JPS6393378A - Resin product having weatherability and abrasion resistance and its preparation - Google Patents
Resin product having weatherability and abrasion resistance and its preparationInfo
- Publication number
- JPS6393378A JPS6393378A JP24096986A JP24096986A JPS6393378A JP S6393378 A JPS6393378 A JP S6393378A JP 24096986 A JP24096986 A JP 24096986A JP 24096986 A JP24096986 A JP 24096986A JP S6393378 A JPS6393378 A JP S6393378A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- hard coat
- abs
- colored primer
- base material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は耐候性および耐摩耗性を有する樹脂製品および
その製造方法に係り、詳しくは、例えば樹脂製自動車部
品の表面処理や塗装の分野で利用され、耐候性の高くな
い安価な樹脂に、耐候性と耐摩耗性を付与できるように
した樹脂製品とその製造法に関するものである。[Detailed Description of the Invention] [Field of Industrial Application] The present invention relates to a resin product having weather resistance and abrasion resistance, and a method for manufacturing the same. The present invention relates to a resin product that can be used to impart weather resistance and abrasion resistance to an inexpensive resin that does not have high weather resistance, and a method for producing the same.
近年、自動重用部品では金属に代え°Ｃ樹脂が使用され
ることが多く、車体の軽量化やデザイン上の変化を可能
にしている。樹脂は種々なものがあり、その物理的化学
的性質や機械的１ｊｔ性は大きく異なることが多い。自
動車などの部品において、目に付く個所に採用される場
合には、１１χなる耐久性や強度の面だけでな（、見栄
えの維持が強く要求され、例えば紫外線や雨雪などの水
湿の影習も少ないことが必要となる。すなわち、耐候性
、光沢保持性といったことが外装部品には強く要求され
る。紫外線に強く劣化の少ない耐候性のある樹脂として
アクリル樹脂がある。従来の自動車部品などはそのアク
リル樹脂が使用されるが、洗車機などにより表面にすり
傷がつくので、硬度の高い塗膜を形成させて樹脂母材を
保護するようにしている。その丈夫な”！ｉ膜を形成す
るためにハードコートクリヤー塗装が行なわれる場合が
多くなっているが、それは紫外線硬化型の塗料である。In recent years, °C resin is often used instead of metal in heavy-duty automobile parts, making it possible to reduce the weight of vehicle bodies and change their design. There are various resins, and their physical and chemical properties and mechanical properties often differ greatly. When used in highly visible parts of automobiles, etc., it is strongly required not only to have 11x durability and strength, but also to maintain good appearance. In other words, weather resistance and gloss retention are strongly required for exterior parts.Acrylic resin is a weather-resistant resin that is resistant to ultraviolet rays and has little deterioration.Conventional automotive parts The acrylic resin is used in car washes, etc., but since the surface gets scratched by car washes, etc., a highly hard coating film is formed to protect the resin base material.The durable "!i film" In many cases, hard coat clear paint is used to form the coating, but it is an ultraviolet curing type paint.
ところで、上記したような要求を満たず樹脂部品を大量
に生産する場合、母材である樹脂の選定において良好な
性能が発揮される安価なものが好ましいが、上述のアク
リルなどは一般に高価である。そのため、自動車部品で
はしばしば安価なＡＢＳ樹脂が選定されることが多い、
それが人目に触れない個所や紫外線を受けない個所で使
用される場合は問題がないとしても、高い表面光沢を要
求する外装部ｒ＋ｉｓにＡＢＳ樹脂が適用されると、紫
外線の影蓼を受けて樹脂が劣化する。すなわち、ＡＢＳ
樹脂は紫外線に弱く耐候性が低いので、見栄えが著しく
損なわれることになる。そのため表面の耐摩耗性を上げ
るために塗布されるハードコートクリヤーに、隙蔽力の
ある着色タイプや日光透過を防ぐ紫外線吸収剤を添加す
るなどすることができれば都合がよい、しかし、ハード
コートクリヤーは上記したように紫外線硬化型であるの
で、その混入物により硬化が阻害されることになり、結
果的にはハードコートクリヤーをＡＢＳ樹脂に塗布でき
ないことになる。したがって、自動車の車体部品や外装
部品にあっては、ＡＢＳ樹脂とハードコートクリヤーと
の組み合せは実用性がないことになる。By the way, when producing resin parts in large quantities that do not meet the above requirements, it is preferable to select a base material resin that is inexpensive and exhibits good performance, but the above-mentioned acrylic etc. are generally expensive. . Therefore, cheap ABS resin is often selected for automobile parts.
