JPWO2017022765A1 - Laminated film and method for producing the same - Google Patents

Abstract

A laminated film having a polyester layer and a resin layer, wherein at least one surface layer is a resin layer, and the resin layer included in the surface layer has a micro surface roughness (Ra-1) required by AFM (Atomic Force Microscope). A laminated polyester having excellent transparency, scratch resistance and antiblocking properties by a laminated film having a macro surface roughness (Ra-2) of 1 nm or more and 50 nm or less determined by a three-dimensional surface roughness meter, which is 1 nm or more and 20 nm or less. Provide film. [Selection figure] None

Description

  The present invention relates to a laminated film having a polyester layer and a resin layer, wherein at least one surface layer is a resin layer.

  Thermoplastic resin films, especially biaxially stretched polyester films, have excellent properties such as mechanical properties, electrical properties, dimensional stability, transparency, and chemical resistance. Widely used in applications. Particularly in recent years, it has been used for various optical films including display member applications such as a touch panel, a liquid crystal display panel (LCD), a plasma display panel (PDP), and organic electroluminescence (organic EL).

In these optical films, a layer having a different refractive index (hereinafter referred to as an optical adjustment layer) is laminated on a polyester film, and then a conductive layer is provided to be used as a conductive film. Here, in general, when laminating an optical adjustment layer, a functional film is applied to a base film wound in a roll shape, cured, and then wound in a roll shape. Processing is performed in the form. The conductive layer is formed by forming a metal oxide film on the roll film by sputtering in a vacuum environment.
Therefore, in such an application, a laminated film in which a scratch-resistant layer is laminated on a polyester film is used in order to prevent scratches during film roll conveyance.

As this laminated film, a hard coat film in which a layer made of a UV curable resin is laminated as a scratch-resistant layer is used. When used for optical applications, since transparency is required, the surface of the resin layer is smoothed in order to improve transparency. Blocking (sticking) occurs. Therefore, in recent years, a laminated film having blocking resistance has been demanded.
In addition to scratch resistance, laminated films used for optical applications are required not only at room temperature but also for adhesion to a substrate under high temperature and high humidity, transparency, and the like. Moreover, since it is often used for the surface of a display etc., visibility and designability are requested | required of the laminated | multilayer film used for an optical use.

  In response to this requirement, Patent Document 1 proposes a method for reducing the contact area of the hard coat film and developing anti-blocking properties by laminating a coating film containing particles larger than the coat film thickness. Patent Document 2 proposes a method of obtaining a laminated film having excellent antiglare property and scratch resistance by laminating a coating film containing acrylic particles smaller than the coat film thickness.

JP 2014-228833 A JP 2011-186287 A

  However, the method described in Patent Document 1 has a problem in that light scattering occurs and transparency is impaired because the particle diameter of the particles present in the coat layer is large. Further, even in the method described in Patent Document 2, since the particle diameter of the acrylic particles present in the coat layer having a film thickness of 6 to 8 μm is as large as about 2 to 5 μm, it is a region where light scattering occurs, In optical applications that require high transparency, there is a problem with transparency.

  Therefore, an object of the present invention is to provide a laminated film that eliminates the above-mentioned drawbacks and is excellent in transparency, scratch resistance, and antiblocking properties.

In order to solve the above problems, the laminated film of the present invention has the following constitution.
[I] A laminated film having a polyester layer and a resin layer, wherein at least one surface layer is a resin layer, and the resin layer included in the surface layer has a micro surface roughness (Ra-) determined by AFM (Atomic Force Microscope). A laminated film in which 1) is 1 nm or more and 20 nm or less, and a macro surface roughness (Ra-2) determined by a three-dimensional surface roughness meter is 1 nm or more and 50 nm or less.
[II] The laminated film according to [I], wherein the resin layer included in the surface layer has a macro surface roughness (Ra-2) determined by a three-dimensional surface roughness meter of 5 nm to 50 nm.
[III] The ratio (Ra-2 / Ra-1) of the micro surface roughness (Ra-1) to the macro surface roughness (Ra-2) of the resin layer in the surface layer is 3 or more and 30 or less, The laminated film according to [I] or [II].
[IV] The resin layer in the surface layer contains particles, and the particle abundance ratio in the range from the resin layer surface to the position of 10% of the resin layer thickness when the cross section in the thickness direction of the resin layer is observed ( Any one of [I] to [III] in which P-1) is larger than the particle abundance ratio (P-2) in the range from the position of 40% to 60% of the resin layer thickness from the resin layer surface The laminated film as described.
[V] Particle existence ratio (P-1) in the range from the resin layer surface to the position of 10% of the resin layer thickness, and the range from the position of 40% to the position of 60% of the resin layer thickness from the resin layer surface The laminated film according to [IV], in which the ratio (P-1 / P-2) of the particle abundance ratio (P-2) is 1.1 or more and 5.0 or less.
[VI] The laminated film according to [IV] or [V], in which the thickness (t) of the resin layer in the surface layer is 100 nm or more and 5000 nm or less.
[VII] The average particle size (d) of the particles contained in the resin layer in the surface layer is 1 nm or more and 100 nm or less, and the ratio (t) between the thickness (t) of the resin layer and the average particle size (d) of the particles / (D) is 2 or more and 1000 or less, The laminated film as described in [VI].
[VIII] The laminated film according to any one of [I] to [VII], in which a polyester layer and a resin layer are directly laminated.
[IX] A coating liquid containing a polyfunctional acrylic resin and particles is applied to at least one surface of the polyester film before crystal orientation is completed, and then the polyester film is stretched at least in a uniaxial direction, and the polyester film is heat-treated. The manufacturing method of the laminated | multilayer film in any one of [I]-[VIII] including the process of giving crystallinity and completing the crystal orientation of this polyester film.

  The laminated film of the present invention is excellent in transparency, scratch resistance, and blocking resistance, can improve transportability during the film processing step, and can suppress scratches on the film.

Hereinafter, the laminated film of the present invention will be described in detail.
The present invention is a laminated film having a polyester layer and a resin layer, wherein at least one surface layer is a resin layer, and the resin layer included in the surface layer is determined by an AFM (Atomic Force Microscope). It is a laminated film having a micro surface roughness (Ra-1) of 1 nm to 20 nm and a macro surface roughness (Ra-2) determined by a three-dimensional surface roughness meter of 1 nm to 50 nm.

  The micro surface roughness in the present invention represents the roughness of the surface of the resin layer measured in an area of 10 μm × 10 μm using an AFM (Atomic Force Microscope) manufactured by BRUKER. This micro surface roughness is a characteristic that affects the transparency and scratch resistance of the resin layer. Details of the measurement method will be described later.

  If the micro surface roughness of the resin layer on the surface layer of the laminated film is 1 nm or more and 20 nm or less, the resin layer does not have large irregularities that scatter light, so that the transparency of the laminated film can be improved. it can. Moreover, since the resin layer is hardly caught, the scratch resistance can be improved. More preferably, they are 1 nm or more and 15 nm or less. As a method for setting the micro surface roughness of the resin layer to 1 nm or more and 20 nm or less, a curable resin made of an acrylic resin having excellent fluidity is applied on a polyester layer having a micro surface roughness of 1 nm or more and 20 nm or less, and cured. There is a method of forming a resin layer by applying a resin, and a method of forming a resin layer by applying and curing a curable resin made of an acrylic resin containing nanoparticles having an average particle diameter of 100 nm or less. Among these, a method of applying and curing a curable resin made of an acrylic resin containing nanoparticles and excellent in fluidity is preferable from the viewpoint of excellent transparency.

  The macro surface roughness in the present invention represents the roughness of the surface of the resin layer measured in a 400 μm × 900 μm region using a three-dimensional roughness meter manufactured by Kosaka Laboratory. This macro surface roughness is a characteristic that affects the anti-blocking property and transparency of the resin layer. Details of the measurement method will be described later.

  When the macro surface roughness of the resin layer on the surface layer of the laminated film is in the region of 1 nm or more and 50 nm or less, the resin layer surface has a gentle concavo-convex structure, so that the anti-blocking property and transparency of the laminated film can be improved. it can. Preferably, they are 5 nm or more and 50 nm or less, More preferably, they are 5 nm or more and 30 nm or less. As a method of setting the macro surface roughness to 1 nm or more and 50 nm or less, a resin layer is formed using a curable resin made of an acrylic resin, and the resin layer contains particles having an average particle diameter larger than the film thickness of the resin layer. After applying a method or a curable resin made of an acrylic resin, a mold having an uneven shape is transferred to a coating film in which the acrylic resin is still uncured, and then the acrylic resin is cured to form a resin layer. There are a so-called nanoimprinting method and a method of giving fine stretching unevenness by applying a stretching treatment to the resin layer in a state where the acrylic resin is still uncured after applying a curable resin made of an acrylic resin. Among these, after applying a curable resin made of an acrylic resin, a smooth uneven structure is formed on the surface of the resin layer by fine stretching unevenness by applying a stretching process to the resin layer while the acrylic resin is still uncured. The method is preferable from the viewpoint of excellent antiblocking properties. Moreover, since it is a gentle uneven structure, it is preferable from the point which can suppress scattering of light and is excellent in transparency.

  In the laminated film of the present invention, the ratio (Ra-2 / Ra-1) of the micro surface roughness (Ra-1) and the macro surface roughness (Ra-2) of the resin layer in the surface layer is 3 or more. When it is 30 or less, the antiblocking property is improved, which is preferable. Preferably they are 5 or more and 25 or less, More preferably, they are 5 or more and less than 10. The ratio (Ra-2 / Ra-1) of the micro surface roughness (Ra-1) to the macro surface roughness (Ra-2) is achieved by adjusting the average particle size of the particles to be contained in the resin layer. be able to. Specifically, when the average particle diameter of the particles contained in the resin layer is increased, both the micro surface roughness (Ra-1) and the macro surface roughness (Ra-2) tend to increase. In particular, since the macro surface roughness (Ra-2) is a surface roughness in a wide field of view, when the average particle diameter of the particles to be contained in the resin layer is increased, it is compared with the micro surface roughness (Ra-1). Numbers tend to be larger.

  In the laminated film of the present invention, the resin layer in the surface layer contains particles, and the range from the resin layer surface to the position of 10% of the resin layer thickness when the cross section in the thickness direction of the resin layer is observed The particle abundance ratio (P-1) is preferably larger than the particle abundance ratio (P-2) in the range from the position of 40% to 60% of the resin layer thickness from the resin layer surface. By making (P-1) larger than (P-2), scratch resistance can be improved. When the ratio (P-1 / P-2) of (P-1) to (P-2) is 1.1 or more and 5.0 or less, scratch resistance is particularly improved, which is preferable. More preferably, it is 1.1 or more and 2.0 or less. As a method of making (P-1) larger than (P-2), as a particle to be contained in the resin layer, a method using particles having a small specific gravity or a modification of low surface energy components such as fluorine and silicone A method of arranging the particles on the air side using the prepared particles can be mentioned.

