KR100286825B1 - Manufacturing method of partition wall for plasma display panel - Google Patents
Manufacturing method of partition wall for plasma display panel Download PDFInfo
- Publication number
- KR100286825B1 KR100286825B1 KR1019980021101A KR19980021101A KR100286825B1 KR 100286825 B1 KR100286825 B1 KR 100286825B1 KR 1019980021101 A KR1019980021101 A KR 1019980021101A KR 19980021101 A KR19980021101 A KR 19980021101A KR 100286825 B1 KR100286825 B1 KR 100286825B1
- Authority
- KR
- South Korea
- Prior art keywords
- dry film
- partition wall
- laser beam
- partition
- mask
- Prior art date
Abstract
본 발명은 대형 평판표시 소자로 각광 받고있는 플라즈마 디스플레이 패널(Plasma Display Panel, PDP)의 격벽을 제조하는 방법에 관한 것으로서 보다 상세하게는 PDP 기판(4)의 상부에 소성가공성이 우수한 격벽용 건식필름(2)을 압착시키면서 상기 격벽용 건식필름(2)의 상부를 유사격벽형상(5)으로 성형하는 단계와, 상기 유사격벽형상(5)의 돌기(5-1) 상부에 마스크(10)를 위치시키는 단계와, 상기 마스크(10)가 위치한 유사격벽형상(5)의 상부에서 레이져발진기(6)를 이용 레이져 빔(7)을 조사하여 유사격벽형상(5)의 돌기(5-1)와 돌기(5-1) 사이의 격벽용 건식필름(2)을 식각시키면서 에어노즐(11)에 의해 분사된 공기로 레이져 빔(7)에 의해 열화된 격벽용 건식필름(2)을 배제시키는 단계로 이루어지는 것을 특징으로 하는 플라즈마 디스플레이 패널용 격벽의 제조방법에 관한 것이다.The present invention relates to a method for manufacturing a partition of a plasma display panel (PDP), which has been spotlighted as a large flat panel display device. More specifically, a dry film for partition walls having excellent plastic workability on an upper portion of a PDP substrate 4. (2) compressing the upper part of the dry film (2) for the partition wall to form a similar partition wall (5), and the mask (10) on the top of the projection (5-1) of the similar partition wall (5) Positioning and the projection (5-1) of the similar partition wall (5) by irradiating the laser beam (7) using the laser oscillator (6) on the upper part of the similar partition wall (5) where the mask 10 is located Removing the partition dry film 2 deteriorated by the laser beam 7 with the air injected by the air nozzle 11 while etching the partition dry film 2 between the projections 5-1. In the manufacturing method of the partition wall for plasma display panel It is about.
상기와 같은 본 발명에 의해 제조공정이 단순하고 균일성이 우수하여 격벽용 원재료의 절감 및 공정시간의 단축으로 PDP격벽의 제조원가를 저감시킬 수 있음은 물론 연속적인 공정이 가능하여 생산성을 향상시킬 수 있다.According to the present invention as described above, the manufacturing process is simple and excellent in uniformity, which can reduce the manufacturing cost of PDP bulkheads by reducing raw materials for bulkheads and shortening the process time, as well as enabling continuous processes to improve productivity. have.
Description
본 발명은 대형 평판표시 소자로 각광 받고있는 플라즈마 디스플레이 패널(Plasma Display Panel, PDP)의 격벽을 제조하는 방법에 관한 것으로서 보다 상세하게는 PDP에서 표시 소자의 해상도(Resolution)를 결정하고, 화소간의 혼색(Cross Talk)을 방지하는 역할을 하는 플라즈마 디스플레이 패널용 격벽의 제조방법에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for manufacturing partition walls of a plasma display panel (PDP), which has been spotlighted as a large flat panel display device. More particularly, a resolution of a display device is determined in a PDP, and color mixing between pixels is performed. The present invention relates to a method of manufacturing a partition wall for a plasma display panel, which serves to prevent cross talk.
