KR100275137B1 - The process for preparing hemp yarn - Google Patents
The process for preparing hemp yarn Download PDFInfo
- Publication number
- KR100275137B1 KR100275137B1 KR1019980049785A KR19980049785A KR100275137B1 KR 100275137 B1 KR100275137 B1 KR 100275137B1 KR 1019980049785 A KR1019980049785 A KR 1019980049785A KR 19980049785 A KR19980049785 A KR 19980049785A KR 100275137 B1 KR100275137 B1 KR 100275137B1
- Authority
- KR
- South Korea
- Prior art keywords
- hemp
- fibers
- raw material
- skin
- vegetable
- Prior art date
Abstract
본 발명은 천연 섬유인 대마사 제조 방법에 관한 것으로서, 특히 100% 대마사를 수공정에 의하지 않고 기계를 이용한 자동화 공정을 통해 양질의 대마사를 제조할 수 있도록 한 대마사 제조 방법에 관한 것이다.The present invention relates to a method for producing hemp yarn, which is a natural fiber, and in particular, to a hemp yarn production method that enables the production of high-quality hemp yarn through an automated process using a machine without 100% hemp yarn by a manual process.
이와 같은 본 발명은 대마 원료를 일정한 길이로 절단하여 염산 및 식물성 액이 섞인 물통에 넣고 일정 시간 정도 담궈둔 후, 고온으로 삶으면서 대마 원료의 겉피와 속피 사이의 결합력을 약화시키는 제1 과정과; 상기 겉피와 속피가 약화된 대마 원료를 타마기에 넣고 두들겨 겉피를 벗겨낸 후, 속피를 일정 기간 물속에 담궈서 염산 및 식물성 액을 희석시키는 제2 과정과; 상기 속피에 함유된 수분을 탈수하고, 식물성 유연제를 소량 뿌린 상태에서 완전 건조하는 제3 과정과; 상기에서 건조된 속피를 다시 타마기에 넣고 두들겨 딱딱한 성질이 약화시키는 제4 과정과; 상기 속피를 그늘진 양생 창고에서 식물성 유연제를 뿌리면서 적층시킨 다음, 일정 기간 자연 양생시키면서 부풀어지게 만드는 제5 과정과; 상기 과정에서 부풀어진 속피를 섬유질대로 가늘게 세분화시켜 장섬유와 단섬유로 분리시키는 제6 과정과; 상기 장섬유와 단섬유를 각각 부드러운 반솜 상태로 만든 다음 일정 굵기의 대마사를 뽑는 제7 과정으로 이루어진 것을 특징으로 한다.Such a present invention comprises the first step of cutting the hemp raw material to a certain length, put it in a bucket of hydrochloric acid and vegetable liquid mixed and soaked for a certain time, and then weakens the binding force between the outer skin and the skin of the hemp raw material while boiling at high temperature; A second step of dipping hydrochloric acid and a vegetable liquid by putting the hemp weakened hemp raw material into a tamper and peeling the outer skin to immerse the inner skin in water for a predetermined time; A third step of dehydrating water contained in the cuticle and completely drying in a state of spraying a small amount of a vegetable softener; A fourth step of putting the dried epithelium in the tamper again and knocking to weaken the hard property; A fifth process of laminating the inner skin while sprinkling the vegetable softener in a shaded curing warehouse and swelling while spontaneously curing for a certain period of time; A sixth process of dividing the inflated epidermis into thin fibers into fibers to separate the long fibers and the short fibers; Each of the long fibers and short fibers is made of a soft half cotton state, characterized in that consisting of a seventh process of extracting the hemp of a certain thickness.
Description
본 발명은 천연 섬유인 대마사 제조 방법에 관한 것으로서, 특히 100% 대마사를 수공정에 의하지 않고 기계를 이용한 자동화 공정을 통해 양질의 대마사를 제조할 수 있도록 한 대마사 제조 방법에 관한 것이다.The present invention relates to a method for producing hemp yarn, which is a natural fiber, and in particular, to a hemp yarn production method that enables the production of high-quality hemp yarn through an automated process using a machine without 100% hemp yarn by a manual process.
