JPS63256678A - Silicone self-adhesive sheet and tape - Google Patents
Silicone self-adhesive sheet and tapeInfo
- Publication number
- JPS63256678A JPS63256678A JP9217587A JP9217587A JPS63256678A JP S63256678 A JPS63256678 A JP S63256678A JP 9217587 A JP9217587 A JP 9217587A JP 9217587 A JP9217587 A JP 9217587A JP S63256678 A JPS63256678 A JP S63256678A
- Authority
- JP
- Japan
- Prior art keywords
- separator
- silicone adhesive
- silicone
- tape
- adhesive layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
（ａ）産業上の利用分野
本発明は、シリコーン粘着剤層の露出面を被覆するセパ
レータを備えてなるシリコーン粘着シート及びシリコー
ン粘着テープの改良に関し、特に、容易にかつ完全にセ
パレータを剥離して、セパレータ剥離後の透明性を確保
できるようにしたシリコーン粘着シート及びシリコーン
粘着テープに関するものである。Detailed Description of the Invention (a) Industrial Application Field The present invention relates to improvements in silicone adhesive sheets and silicone adhesive tapes comprising a separator that covers the exposed surface of a silicone adhesive layer, and particularly relates to improvements in silicone adhesive sheets and silicone adhesive tapes that can be easily and easily applied. The present invention relates to a silicone adhesive sheet and a silicone adhesive tape that can completely remove the separator and ensure transparency after the separator is removed.
（ｂ）従来の技術
従来、例えば、オーブン電子レンジ用ドアのように、外
側から内部の状態が容易に観察しうるように透明性と、
耐熱性とが同時に要求される場合には、耐熱ガラスが使
用されることが多かった。(b) Conventional Technology Conventionally, for example, a door for an oven or microwave oven has transparency so that the internal state can be easily observed from the outside.
Heat-resistant glass was often used when heat resistance was also required.
しかしながら、耐熱ガラスは破損し易く、装着構造が複
雑になり、重量が重くなる等の欠点を有している。However, heat-resistant glass has drawbacks such as being easily broken, requiring a complicated mounting structure, and being heavy.
このような欠点を解消するために、最近では耐熱プラス
に代えて耐熱性フィルムを使用することが提案されてい
る。In order to eliminate such drawbacks, it has recently been proposed to use a heat-resistant film instead of heat-resistant plus.
即ち、ポリイミドフィルム等の耐熱性フィルムの片面に
、耐熱性が優れたシリコーン粘着剤層を設けてなるシリ
コーン粘着シートを高周波放散防止用のパンチングパネ
ルに貼り合わせることにより、破損し難く、装着構造が
簡単で、しかも、軽量化が図られたオーブン電子レンジ
用ドアが提案されている。In other words, by bonding a silicone adhesive sheet, which is made by providing a silicone adhesive layer with excellent heat resistance on one side of a heat-resistant film such as a polyimide film, to a punching panel for preventing high-frequency radiation, it is difficult to break and the mounting structure is created. A simple and lightweight oven/microwave door has been proposed.
このシリコーン粘着シートのシリコーン粘着剤層（粘着
面）は、通常、これをほこり埃等の異物の付着や他物と
の接触による損傷から保護するたりにセパレ、−タで覆
われる。The silicone adhesive layer (adhesive surface) of this silicone adhesive sheet is usually covered with a separator to protect it from adhesion of foreign matter such as dust or damage due to contact with other objects.
そして、このセパレータとしては、離型剤で背面処理を
してなる離型紙もしくは離型フィルムが使用される。As this separator, a release paper or a release film whose back surface is treated with a release agent is used.
（ｃ）発明が解決しようとする問題点
ところで、シリコーン粘着剤は、非常に優れた耐熱性を
有するとともに、粘着力が強力であることがよく知られ
ている。この粘着力の強さが仇となって、セパレータを
引き剥がすときに非常に強い引き剥がし力が必要になる
うえ、セパレータの一部分が薄く剥がし残されて、粘着
剤層の表面に付着したり、シリコーン粘着剤層がつや消
し状態になり、透明性が損なわれるという問題があった
。(c) Problems to be Solved by the Invention Incidentally, it is well known that silicone adhesives have extremely excellent heat resistance and strong adhesive strength. This strong adhesive force becomes the enemy, and when peeling off the separator, a very strong peeling force is required, and a thin part of the separator may be left behind and adhere to the surface of the adhesive layer. There was a problem in that the silicone adhesive layer became matte and the transparency was impaired.
