KR100255271B1 - 폴리이미드 담지 전이금속착체 에폭시화 촉매 및 그를 이용한 에폭시화합물의 제조방법 - Google Patents
폴리이미드 담지 전이금속착체 에폭시화 촉매 및 그를 이용한 에폭시화합물의 제조방법 Download PDFInfo
- Publication number
- KR100255271B1 KR100255271B1 KR1019970067965A KR19970067965A KR100255271B1 KR 100255271 B1 KR100255271 B1 KR 100255271B1 KR 1019970067965 A KR1019970067965 A KR 1019970067965A KR 19970067965 A KR19970067965 A KR 19970067965A KR 100255271 B1 KR100255271 B1 KR 100255271B1
- Authority
- KR
- South Korea
- Prior art keywords
- polyimide
- catalyst
- peroxide
- olefin
- group
- Prior art date
Abstract
본 발명은 올레핀 에폭시화 반응을 위한 폴리이미드 수지입자 담지 전이 금속착체 불균일 촉매 및 그를 이용한 에폭시화합물의 제조방법에 관한 것이다. 좀 더 구체적으로, 본 발명은 디안하이드리드(dianhydride)와 디아민(diamine)의 현탁 축합중합에 의하여 내열성 및 내산화성이 있는 폴리이미드 수지입자를 합성한 후, 전기 폴리이미드 담체에 몰리브덴, 바나듐, 텅스텐 또는 티타늄의 균일 촉매를 결합시켜 제조한, 폴리이미드 담지 전이금속착체 불균일 촉매 및 그를 이용한 올레핀 에폭시화합물의 제조방법에 관한 것이다. 본 발명의 폴리이미드 담지 전이금속착체 불균일 촉매는 용이하면서도 경제적으로 제조될 뿐만 아니라, 고급 올레핀의 에폭시화 반응에서도 우수한 촉매활성, 선택성 및 촉매안정성을 나타낸다. 아울러, 본 발명의 불균일 촉매는 내열 및 내산화성이 강하고, 올레핀의 에폭시화 반응에 대한 선택성 및 에폭시화합물의 수율이 높다. 또한, 에폭시화 반응의 생성물로부터 불균일 촉매의 분리가 용이하고, 분리된 불균일 촉매의 재사용이 가능하다.
Description
본 발명은 올레핀 에폭시화 반응을 위한 폴리이미드 수지입자 담지 전이 금속착체 불균일 촉매 및 그를 이용한 에폭시화합물의 제조방법에 관한 것이다. 좀 더 구체적으로, 본 발명은 디안하이드리드(dianhydride)와 디아민(diamine)의 현탁 축합중합에 의하여 내열성 및 내산화성이 있는 폴리이미드 수지입자를 합성한 후, 전기 폴리이미드 담체에 몰리브덴, 바나듐, 텅스텐 또는 티타늄의 균일 촉매를 결합시켜 제조한, 폴리이미드 담지 전이금속착체 불균일 촉매 및 그를 이용한 올레핀 에폭시화합물의 제조방법에 관한 것이다.
올레핀 화합물의 에폭시화 반응은 널리 사용되고 있는 공정으로서, 그의 일예로는 균일 몰리브덴 촉매와 불균일 티타늄/실리카 촉매상에서 산소공급원으로 알킬 히드로퍼옥사이드를 이용하여 프로필렌을 프로필렌 옥사이드로 전환시키는 엑폭시화 반응이 있다.
쉐링톤(Sherrington)과 심프슨(Simpson)은 폴리스티렌 계통의 킬레이트 수지에 몰리브덴과 바나듐 금속촉매를 담지시켜, 촉매활성, 촉매안정성 및 촉매활성화 효과 등에 대해서 연구하였다(참조: D.C. Sherrington and S. Simpson, Journal of Catalysis, 131: 115-126(1991)). 또한, 밀러(Miller) 및 쉐링톤(Sherrington)은 내열성 고분자인 폴리벤지미다졸에 담지된 몰리브덴 촉매를 이용한 시클로헥센의 에폭시화 반응에서, 전기 촉매의 활성, 안정성 및 활성화 효과 등을 연구하였다(참조: M. Miller and D.C. Sherrington, Journal of Catalysis, 152: 377-383(1995)).
두가지 문헌의 내용을 비교 검토하면, 폴리스티렌 계통의 고분자 담체보다는 내열성 고분자인 폴리벤지미다졸에 담지된 몰리브덴 촉매의 경우가 촉매 활성 및 촉매안정성 측면에서 우수하였다. 그러나, 이들은 모두 고급 올레핀의 에폭시화 반응에서 촉매안정성이 저하되는 문제점을 갖고 있었다.
아울러, USP5,420,313에는 내열성 고분자인 폴리벤지미다졸 수지입자에 결합된 몰리브덴 촉매상에서의 올레핀 에폭시화 반응이 개시되어 있다. 그 특허에 의하면, 상업적 공정인 프로필렌으로부터 프로필렌 옥사이드를 제조하는 공정에서 촉매활성과 선택성이 뛰어났으며, 반복사용시에도 촉매의 침출(leaching)이 없이 촉매활성이 지속된다고 하였다. 그러나, 고급 올레핀인 시클로헥센의 에폭시화 반응에서는 반복사용하였을 때, 촉매활성이 점진적으로 감소하는 경향을 나타내었다. 그리고, 촉매담체로 사용된 폴리벤지미다졸 수지입자는 200℃ 이상의 고온에서 용융공정에 의하여 제조되는데, 그의 제조방법이 매우 까다로울 뿐만 아니라, 그를 제조하기 위한 단량체도 매우 고가이라는 단점이 있었다.
