JPS62117746A - Decorative material - Google Patents
Decorative materialInfo
- Publication number
- JPS62117746A JPS62117746A JP25818985A JP25818985A JPS62117746A JP S62117746 A JPS62117746 A JP S62117746A JP 25818985 A JP25818985 A JP 25818985A JP 25818985 A JP25818985 A JP 25818985A JP S62117746 A JPS62117746 A JP S62117746A
- Authority
- JP
- Japan
- Prior art keywords
- resin layer
- material according
- decorative material
- surface resin
- embossed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
ユ皿ｏｇ力
［産業上の利用分野］
本発明は、大理石のような立体的で深みのおる絵柄模様
を有する、意匠性の高い化粧材に関する。
本発明の化粧材は、壁紙、壁面材、天井材、家具材料お
よび家電化粧材として適している。
［従来の技術］
従来、化粧材として下記のような、種々のものがある。
まず、表面にメラミン樹脂またはポリエステル樹脂を
塗布した化粧材は最も広く使われているが、絵柄模様が
平面的で、深みのある意匠性の高い表現ができない。
顔料練込み樹脂を使用し、いわゆる墨流し法によって製
造した化粧材は、意匠性は高いが生産性が低いためコス
ト高になる。 立体感を出すひとつの手法としてワイピ
ング法があるが、この製法による化粧材も、あまり深み
のある絵柄はできず、意匠性を高めることに限界がある
。
［発明が解決しようとする問題点］
本発明の目的は、上記した従来技術がなお不満足である
ことを改善し、平面的でなく、大理石のような立体的で
深みのある絵柄模様を有する、意匠性の高い化粧材を提
供することにある。
発明の構成
［問題点を解決するための手段］
本発明の化粧材は、基材シート上に、着色顔料を含有す
る合成樹脂からなり表面に絵柄の印刷およびエンボス加
工を施した中間樹脂層を設け、その上に少なくとも一層
の表面樹脂層を設けてなる。
基本的な製造工程を説明すれば、まず第１図に示すよう
に、基材シート１上に着色顔料を含有する合成樹脂の層
２Ａを設け、これに絵柄の印刷３を施す。 ついで、第
２図に示すように、中間樹脂層２の表面にエンボス加工
を行なってエンボス４を与え、その上に、第３図に示す
ように表面樹脂層５を設ける。 所望により、表面樹脂
層に着色顔料を含有させたり、微細粉末からなるマット
材を含有させてもよい。 中間樹脂層２を発泡樹脂で形
成することもできる。
本発明の化粧材には種々の態様があり得る。
第一の態様は、第３図に示すように、表面樹脂層５の表
面が平面である。
第二の態様は、表面樹脂層５の表面にエンボス加工を施
したものである（図示してない）。
第三の態様は、第４図に示すように、表面樹脂層５の表
面に絵柄の印刷６を施してある。
第四の態様は、第５図に示すように、表面樹脂層５の表
面に絵柄の印刷６を施し、エンボス７を与えである。
第五の態様は、第一の表面樹脂層５の表面にエンボス７
を与え第二層の表面樹脂層を施してあるのである（図示
してない）。
第六の態様は、第６図に示すように、表面樹脂層５の表
面に絵柄の印刷６を施し、エンボス７を与えた上に、第
二層の表面樹脂層８を設けである。
表面樹脂層は、３層以上設けてもよい。
基材シートとしては、薄葉紙、さらしクラフト紙、クラ
フト紙、紙壁紙用難燃紙、チタン紙、リンター紙などの
紙類、ポリエチレン、ポリプロピレン、ポリ塩化ビニル
、ポリ塩化ビニリデン、ポリビニルアルコール、ポリエ
チレンテレフタレート、ポリカーボネート、ナイロン、
ポリスチレン、エチレン酢酸ビニル共重合体、エチレン
ビニルアルコール共重合体、アイオノマー、アクリル樹
脂などのプラスチックのフィルムまたはシートがおり、
用途に応じて適宜に選べばよい。
任意の絵柄の印刷は、既知の印刷技術に従って行えばよ
い。
エンボス加工の方法としては、エンボスロール法、エン
ボス金属プレス法、エンボス離型フィルム法などが常用
されており、中間樹脂層および表面樹脂層の材質に応じ
てその中から選択すればよい。
中間樹脂層とする合成樹脂は、セラック、コーパル、ダ
ンマル、ロジン、ロジンエステルなどの天然樹脂または
その変性樹脂類、ニトロセルロース、アセチルセルロー
ス、エチルセルロース、ベンジルセルロースなどのセル
ロース誘導体類、フェノール樹脂、尿素樹脂、フタル酸
樹脂、マレイン酸樹脂、メラミン樹脂、ポリ酢酸ビニル
、ポリ塩化ビニル、アクリル樹脂、ポリビニルアルコー
ル、ポリビニルブチラール、エポキシ樹脂、シリコーン
樹脂、ポリエステル樹脂、ポリアミド、ポリウレタンそ
の伯の合成樹脂類、おるいは塩化ゴム、環化ゴム、合成
ゴムなどのゴムまたはゴム誘導体をベヒクルとし、その
中に着色剤、沈降性硫酸バリウムなどの体質顔料、可塑
剤などを添加してなるものを用いる。
中間樹脂層は、上記の樹脂を基材シート上に、ロールコ
ート、ナイフコート、エアナイフコート、コンマコート
、リバースコートなどのコート法により塗布して形成す
る。
表面樹脂層は、中間樹脂と同様の樹脂を用いて、中間樹
脂上に上記のコート法により塗布して形成する。
表面樹脂層に含有する着色顔料としては、表面を酸化チ
タンまたは酸化鉄で被覆したマイカ片からなるパール顔
料、またはジスアゾイエロー、イソイントリノン、スレ
ンブルー、シアニンブルー、キナクリドンのいずれかの
