KR100700662B1 - Antimicrobial brush of a toothbrush

Info

Publication number: KR100700662B1
Application number: KR1020050119547A
Authority: KR
Inventors: 김경태
Original assignee: 김경태
Priority date: 2005-12-08
Filing date: 2005-12-08
Publication date: 2007-03-28

Abstract

An antimicrobial brush of a toothbrush is provided to restrain bacteria causing a decayed tooth by using sulfadiazine, and to keep the toothbrush in a sanitary way by using chlorhexidine gluconate. The antimicrobial brush of a toothbrush is processed by mixing 1.5-5 weight% of sulfadiazine and 1-3 weight% of chlorhexidine gluconate in 93-97 weight% of raw material resin. The density of the chlorhexidine gluconate is 0.2%. The chlorhexidine gluconate and sulfadiazine are not applied on the surface of the brush of the toothbrush, but are mixed with law material resin to manufacture the brush of the toothbrush to prevent peeling of the coating. When less than 1.5 weight% of sulfadiazine is used, antimicrobial effects are not obtained.

Description

Antimicrobial brush of a toothbrush

본 발명은 항균 칫솔모에 관한 것으로, 보다 상세하게는 칫솔모 제조시, 설파디아진(sulfadiazine)과 클로로헥시딘 글루코네이트(chlorhexidine gluconate)를 칫솔모의 원료수지와 혼합하여 제조한 칫솔모인 것으로 각종 세균으로부터 발생되는 염증, 충치, 구취 등의 억제 및 예방효과가 있으며 칫솔의 위생적 보관이 가능하도록 하는 것이다.The present invention relates to antibacterial bristles, and more specifically, to the bristles, the bristles are prepared by mixing sulfadiazine and chlorohexidine gluconate with the raw material of the bristles from various bacteria. It has the effect of preventing and preventing inflammation, tooth decay, bad breath, etc., and enables the hygienic storage of toothbrushes.

우리는 일반적으로 하루 중 2~3회 정도의 양치질을 통하여 치아, 잇몸건강의 유지 및 구취의 예방 등에 힘쓰고 있다. We usually try to brush your teeth and gums and prevent bad breath by brushing your teeth 2-3 times a day.

신체의 어느 부위 못지 않게 치아 및 잇몸건강의 중요성이 대두 되면서 점차 각종의 기능성 및 효과를 갖는 치약조성물 및 칫솔의 개발이 이루어지고 있다. As the importance of teeth and gum health is rising as much as any part of the body, the development of toothpaste compositions and toothbrushes having various functionalities and effects are being made.

그 중에서도 칫솔은 위생적인 관리가 가능하도록 다양한 소재를 적용한 항균 칫솔의 개발이 주를 이룬다. Among them, toothbrushes mainly focus on the development of antibacterial toothbrushes with various materials for hygienic management.

칫솔은 칫솔의 머리부에 있는 칫솔모가 늘 습하고 환기가 잘 되지 않는 상태로 있기 때문에 위생적으로 처리 및 보관이 어렵다. 또한 칫솔은 사람의 입으로 들어가는 것이기에 위생적 관리가 그 어느 무엇보다 중요하다.Toothbrushes are difficult to handle and store hygienically because the bristles on the head of the toothbrush are always wet and poorly ventilated. In addition, the toothbrush enters the mouth of the person, so hygiene is more important than anything else.

이에 칫솔의 위생적 관리를 위한 화학적 소독 및 자외선 소독 등의 방법 및 장치가 개발되어 있긴 하나 일반적으로 장치의 가격이 고가이거나 절차가 번거로워 실제적으로 널리 행하여지고 있지는 않다.Thus, although methods and devices such as chemical disinfection and ultraviolet disinfection for hygienic management of toothbrushes have been developed, they are generally not widely practiced due to the high price of the device or the cumbersome procedure.

이러한 문제점을 개선하기 위하여 칫솔모와 손잡이 등에 살균 및 항균성을 갖는 다양한 원료를 코팅 및 혼합하는 방법이 개발되어 있다. In order to improve this problem, a method of coating and mixing various raw materials having antiseptic and antimicrobial properties on bristles and handles has been developed.