따라서, 저가의 단량체를 사용하여 용이하게 내열성의 고분자 담체를 제조하며, 나아가 그 담체와 금속촉매의 결합시, 고급 올레핀의 에폭시화 반응에서도 촉매활성과 선택성이 높고, 반복사용시에도 촉매활성이 계속 유지될 수 있는 불균일 에폭시화 촉매를 개발할 필요성이 당업계에서 절실히 대두되었다.
이에, 본 발명자들은 전술한 당업계의 요구에 부응하는 에폭시화 촉매를 개발하고자 예의 연구노력한 결과, 디안하이드리드(dianhydride)와 디아민(diamine)의 현탁 축합중합에 의하여 내열성 및 내산화성이 있는 폴리이미드 수지입자를 용이하면서도 경제적으로 합성한 다음, 그 폴리이미드 담체에 몰리브덴, 바나듐, 텅스텐 또는 티타늄의 균일 촉매를 담지시켜 제조한 불균일 에폭시화 금속촉매가 과산화물과 고급 올레핀의 에폭시화 반응에서 우수한 촉매 활성, 선택성 및 촉매안정성을 나타냄을 확인하고, 본 발명을 완성하게 되었다.
결국, 본 발명의 첫번째 목적은 올레핀 에폭시화 반응을 위한, 폴리이미드 수지입자 담지 전이금속착체 불균일 촉매를 제공하는 것이다.
본 발명의 두번째 목적은 전기 불균일 촉매를 이용한 올레핀 에폭시화합물의 제조방법을 제공하는 것이다.
제1도는 본 발명에서 합성한 폴리이미드 구형입자와 폴리이미드 구형입자에 담지된 몰리브덴 촉매의 열중량 분석 결과를 나타내는 그래프이다.
제2도는 본 발명에서 합성한 폴리이미드 구형입자와 폴리이미드 구형입자에 담지된 몰리브덴 촉매의 퓨리에 변환 적외선 스펙트럼을 나타낸다.
이하, 본 발명을 보다 구체적으로 설명하고자 한다.
먼저, 본 발명의 폴리이미드 수지입자는 디안하이드리드(dianhydride)와 디아민(diamine)의 축합중합에 의해 제조한다. 공정에서의 취급을 용이하게 하기 위해 구형입자 형태로 제조한다. 그 예로서, 피로멜리틱 디안하이드리드(pyromellitic dianhydride)와 1,4-페닐렌디아민(1,4-phenylenediamine)에 의해 제조된 폴리이미드 수지입자가 있으며, 하기의 화학식(I)으로 표현된다.
전기 폴리이미드 수지입자는 실질적으로 금속성분을 화학적으로 결합할 수 있는 기능기가 없으나, 중합과정에서 완전하게 이미드고리가 형성되지 않아 금속성분을 화학적으로 결합할 수 있는 것으로 밝혀졌다. 또한, 금속성분을 화학적으로 결합할 수 있는 트리아졸기, 카르복실기, 술폰기, 피리딘기 또는 히드록실기 등의 기능기를 포함하는 디아민을 사용하여 하기의 화학식(II)로 표현되는 기능성 폴리이미드 수지입자를 제조한다.
본 발명에 사용되는 디아민으로는 1,4-페닐렌디아민(1,4-phenylenediamine), 3,5-디아미노-1,2,4-트리아졸(3,5-diamino-1,2,4-triazole), 3,5-디아미노벤젠술폰산(3,5-diaminobenzenesulfonic acid), 3,5-디아미노벤조산(3,5-diaminobenzoic acid), 2,6-디아미노피리딘(2,6-diaminopyridine), 1,3-디아미노-2-히드록시프로판(1,3-diamino-2-hydroxypropane), 디아미노말레오니트릴(diaminomaleonitrile), 2,6-디아미노안트라퀴논(2,6-diaminoanthraquinone), 3,3′-디아미노-4,4′-디히드록시비페닐(3,3′-diamino-4,4′-dihydroxybiphenyl) 등 아민기가 둘 이상인 것은 모두 가능하다.
본 발명에 사용되는 디안하이드리드로는 1,2,4,5-벤젠테트라카르복실릭 디안하이드리드(1,2,4,5-benzene tetracarboxylic dianhydride), 3,3′,4,4′-벤조페논테트라카르복실릭 디안하이드리드(3,3′,4,4′-benzophenonetetracarboxylic dianhydride) 등 안하이드리드기가 둘 이상인 것은 모두 가능하다.
상기와 같이 제조된 폴리이미드 수지입자와, 몰리브덴, 바나듐, 텡스텐 또는 티타늄 등의 균일 유기금속착체, 가장 바람직하게는 몰리브덴과 반응시켜, 금속촉매와 폴리이미드의 기능기와의 화학적 결합에 의하여 제조되는 폴리 이미드 담지 불균일 촉매를 제조한다. 이때, 금속촉매 조성은 항상 한 성분일 필요는 없고, 두 가지 성분이 동시에 폴리이미드에 담지되어 사용될 수도 있다.
폴리이미드 담지 불균일 촉매 조성에서, 리간드 함량은 0.1mmol/g에서 4mmol/g까지 가능하며, 0.25mmol/g에서 2.5 mmol/g까지의 리간드 함량이 바람직하다. 또한, 담지촉매 조성에서 금속의 함량은 0.1mmol/g에서 5mmol/g까지 가능하며, 0.1mmol/g에서 2mmol/g까지의 촉매함량이 바람직하다. 그리고, 리간드와 금속의 몰비는 1:1에서 15:1의 범위이며, 1:1에서 10:1의 범위가 바람직하다.
아울러, 본 발명에서 폴리이미드 담지 불균일 촉매는 올레핀 에폭시화 반응의 촉매로 사용하기 전에 적절한 과산물화로 활성화될 수 있다. 또한, 그 촉매는 올레핀 에폭시화 반응에서의 반응물인 과산화물에 의해 에폭시화 반응 중에 활성화될 수도 있다.
