KR100648177B1 - Improved asphalt waterproof sheets and waterproof structure using the same - Google Patents

Improved asphalt waterproof sheets and waterproof structure using the same Download PDF

Info

Publication number
KR100648177B1
KR100648177B1 KR1020060043317A KR20060043317A KR100648177B1 KR 100648177 B1 KR100648177 B1 KR 100648177B1 KR 1020060043317 A KR1020060043317 A KR 1020060043317A KR 20060043317 A KR20060043317 A KR 20060043317A KR 100648177 B1 KR100648177 B1 KR 100648177B1
Authority
KR
South Korea
Prior art keywords
layer
rubber asphalt
waterproof
composite
waterproofing
Prior art date
Application number
KR1020060043317A
Other languages
Korean (ko)
Inventor
현흥창
현우창
정민곤
Original Assignee
현흥창
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 현흥창 filed Critical 현흥창
Application granted granted Critical
Publication of KR100648177B1 publication Critical patent/KR100648177B1/en

Abstract

A rubber asphalt waterproof sheet for hybrid waterproofing purpose is provided to promote unification and to form a waterproofing membrane layer evenly by improving the binding strength of a rubber asphalt layer and a waterproofing membrane layer and to be attached directly to a base plane with excellent self-adherence without using primer, and a hybrid waterproofing structure is provided to maximize waterproofing efficiency by completing a double hybrid waterproofing layer. A rubber asphalt waterproof sheet(S) for hybrid waterproofing purpose is formed by attaching a synthetic resin film(30) on a rubber asphalt layer(20), and forming a primary primer coating layer(40) by coating the synthetic resin film with primer. Hereon fiber cloth and a secondary primer coating layer are formed to increase the adhesive strength between the rubber asphalt layer and the synthetic resin film and an adhesive layer(10) is formed below the rubber asphalt layer to redouble self-adherence of the rubber asphalt waterproof sheet. The hybrid waterproofing structure is formed by attaching a rubber asphalt waterproof sheet on a base plane using adhesive strength of an adhesive layer after removing release paper, and forming a waterproofing membrane layer by applying waterproofing membrane on a primary primer coating layer of the rubber asphalt waterproof sheet. Therefore the rubber asphalt layer and the waterproofing membrane layer are coupled with each other by a synthetic resin film and a primary primer coating layer to complete a double hybrid waterproofing structure.

Description

복합방수용 고무아스팔트 방수시트 및 이를 이용한 복합방수구조{Improved asphalt waterproof sheets and waterproof structure using the same}Composite asphalt waterproof sheets and waterproof structure using the same

도 1 및 도 2는 본 발명에 따른 복합방수용 고무아스팔트 방수시트의 실시예를 도시한 도면이다.1 and 2 is a view showing an embodiment of a composite waterproof rubber asphalt waterproof sheet according to the present invention.

도 3 및 도 4는 본 발명에 따른 복합방수구조의 실시예를 도시한 단면도이다.3 and 4 are cross-sectional views showing an embodiment of a composite waterproof structure according to the present invention.

<도면의 주요부분에 관한 부호의 설명><Explanation of symbols on main parts of the drawings>

10: 점착층 11, 51: 섬유포10: adhesion layer 11, 51: fiber cloth

20: 고무아스팔트층 30: 합성수지필름20: rubber asphalt layer 30: synthetic resin film

40: 제1프라이머코팅층 50: 제2프라이머코팅층40: first primer coating layer 50: second primer coating layer

C: 바탕면 C: ground plane

S: 복합방수용 고무아스팔트 방수시트(이형지 제거상태)S: Composite waterproof rubber asphalt waterproof sheet (release paper removed)

T:이음테이프 U: 도막방수층T: Joint tape U: Coating waterproofing layer

본 발명은 복합방수용 고무아스팔트 방수시트 및 이를 이용한 복합방수구조에 관한 것으로, 더욱 상세하게는 고무아스팔트층과 도막방수층의 결합력을 향상시킬 수 있음은 물론 균일한 도막방수층의 형성을 가능케 하고 나아가 프라이머의 사용없이도 자체의 우수한 점착력으로 바탕면에 직접 부착 설치가 가능한 복합방수용 고무아스팔트 방수시트와, 이를 이용함으로 도막방수층과의 결합력 상승에 따른 방수성능의 극대화를 기대할 수 있고 나아가 바닥에서 수직으로 치켜 올라가는 코너에도 전면 부착이 가능해져 밀실한 방수처리를 도모할 수 있게 된 복합방수구조에 관한 것이다.The present invention relates to a rubber waterproof sheet for composite waterproofing and a composite waterproof structure using the same. More specifically, the bonding force between the rubber asphalt layer and the coating waterproof layer can be improved, as well as the formation of a uniform coating waterproof layer, and furthermore, Composite waterproof rubber asphalt waterproof sheet that can be directly attached to the base surface with its own excellent adhesive strength without use, and by using this, it can be expected to maximize the waterproofing performance by increasing the bonding strength with the film waterproofing layer. The present invention relates to a composite waterproof structure that can be attached to the front surface thereof and can achieve a tight waterproof treatment.

