JPS636278B2 - - Google Patents
Info
- Publication number
- JPS636278B2 JPS636278B2 JP13793679A JP13793679A JPS636278B2 JP S636278 B2 JPS636278 B2 JP S636278B2 JP 13793679 A JP13793679 A JP 13793679A JP 13793679 A JP13793679 A JP 13793679A JP S636278 B2 JPS636278 B2 JP S636278B2
- Authority
- JP
- Japan
- Prior art keywords
- ink
- transparent
- raised
- printing
- raised printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明は立体感を有する化粧板の製造方法に関
し、更に詳しくは模様印刷を施した基板上に透明
盛り上げ印刷インク及び加熱発泡剤混入インクと
を併用してスクリーン印刷を施こしてなる化粧板
の製造方法に関する。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a method for manufacturing a decorative board with a three-dimensional effect, and more specifically, the present invention relates to a method for manufacturing a decorative board having a three-dimensional effect, and more specifically, screen printing is performed on a pattern-printed substrate using a combination of a transparent raised printing ink and an ink containing a heating foaming agent. The present invention relates to a method for manufacturing decorative laminates.
従来より模様印刷を施した基板上にスクリーン
印刷を施こして立体感を付与する方法があるが、
得られる化粧板はクリスタルの硬さは感じられる
がつめたい感じがし、又盛り上げ部と平坦模様部
との艷が同一であるため見る方向によつては全体
が平坦に見え、立体感を付与しようとしたにもか
かわらず、逆の結果を生ずることもあつた。 Conventionally, there is a method of screen printing on a pattern-printed substrate to give it a three-dimensional effect.
The resulting decorative board has the hardness of crystal, but it feels cold, and since the ridges of the raised part and the flat patterned part are the same, depending on the direction you look at it, the whole looks flat, giving it a three-dimensional effect. Despite this, the opposite result sometimes occurred.
本発明はかかる従来の欠点を解消するために従
来のスクリーン印刷による化粧板の製造方法にお
いて、加熱発泡剤を混入したインクを用いて盛り
上げ印刷を行い目地やその他の部分を発泡させる
ことにより更に立体感を付与しようとするもので
ある。 In order to eliminate such conventional drawbacks, the present invention has developed a method for manufacturing decorative laminates by conventional screen printing, by performing raised printing using ink mixed with a heating foaming agent to foam the joints and other parts, thereby creating a more three-dimensional effect. It is intended to give a feeling.
すなわち本発明は、所要の下地処理を施こした
常用の基板上に透明インクを用いて盛り上げ印刷
を施こした後、該透明盛り上げ印刷インクを半乾
燥し、ついで該透明盛り上げ印刷インク部以外の
所望部分に加熱発泡剤を混入したインクを用いて
盛り上げ印刷を施こし、透明又は着色透明の上塗
り塗料を全面に塗布し、全体を加熱乾燥して加熱
発泡剤混入インク部を発泡乾燥させるとともに透
明盛り上げ印刷インク部と上塗り塗料を乾燥する
ことを特徴とする立体感を有する化粧板の製造方
法に関する。 That is, the present invention performs raised printing using a transparent ink on a commonly used substrate that has been subjected to necessary base treatment, and then semi-dries the transparent raised printing ink, and then removes the area other than the transparent raised printing ink area. Apply raised printing to the desired area using ink mixed with a heat foaming agent, apply a transparent or colored transparent top coat to the entire surface, heat dry the whole area, foam dry the ink area mixed with the heat foaming agent, and make it transparent. The present invention relates to a method for manufacturing a decorative board having a three-dimensional effect, which comprises drying a raised printing ink portion and a top coat.
以下本発明を図面により更に詳細に説明する。 The present invention will be explained in more detail below with reference to the drawings.
第１図は従来の化粧板を示す断面図。第２図は
本発明の化粧板の実施例を示す断面図。 FIG. 1 is a sectional view showing a conventional decorative board. FIG. 2 is a sectional view showing an embodiment of the decorative board of the present invention.
図中１は基板、２は透明盛り上げインク部、３
は模様印刷紙、４は印刷紙模様部、５は上塗り塗
料、６は発泡盛り上げインク部を示す。 In the figure, 1 is the substrate, 2 is the transparent raised ink part, and 3
4 indicates a patterned printing paper, 4 indicates a patterned portion of the printed paper, 5 indicates a top coat, and 6 indicates a foamed raised ink section.