本発明は、上記の事情を考慮してなされたものであって
、容易にかつ完全にセパレータを剥離して、セパレータ
剥離後の透明性を確保できるようにしたシリコーン粘着
シート及びシリコーン粘着テープを提供することを目的
とするものである。The present invention has been made in consideration of the above circumstances, and provides a silicone adhesive sheet and a silicone adhesive tape that can easily and completely peel off a separator and ensure transparency after the separator is peeled off. The purpose is to
（ｄ）問題点を解決するための手段
本発明に係るシリコーン粘着シート及びシリコーン粘着
テープでは、耐熱性を有するフィルム・テープと、該フ
ィルム或いはテープの少なくとも片面に積層されたシリ
コーン粘着剤層と、このシリコーン粘着剤層を被覆する
セパレータとからなるものにおいて、上記の目的を達成
するために、上記セパレータを親木性フィルム・テープ
で構成する、という技術的手段が講じられている。(d) Means for solving the problem The silicone adhesive sheet and silicone adhesive tape according to the present invention include a heat-resistant film/tape, and a silicone adhesive layer laminated on at least one side of the film or tape. In order to achieve the above object, a technical measure has been taken in which the separator is made of a wood-philic film/tape.
耐熱性を有するフィルム・テープの素材とじては、ポリ
アミド系、ポリイミド系、ポリエーテル系、ポリエステ
ル系、シリコーン樹脂、ポリ４７ツ化エチレン（Ｐ Ｔ
Ｅ Ｆ ）等のフッ素樹脂、その他ポリフェニレンサ
ルファイド（ｐ ｐ ｓ ）、ポリベンズイミグゾール
等の合成樹脂が使用される。Materials for heat-resistant films and tapes include polyamides, polyimides, polyethers, polyesters, silicone resins, and polyethylene chloride (PT).
Fluororesins such as E F ) and other synthetic resins such as polyphenylene sulfide (pps) and polybenzimigsol are used.
ポリアミド系合成樹脂としては、芳香族ポリアミド等が
例として挙げられる。Examples of polyamide-based synthetic resins include aromatic polyamides and the like.
ポリイミド系合成樹脂としては、ポリイミド樹脂、ビス
マレイミド・トリアジン樹脂（ＢＴ樹脂）、ポリアミド
イミド樹脂、ポリアミドビスマレイミドＩ（ＪＪＷ等が
その例として挙げられる。Examples of the polyimide-based synthetic resin include polyimide resin, bismaleimide triazine resin (BT resin), polyamideimide resin, and polyamide bismaleimide I (JJW).
ポリエーテル系合成樹脂としては、エポキシ樹層、ポリ
アセタール（ポリオキシメチレン）樹脂、ポリフェニレ
ンオキサイド（ＰＰＯ）Ｉ！脂、変性ポリフェニレンオ
キサイド樹脂、ポリエーテルエーテルケトン（ＰＥＥＫ
）Ｉｔ脂、ポリエーテルサルホン（Ｐ Ｅ Ｓ ）樹脂
、ポリサルホン樹脂等がその例として挙げられる。Examples of polyether-based synthetic resins include epoxy tree layer, polyacetal (polyoxymethylene) resin, and polyphenylene oxide (PPO) I! resin, modified polyphenylene oxide resin, polyether ether ketone (PEEK)
) It resin, polyethersulfone (PES) resin, polysulfone resin, etc. are mentioned as examples.