건축물에는 우수 및 지하수의 유입을 막아 구조체의 균열이나 내구성의 저하를 막기 위하여 필수적으로 방수작업이 요구되며, 통상 방수공법은 시공방법에 따라 시트방수, 도막방수, 복합방수로 구분된다. 도막방수는 액상형의 방수제를 반복하여 도포하는 방법으로, 액상 자체의 퍼짐성으로 인해 건축물 바탕의 평활도가 좋지 않으면 균일한 두께의 도막형성이 어렵다는 점과, 바탕의 습기에 의해 부풀림이 쉽게 발생한다는 점, 그리고 바탕의 크랙에 대한 대응성이 떨어진다는 점 등이 단점으로 지적된다. 시트방수는 상기 도막방수의 단점 중 방수층 두께 확보와 크랙에 대한 대응성에 대한 문제를 해결하기는 하나, 복잡한 구조물의 모서리나 돌출부의 밀실한 방수층의 확보에 어렵다는 단점이 있다. 이러한 도막방수와 시트방수를 결합하여 양자의 단점을 보완하고 장점을 상승시킨 것이 복합방수이다.In order to prevent rainwater and groundwater from entering the building, watertight work is required in order to prevent cracking or deterioration of the structure. In general, the waterproofing method is classified into sheet waterproofing, film waterproofing, and composite waterproofing according to the construction method. Coating waterproofing is a method of repeatedly applying a liquid-type waterproofing agent, it is difficult to form a coating film of uniform thickness without the smoothness of the building ground due to the spreadability of the liquid itself, it is easy to swell due to the moisture of the ground, The disadvantage is that it is less responsive to background cracks. Sheet waterproofing solves the problem of securing the thickness of the waterproof layer and the response to cracks among the disadvantages of waterproofing the coating film, it is difficult to secure a tight waterproof layer of the corners or protrusions of the complex structure. The combined waterproofing of the coating film and the sheet waterproofing is to complement the disadvantages of both of them and increase the advantages are complex waterproofing.

복합방수는 고무아스팔트류, 합성고분자계 등으로 제작된 베이스시트를 바탕면에 부착하고 그 위에 액상의 도막방수재를 도포하는 방법이다. 복합방수에서 통상의 베이스시트를 그대로 사용하게 되면 베이스시트와 액상의 도막방수재가 각기 다른 재료적 특성으로 인하여 서로 부착되지 않고 들뜨게 되는 문제점이 있다. 이를 해결하기 위해 베이스시트와 액상의 도막방수재 사이의 매개체 역할을 하도록 상부에 부직포를 부착한 베이스시트가 개발된 바 있으나, 이러한 개량 베이스시트에 액상의 도막방수재를 도포하면 부직포로 도막방수재가 다량 흡수되므로 원하는 도막방수층을 형성하기 위해서는 여러겹으로 도막방수재를 도포해야 하는 새로운 문제가 발생하게 된다. 또한, 우천시 부직포가 젖으면 마를때까지 기다려야 하므로 공사가 지연될 우려가 있으며, 균일한 표면으로 마무리되지 못하므로 도막방수층 또한 균일한 두께로 형성되지 못한다는 문제가 있다.Composite waterproofing is a method of attaching a base sheet made of rubber asphalt, synthetic polymer, etc. to the base surface and applying a liquid coating waterproofing material thereon. When the conventional base sheet is used as it is in the composite waterproof, there is a problem that the base sheet and the liquid coating waterproofing material are lifted up without being attached to each other due to different material properties. In order to solve this problem, a base sheet having a nonwoven fabric attached to the upper part has been developed to act as a medium between the base sheet and the liquid film waterproofing material. However, when the liquid film waterproofing material is applied to such an improved base sheet, the film waterproofing material is absorbed by the nonwoven fabric. Therefore, in order to form a desired coating waterproof layer, a new problem arises in that the coating film waterproofing material must be applied in several layers. In addition, there is a risk that construction will be delayed if the nonwoven fabric is wet when it rains, and thus the construction may be delayed. Thus, the coating layer may not be formed to a uniform thickness because it may not be finished with a uniform surface.

한편, 통상 복합방수에서 베이스시트로 시트방수에서 사용되는 고무아스팔트시트가 많이 사용하고 있는데, 고무아스팔트시트는 토치작업으로 용융시키면서 바탕면에 부착하거나 프라이머 처리된 바탕면에 부착하였으나, 이와 같은 방법은 프라이머 도포작업으로 인한 재료와 인건비의 비용문제, 프라이머 도포 후 시간적인 문제가 있었다. 이에 자체의 점착력을 가지는 자착식 방수시트의 개발이 필요한 실정이다. 그러나, 지금까지의 자착식 방수시트는 고무아스팔트시트 자체가 갖는 점착력을 활용하거나 고무계 점착제를 이용하는 정도에 머물기 때문에 바탕면에의 부착력이 그다지 우수하지 못하였고, 나아가 저온에서 부착력이 현저히 떨어진다는 문제가 있어 통상의 고무아스팔트시트와 다름없이 프라이머 처리된 바탕면에 부착하여 사용하는 것이 일반적이었다.On the other hand, rubber asphalt sheet used in the waterproof sheet is commonly used as the base sheet in the composite waterproof, rubber asphalt sheet is attached to the base surface or melted by the torch work, but attached to the base surface treated with the primer, There was a problem of the cost of materials and labor due to primer application, and a time problem after primer application. Therefore, it is necessary to develop a self-adhesive waterproof sheet having its own adhesive force. However, the self-adhesive waterproof sheet has not been so excellent in adhesion to the base surface because it uses the adhesive force of the rubber asphalt sheet itself or uses a rubber-based adhesive. In general, it was used to attach to a primer-treated base surface as usual rubber asphalt sheet.