이상과 같은 본 발명의 폴리이미드 담지 불균일 촉매는 과산화물과 올레핀 화합물을 1:0.5에서 1:100의 몰비에서, 바람직하게는 1:1에서 1:50의 몰비에서 반응시켜, 올레핀 에폭시화합물을 제조한다. 이때, 촉매와 과산화물의 몰비는 0.00001:1에서 1:1까지 사용될 수 있으며, 0.002:1에서 0.03:1이 바람직하다.
본 발명에서 사용되는 올레핀 화합물은 적어도 하나의 이중결합을 갖는 유기 올레핀 화합물이다. 이 올레핀 화합물은 직선형, 곁사슬형 또는 고리형 화합물일 수 있다. 또한, 이 올레핀 화합물은 아크릴, 고리가 하나, 둘 또는 그 이상일 수도 있다. 이중 결합이 하나 이상일 경우, 그 올레핀 화합물은 콘쥬게이트 될 수도 있고, 콘쥬게이트가 아닐 수도 있다. 이 올레핀 화합물은 치환기로 알릴 히드록시, 알릴클로린, 알릴 에테르 또는 에스테르기를 가질 수 있다. 이 올레핀 화합물은 비닐 에스테르, 페닐 또는 니트릴 화합물이어도 된다. 예를 들어, 니트릴과 같은 전자를 끌어당기는 기로 치환되어 있으면, 이러한 기들은 이중결합에 직접 치환되어 있으면 안되고, 이중결합으로부터 멀리 떨어져 있어야 된다. 아마 전자주게 그룹들이 치환되어 있는 것이 바람직하다. 이러한 올레핀 화합물에 대한 일반식(III)은 다음과 같다:
상기에서, R 및 R′는 동일하거나 상이하며, 탄소수 30이하인 경우가 바람직하다. R과 R′가 고리형 화합물일 경우는 탄소수 10이하인 경우가 바람직하다. R과 R′ 중 하나 혹은 양쪽 모두 알릴 히드록시, 클로린, 에테르 또는 에스테르 치환기를 가질 수 있다. 또한, R과 R′ 중 하나 혹은 양쪽 모두 비닐 에스테르, 니트릴 또는 페닐 치환기를 가질 수 있다.
바람직한 올레핀 화합물은 에틸렌, 프로필렌, 부텐 중 하나 혹은 그 이상일 수 있으며, 예를 들면 1-부텐, 시스 또는 트랜스 2-부텐, 펜텐, 헥센, 옥텐, 데켄, 시클로헥센, 4-비닐-시클로헥센, 불포화 글리세린 에스테르, 알릴클로라이드, 스티렌, 메틸렌 헥산, 시클로펜타디엔, 부타디엔 등이다. 이러한 올레핀들의 혼합물이 사용될 수도 있다. 이러한 올레핀은 소량의 불순물과 함께 사용될 수도 있는데, 이 불순물로는 알칸, 방향족 화합물, 알콜류, 에테르, 산 등이며, 이 불순물들은 반응에 활성이 없어야 한다.
아울러, 본 발명에서 사용될 수 있는 과산화물로는 과산화수소, 알킬 히드로퍼옥사이드와 같은 유기 과산화물, 과산화 에테르 또는 산 등이다. 이중에서, 3차-부틸히드로퍼옥사이드(tert-butyl hydroperoxide), 큐멘 히드록퍼옥사이드(cumene hydroperoxide), 에틸벤젠 히드로퍼옥사이드(ethylbenzene hydroperoxide) 또는 과산화수소(hydrogen peroxide)가 바람직하다.
본 발명의 에폭시화 반응에서는 반응물 혼자만 사용할 수도 있고, 방향족, 지방족, 알콜, 알칸, 에스테르, 케톤 또한 1,2-디클로로에탄과 같은 염소화 용매 등이 용매로 사용될 수 있다. 물은 소량은 존재해도 괜찮으나, 없는 것이 가장 바람직하다.
또한, 본 발명의 에폭시화 공정은 상압 또는 고압에서도 수행될 수 있다. 만약, 올레핀 화합물이 상압에서 가스일 경우는 액상에서 반응을 수행하기에 알맞게 고압에서 반응을 수행하여야 한다. 일 예로서, 프로필렌의 에폭시화 공정시 압력을 100bar까지 올려야 한다. 질소, 헬륨, 공기 또는 알칸과 같은 불활성 기체들이 고압을 유지하기 위하여 사용될 수 있다.
본 발명의 에폭시화 공정은 사용된 반응물의 종류에 따라 적당한 온도에서 수행될 수 있다. 본 발명의 공정을 위해서는 20℃에서 500℃까지의 온도가 바람직하다. 본 발명에서 합성된 폴리이미드 수지입자에 결합된 몰리브덴 촉매인 경우는 400℃ 이상의 높은 온도까지도 매우 안정하다. 본 발명의 공정은 회분식 또는 연속식 공정이 사용될 수도 있으며, 연속식 공정이 더욱 효과적일 것이다.
이하, 실시예를 통하여 본 발명을 상세히 설명하고자 한다. 이들 실시예는 오로지 본 발명을 설명하기 위한 것으로, 이들 실시예에 의해 본 발명의 범위가 한정되지 않는다는 것은 본 발명이 속하는 분야에서 통상의 지식을 가진 자들에게 있어서 자명할 것이다.
[실시예 1]
[폴리이미드 수지입자의 제조]
본 발명에서 내열성 고분자 수지입자 담지촉매를 제조하기 위한 담체로 사용되는 폴리이미드 수지입자는 다음과 같이 합성하였다.