有機顔料が好適である。TECHNICAL FIELD The present invention relates to a highly decorative decorative material having a marble-like three-dimensional and deep pattern. The decorative material of the present invention is suitable as wallpaper, wall material, ceiling material, furniture material, and home appliance decorative material. [Prior Art] Conventionally, there are various types of decorative materials as shown below. First, decorative materials whose surfaces are coated with melamine resin or polyester resin are the most widely used, but the patterns are flat and cannot express a deep design.
Decorative materials manufactured by the so-called suminagashi method using pigment-kneaded resins have a high design quality, but are low in productivity and therefore expensive. The wiping method is one method for creating a three-dimensional effect, but decorative materials produced using this method do not produce very deep patterns, and there are limits to how much design can be achieved. [Problems to be Solved by the Invention] The purpose of the present invention is to improve the unsatisfactoriness of the above-mentioned prior art, and to provide a design that has a three-dimensional and deep pattern like marble instead of a flat one. Our goal is to provide decorative materials with a high level of design. Composition of the Invention [Means for Solving the Problems] The decorative material of the present invention comprises, on a base sheet, an intermediate resin layer made of a synthetic resin containing a colored pigment and having a pattern printed and embossed on the surface. and at least one surface resin layer is provided thereon. To explain the basic manufacturing process, first, as shown in FIG. 1, a layer 2A of synthetic resin containing colored pigments is provided on a base sheet 1, and a pattern 3 is printed on this. Next, as shown in FIG. 2, the surface of the intermediate resin layer 2 is embossed to give an embossment 4, and a surface resin layer 5 is provided thereon as shown in FIG. If desired, the surface resin layer may contain a colored pigment or a mat material made of fine powder. The intermediate resin layer 2 can also be formed of foamed resin. The decorative material of the present invention may have various embodiments. In the first embodiment, as shown in FIG. 3, the surface of the surface resin layer 5 is flat. In the second embodiment, the surface of the surface resin layer 5 is embossed (not shown). In the third embodiment, as shown in FIG. 4, a pattern 6 is printed on the surface of the surface resin layer 5. In a fourth embodiment, as shown in FIG. 5, a pattern is printed 6 on the surface of the surface resin layer 5 and embossing 7 is provided. The fifth aspect is the embossing 7 on the surface of the first surface resin layer 5.
