JPS62228563A - Floor material - Google Patents

Abstract

(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.

Description

[Detailed Description of the Invention] [Field of use on wood beams] Does this invention apply to natural wood or artificial stone? 2 blockade yl-
Regarding artificial flooring materials, it is possible to combine the beauty of natural wood and the counterfeit resistance of artificial stone by burying the wood cut into artificial stones.

[Prompting literature and seven problems]

In Europe and the United States, flooring materials include wood alone, wood thin wood, and
There is one thing that stands out against the defeat. Craft this thing.

It has the beauty of book +4, but is it durable? 4) Wear resistance is insufficient.

Although it is sufficient for the upper Sumizagawadoko of Shoma, etc., there was a problem that it could not be used for shoes that require footing, such as for entrance pitchers.

In addition, natural stone fragments can be used to make 1F of unsaturated polyester resin, etc.
Artificial stone made from a fraction of T-no-ishi is used as flooring material, but although it has good early wear resistance, it has a warmth-I
There was a problem with her lack of good looks.

[Middle part of the process to decide on issues]

Therefore, in this invention, by embedding round slices of natural wood in artificial stone, it is possible to provide both aesthetic appearance and wear resistance.

1 box contains 2 pieces of the flooring material of this invention (91:2).
Entrance 1 in Figure A is a round cut piece of wood. This wood #a';
'j materials 1 are oak, beech, Japanese ash, ash, maple, and birch.

Natural wood such as pine and sucrose has a cut of 9 and a cut of 11.
It is made of flint and butterbur, and is used with a diameter of 50 to 300 nm and a thickness of 5 to 10 mm. It is useful to use this circular cut material 2, which has a bond shield 2 on top of it, for the slow rolling of S'4 between the single circular cut material 1 and artificial stone. In addition, this import 1) J material is impregnated with Kengetsu and used as a substitute, as a IIIf water condition: +a4
This wood round cut l, which is preferable in terms of abrasion resistance, stain resistance, durability, etc., is embedded in the artificial stone 3.The artificial stone 3 is made of natural stone 7a, such as large buried stone, which is crushed and has a particle diameter of T. 5-5
It is made by adding a fraction of aggregate such as crushed natural stone and silica sand to 1 part of polyester, 1 part of fat, polyurethane, 1 part of epoxy, and 1 part of acrylic phenol resin. A level of about 10 to 10 degrees is used.

This artificial stone 3 is in the form of a flat plate with a thickness of about 5 to 20 mm. A round cut lumber l is embedded in the surface with the end exposed at 5, and both 8 are attached to [i! It has a d layer.

Then, the wood 4-round cut lumber l and the artificial stone 3 are placed on a flat plate-shaped base material 4. Fixed. The base material 4 was made of temporary cement with a thickness of 5NlO. Gypsum board, calcium modified calcium board, wood wool cement board, etc. are used.7)) This Yotna Captain is preferably a rectangle with a size of 30c+n square. Cement mortar on concrete with dirt floor? 44J was used, and it was directly laid out and pasted, and the construction was completed with a monkey work 5.

Next, an example of a manufacturing method for such a flooring material will be explained.

First, the wood round cut material 1 is subjected to a cutting process. If the wood is fresh and unseasoned, it will be heated and dried to reduce moisture content. 1. Immerse uncured polyurethane resin, epoxy resin, etc. in a curable resin solution such as deacrylate prepolymer. Harden the round cut lumber (J Ishikaori included NL, harden it).

Well, if wood is used as dry flooring material. Place it in a pressure-resistant container such as an autoclave, and after reducing the pressure of (c) B', pour the self-curing resin liquid into the upper layer. After soaking the wood.

Apply pressure to penetrate and harden.

Next, we will use aggregates such as crushed natural debris! A-phase polyester resin, epoxy resin. A hardening mixture made by mixing a fixed amount of hardening resin such as polycrethane oil and other hardening resins.

