JPS63247330A - Zinc alloy for hot dipping for forming olive-gray colored plating and formation of above-mentioned colored plating - Google Patents
Zinc alloy for hot dipping for forming olive-gray colored plating and formation of above-mentioned colored platingInfo
- Publication number
- JPS63247330A JPS63247330A JP62080500A JP8050087A JPS63247330A JP S63247330 A JPS63247330 A JP S63247330A JP 62080500 A JP62080500 A JP 62080500A JP 8050087 A JP8050087 A JP 8050087A JP S63247330 A JPS63247330 A JP S63247330A
- Authority
- JP
- Japan
- Prior art keywords
- olive
- alloy
- plating
- hot
- zinc alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
産呈上二剋■立■
本発明は、鉄鋼にオリーブ灰色の着色メッキを形成する
ための溶融亜鉛合金及び該亜鉛合金を用いて鉄鋼にオリ
ーブ灰色の着色メッキを形成する方法に関する。[Detailed description of the invention] The present invention relates to a molten zinc alloy for forming an olive gray colored plating on steel, and a method for forming an olive gray colored plating on steel using the zinc alloy. Regarding how to.
皿米鬼及先
従来、溶融亜鉛を用いてメッキを施した溶融亜鉛メッキ
鋼は、建築、土木、電力通信、運輸、農業及び水産等の
部門での材料や施設に至る広範囲な分野において耐食材
料として使用されている。Conventionally, hot-dip galvanized steel, which is plated using molten zinc, is used as a corrosion-resistant material in a wide range of fields, including materials and facilities in sectors such as architecture, civil engineering, power communications, transportation, agriculture, and fisheries. is used as.
一方、近年、鉄鋼製品の用途の多様化に伴い、特に、鉄
塔、照明用ポール、ガードレール、種々の仮設用架台、
外板等では、従来の溶融亜鉛メッキ鋼のような金属色の
ものよりも周囲の環境に適合して美観性を呈する着色溶
融亜鉛メッキ鋼が要望されるようになり、今後、建築、
土木、電力通信等のほかに、運輸、農業及び水産等の部
門においても着色溶融亜鉛メッキ鋼の巾広い需要が見込
まれる。On the other hand, in recent years, with the diversification of uses for steel products, in particular steel towers, lighting poles, guardrails, various temporary frames,
For exterior panels, etc., there is a growing demand for colored hot-dip galvanized steel, which is more aesthetically pleasing and matches the surrounding environment than conventional hot-dip galvanized steel.
In addition to civil engineering, power communications, etc., a wide range of demand for colored hot-dip galvanized steel is expected in sectors such as transportation, agriculture, and fisheries.
従来の溶融亜鉛メッキ鋼の着色法としては、該メッキ鋼
に塗装により着色することが主として行われているが、
溶融亜鉛メッキ鋼のメッキ被膜中のZnは活性なため、
塗料の油分の構成分である脂肪酸が徐々にアルカリ分解
して亜鉛石けんを形成するようになる。そのため、着色
に用いた塗料の皮膜がメッキ皮膜表面に付着せずに剥離
するに至る欠点がある。The conventional coloring method for hot-dip galvanized steel is mainly to color the galvanized steel by painting.
Since Zn in the plating film of hot-dip galvanized steel is active,
The fatty acids that make up the oil component of the paint gradually decompose with alkali to form zinc soap. Therefore, there is a drawback that the paint film used for coloring does not adhere to the surface of the plating film and peels off.
したがって、従来はこのような欠点を防ぐために、鉄鋼
に溶融亜鉛を用いてメッキを施し、ついで得られたメッ
キ鋼を大気中に1〜3週間暴露して上記メッキ皮膜上に
さらにZn (jH)いZnO1ZnCO3及びZnC
1を等の腐食生成物を形成させ、次いでメッキ鋼の表面
をクリーニングした後、着色のための塗装を施すという
煩雑な操作を行うことが余儀なくされている。Therefore, in order to prevent such defects, conventionally, steel is plated with molten zinc, and then the plated steel obtained is exposed to the atmosphere for 1 to 3 weeks to further coat the plated film with Zn (jH). ZnO1ZnCO3 and ZnC
It is necessary to perform the complicated operations of forming corrosion products such as No. 1, cleaning the surface of the plated steel, and then applying a coating for coloring.
