KR100457320B1 - A textile machine for finishing water repellent to the surface layer - Google Patents
A textile machine for finishing water repellent to the surface layer Download PDFInfo
- Publication number
- KR100457320B1 KR100457320B1 KR10-2002-0071349A KR20020071349A KR100457320B1 KR 100457320 B1 KR100457320 B1 KR 100457320B1 KR 20020071349 A KR20020071349 A KR 20020071349A KR 100457320 B1 KR100457320 B1 KR 100457320B1
- Authority
- KR
- South Korea
- Prior art keywords
- fiber
- water repellent
- present
- surface layer
- processing
- Prior art date
Abstract
본 발명은 이중 조직을 갖는 섬유의 표면층에만 발수 가공을 처리할 수 있는 섬유가공 기계의 제조 방법에 관한 것이다.The present invention relates to a method for producing a fiber processing machine capable of treating water repellent only on the surface layer of a fiber having a double structure.
본 발명의 단면 발수기는 양면 조직을 갖는 섬유의 한 단면에만 선택적으로 액상 상태의 가공약제를 처리할 수 있어 특수 기능성을 섬유에 부여할 수 있다.The single-sided water repellent device of the present invention can selectively treat the processing agent in a liquid state only to one end face of the fiber having a double-sided structure, thereby imparting special functionality to the fiber.
본 발명의 단면 발수기는 두개의 상하 수직 이동형 장력 조절 가이드바가 존재하며 미세한 표면 요철을 갖는 그라비아 로우러와 액상의 가공약제를 담을 수 있는 저장조, 공기 흡입바 및 가공의 고착을 높여 주기 위한 열풍 건조관과 필요에 따라 이면층에 흡수 가공을 처리할 수 있는 스프레이 분사기로 구성된다.The cross-section water repellent of the present invention has two vertically vertical tension guide bar and a hot air drying to increase the adhesion of the storage tank, air suction bar and processing that can contain a gravure roller having a fine surface irregularities and liquid processing agent It consists of a pipe and a spray injector capable of treating the backing layer as needed.
Description
본 발명은 두개의 상하 수직 이동형 장력조절 가이드바(1)와 미세한 표면에 음각과 양각을 갖는 그라비아 로우러(2), 저장조(3) 그리고 이중조직을 갖는 섬유에 있어 섬유의 표면층(10)에만 발수가공을 처리시 그 반대면인 이면층(11)에 전이되는 것을 억제시켜 주는 공기 흡입바(4) 및 가공의 고착을 도와 주는 열풍 건조관(5)과 이면층(11)에 흡수가공을 선택적으로 처리할 수 있는 스프레이 분사기(6)로 구성된다.In the present invention, only the top and bottom vertically movable tension adjusting bar (1) and the gravure roller (2), the reservoir (3) and the double structure of the fiber having a double structure and the intaglio and embossing on the fine surface are only the surface layer (10) of the fiber. Absorption processing is applied to the air intake bar 4, which suppresses the transfer of water to the back surface layer 11 on the other side of the water repellent process, and the hot air drying tube 5 and the back layer 11, which help fix the process. It consists of a spray injector 6 which can be selectively treated.
종전의 섬유가공 기계는 액상 상태의 섬유 가공 약제를 섬유 표면의 어느 한 단면만 선택적으로 가공 처리할 수가 없으며 Pad법(침지법)으로 섬유의 표면층(10)과 이면층(11)에 동시에 약제가 침투된다. 또한 Gel 상태의 섬유 약제로 나이프코팅 처리하게 되면 섬유의 한 단면에만 선택적으로 가공 처리할 수 있지만 이 경우 섬유의 공극을 막게 되어 통기성을 유지할 수 없게 된다.Conventional fiber processing machine can not selectively process any cross-section of the fiber surface of the fiber processing agent in the liquid state, and the drug is applied simultaneously to the surface layer 10 and the back layer 11 of the fiber by the Pad method (immersion method). Infiltrate In addition, if the knife coating treatment with a gel fiber agent can be selectively processed to only one end surface of the fiber, in this case, it will not be able to maintain the air permeability to block the pores of the fiber.
본 발명은 통기성은 유지하되 섬유의 표면층(10)에만 액상의 섬유 가공 약제를 용이하게 처리할 수 있는 섬유 가공 기계에 관한 것이다.The present invention relates to a fiber processing machine that can maintain the breathability but can easily process a liquid fiber processing agent only on the surface layer (10) of the fiber.