통상 대마사는 천연 섬유로서, 이를 직조하여 삼베를 제작하는 실이다. 이와 같이 대마사로 직조된 삼베는 통기성이 우수하고, 땀 흡수력이 뛰어나 인체의 건강에 좋은 영향을 주게 된다.Usually, hemp is a natural fiber, a yarn for weaving it by weaving it. The hemp woven hemp is excellent in breathability, sweat absorption and good health of the human body.
또한, 상기 대마사는 섬유질의 성질이 강해 다른 섬유 보다 신축성이 떨어지는 단점은 있으나 다른 섬유보다 질기고 강해서 수명이 긴 장점이 있다.In addition, the hemp yarn has the disadvantage of inferior elasticity than other fibers due to the strong properties of the fiber, but has the advantage of long life due to being stronger and stronger than other fibers.
여기서, 종래 기술의 대마사 제조 방법은 양재물이나 염산 수용액등에 대마 원료를 넣고 일정 기간 담궈서 대마 원료의 겉피와 속피 사이의 유조직인 펙틴질을 어느 정도 약화시킨 다음, 사람이 직접 칼등의 도구를 이용하여 대마 원료의 겉피를 벗겨낸다.Here, according to the prior art hemp yarn manufacturing method, by putting hemp raw material in a couture or hydrochloric acid solution and soaking for a certain period of time to weaken the pectin, which is an oil tissue between the skin and the epidermis of the hemp raw material, and then directly by using a tool such as a knife. Peel off the outer skin of the raw material.
다음, 상기와 같이 겉피가 벗겨진 속피를 짓이겨 섬유질대로 가늘게 분리하여 사람의 손으로 직접 일정 길이로 세분화된 대마사를 길게 이어서 타래로 감은 후 직조 기계를 통해 삼베 등의 천을 제작하고 있다.Next, as shown above, the outer skin of which the outer skin is peeled off is crushed and finely divided into fibrous fibers. The hemp hemp is further divided into a certain length directly by a human hand, then wound into a skein, and fabrics such as burlap are produced through a weaving machine.
그러나, 상기와 같은 종래 기술의 대마사 제조 방법은 다른 섬유와는 달리 대마 원료를 사람이 직접 수공정을 통해 섬유로 제작하기 때문에 대마사를 대량으로 생산하기 어렵고, 이 때문에 대마사의 가격이 다른 섬유에 비해 높아지는 문제점이 있다.However, the conventional hemp yarn manufacturing method of the prior art, unlike other fibers, hemp raw material is difficult to produce a large amount of hemp yarn because the man-made raw material is made of the fiber through a manual process, which is why the price of hemp yarn compared to other fibers There is a problem that increases.
또한, 종래 기술의 대마사 제조 방법은 사람이 직접 대마사를 세분화시키고 길게 연결하여 제조하기 때문에 섬유 조직이 곱지 못하여 고급 섬유로 사용하는 데는 한계가 있고, 직조 기계를 이용하여 조직이 치밀한 천류로 제작하는 데도 어려운 문제점이 있어 폭넓게 일반화되지 못한 실정이다.In addition, the prior art hemp yarn manufacturing method has a limitation in using it as a high-grade fiber because the fiber tissue is not multiply because the person directly subdivided and manufactured long hemp yarn, it is also used to produce a dense stream of tissue using a weaving machine It is a difficult problem that has not been widely generalized.
본 발명은 상기한 문제점을 해결하기 위하여 안출된 것으로서, 기계 자동화 공정을 통해 조직이 곱고 치밀한 대마사를 방적함으로써 마섬유의 대량 생산이 가능해지고 삼베 등의 천도 용이하게 직조할 수 있도록 하는 대마사 제조 방법을 제공하는 데 있다.The present invention has been made in order to solve the above problems, by the machine automation process by spinning the fine and dense hemp tissue, mass production of hemp fiber is possible, and can also easily weave fabric such as hemp fabric To provide.