There may be no problem if ABS resin is used in a place that is not exposed to public view or is not exposed to ultraviolet rays, but if ABS resin is applied to the exterior r+is, which requires high surface gloss, it may be affected by ultraviolet rays. Resin deteriorates. That is, ABS
Since resin is sensitive to ultraviolet rays and has low weather resistance, the appearance will be significantly impaired. For this reason, it would be convenient if the hard coat clear coated to increase the abrasion resistance of the surface could be colored with opacity or add ultraviolet absorbers to prevent sunlight from passing through. As mentioned above, since it is an ultraviolet curing type, its contaminants will inhibit curing, and as a result, hard coat clear cannot be applied to ABS resin. Therefore, for automobile body parts and exterior parts, the combination of ABS resin and hard coat clear is not practical.
上述のハードコートクリヤーは透明の薄い膜を母材樹脂
の表面に形成するわけであるが、自動車外装部品などに
要求される耐摩耗性を有するものは紫外線硬化型のみが
一般的である。そのハードコートクリヤーに、隠蔽力の
ある着色タイプにしたり日光透過を防ぐ紫外線吸収剤を
添加することが不可能となるのは上で述べた通りであり
、日光を透過するハードコートクリヤーを使用する限り
、母材はそれ自体耐候性の良好な樹脂に限定されること
になる。そのような樹脂は前述したＡＢＳ樹脂などより
は高価であり、車体コストの増加を来たす。一方、ＡＢ
Ｓ樹脂などの耐候性の低いものを採用すると、ハードコ
ートクリヤーによって耐摩耗性を向上させることができ
ても、紫外線による劣化は避けられず、高価なアクリル
樹脂に代わる安価な樹脂の採用が実現できない問題が生
じる。The above-mentioned hard coat clear forms a transparent thin film on the surface of the base resin, but generally only the ultraviolet curing type has the abrasion resistance required for automotive exterior parts. As mentioned above, it is impossible to make the hard coat clear a colored type with hiding power or add ultraviolet absorbers to prevent sunlight from passing through, so it is impossible to use a hard coat clear that allows sunlight to pass through. As far as possible, the base material itself is limited to resins that have good weather resistance. Such resins are more expensive than the above-mentioned ABS resins and increase the cost of the vehicle body. On the other hand, AB
If a material with low weather resistance such as S resin is used, even if the abrasion resistance can be improved with a hard coat clear, deterioration due to ultraviolet rays is unavoidable, making it possible to use a cheaper resin instead of the expensive acrylic resin. A problem arises that cannot be done.
本発明は、このような問題に鑑みなされたもので、その
目的は、耐候性Ｏ高（ないＡＢＳなどの樹脂に、耐摩耗
性を付与するハードコートクリヤーを塗布する場合に、
樹脂母材に耐候性を付与することができると共に、付着
性の向上とハードコートクリヤーの硬化を阻害すること
のない安価で耐候性および６（摩耗性を有する）Ｍ脂製
品およびその製造方法を提供することである。The present invention was developed in view of these problems, and its purpose is to provide a hard coat clear that imparts abrasion resistance to resins such as ABS that do not have high weather resistance.
To provide an inexpensive, weather-resistant and 6 (abrasion-resistant) M resin product that can impart weather resistance to a resin base material, improve adhesion, and do not inhibit the hardening of a hard coat clear, and a method for producing the same. It is to provide.
