emulsifier 8.58.5 알킬폴리에틸렌옥사이드Alkyl Polyethylene Oxide 접착제glue 9191 아크릴바인더Acrylic Binder 총합total 100100

실시예 1에 의해 얻어진 플로킹용 항균바인더를 이용하여 나일론 직물로 이루어진 기재상에 2㎜ 두께로 도포하고 그 위에 직류 60Kv의 고압전기를 이용하여 나일론으로 된 파일섬유를 부착시키고 컷팅한 후, 160℃조건의 텐터에 의해 건조시킨 후 캘린더링 공정, 건조한 후, 160℃조건에서 열처리하고 브러싱하여 플로킹제품을 제조하였다.After the antibacterial binder for flocking obtained in Example 1 was applied on a substrate made of nylon fabric with a thickness of 2 mm, the pile fiber made of nylon was attached and cut using a direct-current 60 Kv high voltage electric machine, and then cut to 160 ° C. After drying by a tenter under conditions, calendering process, dried, heat-treated and brushed at 160 ℃ condition to produce a flocking product.

상기 제조된 플로킹제품의 항균성을 시험하기 위해 직물의 항균성 시험방법[KS K 0693-2001]에 준하여 실험하였다. 실험결과 및 측정 조건은 다음과 같으며, 시험결과는 표3 및 도 1에 나타내었다.In order to test the antimicrobial properties of the prepared flocking product was tested in accordance with the antimicrobial test method [KS K 0693-2001]. Experimental results and measurement conditions are as follows, and the test results are shown in Table 3 and FIG. 1.

-시험 방법 : KS K 0693 - 2001, 직물의 항균성 시험방법.-Test method: KS K 0693-2001, Test method for antimicrobial activity of fabrics.

-시험 조건 -Exam conditions

1. 시험균종 :       Test species:

1) 균주Ⅰ - Staphylococcus aureus ATCC 6538 포도상구균1) Strain I- Staphylococcus aureus ATCC 6538 Staphylococcus

2) 균주Ⅱ - Klebsiella pneumoniae ATCC 4352 폐렴균2) Strain II- Klebsiella pneumoniae ATCC 4352 pneumococcal

2. 접종균의 농도 :      2. The concentration of inoculation bacteria:

1) 균주Ⅰ - 1.3×105 개/㎖1) Strain I-1.3 × 10 5 / ml

2) 균주 Ⅱ - 1.1×105 개/㎖2) Strain Ⅱ-1.1 × 10 5 pcs / ml

3. 증가율 :      3. Increase rate:

1) 균주 Ⅰ - 34배 증식1) Strain I-34-fold multiplication

2) 균주 Ⅱ - 36배 증식              2) Strain Ⅱ-36-fold multiplication

4. 비이온 계면활성제 : Tween 80 (0.05%)       4. Nonionic Surfactant: Tween 80 (0.05%)

정균감소율(%) Bacteriostatic reduction rate (%) 균주 ⅠStrain I 균주 ⅡStrain II 99.9%99.9% 99.9%99.9%

도 1은 본 발명의 플로킹용 항균바인더를 이용하여 제조된 플로킹제품의 KS K 0693 - 2001에 의한 직물의 항균성 시험 성적서의 사진이다. 시험결과 포도상 구균 및 폐렴균 모두 정균 감소율이 99.9%를 나타내어 완벽한 항균성을 나타냄을 확인할 수 있었다.1 is a photograph of the antimicrobial test report of the fabric according to KS K 0693-2001 of the flocking product manufactured using the antibacterial binder for flocking of the present invention. As a result of the test, both the Staphylococcus aureus and Pneumococcal bacteria showed a 99.9% bacteriostatic rate, indicating that they exhibited perfect antibacterial activity.

본 발명에 의해 종래의 방법보다 플로킹제품의 외관이나 촉감을 개선할 뿐만 아니라 높은 항균성을 가지는 고품질의 제품을 제공할 수 있었다. According to the present invention, it is possible to provide a high-quality product having a high antibacterial property as well as improving the appearance and feel of the flocking product over the conventional method.

Claims (4)

아크릴레이트계 모노머 22~40 중량%, 아크릴산 1~3중량%, 계면활성제 1.9~5 중량%, 촉매 0.1~2 중량% 및 물 50~75중량%를 유화중합하여 얻은 바인더 90 ~ 95 중량%와 항균제로써 하기 화학식 1의 2,4,4-트리클로로-2-하이드록시디페닐 이써( 2,4,4-trichloro-2-hydroxydiphenyl ether)를 함유하는 유화액 5~10중량%를 포함하는 것을 특징으로 하는 플로킹용 항균바인더.90 to 95% by weight of the binder obtained by emulsion polymerization of 22 to 40% by weight of acrylate monomer, 1 to 3% by weight of acrylic acid, 1.9 to 5% by weight of surfactant, 0.1 to 2% by weight of catalyst and 50 to 75% by weight of water; 5 to 10% by weight of an emulsion containing 2,4,4-trichloro-2-hydroxydiphenyl ether as the antibacterial agent Antibacterial binder for flocking. [화학식 1][Formula 1]
Figure 112006047050792-pat00003
Figure 112006047050792-pat00003
 제 1항에 있어서, 상기 유화액은 화학식 1의 2,4,4-트리클로로-2-하이드록시디페닐 이써( 2,4,4-trichloro-2-hydroxydiphenyl ether) 0.1~2중량%, 유화제 4.9~13중량% 및 접착제 85~95중량%로 이루어진 것을 특징으로 하는 플로킹용 항균바인더.According to claim 1, wherein the emulsion is 2,4,4-trichloro-2-hydroxydiphenyl ether of formula 1 (2,4,4-trichloro-2-hydroxydiphenyl ether) 0.1 to 2% by weight, emulsifier 4.9 Flocking antibacterial binder, characterized in that consisting of ~ 13% by weight and 85 to 95% by weight of the adhesive. a) 부직포 또는 직물로 이루어진 기재상에 상기 제 1항 또는 제 2항 기재의 플로킹용 항균바인더를 도포하는 공정, a) applying the antimicrobial binder for flocking according to claim 1 or 2 on a substrate made of a nonwoven fabric or fabric, b) 상기 바인더가 도포된 기재상에 직류의 고압전기를 이용하여 파일섬유를 부착시키고 컷팅한 후 텐터에 의해 건조시키는 플로킹 공정,b) a flocking process of attaching and cutting pile fibers using direct current high voltage electricity on the binder-coated substrate and drying by tenter; c) 상기 플로킹 공정에 의한 플로킹 원단의 접착성 및 표면질감을 개선하기 위한 캘린더링 공정,c) calendaring process for improving the adhesion and surface texture of the flocking fabric by the flocking process, d) 상기 캘린더링 공정 후, 건조, 열처리 및 브러싱공정을 포함하는 것을 특징으로 하는 플로킹 방법.d) after the calendering process, drying, heat treatment and brushing process comprising a. 제 3항에 있어서, 상기 c)캘린더링 공정 후 제2차 항균바인더를 도포하고 제2차 플로킹공정을 더 행하는 것을 특징으로 하는 플로킹 방법.The flocking method according to claim 3, wherein the c) second antibacterial binder is coated after the calendering step, and the second flocking step is further performed.
KR1020060060259A 2006-06-30 2006-06-30 Antimicrobial flocking binder and process of flocking using thereof KR100718441B1 (en)