KR0155674B1 - Dyeing process of corduroy texture using discharge printing - Google Patents

Abstract

The present invention relates to a dyeing and processing method of a pile fabric using the balconitis, in particular to be applied to the fabric long piles, such as corden fabrics in the bone shape, so that the color of the floor and the color of the pile to be expressed differently In addition to the unusual aesthetics that could not be felt in the corden fabric so far, the characteristic characteristics of the corden fabric, the file can be clearly expressed.

In other words, the primary dyeing and drying of the corden fabric is printed on the pile of the corden fabric with a printing foil mixed with the dye and the dye which is not printed by the dye and the dye. At the same time, the dye is used for printing and at the same time, only the dye used for printing, and the color of the dye remaining during the first dyeing on the bottom surface to express a double color on the fabric.

Description

Method for dyeing corden fabrics using anti-inflammatory

The present invention relates to a method of dyeing a pile fabric using a flame retardant, and in particular, to be processed by applying to a fabric in which a pile, such as a corden fabric, is formed in a long bone shape, the processed fabric is different from the color of the floor paper and the pile color It was made to be different so that a very unique aesthetic that could not be felt so far in the corden fabric was expressed so that the merchandise could be doubled.

In general, a method for producing a corden fabric is to weave through the weaving process, then bleached the whole hair, hair loss, consumption and refining, and to obtain a finished corden fabric by dyeing and processing the finished fabric bleached.

However, such a conventional corden fabric product can not fully highlight the characteristics of only the corden fabric because the entire fabric was dyed only one color by dyeing.

In other words, because the whole product is dyed with the same color, it is difficult to expect a distinctive aesthetic effect because the distinction between the pile and the floor protruding into the bone shape is not clear.

The present invention is different from the corden fabric, which has been dyed in only one color until now to correct all the disadvantages of the prior art, so that the product itself is a double color, that is, the color of the floor and the color of the file to be expressed differently from each other The unique characteristics of the fabric are fully emphasized so that the product quality can be doubled.

In order to achieve the above object, the present invention is woven fabric woven hair, hair loss, consumption and refining bleaching, dyeing the refined bleached product in the same manner as usual, and printed with a ready-to-preventive printing printing foil of the first dyed fabric It is to make the printing foil to be printed only on the pile part of the fabric, and then to produce it by heating and hand-processing. In this case, it is ideal to dye the first dye dye with a reactive dye of vinyl sulphone type which is easily spread by the dye. The dye of the printing foil, which is printed secondarily on the first dyed fabric, is printed by using a monochlorochloroagen-based reactive dye which is not easily printed by the printing agent, and thus, by the printing agent added to the printing lake. Dyed dyes are printed and the dye added to the printing foil is colored on the fabric of the fabric, so the fabric is colored with the primary dyed bottom and secondary. The color of the colored files salts are dyed in different colors double.

In order to print only on the pile part at the time of the second printing, it is preferable to use it by increasing the viscosity of the printing arc, and to use the high viscosity printing arc, the printing arc does not flow down to the bone between the piles of the file, so it is an ideal balmitis You can expect the effect.

At this time, the screen used for printing is ideal to use a high density screen and many openings.

The above two conditions, namely high viscosity and screen conditions, may be selected and used according to the type of fabric and the design effect to be obtained.

Under these conditions, the fabrics treated with the flame retardant can be provided with an ideal product by tumbling at high temperature and high pressure to obtain a unique surface effect and a soft touch.

Hereinafter, an embodiment of the present invention will be described in detail by process.

[First Step: (Dyeing Process)]

Woven corden fabrics are woven, haired, worn and refined, bleached, and dyed refined bleached fabrics.

In this case, the dye used in the primary dyeing is dyed by a conventional method using a vinyl sulphone-based reactive dye, but is dyed in the same color over the entire bottom part and pile part.

It is preferable to use a dye which can be easily colored by the dye as the reactive dye to be primary dye in the above.

[2nd process (protocol treatment process]

The printing foil is printed on the pile part of the fabric by second printing the printing foil prepared on the surface of the fabric soaked with the dye that can be easily printed by the printing agent with a rotary printer.

The printing foil used at this time is sufficiently mixed with MC T (Mono chloro triagine) -based reactive dye, high viscosity arc (pool), acidic or sodium sulfate (dye) and fixing agent with water at an appropriate ratio. One printing foil is used, and the screen used for printing should use a high-density screen but ideally use as many open parts as possible.

The mixing ratio of the various components mixed in the above is based on 100% of the salt lake, about 60% acid or sodium sulfate 10 ~ 15% fixing agent 0.1 ~ 0.3%, the remaining% adjusts the water and dye according to the color The mixing ratio of each component is not absolute and there may be a lot of flow depending on the conditions.

When the second printing is completed on the first dyed fabric under the same conditions as described above, the fabric is subjected to steaming (steaning) for about 10 minutes at about 100 to 110 ° C, followed by washing with water and drying.

In the steaming process, the printing foil, which is only stamped on the pile part of the fabric, is deposited on the pile part, and in this process, the vinyl sulfone is dyed in the pile part in the first step by a dyeing agent based on acidic or sodium sulfate added to the printing foil. Reactive dyes in the (vinyl shlphone) system are dyed (discolored), and only MC T-based reactive dyes, which are not fired by the dyeing agent added to the printing foil, are colored in the pile part. The dyed color appears, and in the pile part, different colors deposited in the second dyeing remain, so that the fabric has a double color with different colors of the floor paper and the pile.

[3rd process (Tumblering process)

In the second process, the fabric that has been dried and sprayed into the Roto Tumbler is tumbled at high temperature and high pressure, so that the pile of the fabric is completely defrosted, thus providing a more ideal product by doubling the feel and flexibility. It becomes possible.

Since the product of the present invention manufactured by the above method is expressed in different colors with different colors of the floor paper and the pile, only the corden fabric has a distinctive golgue effect of the same unique stripes, so it is unusual The aesthetics can be provided and the merchandise will be doubled.

Claims (1)

After weaving, weaving, scouring, refining, and bleaching the fabric of the woven corden fabric, the first dyeing is carried out by conventional methods, and the dye used in the first dyeing is dyed with a dye that can be dissipated by a dyeing agent, and the first dyeing fuel is used. Dye, which is manufactured by mixing dye that is not printed by printing agent, foil and dye on the surface of the fabric, is printed only on the pile part, heated and washed with water. Dyeing process for dyeing corden fabrics using the balsa dye, which is dyed by different colors on the floor and pile by depositing the dye that is printed in the second printing process.