종래 격벽을 제조하는 방법으로는 크게 2가지가 있는데 먼저, 격벽재료를 함유하고 있는 페이스트(Paste)를 일정한 높이가 될 때 까지 인쇄하는 방법으로 통상 10회 이상의 인쇄와 건조공정이 반복되어야 하며, 인쇄된 격벽의 형상이 작업환경의 온도, 습도 등에 많은 영향을 받는 문제점을 갖고 있다.Conventionally, there are two methods for manufacturing bulkheads. First, a paste containing partition material is printed until it reaches a certain height, and at least 10 printing and drying processes must be repeated. The shape of the partition wall has a problem that is greatly affected by the temperature, humidity, etc. of the working environment.
그리고, 다른 또 하나의 방법으로는 통상 물 또는 알콜 등의 용매, 바인더, 알루미나, 산화철, 소결용 유리분말, 바인더 등으로 구성된 용액을 일정두께로 흘려 건조시키는 테잎 캐스팅(Tape Casting)법으로 제조되는 격벽용 건식필름의 일정부분을 경화시켜 감광성 코팅층을 형성시킨후 샌드 블라스트(Sand Blast)법으로 코팅되지 않은 부분을 식각하여 격벽을 형성하는 방법으로, 이 방법은 전공정 즉, 격벽형성을 하기위한 샌드 블라스트 공정전에 감광성 코팅층을 형성시키는 공정이 매우 복잡하며, 이러한 일련의 공정이 단속(Batch)공정임으로 인해 생산성이 떨어지는 등의 문제점이 있었다.In addition, another method is usually produced by a tape casting method in which a solution composed of a solvent such as water or alcohol, a binder, alumina, iron oxide, glass powder for sintering, a binder, and the like is flowed to a predetermined thickness and dried. A part of the dry film for partition walls is hardened to form a photosensitive coating layer, and then a part of the dry film for etching is formed by etching the uncoated part by sand blast method. The process of forming the photosensitive coating layer before the sand blasting process is very complicated, and there is a problem that productivity is reduced due to the batch process being a batch process.
또한, 최근 평판표시 소자가 대형화, 고선명화됨에 따라 40"급 이상의 PDP 개발이 활발하게 이루어지고 있는데, 이와같은 균일한 해상도와 장수명을 갖는 PDP를 얻기위해서는 패널내 격벽간의 거리와 격벽높이의 비(aspect ratio)가 4:1 이상이어야 하며, 두께 및 높이의 편차가 적고, 격벽내부의 결함이 적어야 한다.In addition, as the size of flat panel display devices becomes larger and sharper, the development of PDPs of 40 "or more has been actively developed. In order to obtain PDPs having a uniform resolution and long life, the ratio of the distance between the partition walls and the partition height ( The aspect ratio should be 4: 1 or more, the thickness and height variation should be small, and the defect inside the bulkhead should be small.
상기와 같은 문제점을 해결하기 위하여 본 발명은 롤러형 압축몰드 및 레이져를 이용하여 연속적, 경제적이며 고해상도를 가질 수 있는 플라즈마 디스플레이 패널용 격벽의 제조방법을 제공하는 것을 그 목적으로 한다.In order to solve the above problems, an object of the present invention is to provide a method for manufacturing partition walls for plasma display panels that can have a continuous, economical and high resolution by using a roller-type compression mold and a laser.