ポリエステル系合成樹脂としては、ポリエチレンテレ７
タレー）ＣＰＥＴ）ｔＨ脂、ポリブチレンテレ７タレー
）（ＰＢＴ）樹脂、ボリアリレート（Ｕポリマー）樹脂
、ポリカーボネート（ポリ炭酸エステル）樹脂、ポリオ
キシベンゾイル（芳香族ポリエステル）樹脂等がその例
として挙げられる。As a polyester synthetic resin, polyethylene tele 7
Examples include tH resin (CPET), polybutylene (PBT) resin, polyarylate (U polymer) resin, polycarbonate (polycarbonate) resin, polyoxybenzoyl (aromatic polyester) resin, etc. .
耐熱性フィルムの厚さは、特に限定されるものではな（
、その用途に応じて適宜選定すればよい。The thickness of the heat-resistant film is not particularly limited (
, may be selected as appropriate depending on the application.
例えば、オープン電子レンジのドア用としては５〜１０
００μ醜程度の厚さが適当とされる。For example, for an open microwave door, 5 to 10
A thickness of approximately 00 μm is considered appropriate.
シリコーン粘着剤としては公知のものを使用すればよく
、また、これにペンソイルパーオキサイド等の過酸化物
触媒を添加することも可能である。Any known silicone adhesive may be used, and it is also possible to add a peroxide catalyst such as pensoyl peroxide.
具体的には熱硬化型シリコーン樹脂を接着成分とし、こ
れにベンゾイルパーオキシドの如き有機過酸化物や白金
触媒などの硬化剤その他の公知の添加剤を配合したもの
が用いられる。Specifically, a thermosetting silicone resin is used as the adhesive component, and an organic peroxide such as benzoyl peroxide, a curing agent such as a platinum catalyst, and other known additives are blended therein.
熱硬化型シリコーン樹脂としては、従来公知のものを広
く適用できるが、その代表的なものを例示すると、下記
のａ−ｄ成分からなるシリコーン樹脂組成物を挙げるこ
とができる。As the thermosetting silicone resin, a wide variety of conventionally known thermosetting silicone resins can be used, and typical examples thereof include silicone resin compositions consisting of the following components a to d.
ａ）けい素１原子当たりのメチル基およびフエニル基数
の平均値が１．４〜１．８で、フェニル基とけい素原子
の比が０．５：１〜０．８：１であり、けい素原子に結
合した水酸基を含むようなメチルフェニルボリシロキサ
ンム（脂。a) The average number of methyl groups and phenyl groups per silicon atom is 1.4 to 1.8, the ratio of phenyl groups to silicon atoms is 0.5:1 to 0.8:1, and silicon Methylphenylborisiloxanes (fats) containing hydroxyl groups attached to atoms.
ｂ）けい素１原子当たり０．１５〜０．６０のビニル基
を含み、１分子当たりのけい素原子数の平均値が８以上
で、フェニル基とけい素原子の比が０．３５：１．７５
〜１．７５：１であり、又けい素−炭酸結合によってけ
い素原子に付加されているけい素１原子当たりの炭化水
素基数の平均値が１以上であり、上記炭化水素基がメチ
ル基、フェニル基およびビニル基から選択されたもので
あるポリシロキサン。b) contains 0.15 to 0.60 vinyl groups per silicon atom, the average number of silicon atoms per molecule is 8 or more, and the ratio of phenyl groups to silicon atoms is 0.35:1. 75
~1.75:1, and the average number of hydrocarbon groups per silicon atom added to a silicon atom through a silicon-carbonate bond is 1 or more, and the hydrocarbon group is a methyl group, Polysiloxanes selected from phenyl and vinyl groups.
ｃ） １分子当たりのＳｉＨ基数の平均値が２以上で、
けい素原子の残りの原子価は芳香族炭化水素基、メチル
基及びＳ ｉｏ Ｓ ｉ結合鎖によって本質的にすべて
満たされ、上記す成分のゲル化に必要な分量で存在する
ような上記ａＳｂ成分と相溶しうるシロキサン。c) The average number of SiH groups per molecule is 2 or more,
The aSb component is such that the remaining valences of the silicon atoms are essentially all satisfied by aromatic hydrocarbon groups, methyl groups, and S io Si bonded chains, and are present in the amounts necessary for gelation of the component. Siloxane that is compatible with.
ｄ）上記のｂ成分とＣ成分との反応を促進するための触
媒。d) A catalyst for promoting the reaction between component b and component C above.
