KR100214433B1 - Pvc floor materials and their manufacturing method - Google Patents
Pvc floor materials and their manufacturing method Download PDFInfo
- Publication number
- KR100214433B1 KR100214433B1 KR1019970038397A KR19970038397A KR100214433B1 KR 100214433 B1 KR100214433 B1 KR 100214433B1 KR 1019970038397 A KR1019970038397 A KR 1019970038397A KR 19970038397 A KR19970038397 A KR 19970038397A KR 100214433 B1 KR100214433 B1 KR 100214433B1
- Authority
- KR
- South Korea
- Prior art keywords
- pvc
- resin
- wood
- wood powder
- flooring
- Prior art date
Abstract
본 발명은 PVC 바닥장식재의 하지층의 경량화를 위하여 그 표면이 바인더로 코팅된 목분 칩(CHIP)과 PVC 스트레이트 수지, 공중합 수지, 페이스트 수지, 발포제, 가소제, 그리고 열안정제 등으로 제조된 PVC 콤파운드를 서로 혼합시킴으로써, 바닥장식재의 경량화 뿐만아니라 바닥의 습기를 예방하고 보온을 유지시키며, 천연 소재의 목분을 이용함으로써 천연 소재 자체의 자연향을 그대로 유지시킬 수 있는 PVC 바닥장식재용 목분 콤파운드 조성물과 그 제조방법, 그리고 이를 이용한 바닥장식재에 관한 것으로서, 표면이 바인더에 의해 코팅되는 목분 칩의 제조단계와 PVC 콤파운드 제조단계, 그리고 상기 목분 칩과 PVC 콤파운드를 혼합하는 단계로 이루어지는 것을 특징으로 한다.The present invention provides a PVC compound made of wood chip chip (CHIP) coated with a binder, PVC straight resin, copolymer resin, paste resin, foaming agent, plasticizer, and heat stabilizer to reduce the weight of the base layer of PVC flooring material. By mixing with each other, wood flooring compound composition for PVC flooring material and its manufacture that can keep the natural flavor of natural material itself by using wood powder of natural material as well as lightening floor decoration material, preventing moisture of floor and keeping warm. The method, and a flooring material using the same, characterized in that the surface is coated with a binder, the manufacturing step of the wood chip chip and PVC compound manufacturing step, and the step of mixing the wood chip chip and the PVC compound.
Description
본 발명은 PVC 바닥장식재용 목분 콤파운드에 관한 것으로, 특히 바닥장식재의 하지층의 경량화를 위하여 그 표면이 바인더로 코팅된 목분 칩(CHIP)과 PVC 스트레이트 수지, 공중합 수지, 페이스트 수지, 발포제, 가소제, 그리고 열안정제 등으로 제조된 PVC 콤파운드를 서로 혼합시킴으로써, 바닥장식재의 경량화 뿐만아니라 바닥의 습기를 예방하고 보온을 유지시키며, 천연 소재의 목분을 이용함으로써 천연 소재 자체의 자연향을 그대로 유지시킬 수 있는 PVC 바닥장식재용 목분 콤파운드 조성물과 그 제조방법, 그리고 이를 이용한 바닥장식재에 관한 것이다.The present invention relates to wood flour compound for PVC floor coverings, and in particular, in order to reduce the weight of the base layer of the floor covering material, wood chip chips (CHIP) coated with a binder, PVC straight resin, copolymer resin, paste resin, foaming agent, plasticizer, In addition, by mixing PVC compounds made of heat stabilizers with each other, not only reduce the weight of the flooring material, but also prevent moisture on the floor and maintain warmth, and by using wood powder from natural materials, the natural flavor of the natural material itself can be maintained as it is. It relates to wood flour compound composition for PVC floor coverings and a method of manufacturing the same, and floor decoration using the same.
일반적으로 PVC 바닥장식재는 바닥의 습기를 예방하고 보온을 유지시키며, 보행자의 보행촉감을 향상시키고 바닥의 장식미를 유발시키는 등 다양한 용도로 사용하고 있다.In general, PVC flooring materials are used for a variety of purposes, such as to prevent the moisture of the floor, to maintain warmth, to improve the pedestrian walking feeling and to induce the decoration of the floor.
