KR100307098B1 - A touch panel with a transparent plastic substrate and a method thereof - Google Patents
A touch panel with a transparent plastic substrate and a method thereof Download PDFInfo
- Publication number
- KR100307098B1 KR100307098B1 KR1019990016304A KR19990016304A KR100307098B1 KR 100307098 B1 KR100307098 B1 KR 100307098B1 KR 1019990016304 A KR1019990016304 A KR 1019990016304A KR 19990016304 A KR19990016304 A KR 19990016304A KR 100307098 B1 KR100307098 B1 KR 100307098B1
- Authority
- KR
- South Korea
- Prior art keywords
- transparent
- lower plate
- conductive film
- electrode
- transparent conductive
- Prior art date
Abstract
본 발명은 한쪽면상에 투명 도전막이 형성된 투명 필름을 투명 플라스틱 기판에 접합하여 하부 기판으로 사용하는 아날로그형 도전필름 방식의 터치 패널에 있어서, 배선 전극 형성에 필요한 공간 확보를 위하여 필요한 투명 도전막의 포토 공정을 생략할 수 있는 터치 패널 및 그의 제조방법을 제시한 것으로, 상기 투명 필름을 상기 투명 플라스틱 기판에 접합시키기 전에 상기 투명 플라스틱 기판상에 배선 전극을 형성하는 것을 특징으로 한다.The present invention is a touch panel of the analog type conductive film method using a transparent film having a transparent conductive film formed on one side to a transparent plastic substrate and used as a lower substrate, the photo process of the transparent conductive film required for securing the space required for wiring electrode formation The present invention provides a touch panel and a method of manufacturing the same, wherein a wiring electrode is formed on the transparent plastic substrate before bonding the transparent film to the transparent plastic substrate.
본 발명에 의한 터치 패널의 구성은, 투명 필름의 일면상 전체에 투명 도전막이 형성되고, 상기 투명 도전막상에 형성되며 상기 투명 필름의 서로 마주보는 한 쌍의 가장자리 부분에 소정 폭의 전극이 형성된 상판부와, 일면상 전체에 투명 도전막이 형성된 투명 필름을 투명 양면 접착 테이프를 통해 투명 플라스틱 기판과 접착시킨 하판부와, 상기 하판부의 상기 투명 도전막상에 일정 형상 및 크기를 갖고 돌출 형성된 다수개의 도트형 스페이서로 구성되며, 상기 상판부의 투명 도전막과 상기 하판부의 투명 도전막이 서로 마주 보도록 배치되어 양면 접착 테이프에 의하여 상기 상판부와 상기 하판부의 가장자리가 상호 접착된 터치 패널에 있어서,In the configuration of the touch panel according to the present invention, a transparent conductive film is formed on one surface of a transparent film, and an upper plate portion formed on the transparent conductive film and having electrodes having a predetermined width at a pair of edge portions of the transparent film facing each other. And a lower plate portion in which a transparent film having a transparent conductive film formed on one surface thereof is bonded to the transparent plastic substrate through a transparent double-sided adhesive tape, and a plurality of dot-shaped spacers protruding with a predetermined shape and size on the transparent conductive film of the lower plate portion. The touch panel comprising a transparent conductive film of the upper plate portion and the transparent conductive film of the lower plate portion facing each other, the edge of the upper plate portion and the lower plate portion is bonded to each other by a double-sided adhesive tape,
외부로부터 상기 상판부 및 하판부의 투명 도전막에 전압을 인가하고, 외부로부터 상판부의 한 점이 눌렸을 때 눌린 위치의 좌표를 감지하기 위해 소정의 폭을 가지고 상기 투명 플라스틱 기판상의 양 가장자리를 따라 형성된 전극과;An electrode formed along both edges of the transparent plastic substrate with a predetermined width to apply a voltage to the transparent conductive films of the upper plate portion and the lower plate portion from the outside, and to sense the coordinates of the pressed position when a point of the upper plate portion is pressed from the outside; ;
상기 하판부의 전극 일부와 상기 하판부의 투명 도전막을 전기적으로 연결하기 위해 상기 하판부의 투명 양면 테이프와 투명 필름과 투명 도전막을 관통하여 형성된 제1 상하 연결용 전극;A first vertical connection electrode formed through the transparent double-sided tape, the transparent film, and the transparent conductive film of the lower plate to electrically connect a portion of the lower plate of the electrode to the transparent conductive film of the lower plate;
상기 하판부의 전극 일부와 상기 상판부의 전극을 전기적으로 연결 하기 위해 상기 상판부와 상기 하판부를 접착하는 상기 양면 접착 테이프를 관통하여 상기 하판부의 전극과 상기 하판부의 전극이 연결되도록 형성된 제2 상하 연결용 전극을 포함하여 이루어진다.A second upper and lower connection electrode formed to connect the electrodes of the lower plate and the lower plate by penetrating the double-sided adhesive tape which bonds the upper plate and the lower plate to electrically connect a portion of the electrodes of the lower plate and the electrodes of the upper plate; It is made, including.
