KR100193236B1 - Manufacturing Equipment Of Magnesium Castings - Google Patents
Manufacturing Equipment Of Magnesium Castings Download PDFInfo
- Publication number
- KR100193236B1 KR100193236B1 KR1019930028602A KR930028602A KR100193236B1 KR 100193236 B1 KR100193236 B1 KR 100193236B1 KR 1019930028602 A KR1019930028602 A KR 1019930028602A KR 930028602 A KR930028602 A KR 930028602A KR 100193236 B1 KR100193236 B1 KR 100193236B1
- Authority
- KR
- South Korea
- Prior art keywords
- magnesium
- crucible
- mold
- casting
- molten metal
- Prior art date
Abstract
본 발명이 목적은 마그네슘 용량을 밀폐시킨 로에 저압의 공기로 가압하여 마그네슘 용탕이 공급 통로를 따라 주형의 캐비티까지 용이하게 공급됨으로서 주조품의 산화 방지 및 작업의 안정성을 도모한 마그네슘 주조품 제조장치를 제조하는데 있다.An object of the present invention is to manufacture a magnesium casting manufacturing apparatus that is to prevent the oxidation of the casting and stability of the work by easily supplying the molten magnesium to the mold cavity along the supply passage by pressurizing with a low pressure air in the furnace sealed magnesium capacity have.
이를 실현하기 위한 본 발명은 상기한 주조품의 주형을 상측에 위치하도록 하는 커버에 의해 개구되는 용해로의 가열수단과; 상기 용해로가 가열됨에 따라 마그네슘이 용융되어 채워지는 도가니의 저장수단과; 상기 도가니에 채워진 용탕에 잠기도록 커버에 나사 결합되는 공급관의 관부재와; 상기 공급관을 통해 용탕이 주형에 공급되도록 도가니에 가압공기를 충진하는 가압장치의 가압수단을 포함하여 이루어지는 마그네슘 주조품의 제조장치를 특징으로 한다.The present invention for realizing this, the heating means of the melting furnace which is opened by the cover for placing the above-mentioned mold of the casting; Storage means for the crucible in which magnesium is melted and filled as the melting furnace is heated; A pipe member of the supply pipe screwed to the cover to be immersed in the melt filled in the crucible; Characterized in that the apparatus for producing a magnesium casting comprising the pressing means of the pressurizing device for filling the crucible pressurized air so that the molten metal is supplied to the mold through the supply pipe.
Description
제1도는 본 발명에 따른 마그네슘의 주조품의 제조장치를 도시한 도면.1 is a view showing an apparatus for producing a cast of magnesium according to the present invention.
* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings
1 : 제조장치 10 : 용해로1: manufacturing apparatus 10: melting furnace
11 : 하우징 12 : 히이터선11 housing 12 heater wire
13 : 커버 14 : 홀13: cover 14: hole
16 : 용탕 17 : 주형16: molten metal 17: mold
18 : 주입구 19 : 캐비티(CAVITY)18: injection hole 19: cavity (CAVITY)
20 : 도가니 30 : 공급관20: crucible 30: supply pipe
31 : 공급통로부 32 : 나사부31: supply passage portion 32: screw portion
40 : 가압장치 41 : 파이프40: pressurization device 41: pipe
42 : 개폐밸브42: on-off valve
[산업상의 이용분야][Industrial use]
본 발명은 마그네슘 주조품의 제조장치에 관한 것으로서, 보다 상세하게는 마그네슘 용융물을 밀폐시킨 로에 저압의 공기로 가압하여 마그네슘 용탕이 공급 통로를 따라 주형의 캐비티까지 용이하게 공급됨으로써 주조품의 산화 방지 및 작업의 안정성을 도모한 마그네슘 주조품의 제조장치에 관한 것이다.The present invention relates to an apparatus for manufacturing a magnesium casting, and more particularly, to prevent the oxidation and operation of the casting product by pressurizing the magnesium melt with low pressure air to easily supply the magnesium molten metal along the supply passage to the mold cavity. The present invention relates to an apparatus for producing magnesium castings aimed at stability.