물론, 종래에는 복합방수에서 고무아스팔트시트를 절연시트로 제작하여 바탕면에 부착시키기 않고 절연시킴으로 바탕면과 무관하게 거동하도록 한 절연방법이 제안된 바 있다. 그러나, 절연방법은 고무아스팔트시트 위에 누름콘크리트를 타설하여 비노출공법으로 마무리하게 되는 경우 누름콘크리트 타설시 고무아스팔트시트와 바탕면 사이에 존재하는 공기에 의해 고무아스팔트시트가 부풀어 오르거나 밀리는 현상이 초래되어 그다지 유용하게 활용되지는 못하고 있다.Of course, in the related art, an insulating method has been proposed in which a rubber asphalt sheet is made of an insulating sheet in a composite waterproofing and thus is insulated without attaching to the base surface. However, insulation method is that when the pressed concrete is placed on the rubber asphalt sheet to finish by the non-exposure method, the rubber asphalt sheet swells or is pushed by air existing between the rubber asphalt sheet and the base surface when the pressed concrete is poured. It is not very useful.

본 발명은 상기한 종래의 문제를 개선하고자 안출된 것으로서, 복합방수에서 고무아스팔트층과 도막방수층의 결합력을 향상시켜 일체화를 도모함은 물론 균일한 도막방수층의 형성을 가능케 한 복합방수용 고무아스팔트 방수시트와 이를 이용함으로 방수성능을 극대화할 수 있게 된 복합방수구조를 제공하는데 그 목적이 있다.The present invention has been made to improve the above-described conventional problems, and improve the bonding strength of the rubber asphalt layer and the film waterproof layer in the composite waterproofing to facilitate the integration and as well as the composite waterproof rubber asphalt waterproof sheet for the formation of a uniform film waterproof layer and The purpose is to provide a composite waterproof structure that can maximize the waterproof performance by using this.

본 발명의 다른 목적은 프라이머의 사용없이도 자체의 우수한 점착력으로 바탕면에 직접 부착 설치가 가능한 복합방수용 고무아스팔트 방수시트와 이를 이용함으로 바닥에서 수직으로 치켜 올라가는 코너에도 전면 부착이 가능해져 밀실한 방수처리를 도모할 수 있게 된 복합방수구조를 제공하는 것이다.Another object of the present invention is a composite waterproof rubber asphalt waterproof sheet that can be directly attached to the base surface with its excellent adhesive strength without the use of a primer and the front surface can be attached to the corners raised vertically from the bottom by using the same. It is to provide a composite waterproof structure that can be planned.

상기한 목적달성을 위해 본 발명은 고무아스팔트층; 상기 고무아스팔트층 위에 부착되는 합성수지필름; 및, 상기 합성수지필름 위에 형성되는 제1프라이머코팅층;을 포함하여 구성되는 것을 특징으로 하는 복합방수용 고무아스팔트 방수시트를 제공한다. 또한, 본 발명은 바탕면; 상기 바탕면에 이형지를 제거하면서 점착층의 점착력으로 부착 설치되는 복합방수용 고무아스팔트 방수시트; 및, 상기 복합방수용 고무아스팔트 방수시트의 제1프라이머코팅층 위로 형성되는 도막방수층;을 포함하여 구성되는 것을 특징으로 하는 복합방수구조를 제공한다.The present invention for achieving the above object is a rubber asphalt layer; A synthetic resin film attached on the rubber asphalt layer; And a first primer coating layer formed on the synthetic resin film. Provides a composite waterproof rubber asphalt waterproof sheet, comprising: a first primer coating layer formed on the synthetic resin film. In addition, the present invention; Composite waterproof rubber asphalt waterproof sheet is attached to the adhesive layer of the adhesive layer while removing the release paper on the base surface; And a coating film waterproof layer formed on the first primer coating layer of the composite waterproof rubber asphalt waterproofing sheet.

이하, 첨부한 도면 및 바람직한 실시예에 따라 본 발명을 상세히 설명한다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings and preferred embodiments.

도 1 및 도 2는 본 발명에 따른 복합방수용 고무아스팔트 방수시트의 실시예를 도시한 도면으로서, 본 발명의 복합방수용 고무아스팔트 방수시트(S)는 시트방수와 도막방수가 결합된 복합방수에서 사용하기 위한 방수시트로서 고무아스팔트층(20) 위에 프라이머가 코팅된 합성수지필름(30+40)을 부착시키는 것을 특징으로 한다. 나아가, 상기 고무아스팔트층과 합성수지필름과의 부착력 향상을 위해 섬유포(41)와 제2프라이머코팅층(50)을 부가적으로 형성시키거나, 복합방수용 고무아스팔트 방수시트(S)의 자착성을 배가시키기 위해 고무아스팔트층(20) 아래에 점착층(10)을 부가적으로 형성시킨다는데 특징이 있다.1 and 2 is a view showing an embodiment of a composite waterproof rubber asphalt waterproof sheet according to the present invention, the composite waterproof rubber asphalt waterproof sheet (S) of the present invention is used in the composite waterproof combined sheet waterproof and waterproof film As a waterproof sheet for the rubber asphalt layer 20, characterized in that for attaching a synthetic resin film (30 + 40) coated with a primer. Furthermore, in order to improve adhesion between the rubber asphalt layer and the synthetic resin film, the fabric cloth 41 and the second primer coating layer 50 are additionally formed, or the self-adhesion of the composite waterproof rubber asphalt waterproof sheet S is doubled. In order to additionally form an adhesive layer 10 under the rubber asphalt layer 20.

