KR100303380B1 - 전하 발생 물질이 첨가된 방수제의 제조방법 - Google Patents
전하 발생 물질이 첨가된 방수제의 제조방법 Download PDFInfo
- Publication number
- KR100303380B1 KR100303380B1 KR1019990035730A KR19990035730A KR100303380B1 KR 100303380 B1 KR100303380 B1 KR 100303380B1 KR 1019990035730 A KR1019990035730 A KR 1019990035730A KR 19990035730 A KR19990035730 A KR 19990035730A KR 100303380 B1 KR100303380 B1 KR 100303380B1
- Authority
- KR
- South Korea
- Prior art keywords
- waterproofing agent
- charge generating
- added
- generating material
- manufacturing
- Prior art date
Abstract
본 발명은 전하 발생 물질이 첨가된 방수제의 제조방법에 관한 것으로, 방수제의 단순 목적인 방수기능이외에 독성성분을 사용하지 않으면서도 살균능력을 가질 수 있도록 한 전하 발생 물질이 첨가된 방수제의 제조방법을 제공하는 데 그 목적이 있으며, 상기한 목적을 달성하기 위한 본 발명은 흡수성수지에 침투성 발수 방수제 혼합하는 일반적인 방수제 제조방법에 있어서, 상기 흡수성 수지 100중량부에 대하여 3내지 45㎛로 미분쇄한 전하 발생 물질을 5내지 15중량부 첨가하고 교반하여 혼합용액을 제조한 다음, 제조된 혼합용액 100㎖에 대하여 메틸 셀룰로우스(methyl cellulose)를 50내지 70㎎의 비율로 첨가하여 점도를 740내지 780 cp로 조절하는 것을 특징으로 하는 전하 발생 물질이 첨가된 방수제의 제조방법을 제공함으로써 달성할 수 있다.
Description
본 발명은 전하 발생 물질이 첨가된 방수제의 제조방법에 관한 것으로, 보다 상세하게는 통상의 방수제가 가지는 물이 침투하는 것을 방지하는 기능 이외에 살균력이 부가되어 방수제를 바른 부위에 미생물 증식을 막아 청결한 상태를 유지 할 수 있도록 한 전하 발생 물질이 첨가된 방수제의 제조방법에 관한 것이다.
종래로 부터 건축물 내외의 물과 접하는 부분에서 외부로부터 침투되는 물과 내부에서 외부로 빠져나가는 물을 방지하기 위해 방수제를 필요한 부분에 발라 처리하였다.
즉 배의 밑바닥이나 주택가구 건물내부의 지하실 또는 화장실 등의 물과 접하는 다양한 분야에서 누수가 생기는 것을 방지하기 위하여 방수제를 이용하여 처리하여 왔다.
상기와 같이 다양한 용도로 사용되는 방수제의 제조방법은 에폭시수지, 비스페놀A, 폴리에스테르수지, 페놀수지, 우레아수지, 멜라민수지, 폴리에틸렌수지 등의 통상적으로 방수제로 사용되는 수지에 침투성 발수 방수제 혼합한 다음, 방수제의 종류 및 필요한 용도에 따라 에스테르 및 케톤 등의 적당한 유기용제를 선택하여 희석하는 방법으로 방수제를 제조하여 왔다.
상기에서 제조된 방수제를 사용는 경우 아민류, 산무수물, 폴리아미드 및 이미다졸류의 경화제를 첨가하여 사용하여 왔다.
그러나 상기한 제조방법으로 제조된 방수제의 경우 단순히 방수기능만을 가지므로, 상기한 방수제를 배의 밑바닥이나 주택의 지하실 및 화장실 등에 바르게 되면 습기가 찬 부분에 곰팡이 및 각종 미생물이 번식하게 되는 문제점이 발생하였다.
따라서 상기와 같은 문제점을 해결하기 위해 에폭시수지에 무기항균제를 첨가하여 방수제를 제조하는 방법이 제시되었다.
그러나 상기한 무기항균제를 첨가한 방수제를 배의 밑바닥에 칠하여 사용하는 경우 무기항균제가 가지는 독성성분이 바닷물속에 용해되어 해양오염을 일으키는 원인으로 작용할 뿐만 아니라, 주택건물에 사용할 경우에도 독성성분이 공기중으로 용출되어 나와 인체에 나쁜 영향을 미친다는 문제점이 발생하였다.
