KR100587238B1 - Noninflammability interior decoration panel and method for manufacturing the same - Google Patents

Noninflammability interior decoration panel and method for manufacturing the same Download PDF

Info

Publication number
KR100587238B1
KR100587238B1 KR1020040076462A KR20040076462A KR100587238B1 KR 100587238 B1 KR100587238 B1 KR 100587238B1 KR 1020040076462 A KR1020040076462 A KR 1020040076462A KR 20040076462 A KR20040076462 A KR 20040076462A KR 100587238 B1 KR100587238 B1 KR 100587238B1
Authority
KR
South Korea
Prior art keywords
panel
weight
veneer
layer
resin
Prior art date
Application number
KR1020040076462A
Other languages
Korean (ko)
Other versions
KR20060027598A (en
Inventor
민병권
Original Assignee
성신종합목재(주)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 성신종합목재(주) filed Critical 성신종합목재(주)
Priority to KR1020040076462A priority Critical patent/KR100587238B1/en
Publication of KR20060027598A publication Critical patent/KR20060027598A/en
Application granted granted Critical
Publication of KR100587238B1 publication Critical patent/KR100587238B1/en

Abstract

본 발명은 실내용 벽판재, 천장재, 인테리어용 장식 판재 등으로 널리 사용되는 내장판넬에서 석고판과 무늬목, 예를 들면, 비닐, 얇은 나무, 금속판, 월낫트, 오크, 나토, 티크, 오동과의 접착성을 강화시켜서 제작되는 불연성 내장판넬의 제조방법과 그 방법으로 제작된 불연성 내장판넬을 제공하기 위한 것이다. The present invention is a plaster board and veneer, such as vinyl, thin wood, metal plate, walnut, oak, natto, teak, paulownia in the interior panel widely used as interior wall boards, ceiling materials, interior decoration boards, etc. An object of the present invention is to provide a method for manufacturing a non-flammable interior panel manufactured by enhancing adhesion and a non-flammable interior panel manufactured by the method.

본 발명에서는 특히 상기 소지와 무늬목의 접착성을 강화시켜 주기 위해 에폭시 수지와 폴리아마이드 수지를 주제로 한 2액형 투명 프라이머를 사용한다.In the present invention, in order to enhance the adhesion between the base and veneer, a two-component transparent primer based on an epoxy resin and a polyamide resin is used.

불연성, 석고판넬, 무늬목, 에폭시 수지, 폴리아마이드 수지, 접착성Nonflammable, Gypsum Panel, Veneer, Epoxy Resin, Polyamide Resin, Adhesive

Description

불연성 내장판넬의 제조방법 및 그 방법에 의해 제조된 불연성 내장판넬{Noninflammability interior decoration panel and method for manufacturing the same}Non-flammable interior panel and method for manufacturing the same

도 1은 본 발명에 따른 불연성 내장판넬의 한 실시예의 단면도이다.1 is a cross-sectional view of one embodiment of a non-flammable interior panel according to the present invention.

도 2는 본 발명에 따른 불연성 내장판넬의 다른 실시예의 단면도이다.2 is a cross-sectional view of another embodiment of a non-flammable interior panel according to the present invention.

<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>

10,20 ---- 내장판넬 11,21 ---- 석고판넬10,20 ---- Interior Panel 11,21 ---- Gypsum Panel

12,22 ---- 프라이머 13,23 ---- 무늬목12,22 ---- primer 13,23 ---- veneer

24 ---- 수성본드 25 ---- 비닐시트24 ---- Aqueous Bond 25 ---- Vinyl Sheet

본 발명은 불연성 내장판넬의 제조방법 및 그 방법에 의해 제조된 불연성 내장판넬에 관한 것이다. 더욱 상세하게는 실내용 벽판재, 천장재, 인테리어용 장식 판재 등으로 널리 사용되는 내장판넬에서 석고판과 무늬목, 예를 들면, 비닐, 얇은 나무, 금속판, 월낫트, 오크, 나토, 티크, 오동과의 접착성을 강화시켜서 제작되는 불연성 내장판넬의 제조방법과 그 방법으로 제조된 불연성 내장판넬에 관한 것이 다.The present invention relates to a method for producing a nonflammable interior panel and a nonflammable interior panel manufactured by the method. More specifically, gypsum boards and veneers, such as vinyl, thin wood, metal plates, walnuts, oak, natto, teak, paulownia, etc., in interior panels that are widely used as interior wallboards, ceilings, and interior decorative boards. The present invention relates to a method for manufacturing a non-flammable interior panel manufactured by enhancing the adhesiveness of and a non-flammable interior panel manufactured by the method.

