JPS6289878A - Aluminum alloy plate having superior corrosion resistance and treatment of its surface - Google Patents

Aluminum alloy plate having superior corrosion resistance and treatment of its surface

Info

Publication number
JPS6289878A
JPS6289878A JP21632285A JP21632285A JPS6289878A JP S6289878 A JPS6289878 A JP S6289878A JP 21632285 A JP21632285 A JP 21632285A JP 21632285 A JP21632285 A JP 21632285A JP S6289878 A JPS6289878 A JP S6289878A
Authority
JP
Japan
Prior art keywords
alloy plate
corrosion resistance
aluminum alloy
treatment
excellent corrosion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP21632285A
Other languages
Japanese (ja)
Inventor
Kikuro Toyose
豊瀬 喜久郎
Koichi Hatanaka
畑中 孝一
Masanobu Fukui
福井 正信
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kobe Steel Ltd
Original Assignee
Kobe Steel Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kobe Steel Ltd filed Critical Kobe Steel Ltd
Priority to JP21632285A priority Critical patent/JPS6289878A/en
Publication of JPS6289878A publication Critical patent/JPS6289878A/en
Pending legal-status Critical Current

Abstract

PURPOSE:To improve the corrosion resistance of an Al alloy plate when the plate is chromated, by carrying out treatment with a treating bath contg. hydrofluoric acid in a prescribed concn. ratio so that pits of >=0.1mu diameter are not produced. CONSTITUTION:A phosphate-chromate treating soln. having 0.01-0.5 weight ratio of HF/CrO3 is prepd. The surface of an Al alloy plate is treated with the treating soln. so that pits of >=0.1mu diameter are not produced. By the treat ment, a phosphate-chromate film is formed by >=5mg/m<2> (expressed in terms of Cr).

Description

【発明の詳細な説明】 1産業上の利用分野1 本発明は耐蝕性に優れたアルミニウム合金板(アルミニ
ウム板を含む。)およびその表面処理方法に関するもの
である。
DETAILED DESCRIPTION OF THE INVENTION 1. Industrial Application Field 1 The present invention relates to an aluminum alloy plate (including an aluminum plate) having excellent corrosion resistance and a surface treatment method thereof.

[従来技術1 一般的に、アルミニウムおよびアルミニウム合金は、表
面1こ保護力の強い酸化皮膜を形成し、実用上優れた耐
蝕性を有しているので、日用品や建材等に使用されてい
る。
[Prior Art 1] Aluminum and aluminum alloys are generally used for daily necessities, building materials, etc. because they form a highly protective oxide film on the surface and have excellent corrosion resistance in practical use.

しカルなが呟アルミニウムおよびアルミニウム合金は高
温の水にさらされると黒く変色したり、また、高温の水
蒸気にさらされると白く変色することがあり、そのため
、このような黒色変化および白色化を防止するために、
アルミニウムお上りアルミニウム合金に種々の表面処理
が行なわれている。
Aluminum and aluminum alloys can turn black when exposed to high-temperature water, or turn white when exposed to high-temperature steam, so we recommend preventing such blackening and whitening. In order to
Various surface treatments have been applied to aluminum alloys.

その一つに、アルミニウムおよびアルミニウム合金の表
面に燐酸クロメート処理を行なう方法があるが、この燐
酸クロメート処理を行なっても、高温水或いは高温水蒸
気にさらされると、このような処理を行なわないアルミ
ニウムおよびアルミニウム合金と同様に表面に黒色変化
、また、白色化が発生して、実用上問題となる。
One method is to perform phosphoric acid chromate treatment on the surface of aluminum and aluminum alloys, but even if this phosphoric acid chromate treatment is performed, aluminum and aluminum alloys that have not undergone such treatment will deteriorate when exposed to high-temperature water or high-temperature steam. Similar to aluminum alloys, blackening and whitening occur on the surface, which poses a practical problem.

[発明か解決しようとする問題点1 本発明はこのような現状に鑑みなされたものであり、特
に、耐蝕性に優れたアルミニウム合金板の表面処理方法
を提供するものである。
[Problem to be Solved by the Invention 1] The present invention has been made in view of the current situation, and particularly provides a method for surface treatment of an aluminum alloy plate with excellent corrosion resistance.