このようなシリコーン樹脂組成物は、ｂ成分とＣ成分と
の反応でゲル化するが、このデル化物はなお感圧接着特
性を示し、これを更に高温に加熱してＣ成分の硬化反応
を進めることにより、強固な接着力と優れた耐熱性、耐
温性とその他の諸特性を発揮する。Such a silicone resin composition gels due to the reaction between component B and component C, but this gelatinized product still exhibits pressure-sensitive adhesive properties and is further heated to a high temperature to advance the curing reaction of component C. As a result, it exhibits strong adhesive strength, excellent heat resistance, temperature resistance, and other properties.
市販品に、東しシリコーン社製の商品名５Ｈ−４２８０
があるが、これはＣ成分を含まないａＳｂ。Commercially available products include product name 5H-4280 manufactured by Toshi Silicone Co., Ltd.
However, this is aSb which does not contain C component.
Ｃ三成分からなる固形分６０〜６３重量％程度のもので
ある。The solid content is approximately 60 to 63% by weight, consisting of the three C components.
上記耐熱性を有するフィルム・シートに上記シリコーン
樹脂組成物を塗着するに当たっては、一般に浸漬法、刷
毛塗りなどの公知の方法で塗布したのち加熱乾燥してシ
リコーン粘着剤層が形成される。When applying the silicone resin composition to the heat-resistant film/sheet, it is generally applied by a known method such as dipping or brushing, and then heated and dried to form a silicone adhesive layer.
シリコーン粘着剤層の厚みとしては、片面ないし両面塗
布のいずれの場合でも塗着後の全体厚みが塗着前の厚み
の１．１〜３．０倍程度となるようにするのが望ましい
。The thickness of the silicone pressure-sensitive adhesive layer is preferably such that the total thickness after coating is about 1.1 to 3.0 times the thickness before coating, regardless of whether it is coated on one or both sides.
なお、シリコーン樹脂組成物として上記ａ＝ｄ成分から
なるものを用いたものでは、塗布後の加熱乾燥中又はそ
の後の加熱処理によってｂ成分とＣ成分との反応を促進
させる。In addition, when using a silicone resin composition consisting of the above components a=d, the reaction between component b and component C is promoted during heat drying after coating or by subsequent heat treatment.
そして、本発明の特徴は、上記シリコーン粘着剤層を積
層してなるシリコーン粘着シートにおいてそのシリコー
ン粘着剤層の露出面を被覆するセパレータが、親水性を
有するフィルム・テープで構成されている点にある。A feature of the present invention is that in the silicone adhesive sheet formed by laminating the silicone adhesive layers, the separator that covers the exposed surface of the silicone adhesive layer is composed of a hydrophilic film/tape. be.
上記親水性を有するフィルム・テープとしては親水性が
あれば特に限定されることはなく、例えば、セロファン
、ビニロン、セルロースアセテート等が挙げられる。The above-mentioned hydrophilic film/tape is not particularly limited as long as it is hydrophilic, and examples thereof include cellophane, vinylon, cellulose acetate, and the like.
これらの中では、帯電性がなく、このためゴミの付着が
ないうえ、引張り強さが大で、伸びが小さいのでシート
に腰があり、そのため自動包装に適しており、更に安価
であるセロファンが推奨される。Among these, cellophane is non-electrostatic, so it does not attract dust, has high tensile strength, and has low elongation, making the sheet stiff, making it suitable for automatic packaging, and also cheaper. Recommended.
セパレータの厚さは引き剥がす時に破断を生じ一般に、
５〜３００μ艶とすることが好ましい。The thickness of the separator generally causes breakage when it is peeled off.
It is preferable to have a gloss of 5 to 300μ.
その厚さが、５μ論を下回るときには引き剥がすときに
破断を生じる恐れがあるので好ましくなく、一方、３０
０μ−を越えるとコストが高くなると共に取扱い性の点
で好ましくない。If the thickness is less than 5 μm, it is not preferable because it may cause breakage when peeled off.
If it exceeds 0 μ-, the cost becomes high and it is not preferable in terms of handling.