上記の問題点を解決するための本発明の特徴は、樹脂製
品の発明にあっては、ＡＢＳなどの耐候性の高（ない樹
脂に、耐摩耗性を付与するハードコートクリヤーを塗布
した樹脂製品であって、前記ＡＢＳなどの樹脂の表面に
、紫外線吸収剤および酸化防止剤の添加されている着色
プライマーおよび紫外線硬化型ハードコートクリヤーが
塗布されている樹脂製品としたことである。A feature of the present invention to solve the above problems is that in the invention of resin products, resin products are made by applying a hard coat clear that imparts wear resistance to resins with high weather resistance such as ABS. The present invention is a resin product in which a colored primer containing an ultraviolet absorber and an antioxidant and an ultraviolet curable hard coat clear are applied to the surface of the resin such as ABS.
一方、製造法の発明にあっては、八ＢＳなどの耐候性の
高くない樹脂に、耐摩耗性を付与するハードコートクリ
４・−を塗布した樹脂製品の製造において、
前記ＡＢＳなどの樹脂の表面に、紫外線吸収剤および酸
化防止剤の添加されている着色プライマーを、熱風加熱
または自然乾燥させ”ζ塗着する工程と、
その着色プライマー上に、前記ハードコートクリヤーを
塗布して、紫外線により塗膜を硬化形成させる工程を含
む製造法としたことである。On the other hand, in the invention of a manufacturing method, in manufacturing a resin product in which a hard coat cream 4-- which imparts wear resistance is applied to a resin that does not have high weather resistance such as 8BS, A process of applying a colored primer containing an ultraviolet absorber and an antioxidant to the surface by heating with hot air or air drying, and applying the hard coat clear on the colored primer, and applying ultraviolet rays to the colored primer. The manufacturing method includes a step of curing and forming the coating film.
耐候性の高くないＡＢＳなどの樹脂の表面に、紫外線吸
収剤および酸化防止剤の添加されている着色プライマー
を、熱風加熱または自然乾燥などにより塗着させる。樹
脂母材は着色プライマーで隠蔽されることになり、紫外
線が着色プライマーで吸収され、また着色プライマーの
酸化が軽減され、樹脂母材に紫外線が及ぶことなく樹脂
母材の紫外線劣化が防止される。その着色プライマー上
に、耐摩耗性を付与するハードコートクリヤーを紫外線
硬化させて塗膜が形成され、外装部品としての所定の耐
摩耗性が確保される。A colored primer containing an ultraviolet absorber and an antioxidant is applied to the surface of a resin such as ABS, which does not have high weather resistance, by heating with hot air or air drying. The resin base material is hidden by the colored primer, UV rays are absorbed by the colored primer, oxidation of the colored primer is reduced, and UV rays do not reach the resin base material, preventing UV deterioration of the resin base material. . A coating film is formed on the colored primer by curing a hard coat clear that imparts wear resistance with ultraviolet light, thereby ensuring a predetermined wear resistance as an exterior component.
本発明の耐候性および耐摩耗性を有する樹脂製品にあっ
ては、ＡＢＳなどの樹脂の表面に、紫外線吸収剤および
酸化防止剤の添加されている着色プライマーと、耐摩耗
性を付与するハードコートクリヤーとが塗布されている
ので、安価であるが耐候性の高（ないＡＢＳなどの樹脂
に耐候性と耐摩耗性さらには良好な付着性が付与され、
自動車外装部品などとして所望の耐久性を確保すること
ができる。また、上記の着色プライマーを、熱風加熱ま
たは自然乾燥で塗着させる工程を経た後、その着色プラ
イマー上に、ハードコートクリヤーを紫外線により塗膜
を硬化形成させるようにしたので、それらの密着性がよ
（、付着性が良好でクランクの発生の極めて少ない見栄
えが維持されると共に、ハードコートクリヤーの硬化が
阻害されることなく、所望の耐摩耗性ををする塗膜を形
成し、樹脂部品に耐ＦｔＸ耗カを付与することができる
。In the resin product having weatherability and abrasion resistance of the present invention, a colored primer containing an ultraviolet absorber and an antioxidant is added to the surface of the resin such as ABS, and a hard coat that imparts abrasion resistance. Because it is coated with a clear coating, it is inexpensive but highly weather resistant, giving it weather resistance, abrasion resistance, and good adhesion to resins such as ABS.