일반적으로 불연내장재는 원료인 석고를 주 재료로 하여 만들기 때문에 불연성이 매우 높으며, 석고 자체는 안정된 결정상태를 지니고 있어 습도, 온도 변화에 대해 안정성이 강하고, 시공 후에도 뒤틀림, 처짐, 균열 등의 신축 변형의 염려가 없어 내장재로서 널리 사용되고 있다. In general, non-combustible interior materials are made of gypsum as the main material, so it is highly incombustible, and the gypsum itself has a stable crystal state, which is stable against humidity and temperature changes. It is widely used as interior material because there is no concern.

상기 석고판넬은 보통 두 장의 석고보드 원지 사이에 안정된 결정상태의 석고가 판상으로 성형되어 있는 것으로 내장재의 구비조건인 불연, 단열, 차음 성능이 뛰어나다. 그 뿐만 아니라 공기의 단축으로 시공비를 절감할 수 있고 조립화 및 경량화 추세에도 적합할 뿐 아니라 경제성도 뛰어난 특징이 있다.The gypsum panel is usually formed in the form of a plate of stable crystalline gypsum between two sheets of gypsum board base material is excellent in the non-combustible, heat insulation, sound insulation performance of the interior materials. In addition, the construction cost can be reduced due to the shortening of air, and it is suitable for the assembly and light weighting trend, and also has excellent economical characteristics.

불연성 내장판넬로서 앞에서 설명한 바와 같이 석고판넬은 물론 세라믹 판넬, 도자기 판넬 등 불연성, 내화성 판넬이 여러 가지 공지되어 있기는 하지만, 이들은 제조에 따른 원료비 및 고온 소성처리에 의한 가공비가 매우 높아 비교적 원가가 과중되고, 내화성, 보온성 및 내후성 면에서도 미흡하여 등록실용신안 제321,987호에서와 같이 산화마그네슘과 섬유포지와 같은 보강재로 불연성 내장재를 제작하여 내장판넬이 요구하는 내열성, 내화성, 보온성, 방음성, 장식성 등을 개선하려는 시도가 있었다.As described above, non-combustible and fire-resistant panels such as ceramic panels and porcelain panels as well as gypsum panels are known as non-flammable interior panels. In addition, in terms of fire resistance, heat resistance, and weather resistance, as described in Korean Utility Model No. 321,987, non-combustible interior materials are made of reinforcing materials such as magnesium oxide and fiber cloth, and the heat resistance, fire resistance, thermal insulation, sound insulation, decorative properties, etc. There was an attempt to improve.

그러나, 상기한 바와 같이 석고판넬, 세라믹 판넬, 도자기 판넬은 물론 물성을 개선시킨 산화마그네슘 판넬을 미장합판으로 사용할 경우 여러 가지 문제를 야기시키고 있다.However, gypsum panels, ceramic panels, porcelain panels as well as magnesium oxide panels with improved physical properties as described above are causing various problems.

일반적으로 미장합판이라 함은 합판, 보드, 불연내장재와 같은 석고판넬 등 의 한면이나 양면에 무늬목, 예를 들면, 비닐, 얇은 나무, 금속판, 월낫트, 오크, 나토, 티크, 오동 등을 붙인 것을 말하는데, 목재의 아름다운 무늬를 그대로 살린 인테리어 자재로 각광을 받고 있다. 이러한 미장합판은 원하는 판넬 소지에 접착제를 도포하고, 도포된 접착제 위에 무늬목을 원하는 크기로 재단하고 무늬에 맞게 올려놓은 다음에 프레스에 투입하여 일정시간 가압하여서 제조를 하고 있다. In general, unspecified plywood refers to a piece of veneer, board, gypsum panel such as non-flammable linings, and with veneer, such as vinyl, thin wood, metal plates, walnuts, oak, natto, teak, paulownia, etc. In other words, it is spotlighted as an interior material utilizing the beautiful pattern of wood. Such a plywood is manufactured by applying an adhesive to the desired panel holding, cutting the veneer to the desired size on the applied adhesive and put it on the pattern, and then put it in a press to press for a predetermined time.