セロファンの場合、その厚さは、コストダウンを図るう
えで、一般に市販されている４０〜６０μ−とすること
が一層好ましい。In the case of cellophane, the thickness is more preferably 40 to 60 microns, which is generally commercially available, in order to reduce costs.
（ｅ）作用
上記の構成において、セパレータを除去する前にシリコ
ーン粘着シート或いはシリコーン粘着テープを水に浸漬
させたり、これに噴霧等によってセパレータに水分を吸
収させると、シリコーン粘着剤層が有する撥水力により
シリコーン粘着剤層とセパレータとの粘着力が大幅に弱
められ、非常に弱い力で容易にセパレータを完全に除去
することができる。(e) Effect In the above structure, if the silicone adhesive sheet or silicone adhesive tape is immersed in water or sprayed on the separator to absorb water before removing the separator, the water repellency of the silicone adhesive layer is reduced. This greatly weakens the adhesive force between the silicone adhesive layer and the separator, making it possible to easily and completely remove the separator with very weak force.
この場合、シリコーン粘着剤層の粘着力が大幅に弱めら
れているからセパレータの一部分が剥ががなく、従って
、セパレータ剥離後の透明性を確保できる作用を有する
のである。In this case, since the adhesive force of the silicone adhesive layer is significantly weakened, a portion of the separator cannot be peeled off, thus ensuring transparency after the separator is peeled off.
ところで、セパレータを除去されたシリコーン粘着剤層
の粘着面には、水分は殆ど残されず、ごく僅かに残され
た水分は直ちに蒸発してなくなるので、セパレータの除
去の後、特に、乾燥工程を経ることなしに貼着作業を行
うことができる。By the way, almost no moisture remains on the adhesive surface of the silicone adhesive layer from which the separator has been removed, and the very small amount of moisture that remains evaporates immediately. You can perform the pasting work without any problems.
（ｆ）実施例
以下、本発明の実施例を図面に基づき詳細に説明するが
、本発明はこれに限定されるものではなり１ 。(f) Examples Hereinafter, examples of the present invention will be explained in detail based on the drawings, but the present invention is not limited thereto1.
実施例ｌ
Ｐｔ４ｉ図は本発明の一実施例に係るシリコーン粘着シ
ートの構成を模式的に示す縦断面図である。Example 1 Pt4i Figure is a longitudinal cross-sectional view schematically showing the structure of a silicone pressure-sensitive adhesive sheet according to an example of the present invention.
このシリコーン粘着シートは、耐熱性を有するフィルム
１と、該フィルム１の少な（とも片面、この場合、片面
に積層されたシリコーン粘着剤層２と、このシリコーン
粘着剤層２を被覆するセパレータ３とからなり、このセ
パレータ３は親水性フィルムで構成されている。This silicone adhesive sheet consists of a heat-resistant film 1, a silicone adhesive layer 2 laminated on one side of the film 1 (in this case, a silicone adhesive layer 2 laminated on one side, and a separator 3 covering this silicone adhesive layer 2). The separator 3 is made of a hydrophilic film.
上記耐熱性フィルム１の素材としては、ポリアミド系回
層、ポリイミド系樹脂、ポリエーテル系樹脂、ポリエー
テル系樹脂、シリコーン樹脂、ポリ４７）化エチレン（
ＰＴＥＦ）等のフッ素樹脂、その他ポリフェニレンサル
ファイド（Ｐ Ｐ Ｓ ）、ポリベンズイミグゾール等
の合成！Ｉ脂が使用される。Materials for the heat-resistant film 1 include polyamide circuit layer, polyimide resin, polyether resin, polyether resin, silicone resin, poly(47) ethylene (
Synthesis of fluororesins such as PTEF), polyphenylene sulfide (PPS), polybenzimigsol, etc.! I fat is used.
ここでは、特に透明性と耐熱性とが共に優れている耐熱
性フィルム（宇部興産製、商品名ユービレックスーＳ）
が使用されている。Here, we will introduce a heat-resistant film that has particularly excellent transparency and heat resistance (manufactured by Ube Industries, product name: Ubilex-S).
is used.
