JPS62270200A - Electric iron - Google Patents
Electric ironInfo
- Publication number
- JPS62270200A JPS62270200A JP11557486A JP11557486A JPS62270200A JP S62270200 A JPS62270200 A JP S62270200A JP 11557486 A JP11557486 A JP 11557486A JP 11557486 A JP11557486 A JP 11557486A JP S62270200 A JPS62270200 A JP S62270200A
- Authority
- JP
- Japan
- Prior art keywords
- base
- resin
- surface treatment
- electric iron
- hanging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
３、発明の詳細な説明
〔産業上の利用分野〕
この発明は衣類等のプレス仕上げに使用する電気アイロ
ンに関する。Detailed Description of the Invention 3. Detailed Description of the Invention [Field of Industrial Application] The present invention relates to an electric iron used for press finishing clothing and the like.
電気アイロンは、ヒータを備えるベースの下面、つまり
掛け面で衣類等のプレス仕上げを行なうものである。そ
して、一般にベースはアルミニウムまたはアルミニウム
合金で形成され、その下面の掛け面には、掛け面の耐蝕
性および非粘着性を得る目的で四フッ化エチレン樹脂に
よる表面処理被膜が施されている。Electric irons press-finish clothing and the like using the lower surface of a base equipped with a heater, that is, the hanging surface. Generally, the base is made of aluminum or an aluminum alloy, and the lower hanging surface is coated with a surface treatment film made of tetrafluoroethylene resin for the purpose of making the hanging surface corrosion resistant and non-adhesive.
四フッ化エチレン樹脂はアルミニウムやアルミニウム合
金に対する密着性が悪く、このため上記表面処理被膜を
施す際には、まずベースの掛け面に密告性を改善するた
めのブライマーをコーティングし、このコーティング被
膜の上に四フッ化エチレン樹脂をコーティングし、加熱
焼成して表面処理被膜としている。Tetrafluoroethylene resin has poor adhesion to aluminum and aluminum alloys, so when applying the above-mentioned surface treatment film, first coat the hanging surface of the base with a brimer to improve adhesion. A polytetrafluoroethylene resin is coated on top, and a surface treatment film is obtained by heating and baking.
しかしながら、四フッ化エチレン樹脂による表面処理被
膜は、第３図の８曲線で示すように、その表面の硬度が
常温で約Ｈ（鉛筆硬度、以下同じ）と比較的低いととも
に、温度の上昇に伴って漸次硬度が低下し、２００″Ｃ
では硬度が約５Ｂにまで低下してしまい、このため衣類
等との摩擦で比較的早期に損耗してしまう難点があった
。また、ベースの掛け面に表面処理波膜を施す際に、ま
ず掛け面に対し密着性を改善するためのブライマーをコ
ーティングし、さらにこのブライマーのコーティング被
膜の上に四フッ化エチレン樹脂をコーティングしなけれ
ばならず、このため作業工程が繁雑となり、製造能率が
低下し、また製造コストも嵩んでしまうという問題があ
った。この発明はこのよ、うな各問題点の解決を目的と
するものである。However, as shown by curve 8 in Figure 3, the surface treatment film made of polytetrafluoroethylene resin has a relatively low surface hardness of about H (pencil hardness, the same applies hereinafter) at room temperature, and it is resistant to rising temperatures. As a result, the hardness gradually decreases to 200″C
However, the hardness is reduced to about 5B, and as a result, it wears out relatively quickly due to friction with clothing, etc. In addition, when applying the surface treatment wave film to the hanging surface of the base, we first coat the hanging surface with a brimer to improve adhesion, and then coat the brimer coating with tetrafluoroethylene resin. Therefore, there were problems in that the working process became complicated, the manufacturing efficiency decreased, and the manufacturing cost increased. The present invention aims to solve each of these problems.
この発明はこのような問題点を解決するために、ベース
の掛け面に設ける表面処理被膜を、四フッ化エチレン樹
脂とポリエーテルサルフォン樹脂との混合物で構成する
ようにしたものである。In order to solve these problems, the present invention is such that the surface treatment coating provided on the hanging surface of the base is made of a mixture of tetrafluoroethylene resin and polyether sulfone resin.