보통 상기 무늬목 접착제로는 에멀젼계 수지를 주성분으로 하는 접착제로서 1,3-부타디엔의 스티렌 중합체 90 내지 95중량%, 폴리우레탄 수지 0 내지 2중량%, 지방족 폴리이소시아네이트 1 내지 5중량% 및 기타 첨가제 0 내지 2중량%로 구성되어 판넬 소지에 대한 접착력이 우수하고, 포름알데히드(HCHO) 및 휘발성 유기화합물이 방출되지 않으며, 휘발성 유기화합물의 규제에 대응할 수 있는 친환경 무늬목 접착제로서 최근 들어 마루바닥재에 대한 접착제로 널리 사용되고 있다. Usually, the veneer adhesive is an adhesive based on an emulsion resin, 90 to 95% by weight of styrene polymer of 1,3-butadiene, 0 to 2% by weight of polyurethane resin, 1 to 5% by weight of aliphatic polyisocyanate, and other additives 0 It is composed of 2% by weight to excellent adhesion to the panel material, formaldehyde (HCHO) and volatile organic compounds are not released, and as an eco-friendly veneer adhesive that can cope with the regulation of volatile organic compounds in recent years adhesive to flooring materials It is widely used.

상기 친환경 무늬목 접착제는 1액형으로서 포름알데히드 및 중금속, 암모니아 등 인체에 유해한 원료를 사용하지 않고, 휘발성 유기 화합물의 사용도 최소화하였고, 접착제의 냄새도 최소화하여 작업성이 우수한 특징이 있는 반면에 접착력이 약하여 장시간 사용 후에 무늬목을 합판이나 보드로부터 작은 힘에도 불구하고, 쉽게 박리되는 문제점이 있다. 특히 석고보드의 경우 분진(가루)이 무늬목에 묻어서 무늬목의 접착력을 떨어뜨리는 문제가 있었다. The eco-friendly veneer adhesive is a one-component type, does not use harmful materials such as formaldehyde, heavy metals, and ammonia, minimizes the use of volatile organic compounds, and minimizes the smell of the adhesive. It is weak and there is a problem that the veneer peels off easily from the plywood or board after long time use. Especially in the case of gypsum board dust (powder) was buried in the veneer had a problem of dropping the adhesion of the veneer.

이에 따라 본 발명은 종래의 이와 같은 문제점을 해결하기 위한 것으로 석고판넬 소지에 특수하게 개선된 프라이머 계통의 수지를 코팅하여 본 조성물이 석고판넬 소지에 흡수 및 하드코팅처리됨으로써 석고판넬 소지에 대한 무늬목의 부착성, 침투성, 내마모성을 우수하게 하여 보다 견고하게 무늬목이 부착되어 있는 불연성 내장판넬을 제조하고자 하는데 그 목적이 있는 것이다. Accordingly, the present invention is to solve such a problem of the prior art by coating a resin of the primer system specially improved on the gypsum panel base material by absorbing and hard coating the gypsum panel base material of the veneer for the gypsum panel body The purpose is to produce a non-flammable interior panel that is more firmly attached to the veneer by excellent adhesion, permeability, wear resistance.

본 발명은 석고판넬, 도자기 판넬, 시멘트 판넬 또는 산화마그네슘 판넬의 소지에 에폭시 수지와 폴리아마이드 수지를 주제로 한 2액형 투명 프라이머를 도포하고, 건조 후에 각종 접착제를 도포한 후 그 위에 무늬목, 비닐시트, 금속시트 또는 종이시트 등을 적층하여 약 110 내지 130℃에서 30초 내지 3분간 열압착시킨 후 냉각시켜서 일체화시켜서 되는 것을 특징으로 한다. The present invention is to apply a two-component transparent primer on the basis of epoxy resin and polyamide resin on the base of gypsum panel, porcelain panel, cement panel or magnesium oxide panel, and after applying various adhesives after drying, veneer, vinyl sheet , Metal sheets or paper sheets, etc. are laminated, thermo-compressed at about 110 to 130 ° C. for 30 seconds to 3 minutes, and then cooled and integrated.