상기한 과제를 실현하기 위한 본 발명의 대마사 제조 방법은, 대마 원료를 일정한 길이로 절단하여 염산 및 식물성 액이 섞인 물통에 넣고 일정 시간 정도 담궈둔 후, 고온으로 삶으면서 대마 원료의 겉피와 속피 사이의 결합력을 약화시키는 제1 과정과; 상기 겉피와 속피가 약화된 대마 원료를 타마기에 넣고 두들겨 겉피를 벗겨낸 후, 속피를 일정 기간 물속에 담궈서 염산 및 식물성 액을 희석시키는 제2 과정과; 상기 속피에 함유된 수분을 탈수하고, 식물성 유연제를 소량 뿌린 상태에서 완전 건조하는 제3 과정과; 상기에서 건조된 속피를 다시 타마기에 넣고 두들겨 딱딱한 성질이 약화시키는 제4 과정과; 상기 속피를 그늘진 양생 창고에서 식물성 유연제를 뿌리면서 적층시킨 다음, 일정 기간 자연 양생시키면서 부풀어지게 만드는 제5 과정과; 상기 과정에서 부풀어진 속피를 섬유질대로 가늘게 세분화시켜 장섬유와 단섬유로 분리시키는 제6 과정과; 상기 장섬유와 단섬유를 각각 부드러운 반솜 상태로 만든 다음 대마사를 방적하는 제7 과정으로 이루어진 것을 특징으로 하여 가능하게 된다.According to the method for producing hemp yarn of the present invention for realizing the above-mentioned problem, the hemp raw material is cut into a predetermined length, placed in a bucket of hydrochloric acid and a vegetable liquid, soaked for a predetermined time, and then boiled at a high temperature between the skin and the skin of the hemp raw material. A first step of weakening the binding force of the; A second step of dipping hydrochloric acid and a vegetable liquid by putting the hemp weakened hemp raw material into a tamper and peeling the outer skin to immerse the inner skin in water for a predetermined time; A third step of dehydrating water contained in the cuticle and completely drying in a state of spraying a small amount of a vegetable softener; A fourth step of putting the dried epithelium in the tamper again and knocking to weaken the hard property; A fifth process of laminating the inner skin while sprinkling the vegetable softener in a shaded curing warehouse and swelling while spontaneously curing for a certain period of time; A sixth process of dividing the inflated epidermis into thin fibers into fibers to separate the long fibers and the short fibers; Each of the long fibers and short fibers is made into a smooth half state, and then characterized in that it consists of a seventh process of spinning the hemp.
도 1은 본 발명에 따른 대마 가공 순서가 도시된 참고도이고,1 is a reference diagram showing the hemp processing sequence according to the present invention,
〈도면의 주요 부분에 대한 부호의 설명〉<Explanation of symbols for main parts of drawing>
10 : 대마 원료 11 : 겉피10: hemp raw material 11: shell
13 : 펙틴질 15, 15' : 속피13: pectin 15, 15 ': inner skin
17 : 대마 섬유 19 : 대마사17: hemp fiber 19: hemp yarn
이하, 첨부된 도면을 참조하여 본 발명의 실시 예를 설명하면 다음과 같다.Hereinafter, exemplary embodiments of the present invention will be described with reference to the accompanying drawings.
도 1은 본 발명에 의한 대마사 제조 방법이 도시된 참고도이다.1 is a reference diagram showing a method for producing hemp yarn according to the present invention.
본 발명에 따른 대마사 제조 방법을 도 1을 참고하면, 크게 대마 원료(10)를 가공하여 겉피(11)와 속피(15)를 분리하는 제1 공정과, 상기 단계에서 분리된 속피(15)를 이용하여 대마 섬유(17)를 가공하는 제2 공정과, 상기 단계에서 만들어진 대마 섬유(17)를 방적하여 소정 굵기의 대마사(19)를 뽑는 제3 공정으로 이루어진다.Referring to Figure 1 of the hemp yarn manufacturing method according to the present invention, the first step of separating the outer skin 11 and the outer skin 15 by processing the hemp raw material 10 large, and the outer skin 15 separated in the step It consists of a 2nd process of processing the hemp fiber 17 using this, and the 3rd process of spinning the hemp fiber 17 produced in the said step, and pulling out the hemp yarn 19 of predetermined thickness.