In addition, it is preferable that the laminated film of the present invention has a thickness (t) of the resin layer in the surface layer of 100 nm or more because the influence of the inhibition of curing of the resin layer surface layer can be suppressed and the scratch resistance is excellent. Although the upper limit of the thickness of a resin layer is not limited, 5000 nm or less is preferable at the point of transparency and productivity. Further, it is more preferably 300 nm or more and 3000 nm, and further preferably 500 nm or more and 1500 nm.
In the laminated film of the present invention, the average particle diameter (d) of the particles contained in the resin layer in the surface layer is 1 nm or more and 100 nm or less, and the thickness (t) of the resin layer and the average particle diameter of the nanoparticles ( When the ratio (t) / (d) to d) is 2 or more and 1000 or less, the diffusion of light by the particles is suppressed, and the transparency of the laminated film is improved, which is preferable. More preferably, it is 2 or more and 100 or less. The above range can be achieved by designing the film thickness of the resin layer and the average particle diameter of the particles contained in the resin layer.

[acrylic resin]
In the laminated film of the present invention, the resin layer included in the surface layer preferably contains an acrylic resin. In particular, an acrylic resin (A) and / or an acrylic resin (F) and / or an acrylic resin (G) described later are preferably included. By using the acrylic resin (A) and / or the acrylic resin (F) and / or the acrylic resin (G), the hardness of the resin layer surface can be improved while maintaining transparency. As a result, the scratch resistance of the laminated film can be improved.

  The acrylic resin (A) in the present invention is a cured composition composed of a monomer component (a) having an acryloyl group in the molecule. Among these, the monomer component (a) is preferably a polyfunctional acrylate having three or more acryloyl groups in the molecule. The polyfunctional acrylate is a monomer or oligomer having 3 (more preferably 4, more preferably 5 or more) or more (meth) acryloyl groups in one molecule. Examples of such a composition include a compound in which the hydroxyl group of a polyhydric alcohol having 3 or more alcoholic hydroxyl groups in one molecule is an esterified product of 3 or more (meth) acrylic acids. it can.

  Specific examples include pentaerythritol tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, dipentaerythritol tri (meth) acrylate, dipentaerythritol tetra (meth) acrylate, dipentaerythritol tetra (meth) acrylate, Dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate, trimethylolpropane tri (meth) acrylate, pentaerythritol triacrylate hexanemethylene diisocyanate urethane polymer and the like can be used. These monomers can be used alone or in combination of two or more. In addition, commercially available polyfunctional acrylic compositions include Mitsubishi Rayon Co., Ltd. (trade name “Diabeam” (registered trademark) series, etc.), Nagase Sangyo Co., Ltd. (trade name “Denacol” (registered trademark) series, etc.) Shinnakamura Co., Ltd .; (trade name “NK Ester” series, etc.), Dainippon Ink Chemical Industries, Ltd. (trade name “UNIDIC” (registered trademark), etc.), Toa Gosei Chemical Co., Ltd .; (“Aronix”) "(Registered trademark) series", Nippon Oil & Fats Co., Ltd .; ("Blemmer" (registered trademark) series, etc.), Nippon Kayaku Co., Ltd .; (trade name "KAYARAD" (registered trademark) series, etc.), Kyoeisha Chemical Co., Ltd. (Trade name “light ester” series, etc.) and the like, and these products can be used.

  In the present invention, it is preferable to use an acrylic resin (A) obtained by using an acrylic monomer component having an amide bond as the acrylic resin (A) because scratch resistance is particularly improved. The reason for this is estimated by the inventors as follows. When an acrylic monomer component having an acryloyl group is cured in the presence of oxygen atoms in the atmosphere, the radical polymerization reaction of the acryloyl group may be inhibited by the oxygen atoms in the atmosphere. Curing may not be sufficient, and scratch resistance may be inferior. When the acrylic monomer component containing an acryloyl group has an amide bond, the oxygen atom in the atmosphere interacts with the amide bond that has a high polarity, so inhibition of curing of the radical polymerization reaction of the acryloyl group by atmospheric oxygen is suppressed. As a result, it is estimated that the curing of the acrylic resin proceeds and the scratch resistance is particularly improved. Examples of the acrylic monomer component having an amide bond include a compound having a structure represented by the following (formula 1).

The acrylic resin (F) in the present invention is a resin having a monomer unit (f ₃ ) represented by (Formula 2).

(In (Formula 2), the R ₃ group represents a hydrogen atom or a methyl group. The R ₅ group represents a hydroxyl group, a carboxyl group, a tertiary amino group, a quaternary ammonium base, a sulfonic acid group, or phosphoric acid. Represents a group.)













When an acrylic resin having a monomer unit in which R ₅ group in (Formula 2) has no hydroxyl group, carboxyl group, tertiary amino group, quaternary ammonium group, sulfonic acid group, or phosphoric acid group is used, the acrylic resin As a result, the compatibility of the resin in the aqueous solvent becomes insufficient, and the acrylic resin (F) is non-uniformly present in the resin composition. As a result, a part of the resin layer has poor scratch resistance, which is not preferable.

In addition, the inorganic particles (B), which will be described later, aggregate or settle, or the inorganic particles (B) aggregate in the drying step, and as a result, the pressure on the resin layer at the time of rubbing is locally increased. Layers can be destroyed and scratched.

Furthermore, since such an aggregate is larger than the wavelength of visible light, a laminated film having good transparency may not be obtained. In order that the acrylic resin (F) in the present invention has the monomer unit (f ₃ ) represented by the following (formula 2), the (meth) acrylate monomer (f ₃ ′) represented by the (formula 3): Must be used as a raw material for polymerization.

Examples of the (meth) acrylate monomer (f ₃ ′) represented by (Formula 3) include the following compounds.

  As the (meth) acrylate monomer having a hydroxyl group, 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 2,3-dihydroxybutyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, polyethylene Examples include monoesterified products of polyhydric alcohols such as glycol mono (meth) acrylate and (meth) acrylic acid, or compounds obtained by ring-opening polymerization of ε-caprolapton on the monoesterified product, and particularly 2-hydroxyethyl ( (Meth) acrylate and 2-hydroxypropyl (meth) acrylate are preferred.

  Examples of the (meth) acrylate monomer having a carboxyl group include α, β-unsaturated carboxylic acids such as acrylic acid, methacrylic acid, itaconic acid, fumaric acid and maleic acid, or hydroxyalkyl (meth) acrylate and acid anhydrides. A half esterified product of Acrylic acid and methacrylic acid are particularly preferable.

  Tertiary amino group-containing monomers include N, N-, such as N, N-dimethylaminoethyl (meth) acrylate, N, N-diethylaminoethyl (meth) acrylate, N, N-dimethylaminopropyl (meth) acrylate, and the like. N, N-dialkylamino such as dialkylaminoalkyl (meth) acrylate, N, N-dimethylaminoethyl (meth) acrylamide, N, N-diethylaminoethyl (meth) acrylamide, N, N-dimethylaminopropyl (meth) acrylamide Examples thereof include alkyl (meth) acrylamide, and N, N-dimethylaminoethyl (meth) acrylate is particularly preferable.

  As the quaternary ammonium base-containing monomer, a monomer obtained by allowing a quaternizing agent such as epihalohydrin, benzyl halide, or alkyl halide to act on the above-mentioned tertiary amino group-containing monomer is preferable. Specifically, 2- (methacryloyloxy ) (Meth) acryloyloxyalkyltrialkylammonium salts such as ethyl trimethylammonium chloride, 2- (methacryloyloxy) ethyltrimethylammonium bromide, 2- (methacryloyloxy) ethyltrimethylammonium dimethyl phosphate, methacryloylaminopropyltrimethylammonium chloride, methacryloyl (Meth) acryloylaminoalkyltrialkylammonium salts such as aminopropyltrimethylammonium bromide, tetrabutylan Tetra (meth) acrylates such as bromide (meth) acrylate, and tri-alkyl benzyl ammonium (meth 9 acrylates such as trimethylbenzylammonium (meth) acrylate. In particular 2- (methacryloyloxy) ethyl trimethyl ammonium chloride are preferred.

  Examples of the sulfonic acid group-containing monomer include (meth) acrylamide-alkanesulfonic acid such as butylacrylamidesulfonic acid and 2-acrylamido-2-methylpropanesulfonic acid, or sulfoalkyl (meth) such as 2-sulfoethyl (meth) acrylate. An acrylate etc. are mentioned, 2-sulfoethyl (meth) acrylate is especially preferable.

Examples of the phosphoric acid group-containing acrylic monomer include acid phosphooxyethyl (meth) acrylate, and acid phosphooxyethyl (meth) acrylate is particularly preferable.
Among these, in particular, the acrylic resin (F) is a resin having the monomer unit (f ₃ ) represented by (Formula 2), and the R ₅ group in (Formula 2) is a hydroxyl group or a carboxyl group. The inorganic particles (B), which will be described later, have a higher adsorption force, can form a stronger film, and are preferable in terms of improving scratch resistance. As a method of using an acrylic resin (F) to have a macro surface roughness of 1 nm or more and 50 nm or less, a method of giving a fine stretching unevenness by subjecting the resin layer to a stretching treatment while the acrylic resin is still uncured. In this case, it is important that the thickness of the resin layer is 300 nm or more. By setting it as the said thickness, a fine extending | stretching nonuniformity expresses suitable height and can improve antiblocking property.

In this invention, it is preferable that content of the acrylic resin in a resin layer is 10 to 90 weight%, and the scratch resistance of a resin layer can be improved by setting it as this range.
In particular, when the acrylic resin (A) is used as the acrylic resin, the content of the acrylic resin (A) is more preferably 40% by weight or more and 90% by weight or less with respect to the entire resin layer. The content of the acrylic resin (A) is preferably 40% by weight to 80% by weight, more preferably 45% by weight to 70% by weight.
Moreover, when using acrylic resin (F) as an acrylic resin, it is preferable that content of the acrylic resin (F) in a resin layer is 20 to 80 weight% with respect to the whole resin layer, More preferably Is 40 wt% or more and 80 wt% or less, more preferably 45 wt% or more and 70 wt% or less.
In the present invention, the content in the resin layer represents the content in the solid content ([(mass of resin composition) − (mass of solvent)]) of the resin composition forming the resin layer.

[Inorganic particles]
The laminated film of the present invention preferably contains inorganic particles (B) in the resin layer included in the surface layer. Examples of the inorganic particles (B) include fine particles such as silicon oxide (silica), titanium oxide, aluminum oxide, zinc oxide, tin oxide, and zirconium oxide. Among these, fine particles of silicon oxide (silica), titanium oxide, aluminum oxide, zinc oxide, tin oxide, and zirconium oxide are preferable. These may be used alone or in combination of two or more.
Moreover, the inorganic particle (B) of the present invention is a composition (B-2) obtained by bonding the inorganic particle (B-1) and a resin component containing an acryloyl group, or the inorganic particle (B-1). It is preferable that it is a composition (B-3) which has an acrylic resin (G) in part or all of the surface of this. The bond here may be a covalent bond or a non-covalent bond (physical adsorption).