또한, 본 발명에 의하면, 석고판넬, 도자기판넬, 시멘트판넬 또는 산화마그네슘판넬로 이루어진 소지층, 그의 표면에 도포된 에폭시 수지와 폴리아마이드 수지를 주재로 한 2액형 투명 프라이머층 및 접착제가 도포된 그의 표면에 열압착된 무늬목층으로 구성되어 있는 불연성 내장판넬인 것을 특징으로 한다. In addition, according to the present invention, a base layer composed of a gypsum panel, porcelain panel, cement panel or magnesium oxide panel, a two-component transparent primer layer mainly composed of an epoxy resin and a polyamide resin applied to the surface thereof, and an adhesive coated thereon It is characterized in that the non-combustible interior panel is composed of a veneer layer thermally pressed on the surface.

본 발명에 의하면, 상기 접착제층 위에 비닐시트를 적층하기 전에 비닐 접착제의 습기 흡수를 위해 얇은 목재 시트를 추가로 적층할 수 있다. According to the present invention, before laminating the vinyl sheet on the adhesive layer, a thin wood sheet may be further laminated for moisture absorption of the vinyl adhesive.

이하 본 발명을 첨부한 도면에 의거하여 더욱 상세하게 설명하면 다음과 같다. Hereinafter, the present invention will be described in more detail with reference to the accompanying drawings.

첨부도면 중 도 1은 본 발명의 불연성 내장판넬의 한 실시예의 단면도이고, 도 2는 본 발명의 불연성 내장판넬의 다른 실시예의 단면도이다. 1 is a cross-sectional view of one embodiment of the non-flammable interior panel of the present invention, Figure 2 is a cross-sectional view of another embodiment of the non-flammable interior panel of the present invention.

본 발명에 따른 불연성 내장판넬의 제조는 먼저 석고판넬, 도자기 판넬, 시멘트 판넬 또는 산화마그네슘 판넬의 소지에 에폭시 수지와 폴리아마이드 수지를 주제로 한 2액형 투명 프라이머를 도포한다.In the manufacture of the non-combustible interior panel according to the present invention, first, a two-component transparent primer based on epoxy resin and polyamide resin is applied to a base of gypsum panel, porcelain panel, cement panel or magnesium oxide panel.

본 발명에서 사용하는 2액형 투명 프라이머는 에폭시 수지와 폴리아마이드 수지를 주성분으로 하되 에폭시 수지 30 내지 40중량%, 우레아 수지 1 내지 5중량%, 크실렌 수지 50 내지 55중량% 및 이소부틸 알콜 10 내지 15중량%로 이루어진 제 1조성과 경화제로서 폴리아마이드 수지 45 내지 50중량%, 2,4,6-(디메틸아미노메틸)페놀 1 내지 5중량%, 크실렌 40 내지 45중량%, 이소부틸알콜 1 내지 5중량%, 부틸 셀루졸브 1 내지 5중량%, 메틸이소부틸케톤 1 내지 5중량%로 이루어진 제 2조성이 무게비로 약 4 : 1로 배합되어서 구성된 것이다. The two-component transparent primer used in the present invention has an epoxy resin and a polyamide resin as main components, but 30 to 40% by weight of epoxy resin, 1 to 5% by weight of urea resin, 50 to 55% by weight of xylene resin and 10 to 15 isobutyl alcohol. The first composition and the curing agent consisting of weight percent of 45 to 50% by weight of polyamide resin, 1 to 5% by weight of 2,4,6- (dimethylaminomethyl) phenol, 40 to 45% by weight of xylene, 1 to 5 of isobutyl alcohol A second composition consisting of% by weight, 1-5% by weight of butyl cellulsolve, and 1-5% by weight of methyl isobutyl ketone, is formulated by mixing about 4: 1 by weight ratio.