四フッ化エチレン樹脂に含有したポリエーテルサルフォ
ン樹脂により、表面処理被膜の硬度およびベースに対す
る密着性が改善される。The polyether sulfone resin contained in the tetrafluoroethylene resin improves the hardness of the surface treatment film and the adhesion to the base.
以下、この発明の一実施例について図面を参照して説明
する。An embodiment of the present invention will be described below with reference to the drawings.
第２図に電気アイロンの全体を示し、図中１が例えばア
ルミニウムで形成されたベースで、このベース１の上面
側に遮熱カバー２を介して例えば合成樹脂で形成された
ハンドル３が取付けられ、このハンドル３の上端前端部
にベース１の温度を設定する温度調節摘み４が設けられ
ている。さらに、ハンドル３の前部には水タンク５が構
成され、この水タンク５の前面に注排水口６が形成され
、この注排水口６を通して水タンク５内に水が収容され
、この水が適宜、ベース１の蒸発室（図示せず）に滴下
されてスチームとなり、このスチームがベース１の下面
の掛け面１ａに形成された噴出孔（図示せず）から噴出
するようになっている。Fig. 2 shows the entire electric iron. In the figure, 1 is a base made of aluminum, for example, and a handle 3 made of synthetic resin, for example, is attached to the upper surface of the base 1 through a heat shielding cover 2. A temperature adjustment knob 4 for setting the temperature of the base 1 is provided at the upper front end of the handle 3. Furthermore, a water tank 5 is configured in the front part of the handle 3, and an inlet/outlet 6 is formed in the front of the water tank 5. Water is stored in the water tank 5 through the inlet/outlet 6, and this water is It is appropriately dripped into an evaporation chamber (not shown) of the base 1 to become steam, and this steam is ejected from an ejection hole (not shown) formed in the hanging surface 1a on the lower surface of the base 1.
なお、６ａは水タンク５の注排水口６に装着された開閉
蓋である。Note that 6a is an opening/closing lid attached to the inlet/outlet 6 of the water tank 5.
ベース１には、第１図に示すように、ヒータ７が埋め込
まれ、このヒータ７の発熱に基づいてベース１が上記温
度調節摘み４により設定された所定温度に保持されるも
のである。そして、このベース１の下面の掛け面１ａに
は均一に表面処理波膜８か施されている。As shown in FIG. 1, a heater 7 is embedded in the base 1, and based on the heat generated by the heater 7, the base 1 is maintained at a predetermined temperature set by the temperature control knob 4. A surface-treated corrugated film 8 is uniformly applied to the hanging surface 1a of the lower surface of the base 1.
この表面処理波膜８は、四フッ化エチレン樹脂とポリエ
ーテルサルフオン樹脂との混合物で、その混合比率が例
えばｓｏ：ｓｏとなっている。この表面処理波膜８をベ
ース１の掛け面１ａに施す工程について述べると、四フ
ッ化エチレン樹脂とポリエーテルサルフオン樹脂とを５
０ ： ５０の比率で混合し、この混合物に溶剤を加え
て液状にし、これを例えばスプレ一手段によりベース１
の掛け面１ａにコーティングし、さらに約４００℃に加
熱焼成して得る。This surface-treated corrugated film 8 is a mixture of tetrafluoroethylene resin and polyether sulfon resin, and the mixing ratio thereof is, for example, so:so. The process of applying this surface-treated wave film 8 to the hanging surface 1a of the base 1 is as follows:
Mix in a ratio of 0:50, add a solvent to this mixture to make it liquid, and apply it to base 1 by, for example, spraying.
It is obtained by coating the hanging surface 1a of and further heating and baking at about 400°C.
このような四フッ化エチレン樹脂とポリエーテルサルフ
オン樹脂との混合物による表面処理被膜８においては、
第３図のへ曲線で示すように、従来の四フッ化エチレン
樹脂単独の表面処理被膜（８曲線）に比べ、常湿での硬
度が約２Ｈと高いとともに、？ＦＡ度の」−Ｈに伴う硬
度の低下がほぼ２００ ’Ｃ近くまでほとんどなく、つ
まり２００℃近くまでほぼ一定の高い硬度（約Ｈ）を保
ち、したがってこの表面処理波膜８は長期に亙ってその
損耗が防止され、掛け面１ａの耐蝕性および非粘着性が
良好に保たれる。In the surface treatment film 8 made of such a mixture of tetrafluoroethylene resin and polyether sulfone resin,
As shown by the curve in Figure 3, compared to the conventional surface treatment film made of tetrafluoroethylene resin alone (curve 8), the hardness at normal humidity is as high as approximately 2H, and There is almost no decrease in hardness associated with the FA degree of -H up to approximately 200'C, that is, the surface-treated wave film 8 maintains an almost constant high hardness (approximately H) up to approximately 200'C. This prevents wear and tear on the hanging surface 1a, and maintains good corrosion resistance and non-adhesiveness of the hanging surface 1a.