  As an example of the resin composition (B-2) formed by bonding inorganic particles (B-1) and a resin component containing an acryloyl group, the inorganic particles (B-1) and a resin component containing an acryloyl group are bonded (surface Modified). By combining the inorganic particles (B-1) and the resin component containing an acryloyl group, the inorganic particles can be prevented from falling off when a force is applied to the resin layer, and scratch resistance can be improved.

  As a specific method for bonding the inorganic particle (B-1) and the resin component containing an acryloyl group, the resin component containing an acryloyl group is a resin component having a silanol group, or a resin component that generates a silanol group by hydrolysis. It is preferable.

  Next, the resin component containing an acryloyl group contained in the resin composition (B-2) containing inorganic particles (B) will be described. The resin component containing an acryloyl group is a compound having an acryloyl group and a hydrolyzable silyl group. The hydrolyzable silyl group is a group that reacts with water to form a silanol group. For example, one or more methoxy groups, ethoxy groups, n-propoxy groups, isopropoxy groups, n-butoxy groups, etc. on silicon. An alkoxy group, an aryloxy group, an acetoxy group, an amino group, or a halogen primitive is bonded.

  Particles obtained by bonding inorganic particles (B-1) and resin components containing acryloyl groups are mixed with inorganic particles (B-1) and resin components (B-2) containing acryloyl groups having hydrolyzable silyl groups. It can be obtained by hydrolyzing and bonding the two. Since the particles obtained in this manner react with the acrylic resin (A), the inorganic particles are difficult to drop off when the resin layer is rubbed, so that the scratch resistance is excellent.

  The resin component ratio including the inorganic particles (B-1) and the acryloyl group contained in the resin composition (B-2) containing the inorganic particles (B) is a resin including the inorganic particles (B-1) and the acryloyl groups. When the component is 100 parts by weight, the resin component (B-2) containing an acryloyl group is preferably 0.1 parts by weight or more and 50 parts by weight or less. By setting it as this range, it is possible to achieve both scratch resistance, transparency, and anti-blocking properties without dropping the inorganic particles. When the resin component containing an acryloyl group exceeds 50 parts by weight, the density of the inorganic particles contained in the resin layer is lowered, and scratch resistance may be deteriorated.

In addition, the composition (B-3) having an acrylic resin (G) on part or all of the surface of the inorganic particles (B-1) of the present invention means part or all of the surface of the inorganic particles (B-1). Furthermore, it is preferable that the particles have the acrylic resin (G) described above.
The acrylic resin (G) here is a resin having a monomer unit (g ₁ ) represented by (Formula 4) and a monomer unit (g ₂ ) represented by (Formula 5).

(In (Formula 4), R ₁ group represents a hydrogen atom or a methyl group. N represents an integer of 9 or more and 34 or less.)

(In (Formula 5), the R ₂ group represents a hydrogen atom or a methyl group. The R ₄ group represents a group containing two or more saturated carbocycles).

Here, the acrylic resin (G) in the present invention is preferably a resin having a monomer unit (g ₁ ) represented by (Formula 4). Since the acrylic resin (G) has the monomer unit (g ₁ ) represented by (Formula 4), the surface energy of the resin layer is reduced, so that the coefficient of friction applied to the resin layer when the rubbing treatment is performed is small. Thus, the scratch resistance can be improved.

  Moreover, in (Formula 4), when an acrylic resin having a monomer unit with n of less than 9 is used, the dispersibility of the inorganic particles (B) in the aqueous solvent (details of the aqueous solvent will be described later) is unstable. It becomes. When an acrylic resin having a monomer unit having n of less than 9 in (Formula 4) is used, the inorganic particles (B) aggregate or settle in the resin composition, or the inorganic particles (B) aggregate in the drying step. Sometimes. As a result, the transparency of the laminated film may be impaired, or the scratch property may be inferior. On the other hand, the acrylic resin having a monomer unit in which n exceeds 34 in (Formula 4) has extremely low solubility in an aqueous solvent, and therefore aggregation of the acrylic resin is likely to occur in the aqueous solvent. Since such an aggregate is larger than the wavelength of visible light, a laminated film with good transparency may not be obtained.

In order that the acrylic resin (G) in the present invention has the monomer unit (g ₁ ) represented by (formula 4), the (meth) acrylate monomer (g ₁ ′) represented by the following (formula 6): Must be used as a raw material for polymerization.

The (meth) acrylate monomer (g ₁ ′) is preferably a (meth) acrylate monomer represented by an integer of 9 to 34 in the formula (6), more preferably 11 to 32 (meth). An acrylate monomer, more preferably a (meth) acrylate monomer of 13 or more and 30 or less.

The (meth) acrylate monomer (g ₁ ′) is not particularly limited as long as it is a (meth) acrylate monomer in which n in (Formula 6) is 9 or more and 34 or less. Specifically, decyl (meth) acrylate, dodecyl ( (Meth) acrylate, tridecyl (meth) acrylate, tetradecyl (meth) acrylate, 1-methyltridecyl (meth) acrylate, hexadecyl (meth) acrylate, octadecyl (meth) acrylate, eicosyl (meth) acrylate, docosyl (meth) acrylate, Tetracosyl (meth) acrylate, triacontyl (meth) acrylate, etc. are mentioned, and especially dodecyl (meth) acrylate and tridecyl (meth) acrylate are preferable. These may be used alone or in a mixture of two or more.

Further, the acrylic resin (G) in the present invention, the is preferably a resin having a monomer unit represented by formula ₍₅₎ (g 2). When the acrylic resin (G) has the monomer unit (g ₂ ) represented by (Formula 5), the resin layer becomes rigid due to the steric hindrance of the saturated carbocyclic ring, and the scratch resistance can be improved. .

  Moreover, in (Formula 5), when an acrylic resin having a monomer unit containing only one saturated carbocycle is used, the function as steric hindrance is insufficient, and the inorganic particles (B) are aggregated or formed in the resin composition. It may settle or the inorganic particles (B) may aggregate in the drying step.

Since such an aggregate is larger than the wavelength of visible light, a laminated film with good transparency may not be obtained. In order that the acrylic resin (G) in the present invention has the monomer unit (g ₂ ) represented by (Formula 5), the (meth) acrylate monomer (g ₂ ′) represented by the following (Formula 7): Must be used as a raw material for polymerization.

As the (meth) acrylate monomer (g ₂ ′) represented by (Formula 7), a bridged condensed cyclic formula (having a structure in which two or more rings each share two atoms and are bonded) And various cyclic structures such as spirocyclic (having a structure in which two cyclic structures are shared by sharing one carbon atom), specifically, compounds having bicyclo, tricyclo, tetracyclo groups, etc. Of these, (meth) acrylates containing a bicyclo group are particularly preferred from the viewpoint of compatibility with the binder.

Examples of the (meth) acrylate containing the bicyclo group include isobornyl (meth) acrylate, bornyl (meth) acrylate, dicyclopentanyl (meth) acrylate, dicyclopentenyl (meth) acrylate, adamantyl (meth) acrylate, and dimethyladamantyl (Meth) acrylate etc. are mentioned, and isobornyl (meth) acrylate is particularly preferred.
By having the acrylic resin (G) on the surface of the inorganic particles (B-1), the interfacial adhesion between the inorganic particles (B-1) and the acrylic resin (G) in the resin layer becomes strong, and thus the rubbing treatment is performed. Dropping of particles during application is suppressed, and scratch resistance is excellent. Furthermore, aggregation of the inorganic particles (B) during the drying process can be suppressed, and the micro surface roughness and macro surface roughness of the resin layer can be set within a predetermined range.

  In addition, although the manufacturing method of inorganic particle (B-1) is not specifically limited, The method of surface-treating inorganic particle (B-1) with an acrylic resin (G) etc. can be mentioned, Specifically Is exemplified by the following methods (i) to (iv). In the present invention, the surface treatment refers to a treatment for adsorbing and adhering the acrylic resin (G) to all or a part of the surface of the inorganic particles (B-1).

  (I) A method in which a mixture prepared by previously mixing inorganic particles (B-1) and an acrylic resin (F) is added to a solvent and then dispersed.

  (Ii) A method in which the inorganic particles (B-1) and the acrylic resin (G) are sequentially added and dispersed in a solvent.

  (Iii) A method in which the inorganic particles (B-1) and the acrylic resin (G) are previously dispersed in a solvent and the obtained dispersion is mixed.

  (Iv) A method of adding the acrylic resin (G) to the obtained dispersion after dispersing the inorganic particles (B-1) in a solvent.

  The intended effect can be obtained by any of these methods.

  Further, as a dispersion apparatus, a dissolver, a high speed mixer, a homomixer, a mixer, a ball mill, a roll mill, a sand mill, a paint shaker, an SC mill, an annular mill, a pin mill, and the like can be used.

  As a dispersion method, the rotating shaft is rotated at a peripheral speed of 5 to 15 m / s using the above-described apparatus. The rotation time is 5 to 10 hours.

  Further, it is more preferable to use dispersed beads such as glass beads at the time of dispersion from the viewpoint of improving dispersibility. The bead diameter is preferably 0.05 to 0.5 mm, more preferably 0.08 to 0.5 mm, and particularly preferably 0.08 to 0.2 mm.

  The method of mixing and stirring can be performed by shaking the container by hand, using a magnetic stirrer or stirring blade, irradiating ultrasonic waves, vibrating and dispersing.

  In addition, the presence or absence of adsorption | suction and adhesion of the acrylic resin (G) to all or a part of the surface of the inorganic particles (B-1) can be confirmed by the following analysis method. An object to be measured (for example, a composition (B-3) containing inorganic particles (B-1)) is centrifuged with a Hitachi tabletop ultracentrifuge (manufactured by Hitachi Koki Co., Ltd .: CS150NX) (number of revolutions 3, 0000 rpm, separation time 30 minutes), the inorganic particles (B-1) (and the acrylic resin (G) adsorbed on the surface of the inorganic particles (B-1)) were allowed to settle, the supernatant was removed, and the sediment was removed. Concentrate to dryness. The concentrated and dried precipitate is analyzed by X-ray photoelectron spectroscopy (XPS), and the presence or absence of the acrylic resin (F) on the surface of the inorganic particles (B-1) is confirmed. When it is confirmed that 1% by mass or more of the acrylic resin (G) is present on the surface of the inorganic particles (B-1) with respect to 100% by mass in total of the inorganic particles (B-1), the inorganic particles (B It is assumed that the acrylic resin (G) is adsorbed and adhered to the surface of -1).

  Here, the number average particle diameter of the inorganic particles (B-1) will be described. Here, the number average particle diameter refers to the particle diameter determined by a transmission electron microscope (TEM). The magnification is 500,000 times, and the outer diameter of 10 particles existing on the screen is the number average particle diameter obtained by measuring a total of 100 particles for 10 fields of view. Here, the outer diameter means the maximum diameter of the particle (that is, the longest diameter of the particle and indicates the longest diameter in the particle). Similarly, in the case of a particle having a cavity inside, the maximum diameter of the particle is also defined. Represent.