상기한 본 발명의 목적은, PDP기판의 상부에 소성가공이 우수한 격벽용 건식필름을 압착시키면서 상기 격벽용 건식필름의 상부를 성형용 압축롤의 외주면 형성과 대응되는 유사격벽형상을 갖도록 성형하는 단계와; 상기 유사격벽형상의 돌기 상부에 마스크를 위치시키는 단계와; 상기 마스크가 위치한 유사격벽형상의 상부에서 레이져발진기를 이용 레이져빔을 상기 유사격벽형상의 내부 바닥면을 이루는 건식 필름에 조사하여 이를 구성하는 폴리머의 분자간 결합을 파괴함으로써 상기 건식필름을 식각시킴과 동시에 에어노즐을 통해 분사된 공기로 레이져빔에 의해 열화된 격벽용 건식필름을 배제시키는 단계를 포함하여 이루어짐에 의해 달성된다.An object of the present invention, the step of molding the upper part of the dry film for the partition wall to have a similar partition wall shape corresponding to the outer peripheral surface of the compression roll for forming while pressing the dry film for partition wall excellent in plastic processing on the upper portion of the PDP substrate Wow; Positioning a mask on an upper portion of the similar barrier rib-shaped protrusion; The dry film is etched by irradiating a dry film forming the inner bottom surface of the quasi-barrier shape with a laser oscillator on the upper part of the quasi-barrier shape where the mask is located to destroy the intermolecular bonds of the polymer constituting the mask. It is achieved by including the step of excluding the dry film for the partition wall degraded by the laser beam with the air injected through the air nozzle.
그리고, 상기 PDP기판의 하부에는 히터를 설치하여 건식필름의 압착을 활성화시키며, 상기 건식필름의 성형은 외주면에 격벽형상과 동일한 형상을 갖는 압축롤을 이용하며, 상기 마스크는 다수개의 레이져빔홀과 격벽보호판이 교대로 형성되어 있는 것을 그 특징으로 한다.In addition, a heater is installed on the lower portion of the PDP substrate to activate the crimping of the dry film, and the forming of the dry film uses a compression roll having the same shape as the partition wall on the outer circumferential surface, and the mask includes a plurality of laser beam holes and partition walls. The protective plate is characterized in that the alternately formed.
또한, 상기 레이져발전기와 마스크의 사이에는 실린더형 렌즈를 설치하여 상기 레이져빔을 선형레이져빔으로 변환시켜 조사하며, 에어노즐에 의해 분사되는 공기에 세라믹분말을 혼입시켜 분사함으로써 식각효율을 향상시키고, 레이져빔의 조사에는 CO2, Nd-YAG, Excimer 레이져발진기가 사용되는 것을 특징으로 한다.In addition, a cylindrical lens is installed between the laser generator and the mask to convert the laser beam into a linear laser beam and irradiate it, and improve the etching efficiency by mixing and spraying ceramic powder into the air injected by the air nozzle. The laser beam is characterized in that CO 2 , Nd-YAG, Excimer laser oscillator is used.
이하, 도면을 참조하여 본 발명을 보다 상세하게 설명한다.Hereinafter, the present invention will be described in more detail with reference to the drawings.
도 1a는 외주면에 다수개의 격벽형상이 성형된 압축롤과 압축선 PDP기판 상부에 위치하는 건식필름의 모식도이고, 도 1b는 압축후 격벽형상으로 성형된 건식필름의 모식도이며, 도 2는 레이져빔을 이용하여 격벽을 식각하는 것을 도시한 개략도이고, 도 3은 마스크의 평면도이다.Figure 1a is a schematic diagram of a dry film formed on the compression roll and the compression line PDP substrate formed on the outer peripheral surface of the plurality of partition wall shape, Figure 1b is a schematic view of a dry film formed into a partition wall shape after compression, Figure 2 is a laser beam 3 is a schematic view showing etching of the partition wall using FIG. 3, and FIG. 3 is a plan view of the mask.
먼저, 본 발명은 도 1에 나타낸 바와 같이, 소성가공성이 우수한 격벽용 건식 필름(2)을 PDP기판(4)의 상부에 위치시킨 후 다수개의 격벽형상이 외주면에 성형되어 있는 압축롤(1)을 이용하여 격벽용 건식필름(2)을 PDP기판(4)에 압착시키면서 상기 건식필름(2)을 격벽(12) 형태의 유사격벽형상(5)으로 만들어, 상기 건식필름(2)의 압착효율을 향상시키기 위하여 PDP기판(4)의 하부에 히터(3)를 설치한다.First, as shown in FIG. 1, the present invention provides a compression roll 1 in which a plurality of partition walls are formed on an outer circumferential surface after placing a dry film 2 for barrier ribs having excellent plastic workability on an upper portion of a PDP substrate 4. By pressing the dry film 2 for the partition wall to the PDP substrate 4 to form a similar partition wall shape 5 in the form of the partition wall 12 while pressing the dry film 2, the compression efficiency of the dry film (2) In order to improve the temperature, the heater 3 is installed under the PDP substrate 4.