[종래 기술][Prior art]
일반적으로 마그네슘 주조품을 제조하기 위한 주형을 주형공장의 바닥에 놓고 마그네슘 용탕을 주입하고 있다.Generally, a mold for manufacturing a magnesium casting is placed on the bottom of a mold factory and magnesium molten metal is injected.
상기한 용탕은 주형의 한쪽에 설치되면서 대기중에 노출된 주입구를 통하여 용탕통로를 거쳐 주형에 용탕이 흘러 들어가게 되어 있다.The molten metal is installed on one side of the mold, and the molten metal flows into the mold through the molten metal passage through an injection hole exposed to the atmosphere.
[발명이 해결하려고 하는 문제점][Problem trying to solve the invention]
상기한 종래기술은 마그네슘 주조품을 주조할 용탕의 표면이 대기에 노출되어 마그네슘이 산화함으로서 주조품에 산화된 물질이 혼입할 수 있는 문제점이 있다.The prior art has a problem in that the surface of the molten metal for casting the magnesium casting is exposed to the atmosphere and the magnesium is oxidized to mix the oxidized material in the casting.
또한, 상기한 마그네슘 용탕의 이송시 수분등에 의해 발화할 위험성을 내포하고 있음으로서 작업의 불안정성에 대한 문제점이 있다.In addition, there is a problem with the instability of the work because it contains the risk of ignition by moisture or the like during the transfer of the molten magnesium.
본 발명의 목적은 마그네슘 용탕을 밀폐시킨 로에 저압의 공기로 가압하여 마그네슘 용탕이 공급 통로를 따라 주형의 캐비티까지 용이하게 공급됨으로써 주조품의 산화 방지 및 작업의 안정성을 도모한 마그네슘 주조품 제조장치를 제공하는데 있다.SUMMARY OF THE INVENTION An object of the present invention is to provide a magnesium casting product manufacturing apparatus for preventing oxidation of a casting and stability of work by easily supplying magnesium molten metal to a mold cavity along a supply passage by pressurizing the magnesium molten metal with a low pressure air in a sealed furnace. have.
[문제점을 해결하기 위한 수단][Means to solve the problem]
이를 실현하기 위한 본 발명은 주형을 상측에 위치하도록 하는 커버에 의해 열리는 용해로의 가열수단과; 상기 용해로가 가열됨에 따라 마그네슘이 용융되어 채워지는 도가니의 저장수단과; 상기 도가니에 채워진 용탕에 잠기도록 커버에 나사 결합되는 공급관의 관부재와; 상기 공급관을 통해 용탕이 주형에 공급되도록 도가니에 가압공기를 충진하는 가압장치의 가압수단을 포함하여 이루어지는 마그네슘 주조품의 제조장치를 특징으로 한다.The present invention for realizing this and the heating means of the melting furnace opened by the cover for placing the mold on the upper side; Storage means for the crucible in which magnesium is melted and filled as the melting furnace is heated; A pipe member of the supply pipe screwed to the cover to be immersed in the melt filled in the crucible; Characterized in that the apparatus for producing a magnesium casting comprising the pressing means of the pressurizing device for filling the crucible pressurized air so that the molten metal is supplied to the mold through the supply pipe.
상기한 공급관은 용탕에 잠기는 공급통로부와, 이 공급통로부와 일체이면서 주형의 주입구와 연통하도록 커버와 나사 결합하는 나사부로 이루어지는 마그네슘 주조품의 제조장치를 제공하는 데 있다.The supply pipe is to provide an apparatus for producing magnesium castings comprising a supply passage portion immersed in the molten metal, and a screw portion screwed to the cover so as to be in communication with the inlet of the mold while being integral with the supply passage portion.
상기한 가압장치는 도가니 내에 용융된 마그네슘의 용탕 위에 연통된 파이프를 통해 건조공기를 포함한 산화방지제를 저압으로 가압 분출되도록 한 개폐밸브를 포함하여 이루어지는 마그네슘 주조품의 제조장치를 제공하는데 있다.The pressurizing device is to provide an apparatus for manufacturing a magnesium casting, comprising an on-off valve to pressurize and eject the antioxidant at low pressure through the pipe connected to the molten magnesium of molten crucible at a low pressure.