  When the number average particle diameter of the inorganic particles (B) is smaller than 1 nm, the van der Waals force between the particles increases, and as a result of aggregation of the particles, light scattering may occur and transparency may be lowered. On the other hand, when the number average particle diameter of the inorganic particles (B) is larger than 100 nm, from the viewpoint of transparency, there is a possibility that the light becomes a starting point for scattering and the transparency is deteriorated. Further, the filling of the inorganic particles in the coating film may not sufficiently proceed, and the scratch resistance may be lowered. Therefore, the inorganic particles (B) preferably have a number average particle diameter of 5 nm or more and 100 nm or less. Preferably they are 10 nm or more and 80 nm or less, More preferably, they are 20 nm or more and 60 nm or less.

In the present invention, the inorganic particles (B) contained in the resin layer (X) are preferably in the range of 10 to 50 parts by weight, more preferably in the range of 15 to 50 parts by weight with respect to 100 parts by weight of the acrylic resin (A). Is more preferable. By setting it as the said range, transparency and scratch resistance can be made compatible.
In the present invention, the inorganic particles (B) contained in the resin layer (X) are preferably in the range of 50 to 200 parts by weight with respect to 100 parts by weight in total of the acrylic resin (F) and the acrylic resin (G). More preferably, the range of 100 to 200 parts by weight is more preferable. By setting it as the said range, transparency and scratch resistance can be made compatible.

[Polyester layer]
In the laminated film of the present invention, a polyester layer used as a base material layer (hereinafter, a polyester layer used as a base material layer may be referred to as a polyester film) will be described. First, polyester is a general term for polymers having an ester bond in the main chain, and includes ethylene terephthalate, propylene terephthalate, ethylene-2,6-naphthalate, butylene terephthalate, propylene-2,6-naphthalate, ethylene-α, β. One having at least one component selected from -bis (2-chlorophenoxy) ethane-4,4'-dicarboxylate and the like can be preferably used.

  The polyester film using the polyester is preferably biaxially oriented. A biaxially oriented polyester film is generally an unstretched polyester sheet or film that is stretched about 2.5 to 5 times in the longitudinal direction and in the width direction perpendicular to the longitudinal direction, and then subjected to heat treatment to produce crystals. The alignment is completed, and it indicates a biaxial alignment pattern by wide-angle X-ray diffraction. When the polyester film is biaxially oriented, thermal stability, particularly dimensional stability and mechanical strength are sufficient, and flatness is also good.

  In the polyester film, various additives such as antioxidants, heat stabilizers, weathering stabilizers, ultraviolet absorbers, organic lubricants, pigments, dyes, organic or inorganic fine particles, fillers, antistatic agents. An agent, a nucleating agent, etc. may be added to such an extent that the properties are not deteriorated.

  The thickness of the polyester film is not particularly limited and is appropriately selected depending on the application and type, but is preferably preferably 10 to 500 μm, more preferably 15 to 250 μm from the viewpoint of mechanical strength, handling properties, and the like. Most preferably, it is 20-100 micrometers. The polyester film may be a composite film obtained by coextrusion or a film obtained by bonding the obtained film by various methods.

[Production method of resin layer]
Examples of the production method of the resin layer of the laminated film of the present invention are shown below, but the materials, amounts used, ratios, treatment details, treatment procedures, etc. shown below may be changed as appropriate without departing from the spirit of the present invention. it can. Therefore, the scope of the present invention should not be construed as being limited by the examples shown below.

  When the resin layer of the present invention contains an acrylic resin (A) and / or an acrylic resin selected from at least one of the acrylic resins (F) and inorganic particles (B), the transparency, scratch resistance, It is excellent in anti-blocking property and is preferable.

  Further, in the resin layer, if necessary, other compounds than (A), (F) and (B), for example, polymer resins such as polyester resins, acrylic resins and urethane resins, carbodiimide compounds, oxazoline compounds , Aziridine compounds, titanate coupling agents such as titanium chelates, and methylolated or alkylolated melamine compounds may be included. Various additives such as organic lubricants, organic or inorganic fine particles, antistatic agents and the like may be added to such an extent that the characteristics are not deteriorated.

  In particular, as other compounds other than (A), (F) and (B), an oxazoline compound and / or a melamine compound are preferable, and a melamine compound is particularly preferable.

  Examples of melamine compounds include melamine, methylolated melamine derivatives obtained by condensing melamine and formaldehyde, compounds partially or completely etherified by reacting methylolated melamine with a lower alcohol, and mixtures thereof. Can be used. Specifically, a compound having a triazine and a methylol group is particularly preferable. Further, the melamine compound may be a monomer or a condensate composed of a dimer or higher polymer, or a mixture thereof. As the lower alcohol used for etherification, methyl alcohol, ethyl alcohol, isopropyl alcohol, n-butanol, isobutanol and the like can be used. The group has an imino group, a methylol group, or an alkoxymethyl group such as a methoxymethyl group or a butoxymethyl group in one molecule, and an imino group type methylated melamine resin, a methylol group type melamine resin, or a methylol group type methyl group. Melamine resin, fully alkyl methylated melamine resin, and the like. Of these, methylolated melamine resins are most preferred. Further, an acidic catalyst such as p-toluenesulfonic acid may be used in order to accelerate the thermal curing of the melamine compound.

  When such a melamine compound is used, not only is the scratch resistance improved due to the coating film hardness being increased due to the self-condensation of the melamine compound, but the reaction between the hydroxyl group or carboxylic group contained in the acrylic resin and the melamine compound proceeds. Thus, a stronger resin layer can be obtained, and a film having excellent scratch resistance can be obtained. Furthermore, due to the effect of suppressing the dropout of the inorganic particles (B) in the resin layer, it is possible to prevent the protrusions of the concavo-convex structure necessary for the antiblocking property from being scraped.

[Production method of laminated film]
The production method of the laminated film of the present invention will be described below with reference to examples, but the materials, amounts used, ratios, treatment contents, treatment procedures, etc. shown below may be changed as appropriate without departing from the spirit of the present invention. it can. Therefore, the scope of the present invention should not be construed as being limited by the examples shown below.

In the laminated film of the present invention, an acrylic monomer (a) constituting an acrylic resin (A) and a resin composition (b) containing inorganic particles (B) are applied onto a polyester film, and the resin composition contains a solvent. When it contains, it can obtain by forming a resin layer on a polyester film by drying a solvent.
When the acrylic monomer (f) constituting the acrylic resin (F) and the resin composition (b) containing the inorganic particles (B) are applied onto the polyester film, and the resin composition contains a solvent, It can be obtained by forming a resin layer on the polyester film by drying the solvent.

  Moreover, in this invention, when making a resin composition contain a solvent, it is preferable to use an aqueous solvent as a solvent. This is because the use of the aqueous solvent can suppress the rapid evaporation of the solvent in the drying step and can form a uniform composition layer, and is excellent in terms of environmental load.

  Here, the aqueous solvent is soluble in water or water and alcohols such as methanol, ethanol, isopropyl alcohol and butanol, ketones such as acetone and methyl ethyl ketone, and glycols such as ethylene glycol, diethylene glycol and propylene glycol. Is an organic solvent mixed in an arbitrary ratio.

  Moreover, in this invention, when using an aqueous solvent, the acrylic monomer (a) which comprises an acrylic resin (A), the acrylic monomer (f) which comprises an acrylic resin (F), and an inorganic particle (B) are contained. It is preferable to apply an aqueous coating material containing the resin composition (b). This is applied as a water-based coating. Compared with organic solvent-based coatings, the water-dispersing agent or emulsifier is arranged on the surface of the coating film when the solvent is dry. This is because the inhibition of curing is suppressed and the resin layer is excellent in scratch resistance even when the resin layer is thin.

  In addition, as a method of forming the acrylic monomer (a) constituting the acrylic resin (A) and the resin composition (b) containing the inorganic particles (B) into an aqueous coating, acrylic constituting the acrylic resin (A) is used. Examples thereof include a method of incorporating a hydrophilic group such as carboxylic acid and sulfonic acid into the monomer (a) and the resin composition (b) containing the inorganic particles (B), and a method of emulsifying using an emulsifier.

  The application method of the resin composition to the polyester film is preferably an in-line coating method. The in-line coating method is a method of applying in the process of manufacturing a polyester film. Specifically, it refers to a method of coating at any stage from melt extrusion of a polyester resin to biaxial stretching followed by heat treatment and winding up, and is generally substantially non-obtainable after melt extrusion and rapid cooling. Crystalline unstretched (unoriented) polyester film (A film), then uniaxially stretched (uniaxially oriented) polyester film (B film) stretched in the longitudinal direction, or biaxially before heat treatment stretched further in the width direction It is applied to any one of stretched (biaxially oriented) polyester film (C film).

  In the present invention, the resin composition is applied to the polyester film of any one of the A film and the B film before the crystal orientation is completed, and then the polyester film is stretched in a uniaxial direction or a biaxial direction. It is preferable to employ a method in which a heat treatment is performed at a temperature higher than the boiling point to complete the crystal orientation of the polyester film and a resin layer is provided. According to this method, the polyester film can be formed and the resin composition can be applied and dried (that is, the resin layer is formed) at the same time. Moreover, it is easy to make the thickness of the resin layer thinner in order to perform stretching after coating.

  Especially, the method of apply | coating a resin composition to the film (B film) uniaxially stretched to the longitudinal direction, and extending | stretching to the width direction after that and heat-processing is excellent. After applying to an unstretched film, the stretching process is less than once compared to the method of biaxial stretching, so it is difficult to cause defects or cracks in the composition layer due to stretching, and a composition layer excellent in transparency and smoothness This is because it can be formed.

  Furthermore, by providing the resin layer by an in-line coating method, the resin layer can be stretched before the resin layer is completely cured, and a gentle uneven structure can be easily formed. Furthermore, the concavo-convex structure can form a more prominent concavo-convex structure when the thickness of the resin layer is 300 nm or more. As a result, the anti-blocking property of the film can be expressed without forming a large protrusion on the resin layer. This gentle concavo-convex structure means that the macro surface roughness measured using a three-dimensional roughness meter manufactured by Kosaka Laboratory is 5 to 50 nm.

  In the present invention, the resin layer is preferably provided by an in-line coating method from the various advantages described above. Here, as a method for applying the resin composition to the polyester film, any known method such as a bar coating method, a reverse coating method, a gravure coating method, a die coating method, or a blade coating method can be used.

  Therefore, the best method for forming a resin layer in the present invention is a method in which a resin composition using an aqueous solvent is applied on a polyester film by using an in-line coating method, dried and heat-treated. More preferably, the resin composition is in-line coated on the uniaxially stretched B film. In the method for producing a laminated film of the present invention, drying can be performed in a temperature range of 80 to 130 ° C. in order to complete the removal of the solvent of the resin composition. Moreover, heat processing can be implemented in a 160-240 degreeC temperature range in order to complete the crystal orientation of a polyester film, to complete the thermosetting of a resin composition, and to complete formation of a resin layer.