본 발명의 목적은 액상의 섬유 가공 약제를 섬유의 표면층(10)에만 선별적으로 처리하여 발수기능을 부여하고 동시에 피부에 접촉하는 이면층(11)에는 흡수가공을 부여하여 원단에 동시에 두 기능을 발현시키기 위한 섬유기계를 제작키 위한것이다.It is an object of the present invention to selectively treat the liquid fiber processing agent only on the surface layer 10 of the fiber to impart a water repellent function, and at the same time to give the back layer 11 in contact with the skin absorbing processing to give both functions to the fabric at the same time. To make textile machinery to express.
도 1은 본 발명에 따른 섬유 단면 발수기의 측면도이다.1 is a side view of a fiber cross-section water repellent according to the present invention.
도 2는 본 발명에 따른 공기 흡입바의 평면도이다.2 is a plan view of an air intake bar according to the present invention.
도 3은 본 발명에 따른 스프레이 분사기의 측면도이다.3 is a side view of a spray injector according to the present invention.
<도면중 주요 부분에 대한 부호 설명><Description of Signs of Main Parts in Drawings>
1. 상하 수직 이동형 장력 조절 가이드바1. Vertically movable tension adjusting bar
2. 그라비아 로우러2. Gravure Roller
3. 저장조3. Storage tank
4. 공기 흡입바4. Air intake bar
5. 열풍 건조관5. Hot air drying tube
6. 스프레이 분사기6. Spray Injector
7. 일자형 홈7. Slotted groove
8. 노즐8. Nozzle
9. 일반 가이드 로우러9. General guide roller
10. 섬유의 표면층10. Surface layer of the fiber
11. 섬유의 이면층11. The back layer of fiber
이와 같은 과제들을 해결하기 위한 본 발명은 크게 두개의 상하 수직 이동형 장력조절 가이드바(1)와 미세하게 섬유의 표면층(10)에만 최소의 발수제를 처리할 수 있는 그라비아 로우러(2), 가공 약제를 담을 수 있는 저장조(3), 처리한 약제가 반대면인 이면층(11)에 전이되는 것을 막아 주는 공기 흡입바(4), 처리한 약제를 단시간내에 고착시켜 주는 열풍 건조관(5), 필요에 따라 피부에 접촉되는 섬유의 이면층(11)에 흡수가공을 처리할 수 있는 스프레이 분사기(6)로 구성된다.The present invention for solving these problems is large gravure roller (2), processing agent that can treat a minimum of the water repellent agent only two vertically vertical tension guide bar (1) and the fine surface layer 10 of the fiber A storage tank (3) capable of holding a, an air intake bar (4) which prevents the treated agent from being transferred to the back layer 11 on the opposite side, a hot air drying tube (5) which fixes the treated agent in a short time; It consists of the spray injector 6 which can process an absorption process to the back layer 11 of the fiber which contacts skin as needed.
이하 본 발명은 첨부 도면을 참조하여 상세하게 설명한다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.
먼저 본 발명의 섬유 단면 발수기는 도1과 같이 두개로 이루워진 상하 수직 이동형 장력조절 가이드바(1)와 음각과 양각을 갖는 그라비아 로우러(2), 액상의 가공약제를 담는 저장조(3), 동력장치가 달린 공기 흡입바(4), 130∼180℃의 온도로 섬유가공 약제를 고착시켜 주기 위한 열풍 건조관(5), 이면층(11)에 흡수가공을 처리할수 있는 노즐이 부착된 스프레이 분사기(6)로 구성된다.First, the fiber cross-section water repellent of the present invention is a vertical and vertical tension guide bar (1) made of two, as shown in Figure 1 and the gravure roller (2) having an intaglio and embossed, a reservoir containing a liquid processing agent (3) , Air suction bar 4 with power unit, hot air drying tube 5 for fixing the fiber processing agent at a temperature of 130 to 180 ° C., and a nozzle capable of treating the absorption process on the back layer 11 It consists of a spray injector 6.
본 발명의 기계는 단독 또는 기존의 섬유 건조를 목적으로 사용되는 텐터기에 연결하여 사용될 수 있다.The machine of the present invention can be used alone or in connection with a tenter used for the purpose of drying existing fibers.