본 발명의 복합방수용 고무아스팔트 방수시트는 고무아스팔트층(20) 위에 합성수지필름(30)이 부착되고 상기 합성수지필름(30) 위에 프라이머를 코팅하여 제1프라이머코팅층(40)이 형성되는 것을 가장 기본적인 구조로 한다. 즉, 고무아스팔트층(20)과 도막방수층(U)은 서로 친화성이 없기 때문에 고무아스팔트층(20)과 도막방수층(U)은 서로 접착되지 않아 분리되기 마련이므로, 프라이머로 코팅된 합성수지필름(30+40)을 고무아스팔트층(20)과 도막방수층(U)의 결합매개가 되도록 고무아스팔트층(20)에 부착하고 있는 것이다. 본 발명에서는 상기 프라이머로 주제와 경화제로 이루어진 2성분형으로, 상기 주제는 염화 폴리올레핀 10~15중량%, 용제 80~85중량%를 포함하여 이루어지고, 상기 경화제는 폴리이소시아네이트 100중량%로 이루어진 것을 제안한다. 이액형으로 이루어지므로 경화제에 의한 주제의 경화과정에서 합성수지필름 위에 안정적으로 코팅층을 형성시킬 수 있게 된다. 특히, 상기와 같은 프라이머를 사용하면 도막방수재로 우레탄을 적용하는 경우 도막방수층(U)과 일체 결합하는데 더욱 유리한 효과를 발휘할 것이데, 이는 경화제로 우레탄의 주원료와 동일한 폴리이소시아네이트를 사용하였는 바 제1프라이머코팅층(40)이 우레탄 도막방수층과 친화성을 발휘할 것이기 때문이다.The composite waterproof rubber asphalt waterproof sheet of the present invention has the most basic structure that the first primer coating layer 40 is formed by attaching a synthetic resin film 30 on the rubber asphalt layer 20 and coating a primer on the synthetic resin film 30. Shall be. That is, since the rubber asphalt layer 20 and the coating waterproof layer U are not compatible with each other, the rubber asphalt layer 20 and the coating waterproof layer U do not adhere to each other and are separated from each other, and thus, a synthetic resin film coated with a primer ( 30 + 40 is attached to the rubber asphalt layer 20 so as to be a bonding medium of the rubber asphalt layer 20 and the coating waterproof layer U. FIG. In the present invention, the primer is a two-component type consisting of a main agent and a curing agent, wherein the main agent comprises 10 to 15% by weight of chlorinated polyolefin, 80 to 85% by weight of the solvent, and the curing agent is composed of 100% by weight of polyisocyanate Suggest. Since it is made of a two-component type, it is possible to stably form a coating layer on the synthetic resin film during the curing process of the main body by the curing agent. In particular, the use of such a primer will have a more advantageous effect of integrally bonding with the coating film waterproofing layer (U) when urethane is applied as a coating film waterproofing material, which is the first polyisocyanate as the main raw material of the urethane as a curing agent This is because the primer coating layer 40 will exhibit affinity with the urethane coating waterproof layer.

상기 합성수지필름(30)은 표면이 코로나 처리되도록 한 후 상기 제1프라이머코팅층(40)이 코로나 처리된 합성수지필름(30) 표면에 형성되도록 하는 것이 제1프라이머코팅층(40)의 코팅력 향상에 유리하다. 코로나 처리된 합성수지필름(30)에 프라이머를 롤 코팅하여 제1프라이머코팅층(40)을 적층시키고, 이를 고무아스팔트층(20) 위에 합지하면 본 발명에 따른 복합방수용 고무아스팔트 방수시트가 완성된다. 이때, 합성수지필름(30)과 고무아스팔트층(20)의 부착력 향상을 위해 도 2와 같이 상기 합성수지필름(30) 아래에 섬유포(51)가 부착되도록 하고, 상기 섬유 포(51) 아래에 제2프라이머코팅층(50)이 형성되도록 할 수 있다. 상기 섬유포(51)로는 타폴린 직포와 같은 것을 채택할 수 있으며, 이와 같은 섬유포(51)의 채택으로 합성수지필름(30)과 고무아스팔트층(20)과의 부착면적이 확대되어 부착력향상을 기대할 수 있게 된다. 또한, 상기 제2프라이머코팅층(50)은 고무아스팔트층(20)에 융화하면서 섬유포(51)가 고무아스팔트층에 합지되는 것을 보완한다. 도 2와 같은 구조의 방수시트는 일단 섬유포(51, 타폴린 직포) 표면에 합성수지액을 부어 합성수지필름(30)을 적층 형성하고, 그 위와 아래로 프라이머를 롤 코팅하여 제1프라이머코팅층(40)과 제2프라이머코팅층(50)을 적층하여 필름형태로 완성한 후(물론, 롤 코팅 전에 합성수지필름(30) 표면에 코로나처리 가능) 이를 고무아스팔트층(20) 위에 합지하는 방법으로 제작 완성할 수 있다.The synthetic resin film 30 has a surface that is corona treated, and then the first primer coating layer 40 is formed on the surface of the corona treated synthetic resin film 30, which is advantageous for improving the coating power of the first primer coating layer 40. Do. The first primer coating layer 40 is laminated by roll coating a primer on the corona-treated synthetic resin film 30, and laminating it on the rubber asphalt layer 20 to complete the composite waterproof rubber asphalt waterproof sheet according to the present invention. At this time, in order to improve the adhesion between the synthetic resin film 30 and the rubber asphalt layer 20, the fabric cloth 51 is attached to the bottom of the synthetic resin film 30 as shown in Figure 2, the second under the fiber cloth 51 The primer coating layer 50 may be formed. The fiber cloth 51 may be the same as that of a tarpaulin woven fabric, and the adoption of the fiber cloth 51 may increase the adhesion area between the synthetic resin film 30 and the rubber asphalt layer 20, thereby improving adhesion. Will be. In addition, the second primer coating layer 50 complements that the fiber cloth 51 is laminated to the rubber asphalt layer while being fused to the rubber asphalt layer 20. In the waterproof sheet having the structure as shown in FIG. 2, the synthetic resin solution is poured onto the surface of the fiber cloth 51 (tarpaulin woven fabric) to form a synthetic resin film 30, and the first primer coating layer 40 is formed by applying a roll coating on and below the primer. After the second primer coating layer 50 is laminated and finished in the form of a film (of course, the corona treatment may be performed on the surface of the synthetic resin film 30 before the roll coating), it may be completed by laminating on the rubber asphalt layer 20. .