상기한 주형의 내부에 형성된 캐비티에 용탕이 저면의 공급관에서 공급되도록 하부 주형에 주입구가 형성되어 이루어지는 마그네슘 주조품이 제조장치를 제공하는데 있다.The present invention provides a manufacturing apparatus for magnesium castings in which an injection hole is formed in a lower mold such that a molten metal is supplied from a supply pipe on a bottom surface to a cavity formed inside the mold.
[작용][Action]
상기한 본 발명은 마그네슘을 이용 주조할 때 밀폐된 도가니 내에 SF6+CO2의 산화방지제가 충진된 상태에서 용해로를 가열함으로써 도가니 내의 마그네슘을 용해한다.The present invention described above dissolves magnesium in the crucible by heating the furnace in a state in which an antioxidant of SF 6 + CO 2 is filled in a sealed crucible when casting with magnesium.
상기한 용해된 마그네슘이 채워진 도가니에 가압공기인 SF6+CO2와 건조공기를 저압으로 도가니 내에 가압장치를 이용 분출함으로써 마그네슘의 신화가 방지되면서 용탕이 가압되도록 한다.The molten magnesium-filled crucible is pressurized with SF 6 + CO 2 , which is pressurized air, and dry air at low pressure using a pressurizing device in the crucible to prevent the myth of magnesium, while allowing the melt to be pressurized.
상기한 마그네슘의 용탕이 가압됨으로써 공급관을 통해 주형의 저부에 형성된 주입구를 거쳐 캐비티에 충진시 대기중에 노출되지 않는 새로운 제조장치로 고품질의 주조품을 제조할 수 있게 된다.As the molten metal of the magnesium is pressurized, it is possible to manufacture high-quality castings using a new manufacturing apparatus that is not exposed to the air when filling the cavity through an injection hole formed at the bottom of the mold through a supply pipe.
[실시예]EXAMPLE
이하, 본 발명의 바람직한 일 실시예를 첨부한 도면에 의하여 더욱 상세히 설명한다.Hereinafter, with reference to the accompanying drawings a preferred embodiment of the present invention will be described in more detail.
도면은 본 발명에 따른 마그네슘 주조품의 제조장치를 도시한 도면으로, 부호(1)은 제조장치를 지칭한다.The figure shows a manufacturing apparatus of a magnesium casting according to the present invention, wherein reference numeral 1 denotes a manufacturing apparatus.
상기한 제조장치(1)는 주형(17)을 상측에 위치하도록 하는 커버(13)에 의해 열리는 용해로(10)와, 상기 용해로가 가열됨에 따라 마그네슘이 용융되어 채워지는 도가니(20)와, 상기 도가니에 채워진 용탕에 잠기도록 커버에 나사 결합되는 공급관(30)과, 상기 공급관을 통해 용탕이 주형에 공급되도록 용해로의 도가니에 가압공기를 충진하는 가압장치(40)를 포함하여 이루어지고 있다.The manufacturing apparatus 1 includes a melting furnace 10 opened by a cover 13 for positioning the mold 17 upward, a crucible 20 in which magnesium is melted and filled as the melting furnace is heated, and It comprises a supply pipe 30 screwed to the cover to be immersed in the melt filled in the crucible, and a pressurizing device 40 for filling the crucible of the melting furnace so that the molten metal is supplied to the mold through the supply pipe.
상기한 용해로(10) 내에 내장하는 도가니(20)를 저장하는 하우징(11) 내부에는 히이터선(12)이 내장되어 도가니(20)를 가열하게 되어 있다.A heater wire 12 is built into the housing 11 for storing the crucible 20 embedded in the melting furnace 10 to heat the crucible 20.
상기한 도가니(20)를 내장한 용해로(10)의 상측부를 개폐하도록 한 커버(13)가 설치되어 있으며, 이 커버(13)의 중심에 형성된 홀(14)과 나사 결합한 공급관(30)은 하향으로 형성되어 있다.A cover 13 is provided to open and close the upper side of the melting furnace 10 having the crucible 20 embedded therein, and the supply pipe 30 screwed with the hole 14 formed in the center of the cover 13 is downward. It is formed.