1問題点を解決するための手段1 本発明に係る耐蝕性に優れたアルミニウム合金板および
その表面処理方法は、 (1) ピントが最大径0.1μ未満であり、かつ、ク
ロム付着量が5 m 8/ l+1 ”以上である燐酸
クロメート皮膜が設けられていることを特徴とする耐蝕
性に優れたアルミニウム合金板を@1の発明とし、(2
) アルミニウム合金板の表面処理として燐酸クロメー
ト処理を行なう際に、クロム酸に対する弗酸の重量濃度
比を0.01−0.5の処理浴を使用し、0.1μ以上
の径のビットが生成しないように処理することを特徴と
する耐蝕性に優れたアルミニウム合金板の表面処理方法
を第2の発明とする2つの発明よりなるものである。
1 Means for Solving Problem 1 The aluminum alloy plate with excellent corrosion resistance and the surface treatment method thereof according to the present invention are as follows: (1) The maximum diameter of the pinto is less than 0.1μ, and the amount of chromium deposited is 5. The invention of @1 is an aluminum alloy plate with excellent corrosion resistance characterized by being provided with a phosphoric acid chromate film having a thickness of m 8 / l + 1 ” or more,
) When performing phosphoric acid chromate treatment as a surface treatment for aluminum alloy plates, a treatment bath with a weight concentration ratio of hydrofluoric acid to chromic acid of 0.01-0.5 is used to produce bits with a diameter of 0.1μ or more. This invention consists of two inventions, the second invention being a method for surface treatment of an aluminum alloy plate with excellent corrosion resistance, which is characterized in that the surface treatment method is performed to prevent corrosion.

本発明に係る耐蝕性に優れたアルミニウム合金板お上び
そのの表面処理方法について以下詳細に説明する。
The aluminum alloy plate with excellent corrosion resistance and the surface treatment method thereof according to the present invention will be described in detail below.

先ず、本発明に係る耐蝕性に優れたアルミニウム合金板
およびそのの表面処理力法において、クロム酸に対する
弗酸の重量濃度比を0.O1〜0.5とすることi二つ
いて説明する。
First, in the aluminum alloy plate with excellent corrosion resistance and its surface treatment method according to the present invention, the weight concentration ratio of hydrofluoric acid to chromic acid is set to 0. The explanation will be based on two values i, which are O1 to 0.5.

一般にlIFは燐酸クロメート処理における皮膜の生成
を促進するものであるが、本発明者は燐酸クロメート処
理材の耐蝕性改善について鋭意研究した結果、HFは皮
膜に0.1〜1.0μの微小なビットを生成させる作用
かあり、これが耐蝕性を低下させることを見出した。
In general, lIF promotes the formation of a film during phosphoric acid chromate treatment, but as a result of intensive research into improving the corrosion resistance of phosphoric acid chromate treated materials, the present inventor found that HF causes minute particles of 0.1 to 1.0μ in the film. It has been found that this has the effect of generating bits, which reduces corrosion resistance.

そして、このような微小なビットを生成させないために
は、クロム酸に対する弗酸の重量濃度比を0.01〜0
.5とすることが必要であり、この比が0.01未満で
は皮膜の生成効率が不充分であって所望の効果が得られ
ず、また、0.5を越えると0.1μを越える大きなビ
ットが生成して耐蝕性が極端に低下するようになる。
In order to prevent the generation of such minute bits, the weight concentration ratio of hydrofluoric acid to chromic acid should be set at 0.01 to 0.
.. If this ratio is less than 0.01, the film generation efficiency will be insufficient and the desired effect will not be obtained, and if it exceeds 0.5, large bits exceeding 0.1 μ will be produced. is formed, resulting in an extremely poor corrosion resistance.

そして、本発明者の知見によると耐蝕性を向上させるた
めには、少なくとも最大径0.1μの微小ビットを生成
させないようにすることが必要であす、二の0,1μよ
り大きい径のピントが生成すると耐蝕性か劣化するので
ある。
According to the findings of the present inventor, in order to improve the corrosion resistance, it is necessary to prevent the generation of minute bits with a maximum diameter of at least 0.1μ; When it forms, its corrosion resistance deteriorates.

[実施例1 本発明に係る耐蝕性に優れたアルミニウム合金板および
その表面処理方法の実施例を説明する。
[Example 1] An example of an aluminum alloy plate with excellent corrosion resistance and a surface treatment method thereof according to the present invention will be described.