본 발명에서 사용하는 에폭시 수지는 에피클로로히드린과 비스페놀 A를 반응시켜 생성된 통상의 에폭시 수지로서, 전체 프라이머 조성물 중에서 30 내지 40중량%가 바람직하다. 만일 30중량% 미만으로 사용할 경우에는 프라이머 조성물의 내열성과 내화학성이 떨어지게 되는 문제점이 발생할 뿐 아니라 침투력 및 접착력도 감소하는 문제가 발생하게 되고, 반대로 40중량%를 초과하여 사용할 경우에는 첨가효과가 나타나지 않거나 경제적이지 못한 문제가 발생하게 되므로 상기 범위로 첨가하여 사용하는 것이 좋다.The epoxy resin used in the present invention is a conventional epoxy resin produced by reacting epichlorohydrin and bisphenol A, and preferably 30 to 40% by weight in the total primer composition. If less than 30% by weight, not only the heat resistance and chemical resistance of the primer composition are degraded, but also a problem of decreasing the penetration and adhesive strength. On the contrary, when used in excess of 40% by weight, the additive effect does not appear. It is good to use it in addition to the above range because it causes a problem that is not economical.

보통 수용액으로 사용하는 우레아 수지는 요소와 알데히드류(주로 포름알데히드)의 축합반응으로 생기는 저분자의 열경화성 수지로서, 상기 에폭시 수지와 같이 1중량% 미만으로 사용할 경우에는 프라이머 조성물의 내수성이 떨어지고, 옥외에서의 내구성이 없어지는 문제가 발생하게 되고, 반대로 5중량%를 초과하여 사용 할 경우에는 합판, 목재, 장식류 등의 접착성을 오히려 떨어뜨릴 뿐 아니라 그에 따른 상승효과가 발생하지 않아 경제적이지 못한 문제점이 있게 된다.Urea resin, usually used as an aqueous solution, is a low-molecular thermosetting resin produced by condensation reaction between urea and aldehydes (primarily formaldehyde). The problem of loss of durability will occur, and in contrast, when used in excess of 5% by weight, not only the adhesiveness of plywood, wood, and ornaments will be lowered, but also a synergistic effect will not occur. Will be.

본 발명에서 사용하는 크실렌 수지도 상기 에폭시 수지나 우레아 수지와 같이 50중량% 미만으로 사용할 경우에는 접착력이 감소하게 되고, 반대로 55중량%를 초과하여 사용할 경우에는 사용량의 과다로 인하여 오히려 물성의 저하를 초래하는 문제가 있다.The xylene resin used in the present invention also decreases the adhesive strength when used in an amount of less than 50% by weight, such as the epoxy resin or urea resin. There is a problem that results.

이소부틸알콜은 본 발명의 프라이머 조성물에서 계면활성제로 사용되며, 만일 10중량% 미만으로 사용할 경우에는 요제로서의 역할을 제대로 하지 못하게 되고, 반대로 15중량%를 초과하여 사용할 경우에는 프라이머 조성물의 접착력을 떨어뜨리는 부작용을 발생시키게 된다.Isobutyl alcohol is used as a surfactant in the primer composition of the present invention, if it is used less than 10% by weight does not function properly as a urea, on the contrary, when used in excess of 15% by weight, the adhesion of the primer composition is lowered Degradation will cause side effects.

한편, 본 발명에 따른 경화제(가교제)로서, 폴리아마이드 수지는 다이머(Dimer)산과 폴리아민의 축합반응에 의해 생성하는 것으로 분자 중에 반응성의 제1 및 제2 아민기를 갖는 구조로 저 연화점, 고점도의 선상 고분자로 생성되는 바, 전체 경화제 조성물에서 45 내지 50중량%로 사용하는 것이 바람직한데, 만일 상기 범위를 벗어날 경우에는 가교제로서의 효과가 미약하여 전체적으로 프라이머 조성물의 접착성능을 감소시키는 문제가 발생하게 된다. On the other hand, as a curing agent (crosslinking agent) according to the present invention, the polyamide resin is produced by the condensation reaction of dimer acid and polyamine, and has a low softening point and a high viscosity linear structure with a structure having reactive first and second amine groups in the molecule. It is preferable to use 45 to 50% by weight of the total curing agent composition in the polymer composition. If it is out of the above range, the effect as a crosslinking agent is weak, resulting in a problem of reducing the adhesive performance of the primer composition as a whole.