이러한 용도로 사용되고 있는 PVC 바닥장식재는 일반적으로 상지층, 중지층, 그리고 하지층의 구조로 이루어지고 있는데, 생산비용을 절감시키고 장식재의 수축성을 보강시키기 위하여, 상술한 바닥장식재의 하지층에 다량의 탄석을 함유시켜 제조하고 있다.PVC flooring material used for this purpose is generally composed of the upper layer, middle layer, and base layer structure, in order to reduce the production cost and reinforce the shrinkage of the decorative material, a large amount of the floor layer of the above-mentioned flooring material It is produced by containing coal stone.
이와 같이 다량의 탄석이 함유되어 있는 종래의 바닥장식재의 하지층은 바닥장식재의 생산비용을 절감시키고 수축성을 보강시키는데는 나름대로의 장점을 가지고 있으나, 바닥장식재의 중량을 증가시키는 원인이 되고 있다. 이러한 바닥장식재의 과다한 중량은 바닥장식재의 시공 시에 그 운송 내지 운반을 용이하지 않게하여 시공자들이 기피하는 원인이 되고 있다.As such, the base layer of the conventional floor decoration material containing a large amount of coal has its advantages in reducing the production cost of the floor decoration material and reinforcing shrinkage, but is causing the weight of the floor decoration material. Excessive weight of such a flooring material is not easy to transport or transport during the construction of the flooring material is causing the builders to avoid.
이러한 문제점을 해결하기 위하여 다양한 바닥장식재의 대체소재의 개발이 진행되어 왔으며, 특히 그 대체물로서 유리섬유나 합성섬유 등을 이용하여 바닥장식재의 물성을 보강하고 탄석의 함량을 감소시키는 등 바닥장식재의 경량화를 위하여 다양한 방법이 시도되고 있다. 그러나 이러한 시도는 바닥장식재의 생산비용을 증가시킬 뿐만아니라 바닥장식재의 기능을 보완시키는데 그 한계가 있기 때문에 제한적으로 적용하고 있어 종래 기술의 문제점을 해결하는데는 미완적이다.In order to solve these problems, development of alternative materials for various flooring materials has been developed. In particular, the weight of flooring materials is reduced by reinforcing the properties of flooring materials and reducing the content of coal by using glass fibers or synthetic fibers as substitutes. Various methods have been tried for this purpose. However, such an attempt is not only to increase the production cost of the flooring material, but also limited to supplementing the function of the flooring material, and thus it is applied in a limited manner, and thus it is incomplete to solve the problems of the prior art.
이와 같은 종래의 바닥장식재의 중량을 감소시키기 위한 또 다른 방법으로서 목재를 사용하고 있는데, 박편의 목재를 PVC에 접합시켜 바닥장식재의 하지층으로 이용하거나, 또는 목분을 PVC에 혼합시켜 바닥장식재의 하지층으로 이용하는 방법이 연구되고 있다.Wood is used as another method for reducing the weight of the conventional floor coverings, and the wood of the flakes is bonded to the PVC to use as a base layer of the flooring material, or the wood powder is mixed with the PVC to the floor decoration material. The method of use as a layer is researched.
그러나, PVC에 목편을 접합시켜 바닥장식재로 사용할 경우에는 PVC와 목편의 상용성이 개발되지 않아 상호간의 접착력이 불량함으로 인하여 그 사용이 적절하지 못하기 때문에 해결책이 되지 못하고 있다.However, when the wood pieces are bonded to PVC and used as a floor decoration material, the compatibility between the PVC and the wood pieces is not developed, and thus the use of the wood pieces is poor and the use of the wood pieces is not appropriate.
또한, PVC에 목분을 혼합하여 바닥장식재로 이용할 경우에는 목분의 장점인 섬유소 사이의 다공질을 PVC 및 기타 혼합 원료가 침투하여 막아버림으로써 그 기능을 제대로 발휘시키지 못하는 문제점이 있다.In addition, in the case of mixing wood powder in PVC and using it as a floor decoration material, there is a problem that PVC and other mixed raw materials penetrate and prevent the porous material between fibers, which is an advantage of wood powder, so that its function cannot be properly exhibited.
상술한 바와 같은 문제점을 지닌 종래의 바닥장식재의 과다한 중량은 중보행용 내구성이 양호한 바닥장식재의 경우에는 보다 큰 문제점, 즉 보다 큰 중량으로 인하여 소비자의 기피의 원인이 되고 있다.Excessive weight of the conventional flooring material having the problems as described above is a cause of consumer avoidance due to the greater problem, that is, the greater weight in the case of a flooring material with good durability for heavy walking.