여기에서, 상기 유사격벽형상(5)은 완전한 격벽(12)이 형성되기 전의 격벽, 즉 격벽(12)을 제외한 PDP기판(4)과 연결된 돌기(5-1)들 사이의 불필요부위인 바닥면(5-2)이 식각되기 전의 형상을 지칭하는 것으로 다양한 형상을 가질 수 있으나 바람직하게는 미세하지만 사다리꼴형상을 갖도록 하여 준다.Here, the similar partition wall shape 5 is a bottom surface which is an unnecessary part between the partitions before the complete partition 12 is formed, that is, the projections 5-1 connected to the PDP substrate 4 except for the partition wall 12. (5-2) refers to the shape before etching, which may have various shapes, but is preferably fine but trapezoidal.
이후, 유사격벽형상(5)으로 성형된 격벽용 건식필름(2)의 상부에 다수개의 레이져빔 통로인 레이져빔홈(10-1)과 격벽보호판(10-2)이 교대로 형성된 마스크(10)를 위치시킨 후 CO2, Nd-YAG, Excimer레이져 발진기(6)에서 마스크(10)의 레이져빔홀(10-1)을 통해 레이져빔(7)을 조사하여 유사격벽형상(5)의 돌기(5-1)외 돌기(5-1) 사이인 바닥면(5-2)을 형성하는 건식필름(2)을 식각하게 된다.Subsequently, a mask 10 having a plurality of laser beam passages 10-1 and a barrier protection plate 10-2 alternately formed on the upper portion of the dry film 2 for barrier ribs formed into a pseudo barrier rib shape 5 is formed. After placing the laser beam 7 through the laser beam hole 10-1 of the mask 10 in the CO 2 , Nd-YAG, Excimer laser oscillator 6, the projections of the similar bulkhead shape 5 are formed. The dry film 2 forming the bottom surface 5-2 between the protrusions 5-1 is etched.
이때, 상기 레이져발진기(6)와 마스크(10) 사이에 실린더형렌즈(8)를 실시하여 단선인 레이져빔(7)을 선형레이져빔(9)으로 변환하여 보다 효율적인 격벽용 건식필름(2)의 식각작업을 행할 수 있다.At this time, a cylindrical lens 8 is applied between the laser oscillator 6 and the mask 10 to convert the laser beam 7, which is a single line, into a linear laser beam 9, so that the dry film 2 for barrier ribs is more efficient. Can be etched.
한편, 상기와 같이 레이져빔(7) 또는 선형레이져빔(9)으로 격벽용 건식필름(2)을 식각하면서 레이져발진기(6)와 마스크(10) 사이 또는 실리더형렌즈(8)의 양측면에 위치한 에어노즐(11)을 통해 공기가 분사되어 레이져빔(7,9)에 의해 열화된 필름이 배제된다.Meanwhile, as described above, the barrier dry film 2 is etched using the laser beam 7 or the linear laser beam 9, and is disposed between the laser oscillator 6 and the mask 10 or on both sides of the cylindrical lens 8. Air is blown through the air nozzle 11 located so that the film degraded by the laser beams 7, 9 is excluded.
이와 같이 식각된 식각된 격벽용 건식필름(2)의 배제공정시 상기 에어노즐(11)에 의해 분사되는 공기에 세라믹분말을 혼입시켜 분사함으로써 식각효율을 향상시킬 수 있다.In this way, the etching efficiency may be improved by mixing and spraying ceramic powder into the air injected by the air nozzle 11 during the removal process of the etched partition dry film 2 for etching.