Desired durability can be ensured as automotive exterior parts and the like. In addition, after the above-mentioned colored primer was applied by heating with hot air or air drying, the hard coat clear was hardened and formed on the colored primer using ultraviolet rays, which improved the adhesion of the hard coat clear. It maintains a good appearance with good adhesion and minimal occurrence of cranking, and forms a coating film with the desired abrasion resistance without inhibiting the curing of the hard coat clear. FtX wear resistance can be imparted.
以下に、本発明をその実施例に基づき詳細に説明する。 The present invention will be described in detail below based on examples thereof.
第１図は樹脂母材１に、耐摩耗性を付与するバー）’：
Ｉ−）クリヤー２を塗布した樹脂製品３であり、Ｍｒｋ
性を備えさせるための着色プライマー４も塗着された断
面の拡大模式図である。その上記母材１の素材は例えば
ＡＢＳ樹脂であり、耐候性は一般的にいって高（ないも
のである、そのような樹脂が採用されているのは、それ
が安価であること、および本発明により耐候性はあるが
高価であるアクリル樹脂などを使用しなくても済むよう
にしたことに基づいている。Figure 1 shows a bar that imparts wear resistance to the resin base material 1)':
I-) Resin product 3 coated with clear 2, Mrk
It is an enlarged schematic view of a cross section coated with a colored primer 4 for imparting properties. The material of the base material 1 is, for example, ABS resin, and its weather resistance is generally not high. This invention is based on the fact that there is no need to use acrylic resin, which is weather resistant but expensive.
その樹脂母材ｌの表面には、紫外線吸収剤および酸化防
止剤の添加されている着色プライマー４が、熱風加熱ま
たは自然乾燥により塗着されている。そして、その着色
プライマー４上には透明なハードコートクリヤー２が塗
布され、紫外線により塗膜が硬化形成されている。この
ような製法により樹脂部品が塗装されると、母材１が部
品を形成維持した基材をなし、それに塗着された着色プ
ライマー４が色彩と光沢を発揮して外装部品としての見
栄えを確保し、それを透明なハードコートクリヤーが保
護すると共に表面に耐ＦｉＢ性が付与される。このよう
にして耐候性の高くない安価なＡＢＳなどの樹脂に耐候
性と耐摩耗性を持たせ、さらに着色プライマーならびに
ハードコートクリヤーの剥離やひび割れなどの発生すな
わち耐クラツク性の向上いわゆる付着性を高くすること
ができるのである。したがって、樹脂部品の重体への導
入がより一層可能となり、しがち洗軍機のブラシなどの
擦れに対しても傷のつがない外袋樹脂部品とすることが
できる。A colored primer 4 containing an ultraviolet absorber and an antioxidant is applied to the surface of the resin base material 1 by heating with hot air or by air drying. A transparent hard coat clear 2 is applied onto the colored primer 4, and the coating film is cured by ultraviolet rays. When a resin part is painted using this manufacturing method, the base material 1 serves as the base material that maintains the formation of the part, and the colored primer 4 applied to it provides color and gloss to ensure the appearance of the exterior part. A transparent hard coat clear protects it and imparts FiB resistance to the surface. In this way, inexpensive resins such as ABS, which do not have high weather resistance, can be made to have weather resistance and abrasion resistance, and also improve the so-called adhesion of colored primers and hard coat clears to prevent peeling and cracking, that is, to improve crack resistance. It can be made higher. Therefore, it becomes even more possible to introduce the resin part into a heavy body, and it is possible to make the outer bag resin part free from scratches even when rubbed by the brush of a laundry machine.
