KR100331539B1 - Shadow-mask for Cathode Ray Tube - Google Patents
Shadow-mask for Cathode Ray Tube Download PDFInfo
- Publication number
- KR100331539B1 KR100331539B1 KR1020000027335A KR20000027335A KR100331539B1 KR 100331539 B1 KR100331539 B1 KR 100331539B1 KR 1020000027335 A KR1020000027335 A KR 1020000027335A KR 20000027335 A KR20000027335 A KR 20000027335A KR 100331539 B1 KR100331539 B1 KR 100331539B1
- Authority
- KR
- South Korea
- Prior art keywords
- shadow mask
- film
- ray tube
- cathode ray
- electron
- Prior art date
Abstract
본 발명은 섀도우마스크의 표면에 제올라이트를 주성분으로 하는 단열막과 산화텅스텐을 주성분으로 하는 전자반사막을 적층하고, 선택적으로 알루미늄을 주성분으로 하는 열전도막을 더 적층하여 도밍저감물질층을 형성함으로써, 도밍저감물질층이 열전자의 전자반사, 열전달 및 단열 역할을 복합적으로 갖기 때문에 섀도우마스크의 열적 변형을 감소하여 도밍 현상을 실질적으로 감소시킴과 아울러 스크린 상의 전자빔의 미스랜딩을 방지하여 음극선관의 색순도를 향상시킬 수 있는 음극선관용 섀도우마스크를 제공한다.According to the present invention, a doping reduction material layer is formed by stacking a zeolite-based heat insulating film and a tungsten oxide electron reflecting film on the surface of a shadow mask, and optionally further laminating a heat conductive film containing aluminum as a main component. Since the material layer has a combination of electron reflection, heat transfer, and thermal insulation of hot electrons, the thermal deformation of the shadow mask can be reduced, thereby substantially reducing the domming phenomenon, and preventing the mis-landing of the electron beam on the screen, thereby improving the color purity of the cathode ray tube. Provides a shadow mask for cathode ray tube.
Description
본 발명은 칼라 음극선관에 관한 것으로, 특히 섀도우마스크의 도밍량을 감소시키기 위하여 그 표면에 단열막과 전자반사막을 형성하거나 단열막, 열전도막 및 전자반사막을 순차적으로 형성하여 각 도막의 복합효과에 의한 도밍(Doming) 현상을 억제하는 음극선관용 섀도우마스크에 관한 것이다.The present invention relates to a color cathode ray tube, and in particular, in order to reduce the amount of shadowing of the shadow mask, a heat insulating film and an electron reflecting film are formed on the surface thereof, or a heat insulating film, a heat conductive film, and an electron reflecting film are sequentially formed to reduce the complex effect of each coating film. The present invention relates to a shadow mask for a cathode ray tube that suppresses a doming phenomenon caused by the same.
도 1은 일반적인 칼라 음극선관을 도시한 부분 단면도로서, 전방에 위치한 장방형의 패널(10)과, 패널의 후방에 위치한 펀넬(14), 그리고 펀넬의 끝단에서 연장 연결된 네크부(16)로 이루어진 진공용기가 전자의 원활한 비행을 위해 그 내부가 약 10-7Torr의 고진공으로 유지되어 있다.1 is a partial cross-sectional view of a typical color cathode ray tube, comprising a rectangular panel 10 positioned at the front, a funnel 14 positioned at the rear of the panel, and a vacuum consisting of a neck portion 16 extending from the end of the funnel. The vessel is maintained at a high vacuum of approximately 10 -7 Torr to allow the electrons to fly smoothly.
상기 패널(10)의 내측 표면에는 각각 적, 녹, 청의 색상으로 발광하는 형광체가 도트 혹은 스트라이프 형태로 도포되어진 형광막(12)이 형성되어져 있다.On the inner surface of the panel 10, there is formed a phosphor film 12 in which phosphors emitting in red, green, and blue colors are applied in the form of dots or stripes.
전자총(17)에서 방사되어진 전자빔은 전 화면 영역으로 편향시키는 편향요크(18)의 역할에 따라 화면 전체의 색선별 기능을 하는 섀도우마스크(20)를 통과한 후 형광막(12)에 도착하여 화면을 발광시키게 된다.The electron beam radiated from the electron gun 17 passes through the shadow mask 20, which performs the color discrimination function of the entire screen according to the role of the deflection yoke 18, which deflects to the entire screen area, and arrives at the fluorescent film 12. Will emit light.