대한민국 특허 제109751호 “칫솔”은 필라멘트가 양이온성 교환성과 양이온성 살균제를 갖는 중합체로 이루어진 복합체에 의해 코팅되어 있음을 특징으로 하는 칫솔에 관한 것으로 양이온성 살균제로써는 벤제로늄, 클로로헥시딘 등이 사용되고 있다. 클로로헥시딘은 광범위한 항균작용이 있어 치은염 예방효과로 가글용액이나 치약조성물의 구성성분으로 이용되어 지고 있는 것이다. Republic of Korea Patent No. 107571 "Toothbrush" relates to a toothbrush characterized in that the filament is coated by a composite consisting of a polymer having a cationic exchanger and a cationic fungicide, cationic fungicides such as bengeronium, chlorohexidine, etc. Is being used. Chlorohexidine has a wide range of antibacterial effects and is used as a component of gargle solution or toothpaste composition to prevent gingivitis.

이에 상기 발명은 양이온 살균제를 이용하여 항균성을 갖는 칫솔을 제조코자 하는 것이다. 하지만 상기 발명은 양이온성 살균제가 포함된 복합체를 칫솔의 필라멘트에 코팅함으로써 칫솔의 사용에 따라 코팅이 벗겨지는 문제점이 발생하고 이에 항균의 효과가 점차 감소하게 된다. Therefore, the present invention is to produce a toothbrush having antimicrobial activity using a cationic fungicide. However, the present invention has a problem that the coating is peeled off according to the use of the toothbrush by coating the composite containing the cationic fungicide on the filament of the toothbrush, and the antimicrobial effect is gradually reduced.

또한 광범위한 살균력을 갖기는 하나 치아를 얼룩지게 하는 부작용을 가지는 클로로헥시딘을 사용함에 있어 클로로헥시딘의 농도를 기재하고 있지 않아 그에 따른 부작용을 예상할 수 있다. In addition, the use of chlorohexidine, which has a wide range of bactericidal properties but has side effects of staining teeth, does not describe the concentration of chlorohexidine.

상기 발명 이외에도 항균 칫솔에 사용되는 재료로는 은나노, 숯, 쑥, 옥 등 다양하다. 이들 대부분이 칫솔모 제조에 사용되는 수지에 상기 분말을 혼합하여 칫솔모를 성형하거나 혹은 칫솔모의 표면에 코팅함으로써 항균 칫솔의 목적을 달성하 고자 한다. In addition to the above invention, the material used in the antibacterial toothbrush is various, such as silver nano, charcoal, mugwort, jade. Most of them try to achieve the purpose of the antibacterial toothbrush by mixing the powder with the resin used for bristle production to form the bristles or coating the surface of the bristles.

하지만 은나노의 경우 불용성의 것이어서 물에 용해되지 않은 만큼 효과가 떨어지고 은이온의 독성이 있을 수 있다는 점 때문에 제한적으로 사용되어 지고 있다. 또한 숯, 쑥, 옥 등을 칫솔모의 수지와 혼합하여 사용할 때는 이들이 갖는 고유의 색상으로 칫솔모의 착색이 일어나는 문제점이 있다. However, silver nanoparticles are insoluble because they are insoluble, so they are less effective in dissolving in water and may be toxic to silver ions. In addition, when using a mixture of charcoal, mugwort, jade and the like of the bristles, there is a problem that the coloring of the bristles with their own color.

또한 상기와 같은 칫솔들은 항균성을 갖는 칫솔이기는 하나 충치를 예방할 수 있는 효과는 없어 한정적인 것이 된다. In addition, the toothbrushes as described above are limited to toothbrushes having antimicrobial properties but have no effect of preventing tooth decay.

이에 본원발명은 위생적으로 처리 및 보관이 가능함은 물론 충치의 원인이 되는 충치균을 억제하는 칫솔을 개발하고자 하는 것으로 설파디아진과 클로로헥시딘 글루코네이트를 칫솔모의 원료수지에 일정량 혼합하여 칫솔모를 제조하고 이로부터 칫솔을 제조할 수 있도록 하고자 하는 것이다. Therefore, the present invention is intended to develop a toothbrush that can be hygienically treated and stored, as well as to suppress tooth decay, which causes tooth decay, to prepare bristles by mixing a certain amount of sulfadiazine and chlorohexidine gluconate into the raw material of the bristles. It is intended to be able to manufacture a toothbrush from this.

본원 발명은 항균 칫솔모에 관한 것으로, 보다 상세하게는 칫솔모 제조시, 설파디아진(sulfadiazine)과 클로로헥시딘 글루코네이트(chlorhexidine gluconate)를 칫솔모의 원료수지와 혼합하여 제조하는 충치 및 치은염 억제,예방 및 칫솔의 위생적 보관이 가능하도록 하는 항균 칫솔모에 관한 것이다.The present invention relates to antibacterial bristles, and more specifically, in the preparation of the bristles, to prevent tooth decay and gingivitis prepared by mixing sulfadiazine and chlorhexidine gluconate with the raw resin of the bristles. And it relates to antibacterial bristles to enable the hygienic storage of the toothbrush.