본 발명은 상기와 같은 종래의 바닥장식재의 문제점을 해결하기 위하여 창안된 것으로서, 다른 액상의 원료의 침투를 막고 PVC와의 접착력을 높이기 위하여 그 표면이 바인더(BINDER)로 코팅 처리되어 제조된 다공질의 목분과 PVC 스트레이트 수지, 공중합 수지, 페이스트 수지, 발포제, 가소제, 그리고 열안정제를 혼합하여 제조된 PVC 콤파운드를 서로 혼합함으로써, 다공질의 목분과 PVC 사이의 접착력, 즉 상용성을 향상시키고, 경량화된 바닥장식재를 제공할 수 있을 뿐만 아니라, 천연 소재인 목분을 사용함으로써 목분의 자연향을 그대로 유지시킬 수 있는 PVC 바닥장식재용 목분 콤파운드 조성물과 그 제조방법, 그리고 이를 이용한 바닥장식재를 제공하는데 그 목적이 있다.The present invention was devised to solve the above problems of the conventional floor decoration material, the surface of the porous wood prepared by coating the surface of the binder (BINDER) to prevent the penetration of other liquid raw materials and to increase the adhesion with PVC PVC powder prepared by mixing powder, PVC straight resin, copolymer resin, paste resin, foaming agent, plasticizer, and thermal stabilizer are mixed with each other to improve the adhesion between porous wood powder and PVC, that is, compatibility and lightweight flooring materials. Not only to provide, but also by using a natural wood powder wood flour compound composition for the PVC floor decoration material that can maintain the natural flavor of the wood powder as it is, and a method for providing the floor decoration material using the same.
상기의 목적을 달성하기 위한 본 발명에 따른 PVC 바닥장식재용 목분 콤파운드 조성물은 전체 조성물 중량% 100에 대하여 그 표면이 바인더로 코팅처리되어 제조되는 목분 칩 18∼22%와 PVC 스트레이트 수지, 공중합 수지 및 페이스트 수지가 혼합된 PVC 수지 45∼49%, 가소제 14∼18%, 열안정제 4∼6%, 발포제 7∼9%, 그리고 바인더 3∼5%가 포함되는 것을 특징으로 한다.Wood flour compound composition for PVC flooring according to the present invention for achieving the above object is 18 to 22% of wood chips prepared by coating the surface with a binder with respect to 100% by weight of the total composition, PVC straight resin, copolymer resin and 45 to 49% of the PVC resin mixed with the paste resin, 14 to 18% of the plasticizer, 4 to 6% of the heat stabilizer, 7 to 9% of the blowing agent, and 3 to 5% of the binder are included.
또한, 상기의 또 다른 목적을 달성하기 위한 본 발명에 따른 PVC 바닥장식재용 목분 콤파운드 조성물의 제조방법은, 상기의 목분 칩을 제조하기 위하여, 목분을 고속 훈련기에 투입한 후 고속회전시킴으로써 전단열에 의하여 목분에 함유되어 있는 잔류수분을 제거하는 목분의 수분 제거단계; 잔류수분이 제거된 목분에 바인더를 투입하여 목분의 표면을 코팅처리하는 목분 표면의 코팅처리단계로 이루어지며, 상기의 PVC 콤파운드를 제조하기 위하여, 상기와 같은 일정량의 PVC 스트레이트 수지, 공중합 수지, 페이스트 수지를 고속 믹서기에 투입하여 혼합한 후 소정의 속도로 회전시킴으로써 수지 덩어리를 제거하는 단계; 상기 고속 믹서기 내에서 수지 덩어리가 제거된 상기 수지 혼합물을 고속 회전시킴으로써 소정의 온도로 유지시킨 후 일정량의 발포제를 투입하여 균일하게 혼합하는 단계; 발포제가 혼합된 상기 수지 혼합물에 일정량의 가소제 및 열안정제의 혼합물을 서서히 투입시켜 함침시킴으로써 일정한 크기의 미립자형 PVC 수지가 형성되는 단계; 상기 미립자형 PVC 수지를 냉각 믹서기를 이용하여 소정의 온도 이하로 냉각시키는 단계; 냉각된 상기 PVC 수지를 선별기를 이용하여 소정의 메쉬(MESH) 크기의 PVC 수지만을 선별하는 단계로 이루어지며, 상기 PVC 바닥장식재용 목분 콤파운드 조성물을 제조하기 위하여, 상기에서 제조된 일정한 량의 미립자형 PVC 콤파운드에 바인더에 의해 그 표면이 코팅처리되어 제조된 일정한 량의 상기 목분을 투입하여 균일하게 서로 혼합시키는 단계로 이루어지는 것을 특징으로 한다.In addition, the method for producing a wood flour compound composition for PVC flooring according to the present invention for achieving the above another object, in order to produce the wood chips, the wood powder is put into a high speed trainer and then rotated at high speed to shear heat Moisture removal step of wood powder to remove the residual moisture contained in the wood powder; It is composed of the coating process