이와 같이 구성된 칼라 음극선관에 전원이 인가되면 네크부(16)에 삽입된 전자총(17)으로부터 전자빔이 방사되고, 이 전자빔의 약 20%는 섀도우마스크(20)의 개공을 통과한 후 형광막(12)을 타격하여 형광체를 발광시키게 된다.When power is applied to the color cathode ray tube configured as described above, an electron beam is emitted from the electron gun 17 inserted into the neck portion 16, and about 20% of the electron beam passes through the opening of the shadow mask 20 and then the fluorescent film ( 12) strikes the phosphor to emit light.
한편, 전자빔의 나머지 80%는 섀도우마스크(20)의 면에 충돌하여 온도상승을일으키게 되고, 이에 따라 섀도우마스크(20)는 열팽창이 일어나게 되어 그 면이 부풀어오르는 도밍 현상이 일어나게 된다.Meanwhile, the remaining 80% of the electron beam collides with the surface of the shadow mask 20 to cause a temperature increase. As a result, the shadow mask 20 undergoes thermal expansion, thereby causing a dominant phenomenon in which the surface swells.
이로 인해서 미스랜딩이 증가하여 색순도가 저하되는 현상을 보이게 되는 것이다.As a result, mislanding increases and color purity decreases.
섀도우마스크(20)의 도밍 현상을 저감하기 위하여 섀도우마스크(20)의 전자빔 조사면에 피복층을 형성하는 여러 방안이 고안되어 시행되고 있다.In order to reduce the dope phenomenon of the shadow mask 20, various methods of forming a coating layer on the electron beam irradiated surface of the shadow mask 20 have been devised and implemented.
미국특허 제3,562,518호에서는 섀도우마스크(20)의 면에 산화 비스무스(Bi2O3)와 유리 성분으로 전자막을 형성하는 것이 제안되었고, 일본공개특허 소55-76553호에서는 텅스텐(W), 납(Pb), 비스무스(Bi) 등을 함유하는 전자반사층을 10㎛ 두께로 형성하는 것이 제안되었으나, 그 예에서는 다음과 같은 문제점이 노출되었다.In US Pat. No. 3,562,518, it is proposed to form an electron film with bismuth oxide (Bi 2 O 3 ) and a glass component on the surface of the shadow mask 20. In Japanese Patent Laid-Open No. 55-76553, tungsten (W), lead ( Although it has been proposed to form an electron reflection layer containing Pb), bismuth (Bi) and the like in a thickness of 10 µm, the following problems have been exposed in the example.
또한, 미국특허 제3,562,518호에서는 전자반사 효과는 있지만 5㎎/㎠ 이상 스프레이 도포할 경우에는 섀도우마스크(20)에 구성해 높은 홀의 막힘 현상이 발생하여 다량의 불량이 발생하며, 한국특허공개 제97-63326호에서는 텅스텐(W), 비스무스(Bi) 등을 함유하는 전자반사재를 30∼60중량% 가량 사용하여 인쇄 방식을 이용하여 일정한 두께로 막을 형성하여 도밍 현상을 억제하고 있다.In addition, US Patent No. 3,562,518 has an electron reflection effect, but when sprayed at 5mg / cm 2 or more, the mask is formed in the shadow mask 20 to cause a high hole clogging phenomenon, resulting in a large amount of defects. -63326 uses about 30 to 60% by weight of an electronic reflector containing tungsten (W), bismuth (Bi) and the like to form a film with a constant thickness by using a printing method to suppress the doming phenomenon.
그러나, 이와 같은 방식은 10㎛ 두께로 형성하면 전자반사 효과가 있으나 2∼3㎛ 정도로 얇게 도포하면 전자반사 효율이 약해 도밍저하 효과는 미약해 진다.However, this method has an electron reflection effect when formed to a thickness of 10㎛, but when applied thinly to about 2 ~ 3㎛ the electron reflection efficiency is weak and the dominant reduction effect is weak.
또한, 텅스텐을 이용하여 증착하거나 막을 형성하는 방안이 있으나, 섀도우마스크의 열처리하는 동안에 열처리 또는 프린트씰링 공정의 온도가 450∼500℃이기 때문에 텅스텐이 산화텅스텐(WO3)으로 변화되어 막의 박리 현상이 발생하기도 한다.In addition, there is a method of depositing or forming a film using tungsten, but since the temperature of the heat treatment or print sealing process is 450 to 500 ° C. during the heat treatment of the shadow mask, tungsten is changed to tungsten oxide (WO 3 ), thereby causing the film to be peeled off. Occurs.