日が解ンしようとする課題
本発明は、溶融亜鉛メッキ鋼の着色における叙上の問題
点に鑑みなされたものであって、鉄鋼母材に溶融亜鉛に
よるメッキとオリーブ灰色に着色した溶融亜鉛メッキ鋼
を得るための溶融メッキ用亜鉛合金を提供すること、及
び該亜鉛合金を使用して鉄鋼にオリーブ灰色の着色メッ
キを形成するための方法を提供することを課題とする。The present invention was made in view of the above-mentioned problems in coloring hot-dip galvanized steel. It is an object of the present invention to provide a zinc alloy for hot-dip plating to obtain steel, and to provide a method for forming an olive gray colored plating on steel using the zinc alloy.
以下本発明の詳細な説明する。The present invention will be explained in detail below.
衾肌立盪底
本発明の特徴は、■0.2〜0.8重量%Mn −Zn
の組成を有するオリーブ灰色の着色メッキを形成するた
めの溶融メッキ用亜鉛合金及び■該溶融メッキ用亜鉛合
金を用いて浴温度490〜530℃で鉄鋼材料にメッキ
を施し、次いでメッキ鉄鋼材料を500〜520℃の温
度の雰囲気中で50〜150秒加熱した後1.a水冷す
るか又は大気中で強制空冷復温水冷して鉄鋼にオリーブ
灰色の着色メッキを形成することにある。Features of the present invention include: ■ 0.2 to 0.8% by weight Mn-Zn
A zinc alloy for hot-dip plating to form an olive gray colored plating having the composition; After heating for 50-150 seconds in an atmosphere at a temperature of ~520°C1. a) To form an olive gray colored plating on steel by water cooling or forced air cooling and reheating water cooling in the atmosphere.
1 を”するための
本発明においては、溶融亜鉛合金に主として使用する亜
鉛地金であるJIS H2107に規定される最純亜鉛
地金地(99,995%以上)もしくは特殊亜鉛地金(
99,99%以上)に対し0.2〜0.8重量%の割合
のMnを添加、含有させた溶融亜鉛合金浴を用いてメッ
キを行う、なお、溶融亜鉛合金に使用する上記亜鉛地金
はpb含有量が0.005重量%以下であることが好ま
しい。1. In the present invention, the purest zinc ingot (99,995% or more) specified in JIS H2107, which is the zinc ingot mainly used for molten zinc alloy, or the special zinc ingot (
99.99% or more), plating is performed using a molten zinc alloy bath containing 0.2 to 0.8% by weight of Mn. It is preferable that the pb content is 0.005% by weight or less.
上記組成の溶融亜鉛合金浴を用いて、オリーブ灰色の着
色メッキを行うには、被メツキ母材である鉄鋼材料を4
90〜530℃の浴温度で少なくとも1分間浸漬し、次
いでメッキ鋼材を浴から引上げて500〜520℃の温
度の雰囲気中で50〜150秒間加熱した後、温水冷す
るかもしくは大気中で強制空冷復温水冷する。In order to perform olive gray colored plating using a molten zinc alloy bath having the above composition, the steel material that is the base material to be plated must be
Immerse for at least 1 minute at a bath temperature of 90-530°C, then remove the plated steel from the bath and heat for 50-150 seconds in an atmosphere at a temperature of 500-520°C, followed by cooling with hot water or forced air cooling in the atmosphere. Cool with reheated water.
上述のとおり、0.2〜0.8重量%Mn −Znの組
成の溶融亜鉛合金浴を用いてオリーブ灰色の着色メッキ
を形成するには、メッキを施した鋼材を500〜520
℃の温度の雰囲気中で加熱することが重要である。As mentioned above, in order to form an olive gray colored plating using a molten zinc alloy bath having a composition of 0.2 to 0.8 wt% Mn-Zn, the plated steel material must be
It is important to heat in an atmosphere at a temperature of °C.
また、溶融亜鉛合金浴の組成及びメッキ処理条件が上述
の特定範囲外になると、着色メッキの色相にムラが生じ
たり、色相が消失するほか、メッキにより生成した着色
酸化膜が剥離して所望のオリーブ灰色の色相のメッキが
得られなくなる。In addition, if the composition of the molten zinc alloy bath and the plating conditions are outside the specified ranges mentioned above, the hue of the colored plating may become uneven or disappear, and the colored oxide film formed by plating may peel off, resulting in the desired color being removed. It is no longer possible to obtain plating with an olive gray hue.