of the surface of the wood powder coating the surface of the wood powder by adding a binder to the wood powder from which residual moisture has been removed, and in order to manufacture the PVC compound, the above-mentioned amount of PVC straight resin, copolymer resin, paste Injecting the resin into a high speed mixer to mix and rotating the resin at a predetermined speed to remove the resin mass; Maintaining the temperature at a predetermined temperature by rotating the resin mixture from which the resin mass is removed in the high speed mixer at a high speed, and then mixing a uniform amount by adding a blowing agent; Forming a particulate-form PVC resin of a predetermined size by slowly impregnating a mixture of a plasticizer and a heat stabilizer in a predetermined amount into the resin mixture mixed with a blowing agent; Cooling the particulate PVC resin to a temperature below a predetermined temperature using a cooling mixer; A step of sorting the PVC resin of the predetermined mesh (MESH) size using the cooled PVC resin using a sorting machine, in order to produce the wood flour compound composition for PVC flooring, a predetermined amount of fine particles prepared above It is characterized by consisting of a step of uniformly mixing with each other by adding a predetermined amount of the wood powder prepared by coating the surface of the type PVC compound by a binder.
상기의 또 다른 목적을 달성하기 위하여, 상기 PVC 바닥장식재용 목분 콤파운드 조성물을 이용한 바닥장식재는 하지층, 중지층, 그리고 상지층으로 이루어지는 PVC 바닥장식재에 있어서, 상기 하지층이 상기에서 제조된 PVC 바닥장식재용 목분 콤파운드 조성물로 이루어지는 것을 특징으로 한다.In order to achieve the above another object, the flooring material using the wood powder compound composition for PVC flooring material is a PVC flooring material consisting of a bottom layer, a middle layer, and the upper layer, the bottom layer is a PVC floor prepared above It is characterized by consisting of a wood powder compound composition for decoration.
이하에서 본 발명에 따른 바람직한 실시예를 상세히 설명하기로 한다.Hereinafter, a preferred embodiment according to the present invention will be described in detail.
본 발명에 따른 PVC 바닥장식재용 목분 콤파운드 조성물은 전체 조성물 중량% 100에 대하여 그 표면이 바인더로 코팅처리되어 제조된 목분 칩 18∼22%와 PVC 스트레이트 수지, 공중합 수지 및 페이스트 수지가 혼합된 PVC 수지 45∼49%, 가소제 14∼18%, 열안정제 4∼6%, 발포제 7∼9%, 그리고 바인더 3∼5%가 포함되는 것을 특징으로 한다.The wood flour compound composition for PVC flooring according to the present invention is a PVC resin in which 18 to 22% of wood chips prepared by coating the surface with a binder with respect to 100% by weight of the total composition and a PVC straight resin, a copolymer resin and a paste resin are mixed. 45 to 49%, plasticizer 14 to 18%, thermal stabilizer 4 to 6%, foaming agent 7 to 9%, and binder 3 to 5%.
상기와 같이 목분의 칩은 접착제의 일종인 바인더에 의해 그 표면이 코팅 처리되는데, 이러한 코팅 처리로 인하여 다공질의 목분의 칩 내부로 다른 액상의 원료가 침투되지 않게 될 뿐만아니라, 목분과 PVC 수지 사이의 친화력을 증가시켜 서로간의 접착력을 향상시킬 수 있게 된다.As described above, the wood chips are coated with a binder, which is a kind of adhesive, and the coating does not prevent other liquid raw materials from penetrating into the wood chips of the porous wood powder. By increasing the affinity of the can be improved adhesion to each other.