이에 본 발명은 상기와 같은 종래의 문제점을 해결하기 위한 것으로 방수제의 단순 목적인 방수기능이외에 독성성분을 사용하지 않으면서도 살균능력을 가질 수 있도록 한 전하 발생 물질이 첨가된 방수제의 제조방법을 제공함을 그 목적으로 한다.
상기한 목적을 달성하기 위한 본 발명은 흡수성수지에 침투성 발수 방수제 혼합하는 일반적인 방수제 제조방법에 있어서, 상기 흡수성 수지 100중량부에 대하여 3내지 45㎛로 미분쇄한 전하 발생 물질을 5내지 15중량부 첨가하고 교반하여 혼합용액을 제조한 다음, 제조된 혼합용액 100㎖에 대하여 메틸 셀룰로우스(methyl cellulose)를 50내지 70㎎의 비율로 첨가하여 점도를 740내지 780 cp로 조절하는 것을 특징으로 하는 전하 발생 물질이 첨가된 방수제의 제조방법을 제공함으로써 달성할 수 있다.
상기에서 사용가능한 흡수성수지에는 에틸렌 비닐 아세테이트, 아크릴 수지, 폴리비닐 알코올, 폴리아크릴산 나트륨, 폴리에틸렌 옥사이드, 아크린산아미드, 셀룰로스, 아라비아 고무, 알긴산나트륨 등이 있으며, 또한 비닐 알코올-아크린산염 공중합체, 초산비닐-아크린산 메틸 공중합체, 아크린산-아크린산 에스테르 공중합체등 흡수성이 높은 공중합체 수지도 사용할 수 있다.
상기 방수제의 제조공정에서 흡수성 수지에 미분쇄한 전하발생 물질을 첨가하게 되는 데, 전하 발생 물질로는 일반적으로 전기석이라고 불리는 우라늄광, 자철광 및 토루마린 등의 천연광물을 사용할 수 있으며, 이온화경향이 다른 두개의 금속물질을 사용할 수 있다.
일반적으로 전기석이란 현재 지구상에 존재하는 광물중에서 자체적으로 에너지를 갖고 있어 자연상태에서 스스로 전하를 띠고 있는 광물을 말하며, 특히 토루마린은 붕소를 함유하는 규산염 광물질로 특이한 결정구조를 가지며, 외부로부터 충격에너지 또는 열에너지를 흡수하여 이를 전류에너지로 변환시켜 약 0.06㎃의 미세한 전류가 영구적으로 흐른다는 특징이 있다.
상기와 같은 전기석의 일반적인 화학적 조성은 하기한 화학식 1과 같으며, 흑, 청, 적, 녹, 자, 백색등 그 색상 또한 다양하다.
X는 Ca, Na, K, Mn등의 물질로 1개 또는 그 이상.
Y는 Mg, Fe, Al, Cr, Mn, Ti, Li등의 물질로 1개 또는 그 이상.
상기와 같은 특징을 갖는 전하 발생 물질이 방수제를 제조하는 과정에서 첨가되게 되면 이온화 경향이 서로 다른 두개의 금속류는 전위차에 의해서 전류가 흐르게 되고, 또한 전기석은 자체에 의해 전류가 흐르게 된다.
이 전류에 의해 물은 수산화 이온(OH-)과 수소이온(H+)으로 전기분해 되며, 이때 수소이온은 전하 발생 물질에서 방출되는 전자을 받아 수소가스 상태로 공기중으로 방출 되며, 또한 수산화이온은 상기와 같은 반응의 연속으로 계속적으로 생성되어 물을 pH 7.5의 약 알칼리성이 되게 한다.
상기와 같은 반응에 의해 수중에는 미세한 전류가 흐르게 되고, 발생되는 미세한 전류는 단백질을 분해하게 됨으로써 수중 미생물을 살균할 수 있는 능력을 갖게 되는 것이다.
따라서, 상기에서 설명한 살균력을 갖기 위해 전하 발생 물질은 3내지 45㎛로 미분쇄한 다음, 흡수성 수지 100중량부에 대하여 5내지 15중량부 첨가하여 교반하게 되는 것이다.