예로써 1,4-페닐렌디아민(PDA)과 피로멜리틱 디안하이드리드(PMDA)의 중합에 의하여, 기능기를 갖지 않는 폴리이미드 수지입자를 합성하였다. 먼저, 비양성자성 용매(aprotic solvent)에서 폴리아믹산(poly(amic acid))(PAA) 용액을 제조하였다.
250㎖ 3구 둥근 플라스크에 PDA(5.4g, 0.050mol)과 N,N′-디메틸아세트아미드(N,N′-dimethyl-acetamide)(DMAc) (66.08g)을 넣고, 기계적으로 교반시키면서 질소 분위기에서 PDA를 완전히 용해시켰다. 계속해서 PMDA(11.12g, 0.052mol)를 소량씩 천천히 가하였다. 이때 온도를 낮게 유지하기 위해서 냉각수조를 사용하였다. 이 용액은 맑게 변하면서 점도가 높아지는데, 계속해서 약 3시간 동안 교반한 후 질소분위기에서 보관하였다.
그런 다음, 현탁안정제를 포함하는 중합반응기에 파라핀 오일(500g)을 넣고, 질소분위기를 유지하면서 이미 제조한 PAA 용액(240.38g, DMAc 용매에 20% PAA)을 넣고 400rpm으로 교반시켰다. 이때, 현탁안정제로는 무수말레산과 1-옥타데켄 공중합체(poly(maleic anhydride-co-octadec-1-ene)(1:1)) 또는 ICI 고분자분산제(polymeric dispersant)를 사용하였다. 60℃에서 약 2시간 교반시킨 후, 탈수제인 무수초산(acetic anhydride)(35.73g, 0.35mol)와 피리딘(pyridine)(23.73g, 0.30mol)의 혼합물을 한시간에 걸쳐 소량씩 첨가하였다. 교반을 계속 유지하면서 24시간 동안 탈수반응시켜 폴리이미드를 합성하고, 80℃ 진공오븐에서 24시간 건조시켰다.
한편, 기능기를 갖는 폴리이미드 수지입자를 합성하기 위하여, 기능기를 포함하는 디아민을 사용하였으며, 본 실시예에서 사용된 디아민은 3,5-디아미노벤젠술폰산이었다 피로멜리틱 디안하이드리드와 3,5-디아미노벤젠술폰산의 중축합에 의해 상술한 방법으로 폴리이미드 수지입자를 제조하였으며, 이 수지입자는 거의 구형 입자에 가까운 형태를 가지고, 기능기로서 술폰기(-SO3H)를 포함하고 있다.
폴리이미드 수지입자의 내부 구조를 변화시켜 사용목적에 알맞은 내열성 고분자 담체를 제조하기 위하여, 적절한 가교제로 가교시켰다. 이러한 방법은 폴리스티렌 고분자 담체에서 널리 쓰이는 방법이다. 가교 폴리이미드 수지입자를 얻기 위해서는 디아민 대신에 아민기를 3개 이상 갖는 가교제를 원하는 양만큼 대체하여 위와 같은 방법으로 합성하였다. 사용한 가교제로는 상업적으로 얻을 수 있는 트리스(2-아미노에틸)아민(tris(2-aminoethyl)amino), 멜라민(melamine)과 직접 합성한 3,3′,5,5′-테트라아미노-벤조페논(3,3′,5,5′-tetraamino-benzophenone)이다.
[실시예 2]
[폴리이미드 수지입자 담지촉매의 제조]
폴리이미드 담지 전이금속촉매는 다음과 같은 방법으로 제조하였다. 기능기를 가진 폴리이미드 입자(PI-DAT)(2.0g)와 균일 금속착체인 몰리브데닐 아세틸아세토네이트(molybdenyl acetylacetonate)(MoO2(acac)2)(7.0g)를 50ml 둥근 플라스크에 넣고, 20ml 에탄올을 첨가하였다. 이 혼합물은 3일 동안 환류시켰다. 여과하여 고분자 담지 촉매입자를 분리하고 톨루엔으로 세척한 후, Soxhlet 장치를 이용해서 에탄올로 추출하여 80℃ 진공오븐에서 건조시켰다.
고분자에 담지된 촉매성분의 담지량 측정은 다음과 같은 방법으로 하였다. 고분자 담지 금속착체 0.02g을 정확하게 측정하여 실리카 도가니에 넣고 산화제로써 질산칼륨(KNO3)(1g)와 왕수 2ml를 첨가하였다. 같은 방법으로 금속착체없이 질산칼륨(1g)와 왕수 2ml로 된 공(blank)샘플 2개를 제조하였다. 이 도가니를 노(furnace)속에 넣고 온도를 천천히 420℃까지 올려 3∼4시간 방치하였다. 상온까지 식힌 후, 왕수 8ml를 첨가하여 도가니속의 잔유물을 완전히 용해시켰다. 이 용액을 50ml 용적 플라스크에 넣고 여기에 증류수를 첨가하여 50ml로 만들었다.
용액내에 있는 금속성분의 양은 원자흡수분광광도계와 유도 플라즈마 분광광도계를 이용하여 분석하였고, 금속분석을 위한 표준용액은 다음과 같이 제조하였다. Mo을 예로 들면, 표준용액은 상업용 1000ppm Mo을 하나의 공샘플과 희석시켜 50, 75, 100 그리고 200ppm 용액을 만들었고, 나머지는 공샘플로 사용하였다. 이 용액은 원자흡수분광광도게로 분석하였다. 유도 플라즈마 분광광도계로 분석할 경우, 표준용액은 10ppm을, 샘플은 10ppm 미만으로 만들어서 측정하였다. 위와 같은 방법으로 측정된 PI-DAT.Mo(트리아졸기를 포함하는 폴리이미드에 담지된 금속촉매)의 촉매 담지량은 0.86mmolMo/g이었다. 상술한 방법으로 제조된 다른 PI-DAT.Mo(카르복실기를 포함하는 폴리이미드에 담지된 금속촉매)의 촉매 담지량은 1.30mmolMo/g이었다. 이 담지 촉매들을 반응에 사용할 때는 같은 Mo 농도가 되도록 유지하였다.