2,4,6-(디메틸아미노메틸)페놀은 페놀과 포름알데히드와의 부가축합물로서 1 내지 5중량%의 범위를 벗어나서 첨가할 경우에는 내열성, 난연성 등의 성능이 떨어지는 문제가 발생하게 되므로 상기의 범위내로 첨가하는 것이 바람직하다.Since 2,4,6- (dimethylaminomethyl) phenol is an addition condensate of phenol and formaldehyde, when added outside the range of 1 to 5% by weight, problems such as poor heat resistance and flame retardancy may occur. It is preferable to add in the range of.

본 발명에 따른 경화제로서 상기 크실렌은 40 내지 45중량%의 범위로 사용하 는 것이 바람직하며, 만일 상기 범위를 벗어날 경우에는 경화제로서의 역할이 미미하게 된다.As the curing agent according to the present invention, the xylene is preferably used in the range of 40 to 45% by weight, and if it is out of the range, the role of the curing agent becomes insignificant.

본 발명의 경화제에서 용제로서는 이소부틸알콜 1 내지 5중량%, 부틸 셀루졸브 1 내지 5중량%, 메틸이소부틸케톤 1 내지 5중량%를 사용하는 것이 바람직하며, 상기 제 1조성의 주제와 제 2조성의 경화제는 무게비로 약 4 : 1로 배합하는 것이 바람직하다. 상기 주제와 경화제를 배합하는 과정에서 약간의 열이 발생하게 되는데, 경화시간이 빨라질수록 열은 더 많이 발생하게 되며, 상기 배합비율을 벗어나서 배합할 경우에는 더 많은 열이 발생하게 되어 제품의 품질을 떨어뜨리게 되어 바람직하지 못하다. In the curing agent of the present invention, it is preferable to use 1 to 5% by weight of isobutyl alcohol, 1 to 5% by weight of butyl cellulsolve, and 1 to 5% by weight of methyl isobutyl ketone. It is preferable to mix | blend the hardening | curing agent of a composition by about 4: 1 by weight ratio. In the process of blending the subject and the curing agent, a little heat is generated. The faster the curing time, the more heat is generated, and when blended outside the blending ratio, more heat is generated to improve the quality of the product. It is not desirable to drop it.

상기한 바와 같이 판넬 소지에 프라이머 코팅 건조후 접착제층을 90 내지 120 g/㎡으로 도포한 후 그 위에 무늬목, 금속시트 또는 종이를 적층하고 약 110 내지 130℃에서 30초 내지 3분간 열압 프레스를 이용하여 압착시킨 후 냉각시켜서 일체화시키게 되면 본 발명에 따른 불연성 내장판넬이 얻어지게 된다.As described above, after the primer coating is dried on the panel material, the adhesive layer is applied at 90 to 120 g / m 2, and then the veneer, metal sheet or paper is laminated thereon, using a hot press for about 30 seconds to 3 minutes at about 110 to 130 ° C. After compression, after cooling, to integrate the non-combustible interior panel according to the present invention.

이와 같은 본 발명의 불연성 내장판넬(10)은 첨부도면 중 도 1에 나타낸 바와 같이 석고판넬, 도자기판넬, 시멘트판넬 또는 산화마그네슘판넬로 이루어진 소지층(11), 그의 표면에 도포된 에폭시 수지와 폴리아마이드 수지를 주재로 한 2액형 투명 프라이머층(12) 및 접착제가 도포된 그의 표면에 열압착된 무늬목, 금속 시트 또는 종이층(13)으로 구성되어 있다.Such non-flammable interior panel 10 of the present invention is a base material layer 11 consisting of a gypsum panel, porcelain panel, cement panel or magnesium oxide panel, as shown in Figure 1 of the accompanying drawings, the epoxy resin and poly coated on the surface thereof It consists of the two-component transparent primer layer 12 mainly based on an amide resin, and the veneer, metal sheet, or paper layer 13 heat-compressed on the surface by which the adhesive agent was apply | coated.