또한 본 발명에서는 상기와 같은 본 발명에 의한 터치 패널을 제조하는 제조 방법을 제공한다. 상기 제조 방법은 상기 하판부의 투명 도전막, 투명 필름, 투명 양면 접착 테이프를 관통하는 구멍을 형성하는 단계와, 상기 양면 접착 테이프를 관통하는 구멍을 형성하는 단계와, 상기 형성된 구멍에 도전 물질을 채워 넣어 하판부의 전극 및 투명 도전막을 전기적으로 연결하고 하판부의 전극 및 상판부의 전극을 전기적으로 연결하는 단계로 이루어 진다.In addition, the present invention provides a manufacturing method for manufacturing a touch panel according to the present invention as described above. The manufacturing method includes forming a hole penetrating the transparent conductive film, the transparent film, and the transparent double-sided adhesive tape in the lower plate, forming a hole penetrating the double-sided adhesive tape, and filling a conductive material in the formed hole. It is made of a step of electrically connecting the electrode of the lower plate and the transparent conductive film and the electrode of the lower plate and the electrode of the upper plate.
Description
터치 패널은 정보 입력 장치의 하나로서, 화면을 보면서 화면상에 직접 정보나 데이터를 입력시킬 수 있는 입력 장치이다.The touch panel is an information input device, and is an input device capable of directly inputting information or data onto a screen while viewing the screen.
입력수단중 하나인 키(Key)에 의한 정보 입력은 가장 오래되고 보편화된 입력 방법이며 자동판매기, TV 리모콘, 전화기 등 현재 우리의 일상생활에 필수 불가결한 것이 되어 있다. 그러나 이러한 키 입력은 사람의 손의 조작범위 내에서 몇 개의 키를 누르거나 접촉하는 것에 의해 그 키에 할당된 명령을 그 기기에 내리게 되지만, 컴퓨터를 사용하는 본래의 목적인 정확, 신속, 편리 등을 위해서는 사용자가 더욱 편리하게 기기에게 명령을 내릴 수 있는 방법이 필요했다.Information input by key, one of the input means, is the oldest and most common input method, and is indispensable in our daily life such as vending machine, TV remote control and telephone. However, such a key input causes the device to issue a command assigned to the key by pressing or touching a few keys within the operating range of the human hand. This required a more convenient way for the user to command the device.
이와 같은 목적으로 개발된 방법중 하나가 기존의 키보드를 누르는 대신 디스플레이 화면을 직접 손가락으로 누름으로써 조작의 오류 없이 간편하게 기기를 조작할 수 있는 터치 패널이다.One of the methods developed for this purpose is a touch panel that can easily operate the device without an error of operation by directly pressing the display screen with a finger instead of pressing a conventional keyboard.
이를 위해서는 손가락으로 누른 부분의 좌표를 검지해서 그 정보를 기기에 전달해 주는 터치형 입력장치를 디스플레이 전면에 부착해야 하며, 이것을 가능하게 해 주는 장치가 터치 패널이다.To this end, a touch input device that detects the coordinates of a portion pressed by a finger and transmits the information to the device must be attached to the front of the display, and a device that enables this is a touch panel.
일반적으로 터치 패널은 디지털 방식과 아날로그 방식으로 나뉘어진다. 디지털 방식은 적외선 방식, 도전 필름 방식, 용량 변화 방식, 금속 세선 매립 방식으로 세분화되고, 아날로그 방식은 좌표 인식 수단에 따라 도전 필름 방식, 하중 분압 방식, 표면파 반사 방식, 금속 세선 매립 방식 등으로 세분된다.In general, touch panels are divided into digital and analog methods. Digital methods are subdivided into infrared method, conductive film method, capacitance change method, and metal wire embedding method, and analog methods are subdivided into conductive film method, load partial pressure method, surface wave reflection method, and metal wire embedding method according to coordinate recognition means. .
본 발명은 상기 여러 방식중 아날로그 방식의 도전 필름 방식에 관한 것이다.The present invention relates to an analog conductive film method of the various methods.
터치 패널에 필요한 기본 기능은 터치 입력의 유무 판단 기능과, 터치 입력이 있을 때 입력점의 좌표를 감지하는 기능과, 컴퓨터와의 인터페이스를 하는 기능이 필요하다.Basic functions required for the touch panel require a function for determining whether a touch input is present, a function for detecting coordinates of an input point when there is a touch input, and a function for interfacing with a computer.