Then, a hole is provided around the base material 4. Polyurethane@B't1. on the surface of the base material 4. After applying a primer treatment using a primer such as epoxy resin to improve adhesion, the curable mixture that will become the artificial stone is poured onto the base material.
While it is still uncured, place the previously prepared 1d processed round cut material 1 on it. After pressing lightly, press the mixture around the round cut material 1 with a trowel or spatula, level it, and form the same plane as the front threshold of the round cut material 10. After setting it to I:5. The mixture is alternatively cured by mixing v/j under heating. Then, L9, the wood round cut l, the artificial stone 3, and the base material 4 are joined and bonded to obtain a self-splitting flooring material.

In addition, in order to improve the texture of the wood ring l and the artificial stone 3. It is preferable to use cutting fat of the same value.

Well, when processing lumber from round cuts 101. 1ft+
jl&? S is in an uncured or semi-cured state. It may be hardened simultaneously with the curing of the curable mixture that will become the artificial stone material 3, which is preferable because it further improves the tight shielding properties between the wood ring material 1 and the artificial stone material 3.

Top T, 5 glass lR at the bottom of artificial stone 3? aO)
Cloth, mat, net, Kotobuki reinforcing material/! - The buried shingle can be omitted to 4 materials 4, and can be made of thin, light-layered wood.

[Effect]

In this type of flooring, 1 piece of wood cut into pieces is arranged in fractions on 3 pieces of V-shaped artificial stone and finished as 1 piece.
Even if one walks on this floor with shoes on, only the surface of the round cut material 1 will not wear out unnecessarily, and the wear resistance of the floor as a whole will be improved. Second, since the wood end of the round cut lumber is exposed on the surface, the grain of the hard wood is distributed over many times, and the wood is iron-treated.

- The abrasion resistance of the cut lumber 1 itself is the same as that of wood grains with straight grains exposed on the surface, and it becomes a tile. Furthermore, the round cut lumber was treated with lumber. Since it is surrounded by artificial stone 3, cracking of the round cut material 10) is prevented.

In addition, the beauty of the wood is directly reflected in the clothing ■. This becomes the A1 pattern on the artificial stone 3, giving it a unique real parent.

Furthermore, cement mortar etc? It can be used to perform construction using the same construction method as Takumai.

〔6〆〆〆〆〆Slices of oak (5 mm thick, about 150 mm thick) were dried, then soaked in unsaturated polyester solution. It was impregnated with fat and left at room temperature to become semi-cured.

After preparing the TSS-forming mixture, a ridge was provided around the base material 4, the curable mixture was poured onto the base material 4, and a resin-impregnated oak log was placed on the center line.

Press down lightly and use a trowel to flatten the edges and heat to approximately 50°C.
Warm it up with 12mm thick flooring? To create.

This flooring? On the dirt floor concrete IJ at the entrance of the house 4
゜When I laid it with cement mortar and used it, there were almost no 4 strands even after one year of use.

She maintained a beautiful appearance.

〔Effect of the invention〕

Now that the situation is clear, is the flooring material of this invention made from wood cut into wood? Because it is embedded in artificial stone.

Wood - It combines the beauty of natural wood, which comes from cutting, and the wear resistance of artificial stone. Well, this is because the wood logs are surrounded by artificial stones.

Prevent the cut wood from absorbing moisture, drying VC, cracking, and splitting. In addition, if you use a knife made of wood round cut and treated with fat,
Furthermore, cement board is preferable because the water resistance, abrasion resistance, stain resistance, durability, etc. of the cut wood itself are improved, and its use as a flooring material is improved.

When it is integrated with a base material such as gypsum board, it can be painted using cement mortar or the like, and can be painted using the Takuhama construction method, making it widely applicable.

Therefore, this flooring material is suitable as a decorative flooring material for walking with shoes on, such as an entrance dirt floor of a house or the like.

[Brief explanation of drawings]

The drawing is a schematic diagram of an example of the flooring material of the present invention. 191. Non-material import ν); V3...artificial stone.

Claims (2)

[Claims] (1) A flooring material made by embedding wood logs into artificial stone. (2) The flooring material according to claim 1, wherein the wood round cut material is treated with a resin.