또한, 본 발명의 불연성 내장판넬(20)의 다른 실시예에 의하면, 첨부 도면 중 도 2에 나타낸 바와 같이 석고판넬, 도자기판넬, 시멘트판넬 또는 산화마그네슘판넬로 이루어진 소지층(21), 그의 표면에 도포된 에폭시 수지와 폴리아마이드 수지를 주재로 한 2액형 투명 프라이머층(22), 접착제가 도포된 그의 표면에 열압착된 무늬목, 금속 시트 또는 종이층(23), 상기 무늬목, 금속시트 또는 종이층(23) 위에 도포되는 수성본드층(24) 및 상기 수성본드층(24)에 접착되는 비닐시트층(25)으로 구성되어 있다.In addition, according to another embodiment of the non-combustible interior panel 20 of the present invention, as shown in Figure 2 of the accompanying drawings, the base layer 21 made of a gypsum panel, porcelain panel, cement panel or magnesium oxide panel, the surface thereof Two-component transparent primer layer 22 mainly based on the applied epoxy resin and polyamide resin, veneer, metal sheet or paper layer 23, and the veneer, metal sheet or paper layer, which are thermocompression-bonded to the surface of which adhesive is applied It consists of the aqueous bond layer 24 apply | coated on (23), and the vinyl sheet layer 25 adhere | attached on the said aqueous bond layer 24. As shown in FIG.

상기 석고판넬, 도자기판넬, 시멘트판넬 또는 산화마그네슘판넬의 소지층(21)에 프라이머 작업을 한 후 비닐시트를 부착할 경우, 비닐시트의 부착을 위해 수성본드를 사용하게 된다. 하지만, 수성본드의 습기가 판넬 바닥이나 비닐시트의 어느 방향이든 흡입이 되어야 하지만, 판넬 바닥에는 프라이머 도장이 되어 있고, 비닐시트 자체는 수분을 흡수하지 못하므로 중간층에 먼저 얇은 나무판과 같은 무늬목을 부착하고, 그 위에 수성본드를 도포한 후에 비닐시트를 부착하는 방법이 가장 바람직하다. When the vinyl sheet is attached after the primer work on the base layer 21 of the gypsum panel, porcelain panel, cement panel or magnesium oxide panel, an aqueous bond is used to attach the vinyl sheet. However, the moisture of the water-based bond should be sucked in either direction of the panel floor or vinyl sheet, but the panel floor is primed and the vinyl sheet itself does not absorb moisture. Most preferred is a method of adhering and applying a vinyl sheet after applying the aqueous bond thereon.

본 발명의 불연성 내장판넬은 특수하게 조제된 에폭시 수지와 폴리아마이드 수지를 주제로 한 2액형 투명 바나쉬를 사용하므로 불연 내장재인 석고판넬에 대한 무늬목의 부착성을 향상시켜 주어 장기동안 내장재로 사용하여도 무늬목이 박리되지 않으며, 석고판넬에 대한 코팅시 침투성 및 내마모성도 우수하고, 내수성, 내약품성도 우수하여 내장재로서 우수한 효과를 발휘하는 특징이 있다.The non-flammable interior panel of the present invention uses a two-component transparent varnish based on a specially formulated epoxy resin and polyamide resin, thereby improving the adhesion of veneer to the plaster panel, which is a non-combustible interior material, to be used as interior materials for a long time. It does not peel off the veneer, it is excellent in permeability and abrasion resistance when coating the gypsum panel, and also excellent in water resistance and chemical resistance, it has the characteristics of showing an excellent effect as interior materials.