도 1은 종래의 유리기판을 이용한 터치 패널의 단면구조를 나타내는 것으로, 상판(④)과 유리로 된 하판(①)에 균일하게 투명 도전막(②)을 형성시킨 후, 필요 없는 부분의 투명 도전막을 사진 식각공정을 통해 식각해서 없앤 다음, 후막 인쇄법등으로 전극(⑧)을 형성하고, 2개의 투명 도전막 사이의 간격을 유지하기 위해서 하판에 일정 두께의 양면 테이프(③)를 접착하며, 인접부위와의 오동작을 막기 위해 도트 스페이서(dot spacer. ⑤)를 형성한다.1 illustrates a cross-sectional structure of a touch panel using a conventional glass substrate. After the transparent conductive film ② is uniformly formed on the upper plate ④ and the lower plate ① made of glass, transparent conductive portions are not required. The film is etched away through a photolithography process, and then an electrode (8) is formed by a thick film printing method, and a double-sided tape (③) having a predetermined thickness is adhered to the lower plate to maintain a gap between the two transparent conductive films. A dot spacer (⑤) is formed to prevent malfunction with the site.
이와 같이 구성된 종래의 터치 패널은 종 또는 횡 방향의 상기 전극 양단에 전압을 인가하여 사용자에 의해 터치되어 눌러진 부분의 분압된 전위를 상호 교대로 검출하여 위치를 인지한다.In the conventional touch panel configured as described above, a voltage is applied to both ends of the electrode in the longitudinal or transverse direction to alternately detect the divided potential of the portion pressed and touched by the user to recognize the position.
하지만 종래 하판으로 사용되는 유리는 무게가 무겁고 충격에 깨질 수 있는 문제를 가지고 있어 모빌용 제품에는 적용성이 나쁘다. 이를 해결하기 위해 일본 공개 특허 평성 제6-309101호에서는 하판의 기판을 유리 대신 투명 플라스틱을 사용하였고, 상기 투명 플라스틱 위에 직접 투명 도전막을 형성하는 것이 어려우므로도 2 와 같이 투명 도전막이 형성된 투명 필름(④)을 투명한 양면 테이프(⑦)를 사용하여 하판에 부착시키는 방법을 제안하였다.However, conventional glass is used as a lower plate has a problem that the weight is heavy and can be broken in impact, the applicability is bad for mobile products. In order to solve this problem, Japanese Unexamined Patent Publication No. Hei 6-309101 uses a transparent plastic instead of glass, and since it is difficult to form a transparent conductive film directly on the transparent plastic, a transparent film having a transparent conductive film as shown in FIG. ④) using a transparent double-sided tape (⑦) was proposed to attach to the lower plate.
그러나 이 경우 투명 도전막 상에 전극 배선을 형성시키기 위해서는 일정 부위의 투명 도전막의 제거가 필요하며, 따라서 일련의 복잡하고 비용이 많이 드는 사진 식각공정이 필요하다. 그후 상판(④)과 하판(①)의 간격을 유지하기 위해 하판의 투명 도전막(②) 위에 도트 스페이서(⑤)를 형성한다. 이러한 방법으로 하판이 완성되면, 상판을 양면 테이프(③)를 사용하여 하판에 부착하게 된다.However, in this case, in order to form the electrode wiring on the transparent conductive film, it is necessary to remove the transparent conductive film at a certain portion, and thus a series of complicated and expensive photolithography processes are required. Thereafter, in order to maintain a gap between the upper plate ④ and the lower plate ①, a dot spacer ⑤ is formed on the transparent conductive film ② of the lower plate. When the lower plate is completed in this way, the upper plate is attached to the lower plate using double-sided tape ③.
본 발명에서는 이와 같이 종래기술에서 전극배선을 하기위해 공정 설비와 재료비가 많이 들고, 장시간을 요하는 사진 식각공정을 없앰으로써 생산성을 크게 향상시킬 수 있는 터치 패널 및 그 제조방법을 제공한다.The present invention provides a touch panel and a method for manufacturing the same, which greatly increase the productivity by eliminating the photolithography process, which requires a lot of processing equipment and material costs and requires a long time for electrode wiring in the prior art.
도 1 은 종래 유리기판을 이용한 터치 패널의 단면구조.1 is a cross-sectional structure of a touch panel using a conventional glass substrate.
도 2 는 종래 투명 플라스틱 기판을 이용한 터치 패널의 단면 구조.Figure 2 is a cross-sectional structure of a touch panel using a conventional transparent plastic substrate.
도 3 은 본 발명에 의해 투명 플라스틱 기판을 이용한 터치 패널의 중앙부분의 단면 구조.Figure 3 is a cross-sectional structure of the central portion of the touch panel using a transparent plastic substrate according to the present invention.
도 4 는 본 발명에 의해 투명 플라스틱 기판을 이용한 터치 패널의 가장자리 부분의 단면 구조.4 is a cross-sectional structure of an edge portion of a touch panel using a transparent plastic substrate according to the present invention.