이러한 담지촉매들은 사용하기에 앞서, 10ml의 톨루엔 속에 3차-부틸히드로퍼옥사이드(TBHP) 5mmol이 들어있는 용액에서 환류시켜 활성화시켰다. 활성화시키면 촉매색깔은 연한 노란색으로 바뀐다.
한편, 실시예 1에서 합성한 폴리이미드 구형입자와 본 실시예에서 합성한 폴리이미드 구형입자에 담지된 몰리브덴 촉매의 열중량 분석 결과는 제1도에 나타내었고, 그들 각각의 퓨리에 변환 적외선 스펙트럼은 제2도에 나타내었다. 제1도 및 제2도에서, PI는 폴리이미드 구형입자; PI.Mo는 기능기를 갖지 않는 폴리이미드 수지 입자에 Mo 촉매를 결합시킨 폴리이미드 수지입자 담지 Mo 촉매; PI-DAT는 기능기를 갖는 폴리이미드 수지 입자, PI-DAT.Mo는 기능기를 갖는 폴리이미드 수지 입자에 Mo 촉매를 결합시킨 폴리이미드 수지입자 담지 Mo촉매를 각각 나타낸다.
[시클로헥센의 에폭시화 반응]
우선, 에폭시화 반응에 사용된 과산화물은 톨루엔에 있는 무수 TBHP로서 다음과 같이 제조하였다. 70% TBHP 수용액 60㎖와 톨루엔 80㎖를 250㎖ 분액 깔대기에 넣고 1분 정도 천천히 흔들어 준 다음, 상분리가 일어나면 아래층인 물층을 분리하고, 상층은 트랩을 사용하여 다음과 같이 물을 제거하였다.
둥근 플라스크에 환류 냉각기를 장치하여 상층용액과 비등석을 넣고 환류시켰다. 한시간 후 4㎖의 물과 과량의 톨루엔이 증류되어 곁가지로부터 분리되었다. 건조튜브(drying tube)를 냉각기 위에 장착하였다. 한시간 후 2㎖의 물과 톨루엔이 분리되고, 나머지 한시간 동안 톨루엔만 증류되어 나왔다. 톨루엔 속의 TBHP는 5Å 분자체(molecular sieves)와 함께 플라스크에 넣어 냉장고에 보관하였다. 제조한 TBHP의 농도는 요오드화법으로 측정하였다.
시클로헥센의 에폭시화반응은 삼구 반응기를 사용하였으며, 반응온도를 정확하게 조절하기 위하여 항온순환수조를 사용하였다. 반응실험에 사용된 일반적인 과정은 다음과 같다. 질소분위기하에서, 폴리이미드 담지 금속촉매 0.08g, 시클로헥센 7.5㎖(74mmol), 그리고 GC의 내부표준물질로써 오르소-디클로로벤젠(o-dichlorobenzene) 0.5㎖를 교반기, 시료채취기 그리고 냉각기가 장착된 반응기에 넣고, 열적 평형에 도달하기 위해 반응 개시전 60℃에서 20분동안 교반시켰다. 이어, 상기에서 제조한 과산화물인 무수 TBHP(5mmol)/톨루엔 1.4∼1.5㎖을 첨가하여 반응을 시작하였다. 생성물의 농도는 일정한 시간에 시료를 채취하여 GC에 의해 분석하였다. 에폭시화반응에서 반응생성물의 가스크로마토그래프 분석조건은 다음과 같다.
가스크로마토그래프 : HP 5890II Plus
컬럼 : Ultra 2 (Crosslinked 5% Ph Me Silicone)
길이 : 25m
내경 : 0.22mm
필름 두께 : 0.52㎛
오븐온도 : 60℃(5분) → 120℃(30℃/분)
주입기(Injector) : 250℃
검출기(Detector) : 270℃ (FID)
캐리어가스(Carrier Gas) : 헬륨 1㎖/분
에폭사이드 수율은 첨가한 산소공급원인 TBHP가 완전히 반응하여 그에 해당하는 시클로헥센옥사이드(cyclohexene oxide)를 생성하였을 때를 100% 수율로 계산하였다.
반응 중에 폴리이미드 수지입자로부터 촉매가 떨어져나오는 양을 측정하였다. 반응이 종료된 후 촉매성분을 여과하여 철저히 세척하였다. 마찬가지로 반응기 내부도 철저히 세척하여, 용액을 모두 모아 회전식 증발기에 넣고 용매를 전부 날려보내면 엷은 노란색의 잔유물이 남는데, 이것을 약 48시간 동안 왕수에 용해시킨 후 증류수로 희석시켜 원자흡수분광광도계 또는 유도 플라즈마 분광광도계로 분석하였다.
[실시예 3]
트리아졸기를 포함하는 폴리이미드에 담지된 몰리브덴 촉매를 사용하여 80℃에서 시클로헥센의 에폭시화 반응을 실시예 2의 방법으로 수행하였을 때, 생성되는 시클로헥센옥사이드의 수율은 하기 표 1에 나타내었다. 에폭시화 반응 전에 10ml의 톨루엔 속에 3차-부틸히드로퍼옥사이드(TBHP) 5mmol이 들어있는 용액으로 담지촉매가 활성화되는 정도를 구분하여 실험하였다.