전자반사막을 형성하는 방법은 통상적으로 전자반사물질, 바인더, 적당량의 알코올류 비이클 등을 이용, 슬러리화하여 스프레이 분사를 하거나 또는 고점성을 갖도록 점착물질을 제작하여 인쇄 방식으로 도포막을 형성하여 도막을 구성하기도 한다.In general, an electron reflection film is formed using an electron reflection material, a binder, an appropriate amount of alcohol vehicle, or the like by slurrying to spray spray, or by preparing an adhesive material to have a high viscosity and forming a coating film by printing. It may be configured.
그러나, 이와 같이 산화텅스텐(WO3), 비스무스(Bi) 등을 이용하여 제작한 도포막은 전자반사 효과에 한계가 있어 원하는 도밍 저감을 이룰 수 없다는 단점을 안고 있었다.However, the coating film produced by using tungsten oxide (WO 3 ), bismuth (Bi) and the like has a disadvantage in that the desired anti-doming reduction cannot be achieved because the electron reflection effect is limited.
따라서, 본 발명의 목적은 전자총에서 방사되는 열전자의 도밍 현상을 저감시키기 위하여 섀도우마스크의 표면에 단열효과를 위한 단열막과 열전도재인 알루미늄막 및 전자의 반사효과를 위한 전자반사막을 적어도 2개 이상 선별하여 적층함으로써, 섀도우마스크에 전달되는 열을 보다 효과적으로 차단하여 칼라 음극선관의 동작시 섀도우마스크가 부풀어오르는 도밍(Doming) 현상을 억제할 수 있는 음극선관용 섀도우마스크를 제공하는 데 있다.Accordingly, an object of the present invention is to select at least two heat insulating film for the heat insulating effect, aluminum film which is a heat conductive material and electron reflecting film for the reflection effect of electrons on the surface of the shadow mask in order to reduce the doming phenomenon of the hot electrons emitted from the electron gun. By stacking the layers, it is possible to more effectively block heat transmitted to the shadow mask to provide a shadow mask for a cathode ray tube that can suppress a dominant phenomenon in which the shadow mask swells when the color cathode ray tube is operated.
상기 목적을 달성하기 위한 본 발명의 기술적 수단은, 섀도우마스크를 포함하는 음극선관에 있어서, 상기 섀도우마스크의 표면에 제올라이트와 산화텅스텐을 포함하는 단열 기능 및 전자반사 기능을 하는 코팅층을 형성하며, 바람직하게는 상기 단열 기능의 코팅층은 제올라이트를 주성분으로 하는 단열막이고, 전자반사 기능의 코팅층은 산화텅스텐을 주성분으로 하는 전자반사막인 것을 특징으로 한다.Technical means of the present invention for achieving the above object, in the cathode ray tube including a shadow mask, to form a coating layer having a heat insulating function and an electron reflection function including zeolite and tungsten oxide on the surface of the shadow mask, Preferably, the coating layer of the heat insulating function is an insulating film containing zeolite as a main component, and the coating layer of the electron reflecting function is an electron reflecting film containing tungsten oxide as a main component.
아울러, 상기 섀도우마스크의 표면에 알루미늄을 주성분으로 하는 열전도막을 더 형성한 것을 특징으로 한다.In addition, a heat conductive film mainly containing aluminum is formed on the surface of the shadow mask.
도 1은 일반적인 음극선관의 단면을 나타낸 측면도이고,1 is a side view showing a cross section of a typical cathode ray tube,
도 2는 일반적인 섀도우마스크의 구조를 나타낸 도면이고,2 is a view showing the structure of a general shadow mask,
도 3은 본 발명의 일실시예에 의한 섀도우마스크의 코팅 구조를 나타낸 도면이고,3 is a view showing a coating structure of a shadow mask according to an embodiment of the present invention,
도 4는 본 발명의 다른 실시예에 의한 섀도우마스크의 코팅 구조를 나타낸 도면이고,4 is a view showing a coating structure of a shadow mask according to another embodiment of the present invention,
도 5는 본 발명에 적용한 스크린 인쇄 공정을 설명하기 위해 도시한 도면이고,5 is a view illustrating a screen printing process applied to the present invention,
도 6은 본 발명의 도밍양 측정 위치를 설명하기 위해 도시한 도면이다.FIG. 6 is a diagram for explaining a domming amount measuring position of the present invention. FIG.