도 5 는 종래 터치 패널의 제작 공정도.5 is a manufacturing process diagram of a conventional touch panel.
도 6 은 본 발명에 의한 투명 플라스틱 기판을 이용한 터치 패널의 제작 공정도.6 is a manufacturing process diagram of a touch panel using a transparent plastic substrate according to the present invention.
① 유리 기판 (하판)① glass substrate (bottom plate)
② 투명 도전막② transparent conductive film
③ 양면 테이프③ double sided tape
④ 투명 필름④ transparent film
⑤ 도트 스페이서⑤ Dot spacer
⑥ 투명 플라스틱 기판⑥ transparent plastic substrate
⑦ 투명 양면 테이프⑦ Transparent double sided tape
⑧ 좌표 감지용 전극⑧ Electrode for coordinate detection
⑨ 상하 연결용 전극⑨ Up and down connection electrode
본 발명은 한쪽면상에 투명 도전막이 형성된 투명 필름을 투명 플라스틱 기판에 접합하여 하부 기판으로 사용하는 아날로그형 도전필름 방식의 터치 패널에 있어서, 배선 전극 형성에 필요한 공간 확보를 위하여 필요한 투명 도전막의 포토 공정을 생략할 수 있는 터치 패널 및 그의 제조방법을 제시한 것으로, 상기 투명 필름을 상기 투명 플라스틱 기판에 접합시키기 전에 상기 투명 플라스틱 기판상에 배선 전극을 형성하는 것을 특징으로 한다.The present invention is a touch panel of the analog type conductive film method using a transparent film having a transparent conductive film formed on one side to a transparent plastic substrate and used as a lower substrate, the photo process of the transparent conductive film required for securing the space required for wiring electrode formation The present invention provides a touch panel and a method of manufacturing the same, wherein a wiring electrode is formed on the transparent plastic substrate before bonding the transparent film to the transparent plastic substrate.
본 말명은 투명 필름의 일면상 전체에 투명 도전막이 형성되고, 상기 투명 도전막상에 형성되며 상기 투명 필름의 서로 마주보는 한 쌍의 가장자리 부분에 소정 폭의 전극이 형성된 상판부와, 일면상 전체에 투명 도전막이 형성된 투명 필름을 투명 양면 접착 테이프를 통해 투명 플라스틱 기판과 접착시킨 하판부와, 상기 하판부의 상기 투명 도전막상에 일정 형상 및 크기를 갖고 돌출 형성된 다수개의 도트형 스페이서로 구성되며, 상기 상판부의 투명 도전막과 상기 하판부의 투명 도전막이 서로 마주 보도록 배치되어 양면 접착 테이프에 의하여 상기 상판부와 상기 하판부의 가장자리가 상호 접착된 터치 패널에 있어서,The present invention is a transparent conductive film is formed on the entire surface on one side of the transparent film, the upper plate portion formed on the transparent conductive film and the electrode having a predetermined width on the pair of edge portions facing each other of the transparent film, and transparent on one surface The lower plate portion is formed by adhering a transparent film on which a conductive film is formed to a transparent plastic substrate through a transparent double-sided adhesive tape, and a plurality of dot-shaped spacers protruding with a predetermined shape and size on the transparent conductive film of the lower plate portion. In a touch panel in which a transparent conductive film and a transparent conductive film of the lower plate portion face each other and the edges of the upper plate portion and the lower plate portion are bonded to each other by a double-sided adhesive tape,
외부로부터 상기 상판부 및 하판부의 투명 도전막에 전압을 인가하고, 외부로부터 상판부의 한 점이 눌렸을 때 눌린 위치의 좌표를 감지하기 위해 소정의 폭을 가지고 상기 투명 플라스틱 기판상의 양 가장자리를 따라 형성된 전극과;An electrode formed along both edges of the transparent plastic substrate with a predetermined width to apply a voltage to the transparent conductive films of the upper plate portion and the lower plate portion from the outside, and to sense the coordinates of the pressed position when a point of the upper plate portion is pressed from the outside; ;
상기 하판부의 전극 일부와 상기 하판부의 투명 도전막을 전기적으로 연결하기 위해 상기 하판부의 투명 양면 테이프와 투명 필름과 투명 도전막을 관통하여 형성된 제1 상하 연결용 전극;A first vertical connection electrode formed through the transparent double-sided tape, the transparent film, and the transparent conductive film of the lower plate to electrically connect a portion of the lower plate of the electrode to the transparent conductive film of the lower plate;
상기 하판부의 전극 일부와 상기 상판부의 전극을 전기적으로 연결 하기 위해 상기 상판부와 상기 하판부를 접착하는 상기 양면 접착 테이프를 관통하여 상기 하판부의 전극과 상기 하판부의 전극이 연결되도록 형성된 제2 상하 연결용 전극을 포함하여 이루어진다.A second upper and lower connection electrode formed to connect the electrodes of the lower plate and the lower plate by penetrating the double-sided adhesive tape which bonds the upper plate and the lower plate to electrically connect a portion of the electrodes of the lower plate and the electrodes of the upper plate; It is made, including.