[실시예 4 내지 7]
실시예 3에서와 같은 반응조건에서, 트리아졸기를 포함하는 폴리이미드에 담지된 몰리브덴 촉매(PI-DAT.Mo)를 사용하여 10번 반복실험을 통해 촉매의 안정성을 조사하였다. 그리고 각각의 실험마다 고분자에서 떨어져나오는 금속성분의 양을 측정하였다. 반응이 끝나면 반응혼합물로부터 촉매성분을 여과하여 아세톤으로 세척한 후 건조시켜, 다음 실험에 계속 사용하였다.
반응에 사용하기 전에 미리 활성화시키지 않은 촉매에 대한 10번 반복실험 결과를 표 2에 나타내었으며, 사용하기 전에 12시간, 24시간, 48시간 활성화시켜 10번 반복실험한 결과를 표 3, 표 4 및 표 5에 각각 나타내었다.
[실시예 8]
미리 활성화시키지 않은 PI-DAT.Mo 촉매(트리아졸기를 포함하는 폴리이미드에 담지된 몰리브덴 촉매)를 사용하여 서로 다른 온도에서 시클로헥센의 에폭시화 반응을 수행하였으며, 그 결과를 하기 표 6에 나타내었다.
[실시예 9]
[트리아졸기를 포함하는 가교 폴리이미드 수지입자 담지 Mo 촉매의 제조]
디아민으로는 3,5-디아미노-1,2,4-트리아졸, 디안하이드리드로는 피로멜리틱 디안하이드리드(PMDA), 그리고 가교제로는 트리스(2-아미노에틸)아민을 사용하여, 트리아졸기를 포함하는 가교 폴리이미드 수지입자를 합성하였으며, 이 고분자 담체에 MoO2(acac)2를 담지시켜, 폴리이미드 담지 Mo촉매를 제조하였다.
즉, 1000㎖ 4구 실린더형 중합반응기에 3,5-디아미노-1,2,4-트리아졸(8.919g, 9 × 10-2mol)과 N,N′-디메틸아세트아미드(DMAc)(114.0)을 넣고, 기계적으로 교반시키면서 질소분위기에서 디아민을 완전히 용해시켰다. 계속해서 PMDA(22.4462g, 13.5 × 10-2mol)를 소량씩 천천히 가한 후, 상온에서 약 24시간동안 반응시켰다.
상기 중합반응기에 현탁안정제를 포함하는 파라핀 오일(450g)을 넣고, 60℃에서 약 2시간 교반시킨 후, 가교제인 트리스(2-아미노에틸)아민을 소량씩 첨가하여 다시 24시간 반응시켰다.
상기 현탁용액에 탈수제인 무수 아세트산(36.9g, 0.36mol)과 피리딘(24.93g, 0.32mol)의 혼합물을 한시간에 걸쳐 소량씩 첨가한 다음, 교반을 계속 유지하면서 24시간 동안 탈수반응시켜 가교 폴리이미드를 합성하였다. 폴리이미드 입자를 여과시켜 24시간 동안 디클로메탄으로 속슬렛(Soxhlet)에서 추출하였다. 그 다음 80℃ 진공오븐에서 24시간 건조시켰다.
폴리이미드 담지 전이금속촉매는 실시예 2와 같은 방법으로 제조하였는데, 촉매의 담지량은 0.92mmol/g이었다.
이와 같이 제조된, 트리아졸기를 포함하는 가교 폴리이미드 수지입자 담지 Mo 촉매를 사용하여, 반응온도가 70℃인 점을 제외하고는 실시예 4와 동일한 방법으로 에폭시화 반응시켰다.
[실시예 10]
실시예 1과 같은 방법으로 트리아졸기를 포함하는 폴리이미드 수지입자(PI(C=0)-DAT)를 합성하였으며, 여기에서 사용된 디안하이드리드는 3,3′,4,4′-벤조페논테트라카르복실릭 디안하이드리드이었다. 그리고, 이 폴리이미드 수지입자에 실시예 2와 같이 Mo 촉매를 담지하였으며, 담지량은 0.14mmol/g이었다. 실시예 4와 같은 방법으로 에폭시화 반응실험을 하였으나, 반응온도는 60℃이었다.
[실시예 11]
[시클로옥텐의 에폭시화 반응]
시클로헥센의 에폭시화 반응에 사용된 반응장치와 실험방법에 의하여, 시스-시클로옥텐의 에폭시화 반응을 수행하였다. 실험에 사용된 반응물의 조성은 다음과 같다.
시스-시클로옥텐 옥사이드 56.7 mmol
Mo 3.4 × 10-2mmol
3차-부틸 히드로퍼옥사이드 5 mmol
오르소-디클로벤젠 0.5 ml
톨루엔 0.62 ml
반응물의 전체 부피가 10ml가 되도록 용매인 톨루엔을 첨가하였으며, 반응온도는 80℃이었다. 그리고 실시예 4와 같이 10번 반복실험을 수행하였다.
[실시예 12]
[1-옥텐의 에폭시화 반응]
시클로헥센의 에폭시화 반응에 사용된 반응장치 및 실험방법에 의하여, 1-옥텐의 에폭시화 반응을 수행하였다. 실험에 사용된 반응물의 조성은 다음과 같다.
1-옥텐 48.7 mmol
Mo 3.4 × 10-2mmol
3차-부틸 히드로퍼옥사이드 5 mmol
오르소-디클로벤젠 0.5 ml
톨루엔 0.62 ml
반응물의 전체 부피가 10ml가 되도록 용매인 톨루엔을 첨가하였으며, 반응온도는 80℃이었다. 그리고 실시예 4와 같이 10번 반복실험을 수행하였다.