* 도면의 주요 부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings
20: 섀도우마스크 21: 단열막20: shadow mask 21: insulating film
22: 열전도막(알루미늄) 23: 전자반사막22: heat conductive film (aluminum) 23: electron reflection film
21,22,23: 도밍저감물질층21,22,23: Domingo reducing material layer
이하, 첨부한 도면을 참조하여 본 발명을 보다 상세하게 살펴보고자 한다.Hereinafter, the present invention will be described in more detail with reference to the accompanying drawings.
도 2는 일반적인 섀도우마스크의 구조를 도시한 것으로, 전자빔 통과홀이 형성된 유효면(20-1)과 홀이 형성되어 있지 않은 비유효면(20-2)으로 이루어져 있고, 통상적으로 도밍(Doming) 방지를 위해 섀도우마스크(20)의 유효면(20-1)에 도밍저감물질을 형성한다.FIG. 2 illustrates a structure of a general shadow mask, and includes an effective surface 20-1 having an electron beam passing hole and an invalid surface 20-2 having no hole formed therein. In order to prevent the formation of the dominant reducing material on the effective surface 20-1 of the shadow mask 20.
도 3은 본 발명의 일실시예에 의한 섀도우마스크의 형성 구조를 보인 것으로, 섀도우마스크(20)의 표면에 단열효과를 위한 단열막(21)을 형성하고, 상기 단열막(21)의 상부에 전자의 반사효과를 위한 전자반사막(23)을 형성한 것을 도시하였다.Figure 3 shows the formation of the shadow mask according to an embodiment of the present invention, to form a heat insulating film 21 for the heat insulating effect on the surface of the shadow mask 20, the upper portion of the heat insulating film 21 The electron reflection film 23 for forming the electron reflection effect is shown.
도 4는 본 발명의 다른 실시예에 의한 섀도우마스크의 형성 구조를 보인 것으로, 섀도우마스크(20)의 표면에 단열효과를 위한 단열막(21)을 형성하고, 상기 단열막(21)의 상부에 열전도재인 알루미늄막(22)을 형성하고, 상기 알루미늄막(22)의 상부에 전자의 반사효과를 위한 전자반사막(23)을 순차적으로 형성한 것을 도시하였다.4 is a view illustrating a structure of forming a shadow mask according to another embodiment of the present invention, and forming a heat insulating film 21 for insulating effect on the surface of the shadow mask 20, and on top of the heat insulating film 21. An aluminum film 22, which is a thermal conductive material, is formed, and an electron reflection film 23 for sequentially reflecting electrons is formed on the aluminum film 22.
아울러, 본 발명에 의한 단열막(21), 알루미늄막(22), 전자반사막(23)은 섀도우마스크(20)의 유효면(20-1)에만 형성할 수도 있지만, 비유효면(20-2)까지 확장하여 형성하면 보다 큰 효과를 얻을 수 있다.In addition, although the heat insulation film 21, the aluminum film 22, and the electron reflection film 23 by this invention may be formed only in the effective surface 20-1 of the shadow mask 20, it is ineffective surface 20-2. If it is extended to), a greater effect can be obtained.
본 발명에 의한 섀도우마스크(20)는 음극선관의 동작시 전자빔의 충돌에 의한 섀도우마스크(20)의 표면 온도가 증가하는 것을 방지하며, 표면에서 발생하는 열이 차단되도록 하기 위하여 섀도우마스크(20)의 표면에 단열 효과가 우수한 소재인 제올라이트(Zeolite)를 이용하여 단열막(21)을 구성하고 그 상부에 재차 전자반사막(23)을 형성하여 음극선관 동작시 섀도우마스크(20)의 표면온도가 상승하는 것을 근본적으로 차단하는 도 3과 같은 구조로 구성되어 있다.The shadow mask 20 according to the present invention prevents the surface temperature of the shadow mask 20 from increasing due to the collision of the electron beam during operation of the cathode ray tube, and the shadow mask 20 to block heat generated from the surface. The surface temperature of the shadow mask 20 is increased during operation of the cathode ray tube by forming the insulating film 21 by using zeolite, which is a material having excellent heat insulating effect on the surface of the film, and again forming the electron reflecting film 23 thereon. It is composed of a structure as shown in Figure 3 that essentially blocks.