상기 투명 필름은 폴리 에틸렌 테레후타레이트(PET) 필름인 것이 바람직하다.It is preferable that the said transparent film is a polyethylene terephthalate (PET) film.
상기 하판부의 전극은 4 부분으로 나뉘어져 서로 마주보는 위치에 형성되고, 상기 제1 상하 연결용 전극은 상기 하판의 투명 필름이 덮고 있는 상기 하판부의 전극중 서로 마주보는 위치에 있는 두 부분의 상기 하판부 전극과 연결된다.The lower plate electrode is divided into four parts and is formed at positions facing each other, and the first vertical connection electrode is the lower plate portion of two portions at positions facing each other among the electrodes of the lower plate covered by the transparent film of the lower plate. Connected with the electrode.
상기 제2 상하 연결용 전극은 상기 하판부의 전극중 상기 제1 상하 연결용 전극과 연결되는 전극을 제외한, 서로 마주 보는 위치에 있는 나머지 두 부분의 상기 하판부 전극과 연결된다.The second upper and lower connection electrodes are connected to the lower plate electrodes of the remaining two portions at positions facing each other, except for electrodes connected to the first upper and lower connecting electrodes, among the electrodes of the lower plate.
또한 본 발명에 의한 투명 플라스틱 기판을 이용한 터치 패널의 제조방법은,투명 플라스틱 기판상의 가장자리 부분에 서로 마주보도록 4 개의 부분으로 독립적으로 나뉘어져 각각 소정의 폭과 길이를 갖는 전극을 형성하는 단계;와In addition, the manufacturing method of the touch panel using the transparent plastic substrate according to the present invention, step of forming an electrode having a predetermined width and length, respectively divided into four parts independently facing each other on the edge portion on the transparent plastic substrate; and
일면상에 투명 도전막이 형성된 투명 필름을 상기 투명 도전막이 형성되지 않은 면과 상기 투명 플라스틱 기판의 상기 전극이 형성된 면이 서로 마주하도록 투명 양면 접착 테이프를 이용하여 부착하는 단계;Attaching a transparent film having a transparent conductive film formed on one surface thereof using a transparent double-sided adhesive tape such that a surface on which the transparent conductive film is not formed and a surface on which the electrode of the transparent plastic substrate is formed face each other;
상기 전극과 닿을 수 있도록 상기 투명 도전막과 투명 필름과 상기 투명 양면 접착 테이프를 관통하는 구멍을 다수개 형성하는 단계;Forming a plurality of holes through the transparent conductive film, the transparent film, and the transparent double-sided adhesive tape so as to be in contact with the electrode;
상기 전극과 상기 투명 도전막을 전기적으로 연결시키기 위해 상기 형성된구멍에 금속물질을 채우는 단계;Filling a metal material into the formed hole to electrically connect the electrode and the transparent conductive film;
상기 투명 도전막상의 상기 전극들이 둘러싼 중앙부위에 일정 형태와 크기를 갖는 다수개의 돌출 스페이서 구조물을 형성하는 단계;Forming a plurality of protruding spacer structures having a predetermined shape and size in a central portion of the transparent conductive film surrounding the electrodes;
상기 돌출 스페이서 구조물이 형성된 상기 중앙부위 전체와 상기 전극중 외부와 전기적으로 연결하기위한 단자부를 제외한 부분에 양면 접착 테이프를 부착하여 하판부를 완성하는 단계;Completing a lower plate part by attaching a double-sided adhesive tape to the entirety of the central part where the protruding spacer structure is formed and a part of the electrode other than the terminal part for electrically connecting with the outside;
상판부 제작을 위해 투명 필름상의 한쪽면 전체에 투명 도전막을 형성하는 단계;Forming a transparent conductive film on one entire surface of the transparent film for fabricating the upper plate;
상판부의 상기 투명 도전막상의 서로 대응하여 마주보는 한쌍의 가장자리에 소정의 폭과 길이를 가진 전극을 형성하여 상판부를 완성하는 단계;Comprising: forming an electrode having a predetermined width and length on the pair of edges facing each other on the transparent conductive film of the upper plate portion to complete the upper plate portion;
상기 하판부에 형성된 전극에 닿을 수 있도록 상기 양면 접착 테이프를 관통하는 구멍을 다수개 형성하는 단계;Forming a plurality of holes penetrating the double-sided adhesive tape so as to contact the electrodes formed on the lower plate;
상기 하판부의 전극과 상기 상판부의 투명 도전막을 전기적으로 연결시키기 위해 상기 형성된 구멍을 통해 금속물질을 채우는 단계;Filling a metal material through the formed hole to electrically connect the electrode of the lower plate to the transparent conductive film of the upper plate;
상기 하판부의 최상층에 형성된 양면 접착 테이프를 이용하여 상기 상판부와 상기 하판부를 접착하되, 상기 상판부의 전극이 상기 구멍에 채워진 금속물질과 연결되도록 접착하는 단계를 포함하여 이루어진다.Bonding the upper plate to the lower plate by using a double-sided adhesive tape formed on the uppermost layer of the lower plate, and bonding the upper plate to connect the electrode to the metal material filled in the hole.