実施例 M8含有量が4.5すL%のアルミニウム合金板の厚さ
0.32+nmのものを使用し、アルカリ性エツチング
16(0,2N  NaOH?O’CX−を秒)でエツ
チングを行なってから、11表に示す燐酸クロメート処
理浴により処理を行なった。
Example: Using an aluminum alloy plate with a thickness of 0.32+nm with an M8 content of 4.5L%, etching was performed with alkaline etching 16 (0.2N NaOH?O'CX- for seconds). The treatment was carried out using a phosphoric acid chromate treatment bath shown in Table 11.

耐蝕性は塩水噴霧試験(J I S  Z−2371)
により、耐白錆を調査しrこ。
Corrosion resistance is determined by salt spray test (JIS Z-2371)
We investigated white rust resistance.

第1表から、本発明に係る耐蝕性に優れたアルミニウム
合金板の表面処理方法により製造された耐蝕性アルミニ
ウム合金板は、比較例に比して耐蝕性が格段に優れてい
ることは明らかである。
From Table 1, it is clear that the corrosion-resistant aluminum alloy plate produced by the corrosion-resistant aluminum alloy plate surface treatment method according to the present invention has much better corrosion resistance than the comparative example. be.

また、第1図(a)は本発明に係る耐蝕性に優れたアル
ミニウム合金板の表面処理方法の実施例3により製造さ
れた耐蝕性アルミニウム合金板の表面組織を示す顕微鏡
写真であり、第1図(b)は比較例1のアルミニウム合
金板の表面組織を示す顕微鏡写真であり、第1図(a)
に示す表面組織が緻密であることがわかる。
Moreover, FIG. 1(a) is a micrograph showing the surface structure of a corrosion-resistant aluminum alloy plate manufactured by Example 3 of the surface treatment method for an aluminum alloy plate with excellent corrosion resistance according to the present invention. Figure (b) is a micrograph showing the surface structure of the aluminum alloy plate of Comparative Example 1, and Figure 1 (a)
It can be seen that the surface structure shown in is dense.

[発明の効果1 以上説明したように、本発明に係る耐蝕性に優れたアル
ミニウム合金板およびその表面処理方法は上記の構成を
有しているものであるから、アルミニウム合金板は耐蝕
性においてを極めて優れており、日用品および建材等に
広く使用することができるという効果を有するものであ
る。
[Effect of the invention 1 As explained above, since the aluminum alloy plate with excellent corrosion resistance and the surface treatment method thereof according to the present invention have the above configuration, the aluminum alloy plate has excellent corrosion resistance. It is extremely excellent and has the effect that it can be widely used in daily necessities, building materials, etc.

【図面の簡単な説明】[Brief explanation of drawings]

第1図(a)および′:51図(b)は本発明に係る耐
蝕性に優れたアルミニウム合金板の表面処理方法の実施
例1により得られたアルミニウム合金板の表面組織を示
す顕微鏡写真および比較例1のアルミニウム合金板の表
面組織を示す顕微鏡写真である。 才1 図
Figures 1(a) and 51(b) are micrographs showing the surface structure of an aluminum alloy plate obtained in Example 1 of the method for surface treatment of an aluminum alloy plate with excellent corrosion resistance according to the present invention; 3 is a micrograph showing the surface structure of an aluminum alloy plate of Comparative Example 1. 1 figure

Claims (2)

【特許請求の範囲】[Claims] (1)ピットが最大径0.1μ未満であり、かつ、クロ
ム付着量が5mg/m^2以上である燐酸クロメート皮
膜が設けられていることを特徴とする耐蝕性に優れたア
ルミニウム合金板。
(1) An aluminum alloy plate with excellent corrosion resistance, characterized in that the pits have a maximum diameter of less than 0.1μ and are provided with a phosphoric acid chromate film having a chromium adhesion amount of 5 mg/m^2 or more.
(2)アルミニウム合金板の表面処理として燐酸クロメ
ート処理を行なう際に、クロム酸に対する弗酸の重量濃
度比を0.01〜0.5の処理浴を使用し、0.1μ以
上の径のピットが生成しないように処理することをを特
徴とする耐蝕性に優れたアルミニウム合金板の表面処理
方法。
(2) When performing phosphoric acid chromate treatment as a surface treatment for aluminum alloy plates, a treatment bath with a weight concentration ratio of hydrofluoric acid to chromic acid of 0.01 to 0.5 is used, and pits with a diameter of 0.1 μ or more are used. A method for surface treatment of an aluminum alloy plate with excellent corrosion resistance, characterized by treating the surface so as to prevent the formation of.
JP21632285A 1985-09-30 1985-09-30 Aluminum alloy plate having superior corrosion resistance and treatment of its surface Pending JPS6289878A (en)