A second surface resin layer is applied (not shown). In the sixth embodiment, as shown in FIG. 6, a pattern is printed 6 on the surface of the surface resin layer 5 and embossing 7 is provided, and then a second surface resin layer 8 is provided. Three or more surface resin layers may be provided. Base sheets include tissue paper, bleached kraft paper, kraft paper, flame retardant paper for wallpaper, titanium paper, linter paper, and other papers, polyethylene, polypropylene, polyvinyl chloride, polyvinylidene chloride, polyvinyl alcohol, polyethylene terephthalate, polycarbonate, nylon,
There are plastic films or sheets such as polystyrene, ethylene vinyl acetate copolymer, ethylene vinyl alcohol copolymer, ionomer, and acrylic resin.
It may be selected appropriately depending on the purpose. Any pattern may be printed according to known printing techniques. As the embossing method, an embossing roll method, an embossing metal press method, an embossing release film method, etc. are commonly used, and the method may be selected from among them depending on the materials of the intermediate resin layer and the surface resin layer. Synthetic resins for the intermediate resin layer include natural resins such as shellac, copal, dammar, rosin, and rosin ester, or their modified resins, cellulose derivatives such as nitrocellulose, acetylcellulose, ethylcellulose, and benzylcellulose, phenolic resin, and urea resin. , phthalic acid resin, maleic acid resin, melamine resin, polyvinyl acetate, polyvinyl chloride, acrylic resin, polyvinyl alcohol, polyvinyl butyral, epoxy resin, silicone resin, polyester resin, polyamide, polyurethane and other synthetic resins, orui The vehicle uses rubber or a rubber derivative such as chlorinated rubber, cyclized rubber, or synthetic rubber, and a colorant, an extender pigment such as precipitated barium sulfate, a plasticizer, etc. are added thereto. The intermediate resin layer is formed by applying the above resin onto the base sheet by a coating method such as roll coating, knife coating, air knife coating, comma coating, reverse coating, or the like. The surface resin layer is formed by applying the same resin as the intermediate resin onto the intermediate resin by the coating method described above. The colored pigment contained in the surface resin layer is a pearl pigment made of mica pieces whose surface is coated with titanium oxide or iron oxide, or an organic pigment such as disazo yellow, isointrinon, thren blue, cyanine blue, or quinacridone. is suitable.
表面に絵柄の印刷およびエンボスを有する中間樹脂層の
上に表面樹脂層を設けることにより、表面からある深さ
だけ内部にある絵柄の印刷およびエンボスが効果的に作
用し、大理石のような立体的で深みのある模様をもった
、意匠性が高い化粧材が１ｑられる。 所望により、表
面樹脂層に着色顔料を含有させたり、微細粉末からなる
マット材を含有させたり、あるいは中間樹脂層を発泡樹
脂で形成することにより、それぞれ特徴をもった一層意
匠性の高いものができる。
第二ないし第六の態様においては、加工の度合がより高
いことに応じて、意匠性が高められ、特色をもった製品
が得られる。
［実施例１］