이렇게 도 1 또는 도 2와 같이 고무아스팔트층(20) 위의 적층구조가 완성되면 표면이 얇은 유리면(0.08㎜정도)으로 평활하게 마무리되며 그 결과 그 위로 형성되는 도막방수층(U)은 균일한 두께로 밀착 형성할 수 있게 된다.1 or 2, when the laminated structure on the rubber asphalt layer 20 is completed, the surface is smoothly finished with a thin glass surface (about 0.08 mm), and as a result, the coating layer (U) formed thereon has a uniform thickness. It can be formed in close contact.

전술한 바와 같이 고무아스팔트층(20) 아래로는 점착층(10)을 부가시켜 자착성을 배가시킬 수 있다. 점착층으로는 무용제형 점착제의 한 종류로서 친환경적인 소재이며, 저온(영하 35도 정도)에서도 점착력을 유지하는 이점이 있는 핫멜트를 이용함이 바람직하다. 또한, 핫멜트는 평면이나 표면에 대한 침투력이 뛰어나며 초기 점착력이 매우 강하다는 장점이 있는 재료이다. 이와 같은 핫멜트는 고무아스팔트층의 배합제인 오일과의 친화성이 뛰어나므로 고무아스팔트층(20) 아래로 점 착층(10)을 안정적으로 형성시킬 수 있을 것이다.As described above, the adhesive layer 10 may be added under the rubber asphalt layer 20 to increase the self-adhesiveness. As an adhesive layer, it is an environmentally friendly material as a kind of a solventless adhesive, and it is preferable to use the hot melt which has the advantage of maintaining adhesive force even at low temperature (about 35 degrees below zero). In addition, hot melt is a material having the advantage of excellent penetration force on the plane or surface and very strong initial adhesion. Since such hot melt has an excellent affinity with oil, which is a compounding agent of the rubber asphalt layer, the adhesive layer 10 may be stably formed under the rubber asphalt layer 20.

도 1 및 도 2에서는 상기 점착층(10)에 섬유포(11)가 함침되도록 하고 있는데, 이는 점착층(10)을 소정 두께 이상으로 확보하면서 점착층(10)의 전단력을 보완하기 위함이다. 점착층(10)이 소정 두께 이상으로 확보되면 바탕면과의 부착력 향상에 유리할 것으로 기대되며, 실제 직포가 함침되도록 한 결과 점착층(10)의 두께를 0.3㎜이상 확보하는 것이 가능해졌다.In FIG. 1 and FIG. 2, the fiber cloth 11 is impregnated in the adhesive layer 10, which is to supplement the shear force of the adhesive layer 10 while securing the adhesive layer 10 to a predetermined thickness or more. When the adhesive layer 10 is secured to a predetermined thickness or more, it is expected to be advantageous for improving adhesion to the base surface. As a result of the actual woven fabric being impregnated, it is possible to secure the thickness of the adhesive layer 10 to 0.3 mm or more.