이러한 구성을 갖는 본 발명은 우선 격벽용 건식필름(2)을 히터(3)를 이용하여 적정 성형온도로 가열하고, 압축롤(1)을 이용하여 격벽용 건식필름(2)을 PDP기판(4)에 밀착시키면서 유사격벽형상(5)으로 만든 후, 형성된 상기 유사격벽형상(5)의 돌기(5-1)가 파손되지 않도록 설치된 마스크(10)의 레이져빔홀(10-1)을 통해 조사되는 신형레이져빔(9)이 격벽용 건식필름(2)의 내부 폴리머(POLYMER)를 열화시켜 유사격벽형상(5)의 바닥면(5-2)인 건식필름(2)을 식각시키고 동시에 에어노즐(11)을 통해 공기가 분사되어 열화된 격벽용 건식필름(2)을 배제시킴으로써 완전한 격벽(12)을 형성시킨다.According to the present invention having such a configuration, first, the partition dry film 2 is heated to an appropriate molding temperature by using the heater 3, and the partition dry film 2 is compressed using the compression roll 1 to the PDP substrate 4. After making into a similar bulkhead shape (5) while being in close contact with), and irradiated through the laser beam hole (10-1) of the mask (10) installed so that the projection (5-1) of the formed similar bulkhead shape (5) is not damaged. The new laser beam 9 deteriorates the internal polymer of the barrier dry film 2, thereby etching the dry film 2, which is the bottom surface 5-2 of the pseudo barrier rib 5, and simultaneously removing the air nozzles. 11) air is blown through to form a complete partition wall 12 by excluding the deteriorated dry film 2 for the partition wall.
즉, 레이저빔(9)의 조사에 의해 강한 에너지가 상기 바닥면(5-2)의 건식필름(2) 내부에 결합되어 있는 폴리머의 탄소원자간 결합을 파괴하게 되는 바, 통상 폴리머를 이루는 분자결합이 400~500℃에서 쉽게 파괴되므로 상기 레이져빔(9)의 조사에 의해 전달된 강한 빛에너지는 폴리머의 내부에너지를 강하게 상승시켜 결합되어 있던 분자결합을 끊게 된다. 따라서, 집중적인 레이져빔(9)의 조사를 받게되는 유사격벽형상(5)의 바닥면(5) 부위의 건식필름(2)은 쉽게 식각되게 된다.That is, the strong energy is broken by the irradiation of the laser beam 9 breaks the bond between the carbon atoms of the polymer bonded to the inside of the dry film (2) of the bottom surface (5-2), molecular bonds usually forming a polymer Since the light is easily destroyed at 400 to 500 ° C., the strong light energy transmitted by the irradiation of the laser beam 9 strongly increases the internal energy of the polymer to break the bound molecular bonds. Therefore, the dry film 2 of the bottom surface 5 portion of the quasi-barrier barrier 5 which is subjected to the intensive laser beam 9 is easily etched.
한편, 에어노즐(11)을 통해 분사되는 공기 내에 세라믹분말을 혼입하여 이들의 기계적인 모멘텀에너지(Momentem Energy)에 의하여 식각효율을 항상시킬 수 있으며, 상기 마스크(10)의 격벽보호판(10-2)의 너비를 조절하여 레이져빔을 조사함으로써 격벽(12)의 너비를 50㎛까지 조정할 수 있다.On the other hand, by mixing the ceramic powder in the air sprayed through the air nozzle 11, the etching efficiency can be always made by their mechanical momentum energy (Momentem Energy), the barrier protection plate 10-2 of the mask 10 The width of the partition wall 12 can be adjusted to 50 μm by adjusting the width of the beam.
도 1a는 외주면에 다수개의 격벽형상이 성형된 압축롤과 압축전 PDP기판 상부에 위치하는 건식필름의 모식도, 도 1b는 압축후 격벽형상으로 성형된 건식필름의 모식도,Figure 1a is a schematic diagram of a dry film formed on the compression roll and the upper surface of the PDP substrate before the compression roll formed a plurality of partition wall shape on the outer circumferential surface, Figure 1b is a schematic view of a dry film formed into a partition wall shape after compression,
도 2는 레이져 빔을 이용하여 격벽을 식각하는 것을 나타내는 개략도,2 is a schematic diagram illustrating etching a partition wall using a laser beam;
도 3은 금속 마스크의 평면도이다.3 is a plan view of a metal mask.