光凱皇四果
以上述べたとおり、本発明に従って特定な組成の溶融亜
鉛合金浴を用いて、特定な条件下で鉄鋼材料にメッキを
施し、次いでこれを加熱して温水冷もしくは強制空冷復
温水冷することによって、均一なオリーブ灰色の色相を
呈するメッキを形成し得るので、用途により美観上オリ
ーブ灰色の色彩を呈することが望まれる材料や施設のた
めの耐食性材料を提供することができ、かつ得られる着
色メッキ鋼は耐食性にも優れているので、本発明による
着色メッキを施した鉄鋼製品は広範囲な分野での用途に
有効に供することができる。As described above, according to the present invention, a molten zinc alloy bath with a specific composition is used to plate a steel material under specific conditions, and then heated and cooled with hot water or forced air cooling with reheated water. By cooling, it is possible to form a plating that exhibits a uniform olive gray hue, so it is possible to provide a corrosion-resistant material for materials and facilities that are desired to exhibit an aesthetically olive gray color depending on the application, and Since the resulting colored plated steel has excellent corrosion resistance, the colored plated steel products of the present invention can be effectively used in a wide range of fields.
以下実施例により本発明を具体的に説明する。The present invention will be specifically explained below using Examples.
実施例
幅50mm、長さ1001及び3.2111111の寸
法の5S41鋼板を、80℃のアルカリ浴に30分間浸
漬して脱脂を行った後、湯洗し、次いで10%塩酸溶液
に常温で30分間浸漬してスケールを除去した。次にこ
の鋼板を湯洗後、35%ZnC1z NHaC1溶液
に60℃で1分間浸漬してフラックス処理を行った。こ
のようにして前処理を行った鋼板を下記に示すような組
成の浴を用い、下記条件でメッキを行った。Example A 5S41 steel plate with dimensions of width 50 mm, length 1001, and 3.2111111 was degreased by immersing it in an alkaline bath at 80° C. for 30 minutes, then washed with hot water, and then soaked in a 10% hydrochloric acid solution for 30 minutes at room temperature. The scale was removed by soaking. Next, this steel plate was washed with hot water and then immersed in a 35% ZnC1z NHaC1 solution at 60° C. for 1 minute to undergo flux treatment. The thus pretreated steel plate was plated using a bath having the composition shown below under the following conditions.
メッキ浴組成:
(wt%)
Mn 0.3〜0.5Zn
(Pb含有量50ppm以下) バランスメッキ処理
条件:
畜」Jしふ!L 加でJJし工lし ■糸片5E伎し得
られたメッキ鋼板面には、オリーブ灰色の均一な色相を
呈する着色メッキ層が形成された。Plating bath composition: (wt%) Mn 0.3-0.5Zn
(Pb content 50 ppm or less) Balance plating processing conditions: ``Kiku'' J Shifu! A colored plating layer exhibiting a uniform olive gray hue was formed on the surface of the plated steel plate obtained by processing the thread piece 5E.
Claims (3)
オリーブ灰色の着色メッキを形成するための溶融メッキ
用亜鉛合金。(1) A zinc alloy for hot-dip plating for forming an olive gray colored plating having a composition of 0.2 to 0.8% by weight Mn-Zn.
07に規定される最純亜鉛地金(99.995%以上)
もしくは特殊亜鉛地金(99.99%以上)であつて、
Pbの含有量が0.005重量%以下である特許請求の
範囲第(1)項記載の亜鉛合金。(2) The zinc base metal used for the above zinc alloy is JISH21
The purest zinc metal specified in 07 (99.995% or more)
Or special zinc metal (99.99% or more),
The zinc alloy according to claim 1, wherein the content of Pb is 0.005% by weight or less.
溶融メッキ用亜鉛合金を用い、浴温度490〜530℃
で鉄鋼材料にメッキを施し、次いでこれを500〜52
0℃の温度の雰囲気中で50〜150秒加熱した後、温
水冷するかもしくは大気中で強制空冷後温水冷すること
を特徴とする鉄鋼にオリーブ灰色の着色メッキを形成す
る方法。(3) Using a zinc alloy for hot-dip plating having a composition of 0.2-0.8% by weight Mn-Zn, bath temperature 490-530°C
The steel material is plated with 500-52
A method for forming an olive gray colored plating on steel, characterized by heating in an atmosphere at a temperature of 0° C. for 50 to 150 seconds and then cooling with hot water, or forced air cooling in the atmosphere and then cooling with hot water.