  Next, although the production method of the laminated film of the present invention will be described by taking as an example a case where a polyethylene terephthalate (hereinafter referred to as PET) film is used as the polyester film, it is not limited thereto. First, PET pellets are sufficiently vacuum-dried, then supplied to an extruder, melt extruded into a sheet at about 280 ° C., and cooled and solidified to produce an unstretched (unoriented) PET film (A film). This film is stretched 2.5 to 5.0 times in the longitudinal direction with a roll heated to 80 to 120 ° C. to obtain a uniaxially oriented PET film (B film). The resin composition of the present invention prepared at a predetermined concentration is applied to one side of the B film.

  At this time, surface treatment such as corona discharge treatment may be performed on the coated surface of the PET film before coating. By performing surface treatment such as corona discharge treatment, the wettability of the resin composition to the PET film is improved, the resin composition is prevented from being repelled, and a resin layer having a uniform coating thickness can be formed. After coating, the edge of the PET film is held with a clip and guided to a heat treatment zone (preheating zone) of 80 to 130 ° C., and the solvent of the resin composition is dried. After drying, the film is stretched 1.1 to 5.0 times in the width direction. Subsequently, it is guided to a heat treatment zone (heat setting zone) at 160 to 240 ° C., and heat treatment is performed for 1 to 30 seconds to complete crystal orientation.

  In this heat treatment step (heat setting step), a relaxation treatment of 3 to 15% may be performed in the width direction or the longitudinal direction as necessary. The laminated film thus obtained becomes a laminated film excellent in transparency, scratch resistance and antiblocking properties.

  In the laminated film of the present invention, an intermediate layer may be provided between the resin layer and the polyester layer. However, when the intermediate layer is provided, when the film laminated with the intermediate layer is wound, In the process until the resin layer is provided, the film may be damaged. Therefore, in this invention, it is preferable that the resin layer and the polyester layer are laminated | stacked directly.

[Characteristic measurement method and effect evaluation method]
The characteristic measurement method and effect evaluation method in the present invention are as follows.

(1) Haze (transparency)
The haze is measured in a normal state (23 ° C., relative humidity 50%) after leaving the laminated film sample for 40 hours, and using a turbidimeter “NDH5000” manufactured by Nippon Denshoku Industries Co., Ltd., JIS K 7136 “Transparent The method was in accordance with “How to Obtain Haze of Material” (2000 version). In addition, it measured by irradiating light from the surface side on which the resin layer of the sample was laminated. Ten samples each having a square with a side of 50 mm were prepared, and the average value obtained by measuring once each 10 times in total was used as the haze value of the sample.
Further, the transparency was evaluated by a four-step evaluation based on the haze value. X is a practically problematic level, Δ is a practical level, and those of A and S were considered good.
S: 0.6% or less A: exceeding 0.6% and 1.0% or less B: exceeding 1.0% and not more than 2.0% C: exceeding 2.0%

(2) Scratch resistance Steel wool (Bonster # 0000, manufactured by Nippon Steel Wool Co., Ltd.) was rubbed 10 reciprocally at a load of 200 g / cm ² and visually checked for the presence of scratches on the surface of the laminated film. Evaluation was performed.
S: No scratch A: 1-5 scratches B: 6-10 scratches C: 11 or more scratches

(3) The resin layers of the antiblocking laminated film were bonded together, pressurized with a load of 1 kg / cm2, and stored at room temperature for 24 hours. Thereafter, the presence or absence of blocking (sticking) of the film when peeling the laminated film was visually confirmed, and the following evaluation was performed.
A: Without blocking B: With partial blocking C: With full blocking (4) Adhesiveness 100 pieces of 1 mm ² crosscuts are put on the resin layer side of the laminated film, and “Cello Tape” (registered trademark) (manufactured by Nichiban Co., Ltd.) , CT405AP) was applied and pressed with a load of 1.5 kg / cm ² with a hand roller, and then rapidly peeled in the direction of 90 degrees with respect to the laminated film. Adhesiveness was evaluated in four stages according to the number of remaining lattices. The evaluation was performed using an average value obtained 10 times. C is a practically problematic level, B is a practical level, and A and S are good.
S: 90 to 100 remaining A: 80 to 89 remaining B: 50 to 79 remaining C: 0 to less than 50 remaining.

(5) Number average particle diameter of particles contained in resin layer The number average particle diameter of particles contained in the resin layer was determined by observing the cross-sectional structure of the laminated film with a transmission electron microscope (TEM). The magnification was set to 500,000, and the outer diameter of 10 particles existing in the screen was measured for a total of 100 particles for 10 fields of view, and the average particle size was determined. When 10 particles do not exist in the screen, observe another part under the same conditions, measure the outer diameter of the particles present in the screen, and measure the outer diameter of 100 particles in total. Averaged. Here, the outer diameter means the maximum diameter of the particle (that is, the longest diameter of the particle and indicates the longest diameter in the particle). Similarly, in the case of a particle having a cavity inside, the maximum diameter of the particle is also defined. Represent.

(6) Film thickness of resin layer The thickness of the resin layer on a polyester film was measured by observing a cross section using a transmission electron microscope (TEM). As for the thickness of the resin layer, the thickness of the resin layer was read from an image taken with a TEM at a magnification of 100,000 times. A total of 20 resin layer thicknesses were measured and taken as an average value.

Sample preparation: RuO ₄ staining FIB method
SMI3200SE (manufactured by SIINT)
FB-2000A II Micro Sampling System (manufactured by Hitachi, Ltd.)
Strata400S (manufactured by FEI)
Observation device: High-resolution transmission electron microscope (H9000 UHR II manufactured by Hitachi)
Observation conditions: acceleration voltage 300 kV
(7) Micro surface roughness (Ra-1)
In Bscander AFM (Atomic Force Microscope) “Dimension Icon Scan Asyst” Scan Asist Air mode, the resin layer side surface of the laminated film has a measuring range of 10 μm × 10 μm, a measuring line number of 512, and a measuring rate of 1. The arithmetic average roughness (Ra) was calculated by the method defined in JIS-B-0601-1994 from the surface information obtained by measurement at 0 Hz. Specifically, “NanoScope Analysis” is used as software, “3rd” of “Flatten Order” is selected, and a three-dimensional swell process is performed. Thereafter, “Roughness” is selected, and the numerical value described in “Image Ra” on the screen is set as the arithmetic average roughness. In addition, the measurement was made 10 times in total, and the average value of a total of 8 data excluding the maximum value and the minimum value was obtained as the arithmetic average roughness (Ra) of the sample as the micro surface roughness (Ra-1).

(8) Macro surface roughness (Ra-2)
The resin layer side surface of the laminated film is measured by a stylus method under the following conditions using a three-dimensional surface roughness meter (manufactured by Kosaka Laboratory, ET-4000A), and the resulting centerline surface roughness (SRa) is measured. It calculated | required as macro surface roughness (Ra-2).
In addition, the measurement changed the sampling place, measured 10 samples, and employ | adopted the average value of 8 points | pieces except the maximum value and the minimum value.
Needle diameter 0.5 (μmR)
Needle pressing pressure 100 (μN)
Vertical magnification 20000 (times)
Low frequency CUT OFF 200 (μm)
Wide area CUT OFF 0 (μm)
Measurement speed 100 (μm / s)
Measurement interval X direction 1 (μm), Y direction 5 (μm)
Number of records 81 lines Hysteresis width 0.000 (μm)
Reference area 1 mm in the X direction and 0.4 mm in the Y direction.
(9) Particle abundance ratio With respect to the cross-sectional TEM image (magnification of 100,000 times) obtained by the method described in (6), software (image processing software ImageJ / developer: National Satellite Institute (NIH)) The white balance was adjusted so that the brightest part and the darkest part fit within an 8-bit tone curve. Furthermore, the contrast was adjusted so that the black part (inorganic particles) could be clearly identified.

  Next, for the obtained image, the ratio of the black part in the range from the resin layer surface to the position of 10% of the resin layer thickness is the particle abundance ratio (P-1), and the position of 40% of the resin layer thickness from the resin layer surface. To 60% of the position of the black part was defined as the particle abundance ratio (P-2).

Reference Example 1 Emulsion (EM-5) containing acrylic monomer (a-1) constituting acrylic resin (A) component
Into a flask equipped with a stirrer, 100 parts by weight of acrylic monomer (a-1) (dipentahexaacrylate (KAYARAD DPHA manufactured by Nippon Kayaku Co., Ltd.)), polyoxyethylene polycyclic phenyl ether sulfate (Japanese emulsifier) as an emulsifier 79 parts by weight of a 10% by weight aqueous solution of New Coal 707SF), 2.1 parts by weight of polyoxyethylene lauryl ether (Emulgen 104P manufactured by Kao Corporation), and 128.9 parts by weight of ion-exchanged water were added and mixed. . Then, while cooling in an ice bath, ultrasonic irradiation for 120 seconds was performed 3 times using an ultrasonic disperser (UH-600S manufactured by SMT) to obtain an emulsion.

  Next, the emulsion was refined with a high-pressure homogenizer (Microfluidizer M110Y manufactured by Mizuho Kogyo Co., Ltd.) under a pressure of 70 MPa to obtain an emulsion (EM-5) containing acrylic monomer (a-1). The solid content concentration of the emulsion (EM-5) is 30% by weight.

<Reference Example 2> Resin composition (b-2) containing inorganic particles (B)
While stirring 221 parts by weight of mercaptopropyltrimethoxysilane, 1 part of dibutyltin dilaurate and methyl ethyl ketone, 222 parts by weight of isophorone diisocyanate and 30 parts by weight of perfluoropolyether diol (FLUOROLINK D10H manufactured by Solvay Solexis) are stirred. After dropwise addition at 50 ° C. over 1 hour, the mixture was stirred with heating at 70 ° C. for 3 hours. By adding 549 parts by weight of a polyfunctional acrylate (“NK Ester” A-TMM-3LM-N manufactured by Shin-Nakamura Chemical Co., Ltd.) over 1 hour at 30 ° C. and then stirring at 60 ° C. over 10 hours. Thus, an acryloyl group-containing particle modifier (b-1) is obtained.

  Subsequently, the obtained acryloyl group-containing particle modifier (b-1) 50 parts by weight, colloidal silica water dispersion (Nissan Chemical "Snow Tech OL" particle size 40 nm) 50 parts by weight, ion-exchanged water 0.12 parts by weight , And 0.01 parts by weight of p-hydroxyphenyl monomethyl ether were stirred at 60 ° C. for 4 hours, 1.36 parts by weight of orthoformate methyl ester was added, and the mixture was further heated and stirred at the same temperature for 1 hour. A resin composition (b-2) containing an acryloyl group containing inorganic particles (B) was obtained.