〈도면의 주요부분에 사용된 부호의 설명〉<Description of the code used in the main part of the drawing>
1 : 압축롤, 2 : 격벽용 건식필름(Dry Film), 3 : 히터(Heater), 4 : PDP 기판,1: compression roll, 2: dry film for bulkhead, 3: heater, 4: PDP substrate,
5 : 유사격벽형상, 5-1 : 유사격벽형상 돌기, 6 : 레이져 발진기,5: similar bulkhead shape, 5-1: similar bulkhead protrusion, 6: laser oscillator,
7 : 레이져 빔(Laser Beam), 8 : 실린더형 렌즈, 9 : 선형 레이져 빔,7: Laser Beam, 8: Cylindrical Lens, 9: Linear Laser Beam,
10 : 마스크, 10-1 : 레이져 빔 홀, 10-2 : 격벽보호판, 11 : 에어노즐10: mask, 10-1: laser beam hole, 10-2: bulkhead protection plate, 11: air nozzle
상기와 같은 목적을 달성하기 위하여 본 발명은 PDP 기판의 상부에 소성가공성이 우수한 격벽용 건식필름을 압착시키면서 상기 격벽용 건식필름의 상부를 유사격벽형상으로 성형하는 단계와, 상기 유사격벽형상의 돌기부분 상부에 마스크를 위치시키는 단계와, 상기 마스크가 위치한 유사격벽형상의 상부에서 레이져 빔을 조사하여 유사격벽형상의 돌기와 돌기 사이의 격벽용 건식필름을 식각시키면서 에어노즐에 의해 분사된 공기로 레이져 빔에 의해 열화된 격벽용 건식필름을 배제시키는 단계로 이루어지는 것을 특징으로 하는 플라즈마 디스플레이 패널용 격벽의 제조방법을 제공한다.In order to achieve the above object, the present invention is the step of forming the upper part of the dry film for partition walls in a similar partition wall shape while pressing the dry film for partition walls having excellent plastic workability on the upper portion of the PDP substrate, the projection of the similar partition wall shape Positioning the mask on the upper portion of the portion, and irradiating the laser beam from the upper portion of the pseudo-barrier shape in which the mask is located to etch the dry film for partition wall between the projections and projections of the similar partition wall laser beam by the air injected by the air nozzle The present invention provides a method for manufacturing a partition wall for a plasma display panel, comprising the step of excluding a dry film for partition wall deteriorated by.
그리고, 상기 PDP기판의 하부에는 히터를 설치하여 건식필름의 압착을 활성화시키며, 상기 건식필름의 성형은 외주면에 격벽형상과 동일한 형상을 갖는 압축롤을 이용하며, 상기 마스크는 다수개의 레이져빔 홀과 격벽보호판이 교대로 형성되어 있는 것을 그 특징으로 한다.In addition, a heater is installed at the lower portion of the PDP substrate to activate the crimping of the dry film, and the forming of the dry film uses a compression roll having the same shape as the partition wall on the outer circumferential surface, and the mask comprises a plurality of laser beam holes and The partition protection plate is characterized by being alternately formed.
또한, 상기 레이져발진기와 마스크의 사이에는 실린더형 렌즈를 설치하여 상기 레이져 빔을 선형레이져 빔으로 변환시켜 조사하며, 에어노즐에 의해 분사되는 공기에 세라믹분말을 혼입시켜 분사하므로써 식각효율을 향상시키고, 레이져빔의 조사에는 CO2, Nd-YAG, Excimer 레이져 발진기가 사용되는 것을 특징으로 한다.In addition, a cylindrical lens is installed between the laser oscillator and the mask to convert the laser beam into a linear laser beam and irradiate it, and improve the etching efficiency by mixing and spraying ceramic powder into the air injected by the air nozzle. The irradiation of the laser beam is characterized by using a CO 2 , Nd-YAG, Excimer laser oscillator.