本発明で用いる常用の基板１とは、合板、パー
テイクルボード、ハードボード、石綿スレート、
石膏ボード等の基材である。 Commonly used substrates 1 used in the present invention include plywood, particle board, hardboard, asbestos slate,
It is a base material for gypsum board, etc.
又、本発明で云う所要の下地処理とは、例えば
各種印刷紙及びシートを販着したり、着色塗料に
て基板上に直接ベタ印刷や模様印刷が施こされて
いる場合、あるいは転写印刷、その他含浸紙を貼
着したり、さらには化学的、機械的にあらかじめ
基板上に凹凸処理が施こされている場合などをい
う。 In addition, the necessary surface treatment referred to in the present invention refers to, for example, cases where various printing papers and sheets are sold, solid printing or pattern printing is performed directly on the substrate with colored paint, transfer printing, In addition, this refers to cases where impregnated paper is pasted, or where the surface of the substrate is chemically or mechanically textured in advance.
本発明ではまずこれら常用の基板１上に下地処
理を施こす。本実施例の場合は模様印刷紙３を貼
着する。ついでスクリーン印刷法にて該模様の所
要部分に合わせて透明インクを用いて透明盛り上
げインク部２を形成し、しかる後該透明盛り上げ
インク部２を半乾燥する。 In the present invention, a base treatment is first performed on these commonly used substrates 1. In this embodiment, patterned printed paper 3 is pasted. Next, transparent raised ink portions 2 are formed using transparent ink in accordance with the required portions of the pattern by screen printing, and then the transparent raised ink portions 2 are semi-dried.
透明インクとしてはアクリル樹脂や酢酸ビニル
樹脂エマルジヨン、エポキシ樹脂、ウレタン樹
脂、塩化ビニール樹脂、エタルセルローズ系樹脂
などを用い、スクリーン印刷に適当なチクソ性を
有するものであればよい。 The transparent ink may be made of acrylic resin, vinyl acetate resin emulsion, epoxy resin, urethane resin, vinyl chloride resin, etalcellulose resin, etc., as long as it has thixotropy suitable for screen printing.
なお本発明で透明盛り上げインク部２を完全乾
燥させることなく半乾燥状態とするのは次工程で
の加熱発泡剤を混入したインクを用いてスクリー
ン印刷を施こす際、スクリーン版の押圧により、
透明盛り上げインク部２の型くずれを防止すると
ともに、最終工程とする上塗り塗料との密着性を
良くするためである。 In the present invention, the transparent raised ink portion 2 is kept in a semi-dry state without being completely dried. When performing screen printing using ink mixed with a heating foaming agent in the next step, by pressing the screen plate,
This is to prevent the transparent raised ink portion 2 from deforming and to improve its adhesion with the final coating paint.
次に透明盛り上げインク部２以外の所望部分に
加熱発泡剤を混入したインクを用いて発泡盛り上
げインク部６を形成する。 Next, a foamed raised ink portion 6 is formed in a desired portion other than the transparent raised ink portion 2 using ink mixed with a heated foaming agent.
なお透明盛り上げ印刷インク部２と発泡盛り上
げインク部６はその模様の一部又は全部を重複さ
せて印刷しても良い。 Note that the transparent raised printing ink portion 2 and the foamed raised ink portion 6 may be printed so that part or all of their patterns overlap.
発泡盛り上げインク部６を形成するインクとし
ては前記した透明インクと同一の樹脂を使用する
のが一般的であるが、異なつていてもよく、該イ
ンク中に着色剤などとともに、Ｄ・Ｐ・Ｔ、Ａ・
Ｄ・Ｃ・Ａ、Ａ・Ｉ・Ｂ・Ｎ、TSH、Ｏ・Ｂ・
Ｓ・Ｈ、炭酸ナトリウム、硫化カルシウムなど常
用の加熱発泡剤を混入して使用する。 Generally, the same resin as the above-mentioned transparent ink is used as the ink forming the foamed raised ink portion 6, but it may be different. T.A.
D.C.A., A.I.B.N., TSH, O.B.
Commonly used heat foaming agents such as S・H, sodium carbonate, and calcium sulfide are used.
その後ウレタン樹脂、アミノアルキツド樹脂等
常用の透明又は着色透明の上塗り塗料５を全面に
塗布し、ついで全体を加熱乾燥して加熱発泡剤混
入インク部６を発泡乾燥させるとともに透明盛り
上げインク部２と上塗り塗料５を乾燥し求める立
体感を有する化粧板を得る。 After that, a commonly used transparent or colored transparent top coat 5 such as urethane resin or amino alkyd resin is applied to the entire surface, and then the whole is heated and dried to foam and dry the heated foaming agent-containing ink part 6, and the transparent raised ink part 2 and the top coat. 5 is dried to obtain a decorative board having the desired three-dimensional effect.