上記した樹脂はＡＢＳのほかに、ポリカーボネイト、ポ
リカーボネイト／ＡＢＳ、ノリル（スチレン変性ポリフ
ェニレンオキサイド）、ＡＥＳ（アクリロニトリル・エ
チレンプロピレン・スチレン）、ＡＡＳやＡＳなどが挙
げられる。一方、着色プライマーはアクリルラッカーお
よびアクリルウレタン塗料に紫外線吸収剤と酸化防止剤
を添加し、ハードコートクリヤーを透過してくる太陽光
線に対して十分な耐候性を有するように配慮されている
。塗料用樹脂としＣは、ＣＢＳ （セルロース・アセテ
ート・ブチレート）、硝化綿”／’ り＋） ／ｌ／ラ
ッカー、ポリイソシアネート硬化型アクリル・ウレタン
、ポリイソシアネート硬化型ポリエステル・ウレタンな
どである。隠蔽膜厚（着色力）は、塗料用着色剤および
体ｗ顔料の配合によりｒＪＩｓＫ５４００６．２項の隠
蔽力評価法」における隠蔽膜が、乾燥塗膜で６０．ｃｚ
ｍ以下である。紫外線吸収剤の種類と配合量は、ベン
ゾトリアゾールまたはペンゾフェノンを上述の塗料用樹
脂に対して０．５〜５重量％とされる。酸化防止剤の種
類と配合量は、ヒンダードアミンまたはヒンダードフェ
ノールを上述の塗料用樹脂に対して０．１〜１重量％で
ある。In addition to ABS, the resins mentioned above include polycarbonate, polycarbonate/ABS, Noryl (styrene-modified polyphenylene oxide), AES (acrylonitrile/ethylenepropylene/styrene), AAS, and AS. On the other hand, colored primers are made by adding ultraviolet absorbers and antioxidants to acrylic lacquers and acrylic urethane paints, and are designed to have sufficient weather resistance against sunlight that passes through the hard coat clear. Paint resins C include CBS (cellulose acetate butyrate), nitrified cotton lacquer, polyisocyanate-curable acrylic urethane, polyisocyanate-curable polyester urethane, etc. Hiding film The thickness (tinting power) is determined by the combination of paint colorants and body pigments, and the dry coating film has a hiding film of 60. cz
m or less. The type and amount of the ultraviolet absorber is 0.5 to 5% by weight of benzotriazole or penzophenone based on the above-mentioned coating resin. The type and amount of the antioxidant is 0.1 to 1% by weight of hindered amine or hindered phenol based on the above-mentioned coating resin.
ハードコートクリヤー（表面硬化用塗料）は、不飽和ア
クリル樹脂またはアクリルモノマーを主成分とし、光増
感剤、レベリング剤などの添加剤および有機溶剤で構成
する紫外線硬化型透明塗料である。Hard coat clear (surface curing paint) is an ultraviolet curable transparent paint that has an unsaturated acrylic resin or acrylic monomer as its main component, additives such as a photosensitizer and a leveling agent, and an organic solvent.
以下にへＢＳ樹脂などの樹脂母材に適用した場合の例を
、本発明に基づく場合とその他の例とを比較し°ζ説明
する。３つの実施例を理解しやすくするためにそれに対
応する各比較例も折り混ぜてテストした一例の構成仕様
を第１表に示す、促進耐候試験は、ＪＩＳ Ｄ０２０５
．７．５の６３℃±３℃、降雨１２分／時間のサンシャ
インウェザ−メーター試験を６００時間と、４０℃×９
８％Ｒ，ＩＩ以上の耐湿試験を７２時間と、を１サイク
ルとしてテストしたものであり、第２表の左欄は２サイ
クル経過後の結果、右欄は４サイクル経過後の結果であ
る。その４サイクル経過後の結果が良好であると、外装
部品として十分耐えられるものであると評価できる。Below, examples of applications to resin base materials such as BS resin will be explained by comparing the cases based on the present invention and other examples. In order to make it easier to understand the three examples, the corresponding comparative examples were also mixed together and the configuration specifications of one example are shown in Table 1. The accelerated weathering test is based on JIS D0205.
