JPS63215292A - Diaphragm for speaker - Google Patents
Diaphragm for speakerInfo
- Publication number
- JPS63215292A JPS63215292A JP4923287A JP4923287A JPS63215292A JP S63215292 A JPS63215292 A JP S63215292A JP 4923287 A JP4923287 A JP 4923287A JP 4923287 A JP4923287 A JP 4923287A JP S63215292 A JPS63215292 A JP S63215292A
- Authority
- JP
- Japan
- Prior art keywords
- polymer resin
- impregnated
- conical part
- diaphragm
- manila hemp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
産業上の利用分野
本発明は各種音響機器に利用されるスピーカの振動板に
関するものである。DETAILED DESCRIPTION OF THE INVENTION Field of Industrial Application The present invention relates to a diaphragm for a speaker used in various types of audio equipment.
従来の技術
従来の振動板エツジ基材には、コーンと一体化された天
然パルプ100%のフィックスドエ、ジ、又コーンと貼
り合わせるフリーエツジとしては天然パルプ、5BR−
NBR等の樹脂を含浸した布。Conventional technology Conventional diaphragm edge base materials include 100% natural pulp fixed edge, which is integrated with the cone, and natural pulp, 5BR-, as the free edge that is bonded to the cone.
Cloth impregnated with resin such as NBR.
ウレタン発泡体などがあった。There were urethane foams, etc.
発明が解決しようとする問題点
フィックストエツジはコーンと一体化されているため最
低共振周波数(fo)が高く重低温再生ができない、フ
リーエツジの中で天然パルプは振幅をとりすぎるとエツ
ジが破壊するため入力を大きくできない、また布、ウレ
タン発泡体は重量が重くコストが高い、さらにフリーエ
ツジはコーン部とエツジ部を別々に成形して後で両者を
接着剤で貼り合わせる工程であるため振動板完成品のコ
ストが著るしく高くなるといった問題があった。本発明
は低コストで高耐入力、軽量さらにはコーン部との成形
同時接着可能なスピーカ用振動板を提供することを目的
とする。Problems to be solved by the invention Fixed edge is integrated with the cone, so the minimum resonant frequency (FO) is high and heavy and low temperature regeneration is not possible.In free edge, natural pulp will break if the amplitude is too high. In addition, cloth and urethane foam are heavy and expensive, and free edge molding involves molding the cone and edge separately and then bonding them together with adhesive, which makes it difficult to complete the diaphragm. There was a problem that the cost of the product increased significantly. SUMMARY OF THE INVENTION An object of the present invention is to provide a speaker diaphragm that is low cost, has high input resistance, is lightweight, and can be bonded to a cone portion at the same time as molding.
問題点を解決するための手段
前記の問題点を解決するために本発明は、マニラ麻を基
材とした天然パルプの抄紙シート材に酢酸ビニル−アク
リル共重合体樹脂を含浸し、さらにクロロスルフォン化
ポリマー樹脂を含浸した工ッジ材とコーン部を成形同時
接着してスピーカ用振動板を構成しようとするものであ
る。Means for Solving the Problems In order to solve the above problems, the present invention impregnates a papermaking sheet material of natural pulp based on Manila hemp with a vinyl acetate-acrylic copolymer resin, and further chlorosulfonates it. This method attempts to construct a speaker diaphragm by bonding a cone part and a cone material impregnated with a polymer resin at the same time as molding.
作用
低コスト、軽量化さらには耐入力向上のためにマニラ麻
を基材とした天然パルプの抄紙シート材に、特に湿潤強
度を向上させるために酢酸ビニル−アクリル共重合体樹
脂を含浸し、さらに成形同時接着のためにクロロスルフ
ォン化ポリマー樹脂を含浸する。酢酸ビニル−アクリル
共重合体またクロロスルフォン化ポリマー樹脂はどちら
も熱硬化性樹脂であるため成形時に高温で成形するとコ
ーン部と接着され、振動板完成品を得ることができる。In order to reduce costs, reduce weight, and improve input resistance, we impregnated Manila hemp-based natural pulp paper sheet material with vinyl acetate-acrylic copolymer resin to particularly improve wet strength, and then formed it. Impregnated with chlorosulfonated polymer resin for simultaneous adhesion. Both the vinyl acetate-acrylic copolymer and the chlorosulfonated polymer resin are thermosetting resins, so when molded at high temperatures, they are bonded to the cone portion, allowing a finished diaphragm product to be obtained.
実施例
以下、本発明の一実施例におけるスピーカ用振動板につ
いて説明する。EXAMPLE A speaker diaphragm according to an example of the present invention will be described below.
マニラ麻にリンタパルプを重量比で30%混抄した36
gr/rrlの目付量の抄紙シート材に酢酸ビニル−ア
クリル共重合体樹脂を8grld含浸し、乾燥後クロロ
スルフォン化ポリマー樹脂を40gr/d含浸し、乾燥
する。このエツジ基材を所定の形状に打ち抜いた後、金
型温度180°C、プレス時間4SeCの条件でコーン
部と成形同時接着し、振動板を得た。図面に本発明のス
ピーカ用振動板を使用したスピーカ人と、従来の布エツ
ジを使用したスピーカBのそれぞれの音圧周波数特性を
示す。本発明品は重量が軽いため音圧レベルが高く、ま
たより高音域まで再生している。36 made by mixing Manila hemp with Linta pulp at a weight ratio of 30%.
A papermaking sheet material having a basis weight of gr/rrl is impregnated with 8 grld of vinyl acetate-acrylic copolymer resin, and after drying, impregnated with 40 gr/d of chlorosulfonated polymer resin and dried. After punching this edge base material into a predetermined shape, it was bonded to a cone part at the same time as molding under conditions of a mold temperature of 180°C and a press time of 4SeC to obtain a diaphragm. The drawings show the sound pressure frequency characteristics of a speaker using the speaker diaphragm of the present invention and a speaker B using a conventional cloth edge. Since the product of the present invention is light in weight, it has a high sound pressure level and can reproduce even higher frequencies.
発明の効果
以上のように本発明の振動板は構成されるため、軽量で
低コスト、高耐入力のスピーカ用振動板を簡易な製造方
法で作ることが性能で、これにより大幅な合理化が図ら
れ、工業的価値の大なるものである。Since the diaphragm of the present invention is constructed as described above, the performance is that a lightweight, low-cost, high-input-resistant speaker diaphragm can be manufactured using a simple manufacturing method, and this will result in significant streamlining. It is of great industrial value.
図は従来の振動板と本発明の振動板を用いたスピーカの
音圧周波数特性図である。The figure is a sound pressure frequency characteristic diagram of a speaker using a conventional diaphragm and a diaphragm of the present invention.
Claims (2)
に酢酸ビニル−アクリル共重合体樹脂を含浸し、さらに
クロロスルフォン化ポリマー樹脂を含浸したエッジ材を
コーン部と成形同時接着したスピーカ用振動板。(1) Vibration for speakers made by impregnating vinyl acetate-acrylic copolymer resin into a paper-made sheet material made of natural pulp based on Manila hemp, and adhering an edge material impregnated with chlorosulfonated polymer resin to the cone part at the same time as molding. Board.
抄したことを特徴とする特許請求の範囲第1項記載のス
ピーカ用振動板。(2) A diaphragm for a speaker according to claim 1, characterized in that 0 to 30% by weight of Linta pulp is mixed with Manila hemp.