또한, 상기의 PVC 수지는 요구되는 물성, 즉 바닥장식재의 사용 용도에 따라 스트레이트 수지, 공중합 수지, 페이스트 수지가 그 중합도에 따라 적절한 양으로 혼합되어 이루어진다.In addition, the PVC resin is a mixture of a straight resin, a copolymer resin, and a paste resin in an appropriate amount depending on the degree of polymerization, depending on the required physical properties, that is, the use of the floor decorative material.
그리고, 상기의 가소제와 발포제, 그리고 열안정제 역시 바닥장식재의 사용용도에 따라 적절한 양으로 혼합될 것이다. 이러한 가소제는 재료의 내구성을 위해 사용되며, 열안정제는 PVC 수지에 열안정성을 부여하기 위하여 사용된다.In addition, the plasticizer, the blowing agent, and the heat stabilizer may also be mixed in an appropriate amount depending on the use of the flooring material. These plasticizers are used for the durability of the material, and heat stabilizers are used to impart thermal stability to the PVC resin.
뿐만 아니라, 바닥장식재의 항균 기능을 위하여 PVC 콤파운드에는 적절한 양의 향균제 등이 첨가될 수 있다.In addition, an appropriate amount of antimicrobial agent may be added to the PVC compound for the antibacterial function of the flooring material.
[실시예 1]Example 1
먼저, 본 발명에 따른 PVC 바닥장식재용 목분 콤파운드 조성물의 성분 중에서 그 표면이 바인더에 의해 코팅된 목분 칩의 제조를 위하여, 천연 소재인 목분을 고속 혼련기에 투입한 후, 고속 혼련기를 고속 회전시켜 그 전단열이 약 80℃ 정도가 되게 한다. 이러한 상태는 고속 혼련기 내에서 고속 회전되는 목분에 함유되어 있는 잔류수분을 제거시켜 준다.First, in order to manufacture wood chips having a surface coated with a binder among the components of the wood flour compound composition for PVC flooring according to the present invention, wood powder, which is a natural material, is introduced into a high speed kneader, and then the high speed kneader is rotated at a high speed. The shear heat is about 80 ° C. This condition removes the residual moisture contained in the wood powder rotated at high speed in the high speed kneader.
이렇게 함유되어 있는 잔류수분이 제거된 목분에 접착제의 일종인 바인더를 투입하여 목분의 표면을 코팅 처리하게 된다. 그 표면이 바인더에 의해 코팅되어 있는 목분은 다른 액상의 원료가 침투되지 않을 뿐만 아니라, 그러한 목분과 PVC 상호간의 접착력을 향상시키게 된다.The surface of the wood powder is coated by adding a binder, which is a kind of adhesive, to the wood powder containing the residual moisture. The wood powder whose surface is coated by the binder not only penetrates other liquid raw materials, but also improves the adhesion between such wood powder and PVC.
한편, 본 발명에 따른 PVC 바닥장식재용 목분 콤파운드 조성물 중에서 PVC 콤파운드를 제조하기 위하여, 목분 콤파운드의 전체 조성물의 중량% 100에 대하여 9∼11%의 PVC 스트레이트 수지, 28∼32%의 공중합 수지, 그리고 6∼8%의 페이스트 수지를 분산력이 우수한 헨셀형(HENSCHEL TYPE) 고속 믹서기에 투입한다. 이러한 PVC 수지가 투입되어 있는 고속 믹서기를 400∼450rpm으로 약 5분 동안 회전시키면 PVC 수지 덩어리가 제거된다. 덩어리가 제거된 PVC 수지가 안에 있는 고속 믹서기를 800∼850rpm으로 상승회전시켜 온도를 100℃ 내외로 유지하면서 7∼9%의 발포제를 투입하여 균일하게 혼합한다. 이러한 상태에서 14∼18%의 가소제와 4∼6%의 열안정제를 혼합하여 서서히 투입시켜 PVC 수지에 충분하게 함침시키면, 일정한 크기의 미립자형 PVC 수지가 형성된다.On the other hand, in order to manufacture the PVC compound in the wood compound composition for PVC flooring according to the present invention, 9 to 11% of the PVC straight resin, 28 to 32% copolymer resin, and with respect to 100% by weight of the total composition of the wood powder compound, and 6-8% paste resin is added to HENSCHEL TYPE high speed mixer with excellent dispersibility. When the high speed mixer in which the PVC resin is added is rotated at 400 to 450 rpm for about 5 minutes, the PVC resin lump is removed. The high-speed mixer in which the PVC resin is removed is spun up to 800 to 850 rpm, and 7 to 9% of blowing agent is added and mixed uniformly while maintaining the temperature at about 100 ° C. In such a state, when 14-18% of the plasticizer and 4-6% of the thermal stabilizer are mixed and gradually added, the PVC resin is sufficiently impregnated to form a particulate PVC resin of a certain size.