[실시예 13]
실시예 1에서 합성한, 기능기를 갖지 않는 폴리이미드 수지입자에 Mo 촉매를 결합시켜, 폴리이미드 수지입자 담지 Mo 촉매(PI. Mo)를 제조하였다. Mo 촉매의 담지량은 0.19 mmol/g이었으며, 이 PI. Mo 촉매를 이용하여 80℃에서 에폭시화 반응을 수행하였으며, 그 결과를 하기 표 11에 나타내었다. 에폭시화 반응 전에 10ml의 톨루엔 속에 3차-부틸히드로퍼옥사이드(TBHP) 5mmol이 들어있는 용액으로 담지촉매가 활성화되는 정도를 구분하여 실험하였다.
[실시예 14-17]
실시예 13에서와 같은 반응조건에서 PI. Mo 촉매를 사용하여 10번 반복실험을 통해 촉매의 안정성을 조사하였다. 반복실험은 실시예 4와 같이 수행하였다.
또한, 반응에 사용하기 전에 미리 활성화시키지 않은 촉매에 대한 10번 반복실험 결과를 하기 표 12에 나타내었으며, 사용하기에 앞서 12시간, 24시간, 48시간 활성화시킨 촉매의 10번 반복실험 결과를 하기 표 13, 표 14 및 표 15에 각각 나타내었다.
USP 5,420,313에서, 내열성 고분자인 폴리벤지미다졸에 담지된 Mo 촉매의 경우 시클로헥센의 에폭시화 반응에서 촉매의 활성화 시간이 길수록 촉매의 안정성이 증가한다고 보고하였다. 그러나, 본 발명에서 사용된 PI. Mo 촉매의 경우, 활성화시킨 촉매에 대해서는 활성화 시간이 길수록 촉매가 다소 안정하였으나, 여전히 활성화 시키지 않은 촉매가 가장 안정하였다.
[실시예 18 내지 20]
사용하기 전에 미리 활성화시키지 않은 PI. Mo 촉매를 사용하여 60℃와 70℃에서 반복실험을 수행하였으며, 그 결과를 표 16, 표 17 및 표 18에 나타내었다.
[실시예 21]
실시예 13에서 합성한 PI. Mo 촉매를 시클로헥센의 에폭시화 반응에 사용하였다. 이 실험에서는 산소공급원으로 3차-부틸히드로퍼옥사이드 대신에 큐멘 히드로퍼옥사이드를 사용하였다.
반응조건은 시클로헥센 74mmol, 큐멘 히드로퍼옥사이드 5mmol, 오르소-디클로로벤젠 0.5ml, Mo 1.52 × 10-2mmol이었다. 그리고, 톨루엔을 첨가하여 반응용액 전체 부피가 10ml가 되도록 하였다. 80℃에서 10번 반복실험하여 그 결과를 하기 표 19에 나타내었는데, 결과를 보면 시클로헥센 옥사이드에 대한 선택성이 매우 높을 뿐만 아니라 촉매의 안정성이 뛰어남을 알 수 있었다.
[실시예 22]
[시클로옥텐의 에폭시화 반응]
PI. Mo 촉매를 사용하여 실시예 11과 같이 시스-시클로헥센의 에폭시화 반응을 수행하였다. 실험에 사용된 반응물의 조성은 다음과 같다.
시스-시클로옥텐 57.6 mmol
Mo 1.52 × 10-2mmol
3차-부틸 히드로퍼옥사이드 5 mmol
오르소-디클로벤젠 0.5 ml
톨루엔 0.62 ml
반응물의 전체 부피가 10ml가 되도록 용매인 톨루엔을 첨가하였으며, 반응온도는 80℃이었다. 그리고 실시예 4와 같이 10번 반복실험을 수행하였다.
[실시예 23]
[스티렌의 에폭시화 반응]
PI. Mo 촉매를 사용하여 시클로헥센의 에폭시화 반응에 사용된 반응장치 및 실험방법에 의하여 스티렌의 에폭시화 반응을 수행하였다. 실험에 사용된 반응물의 조성은 다음과 같다.
스티렌 65.5 mmol
Mo 1.52 × 10-2mmol
3차-부틸 히드로퍼옥사이드 5 mmol
오르소-디클로벤젠 0.5 ml
톨루엔 0.62 ml
반응물의 전체 부피가 10ml가 되도록 용매인 톨루엔을 첨가하였으며, 반응온도는 80℃이었다. 그리고 실시예 4와 같이 10번 반복실험을 수행하였다.
[실시예 24]
[1-옥텐의 에폭시화 반응]
PI. Mo 촉매를 사용하여 시클로헥센의 에폭시화 반응에 사용된 반응장치 및 실험방법에 의하여 1-옥텐의 에폭시화 반응을 수행하였다. 실험에 사용된 반응물의 조성은 다음과 같다.
1-옥텐 47.8 mmol
Mo 1.52 × 10-2mmol
3차-부틸 히드로퍼옥사이드 5 mmol
오르소-디클로벤젠 0.5 ml
톨루엔 0.62 ml
반응물의 전체 부피가 10ml가 되도록 용매인 톨루엔을 첨가하였으며, 반응온도는 80℃이었다. 그리고 실시예 4와 같이 10번 반복실험을 수행하였다.
[실시예 25]
실시예 24와 같이 1-옥텐의 에폭시화 반응을 수행하였으나, 산소공급원으로 5mmol의 3차-부틸 히드로퍼옥사이드 대신에 5mmol의 큐멘 히드로퍼옥사이드를 사용하였다.
[비교실험]
균일 촉매인 MoO2(acac)2를 사용하고, 산소공급원으로 3차-부틸 히드로퍼옥사이드와 큐멘 히드로퍼옥사이드를 사용하여 실험한 결과를 표 24과 표 25에 각각 나타내었다.
[실시예 26]
실시예 1에서 합성한 기능기를 갖지 않는 폴리이미드 수지입자에 VO(acac)2촉매를 결합시켜, 폴리이미드 수지입자 담지 V 촉매(PI. V)를 제조하였다. V촉매의 담지량은 0.12mmol/g이었으며, 이 PI. V 촉매를 이용하여 80℃에서 시클로헥센의 에폭시화 반응에 관한 결과를 표 26에 나타내었다.