여기에서, 단열막(21)을 위해 사용하는 인쇄용 잉크는 용제와 바인더를 포함하는 비이클, 프릿 글라스(Frit Glass) 및 단열재 분말로 구성되는 데, 단열재 분말로는 미세한 다공성이 있는 제올라이트 분말을 사용하며, 전자반사막(23)을 형성하기 위한 인쇄용 잉크는 용제와 바인더를 포함하는 비이클, 프릿 글라스 및 전자반사재로 구성되며, 전자반사재로서는 기존의 산화 텅스텐(WO3) 분말을 이용한다.Here, the printing ink used for the heat insulating film 21 is composed of a vehicle, a frit glass and a heat insulating material powder containing a solvent and a binder, the zeolite powder having a fine porosity is used as the heat insulating material powder The ink for printing for forming the electron reflection film 23 is composed of a vehicle, a frit glass, and an electron reflection material including a solvent and a binder, and conventional tungsten oxide (WO 3 ) powder is used as the electron reflection material.
이와 같은 방법으로 단열막(21)과 전자반사막(23) 사이에 열전도재인 알루미늄막(22)을 10 내지 50Å 두께로 증착하여 도 4와 같이 구성할 수도 있다.In this manner, an aluminum film 22, which is a thermal conductive material, is deposited between the heat insulating film 21 and the electron reflecting film 23 to have a thickness of 10 to 50 GPa, and may be configured as shown in FIG.
상기 단열막(21)을 형성하기 위한 인쇄용 잉크의 구성 성분 중 단열재는 대략 40 내지 60중량%를 사용하고, 프릿 글라스는 5 내지 20중량%를 사용하며, 비이클은 20 내지 55중량%를 사용한다. 그리고, 상기 전자반사막(23)을 형성하기 위한 인쇄용 잉크의 구성 성분 중 전자반사재는 대략 40 내지 60중량%를 사용하고, 프릿 글라스는 5 내지 20중량%를 사용하며, 비이클은 20 내지 55중량%를 사용한다.In the constituent components of the printing ink for forming the heat insulating film 21, the heat insulating material uses about 40 to 60% by weight, the frit glass uses 5 to 20% by weight, and the vehicle uses 20 to 55% by weight. . Then, among the components of the printing ink for forming the electron reflecting film 23, the electron reflecting material is used about 40 to 60% by weight, the frit glass is used 5 to 20% by weight, the vehicle 20 to 55% by weight Use
상기 단열재와 프릿글라스 및 비이클로 이루어진 혼합물질을 제조하여 소둔 공정이 완료된 섀도우마스크(20)에 인쇄방식으로 10 내지 30㎛의 두께로 단열막(21)을 형성한 후 80 내지 100℃ 온도에서 건조하고, 전자반사재와 플릿 글라스 및 비이클로 이루어진 혼합물질을 단열막(21)의 상부에 재차 인쇄 방식으로 10 내지 30㎛의 두께로 전자반사막(23)을 형성한 후 건조하여 흑화 공정을 통해 섀도우마스크(20)를 제조하였다.After preparing the mixture consisting of the insulating material and frit glass and vehicle to form a heat insulating film 21 to a thickness of 10 to 30㎛ by a printing method on the shadow mask 20, the annealing process is completed and dried at a temperature of 80 to 100 ℃ In addition, the mixture of the electron reflection material, the fleet glass, and the vehicle is formed on the insulating film 21 again by the printing method to form an electron reflection film 23 having a thickness of 10 to 30 μm, and then dried to form a shadow mask through a blackening process. (20) was prepared.
한편, 저융점 프릿 글라스는 대략 500 내지 600℃에서 열처리하여 완전 유리화하며, 전자반사재 및 세라믹 재료가 흐트러지지 않게 서로를 결합해 주고 더 나아가서 이들을 섀도우마스크 상에 견고하게 부착하는 역할을 하며, 비이클은 인쇄공정시 원활한 인쇄공정이 진행되도록 인쇄 조성물인 잉크의 점도, 농도를 조절하는 역할을 하는 물질로서 점착성 부여제, 결합제 및 용제로 이루어져 있다.On the other hand, the low-melting frit glass is completely vitrified by heat treatment at approximately 500 to 600 ℃, the electronic reflector and the ceramic material are bonded to each other so as not to be disturbed, further serves to firmly attach them on the shadow mask, the vehicle As a material that plays a role of controlling the viscosity and concentration of the ink, which is the printing composition, to facilitate a smooth printing process during the printing process, it is composed of a tackifier, a binder, and a solvent.
상기 비이클의 점착성 부여제는 피막 상호간에 밀착성을 좋게 하기 위하여 첨가되는 물질로서, 실리콘계통 및 광유 등이 사용되며, 결합제로서는 에틸셀룰로오즈, 아크릴수지, 에폭시수지 등이 사용된다.The tackifier of the vehicle is a substance added to improve adhesion between the coatings, silicone type, mineral oil, and the like, and ethyl cellulose, acrylic resin, epoxy resin and the like are used as the binder.