이러한 미립자형 PVC 수지를 냉각 믹서기를 이용하여 50℃ 이하로 냉각시킨후에, 선별기를 통해 필터링하여 크기가 20메쉬 이하의 PVC 수지만을 취하면 본 발명의 PVC 바닥장식재용 목분 콤파운드를 위한 PVC 콤파운드가 제조된다.After the particulate PVC resin is cooled to 50 ° C. or lower using a cooling mixer, the filter is filtered through a sorter to take only a PVC resin having a size of 20 mesh or less, so that the PVC compound for wood flour compound for PVC flooring material of the present invention is obtained. Are manufactured.
상기 선별기로부터 취해지는 크기가 20메쉬 이상인 PVC 수지는 분쇄기를 이용하여 분쇄시킨 후에 재사용할 수 있을 것이다.PVC resin having a size of 20 mesh or more taken from the sorter may be reused after milling using a mill.
상기와 같이 제조된 PVC 콤파운드에 상기와 같이 제조된 그 표면이 바인더에 의해 코팅처리된 22∼26%의 목분을 투입하여 균일하게 혼합하면 본 발명의 PVC 바닥장식재용 목분 콤파운드 조성물이 제조된다.The wood powder compound composition for PVC flooring of the present invention is prepared by uniformly mixing 22 to 26% of the wood powder whose surface is prepared as described above with the binder and uniformly mixing the PVC compound prepared as described above.
이와 같이 제조된 조성물을 PVC 바닥장식재의 하지층으로 이용함으로써 본 발명에 따른 PVC 바닥장식재를 제조할 수 있을 것이다.By using the composition prepared as a base layer of PVC flooring material will be able to manufacture a PVC flooring material according to the present invention.
[실시예 2]Example 2
본 발명에 따른 PVC 바닥장식재용 목분 콤파운드 조성물 중에서 그 표면이 바인더로 코팅되어 있는 목분의 제조에 대한 실시예는 상기 실시예 1과 동일하다.In the wood flour compound composition for PVC flooring according to the present invention the embodiment for the production of wood powder whose surface is coated with a binder is the same as in Example 1.
본 발명의 조성물 중에서 PVC 콤파운드의 제조에 대한 또 다른 실시예는 하기와 같다.Another embodiment for the preparation of the PVC compound in the composition of the present invention is as follows.
본 발명의 전체 조성물 중량% 100에 대하여, 9∼11%의 PVC 스트레이트 수지, 28∼32%의 공중합 수지, 6∼8%의 페이스트 수지를 자켓으로 이루어진 가열식 리본 브렌더에 투입하여 100rpm으로 약 10분간 회전시키면 PVC 수지 덩어리가 제거된다. 이렇게 덩어리가 제거된 PVC 수지가 안에 있는 리본 브렌더의 자켓을 가열시켜 약 100℃의 PVC 수지가 되게 한다.9 to 11% of PVC straight resin, 28 to 32% of copolymer resin, and 6 to 8% of paste resin were added to a heated ribbon blender made of a jacket, based on 100% by weight of the total composition of the present invention, at about 10 rpm at 100 rpm. Rotation for a minute removes the PVC resin mass. The jacket of the ribbon blender in which the lumped PVC resin is removed is heated to a PVC resin of about 100 ° C.
이렇게 가열된 PVC 수지에 7∼9%의 발포제를 투입하여 균일하게 혼합한다.A 7-9% blowing agent is added to the heated PVC resin and mixed uniformly.