また、上記耐熱性フィルム１の厚さは、特に限定される
ものではなく、その用途に応じて適宜選定される。ここ
では、オーブン電子レンジのドア用として、耐熱性フィ
ルム１の厚さは５０μ論とされている。Further, the thickness of the heat-resistant film 1 is not particularly limited, and is appropriately selected depending on its use. Here, the thickness of the heat-resistant film 1 is assumed to be 50 μm for the door of a microwave oven.
上記シリコーン粘着剤としては熱硬化型シリコーン樹脂
を接着成分とし、これにベンゾイルパーオキシド（Ｂ、
Ｐ、Ｏ）の如き有機過酸化物や白金触媒などの硬化剤そ
の他の公知の添加剤を配合したものが用いられる。The above-mentioned silicone adhesive uses a thermosetting silicone resin as an adhesive component, and contains benzoyl peroxide (B,
A compound containing an organic peroxide such as P, O), a curing agent such as a platinum catalyst, and other known additives is used.
熱硬化型シリコーン樹脂としては、上述した従来公知の
ものを広く適用できる。As the thermosetting silicone resin, the conventionally known ones mentioned above can be widely used.
上記耐熱性を有するフィルム１に上述したシリコーン樹
脂組成物を塗着するに当たっては、一般に浸漬法、刷毛
塗りなどの公知の方法で塗布したのち加熱乾燥してシリ
コーン粘着剤層２が形成される。When applying the above-described silicone resin composition to the heat-resistant film 1, it is generally applied by a known method such as dipping or brushing, and then heated and dried to form the silicone adhesive layer 2.
シリコーン粘着剤層２の厚みとしては、片面ないし両面
塗布のいずれの場合でも塗着後の全体厚みが塗着前の厚
みの１．１〜３．０倍程度となるようにするのがよい。The thickness of the silicone adhesive layer 2 is preferably such that the total thickness after coating is about 1.1 to 3.0 times the thickness before coating, regardless of whether it is coated on one or both sides.
上記シリコーン樹脂組成物は塗布後の加熱乾燥中又はそ
の後の加熱処理によって反応が促進される。The reaction of the above-mentioned silicone resin composition is promoted during heat drying after coating or by subsequent heat treatment.
ここでは、市販のもの（信越化学製、商品名シリコーン
粘着剤ＫＲ−１２０）が使用され、これに必要に応じて
Ｂ、Ｐ、Ｏ等の過酸化物触媒が添加されている。Here, a commercially available product (manufactured by Shin-Etsu Chemical, trade name silicone adhesive KR-120) is used, to which peroxide catalysts such as B, P, and O are added as necessary.
又、このシリコーン粘着剤層２は、スプレーイング、ａ
−ルコーティング等の公知の手法により上記セパレータ
３は、親水性を有するフィルムであれば特に限定される
ことはなく、例えば、セロファン、ビニロン、セルロー
スアセテート等の親水性フィルムを使用することが可能
である。Moreover, this silicone adhesive layer 2 can be applied by spraying, a
- The separator 3 can be formed by a known method such as coating, without any particular limitation, as long as it is a hydrophilic film; for example, it is possible to use a hydrophilic film such as cellophane, vinylon, cellulose acetate, etc. be.
ここでは、帯電性がなく、このためゴミの付着がないう
え、引張り強さが大で、伸びが小さいのでシートに腰が
あり、そのため自動包装に適しており、更に安価である
セロファンフィルムでセパレータ３が構成されている。Here, the separator is made of cellophane film, which is non-electrostatic and therefore does not attract dust, has high tensile strength, and has low elongation, so the sheet has stiffness, making it suitable for automatic packaging. 3 are made up.
セパレータ３の厚さは引き剥がす時に破断を生じない程
度の機械的強度を有することが必要であり、この場合、
一般市場で安価に入手できる４０μ鴫のセロファンフィ
ルムが使用されている。The thickness of the separator 3 needs to have enough mechanical strength to prevent breakage when peeled off, and in this case,
A 40 μm cellophane film, which is inexpensively available on the general market, is used.