Reference Example 3 Emulsion (EM-1) containing acrylic monomer (a-1) constituting acrylic resin (A) component and resin composition (b-2) containing inorganic particles (B)
Resin composition containing acryloyl group containing acrylic monomer (a-1) (dipentahexaacrylate (KAYARAD DPHA) manufactured by Nippon Kayaku Co., Ltd.) and inorganic particles (B) in a flask equipped with a stirrer (B-2) 20 parts by weight, 79 parts by weight of a 10% aqueous solution of polyoxyethylene polycyclic phenyl ether sulfate salt (New Coal 707SF manufactured by Nippon Emulsifier Co., Ltd.) as an emulsifier, and polyoxyethylene lauryl ether (manufactured by Kao Corporation) Emulgen 104P) (2.1 parts by weight) was added, and 128.9 parts by weight of ion-exchanged water was added and mixed by stirring. Then, while cooling in an ice bath, ultrasonic irradiation for 120 seconds was performed 3 times using an ultrasonic disperser (UH-600S manufactured by SMT) to obtain an emulsion.

  Next, the above emulsion is refined with a high pressure homogenizer (Microfluidizer M110Y manufactured by Mizuho Kogyo Co., Ltd.) under a pressure of 70 MPa, and the acrylic monomer (a-1) and the inorganic particles (A) constituting the acrylic resin (A) component ( An emulsion (EM-1) containing the resin composition (b-2) containing B) was obtained. The solid content concentration of the emulsion (EM-1) is 30% by weight.

Reference Example 4 Emulsion (EM-2) containing amide bond-containing acrylic monomer (a-2) constituting acrylic resin (A) component and resin composition (b-2) containing inorganic particles (B) )
In a flask equipped with a stirrer, 0.06 g of 2,6-di-t-butyl-p-cresol, 15 g of ethylene diol, and 12 g of 2.4-tolylene diisocyanate (“TOLDY-100” manufactured by Mitsui Chemicals Polyurethanes) And after adding methyl ethyl ketone and adding 0.080g of dibutyltin dilaurate, it heated up to 60 degreeC and heated for 1.5 hours. Next, the reaction mixture was cooled in a water bath, and 35 g of tetramethylolmethane triacrylate (“NK Ester” A-TMM-3LM-N manufactured by Shin-Nakamura Chemical Co., Ltd.) was diluted with methyl ethyl ketone to a solid content concentration of 50% by mass. Things were added. The temperature was raised to 60 ° C. and heated for 4 hours to obtain an acrylic monomer (a-2) represented by the general formula 1.
A resin containing 30 parts of dipentahexaacrylate (KAYARAD DPHA manufactured by Nippon Kayaku Co., Ltd.), 50 parts by weight of acrylic monomer (a-2) represented by the following formula 1, and inorganic particles (B) in a flask equipped with a stirrer 20 parts by weight of the composition (b-2), 79 parts by weight of a 10% aqueous solution of polyoxyethylene polycyclic phenyl ether sulfate (Nippon Emulsifier Co., Ltd. New Coal 707SF) as an emulsifier, and polyoxyethylene lauryl ether (Kao Corporation) ) Emulgen 104P) 2.1 parts by weight and 128.9 parts by weight of ion-exchanged water were added and stirred and mixed. Then, while cooling in an ice bath, ultrasonic irradiation for 120 seconds was performed 3 times using an ultrasonic disperser (UH-600S manufactured by SMT) to obtain an emulsion.

Next, the above emulsion was refined with a high-pressure homogenizer (Microfluidizer M110Y manufactured by Mizuho Kogyo Co., Ltd.) under a pressure of 70 MPa to obtain an emulsion (EM-2) containing acrylic monomer (a-3). The solid content concentration of the emulsion (EM-2) is 30% by weight.
(Formula 1) Acrylic monomer (a-2)

Reference Example 5 An emulsion (EM-3) containing an amide bond-containing acrylic monomer (a-3) constituting the acrylic resin (A) component and a resin composition (b-2) containing inorganic particles (B) )
To a flask equipped with a stirrer, 0.024 g of 2,6-di-t-butyl-p-cresol, 15 g of ethylene diol, and 3-isocyanatomethyl-3,5,5-trimethylcyclohexyl isocyanate (Sumitomo Chemical Bayer Urethane Co., Ltd.) Manufactured, Desmodur I) 12 g and methyl ethyl ketone were added, 0.080 g of dibutyltin dilaurate was added, and then the temperature was raised to 60 ° C. and heated for 1.5 hours. Next, the reaction mixture was cooled in a water bath, and 35 g of tetramethylolmethane triacrylate (“NK Ester” A-TMM-3LM-N manufactured by Shin-Nakamura Chemical Co., Ltd.) was diluted with methyl ethyl ketone to a solid content concentration of 50% by mass. Things were added. It heated up to 60 degreeC and heated for 4 hours, and the acrylic monomer (a-3) obtained by Formula 8 was obtained.
Next, a resin composition containing 30 parts of dipentahexaacrylate (Nippon Kayaku Co., Ltd. KAYARAD DPHA), 50 parts by weight of acrylic monomer (a-3), and inorganic particles (B) in a flask equipped with a stirrer ( b-2) 20 parts by weight, 79 parts by weight of a 10% aqueous solution of polyoxyethylene polycyclic phenyl ether sulfate (Nippon Emulsifier Co., Ltd. New Coal 707SF) as an emulsifier, polyoxyethylene lauryl ether (Emulgen 104P manufactured by Kao Corporation) ) 2.1 parts by weight and 128.9 parts by weight of ion-exchanged water were added and stirred and mixed. Then, while cooling in an ice bath, ultrasonic irradiation for 120 seconds was performed 3 times using an ultrasonic disperser (UH-600S manufactured by SMT) to obtain an emulsion.

Next, the above emulsion was refined with a high-pressure homogenizer (Microfluidizer M110Y manufactured by Mizuho Kogyo Co., Ltd.) under a pressure of 70 MPa to obtain an emulsion (EM-3) containing acrylic monomer (a-3). The concentration of the emulsion (EM-3) is 30%.
(Formula 8) Acrylic monomer (a-3)

Reference Example 6 Emulsion containing amide bond-containing acrylic monomer (a-2) constituting acrylic resin (A) component (EM-4)
In a flask equipped with a stirrer, 30 parts by weight of dipentahexaacrylate (KAYARAD DPHA manufactured by Nippon Kayaku Co., Ltd.), 50 parts by weight of the resulting acrylic monomer (a-2), polyoxyethylene polycyclic phenyl ether sulfate as an emulsifier 79 parts by weight of an ester salt (Nippon Emulsifier Co., Ltd., New Coal 707SF) 79 parts by weight, 2.1 parts by weight of polyoxyethylene lauryl ether (Emulgen 104P manufactured by Kao Corporation), and 128.9 parts by weight of ion-exchanged water are added. And mixed with stirring. Then, while cooling in an ice bath, ultrasonic irradiation for 120 seconds was performed 3 times using an ultrasonic disperser (UH-600S manufactured by SMT) to obtain an emulsion.

  Next, the emulsion was refined with a high-pressure homogenizer (Microfluidizer M110Y manufactured by Mizuho Kogyo Co., Ltd.) under a pressure of 70 MPa to obtain an emulsion (EM-4) containing acrylic monomer (a-2).

Reference Example 7 An emulsion (EM-6) containing an amide bond-containing acrylic monomer (a-2) constituting the acrylic resin (A) component and a resin composition (b-2) containing inorganic particles (B) )
In a flask equipped with a stirrer, resin composition (b-) containing 30 parts of dipentahexaacrylate (KAYARAD DPHA manufactured by Nippon Kayaku Co., Ltd.), 50 parts by weight of acrylic monomer (a-2), and inorganic particles (B). 2) 40 parts by weight, 79 parts by weight of a 10% by weight aqueous solution of polyoxyethylene polycyclic phenyl ether sulfate (Nippon Emulsifier Co., Ltd. New Coal 707SF) as an emulsifier, polyoxyethylene lauryl ether (Emulgen 104P manufactured by Kao Corporation) 2.1 parts by weight and 128.9 parts by weight of ion-exchanged water were added and mixed with stirring. Then, while cooling in an ice bath, ultrasonic irradiation for 120 seconds was performed 3 times using an ultrasonic disperser (UH-600S manufactured by SMT) to obtain an emulsion.

Next, the emulsion was refined with a high-pressure homogenizer (Microfluidizer M110Y manufactured by Mizuho Kogyo Co., Ltd.) under a pressure of 70 MPa to obtain an emulsion (EM-6) containing acrylic monomer (a-2). The solid content concentration of the emulsion (EM-6) is 30% by weight.
<Reference Example 8> Resin composition (b-3) containing inorganic particles (B)
50 parts by weight of an acryloyl group-containing particle modifier (b-1), 50 parts by weight of an aqueous silica particle dispersion (“Sicastar” 43-02-103, particle size 1000 nm, manufactured by Micromod), 0.12 parts by weight of ion-exchanged water, and After stirring a mixed solution of 0.01 parts of p-hydroxyphenyl monomethyl ether at 60 ° C. for 4 hours, 1.36 parts of orthoformate methyl ester was added, and the mixture was further heated and stirred at the same temperature for 1 hour to obtain inorganic particles ( A resin composition (b-3) containing B) was obtained.

<Reference Example 9> An emulsion (EM-7) containing an acrylic monomer (a-1) constituting an acrylic resin (A) component and a resin composition (b-3) containing inorganic particles (B)
A resin composition (b-3) containing 80 parts by weight of an acrylic monomer (a-2) (dipentahexaacrylate (KAYARAD DPHA) manufactured by Nippon Kayaku Co., Ltd.) and inorganic particles (B) in a flask equipped with a stirrer. ) 20 parts by weight, polyoxyethylene polycyclic phenyl ether sulfate ester as an emulsifier (79 parts by weight of a 10% by weight aqueous solution of New Emulsator Co., Ltd., New Coal 707SF), polyoxyethylene lauryl ether (Emulgen 104P manufactured by Kao Corporation) 2 .1 part by weight and 128.9 parts by weight of ion-exchanged water were added and mixed with stirring. Then, while cooling in an ice bath, ultrasonic irradiation for 120 seconds was performed 3 times using an ultrasonic disperser (UH-600S manufactured by SMT) to obtain an emulsion.

Next, the emulsion was refined with a high-pressure homogenizer (Microfluidizer M110Y manufactured by Mizuho Kogyo Co., Ltd.) under a pressure of 70 MPa to obtain an emulsion (EM-7) containing acrylic monomer (a-2). The solid content concentration of the emulsion (EM-7) is 30% by weight.
<Reference Example 10> Resin composition (b-4) containing inorganic particles (B)
50 parts by weight of an acryloyl group-containing particle modifier (b-1), 50 parts by weight of an aqueous silica particle dispersion (“Sicastar” 43-02-503, particle size 5000 nm, manufactured by Micromod), 0.12 parts by weight of ion-exchanged water, and A mixture of 0.01 parts by weight of p-hydroxyphenyl monomethyl ether was stirred at 60 ° C. for 4 hours, 1.36 parts of orthoformate methyl ester was added, and the mixture was further heated and stirred at the same temperature for 1 hour to obtain inorganic particles. A resin composition (b-4) containing (B) was obtained.