발포제가 혼합된 PVC 수지에 14∼18%의 가소제, 4∼6%의 열안정제를 혼합하여 서서히 투입하면 PVC 수지에 충분하게 함침된다. 이와 같이 제조된 PVC 수지를 냉각 믹서기를 이용하여 50℃ 이하로 냉각시킨다. 이렇게 냉각된 PVC 수지는 선별기를 통해 필터링하여 20메쉬 크기 이하의 수지만을 취하면 본 발명의 PVC 콤파운드가 제조된다.The PVC resin mixed with the blowing agent is mixed with 14 to 18% of a plasticizer and 4 to 6% of a thermal stabilizer and gradually added to the PVC resin to be sufficiently impregnated. The PVC resin thus prepared is cooled to 50 ° C. or lower using a cooling mixer. The PVC resin thus cooled is filtered through a separator to take only 20 mesh or less in size to produce the PVC compound of the present invention.
상기 선별기에 의한 20메쉬 이상의 PVC 수지는 분쇄기를 이용하여 분쇄시킨 후에 재사용할 수 있을 것이다.PVC resin of 20 mesh or more by the separator may be reused after milling using a mill.
상기와 같이 제조된 PVC 콤파운드에 상기 실시예 1에서 제조된 그 표면이 바인더에 의해 코팅되어 있는 22∼26%의 목분을 투입하여 균일하게 혼합하면 본 발명의 PVC 바닥장식재용 목분 콤파운드 조성물이 된다.Into the PVC compound prepared as described above, the wood powder compound composition for the PVC flooring material of the present invention is uniformly mixed by adding 22 to 26% of the wood powder whose surface prepared in Example 1 is coated with a binder.
이렇게 제조된 PVC 바닥장식재용 목분 콤파운드 조성물을 PVC 바닥장식재의 하지층으로 이용함으로써 본 발명에 따른 바닥장식재를 제조할 수 있을 것이다.Thus, by using the wood compound composition for the PVC flooring material as a base layer of the PVC flooring material it will be possible to manufacture the flooring material according to the present invention.
부가하면, 일반적으로 PVC 또는 섬유질 등으로 이루어지는 바닥장식재의 중지층의 하부에 본 발명의 조성물로 이루어지는 하지층이 라메네이팅되며, 중지층의 상부에는 PVC 등으로 이루어지는 상지층이 라미네이팅 또는 코팅됨으로써 바닥장식재가 형성된다.In addition, the base layer made of the composition of the present invention is laminated to the bottom of the stop layer of the flooring material made of PVC or fiber, etc., and the upper layer made of PVC or the like is laminated or coated on the top of the stop layer. Decorative materials are formed.
이상에서 설명한 바와 같이, 본 발명의 제조방법에 따라 제조된 PVC 바닥장식재용 목분 콤파운드 조성물에 있어서, 목분의 표면이 바인더에 의해 코팅 처리되기 때문에 다른 액상의 원료의 침투를 방지할 수 있을 뿐만 아니라, 목분과 PVC 수지 상호간의 친화력, 즉 서로간의 접착력을 향상시킬 수 있을 것이다.As described above, in the wood flour compound composition for PVC flooring material prepared according to the production method of the present invention, since the surface of the wood powder is coated with a binder, not only the penetration of other liquid raw materials can be prevented, The affinity between the wood flour and the PVC resin, that is, the adhesion between each other, may be improved.
또한, 이러한 조성물을 이용한 PVC 바닥장식재는 목분 칩과 PVC 스트레이트 수지, 공중합 수지, 페이스트 수지, 발포제, 가소제, 그리고 열안정제 등으로 제조된 PVC 콤파운드를 혼합시켜 제조됨으로써, 바닥장식재의 경량화에 크게 이바지하게 될 것이다.In addition, the PVC flooring material using such a composition is manufactured by mixing PVC powder made of wood chips and PVC straight resin, copolymer resin, paste resin, foaming agent, plasticizer, and heat stabilizer, thereby greatly reducing the weight of flooring material. Will be.
더욱이, 본 발명의 조성물을 이용한 PVC 바닥장식재는 바닥의 습기를 예방하고 보온을 유지시키며, 천연 소재의 목분을 이용함으로써 천연 소재 자체의 자연향을 그대로 유지시킬 수 있는 효과를 갖게 된다.Moreover, PVC flooring material using the composition of the present invention has the effect of preventing the moisture of the floor and keeping warm, and by using the wood powder of the natural material to maintain the natural aroma of the natural material itself.
Claims (3)