상기한 공급관(30)은 마그네슘 용탕(16)에 잠기는 공급통로부(31)와, 이 공급통로부(31)와 일체이면서 주형(17)의 주입구(18)와 연통하도록 커버(13)와 나사 결합하게 나사부(32)로 형성되어 있다.The supply pipe 30 has a cover 13 and a screw so as to be in communication with the inlet 18 of the mold 17 while being integral with the supply passage 31 so as to be immersed in the molten magnesium 16. It is formed of a screw portion 32 to be coupled.
상기한 가압장치(40)는 도가니(20) 내에 용융된 마그네슘의 용탕(16) 위에 연통된 파이프(41)를 통해 건조공기를 포함한 산화방지가스(SF6+CO2)(G)를 저압으로 가압 분출되도록 개폐하는 개폐밸브(42)를 설치되어 있다.The pressurizing device 40 is a low pressure to the antioxidant gas (SF 6 + CO 2 ) (G) including dry air through a pipe 41 communicated with the molten magnesium of molten magnesium 16 in the crucible 20 An on-off valve 42 for opening and closing the pressurized jet is provided.
상기한 주형(17)의 내부에 형성된 캐비티(19)에 용탕(16)이 저면의 공급관(30)에서 공급되도록 하부 주형(171)에 주입구(18)가 형성되어 있다.The injection hole 18 is formed in the lower mold 171 so that the molten metal 16 is supplied from the supply pipe 30 at the bottom to the cavity 19 formed in the mold 17.
이와 같이 이루어지는 본 발명은 마그네슘을 이용 주조할 때 밀폐된 도가니(20) 내에 SF6+CO2의 산화 방지가스가 충진된 상태로 커버(13)를 이용하여 밀폐한 후 용해로(10)의 히이터선(12)에 전원을 인가하면 가열되어 도가니(20) 내의 마그네슘은 용해하게 된다.According to the present invention, the heater vessel of the melting furnace 10 is sealed by using the cover 13 in a state in which an antioxidant gas of SF 6 + CO 2 is filled in the sealed crucible 20 when casting with magnesium. When power is applied to (12), it is heated to dissolve magnesium in the crucible 20.
상기한 용해된 마그네슘이 채워진 도가니(20)에 가압공기인 SF6+CO2(G)와 건조공기가 저압으로 도가니(20)내에 가압장치(40)로 공급하게 된다. 이에 따라 마그네슘의 산화가 방지되면서 용탕(16)이 압력을 받게 된다.In the crucible 20 filled with the dissolved magnesium, SF 6 + CO 2 (G), which is pressurized air, and dry air are supplied to the pressurizing device 40 in the crucible 20 at low pressure. Accordingly, while the oxidation of magnesium is prevented, the molten metal 16 is subjected to pressure.
상기한 가압된 마그네슘의 용탕(16)은 공급관(30)을 통해 상승하게 되고, 이 상승한 용탕(16)은 주형(17)의 저부에 형성된 주입구(18)를 거쳐 캐비티(19)에 충진되게 된다. 이때 용탕(16)이 공급관(30)과 주입구(18)를 통하면서 대기중에 노출되지 않고 공급됨으로써 제조할 수 있게 된다.The pressurized magnesium molten metal 16 rises through the supply pipe 30, and the raised molten metal 16 is filled in the cavity 19 through an injection hole 18 formed at the bottom of the mold 17. . At this time, the molten metal 16 can be manufactured by being supplied without being exposed to the atmosphere while passing through the supply pipe 30 and the inlet 18.
[발명의 효과][Effects of the Invention]
이러한 본 발명은 마그네슘 주조품 주조할 용탕의 표면이 대기에 노출되지 않기 때문에 산화하지 않음으로써 산화 물질의 혼입이 이루어지지 않아 주조품의 질이 고양되는 효과가 있다.In the present invention, since the surface of the molten magnesium to be cast is not exposed to the atmosphere, it is not oxidized, so that the incorporation of oxidizing materials is not performed, thereby improving the quality of the cast.
또한, 상기한 마그네슘 용탕을 이송하지 않고도 주형의 캐비티에 바로 공급됨으로써 수분 등에 의해 발화할 위험성이 해소됨과 아울러 작업의 안전성이 향상되는 효과가 있다.In addition, since the magnesium molten metal is directly supplied to the cavity of the mold without transferring the molten magnesium, the risk of ignition by moisture or the like is eliminated and the safety of the work is improved.
Claims (4)