도 3 및 도 4는 본 발명에 따른 복합방수구조의 실시예를 도시한 단면도로서, 복합방수구조는 도 1 또는 도 2의 복합방수용 고무아스팔트 방수시트(S)를 이형지를 제거하면서 점착층(10)의 점착력으로 바탕면(C)에 부착 설치한 후 상기 복합방수용 고무아스팔트 방수시트의 제1프라이머코팅층(40) 위로 도막방수재를 도포하여 도막방수층(U)을 형성함으로 완성된다. 그 결과 고무아스팔트층(20)과 도막방수층(U)은 합성수지필름(30)과 제1프라이머코팅층(40)을 매개로 서로 일체 결합할 것이고, 이에 따라 완전한 2중 복합방수구조로 완성하게 된다. 도막방수재는 1액형의 무용제형으로 채택함이 환경친화적이라는 이점을 기대할 수 있음은 물론 간편한 작업성과 균일화된 품질확보를 위해서도 바람직하다.3 and 4 is a cross-sectional view showing an embodiment of a composite waterproof structure according to the present invention, the composite waterproof structure is the adhesive layer 10 while removing the release paper of the waterproof rubber waterproofing sheet (S) for composite waterproof of Figure 1 or 2 After the attachment to the base surface (C) by the adhesive force of the) is completed by forming a coating waterproof layer (U) by applying a coating film waterproofing material on the first primer coating layer 40 of the composite waterproof rubber asphalt waterproof sheet. As a result, the rubber asphalt layer 20 and the coating waterproof layer U will be integrally bonded to each other through the synthetic resin film 30 and the first primer coating layer 40, thereby completing a complete double composite waterproof structure. The coating waterproofing material can be expected to be environmentally friendly to adopt a one-part solvent-free type, and is also preferable for easy workability and uniform quality.

상기 복합방수용 고무아스팔트 방수시트(S)의 연결은 도 3의 겹침이음 또는 도 4의 이음테이프에 의한 조인트이음의 방법으로 처리할 수 있다.The connection of the composite waterproof rubber asphalt waterproof sheet (S) can be treated by the method of the joint joint by the overlapping joint of FIG. 3 or the joint tape of FIG. 4.

점착층을 핫멜트와 같이 점착력이 우수한 재료를 이용하여 형성시키는 경우에는 도 3의 겹침이음을 따르는 것도 무방하나, 점착층의 점착력이 그다지 우수하 지 못하는 경우에는 도 4와 같은 조인트이음 방법을 택하도록 한다. 왜냐하면 점착력이 우수하지 못한 경우 복합방수용 고무아스팔트 방수시트(S)가 들뜨기 쉬워 연결부의 방수하자가 우려되기 때문이다.When the adhesive layer is formed using a material having excellent adhesive strength, such as hot melt, the overlapping joint of FIG. 3 may be followed, but when the adhesive layer is not very excellent, the joint joint method as shown in FIG. 4 should be selected. . This is because the composite waterproof rubber asphalt waterproof sheet (S) is easy to be lifted when the adhesive strength is not excellent, so that the connection part may be waterproof.

도 4의 조인트이음 방법은 복합방수용 고무아스팔트 방수시트(S)를 상호간 간격을 두어 바탕면이 노출되도록 배치한 후 노출된 바탕면과 이웃하는 복합방수용 고무아스팔트 방수시트(S) 단부에 동시에 이음테이프(T)를 부착하고, 이어 상기 복합방수용 고무아스팔트 방수시트(S) 및 이음테이프(T) 위로 도막방수재를 도포하여 도막방수층(U)을 형성시키는 방법으로 이루어진다. 상기 이음테이프(T)는 복합방수용 고무아스팔트 방수시트(S)의 단부가 들뜨지 않게 바탕면에 완전히 부착 고정시키는 역할을 하게 된다. 이때, 상기 이음테이프(T)는 상부 표면이 상기 복합방수용 고무아스팔트 방수시트의 제1프라이머코팅층을 형성하는 프라이머에 의해 코팅처리도록 구성하는 것이 바람직하며, 이는 복합방수용 고무아스팔트 방수시트와 마찬가지로 그 위에 도포되는 도막방수층(U)과의 일체결합을 유도하기 위함이다. 이음테이프(T)로는 접착력이 우수한 부틸테이프를 이용하도록 한다.Joint joint method of Figure 4 is a composite waterproof rubber asphalt waterproofing sheet (S) is placed at intervals between each other so that the base surface is exposed to the exposed base surface and neighboring composite waterproof rubber asphalt waterproof sheet (S) at the same time the joint tape (T) is attached, and then the coating film waterproofing material is formed on the composite waterproof rubber asphalt waterproof sheet (S) and the joint tape (T) to form a coating film waterproofing layer (U). The joint tape (T) serves to completely fix the end portion of the composite waterproof rubber asphalt waterproofing sheet (S) to the base surface to prevent lifting. At this time, the joint tape (T) is preferably configured such that the upper surface is coated with a primer forming the first primer coating layer of the composite waterproof rubber asphalt waterproof sheet, which is the same as the composite waterproof rubber asphalt waterproof sheet This is to induce a single bond with the coating film waterproofing layer (U) to be applied. As the joint tape (T), butyl tape having excellent adhesive strength is used.

한편, 옥상 파라펫과 같이 바닥에서 수직으로 치켜 올라가는 바탕면(C)의 코너에는 상기 복합방수용 고무아스팔트 방수시트(S)를 폭이 좁은 테이프(대략 10㎝ 정도)로 제작하여 코너 형태와 동일하게 바닥에서 수직으로 치켜 올라가도록 부착 설치한다. 특히 바탕면의 코너는 통상 1m정도의 폭으로 제작되는 시트의 크기 그대로 이용하게 되는 경우 작업상 불편함과 밀착 부착의 어려움이 따르기 때문에 본 발명에서는 코너용으로 복합방수용 고무아스팔트 방수시트(S)를 폭이 좁은 테이프 형태로 제작하여 이용하고 있다. 다만, 코너용으로 도 2보다는 도 1과 같이 합성수지필름 아래에 섬유포가 생략된 형태의 것을 채택함이 수직도를 유지하면서 설치하는데 유리하다.On the other hand, in the corner of the base surface (C) raised vertically from the floor like a rooftop parapet, the composite waterproof rubber asphalt waterproof sheet (S) is made of a narrow tape (about 10 cm) in the same manner as the corner shape. Attach it so that it rises vertically from the floor. In particular, since the corner of the base surface is usually used as the size of the sheet produced in a width of about 1m due to the inconvenience of work and difficult to adhere closely, in the present invention, the composite waterproof rubber asphalt waterproof sheet (S) for the corner It is produced in the form of a narrow tape. However, it is advantageous to adopt the form of the fabric fabric is omitted under the synthetic resin film as shown in Figure 1 rather than Figure 2 for maintaining the verticality.