상기 상하 수직 이동형 장력조절 가이드바(1)는 섬유의 표면층(10)에 발수가공을 할 때 섬유의 후도에 따라 상하 수직으로 이동하여 로우러에 닿는 섬유의 단면적과 장력을 조절하여 약제의 침투량을 결정하여 준다. 예를 들어 중량이 200g 이하인 얇은 원단인 경우 두개의 수직 이동형 정력조절 장치(1)를 상향 조정하여섬유면과 로우러면의 접촉 각도(θ)를 90°에 가깝게 조정하여 약제의 침투가 최소량이 되도록 하고 후도가 두꺼운 원단은 접촉 각도(θ)를 90°미만이 되도록 하여 약제 침투량을 높이도록 한다.The vertical vertical movement type tension adjusting guide bar (1) is moved up and down vertically according to the back of the fiber when water-repellent processing on the surface layer 10 of the fiber to adjust the cross-sectional area and tension of the fiber in contact with the roller to penetrate the drug To decide. For example, in the case of a thin fabric having a weight of 200 g or less, the two vertically movable stabilization devices 1 are adjusted upward to adjust the contact angle θ of the fiber surface and the roller surface close to 90 ° so that the penetration of the drug is minimal. In addition, the thick fabric has a contact angle θ of less than 90 ° to increase the penetration of the drug.
상기 그라비아 로우러(2)는 미세한 음각과 양각을 갖도록 설계된 Mesh 로우러로서 200g 이하의 중량을 갖는 얇은 후도의 원단에 최소의 발수 약제만을 도포할 수 있는 기능을 갖는다. 그러나 350g이 넘는 높은 후도의 직물은 그라비아 로우러가 아닌 일반 고무 로우러 방식으로도 코팅할 수 있다. 또한 상기 그라비아 로우러(2)는 동력장치를 연결시켜 자동으로 회전하도록 하여 가공 처리할 원단에 무리한 압력을 주지 말아야 한다.The gravure roller 2 is a mesh roller designed to have a fine engraving and embossment, and has a function of applying only a minimum water repellent to a thin thick fabric having a weight of 200 g or less. However, fabrics of more than 350 grams of high thickness can be coated with a conventional rubber roller rather than a gravure roller. In addition, the gravure roller (2) is to connect the power unit to automatically rotate so as not to apply excessive pressure on the fabric to be processed.
상기 공기 흡입바(4)는 발수제가 섬유의 표면층(10)에 처리되었을 때 이면층(11)으로 전이되지 않도록 흡입해 주는 기능을 갖는 원통형 흡입바(4)로서 그 상부에는 1∼3cm 폭의 일자형 홈(7)이 있고 그 말단부에는 동력장치가 연결되어 있어 공기로 약제를 흡입시켜 준다.The air suction bar 4 is a cylindrical suction bar 4 having a function of sucking the water repellent agent so as not to transfer to the back layer 11 when the water repellent is treated on the surface layer 10 of the fiber, and has a width of 1 to 3 cm on the upper side thereof. There is a straight groove (7) and the distal end is connected to the power unit to suck the medicine into the air.
상기 열풍 건조관(5)은 표면층(10)에 처리된 발수약제가 빠른 시간내에 고착되도록 도와 주는 기능을 갖게 되는데 건조관 내 온도는 원단 종류에 따라 100℃~180℃까지 선택적으로 조절될 수 있도록 설계되어야 하며 열손실을 막기 위해 밀폐형으로 하되 섬유면이 관에 닿지 않도록 제작한다.The hot air drying tube 5 has a function of helping the water repellent agent treated on the surface layer 10 to be fixed in a short time. The temperature in the drying tube can be selectively controlled to 100 ° C. to 180 ° C. according to fabric type. It should be designed and made to be sealed to prevent heat loss, but not to let the fiber surface touch the pipe.
상기 스프레이 분사기(6)는 1차 그라비아 로우러에서 처리한 발수 가공과 상반된 기능 예컨데 흡수가공을 섬유의 이면층(11)에 처리하기 위해 노즐(8)이 부착된 것으로서 상기 열풍 건조관에서 원단이 건조된 이후 섬유의 이면층(11)에 노즐에 의해 스프레이 방식으로 분사되도록 설계한다. 상기 스프레이 분사기는 이면층(11)이 흡수기능을 갖는 원단인 경우 필요에 따라 제외될 수도 있다.The spray injector 6 has a function opposite to the water-repellent process treated by the primary gravure roller, for example, a nozzle 8 is attached to the absorbent process to the back layer 11 of the fiber. It is designed to be sprayed by the nozzle to the back layer 11 of the fiber after drying. The spray injector may be excluded if necessary when the back layer 11 is a fabric having an absorption function.