<Reference Example 11> Emulsion (EM-8) containing acrylic monomer (a-1) constituting acrylic resin (A) component and resin composition (b-4) containing inorganic particles (B)
A resin composition (b-4) containing 80 parts by weight of an acrylic monomer (a-1) (dipentahexaacrylate (KAYARAD DPHA) manufactured by Nippon Kayaku Co., Ltd.) and inorganic particles (B) in a flask equipped with a stirrer. 20 parts by weight, 79 parts by weight of a 10% aqueous solution of polyoxyethylene polycyclic phenyl ether sulfate (Nippon Emulsifier Co., Ltd. New Coal 707SF) as an emulsifier, polyoxyethylene lauryl ether (Emulgen 104P manufactured by Kao Corporation) 1 part and 128.9 parts by weight of ion-exchanged water were added and stirred and mixed. Then, while cooling in an ice bath, ultrasonic irradiation for 120 seconds was performed 3 times using an ultrasonic disperser (UH-600S manufactured by SMT) to obtain an emulsion.

  Next, the above emulsion was refined with a high-pressure homogenizer (Microfluidizer M110Y manufactured by Mizuho Kogyo Co., Ltd.) under a pressure of 70 MPa to obtain an emulsion (EM-8) containing acrylic monomer (a-2). The solid content concentration of the emulsion (EM-8) is 30% by weight.

Reference Example 12 Emulsion (EM-10) containing composition (B-3) having acrylic resin (G) on the surface of inorganic particles (B) and acrylic resin (F)
A normal acrylic resin reaction vessel equipped with a stirrer, a thermometer, and a reflux condenser was charged with 100 parts of isopropyl alcohol as a solvent, heated and stirred, and maintained at 100 ° C.
In this, 50 parts of n = 19 nonadecyl methacrylate as (meth) acrylate (g′1) and 50 parts of isobornyl methacrylate having two rings as (meth) acrylate (g′2) for 3 hours It was dripped over. And after completion | finish of dripping, it heated at 100 degreeC for 1 hour, and added the additional catalyst liquid mixture which consists of 1 part of t-butyl peroxy 2-ethyl hexaates next. Next, the mixture was heated at 100 ° C. for 3 hours and then cooled to obtain an acrylic resin (G1).
Further, 100 parts of isopropyl alcohol as a solvent was charged into a normal acrylic resin reaction vessel equipped with a stirrer, a thermometer, and a reflux condenser, and the mixture was heated and stirred and maintained at 100 ° C. As the (meth) acrylate (f′3) having a hydroxyl group, 40 parts of 2-hydroxyethyl acrylate, 20 parts of ethyl (meth) acrylate and 20 parts of methyl methacrylate were added dropwise over 3 hours. And after completion | finish of dripping, it heated at 100 degreeC for 1 hour, and added the additional catalyst liquid mixture which consists of 1 part of t-butyl peroxy 2-ethyl hexaates next. Subsequently, after heating at 100 degreeC for 3 hours, it cooled, and the acrylic resin (F-1) was obtained.

Into an aqueous solvent, inorganic particles (B) (“NanoTek” Al ₂ O ₃ slurry (Cay Kasei Co., Ltd., number average particle size 30 nm) and the acrylic resin (G-1) are added in order, and dispersed by the following method. After that, acrylic resin (F1) was added to obtain emulsion (EM-10) containing mixed composition (B-3) of particles (B), acrylic resin (G) and acrylic resin (F). Method (ii) above.)
The addition amount ratio (mass ratio) of the inorganic particles (B), the acrylic resin (F1), and the acrylic resin (G-1) is (B) / (F-1) / (G-1) = 50/40/10. (The mass ratio was calculated by rounding off the first decimal place). The dispersion treatment was performed by using a homomixer and rotating at a peripheral speed of 10 m / s for 5 hours. Moreover, mass ratio of particle | grains (B), acrylic resin (F-1), and acrylic resin (G) in the composition (B-3) finally obtained is (B) / (F-1) / (G) = 50/50 (Note that the mass ratio was calculated by rounding off the first decimal place).

  In addition, the obtained composition (B-3) was centrifuged with a Hitachi tabletop ultracentrifuge (manufactured by Hitachi Koki Co., Ltd .: CS150NX) (rotation speed: 3000 rpm, separation time: 30 minutes), and inorganic particles (B) (And the acrylic resin (F-1) adsorbed on the surface of the inorganic particles (B)) was allowed to settle, the supernatant was removed, and the sediment was concentrated to dryness. As a result of analyzing the concentrated and solidified sediment by X-ray photoelectron spectroscopy (XPS), it was confirmed that the acrylic resin (F-1) was present on the surface of the inorganic particles (B). That is, the acrylic resin (F-1) is adsorbed and adhered to the surface of the inorganic particles (B), and the resulting composition (B-3) is acrylic resin (F) on the surface of the inorganic particles (B). -1).

<Reference Example 13> Emulsion (EM-11) containing composition (B-3) having acrylic resin (G) on the surface of inorganic particles (B) and acrylic resin (F)
The addition ratio (mass ratio) of the inorganic particles (B) and the acrylic resin (F-1) acrylic resin (G-1) is (B) / (F-1) / (G-1) = 32.5 / An emulsion (EM-11) containing a mixed composition (B-3) of particles (B) and an acrylic resin (F-1) was obtained in the same manner as in Reference Example 12 with 37.5 / 30.

Reference Example 14 Emulsion (EM-12) containing a composition (B-3) having an acrylic resin (G) on the surface of inorganic particles (B-1) and an acrylic resin (F)
As the inorganic particles (B), inorganic particles (“NanoTek” TiO ₂ slurry (Cai Kasei Co., Ltd., number average particle size: 36 nm)) were used in the same manner as in Reference Example 13 on the surface of the particles (B). An emulsion (EM-12) containing a mixed composition (B-3) of the composition (B-3) having the acrylic resin (G) and the acrylic resin (F-1) was obtained.

  The properties of the laminated films obtained in the following examples and comparative examples are shown in the table.

<Example 1>
First, the resin composition 1 was prepared as follows.
<Resin composition>
The above emulsion was mixed with an aqueous solvent at a ratio shown in the table to obtain a resin composition 1.

-Emulsion (EM-5) containing acrylic monomer (a-1) constituting acrylic resin (A) component: 100 parts by weight-Inorganic particles (B) "Snowtech OL" (Colloidal) manufactured by Nissan Chemical Industries, Ltd. Silica, particle size 40 nm): 20 parts by weight Emulsifier: Polyoxyethylene polycyclic phenyl ether sulfate ester salt (Nippon Emulsifier Co., Ltd. New Coal 707SF): 7.9 parts by weight, polyoxyethylene lauryl ether (manufactured by Kao Corporation) Emulgen 104P) 2.1 parts by weight (The emulsifier is accompanied by (EM-5))
<Laminated film>
Next, PET pellets (intrinsic viscosity 0.63 dl / g) substantially free of particles were sufficiently dried in vacuum, then supplied to an extruder, melted at 285 ° C., extruded into a sheet form from a T-shaped die, It was wound around a mirror-casting drum having a surface temperature of 25 ° C. using an electric application casting method and cooled and solidified. This unstretched film was heated to 90 ° C. and stretched 3.4 times in the longitudinal direction to obtain a uniaxially stretched film (B film).
Next, the resin composition 1 was applied to the corona discharge-treated surface of the uniaxially stretched film with a coating thickness of about 6 μm using a bar coat. The both ends in the width direction of the uniaxially stretched film coated with the resin composition are gripped with clips and guided to a preheating zone, and the ambient temperature is set to 75 ° C. Subsequently, the ambient temperature is set to 110 ° C using a radiation heater, and then the ambient temperature. The resin composition was dried at 90 ° C. to form a resin layer. Continuously stretched 3.5 times in the width direction in a heating zone (stretching zone) at 120 ° C, and then heat treated for 20 seconds in a heat treatment zone (heat setting zone) at 230 ° C to complete the crystal orientation. Got. In the obtained laminated film, the thickness of the PET film was 50 μm, and the thickness of the resin layer was 1000 nm.
The characteristics of the obtained laminated film are shown in the table.
It was excellent in transparency, scratch resistance, anti-blocking property and adhesiveness.

<Example 2>
A laminated film was obtained in the same manner as in Example 1 except that the resin composition in the coating liquid was changed as follows. The characteristics of the obtained laminated film are shown in the table.

Emulsion (EM-5) containing acrylic monomer (a-1) constituting acrylic resin (A) component: 100 parts by weight Inorganic particles (B): “Spherica 140” (silica particles) manufactured by Catalyst Kasei Co., Ltd. , Particle diameter 140 nm): 20 parts by weight Emulsifier: Polyoxyethylene polycyclic phenyl ether sulfate ester salt (New Coal 707SF manufactured by Nippon Emulsifier Co., Ltd.): 7.9 parts by weight, polyoxyethylene lauryl ether (Emulgen manufactured by Kao Corporation) 104P) 2.1 parts by weight (the emulsifier is accompanied by (EM-5))
<Example 3>
A laminated film was obtained in the same manner as in Example 1 except that the resin composition in the coating liquid was changed as follows.
The characteristics of the obtained laminated film are shown in the table.

-Emulsion (EM-5) containing acrylic monomer (a-1) constituting acrylic resin (A) component: 100 parts by weight-Inorganic particles (B) ("Seahoster KEW-50" manufactured by Nippon Shokubai Co., Ltd.) (Silica particles, particle diameter 500 nm)): 20 parts by weight Emulsifier: Polyoxyethylene polycyclic phenyl ether sulfate ester salt (Nippon Emulsifier Co., Ltd. New Coal 707SF): 7.9 parts by weight, polyoxyethylene lauryl ether (Kao Corporation) ) Emulgen 104P) 2.1 parts by weight (The emulsifier is accompanied by (EM-5))
<Example 4>
A laminated film was obtained in the same manner as in Example 1 except that the resin composition in the coating liquid was changed as follows.
The characteristics of the obtained laminated film are shown in the table.

-Emulsion (EM-5) containing acrylic monomer (a-1) constituting acrylic resin (A) component: 100 parts by weight-Inorganic particles (B) ("Snowtex O" manufactured by Nissan Chemical Industries, Ltd.) Silica particles, particle size 10 nm)): 20 parts by weight Emulsifier: Polyoxyethylene polycyclic phenyl ether sulfate ester salt (Nippon Emulsifier Co., Ltd. New Coal 707SF): 7.9 parts by weight, polyoxyethylene lauryl ether (Kao Corporation) ) Emulgen 104P) 2.1 parts by weight (The emulsifier is accompanied by (EM-5))
<Example 5>
A laminated film was obtained in the same manner as in Example 1 except that the resin composition in the coating liquid was changed as follows. The characteristics of the obtained laminated film are shown in the table.

Emulsion (EM-1) containing acrylic monomer (a-1) constituting acrylic resin (A) component and resin composition (b-2) containing inorganic particles (B): 100 parts by weight Emulsifier : Polyoxyethylene polycyclic phenyl ether sulfate ester (Nippon Emulsifier Co., Ltd. New Coal 707SF): 7.9 parts by weight, polyoxyethylene lauryl ether (Emulgen 104P manufactured by Kao Corporation) 2.1 parts by weight (Accompanying (EM-1))
<Example 6>
A laminated film was obtained in the same manner as in Example 1 except that the resin composition in the coating liquid was changed as follows. The characteristics of the obtained laminated film are shown in the table.