즉, 칫솔모의 원료수지 93~97중량%에 설파디아진 1.5~5중량%, 0.2%농도의 클로로헥시딘 글루코네이트 1~3중량%를 혼합하여 이를 칫솔모로 가공하는 것이다. In other words, the raw material of the bristles 93 to 97% by weight of sulfadiazine 1.5-5% by weight, 0.2% concentration of chlorohexidine gluconate 1 to 3% by weight is mixed with the bristles.

설파디아진은 설폰아미드계통의 항생제로써 대장균 등에 효과가 있고 특히 충치의 원인균인 스트렙토코커스 뮤탄스(Streptococcus mutans)균을 억제하는 효과가 있다.Sulfadiazine is a sulfonamide-based antibiotic that is effective in Escherichia coli, and particularly, inhibits Streptococcus mutans , a causative agent of caries.

이에 본원발명은 설파디아진을 칫솔모 성형시 칫솔모 성형에 사용되는 원료수지에 혼합하여 사용함으로써 항균칫솔은 물론 충치를 예방할 수 있는 칫솔을 제조할 수 있게 된다. Therefore, the present invention can be prepared by using a sulfadiazine mixed with the raw material resin used in the bristle molding when forming the bristles to prevent tooth decay as well as antibacterial toothbrushes.

또한 설파디아진은 그람양성균이나 그람음성균에 의한 전염병과, 설파제 적응질환인 폐렴, 임질, 패혈증, 적리, 화농석 질환에 내복(內服)하며, 혈중에서 비교적 고농도에 달하고 독성이 적은 성질을 갖고 있다.In addition, sulfadiazine is resistant to infectious diseases caused by Gram-positive bacteria or Gram-negative bacteria and pneumonia-adapted diseases such as pneumonia, gonorrhea, sepsis, erythropoies, and pyrites, and has relatively high concentrations and low toxicity in the blood. .

이러한 설파디아진을 1.5중량% 보다 적게 넣으면 설파디아진의 항균효과 및 충치균 억제의 효과를 볼 수 없으며 5중량% 보다 많이 넣으면 설파디아진의 독성으로 인하여 부적합한 것이 된다. If less than 1.5% by weight of sulfadiazine, the antimicrobial effect of sulfadiazine and the effect of inhibiting caries are not seen, and when more than 5% by weight of sulfadiazine is inadequate due to toxicity.

클로로헥시딘 글루코네이트는 그람양성, 그람음성뿐만 아니라 곰팡이류에 대해서도 광범위한 살균효과가 있다. 치과에서는 클로로헥시딘 용액을 치은염 예방효과를 위하여 가글용액 등으로 광범위하게 사용한다. 이러한 클로로헥시딘 글루코네이트를 1중량% 보다 적게 넣으면 클로로헥시딘 글루코네이트의 살균효과를 볼 수 없으며 3중량% 보다 많이 넣으면 클로로헥시딘 글루코네이트의 독성으로 인하여 부적합한 것이 된다. 또한 클로로헥시딘 글루코네이트는 살균력이 우수하긴 하나 좋지 않은 맛이 나고 치아를 얼룩지게 하는 문제점이 있어 규정농도 및 규정량 이상 넣는 것은 바람직하지 못한 것이 된다. Chlorohexidine gluconate has a wide range of bactericidal effects on fungi as well as gram positive and gram negative. In dentistry, chlorohexidine solution is widely used as a gargle solution to prevent gingivitis. If less than 1% by weight of such chlorohexidine gluconate can not see the bactericidal effect of chlorohexidine gluconate, more than 3% by weight is unsuitable due to the toxicity of chlorohexidine gluconate. In addition, chlorohexidine gluconate has excellent sterilizing power but has a bad taste and stains teeth. Therefore, it is not desirable to put more than the prescribed concentration and prescribed amount.