이때 전하 발생 물질의 입자 크기가 3㎛ 미만일 경우 겉보기 비중이 낮아져 수지와 전하 발생 물질의 혼화가 용이하지 않게 되는 문제점이 발생하며, 45㎛를 초과할 경우 입자가 크므로 쉽게 침전되는 문제점이 있으므로 3내지 45㎛로 미분쇄하는 것이 바람직하다.
또한 그 첨가량은 5중량부 미만일 경우 전하 발생 물질의 량이 적어 살균효과를 충분히 나타낼 수 없다는 문제점이 발생하게 되고, 15중량부를 초과할 경우 전하 발생 물질의 량이 많아지므로 살균력은 향상되지만 점도 조절이 용이하지 못하다는 문제점이 발생하므로 흡수성 수지 100중량부에 대하여 5내지 15중량부 첨가하는 것이 바람직하다.
또한 제조된 혼합용액의 침전을 방지하기 위하여 적당한 점도 조절이 필요하게 되는 데, 이때 메틸 셀룰로우스(methyl cellulose)를 혼합용액 100㎖에 대하여 50내지 70㎎의 비율로 첨가하여 점도가 740내지 780 cp가 되도록 첨가한다.
상기에서 메틸 셀룰로우스의 첨가량이 50㎎미만으로 첨가할 경우 방수제의 점도가 떨어져 상기에서 첨가한 이온화물질의 침전을 빠르게 진행시키게 되며, 70㎎을 초과할 경우 점도가 높아져 침전물을 생기지 않지만 방수제의 상부로 이온화물질이 부상하는 문제점이 발생하므로 혼합용액 100㎖에 대하여 50내지 70㎎ 첨가하여 혼합용액의 점도를 740내지 780 cp로 하는 것이 바람직하다.
이하 본 발명을 하기한 실시예 및 실험예를 참조하여 상세하게 설명하나, 본 발명은 하기한 실시예에 한정되는 것은 아니다.
<실시예 1>
흡수성수지에 침투성 발수 방수제 혼합하는 일반적인 방수제 제조방법에 있어서, 상기 흡수성 수지로 에틸렌 비닐 아세테이트 수지 100중량부에 대하여 10㎛로 미분쇄한 전기석 10중량부를 첨가하고 교반하여 혼합용액을 제조한 다음, 혼합용액 100㎖에 대하여 메틸 셀룰로우스를 70㎎의 비율로 첨가하여 점도를 760 cp로 조절하여 전하 방출 물질이 첨가된 방수제를 제조하였다.
<실시예 2>
흡수성수지에 침투성 발수 방수제 혼합하는 일반적인 방수제 제조방법에 있어서, 상기 흡수성수지로 아크릴 수지 100중량부에 대하여 10㎛로 미분쇄한 전기석 10중량부를 첨가하고 교반하여 혼합용액을 제조한 다음, 혼합용액 100㎖에 대하여 메틸 셀룰로우스를 50㎎의 비율로 첨가하여 점도를 760 cp로 조절하여 전하 방출 물질이 첨가된 방수제를 제조하였다.
<실시예 3>
흡수성수지에 침투성 발수 방수제 혼합하는 일반적인 방수제 제조방법에 있어서, 상기 흡수성수지로 에틸렌 비닐 아세테이트 수지 100중량부에 대하여 10㎛로 미분쇄한 동분(Cu)과 아연분(Zn)을 각각 5중량부씩 첨가하고 교반하여 혼합용액을 제조한 다음, 혼합용액 100㎖에 대하여 메틸 셀룰로우스를 70㎎의 비율로 첨가하여 점도를 760 cp로 조절하여 전하 방출 물질이 첨가된 방수제를 제조하였다.
<비교예>
전하 발생 물질을 첨가하지 않고 상기 실시예 1과 동일한 조건으로 통상의방수제 제조방법에 의해 방수제를 제조하였다.