이하, 도면을 참조하여 본 발명을 보다 상세하게 설명한다.Hereinafter, the present invention will be described in more detail with reference to the drawings.
도 1a는 외주면에 다수개의 격벽형상이 성형된 압축롤과 압축전 PDP기판 상부에 위치하는 건식필름의 모식도이고, 도 1b는 압축후 격벽형상으로 성형된 건식필름의 모식도이고, 도 2는 레이져 빔을 이용하여 격벽을 식각하는 것을 나타내는 개략도이고, 도 3은 마스크의 평면도이다.Figure 1a is a schematic diagram of a dry film formed on the upper surface of the PDP substrate and the compression roll formed with a plurality of partition wall shape on the outer circumferential surface, Figure 1b is a schematic view of a dry film formed into a partition wall shape after compression, Figure 2 is a laser beam Is a schematic diagram showing etching of the partition wall using Fig. 3, and Fig. 3 is a plan view of the mask.
먼저, 본 발명은 도 1에 나타낸 바와 같이 소성가공성이 우수한 격벽용 건식필름(2)을 PDP 기판(4)의 상부에 위치시킨 후, 다수개의 격벽형상이 외주면에 성형되어 있는 압축롤(1)을 이용하여 격벽용 건식필름(2)을 PDP기판(4)에 압착시키면서 상기 격벽용 건식필름(2)을 격벽(12)형태의 유사격벽형상(5)으로 만들며, 상기 격벽용 건식필름(2)의 압착효율을 향상시키기 위하여 PDP기판(4)의 하부에 히터(3)를 설치한다.First, in the present invention, as shown in FIG. 1, the dry film 2 for barrier ribs having excellent plastic workability is placed on the upper portion of the PDP substrate 4, and then a compression roll 1 having a plurality of barrier rib shapes formed on the outer circumferential surface thereof. The barrier dry film (2) is pressed onto the PDP substrate (4) to form the barrier dry film (2) into a pseudo-barrier shape (5) in the form of a partition wall (12), and the dry film for barrier ribs (2). In order to improve the crimping efficiency of), the heater 3 is installed under the PDP substrate 4.
이후, 유사격벽형상(5)으로 성형된 격벽용 건식필름(2)의 상부에 다수개의 레이져 빔 통로(10-1)와 격벽 보호판(10-2)이 교대로 형성된 마스크(10)를 위치시킨후, CO2, Nd-YAG, Excimer 레이져 발진기(6)에서 마스크(10)의 레이져 빔홀(10-1)을 통해 레이져 빔(7)을 조사하여 유사격벽형상 돌기(5-1)와 돌기(5-1)사이의 격벽용 건식필름(2)을 식각하게 되는데, 이때 상기 레이져발진기(6)와 마스크(10)의 사이에 실린더형 렌즈(8)를 설치하여, 단선인 레이져빔(7)을 선형레이져 빔(9)으로 변환하여 보다 효율적인 격벽용 건조필름(2)의 식각작업을 행할 수 있다.Subsequently, a mask 10 having a plurality of laser beam passages 10-1 and barrier ribs 10-2 alternately positioned is positioned on the dry film 2 for barrier ribs formed into a pseudo barrier rib shape 5. Afterwards, the laser beam 7 is irradiated through the laser beam hole 10-1 of the mask 10 in the CO 2 , Nd-YAG, and Excimer laser oscillator 6 to form a similar bulkhead-shaped protrusion 5-1 and a protrusion ( 5-1), the dry film 2 for the partition wall is etched. At this time, a cylindrical lens 8 is installed between the laser oscillator 6 and the mask 10, and the laser beam 7 is disconnected. It can be converted to a linear laser beam (9) to perform the more efficient etching of the dry film for the partition wall (2).