특히, 본 발명에 따른 복합방수용 고무아스팔트 방수시트(S)로 핫멜트 점착층(10)이 형성된 것을 채택하면 핫멜트 점착층이 우수한 부착력을 발휘하므로 도 3에서 도시하고 있는 바와 같이 방수시트 간의 겹침이 이루어지거나 치켜 올라가도록 설치되어도 바탕면에서 들뜨지 않은 상태로 밀착 부착이 가능하게 된다. 이에, 방수시트의 모서리 부분에 겹침이 이루어져 네겹으로 겹쳐지는 경우에도 핫멜트의 점착층의 점착력으로 들뜨는 현상을 억제할 수 있게 된다. 또한, 겹침이 이루어진 부분에서 일부 들뜨는 현상이 일어나더라도 복합방수용 고무아스팔트 방수시트(S)와 도막방수층(U)이 일체로 결합하여 완전한 2중 복합방수층을 형성하게 되므로 밀실한 방수처리가 가능하게 된다.In particular, when the hot melt adhesive layer 10 is formed as a composite waterproof rubber asphalt waterproof sheet (S) according to the present invention, since the hot melt adhesive layer exhibits excellent adhesion, the overlap between the waterproof sheets is made as shown in FIG. 3. Even if it is installed to be raised or raised, it can be attached closely without being lifted from the ground surface. Thus, even when overlapping the corner portion of the waterproof sheet is overlapped in four layers it is possible to suppress the phenomenon of lifting by the adhesive force of the adhesive layer of the hot melt. In addition, even if some of the lifting phenomenon occurs in the overlapped portion, the composite waterproof rubber asphalt waterproofing sheet (S) and the coating film waterproofing layer (U) are integrally combined to form a complete double composite waterproofing layer so that tight waterproofing is possible. .

이상과 같은 본 발명에 따르면, 복합방수에서 고무아스팔트층과 도막방수층의 결합력을 향상시켜 일체화를 도모함은 물론 균일한 도막방수층의 형성을 가능케 한 복합방수용 고무아스팔트 방수시트와 이를 이용함으로 완전한 2중 복합방수층을 완성할 수 있게 되어 방수성능을 극대화시킨 복합방수구조의 제공이 가능해진다. 또한, 별도 프라이머의 사용없이도 자체의 우수한 점착력으로 바탕면에 직접 부착 설치가 가능한 복합방수용 고무아스팔트 방수시트와 이를 이용함으로 바닥에서 수직으로 치켜 올라가는 코너에도 전면 부착이 가능해져 밀실한 방수처리를 도모할 수 있게 된 복합방수구조의 제공이 가능해진다.According to the present invention as described above, to improve the bonding strength of the rubber asphalt layer and the film waterproof layer in the composite waterproofing to facilitate the integration, as well as the composite waterproof rubber asphalt waterproof sheet for enabling the formation of a uniform film waterproof layer and a complete double composite The waterproof layer can be completed to provide a composite waterproof structure that maximizes the waterproof performance. In addition, the composite waterproof rubber asphalt waterproof sheet that can be directly attached to the base surface with its excellent adhesive strength without the use of a separate primer, and the front surface can be attached to the corner that is raised vertically from the floor by using this, to achieve a tight waterproof treatment. It is possible to provide a composite waterproof structure.

Claims (11)