상기 제1 공정은 대마 원료(10)에서 겉피(11)를 분리시키는 과정으로서, 먼저 대마를 일정한 길이로 절단하여 정리하여 대마 원료(10)를 만든다.The first process is a process of separating the sheath 11 from the hemp raw material 10, first cutting the hemp into a certain length to arrange the hemp raw material 10.
다음, 상기 대마 원료(10)를 염산 및 식물성 액이 섞인 물통에 넣고 32시간 정도 담궈둔 후, 100℃ 정도의 고온으로 2시간 정도 삶는다.Next, the hemp raw material 10 is placed in a bucket of mixed hydrochloric acid and vegetable solution, soaked for about 32 hours, and boiled at a high temperature of about 100 ° C. for about 2 hours.
여기서, 상기 염산과 식물성 액은 전체 수용액에 대비하여 각각 0.5% 정도 섞으면 된다. 그리고, 상기 식물성 액은 마늘과 양파를 썩여 만든 부패 액으로서, 여기에서 발생된 미생물이 대마 원료(10)에 들어 있는 겉피(11)와 속피(15) 사이의 유조직인 펙틴질(13)을 약화시키게 된다.Here, the hydrochloric acid and the vegetable liquid may be mixed about 0.5% of the total aqueous solution. In addition, the vegetable liquid is a decaying liquid made by decaying garlic and onion, and the microorganisms generated therein weaken the pectin 13, which is an oily tissue between the outer skin 11 and the inner skin 15 contained in the hemp raw material 10. do.
즉, 상기와 같이 염산과 식물성 액이 섞인 물에 32시간 정도 담근 후, 고온으로 삶게 되면 대마 원료(10)의 겉피(11)와 속피(15) 사이에 있는 펙틴질(13)이 약화되어 겉피(11)가 속피(15)로부터 쉽게 분리될 수 있게 된다.That is, after soaking in water mixed with hydrochloric acid and a vegetable solution for about 32 hours as described above, when boiled at a high temperature, the pectin 13 between the outer skin 11 and the outer skin 15 of the hemp raw material 10 is weakened and the outer skin ( 11 can be easily separated from the skin 15.
그리고, 고온으로 삶을 때는 물통 안에 들어 있는 대마 원료(10)를 회전시키면서 삶는 것이 바람직하다.In addition, when boiled at a high temperature, it is preferable to boil while rotating the hemp raw material 10 contained in the bucket.
다음, 상기 물통 안에서 삶은 대마 원료(50)를 타마기에 통과시키면서 두들겨 대마 원료(10)를 겉피(11)와 속피(13)로 분리시킨다.Next, the hemp raw material (10) is beaten while being passed through the tamper to separate the hemp raw material (10) into the outer skin (11) and the outer skin (13).
여기서, 상기 타마기는 일정 길이의 컨베이어 위에 대마 원료(10)가 이동할 수 있게 되어 있고, 상기 컨베이어를 통과하는 대마 원료(10)를 대마 기계를 통해 두들기면서 대마 원료의 겉피(11)를 벗겨 낸다.In this case, the hemp material is capable of moving the hemp raw material 10 on a conveyor of a predetermined length, while peeling the outer skin 11 of the hemp raw material while knocking the hemp raw material 10 passing through the conveyor through a hemp machine.
이와 같이 하여 벗겨진 겉피(11)는 컨베이어 하측으로 떨어지고, 섬유질인 속피(15)는 컨베이어를 타고 계속 이동하면서 겉피(11)와 완전히 분리된다.The outer skin 11 peeled off in this way falls on the lower side of the conveyor, and the fibrous skin 15 is completely separated from the outer skin 11 while continuously moving on the conveyor.
다음, 상기 과정을 통해 분리된 속피(15)는 그 내부에 염산 및 식물성 기름이 어느 정도 함유되어 있으므로 이틀 정도 물속에 담궈서 염산 및 식물성 액을 희석시킨다.Next, the epidermis 15 separated through the above process contains hydrochloric acid and vegetable oil to some extent, so that the hydrochloric acid and the vegetable liquid are diluted by dipping in water for two days.