上記の構成において、セパレータ３を除去して耐熱性フ
ィルム１をシリコーン粘着剤ＪｖＪ２を介して図示しな
い高周波放散防止用パンチングパネルに貼着する場合、
セパレータ３を除去する前にシリコーン粘着シート全体
を水に浸漬させたり或いはセパレータ３を約３０秒間に
わたって水で濡らｌ ｆｉ’ ｎ ｌ−ｆ 、 セハレ
−９２＋：” ＊ 分１ｙ ＠ Ｗ ５−＋ Ｘそうす
ると、シリコーン粘着剤層２が有する撥水力によりシリ
コーン粘着剤ＷＩ２とセパレータ３との粘着力が大幅に
弱められ、非常に弱い力で容易にセパレータを完全に除
去することができ、従って、セパレータ３の一部分が剥
がし残されたり、艶消しになることがなく、セパレータ
３の剥離後の透明性を確保できるのである。In the above configuration, when the separator 3 is removed and the heat-resistant film 1 is attached to a punching panel for preventing high-frequency radiation (not shown) via the silicone adhesive JvJ2,
Before removing the separator 3, the entire silicone adhesive sheet is immersed in water, or the separator 3 is wetted with water for about 30 seconds. X Then, due to the water repellency of the silicone adhesive layer 2, the adhesive force between the silicone adhesive WI2 and the separator 3 is significantly weakened, and the separator can be easily and completely removed with very weak force. The transparency of the separator 3 after peeling can be ensured without leaving a part of the separator 3 peeled off or becoming matte.
尚、セパレータ３を除去されたシリコーン粘着剤層２の
粘着面には、水分は殆ど残されず、ごく僅かに残された
水分は直ちに蒸発してなくなるので、セパレータ３の除
去の後に、シリコーン粘着剤層２の乾燥工程を経ること
なく貼着作業を行うことができるのである。It should be noted that almost no moisture remains on the adhesive surface of the silicone adhesive layer 2 from which the separator 3 has been removed, and the very small amount of moisture that remains evaporates immediately. The adhesion work can be carried out without going through the drying process of layer 2.
実施例２
本発明の一実施例に係るシリコーン粘着テープは、図示
はしないが、上記のシリコーン粘着シートと同様に、耐
熱性を有するテープと、該テープの少なくとも片面に積
層されたシリコーン粘着剤層と、このシリコーン粘着剤
層を被覆するセパレータとからなり、このセパレータが
親水性テープで構成されている。Example 2 Although not shown, a silicone adhesive tape according to an example of the present invention, like the silicone adhesive sheet described above, includes a heat-resistant tape and a silicone adhesive layer laminated on at least one side of the tape. and a separator covering this silicone adhesive layer, and this separator is made of a hydrophilic tape.
ここでは、耐熱性を有するテープの素材として特に耐熱
性が優れているポリイミドテープ（デュポン社製、商品
名カプトン）が使用される。Here, polyimide tape (manufactured by DuPont, trade name: Kapton), which has particularly excellent heat resistance, is used as a material for the tape having heat resistance.
また、シリコーン粘着剤層は、シリコーン粘着剤（束レ
シリコーン社製、商品名シリコーン粘着剤Ｓ Ｈ−４２
８０）に過酸化物触媒を添加したもので構成されている
。In addition, the silicone adhesive layer is made of silicone adhesive (manufactured by Tsukushi Resilicone Co., Ltd., trade name silicone adhesive S H-42).
80) to which a peroxide catalyst has been added.
その池の構成、作用の説明は、上記のシリコーン粘着シ
ートのそれらの説明と同様であり、それらの説明と重複
するので、ここでは省略する。The explanation of the structure and function of the pond is the same as that of the silicone pressure-sensitive adhesive sheet described above, and since it overlaps with those explanations, it will be omitted here.
このように構成されたシリコーン粘着テープは、従来の
背面処理をしたシリコーン粘着テープではテープ幅が大
きくなればなるほど大きな引き剥がし力が必要となり、
広幅のテープの場合には引き剥がしが困難になる場合も
あろのに対して、広幅のテープの場合でも殆ど引き剥が
し力を要しないという程度に引き剥がし力を小さくする
ことができる。With silicone adhesive tapes constructed in this way, conventional silicone adhesive tapes with backside treatment require greater peeling force as the tape width increases.