Claims (4)

석고판넬, 도자기 판넬, 시멘트 판넬 또는 산화마그네슘 판넬의 소지에 에폭시 수지와 폴리아마이드 수지를 주제로 한 2액형 투명 프라이머를 코팅 및 건조시킨 후 접착제를 도포하고, 그 위에 무늬목, 금속시트 또는 종이를 적층하여 약 110 내지 130℃에서 30초 내지 3분간 열압착시킨 후 냉각시켜서 일체화시켜서 되는 것을 특징으로 하는 불연성 내장판넬의 제조방법. Gypsum panels, porcelain panels, cement panels or magnesium oxide panels are coated and dried with two-component transparent primers based on epoxy resins and polyamide resins, and then coated with adhesive, and laminated veneer, metal sheets or paper on them. The method for producing a non-combustible interior panel, characterized in that the thermocompression bonding for about 30 seconds to 3 minutes at about 110 to 130 ℃ then cooled to integrate. 제 1항에 있어서, 상기 프라이머는 에폭시 수지 30 내지 40중량%, 우레아 수지 1 내지 5중량%, 크실렌 수지 50 내지 55중량% 및 이소부틸 알콜 10 내지 15중량%로 이루어진 제 1조성과 경화제로서 폴리아마이드 수지 45 내지 50중량%, 2,4,6-(디메틸아미노메틸)페놀 1 내지 5중량%, 크실렌 40 내지 45중량%, 이소부틸알콜 1 내지 5중량%, 부틸 셀루졸브 1 내지 5중량%, 메틸이소부틸케톤 1 내지 5중량%로 이루어진 제 2조성이 무게비로 약 4 : 1로 배합되어서 구성된 것을 특징으로 하는 에폭시 수지와 폴리아마이드 수지를 주성분으로 하는 2액형 투명 프라이머를 사용하여서 되는 것을 특징으로 하는 불연성 내장판넬의 제조방법.The method of claim 1, wherein the primer is a first composition comprising 30 to 40% by weight of epoxy resin, 1 to 5% by weight of urea resin, 50 to 55% by weight of xylene resin and 10 to 15% by weight of isobutyl alcohol. Amide resin 45-50%, 2,4,6- (dimethylaminomethyl) phenol 1-5%, xylene 40-45%, isobutyl alcohol 1-5%, butyl cellulsolve 1-5% The second composition consisting of 1 to 5% by weight of methyl isobutyl ketone is blended in a weight ratio of about 4: 1 by using a two-component transparent primer composed mainly of an epoxy resin and a polyamide resin. Method for producing a non-flammable interior panel. 석고판넬, 도자기판넬, 시멘트판넬 또는 산화마그네슘판넬로 이루어진 소지층(11), 그의 표면에 도포된 에폭시 수지와 폴리아마이드 수지를 주재로 한 2액형 투명 프라이머층(12) 및 접착제가 도포된 그의 표면에 열압착된 무늬목, 금속 시트 또는 종이층(13)으로 구성되어 있는 것을 특징으로 하는 불연성 내장판넬(10).A base layer 11 composed of gypsum panel, porcelain panel, cement panel or magnesium oxide panel, a two-component transparent primer layer 12 mainly based on an epoxy resin and a polyamide resin applied to the surface thereof, and a surface thereof coated with an adhesive Non-combustible interior panel (10), characterized in that it is composed of a veneer, a metal sheet or a paper layer (13) thermocompression bonding. 석고판넬, 도자기판넬, 시멘트판넬 또는 산화마그네슘판넬로 이루어진 소지층(21), 그의 표면에 도포된 에폭시 수지와 폴리아마이드 수지를 주재로 한 2액형 투명 프라이머층(22), 접착제가 도포된 그의 표면에 열압착된 무늬목, 금속 시트 또는 종이층(23), 상기 무늬목, 금속시트 또는 종이층(23)위에 도포되어 있는 수성본드층(24), 및 상기 수성본드층(24)의 표면에 접착되어 있는 비닐시트층(25)로 구성되어 있는 것을 특징으로 하는 불연성 내장판넬(20).A base layer 21 composed of gypsum panel, porcelain panel, cement panel or magnesium oxide panel, a two-component transparent primer layer 22 mainly based on epoxy resin and polyamide resin applied to the surface thereof, and a surface thereof coated with an adhesive Adhered to the surface of the veneer, metal sheet or paper layer 23, the aqueous bond layer 24 applied on the veneer, metal sheet or paper layer 23, and the aqueous bond layer 24. Non-combustible interior panel 20, characterized in that consisting of a vinyl sheet layer 25.
KR1020040076462A 2004-09-23 2004-09-23 Noninflammability interior decoration panel and method for manufacturing the same KR100587238B1 (en)