고무아스팔트층(20);Rubber asphalt layer 20; 상기 고무아스팔트층(20) 위에 부착되는 합성수지필름(30); 및,A synthetic resin film 30 attached to the rubber asphalt layer 20; And, 상기 합성수지필름(30) 위에 형성되는 제1프라이머코팅층(40);A first primer coating layer 40 formed on the synthetic resin film 30; 을 포함하여 구성되며,It is configured to include, 상기 합성수지필름(30)은 그 표면이 코로나 처리되고, 상기 제1프라이머코팅층(40)은 코로나 처리된 합성수지필름(30) 표면에 형성되는 것임을 특징으로 하는 복합방수용 고무아스팔트 방수시트.The synthetic resin film 30, the surface is corona treated, the first primer coating layer 40 is a composite waterproof rubber asphalt waterproof sheet, characterized in that formed on the surface of the corona treated synthetic resin film (30). 제1항에서,In claim 1, 상기 고무아스팔트층(20)과 합성수지필름(30) 사이에Between the rubber asphalt layer 20 and the synthetic resin film 30 상기 합성수지필름(30) 아래에 부착되는 섬유포(51);와 상기 섬유포(51) 아래에 형성되는 제2프라이머코팅층(50);이 더 적층되는 것을 특징으로 하는 복합방수용 고무아스팔트 방수시트.Fiber waterproofing sheet 51, characterized in that the synthetic fabric film (30) attached to the bottom; and the second primer coating layer (50) formed under the fiber cloth (51) is further laminated. 삭제delete 제2항에서,In claim 2, 제1프라이머코팅층(40)과 제2프라이머코팅층(50)을 형성하는 프라이머는 주제와 경화제로 이루어진 2성분형으로, The primer forming the first primer coating layer 40 and the second primer coating layer 50 is a two-component type consisting of a main material and a curing agent, 상기 주제는 염화 폴리올레핀 10~15중량%, 용제 80~85중량%를 포함하여 구성되고, 상기 경화제는 폴리이소시아네이트 100중량%로 이루어지는 것을 특징으로 하는 복합방수용 고무아스팔트 방수시트.The main composition is composed of 10 to 15% by weight of chlorinated polyolefin, 80 to 85% by weight of the solvent, the composite waterproof rubber asphalt waterproof sheet, characterized in that made of 100% by weight of polyisocyanate. 제1항, 제2항, 제4항 중 어느 한 항에서,The method according to any one of claims 1, 2 and 4, 상기 고무아스팔트층(20) 아래에 점착층(10)이 더 형성되고,An adhesive layer 10 is further formed below the rubber asphalt layer 20, 상기 점착층(10) 아래에 이형지가 더 부착되는 것을 특징으로 하는 복합방수용 고무아스팔트 방수시트.Composite waterproof rubber asphalt waterproof sheet, characterized in that the release paper is further attached under the adhesive layer (10). 제5항에서,In claim 5, 상기 점착층(10)은 핫멜트 점착층으로 섬유포(11)가 함침되는 것을 특징으로 하는 복합방수용 고무아스팔트 방수시트.The adhesive layer 10 is a composite waterproof rubber asphalt waterproof sheet, characterized in that the fiber cloth 11 is impregnated with a hot melt adhesive layer. 바탕면(C);Base surface (C); 상기 바탕면(C)에 이형지를 제거하면서 점착층의 점착력으로 부착 설치되는 제5항의 복합방수용 고무아스팔트 방수시트(S); 및,The composite waterproof rubber asphalt waterproof sheet (S) of claim 5, which is attached to the base surface (C) while removing the release paper and is attached by adhesive force of the adhesive layer; And, 상기 복합방수용 고무아스팔트 방수시트의 제1프라이머코팅층(40) 위로 형성되는 도막방수층(U);A coating waterproof layer (U) formed on the first primer coating layer 40 of the composite waterproof rubber asphalt waterproof sheet; 을 포함하여 구성되는 것을 특징으로 하는 복합방수구조.Complex waterproof structure, characterized in that comprises a. 제7항에서,In claim 7, 상기 복합방수용 고무아스팔트 방수시트(S)는 겹침이음으로 상호 연결하여 설치되는 것을 특징으로 하는 복합방수구조.The composite waterproof rubber asphalt waterproof sheet (S) is a composite waterproof structure, characterized in that the interconnection is installed by overlapping joints. 제7항에서,In claim 7, 상기 복합방수용 고무아스팔트 방수시트(S)는 상호간 간격을 두어 바탕면(C)이 노출되도록 배치한 후 노출된 바탕면(C)과 이웃하는 복합방수용 고무아스팔트 방수시트(S) 단부에 동시에 이음테이프(T)를 부착함으로 연결 설치되며,The composite waterproof rubber asphalt waterproof sheet (S) is disposed so as to expose the base surface (C) at intervals therebetween, and the joint surface at the same time on the exposed surface (C) and the neighboring composite waterproof rubber asphalt waterproof sheet (S) at the same time. Attached by attaching (T), 상기 도막방수층(U)은 상기 복합방수용 고무아스팔트 방수시트(S) 및 이음테이프(T) 위로 형성되는 것을 특징으로 하는 복합방수구조.The waterproof coating layer (U) is a composite waterproof structure, characterized in that formed on the composite rubber waterproofing waterproof sheet (S) and the joint tape (T). 제9항에서,In claim 9, 상기 이음테이프(T)는 상부 표면이 상기 복합방수용 고무아스팔트 방수시트의 제1프라이머코팅층(40)을 형성하는 프라이머에 의해 코팅처리되는 것을 특징으로 하는 복합방수구조.The joint tape (T) is a composite waterproof structure, characterized in that the upper surface is coated by a primer forming the first primer coating layer 40 of the composite rubber waterproofing waterproof sheet. 제7항에서,In claim 7, 바닥에서 수직으로 치켜 올라가는 바탕면(C)의 코너에는 상기 복합방수용 고무아스팔트 방수시트(S)가 폭이 좁은 테이프로 제작되어 코너 형태와 동일하게 바닥에서 수직으로 치켜 올라가도록 부착 설치되는 것을 특징으로 하는 복합방수구조.The composite waterproof rubber asphalt waterproof sheet S is made of a narrow tape at the corner of the base surface C, which is vertically raised from the bottom, and is installed to be vertically raised from the bottom in the same manner as the corner shape. Composite waterproof structure.
KR1020060043317A 2005-12-14 2006-05-15 Improved asphalt waterproof sheets and waterproof structure using the same KR100648177B1 (en)