In the case of a wide tape, it may be difficult to peel it off, but even in the case of a wide tape, the peeling force can be reduced to such an extent that almost no peeling force is required.
尚、上記の各実施例では、シリコーン粘着剤層２が耐熱
性フィルム１或いは耐熱性テープの片面のみに積層され
ているが、本発明は耐熱性フィルム１或いは耐熱性テー
プのの両面にシリコーン粘着剤層２を積層し、各シリコ
ーン粘着剤層２を親水性のセパレータ３で保護するよう
に構成したシリコーン粘着フィルム或いはシリコーン粘
着テープにも適用できるのである。In each of the above embodiments, the silicone adhesive layer 2 is laminated on only one side of the heat-resistant film 1 or the heat-resistant tape, but in the present invention, the silicone adhesive layer 2 is laminated on both sides of the heat-resistant film 1 or the heat-resistant tape. It can also be applied to a silicone adhesive film or a silicone adhesive tape in which adhesive layers 2 are laminated and each silicone adhesive layer 2 is protected by a hydrophilic separator 3.
（ｇ）発明の効果
以上のように、本発明に係るシリコーン粘着シート或い
はシリコーン粘着テープは、これを構成するシリコーン
粘着剤層を被覆するセパレータが、親水性フィルム或い
は親水性テープで構成されてなるものである。(g) Effects of the invention As described above, in the silicone adhesive sheet or silicone adhesive tape according to the present invention, the separator that covers the silicone adhesive layer constituting the sheet is composed of a hydrophilic film or a hydrophilic tape. It is something.
従って、上記セパレータに水分を与えることにより、シ
リコーン粘着剤層の撥水性が発揮されてシリコーン粘着
剤層とセパレータとの粘着力を非常に弱くすることがで
き、この結果、容易に且つ完全にセパレータを剥離でき
る効果を有するのである。Therefore, by adding moisture to the separator, the water repellency of the silicone adhesive layer is exhibited, and the adhesive force between the silicone adhesive layer and the separator can be made very weak.As a result, the separator can be easily and completely removed. It has the effect of peeling off.
Ｐｔ５１図は本発明の一実施例に係るシリコーン粘着シ
ートの構成を模式的に示す縦断面図である。
１・・・耐熱性フィルム、２・・・シリコーン粘着剤層
、３・・・セパレータ。Pt51 is a vertical cross-sectional view schematically showing the structure of a silicone pressure-sensitive adhesive sheet according to an embodiment of the present invention. DESCRIPTION OF SYMBOLS 1...Heat-resistant film, 2...Silicone adhesive layer, 3...Separator.
Claims (4)
とも片面に積層されたシリコーン粘着剤層と、このシリ
コーン粘着剤層を被覆するセパレータとからなるシリコ
ーン粘着シートにおいて、上記セパレータを親水性フィ
ルムで構成したことを特徴とするシリコーン粘着シート
。(1) A silicone adhesive sheet consisting of a heat-resistant film, a silicone adhesive layer laminated on at least one side of the film, and a separator covering this silicone adhesive layer, in which the separator is made of a hydrophilic film. A silicone adhesive sheet that is characterized by:
求の範囲第１項に記載のシリコーン粘着シート。(2) The silicone adhesive sheet according to claim 1, wherein the hydrophilic film is made of cellophane.
片面に積層されたシリコーン粘着剤層と、このシリコー
ン粘着剤層を被覆するセパレータを備えるシリコーン粘
着テープにおいて、上記セパレータを親水性テープで構
成したことを特徴とするシリコーン粘着テープ。(3) A silicone adhesive tape comprising a heat-resistant tape, a silicone adhesive layer laminated on at least one side of the tape, and a separator covering the silicone adhesive layer, wherein the separator is made of a hydrophilic tape. A silicone adhesive tape characterized by:
の範囲第３項に記載のシリコーン粘着テープ。(4) The silicone adhesive tape according to claim 3, wherein the hydrophilic tape is made of cellophane.