상기 투명 도전막과 투명 필름과 상기 투명 양면 접착 테이프를 관통하는 구멍을 형성하는 단계는, 상기 4개의 부분으로 나뉜 하판부의 전극중 서로 마주보는 위치에 있는 두 부분의 상기 전극과 상기 구멍이 연결되도록 형성한다.Forming a hole penetrating the transparent conductive film, the transparent film and the transparent double-sided adhesive tape, the electrode and the hole of the two parts in the position facing each other of the electrodes of the lower plate divided into four parts so as to connect Form.
상기 양면 접착 테이프를 관통하는 구멍을 형성하는 단계는, 상기 4개의 부분으로 나뉜 하판부의 전극중 하판부의 투명 도전막과 연결된 전극을 제외한 나머지 2개의 서로 마주보는 전극과 상기 구멍이 연결되도록 형성한다.The forming of the hole penetrating the double-sided adhesive tape may be performed such that the two opposing electrodes and the hole are connected to each other except the electrode connected to the transparent conductive film of the lower plate, among the electrodes of the lower plate divided into four parts.
상기 하판부의 투명필름을 상기 투명 플라스틱 기판상에 부착하는 단계는, 상기 하판부의 전극중 상기 제 1 상하 연결용 전극과 연결되는 부분 및 상기 돌출 스페이서 구조물을 포함하는 부분에 부착되지만, 상기 하판부의 전극중 상기 제 2 상하 연결용 전극과 연결되는 부분은 포함되지 않도록 상기 투명필름을 부착한다.The attaching the transparent film on the lower plate portion on the transparent plastic substrate may include attaching to the portion including the protruding spacer structure and the portion connected to the first vertical connecting electrode among the electrodes of the lower plate portion. The transparent film is attached so that the part connected to the second vertical connecting electrode is not included.
본 발명의 구성을 도 3 및 도 4 를 통해 상세히 설명하고자 한다.The configuration of the present invention will be described in detail with reference to FIGS. 3 and 4.
도 3 은 본 발명에 의한 터치 패널의 단면구조로서, 패널의 중앙부분(도 6 의 A-A' 부분)을 절단한 단면 구조이다. 도면 참조번호 ⑥ 은 하부 기판인 투명 플라스틱 기판이다. 투명 플라스틱 기판을 하부 기판으로 사용함으로써 더욱 가볍고 튼튼한 터치 패널을 만들 수 있다.3 is a cross-sectional structure of a touch panel according to the present invention, which is a cross-sectional structure obtained by cutting a central portion (A-A 'portion of FIG. 6) of the panel. Reference numeral 6 in the drawing is a transparent plastic substrate that is a lower substrate. By using a transparent plastic substrate as the lower substrate, a lighter and more robust touch panel can be made.
도면 참조번호 ⑦ 은 플라스틱 기판에 투명 도전막을 형성시키는 어려움을 피하고자 하여, 투명 도전막이 형성된 상기 투명 필름을 하부 기판에 접합하기 위한 투명한 양면 테이프이다. 도면 참조번호 ⑧ 은 외부에서 투명 도전막에 전압을 인가하고, 한 점이 눌렸을때 좌표를 감지할 목적으로 전압을 측정하기 위하여 형성해 놓은 전극이다. 도면 참조번호 ③ 은 상판과 하판을 부착시키기 위한 양면 테이프이며, 상기 양면 테이프는 상판과 하판을 절연시키는 역할도 하게 된다. 도면 참조번호 ⑤ 는 상판과 하판의 투명 도전막의 간격을 유지시켜 주고 인접부위와의 오동작을 막기 위한 도트 스페이서이다.Reference numeral ⑦ in the drawing is a transparent double-sided tape for bonding the transparent film on which the transparent conductive film is formed to the lower substrate in order to avoid the difficulty of forming a transparent conductive film on the plastic substrate. The reference numeral ⑧ in the drawing is an electrode formed to measure a voltage for the purpose of applying a voltage to the transparent conductive film from the outside and detecting a coordinate when a point is pressed. 3 is a double-sided tape for attaching the upper plate and the lower plate, and the double-sided tape also serves to insulate the upper plate and the lower plate. Reference numeral 5 denotes a dot spacer for maintaining a gap between the upper and lower transparent conductive films and preventing malfunctions of adjacent portions.