また、この発明の表面処理波膜８は、四フッ化エチレン
樹脂にポリエーテルサルフオン樹脂が含有するため、ベ
ース１の素地に対する密着性がよく、このため従来のよ
うなブライマーが不要となり、ベース１の掛け面１ａに
直接施すことが可能で、これにより作業工程が簡素化し
、製造能率が向上し、また製造コストも低減する。さら
に、ポリエーテルサルフォン樹脂が含有するこの発明の
表面処理波膜８においては、着色性が良好で、パステル
カラー等の着色も可能となる利点がある。Furthermore, since the surface-treated wave membrane 8 of the present invention contains polyether sulfone resin in the polytetrafluoroethylene resin, it has good adhesion to the substrate of the base 1, which eliminates the need for a conventional brimer and eliminates the need for the base material. 1 can be applied directly to the hanging surface 1a, which simplifies the work process, improves manufacturing efficiency, and reduces manufacturing costs. Furthermore, the surface-treated corrugated film 8 of the present invention containing polyether sulfone resin has the advantage of good coloring properties and can be colored in pastel colors or the like.
なお、上記実施例においては、ベースの材料をアルミニ
ウムとしたが、これに限らず、アルミニウム合金、亜鉛
合金、ステンレス鋼、セラミック等であってもよい。In the above embodiments, the base material is aluminum, but is not limited to this, and may be made of aluminum alloy, zinc alloy, stainless steel, ceramic, or the like.
以上説明したようにこの発明によれば、表面処理被膜の
硬度を、温度の上昇に伴う低下をほとんど招くことなく
高い値に保て、したがって表面処理被膜の損耗を長期に
亙って防止し、ベースの掛け面の耐蝕性および非粘着性
を良好に保て、またベースの掛け面に対して表面処理被
覆を能率よく安価に設けることができるという効果を奏
する。As explained above, according to the present invention, the hardness of the surface treatment film can be maintained at a high value with almost no decrease due to rise in temperature, and therefore wear and tear of the surface treatment film can be prevented over a long period of time. It is possible to maintain good corrosion resistance and non-adhesiveness of the hanging surface of the base, and to provide the surface treatment coating efficiently and inexpensively on the hanging surface of the base.
第１図はこの発明の一実施例を示す要部の断面図、第２
図は同じく全体の斜視図、第３図はこの発明に係る表面
処理被膜と従来の表面処理被膜との特性を比較して示す
特性曲線図である。
１・・・ベース、１ａ・・・掛け面、８・・・表面処理
被膜。
出願人代理人 弁理士 鈴江武彦
第１図
第２図Fig. 1 is a sectional view of the main parts showing one embodiment of the present invention;
The figure is also a perspective view of the whole, and FIG. 3 is a characteristic curve diagram showing a comparison of the characteristics of the surface treatment film according to the present invention and a conventional surface treatment film. 1...Base, 1a...Hanging surface, 8...Surface treatment film. Applicant's agent Patent attorney Takehiko Suzue Figure 1 Figure 2
Claims (3)
エーテルサルフォン樹脂との混合物による表面処理被膜
を施したことを特徴とする電気アイロン。(1) An electric iron characterized in that the hanging surface of the base is coated with a surface treatment film made of a mixture of tetrafluoroethylene resin and polyether sulfone resin.
樹脂との混合比率が５０：５０であることを特徴とした
特許請求の範囲第１項記載の電気アイロン。(2) The electric iron according to claim 1, wherein the mixing ratio of tetrafluoroethylene resin and polyether sulfone resin is 50:50.
あることを特徴とした特許請求の範囲第１項または第２
項記載の電気アイロン。(3) Claim 1 or 2, characterized in that the base is made of aluminum or aluminum alloy.
Electric iron as described in section.