-Emulsion (EM-2) containing amide bond-containing acrylic monomer (a-2) constituting acrylic resin (A) component and resin composition (b-2) containing inorganic particles (B): 100 wt. Part ・ Emulsifier: Polyoxyethylene polycyclic phenyl ether sulfate ester (Nippon Emulsifier Co., Ltd. New Coal 707SF): 7.9 parts by weight, Polyoxyethylene lauryl ether (Emulgen 104P manufactured by Kao Corporation) 2.1 parts by weight ( The emulsifier is accompanied by (EM-2))
<Example 7>
A laminated film was obtained in the same manner as in Example 1 except that the resin composition in the coating liquid was changed as follows. The characteristics of the obtained laminated film are shown in the table.

-Emulsion (EM-3) containing amide bond-containing acrylic monomer (a-2) constituting acrylic resin (A) component and resin composition (b-2) containing inorganic particles (B): 100 wt. Part ・ Emulsifier: Polyoxyethylene polycyclic phenyl ether sulfate ester (Nippon Emulsifier Co., Ltd. New Coal 707SF): 7.9 parts by weight, Polyoxyethylene lauryl ether (Emulgen 104P manufactured by Kao Corporation) 2.1 parts by weight ( The emulsifier is accompanied by (EM-3))
<Example 8>
A laminated film was obtained in the same manner as in Example 1 except that the resin composition in the coating liquid was changed as follows. The characteristics of the obtained laminated film are shown in the table.

-Emulsion (EM-4) containing amide bond-containing acrylic monomer (a-2) constituting acrylic resin (A) component: 80 parts by weight-Inorganic particles (B) ("Snowtech" manufactured by Nissan Chemical Industries, Ltd.) OL "(colloidal silica, particle size 40 nm)): 20 parts by weight Emulsifier: Polyoxyethylene polycyclic phenyl ether sulfate ester (Nippon Emulsifier Co., Ltd. New Coal 707SF): 7.9 parts by weight, polyoxyethylene lauryl ether ( 2.1 parts by weight of Emulgen 104P manufactured by Kao Corporation (the emulsifier is accompanied by (EM-3))
<Examples 9 to 15>
A laminated film was obtained in the same manner as in Example 6 except that the thickness of the resin layer was changed to the thickness described in the table. The characteristics of the obtained laminated film are shown in the table.
<Example 16>
A laminated film was obtained in the same manner as in Example 6 except that the resin composition in the coating liquid was changed as follows. The characteristics of the obtained laminated film are shown in the table.
-Emulsion (EM-6) containing amide bond-containing acrylic monomer (a-2) constituting acrylic resin (A) component and resin composition (b-2) containing inorganic particles (B)
: 100 parts by weight Emulsifier: Polyoxyethylene polycyclic phenyl ether sulfate ester (New Coal 707SF manufactured by Nippon Emulsifier Co., Ltd.): 7.9 parts by weight, polyoxyethylene lauryl ether (Emulgen 104P manufactured by Kao Corporation) 2.1 Parts by weight (the emulsifier is accompanied by (EM-2))

<Example 17>
A laminated film was obtained in the same manner as in Example 1 except that the resin composition in the coating liquid was changed as follows. The characteristics of the obtained laminated film are shown in the table.

-Emulsion (EM-10) containing composition (B-3) having acrylic resin (G) on surface of inorganic particles (B) and acrylic resin (F): 100 parts by weight <Example 18>
A laminated film was obtained in the same manner as in Example 1 except that the resin composition in the coating liquid was changed as follows. The characteristics of the obtained laminated film are shown in the table.

-Emulsion (EM-11) containing composition (B-3) having acrylic resin (G) on the surface of inorganic particles (B) and acrylic resin (F): 100 parts by weight <Example 19>
A laminated film was obtained in the same manner as in Example 1 except that the resin composition in the coating liquid was changed as follows. The characteristics of the obtained laminated film are shown in the table.

-Emulsion (EM-12) containing composition (B-3) having acrylic resin (G) on the surface of inorganic particles (B-1) and acrylic resin (F): 100 parts by weight <Example 20>
A laminated film was obtained in the same manner as in Example 1 except that the resin composition in the coating liquid was changed as follows. The characteristics of the obtained laminated film are shown in the table.

-Emulsion (EM-11) containing composition (B-3) having acrylic resin (G) on the surface of inorganic particles (B) and acrylic resin (F): 80 parts by weight-Melamine compound "Beckamine" ( Registered Trademark) APM (Dainippon Ink Industries, Ltd.): 20 parts


<Examples 21 and 22>
A laminated film was obtained in the same manner as in Example 17 except that the thickness of the resin layer was changed to the thickness described in the table. The characteristics of the obtained laminated film are shown in the table.

<Example 23>
A laminated film was obtained in the same manner as in Example 1 except that the resin composition in the coating liquid was changed as follows.
The characteristics of the obtained laminated film are shown in the table.

-Emulsion (EM-5) containing acrylic monomer (a-1) constituting acrylic resin (A) component: 100 parts by weight-Inorganic particles (B) ("Snowtex O" manufactured by Nissan Chemical Industries, Ltd.) Silica particles, particle size 10 nm)): 20 parts by weight Emulsifier: Polyoxyethylene polycyclic phenyl ether sulfate ester salt (Nippon Emulsifier Co., Ltd. New Coal 707SF): 7.9 parts by weight, polyoxyethylene lauryl ether (Kao Corporation) ) Emulgen 104P) 2.1 parts by weight (The emulsifier is accompanied by (EM-5))
<Comparative Example 1>
A laminated film was obtained in the same manner as in Example 1 except that the composition of the resin composition in the coating liquid was changed as shown in the table. The characteristics of the obtained laminated film are shown in the table.

-Emulsion (EM-5) containing acrylic monomer (a-1) constituting acrylic resin (A) component: 100 parts by weight-Inorganic particles (B) ("Snow Tech OXS" manufactured by Nissan Chemical Industries, Ltd.) Colloidal silica, particle diameter 5 nm)): 20 parts by weight Emulsifier: Polyoxyethylene polycyclic phenyl ether sulfate ester (Nippon Emulsifier Co., Ltd. New Coal 707SF): 7.9 parts by weight, polyoxyethylene lauryl ether (Kao Corporation) ) Emulgen 104P) 2.1 parts by weight (The emulsifier is accompanied by (EM-5))
<Comparative example 2>
The resin composition used in Example 6 was applied to one side of a 50 μm thick PET film (“Lumirror (registered trademark) U34” manufactured by Toray Industries, Inc.) so that the thickness after drying was 1000 nm, and a hot air oven was used. Used, dried at 100 ° C. for 2 minutes, and then dried again at 230 ° C. for 20 seconds to obtain a laminated film. The characteristics of the obtained laminated film are shown in the table.
<Comparative Example 3>
A laminated film was obtained in the same manner as in Example 1 except that the resin composition in the liquid was changed as follows. The characteristics of the obtained laminated film are shown in the table.

Emulsion (EM-7) containing acrylic monomer (a-1) constituting acrylic resin (A) component and resin composition (b-3) containing inorganic particles (B): 100 parts by weight Emulsifier : Polyoxyethylene polycyclic phenyl ether sulfate ester (Nippon Emulsifier Co., Ltd. New Coal 707SF): 7.9 parts by weight, polyoxyethylene lauryl ether (Emulgen 104P manufactured by Kao Corporation) 2.1 parts by weight (Accompanying EM-7)
<Comparative Example 4>
A laminated film was obtained in the same manner as in Example 1 except that the resin composition in the liquid was changed as follows. The characteristics of the obtained laminated film are shown in the table.

Emulsion (EM-8) containing acrylic monomer (a-1) constituting acrylic resin (A) component and resin composition (b-3) containing inorganic particles (B): 100 parts by weight Emulsifier : Polyoxyethylene polycyclic phenyl ether sulfate ester (Nippon Emulsifier Co., Ltd. New Coal 707SF): 7.9 parts by weight, polyoxyethylene lauryl ether (Emulgen 104P manufactured by Kao Corporation) 2.1 parts by weight (Accompanying (EM-8))
<Comparative Example 5>
A laminated film was obtained in the same manner as in Example 17 except that the thickness of the resin layer was changed to the thickness described in the table. The characteristics of the obtained laminated film are shown in the table.

The present invention is a laminated film excellent in transparency, scratch resistance, handling properties, and anti-blocking properties, and can be used as a hard coat film used in conventional display applications and a hard coat film used in molding decoration applications. .

Claims (9)

A laminated film having a polyester layer and a resin layer, wherein at least one surface layer is a resin layer, and the resin layer included in the surface layer has a micro surface roughness (Ra-1) required by AFM (Atomic Force Microscope). A laminated film having a macro surface roughness (Ra-2) of 1 nm to 50 nm, which is 1 nm to 20 nm and is determined by a three-dimensional surface roughness meter. The laminated film according to claim 1, wherein the resin layer in the surface layer has a macro surface roughness (Ra-2) of 5 nm or more and 50 nm or less determined by a three-dimensional surface roughness meter. The ratio (Ra-2 / Ra-1) of the micro surface roughness (Ra-1) and the macro surface roughness (Ra-2) of the resin layer in the surface layer is 3 or more and 30 or less. The laminated film as described. The resin layer in the surface layer contains particles, and the particle abundance ratio (P-1) in the range from the resin layer surface to the position of 10% of the resin layer thickness when the thickness direction cross section of the resin layer is observed. ) Is larger than the particle abundance ratio (P-2) in the range from the position of 40% to the position of 60% of the resin layer thickness from the resin layer surface. Particle existence ratio (P-1) in the range from the resin layer surface to the position of 10% of the resin layer thickness and the presence of particles in the range from the resin layer surface to the position of 40% to 60% of the resin layer thickness The laminated film according to claim 4, wherein a ratio (P-1 / P-2) of the ratio (P-2) is 1.1 or more and 5.0 or less. The laminated film according to claim 4 or 5, wherein the thickness (t) of the resin layer in the surface layer is 100 nm or more and 5000 nm or less. The average particle diameter (d) of the particles contained in the resin layer in the surface layer is 1 nm or more and 100 nm or less, and the ratio (t) / (d) between the thickness (t) of the resin layer and the average particle diameter (d) of the particles. ) Is 2 or more and 1000 or less. The laminated film according to claim 6. The laminated film according to claim 1, wherein the polyester layer and the resin layer are directly laminated. A coating liquid containing a polyfunctional acrylic resin and particles is applied to at least one surface of the polyester film before the crystal orientation is completed, and then the polyester film is stretched at least in a uniaxial direction and subjected to a heat treatment. The manufacturing method of the laminated | multilayer film in any one of Claims 1-8 including the process of completing the crystal orientation of this polyester film.