상기 도트 스페이서는 보통 사진 공정이나 후막 인쇄법으로 형성하게 되는데, 사진 공정은 정교한 도트를 형성할 수 있는 반면에 공정 설비와 공정시간이 오래 걸린다. 또한 상기 도트 스페이서의 간격을 너무 크게 하면 패널을 누를 때 휨이 발생해서 힘을 가하지 않은 다른 부분도 접촉되는 경우가 있어 신뢰성이 저하되며, 반대로 간격을 너무 작게 하면 좌표 검지를 할 수 있는 동작압이 높게 되어 사용감이 나쁘게 되므로, 도트 스페이서의 간격을 적당히 결정하는 것이 매우 중요하다.The dot spacer is usually formed by a photolithography process or a thick film printing method. The photolithography process can form sophisticated dots, but takes a long time and process equipment. In addition, if the interval between the dot spacers is too large, warpage may occur when the panel is pressed, and other parts that do not apply force may also come into contact with each other, thereby reducing reliability. On the contrary, if the interval is too small, the operating pressure for coordinate detection may be reduced. Since it becomes high and the usability becomes bad, it is very important to determine the space | interval of a dot spacer suitably.
도면 참조번호 ⑨ 는 본 발명의 핵심사항으로, 새로운 배선을 위한 연결부인 상하 연결용 전극이다. 투명 플라스틱 기판에 먼저 금속 전극을 형성한 후, 그 위에 투명 양면 테이프를 사용하여 도전막이 형성된 투명 필름을 붙인다. 투명 도전막과 전극을 연결하기 위하여 도전막, 투명 필름, 투명 양면 테이프에 구멍을 뚫어 상기 구멍안에 디스펜서 등으로 금속 물질을 채워 넣음으로써 상기 투명 도전막과 전극을 연결시켰다.Reference numeral ⑨ in the drawing is a key point of the present invention, and is an electrode for vertical connection, which is a connection part for new wiring. A metal electrode is first formed on a transparent plastic substrate, and then a transparent film on which a conductive film is formed is pasted thereon using a transparent double-sided tape. In order to connect the transparent conductive film and the electrode, the transparent conductive film and the electrode were connected by drilling a hole in the conductive film, the transparent film, and the transparent double-sided tape and filling a metal material with a dispenser or the like in the hole.
도 4 는 본 발명에 의한 터치 패널에 있어서, 패널의 가장자리 부분(도 6 의 B-B' 부분)을 절단한 단면도 이다. 상판과 하판에 형성된 전극 ⑧ 이 상하 연결용 전극 ⑨ 에 의해 서로 연결되어 있다.4 is a cross-sectional view of the edge of the panel (part B-B 'of FIG. 6) in the touch panel according to the present invention. The electrodes ⑧ formed on the upper plate and the lower plate are connected to each other by the electrodes ⑨ for vertical connection.
터치 패널 제작과 관련된 종래기술의 터치 패널 제작공정을 도 5 에 자세히 나타내었다. 먼저 유리나 플라스틱 기판상에 투명 도전막을 형성한다. 상기 투명 도전막은 기판 위에 직접 형성하거나, 도전막이 형성된 투명 필름(예: PET 필름)을 기판 위에 투명 양면 테이프를 사용하여 접착함으로써 형성한다. 투명 도전막이 형성되면 전극 배선을 위해 필요 없는 부분의 투명 도전막을 사진 식각 공정을 사용하여 제거한다. 상기 사진 식각 공정에 의한 제거 공정은 감광제(PR:Photo Resist) 도포, 건조, 노광, 식각, 감광제 제거(PR strip)등의 과정을 거쳐 행하게 된다. 상기 사진 식각공정이 끝나면 후막 인쇄법으로 전극 ⑧ 을 형성하고, 후막 인쇄법이나 포토 공정을 사용하여 도트 스페이서 ⑤ 를 형성한다. 그 후 마지막으로 상판과의 결합을 위하여 양변 테이프 ③ 를 부착한다. 이렇게 하여 하판이 완성된다. 상판은 PET 필름 ④ 위에 투명 도전막 ② 을 형성한 후 그 위에 후막 인쇄법을 사용하여 전극 ⑧ 을 형성함으로써 완성된다. 이렇게 하여 상판과 하판이 제작 완료되면 상기 상판 및 하판을 서로 결합시킴으로서 터치 패널을 완성한다.The prior art touch panel fabrication process related to touch panel fabrication is shown in detail in FIG. 5. First, a transparent conductive film is formed on a glass or plastic substrate. The transparent conductive film is formed directly on the substrate, or by forming a transparent film (for example, PET film) having a conductive film on the substrate by using a transparent double-sided tape. When the transparent conductive film is formed, the portion of the transparent conductive film that is not necessary for the electrode wiring is removed using a photolithography process. The removal process by the photolithography process is performed through a photoresist (PR) application, drying, exposure, etching, photoresist removal (PR strip) and the like. After the photolithography process is completed, the electrode ⑧ is formed by the thick film printing method, and the dot spacer ⑤ is formed using the thick film printing method or the photo process. After that, attach both sides of tape ③ to join the top plate. In this way, the bottom plate is completed. The upper plate is completed by forming a transparent conductive film ② on the PET film ④ and then forming an electrode ⑧ on the film using a thick film printing method thereon. In this way, when the upper plate and the lower plate is completed, the upper panel and the lower plate are combined with each other to complete the touch panel.