以下本発明の実施例を述べる。 Examples of the present invention will be described below.
実施例 １
合板基板上に重さ23ｇ／m2の模様印刷紙を貼着
し、該印刷紙の柄に一致するようにスクリーン版
を載置し、該スクリーン版上に透明インクとして
アクリル樹脂を流しスキジーにて印刷紙上に透明
盛り上げ印刷を施こす。Example 1 Pattern printed paper weighing 23 g/m 2 was pasted on a plywood substrate, a screen plate was placed so as to match the pattern of the printed paper, and acrylic resin was applied as transparent ink on the screen plate. Apply transparent raised printing on the printing paper using a sink squeegee.
その後80℃熱風循環ドライヤーにて10分間乾燥
しインクを半乾燥状態とする。 Then, dry the ink for 10 minutes using a hot air circulating dryer at 80°C to make the ink semi-dry.
次に上記アクリル樹脂インク中に該インクに対
して加熱発泡剤としてＤ・Ｐ・Ｔを40重量％添加
し、模様印刷紙の他の選ばれた模様部に上記と同
様にスクリーン印刷を施こす。しかる後、上塗り
塗料としてウレタン樹脂を基板上にフローコータ
ーにて100ｇ／m2塗布し、100℃熱風循環式ドライ
ヤーにて30分間乾燥させ、加熱発泡剤混入インク
部を発泡させると同時に上塗り塗料を乾燥させ求
める立体感を有する化粧板を得た。 Next, 40% by weight of D・P・T is added as a heat foaming agent to the above acrylic resin ink, and screen printing is performed on other selected pattern areas of the pattern printing paper in the same manner as above. . After that, 100 g/m 2 of urethane resin was applied as a top coat onto the substrate using a flow coater, and dried for 30 minutes in a hot air circulation dryer at 100°C to foam the ink area containing the foaming agent and apply the top coat at the same time. After drying, a decorative board with the desired three-dimensional effect was obtained.
以上のように本発明方法によれば、発泡盛り上
げインク部により立体感がさらに強調されるとと
もに、発泡盛り上げインク部中に含まれる発泡ガ
スにより、該部分が艷消し状となつて艷有り部分
と対比してより一層立体感が強調される効果があ
る。 As described above, according to the method of the present invention, the three-dimensional effect is further emphasized by the foamed raised ink portion, and the foamed gas contained in the foamed raised ink portion causes the portion to become elongated, resulting in a curved portion. The contrast has the effect of further emphasizing the three-dimensional effect.
第１図は従来の化粧板の断面図。第２図は本発
明の化粧板の実施例を示す断面図。
図中１は基板、２は透明盛り上げインク部、３
は模様印刷紙、４は印刷紙模様部、５は上塗り塗
料、６は発泡盛り上げインク部。
Figure 1 is a cross-sectional view of a conventional decorative board. FIG. 2 is a sectional view showing an embodiment of the decorative board of the present invention. In the figure, 1 is the substrate, 2 is the transparent raised ink part, and 3
4 is a patterned printing paper, 4 is a printed paper pattern part, 5 is a top coat paint, and 6 is a foamed raised ink part.
Claims (1)
透明インクを用いて盛り上げ印刷を施こした後、
該透明盛り上げ印刷インクを半乾燥し、ついで該
透明盛り上げ印刷インク部以外の所望部分に加熱
発泡剤を混入したインクを用いて盛り上げ印刷を
施こし、透明又は着色透明の上塗り塗料を全面に
塗布し、全体を加熱乾燥して加熱発泡剤混入イン
ク部を発泡乾燥させるとともに透明盛り上げ印刷
インク部と上塗り塗料を乾燥することを特徴とす
る立体感を有する化粧板の製造方法。1. On a commonly used board that has undergone the necessary surface treatment,
After applying raised printing using transparent ink,
The transparent raised printing ink is semi-dried, and then raised printing is performed on desired areas other than the transparent raised printing ink area using ink mixed with a heating foaming agent, and a transparent or colored transparent top coat is applied to the entire surface. A method for producing a decorative board having a three-dimensional effect, which comprises heating and drying the entire body to foam-dry the heated foaming agent-containing ink portion, and drying the transparent raised printing ink portion and the top coat.