상기와 같은 방법으로 제조한 도밍저감물질, 즉 페이스트(21, 23)를 도 5의 스크린 인쇄 공정을 이용하여 섀도우마스크(20)에 각각 프린팅하는 데, 도 5에서보듯이 사각형의 프레임(31)에 튼튼하게 고정된 스크린 메쉬(33; Mesh)에 인쇄용 조성물로 구성된 페이스트(21, 23)를 스크래퍼(35)를 이용하여 골고루 도포하고 난 후, 인쇄기판(37) 상부에 인쇄하고자 하는 섀도우마스크(20)를 올려놓은 다음, 스퀴지(39)로 균일한 압력을 가하면서 페이스트(21, 23)를 이동시켜 원하는 형태로 인쇄한다.The domming reducing materials, that is, pastes 21 and 23 manufactured by the above method, are respectively printed on the shadow mask 20 by using the screen printing process of FIG. 5, as shown in FIG. 5. After the pastes 21 and 23 composed of the printing composition are evenly applied to the screen mesh 33 which is firmly fixed on the screen mesh 33 using the scraper 35, the shadow mask to be printed on the upper portion of the printed circuit board 37 20), and then pastes 21 and 23 are moved and printed in a desired form while applying a uniform pressure to the squeegee 39.
이와 같은 방식을 이용할 경우에 종래 기술의 일종인 스프레이 코팅법을 적용하는 경우보다 두껍고, 전체적으로 균일한 막 두께를 갖는 도밍저감막의 구성이 가능하다.In the case of using such a method, it is possible to configure a dope reducing film having a thicker thickness and overall uniform film thickness than the case of applying the spray coating method, which is a kind of the prior art.
즉, 본 발명은 이와 같은 스크린 인쇄를 이용하여 피막의 두께 조절이 자유롭고, 섀도우마스크(20)에 도밍억제물질을 도포하여 도밍 현상을 저감시키고 있다.That is, according to the present invention, the thickness of the film is freely controlled by using such screen printing, and the doming inhibitor is applied to the shadow mask 20 to reduce the doming phenomenon.
아울러, 본 발명의 목적을 달성하기 위해서는 도밍저감물질(21∼23)의 두께가 수십 ㎛이상, 바람직하게는 20 내지 60㎛정도의 두꺼운 피막을 형성해야 효과가 있으며, 섀도우마스크의 홀을 막아 전자빔의 직진에 방해가 없도록 인쇄방식으로 피막을 형성한 후 건조, 소성하는 과정으로 완성하였으며, 단열막(21)과 전자반사막(23) 사이의 알루미늄막(22)의 경우에는 증착 방식으로 형성하였다.In addition, in order to achieve the object of the present invention, the thickness of the dominant reducing material 21 to 23 should be formed in a thick film of several tens of micrometers or more, preferably 20 to 60 micrometers, and the electron beam is blocked by blocking the holes of the shadow mask. After the film was formed by a printing method so as not to interfere with the straight line of the film, it was completed by a process of drying and baking, and in the case of the aluminum film 22 between the heat insulating film 21 and the electron reflection film 23 was formed by a vapor deposition method.
전자반사막 인쇄용 잉크는 기존의 경우 산화텅스텐 분말이 거의 60 내지 70중량% 정도의 비율로 사용하였으며, 그 효과 또한 막을 도포하기 전의 칼라 음극선관에 비해 도밍억제 능력이 30 내지 35%정도밖에 안되기 때문에 추가적으로 도밍억제 효과를 향상시키는 방법이 필요로 하게 된다.Conventional tungsten oxide powder is used in the ratio of about 60 to 70% by weight in the printing ink for electron reflection films, and the effect is also 30 to 35% because of the dominant suppression ability compared to the color cathode ray tube before coating the film. There is a need for a method of improving the dominant suppression effect.
본 발명에서는 섀도우마스크 표면에서 발생하는 열을 효과적으로 차단하기위하여 섀도우마스크(20)의 표면에 제올라이트 분말과 저융점 프릿 글라스 및 비이클을 혼합하여 제작한 잉크를 이용하여 인쇄 방식으로 형성하고 건조 후 약 500 내지 600℃에서 가열하여 융착 고정하고 완성한다.In the present invention, in order to effectively block the heat generated on the surface of the shadow mask to form a printing method using the ink prepared by mixing the zeolite powder, low melting frit glass and vehicle on the surface of the shadow mask 20 and dried about 500 It is completed by fusion fixing and heating at ~ 600 ℃.