이에 반해 본 발명에 의한 터치 패널 제작공정은 도 6 에 나타낸 바와 같이 먼저 후막 인쇄법등으로 플라스틱 기판 위에 전극 ⑧ 을 형성하고, 투명 도전막을 형성하기 위하여 투명 도전막 ② 이 형성된 PET 필름 ④ 을 알맞은 크기로 절단하여 전극이 형성된 기판 위에 투명 양면 테이프 ⑦ 를 사용하여 접착한다. 그런 후 전극과 투명 도전막을 연결시키기 위해서 투명 도전막이 형성된 PET 필름에 구멍을 뚫어 디스펜서로 상하 연결용 전극 ⑨ 을 형성한다. 상기 상하 연결용 전극이 완성되면 양면 테이프 ③ 를 부착하여 하판을 완성한다. 상판은 기존 공정과 마찬가지 방법으로, PET 필름 ④ 위에 투명 도전막 ② 을 형성하고 그 위에 후막 인쇄법등으로 전극 ⑧ 을 형성한다. 이렇게 하여 완성된 상판 및 하판을 결합함으로써 터치 패널이 완성된다.In contrast, in the manufacturing process of the touch panel according to the present invention, as shown in FIG. 6, the electrode ⑧ is first formed on a plastic substrate by a thick film printing method, and the PET film ④ having the transparent conductive film ② is formed in a suitable size to form a transparent conductive film. Cut and bond the transparent double-sided tape ⑦ onto the substrate on which the electrode is formed. Then, in order to connect the electrode and the transparent conductive film, a hole is formed in the PET film on which the transparent conductive film is formed to form an electrode ⑨ for vertical connection with a dispenser. When the vertical connection electrode is completed, the double-sided tape ③ is attached to complete the lower plate. In the same manner as in the conventional process, the upper plate forms a transparent conductive film ② on the PET film ④ and forms an electrode ⑧ on the film by a thick film printing method or the like. In this way, the touch panel is completed by combining the completed upper and lower plates.
이와같이 본 발명에 의한 제조공정에서는 전극을 먼저 형성하고 그 위에 투명 도전막을 붙인 후 디스펜서로 상하 연결용 전극 ⑨ 을 형성하여 전극 ⑧ 과 투명 도전막 ② 을 연결시키기 때문에 기존의 공정에서는 반드시 필요한 사진 식각 공정이 필요 없게 된다.As described above, in the manufacturing process according to the present invention, an electrode is first formed, and then a transparent conductive film is attached thereon, and a vertically connecting electrode ⑨ is formed by using a dispenser to connect the electrode ⑧ and the transparent conductive film ②. You do not need this.
상기와 같이 구성된 본 발명과 종래의 터치 패널과 비교할 때, 다음과 같은 효과를 기대할 수 있다.When compared with the present invention configured as described above and a conventional touch panel, the following effects can be expected.
첫째, 투명 도전막을 식각하는 사진 식각 공정이 불필요하여 식각 공정시 필요한 스핀 코터(spin coater), 노광기, 오븐, 클리닝 장치(wet station)등 많은 고가의 장비들이 필요 없게 됨으로써 설비비를 줄일 수 있다.First, since a photolithography process for etching a transparent conductive film is unnecessary, many expensive equipments such as a spin coater, an exposure machine, an oven, a wet station, and the like required for the etching process are not required, thereby reducing equipment costs.
둘째, 사진 식각 공정이 필요없어 식각 공정에 필요한 감광제, 투명도전막 식각용액, 현상제등 고가의 재료들을 사용할 필요가 없기 때문에 재료비를 줄일 수 있다.Second, since the photolithography process is not necessary, the cost of the photoresist, the transparent conductive film etching solution, and the developer, which are necessary for the etching process, does not need to use expensive materials, thereby reducing the material cost.
셋째, 감광제 도포, 건조, 식각, 감광제 제거, 세척 등에 소요되는 시간을 줄일 수 있어 생산성을 높일 수 있다.Third, it is possible to reduce the time required to apply a photosensitive agent, drying, etching, removing the photosensitive agent, washing, etc., thereby improving productivity.
Claims (8)