다음, 상기 과정에서 어느 정도 염산 및 식물성 액이 어느 정도 희석된 속피(15)를 건져낸 다음, 탈수기로 속피에 함유된 수분을 제거한다.Next, in the above process, to some extent the hydrochloric acid and the vegetable liquid to some extent dilute the epithelium 15, and then remove the water contained in the epidermis with a dehydrator.
그리고, 상기와 같이 어느 정도 수분이 제거된 속피(15)를 정리한 다음, 섬유의 성질을 유연하게 만드는 식물성 유연제를 소량 뿌려 준 후, 속피(15)에서 수분이 완전히 제거될 수 있도록 건조시킨다. 이와 같이 하여 속피(15)가 건조되면 딱딱한 상태로 된다.Then, after cleaning the epidermis 15 to which the moisture is removed to some extent as described above, after spraying a small amount of a vegetable softener to soften the properties of the fiber, it is dried so that the moisture can be completely removed from the epidermis 15. In this way, when the outer skin 15 is dried, it will be in a hard state.
상기한 바와 같이 대마 원료(10)에서 속피(15)를 추출하여 가공한 제1 공정이 끝나면 속피(15)를 가공하여 섬유(17)로 만드는 제2 공정의 가공을 실시한다.As described above, after the first step of extracting and processing the epidermis 15 from the hemp raw material 10 is finished, the epidermis 15 is processed to process the second process of making the fiber 17.
이와 같은 제2 공정은 먼저, 상기 과정에서 딱딱하게 건조된 속피(15)를 다시 타마기에 넣고 딱딱한 성질이 약화되도록 유연하게 가공한다.This second process, first, put the hard dried skin 15 in the above process to the back to the tamma and flexible processing so that the hard properties are weakened.
다음, 상기 과정을 통해 어느 정도 유연해진 속피(15)를 그늘진 양생 창고에서 식물성 유연제를 뿌리면서 쌓는 것과 같이 차례로 적층시킨 다음, 3-4일간 자연 양생시키면서 부풀어지게 만든다.Next, the skin 15, which has become somewhat flexible through the above process, is laminated in turn, such as being stacked while spraying a vegetable softener in a shaded curing warehouse, and then inflated while natural curing for 3-4 days.
이와 같은 속피(15')는 어느 정도 부패되면서 부풀어지게 되고, 속피(15')의 성질은 부드럽게 변화되면서 건조된다.The epidermis 15 'is swollen to some extent and swells, and the nature of the epidermis 15' is gently changed and dried.
다음, 상기와 같이 양생되어 부드러워진 속피(15')를 일정한 길이로 잘라서 정리하고, 이렇게 정리된 속피(15')를 섬유질대로 가늘게 나눈다. 즉, 약 20cm정도의 길이로 잘라진 속피(15')를 섬유 세분화기를 통해 속피를 짓이기듯 섬유질대로 세분화시켜 하나의 속피에서 적어도 100여 가닥 정도 나오도록 부풀리면서 자른다.Next, the cured and softened epidermis 15 'is cut into a predetermined length and arranged as described above, and the thus-prepared epithelium 15' is finely divided into fibers. In other words, the cuticle (15 ') cut to about 20cm in length is broken down into fibrous fibers such that the cuticle is cut through a fiber granulator and swelled at least 100 strands from one cuticle.
다음, 상기와 같이 세분화된 섬유질피(17)를 섬유 분리기에 넣고 장섬유와 단섬유로 구분하여 감는다. 즉, 섬유 분리기에 넣고 세분화된 섬유질피를 흔들면서 이동시키게 되면 상대적으로 길이가 짧은 단섬유는 하측으로 빠지게 되고, 상대적으로 길이가 긴 장섬유는 그대로 남게 되어 장섬유와 단섬유가 상호 분리되고, 이와 같이 분리된 장섬유와 단섬유를 각각 타래로 감는다.Next, put the fibrous skin (17) broken down as described above into a fiber separator and wound into long fibers and short fibers. That is, when the fine fiber is placed in a fiber separator and moved while shaking the granular fibrous skin, the short fibers are shortened to the lower side, and the long fibers are kept relatively long so that the long fibers and the short fibers are separated from each other. The long fibers and the short fibers separated in this way are wound with a skein.