이때, 섀도우마스크(20)의 홀이 막히지 않도록 잉크의 점성을 조절해야 한다.At this time, the viscosity of the ink should be adjusted so that the holes of the shadow mask 20 are not blocked.
단열재로 사용한 제올라이트는 점토광물로서 수십 Å의 미세한 세공이 있어 흡습제나 효소의 담체, 단열재로서 폭넓게 사용되며, 본 발명에서는 전자의 충돌에 의해 발생한 열이 섀도우마스크(20)에 전달되는 것을 방지하는 역할을 한다.Zeolite used as a heat insulating material has a fine pore of several tens of Å as a clay mineral, and is widely used as a carrier for an absorbent, an enzyme, and a heat insulating material. In the present invention, the zeolite serves to prevent heat generated by the collision of electrons to be transferred to the shadow mask 20. Do it.
섀도우마스크(20)의 최외각 표면은 전자총에서 방사되는 열전자가 섀도우마스크(20)의 표면에 부딪힐 때 전자를 반사하는 효과가 큰 전자반사재료로서, 비스무스(Bi), 텅스텐(W) 및 그 산화물(Bi2O3, WO3)이 있으며, 이러한 산화물은 전자빔의 반사효율(0.45∼0.50)이 큰 재질로서, 섀도우마스크(20)에 입사된 전자빔의 흡수량을 감소시켜 섀도우마스크(20)가 부풀어오르는 도밍량을 감소시킨다.The outermost surface of the shadow mask 20 is an electron reflection material having a large effect of reflecting electrons when hot electrons radiated from the electron gun strike the surface of the shadow mask 20. Bismuth (Bi), tungsten (W) and the Oxides (Bi 2 O 3 , WO 3 ), and these oxides are materials having a large reflection efficiency (0.45 to 0.50) of the electron beam, and the shadow mask 20 reduces the amount of absorption of the electron beam incident on the shadow mask 20. Reduces the amount of swelling
또한, 비스무스, 텅스텐 등의 산화물은 열방사율이 높은 재질로서, 산화텅스텐은 열방사율 ε=0.9이고, 비스무스는 열방사율이 ε=0.85로서 열방사율이 우수한 재질이다.In addition, oxides such as bismuth and tungsten have a high thermal emissivity, tungsten oxide has a thermal emissivity of ε = 0.9, and bismuth has a high emissivity of ε = 0.85.
또한, 단열막(21)과 전자반사막(23) 사이에 증착 설치하는 알루미늄막(22)은 열전도율이 높은 재질로서 전자반사막(23)에서 전달되는 열을 알루미늄막(23)에서 효과적으로 열을 차단하며 섀도우마스크(20)와 용접 지지하는 프레임(19)쪽으로 열을 전달시키는 역할을 하며, 그 일부 열은 단열막(21)에서 다시 차단한다.In addition, the aluminum film 22 deposited between the heat insulation film 21 and the electron reflection film 23 is a material having high thermal conductivity, and effectively blocks heat transmitted from the electron reflection film 23 from the aluminum film 23. It serves to transfer heat toward the shadow mask 20 and the frame 19 for welding support, and part of the heat is blocked again by the heat insulating film 21.
본 발명에 사용되는 인쇄용 잉크의 제작 방법은 비이클과 프릿 글라스에 해당하는 유리원료, 전자반사재 또는 단열재를 롤-밀(Roll-mill)에 함께 투입하여 디스퍼서(Disperser) 등의 기구를 이용하여 2시간 이상 균일 혼합하여 제작하였다.Method of manufacturing printing ink used in the present invention is to use a mechanism such as a dispenser by injecting a glass material, an electronic reflector or a heat insulating material corresponding to the vehicle and frit glass together in a roll-mill (2). It was produced by uniform mixing over time.
이때, 점도를 일정하게 조절하기 위하여 비이클의 선택과 첨가량이 중요하다.At this time, the selection and addition amount of the vehicle is important in order to adjust the viscosity constantly.
본 발명에 따른 도밍 저감 효과를 나타내기 위하여 21" 칼라 음극선관의 섀도우마스크의 표면에 적용하여 그 도밍양을 측정한 결과를 아래 표 1에 나타내었다.In order to show the dominant reduction effect according to the present invention, the result of measuring the dominant amount by applying to the surface of the shadow mask of the 21 "color cathode ray tube is shown in Table 1 below.