<실험예 1>
수중미생물의 살균효과를 측정하기 위하여 상기 실시예 1내지 3 및 비교예에서 제조한 방수제를 이용하여 4개의 비이커 내부에 각각 도포하여 충분히 건조한 다음, 각각의 비이커에 일정량의 물을 붓고 각각 민물조개 5개씩을 넣어 시간 경과에 따른 민물조개의 생존 갯수를 측정하여 표 1에 나타내었다.
| 구분 | 24시간 | 48시간 | 72시간 |
| 실시예 1 | 3 | 0 | 0 |
| 실시예 2 | 4 | 2 | 0 |
| 실시예 3 | 2 | 0 | 0 |
| 비교예 | 5 | 3 | 2 |
상기 표 1에서 보는 바와 같이 전하 발생 물질을 첨가하여 방수제를 제조한 실시예 1내지 3의 경우 24시간 경과 후 실시예 1은 3개, 실시예 2는 4개, 실시예 3은 2개의 민물조개만 생존해 있는 것을 확인할 수 있었으나, 전하 발생 물질을 첨가하지 않은 비교예의 경우 5개 모두 살아 있는 것을 확인 할 수 있었다.
또한 72시간 경과 후에는 실시예 1내지 3의 경우 민물조개가 모두 죽은 것을 확인할 수 있으나, 비교예의 경우 2개가 살아 있는 것을 확인 할 수 있었다.
따라서, 본 발명에 의해 제조된 방수제의 경우 통상의 제조방법에 의해 제조된 방수제에 비해 살균력이 뛰어난 것을 확인 할 수 있다.
상기에서 살펴본 바와 같이 살균력이 뛰어나므로 습기가 차고 미생물이 번식하는 분야에서 사용하게 되면 살균 효과를 얻을 수 있다는 장점이 있다
상기에서 설명한 바와 같이 본 발명은 방수제에 전하 발생 물질을 첨가함으로써 통상의 방수제가 가지는 방수 효과 이외에 독성물질을 사용하지 않으면서도 살균력이 부가됨으로써, 배의 밑바닥이나 주택의 지하실 및 화장실 등 습기가 차고 곰팡이나 각종 미생물 번식이 발생하는 분야에서 사용할 경우 미생물 증식을 막아 깨끗한 환경을 유지할 수 있는 효과를 얻을 수 있다.
또한 본 발명에 의해 제조된 방수제 자체에 전하를 발생하는 물질이 첨가됨으로 방수제로부터 음이온이 발생하여 음이온이 나타내는 공기청정의 효과를 부수적으로 얻을 수 있는 유용한 발명이다.
Claims (4)
- 계면활성제를 첨가하여 만든 흡수성 수지 에멀젼에 침투성 발수 방수제 및 경화제를 혼합하는 방수제의 제조방법에 있어서, 상기 흡수성 수지 100중량부에 대하여 3내지 45㎛로 미분쇄한 전하 발생 물질을 5내지 15중량부 첨가하고 교반하여 혼합용액을 제조한 다음, 제조된 혼합용액 100㎖에 대하여 메틸 셀룰로우스(methyl cellulose)를 50내지 70㎎의 비율로 첨가하여 점도를 740내지 780 cp로 조절하는 것을 특징으로 하는 전하 발생 물질이 첨가된 방수제의 제조방법.
- 상기 제 1항에 있어서, 흡수성 수지는 에틸렌 비닐 아세테이트, 아크릴 수지, 폴리비닐 알코올, 폴리아크릴산 나트륨, 폴리에틸렌 옥사이드, 아크린산아미드, 셀룰로스, 아라비아 고무, 알긴산나트륨 등이 있으며, 또한 비닐 알코올-아크린산염 공중합체, 초산비닐-아크린산 메틸 공중합체, 아크린산-아크린산 에스테르 공중합체등의 흡수성이 높은 공중합체 수지를 포함하는 것을 특징으로 하는 전하 발생 물질이 첨가된 방수제의 제조방법.
- 제 1항 또는 제 2항에 있어서, 전하 발생 물질로 우라늄광, 자철광 및 토루마린 등의 전기석을 사용함을 특징으로 하는 전하 발생 물질이 첨가된 방수제의 제조방법.
- 제 1항 또는 제 2항에 있어서, 전하 발생 물질로 이온화경향이 다른 두개의 금속물질을 사용함을 특징으로 하는 전하 발생 물질이 첨가된 방수제의 제조방법.