이상에서 상세히 설명하고 입증하였듯이, 본 발명의 폴리이미드 담지 전이금속착체 불균일 촉매는 용이하면서도 경제적으로 제조될 뿐만 아니라, 고급 올레핀의 에폭시화 반응에서도 우수한 촉매활성, 선택성 및 촉매안정성을 나타낸다. 아울러, 본 발명의 불균일 촉매는 내열 및 내산화성이 강하고, 올레핀의 에폭시화 반응에 대한 선택성 및 에폭시화합물의 수율이 높다. 또한, 에폭시화 반응의 생성물로부터 불균일 촉매의 분리가 용이하고, 분리된 불균일 촉매의 재사용이 가능하다.
Claims (7)
1,2,4,5-벤젠테트라카르복실릭디안하이드라이드 및 3,3′,4,4′-벤조페논테트라카르복실릭디안하이드라이드로 구성된 그룹으로부터 선택된 디안하이드라이드(dianhydride)와 1,4-페닐렌디아민, 3,5-디아미노-1,2,4-트리아졸, 3,5-디아미노벤젠술폰산, 3,5-디아미노벤조산, 2,6-디아미노피리딘, 1,3-디아미노-2-하이드록시프로판, 디아미노말레오니트릴, 2,6-디아미노안트라퀴논 및 3,3′-디아미노-4,4′-디하이드록시페닐으로 구성된 그룹으로부터 선택된 디아민(diamine)의 축합중합에 의해 제조되는 폴리이미드 담체에, 몰리브덴, 바나듐, 텅스텐 및 티타늄으로 구성된 그룹으로부터 선택된 1종 또는 그 이상의 전이금속을 담지시킨, 폴리이미드 함량이 0.1~4 mmol/g이고, 전이금속의 함량은 0.1~5 mmol/g이며, 폴리이미드와 금속의 몰비는 1:1 ~ 15:1인 것을 특징으로 하는 폴리이미드 담지 전이금속착체 불균일 촉매.
(i) 1,2,4,5-벤젠테트라카르복실릭디안하이드라이드 및 3,3′,4,4′-벤조페논테트라카르복실릭디안하이드라이드로 구성된 그룹으로부터 선택된 디안하이드라이드(dianhydride)와 1,4-페닐렌디아민, 3,5-디아미노-1,2,4-트리아졸, 3,5-디아미노벤젠술폰산, 3,5-디아미노벤조산, 2,6-디아미노피리딘, 1,3-디아미노-2-하이드록시프로판, 디아미노말레오니트릴, 2,6-디아미노안트라퀴논 및 3,3′-디아미노-4,4′-디하이드록시페닐으로 구성된 그룹으로부터 선택된 디아민(diamine)의 축합중합에 의해, 폴리이미드 함량이 0.1~4 mmol/g이고, 전이금속의 함량은 0.1~5 mmol/g이며, 폴리이미드와 금속의 몰비는 1:1 ~ 15:1인 것을 특징으로 하는 폴리이미드 담체를 수득하는 공정; (ii) 전기 폴리이미드 담체에, 몰리브덴, 바나듐, 텡스텐 및 티타늄으로 구성된 그룹으로부터 선택된 1종 또는 그 이상의 전이금속을 담지시켜, 폴리이미드 담지 전이금속착체 불균일 촉매를 수득하는 공정; 및, (iii) 전기 폴리이미드 담지 전이금속착체 불균일 촉매하에 과산화물과 올레핀 화합물을 1:0.5 내지 1:100의 몰비에서 반응시키는 공정(이때, 촉매와 과산화물의 몰비는 0.00001:1 내지 1:1이다)을 포함하는 올레핀 에폭시화합물의 제조방법.
제2항에 있어서, 올레핀 화합물은 에틸렌, 프로필렌, 부텐, 펜텐, 헥센, 옥텐, 데켄, 시클로헥센, 4-비닐-시클로헥센, 불포화 글리세린 에스테르, 알릴클로라이드, 알릴알콜, 스티렌, 메틸렌 시클로헥산, 시클로펜타디엔 및 부타디엔으로 구성된 그룹에서 선택된 1종 또는 그 이상의 화합물인 것을 특징으로 하는 올레핀 에폭시화합물의 제조방법.
제3항에 있어서, 올레핀 화합물은 프로필렌, 1-옥텐, 1-데켄, 시클로헥센, 스티렌, 4-비닐-시클로헥센 및 알릴 클로라이드로 구성된 그룹에서 선택된 1종 또는 그 이상의 화합물인 것을 특징으로 하는 올레핀 에폭시화합물의 제조방법.
제2항에 있어서, 과산화물은 과산화수소, 유기 과산화물, 과산화 에테르 및 과산으로 구성된 그룹에서 선택된 1종 또는 그 이상의 화합물인 것을 특징으로 하는 올레핀 에폭시화합물의 제조방법.
제5항에 있어서, 과산화물은 3차-부틸히드로퍼옥사이드(tert-butylhydroperoxide), 큐멘 히드록퍼옥사이드(cumene hydroperoxide), 에틸벤젠 히드로퍼옥사이드(ethylbenzene hydroperoxide) 및 과산화수소로 구성된 그룹에서 선택된 1종 또는 그 이상의 화합물인 것을 특징으로 하는 올레핀 에폭시화합물의 제조방법.
제2항에 있어서, 과산화물과 올레핀 화합물은 1:1 내지 1:50의 몰비가 되고, 촉매와 과산화물은 0.002:1 내지 0.03:1의 몰비가 되는 조건에서 반응시키는 것을 특징으로 하는 올레핀 에폭시화합물의 제조방법.