．． Sunshine weather meter test of 7.5 at 63°C ± 3°C, rainfall 12 minutes/hour for 600 hours, 40°C x 9
A humidity resistance test of 8% R, II or higher was performed for 72 hours as one cycle. The left column of Table 2 shows the results after 2 cycles, and the right column shows the results after 4 cycles. If the result after 4 cycles is good, it can be evaluated that it can withstand sufficiently as an exterior part.
第２表より判ることは、実施例２および実施例３は４サ
イクル完了しても、着色プライマーおよびハードコート
クリヤーの付着は完全であり、外観には何ら異常もなく
、光沢も８０％以上保持されており、自動車外装部品と
して、ＡＢＳなどの耐候性の高くない樹脂を採用しても
、耐候性、付着性、耐摩耗性は十分確保されているので
ある。したがって、安価なＡＢＳなどのａｔ脂を使用す
ることも可能となり、樹脂母材の選定範囲が広がると共
に部品コストの低減に大きく寄与させることが可能とな
る。Table 2 shows that even after completing 4 cycles in Examples 2 and 3, the adhesion of the colored primer and hard coat clear was complete, there was no abnormality in appearance, and the gloss remained at 80% or more. Therefore, even if resins such as ABS, which do not have high weather resistance, are used for automobile exterior parts, weather resistance, adhesion, and abrasion resistance are sufficiently ensured. Therefore, it becomes possible to use inexpensive attenuated resin such as ABS, which widens the selection range of resin base materials and greatly contributes to reducing component costs.
（以下、余白） 第 １ 表 第 ２ ：Ａ(Hereafter, margin) Table 1 Part 2: A
第１図は本発明の耐候性および耐摩耗性を有する樹脂製
品の断面を拡大して示した模式図である。
１−・樹脂、２−・・ハードコートクリヤー、３−・樹
脂製品、４−・着色プライマー。
特許出願人 マ ツ ダ 株式会社代理人 弁理士
吉相 勝俊（ほか１名）第 １ 図FIG. 1 is a schematic diagram showing an enlarged cross section of a resin product having weather resistance and wear resistance according to the present invention. 1--Resin, 2--Hard coat clear, 3--Resin product, 4--Colored primer. Patent applicant: Mazda Corporation Agent: Patent attorney: Katsutoshi Yoshiso (and one other person) Figure 1
Claims (2)
を付与するハードコートクリヤーを塗布した樹脂製品に
おいて、 前記ＡＢＳなどの樹脂の表面に、紫外線吸収剤および酸
化防止剤の添加されている着色プライマーおよび紫外線
硬化型ハードコートクリヤーが塗布されていることを特
徴とする耐候性および耐摩耗性を有する樹脂製品。(1) In resin products such as ABS, which has low weather resistance and is coated with a hard coat clear that imparts wear resistance, ultraviolet absorbers and antioxidants are added to the surface of the resin such as ABS. A weather-resistant and abrasion-resistant resin product coated with a colored primer and an ultraviolet-curable hard coat clear.
を付与するハードコートクリヤーを塗布した樹脂製品の
製造において、 前記ＡＢＳなどの樹脂の表面に、紫外線吸収剤および酸
化防止剤の添加されている着色プライマーを、熱風加熱
または自然乾燥させて塗着する工程と、 その着色プライマー上に、前記ハードコートクリヤーを
塗布して、紫外線により塗膜を硬化形成させることを特
徴とする耐候性および耐摩耗性を有する樹脂製品の製造
方法。(2) In the production of resin products in which a resin with low weather resistance such as ABS is coated with a hard coat clear that imparts wear resistance, addition of ultraviolet absorbers and antioxidants to the surface of the resin such as ABS. Weather resistance characterized by a step of applying a colored primer by heating with hot air or air drying, and applying the hard coat clear on the colored primer, and curing and forming a coating film with ultraviolet rays. and a method for producing a wear-resistant resin product.