양이온성 살균제, 즉 클로로헥시딘을 칫솔모 또는 칫솔제조에 이용한 예는 있다. 하지만 이들을 칫솔모 성형시 혼합하여 칫솔모로 가공한 예는 없었으며 더욱이 칫솔의 보관 및 처리를 위생적으로 하는 효과 이외에 충치균 예방의 효과를 갖도록 하는 칫솔모 제조를 위한 연구는 없었다. Examples of cationic fungicides, namely chlorohexidine, are used for bristle or toothbrush preparation. However, there was no case in which these were mixed with bristles when the bristles were formed, and furthermore, there was no research for the preparation of the bristles to have the effect of preventing tooth decay in addition to the hygienic effect of storing and treating the toothbrush.

이에 본원 발명은 칫솔모의 원료수지 93~97중량%에 설파디아진 1.5~5중량%, 0.2% 농도의 클로로헥시딘 글루코네이트 1~3중량%를 혼합하여 이를 칫솔모로 가공함으로써 위생적이며 충치예방 및 살균효과를 갖는 칫솔모를 제조할 수 있게 되는 것이다. 또한 클로로헥시딘 클루코네이트와 설파디아진을 칫솔모 표면에 코팅하는 것이 아니라 원료수지와 혼합하여 이를 칫솔모로 제조함으로써 사용횟수 및 시간경과에 따른 코팅의 벗겨짐 없이 효과가 지속 되는 칫솔모를 제조할 수 있는 것이다. Thus, the present invention is mixed hygiene and tooth decay prevention by mixing 1 ~ 3% by weight of sulfadiazine 1.5 ~ 5%, 0.2% chlorohexidine gluconate with raw material resin of 93 ~ 97% by weight of the bristles. And to be able to manufacture the bristles having a bactericidal effect. In addition, chlorohexidine gluconate and sulfadiazine are not coated on the surface of the bristles, but mixed with the raw resin to prepare them as bristles. Thus, the bristles can be manufactured without the peeling off of the coating over time and time. It is.

본원 발명은 칫솔모 제조시 칫솔모의 원료수지 93~97중량%에 설파디아진(Sulfadiazine) 1.5~5중량%, 0.2% 농도의 클로로헥시딘 글루코네이트(chlorhexidine gluconate) 1~3중량%를 혼합하여 이를 칫솔모로 가공한 것으로, 설폰아미드계통의 항생제인 설파디아진을 이용함으로써 충치의 원인균을 억제할 수 있으며 또한 광범위한 항균성을 갖는 클로로헥시딘 글루코네이트의 사용으로 늘 습한 상태에 있어 위생적이지 못한 칫솔을 위생적인 상태로 보관할 수 있는 칫솔모를 제공할 수 있게 된다. The present invention is prepared by mixing 1 to 3% by weight of chlorohexidine gluconate (Sulfadiazine) 1.5 to 5% by weight, 0.2% concentration of raw material of the bristles 93-97% by weight of the bristle It is processed with bristles, and it is possible to suppress the causative agent of tooth decay by using sulfadiamide, an antibiotic of sulfonamide type, and it is not hygienic in the wet state by using chlorohexidine gluconate which has a wide range of antibacterial properties. It is possible to provide a bristles that can be stored in a hygienic state.

이로써 본원 발명의 칫솔모가 적용된 칫솔을 상용하는 사용자는 살균기 및 살균을 위한 화학적 처리 없이 칫솔을 위생적으로 관리할 수 있으며 또한 구강 내 충치, 염증, 구취 등의 원인세균의 위협 없이 구강건강을 유지할 수 있다. Thus, users of the toothbrushes to which the bristles of the present invention are applied can hygienically manage toothbrushes without chemical treatment for sterilizers and sterilization, and can also maintain oral health without threat of causative bacteria such as tooth decay, inflammation, and bad breath. .

또한 설파디아진과 클로로헥시딘 글루코네이트를 칫솔모의 표면에 코팅하는 것이 아니라 칫솔모의 원료가 되는 수지에 규정량 혼합하여 사용함으로써 칫솔의 사용횟수 및 시간경과에 따른 코팅의 벗겨짐 없이 효과가 지속 되는 칫솔모를 제공할 수 있다. In addition, instead of coating sulfadiazine and chlorohexidine gluconate on the surface of the bristles, it is used by mixing a prescribed amount with the resin that is the raw material of the bristles. Can be provided.

Claims

Antibacterial bristles, characterized in that the bristle is mixed with 93 to 97% by weight of the raw material resin, 1.5 to 5% by weight of sulfadiazine, and 1 to 3% by weight of chlorhexidine gluconate.

The antimicrobial bristle of claim 1, wherein the antibacterial bristle has a concentration of 0.2% of chlorohexidine gluconate.