여기서, 상기 장섬유는 섬유 조직이 고운 고급으로 사용되고, 단섬유는 섬유 조직이 떨어지는 보통 섬유로 이용된다.Here, the long fiber is used as a fine fiber fine fiber, the short fiber is used as a normal fiber inferior fiber tissue.
상기한 바와 같이 하여 일정 길이를 갖는 대마 섬유(17)가 만들어지는 제2 공정이 끝나면 대마 섬유(17)를 방적 가공하여 소정 굵기와 강도를 가진 대마사(19)를 뽑아내는 제3 공정을 실시한다.As described above, when the second step of making the hemp fiber 17 having a predetermined length is completed, the third step of spinning the hemp fiber 17 to extract the hemp yarn 19 having a predetermined thickness and strength is performed. .
이와 같은 제3 공정은 통상의 실을 뽑아내는 방적공정으로서, 상기 공정에서 타래로 감은 장섬유와 단섬유를 각각 얇게 퍼진 반솜 상태로 만든 다음, 장섬유는 장섬유대로 단섬유는 단섬유대로 방적 기계를 이용하여 일정 굵기의 대마사(19)를 뽑아내고, 한 타래씩 감게 되면 대마사(19)를 제조하는 공정은 끝나게 된다.The third process is a spinning process for drawing a normal thread, and the long-fiber and short-fibers wound in the process are made into thinly spread half-cotton, and then the long fibers are spun as the short fibers and the short fibers are spun as the short fibers. Using a machine to pull out the hemp hemp (19) of a certain thickness, once wound by the end, the process of manufacturing the hemp hemp (19) is finished.
물론, 상기 방적 기계를 통해 뽑은 대마사를 정방 공정을 통해 재 가공하면서 보다 곱고 질긴 대마사를 제조할 수도 있다.Of course, it is also possible to produce a finer and tougher hemp while reprocessing the hemp extracted through the spinning machine through a spinning process.
또한, 상기와 같이 제3 공정에서 장섬유와 단섬유를 반솜 상태로 만든 다음, 다른 섬유의 반솜을 혼합하여 대마와 다른 섬유가 혼방된 혼방사를 제작할 수도 있을 것이다.In addition, in the third process as described above, the long fibers and short fibers may be made into half cotton state, and then mixed with half fibers of other fibers to prepare a blended yarn in which hemp and other fibers are mixed.
상기와 같은 공정을 통해 제작된 대마사(19)는 통상의 섬유와 같이 조직이 치밀하고 굵기가 일정하며 강도도 크기 때문에 필요에 따라 일반적으로 진행되는 직조 공정을 통해 고급 삼베는 물론 혼방사로 된 천 등도 용이하게 제작할 수 있게 된다.The hemp yarn 19 produced through the process described above is made of high-grade burlap as well as blended yarn through a weaving process that generally proceeds as needed because the tissue is dense, constant in thickness, and high in strength, such as conventional fibers. It can be manufactured easily.
따라서, 상기와 같이 구성되고 작용되는 본 발명의 대마사 제조 방법은 수공정에 의하지 않고 일반 섬유와 같이 기계자동화 공정으로 대마사 제작이 가능해짐으로써 삼베 섬유 제작이 용이해짐은 물론 대마사의 대량 생산을 가능하게 하는 이점을 제공하게 된다.Therefore, the hemp yarn manufacturing method of the present invention configured and operated as described above can be made by hemp yarn production by a mechanical automation process like general fibers without using a hand process, and facilitates the production of hemp fiber as well as mass production of hemp yarn. This provides an advantage.
또한, 본 발명은 가늘고 질긴 대마 섬유를 제작할 수 있으므로 다른 섬유와 섞어 혼방사로 제작할 수 있고, 조직이 보다 치밀한 천을 제작할 수 있게 되어 의류용을 포함한 모든 천의 제작에 용이하게 적용할 수 있는 이점을 제공하게 된다.In addition, the present invention can produce a thin and tough hemp fiber can be mixed with other fibers to produce a blended yarn, the tissue can produce a more dense fabric provides an advantage that can be easily applied to the production of all fabrics, including clothing use Done.
Claims (1)