본 발명은 기존 섬유가공 공장의 텐터기에 부착되어 사용되거나 단독으로도 사용될 수 있으며 작업시에는 섬유의 표면층(10)이 그라비아 로우러에 접촉되도록 밑으로 향하도록 한다.The present invention can be used to be attached to the tenter of the existing textile processing plant, or can be used alone, the working surface of the fiber 10 is directed downward to contact the gravure roller.
본 발명의 섬유 단면 발수기는 원하는 가공을 섬유의 어느 한 단면에만 선택적으로 처리할 수 있어 섬유의 부가율을 높힐 수 있다. 예를 들어 원단의 표면층(10)에는 발수기능, 피부면에 닿는 이면층(11)에는 흡수기능을 동시에 처리하여 최적의 스포츠용 원단을 제조할 수 있다.The fiber cross-section water repellent of the present invention can selectively process the desired processing on only one cross-section of the fiber to increase the addition rate of the fiber. For example, the surface layer 10 of the fabric, water repellent function, the back layer 11 in contact with the skin surface at the same time the absorption function can be processed at the same time to produce the optimal fabric for sports.
본 발명의 섬유 단면 발수기로 처리된 표면층(10) 발수기능과 이면층(11) 흡수기능은 아래와 같은 방법으로 평가하였다.The water repellent function and the water repellent function of the back layer 11 treated with the fiber cross-section water repellent of the present invention were evaluated by the following method.
· 표면 발수기능(%)Surface water repellency (%)
KSK0590 방법으로 측정하였다. 섬유의 시편을 30 x 30cm로 만든 후 45°각도로 비스름이 설치하여 물방울을 떨어 뜨린 후 섬유에 스며들지 않고 흘러 내린 물방울의 개수를 측정하였다. 이 수치가 높을수록 발수기능이 우수하다.It was measured by the KSK0590 method. After making the specimens of the fiber 30 x 30cm, the bismuth was installed at a 45 ° angle to drop the water droplets and then measured the number of water droplets that flowed without penetrating the fiber. The higher this value, the better the water repellency.
측정한 결과는 <표 1>과 같다.The measured results are shown in <Table 1>.
· 이면 흡수기능(mm/분)Back side absorption function (mm / min)
KSK0815. 5. 28. 1 방법으로 측정하였다. 섬유의 시편을 15 x 15cm로 만든 후 이를 반으로 접은 다음 그 끝을 45°각도로 예리하게 절단하여 물에 침지시켜 흡수된 면을 따라 올라온 섬유의 길이를 측정하였다.KSK0815. 5. Measured by 28. 1 method. Specimens of fibers were made 15 x 15 cm, then folded in half, and then the ends were sharply cut at 45 ° angles to be immersed in water to measure the length of the fibers along the absorbed surface.
측정한 결과는 <표 1>과 같다.The measured results are shown in <Table 1>.
(실시예 1)(Example 1)
이중 조직으로 제직된 100% 폴리에스테르 원단을 본 발명의 기계로 액상으로 만들어진 3%농도의 발수약제를 담은 용기에서 표면층(10)에만 그라비아 로우러로 처리한 후 흡입바를 통해 처리된 약제가 이면층(11)으로 전이되지 않도록 공기로 빨아들이고 150℃로 고정된 밀폐형 열풍 건조관에서 30초간 고착시킨 후 이어서 이면층(11)에 스프레이 분사기로 흡수 가공제를 처리하여 180℃ 텐터에서 3분간 고착시킨 후 물성을 평가하였다.In the container containing the 3% concentration of water-repellent agent made of liquid by the machine of the present invention, a 100% polyester fabric woven into a double tissue was treated with a gravure roller only on the surface layer 10, and then the medicine treated through the suction bar was the back layer. It was sucked with air so as not to transition to (11) and fixed in a closed hot air drying tube fixed at 150 ° C. for 30 seconds, followed by treating the backing layer 11 with an absorbent with a spray injector, and fixing it for 3 minutes at 180 ° C. tenter. After the physical properties were evaluated.
평가한 결과는 <표 1>과 같다.The evaluation results are shown in Table 1.