그리고, 도 6은 섀도우마스크상의 도밍측정 지점을 표시한 도면으로서, 전체 화면의 X축으로 1/8되는 지점(A지점)과, 1/16되는 지점(B지점)에서 각각 측정하였다.FIG. 6 is a diagram showing a dominant measurement point on a shadow mask, which is measured at a point 1/8 (point A) and a point 1/16 (point B) on the X-axis of the entire screen.
☞ 비교예는 종래기술에 의한 도밍저감물질인 전자반사재료(WO3), 고열전달재료(AlN), 열방사재료(MnO) 또는 그 혼합물(WO3+MnO, WO3+AlN)의 선택적 코팅시 측정한 도밍량이고, 실시예 1은 전자반사막과 단열막을 각각 형성한 후 측정한 도밍량이고, 실시예 2는 전자반사막과 알루미늄막 및 단열막을 각각 형성한 후 측정한 도밍량임.☞ Comparative Example is a selective coating of the dominant reducing material of the prior art electron reflection material (WO 3 ), high heat transfer material (AlN), thermal radiation material (MnO) or mixtures thereof (WO 3 + MnO, WO 3 + AlN) Doming amount measured during the test, Example 1 is the domming amount measured after forming the electron reflection film and the heat insulating film, respectively, Example 2 is the domming amount measured after forming the electron reflection film, aluminum film and the heat insulating film, respectively.
상기 표 1과 같이 도밍저감물질로 전자반사재료, 고열전달재료 및 열방사재료를 택일적으로 사용하여 제작한 코팅액을 섀도우마스크(20)의 표면에 코팅한 시료(비교예)와, 본 발명에 의한 단열막(21) 및 전자반사막(23)을 각기 코팅한 시료(실시예 1)와, 단열막(21)과 알루미늄막(22) 및 전자반사막(23)을 각기 코팅한 시료(실시예 2)를 각각 제작하여 그 도밍량을 측정해 본 결과, 본 발명에 의한 코팅 방법이 보다 우수한 것임을 알 수 있다.As shown in Table 1 above, a sample (comparative example) coated on the surface of the shadow mask 20 with a coating liquid produced by using an electron reflection material, a high heat transfer material, and a heat radiating material as a dominant reducing material, and in the present invention, A sample coated with the heat insulating film 21 and the electron reflection film 23 (Example 1), and a sample coated with the heat insulating film 21, the aluminum film 22 and the electron reflecting film 23, respectively (Example 2). ) Was produced, respectively, and the domming amount was measured. As a result, it was found that the coating method according to the present invention was more excellent.
이와 같이 본 발명에서는 섀도우마스크(20)의 표면에 제올라이트와 산화텅스텐을 포함하는 단열 기능 및 전자반사 기능을 하는 코팅층(21, 23)을 형성하며, 선택적으로 섀도우마스크(20)의 표면에 알루미늄을 주성분으로 하는 열전도막(22)을 더 형성하여 도밍량을 감소시킨다.As described above, in the present invention, the coating layers 21 and 23 having zeolite and tungsten oxide and insulating properties including zeolite and tungsten oxide are formed on the surface of the shadow mask 20, and aluminum is selectively formed on the surface of the shadow mask 20. A thermally conductive film 22 as a main component is further formed to reduce the amount of domming.
따라서, 본 발명에서는 섀도우마스크의 표면에 단열효과를 위한 단열막과 전자의 반사효과를 위한 전자반사막을 적층하고, 선택적으로 알루미늄을 주성분으로 하는 열전도막을 더 적층함으로써, 도밍저감물질층이 열전자의 전자반사, 열전달 및 단열 역할을 복합적으로 갖기 때문에 섀도우마스크의 열적 변형을 감소하여 도밍 현상을 실질적으로 감소시킴과 아울러 스크린 상의 전자빔의 미스랜딩을 방지하여 음극선관의 색순도를 향상시킬 수 있다.Therefore, in the present invention, by laminating an insulating film for insulating effect and an electron reflecting film for reflecting electron effect on the surface of the shadow mask, and optionally further laminating a heat conductive film mainly composed of aluminum, the dominant reducing material layer is formed of electrons of hot electrons. The combination of reflection, heat transfer, and thermal insulation can reduce the thermal deformation of the shadow mask to substantially reduce the dominant phenomena and prevent the mis-landing of the electron beam on the screen, thereby improving the color purity of the cathode ray tube.
Claims (7)