한편, 상기와 같이 레이져 빔(7) 또는 선형 레이져 빔(9)으로 격벽용 건조필름(2)을 식각하면서 레이져 발진기(6)와 마스크(10) 사이 또는 실린더형 렌즈(8)의 양측면에 위치한 에어노즐(11)을 통해 공기가 분사되어 레이져 빔(7, 9)에 의해 열화된 필름이 배제된다.Meanwhile, as described above, the barrier film 7 is etched by the laser beam 7 or the linear laser beam 9, and is positioned between the laser oscillator 6 and the mask 10 or on both sides of the cylindrical lens 8. Air is blown through the air nozzle 11 to exclude the film degraded by the laser beams 7 and 9.
이와같이 식각된 격벽용 건조필름(2)의 배제공정시 상기 에어노즐(11)에 의해 분사되는 공기에 세라믹분말을 혼입시켜 분사하므로써 식각효율을 향상시킬 수 있다.In this case, the etching efficiency may be improved by mixing and spraying ceramic powder into the air injected by the air nozzle 11 during the removal process of the etched partition dry film 2.
이하, 본 발명의 작용에 대하여 설명한다.Hereinafter, the operation of the present invention will be described.
상기와 같은 방법에 의해 우선 격벽용 건식필름(2)을 히터(3)를 이용하여 적정 성형온도로 가열하고, 압축롤(1)을 이용하여 격벽용 건식필름(2)을 PDP기판(4)에 밀착시키면서 유사 격벽형상(5)으로 만든 후, 형성된 유사격벽형상의 돌기(5-1)가 파손되지 않도록 설치된 마스크(10)의 레이져 빔홀(10-1)를 통해 조사되는 선형 레이져 빔(9)이 격벽용 건식필름(2) 내부의 폴리머를 열화시켜 첨가된 분말들간의 접착력을 약화시켜 유사격벽형상 돌기(5-1)와 돌기(5-1)사이의 격벽용 건식필름(2)을 식각시키고, 동시에 에어노즐(11)을 통해 공기가 분사되어 열화된 격벽용 건식필름(2)을 배제시키므로써 완전한 격벽(12)을 형성시킨다.By the above method, first, the partition dry film 2 is heated to an appropriate molding temperature by using the heater 3, and the partition dry film 2 is compressed using the compression roll 1 to the PDP substrate 4. The linear laser beam 9 irradiated through the laser beam hole 10-1 of the mask 10 installed so as not to be damaged after forming the pseudo partition wall shape 5 while being in close contact with each other. ) The polymer inside the partition dry film (2) deteriorates the adhesion between the powders added to the partition dry film (2) for the partition wall between the similar partition wall projection (5-1) and the projection (5-1). At the same time, air is blown through the air nozzle 11 to remove the deteriorated partition dry film 2 to form a complete partition 12.
한편, 에어노즐(11)을 통해 분사되는 공기내에 세라믹분말을 혼입하여 이들의 기계적인 모멘텀 에너지(Momentem Energy)에 의하여 식각의 효율을 향상시킬 수 있으며, 상기 마스크(10)의 격벽보호판(10-2)의 너비를 조절하여 레이져 빔을 조사하므로써 격벽(12)의 너비를 50㎛까지 조정할 수 있다.On the other hand, by mixing the ceramic powder in the air injected through the air nozzle 11 can improve the efficiency of the etching by their mechanical momentum energy (Momentem Energy), the barrier protection plate 10- of the mask 10 By adjusting the width of 2), the width of the partition wall 12 can be adjusted to 50 μm by irradiating the laser beam.
상기와 같은 본 발명에 의해 제조공정이 단순하고 균일성이 우수하여 격벽용 원재료의 절감 및 공정시간의 단축으로 PDP격벽의 제조원가를 저감시킬 수 있음은 물론 연속적인 공정이 가능하여 생산성을 향상시킬 수 있다.According to the present invention as described above, the manufacturing process is simple and excellent in uniformity, which can reduce the manufacturing cost of PDP bulkheads by reducing raw materials for bulkheads and shortening the process time, as well as enabling continuous processes to improve productivity. have.
Claims (3)