(실시예 2)(Example 2)
이중 조직으로 제직된 100% 면 원단을 본 발명의 기계로 액상으로 만들어진 4%농도의 발수약제를 담은 저장조에서 표면층(10)에만 그라비아 로우러로 발수가공을 처리한 후 흡입바를 통해 처리된 약제가 표면층(10)으로 전이되지 않도록 Air로 빨아들이고 160℃로 고정된 밀폐형 열풍 건조관에서 40초간 고착시킨 후 이어서 이면층(11)에 스프레이 분사기로 흡수가공제를 처리하여 180℃ 텐터에서 3분간 고착시킨 후 물성을 평가하였다.In the reservoir containing the 4% concentration of water repellent agent made of liquid in the liquid of the machine of the present invention, the 100% cotton fabric woven into the double tissue was treated with a gravure roller on the surface layer 10 only and then treated with a suction bar. Soaked with air to prevent transfer to the surface layer 10 and fixed in a closed hot air drying tube fixed at 160 ° C. for 40 seconds, followed by treating the backing layer 11 with an absorbent with a spray sprayer, and fixing it for 3 minutes at 180 ° C. tenter. After the physical properties were evaluated.
평가한 결과는 <표 1>과 같다.The evaluation results are shown in Table 1.
(비교실시예 1)Comparative Example 1
실시예 1과 동일한 원단을 o.w.f 3% 농도의 발수약제를 담은 저장조에서 표면층(10)과 이면층(11) 양면에 동시에 약제가 침투되도록 통상의 Pad법으로 처리한후 180℃ 텐터에서 3분간 고착하여 물성을 평가하였다.The same fabric as in Example 1 was treated in a reservoir containing a water repellent agent of owf 3% concentration by a conventional pad method to simultaneously infiltrate the drugs into both the surface layer 10 and the back layer 11, and then fixed for 3 minutes in a 180 ° C. tenter. The physical properties were evaluated.
평가한 결과는 <표 1>과 같다.The evaluation results are shown in Table 1.
(비교실시예 2)Comparative Example 2
실시예 2와 동일한 원단을 o.w.f 4% 농도의 흡수약제를 담은 용기에서 표면층(10)과 이면층(11) 양면에 동시에 약제가 침투되도록 통상의 Pad법으로 처리한 후 180℃ 텐터에서 3분간 고착하여 물성을 평가하였다.The same fabric as in Example 2 was treated in a container containing an owf 4% absorbent agent by a conventional Pad method to simultaneously infiltrate the drug into both the surface layer 10 and the back layer 11, and then fixed for 3 minutes in a 180 ° C. tenter. The physical properties were evaluated.
평가한 결과는 <표 1>과 같다.The evaluation results are shown in Table 1.
상기 <표 1>에서와 같이 실시예 1, 2는 비교실시예 1, 2에 비해 표면 발수와 이면 흡수 기능을 동시에 갖는다. 따라서 본 발명의 섬유가공 기계로 처리된 원단은 우천시에 방수기능과 운동시 땀 배출 기능을 동시에 갖기 때문에 각종 스포츠의류에 적합하다.As shown in Table 1, Examples 1 and 2 have a surface water repellency and a back surface absorption function as compared with Comparative Examples 1 and 2. Therefore, the fabric treated with the fiber processing machine of the present invention is suitable for various sports clothes because it has a waterproof function in rainy weather and a sweat discharge function during exercise.
본 발명의 섬유 단면 발수기는 원하는 가공을 섬유의 한 단면에만 선택적으로 처리할 수 있다. 예컨데 표면층(10)에는 오염방지 또는 방수를 목적으로 한 발수가공, 이면층(11)에는 땀 흡수력을 높혀 주는 흡수가공을 동시에 처리할 수 있어 고부가 섬유를 제조할 수 있다.The fiber cross-section water repellent of the present invention can selectively process the desired processing on only one side of the fiber. For example, the surface layer 10 can be treated with water repellent for the purpose of pollution prevention or waterproofing, and the back layer 11 can be treated simultaneously with the absorption processing to increase sweat absorption, thereby producing high value-added fibers.
본 발명은 첨부된 도면에 도시된 실시예를 참고로 설명하였으나 이는 예지적인 것에 불과하며 당해 기술분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능하다는 점을 이해할 수 있을 것이다. 따라서 본 발명의 진정한 보호범위는 첨부된 청구 범위에 의해서만 정해져야 할 것이다.Although the present invention has been described with reference to the embodiments shown in the accompanying drawings, this is only foreseeable and it will be understood by those skilled in the art that various modifications and equivalent other embodiments are possible. will be. Therefore, the true scope of protection of the present invention should be defined only by the appended claims.
Claims (3)