下記の原料を配合して（「部」はいずれも重量部）、ペ
ーストを調製した。
ポリ塩化ビニルペーストレジンｒＧ−２５Ｊ（日本ゼオ
ン） １００部可塑剤（ＤＯＰ
） ６０部酸化チタンｒＲ−８
２０Ｊ （？５ｆｉｉ産業＞ １５部炭酸カルシウ
ム「ホヮイトンＨ」
（白石工業＞ ７０部発泡剤
ｒＡＺ−ＨＪ （大家化学） ３部安定剤ｒ
ＦＬ−２５Ｊ （アデカアーガス） ３部合計２５１
部
上記のペーストを厚さｓｏｇ／＊の壁紙裏打紙ｒＷＫ８
ＯＮＲＰＪ （具入）上に、コンマコート法により厚
さ１５０μに塗布した。
ついで、１５０℃に３０秒間加熱して、上記ペーストを
半ゲル化させた。 この上にグラビア印刷により絵柄の
印刷をし、２４０℃に３０秒間加熱して発泡させ、その
復エンボス加工を施したシートを製造した。
下記の原料を配合して、パール顔料入りのベースｉ〜を
調製した。
ポリ塩化ビニルペーストレジンｒＧ−２５Ｊ（日本ゼオ
ン’） １００部７ｉＪａ２剤（
ＤＯＰ＞ ４５部安定剤ｒＡＣ
−１１８Ｊ （アデカアーガス）３部パール顔料「１
ｒｉｏｄｉｎ Ｔｉ １００ＳＪ（メルク）
５部合計１５３部
上記のパール顔料入りのペーストを、前記のシート上に
、コンマコート法により、最凸部において５０μのペー
スト層が残るようにコート量を設定して塗布した。
最後に鏡面金属板で加圧し、第３図に示すように、表面
を平面に仕上げた（第一の態様）。
［実施例２］
実施例１で得た化粧材の表面樹脂層の上に絵柄の印刷を
施し、表面樹脂層に実施例１の中間樹脂層のエンボス柄
と異なる柄のエンボス加工を施し、第５図に示すような
化粧材を製造した（第四の態様）。
（実施例３］
実施例２で得た化粧材の上に、実施例１で用いたパール
顔料入りのペーストをさらに厚さ５０μ塗布し、鏡面金
属板で加圧し、表面を平面に仕上げ、第６図に示すよう
な化粧材を製造した（第六の態様）。
１川塁四３
本発明の化粧材は、平面的でなく、大理石のような立体
的で深みのおる絵柄模様を有する、意匠性の高いもので
ある。By providing a surface resin layer on the intermediate resin layer that has a pattern printed and embossed on the surface, the pattern printed and embossed at a certain depth from the surface works effectively, creating a three-dimensional marble-like appearance. 1q of highly decorative decorative materials with deep patterns are sold. If desired, the surface resin layer may contain colored pigments, a matte material made of fine powder may be contained, or the intermediate resin layer may be made of foamed resin to create products with unique characteristics and even higher design qualities. can. In the second to sixth embodiments, as the degree of processing is higher, the design is enhanced and a product with distinctive features is obtained. [Example 1] A paste was prepared by blending the following raw materials (all parts are by weight). Polyvinyl chloride paste resin rG-25J (Nippon Zeon) 100 parts Plasticizer (DOP
) 60 parts titanium oxide rR-8
20J (?5fii Sangyo> 15 parts Calcium carbonate "Whitton H" (Shiraishi Industries> 70 parts blowing agent rAZ-HJ (Oya Chemical) 3 parts stabilizer r
FL-25J (Adeka Argus) 3 parts total 251
Apply the above paste to wallpaper lining paper rWK8 with thickness sog/*.
It was coated onto ONRPJ (included) to a thickness of 150 μm using the comma coating method. The paste was then heated to 150° C. for 30 seconds to semi-gelatinate the paste. A pattern was printed on this by gravure printing, foamed by heating at 240° C. for 30 seconds, and then re-embossed to produce a sheet. Base i containing pearl pigment was prepared by blending the following raw materials. Polyvinyl chloride paste resin rG-25J (Nippon Zeon') 100 parts 7iJa 2 agent (
DOP > 45 parts stabilizer rAC
-118J (Adeka Argus) 3 parts pearl pigment "1"
riodin Ti 100SJ (Merck)
5 parts, total 153 parts The pearl pigment-containing paste was applied onto the sheet by a comma coating method, with the coating amount set so that a paste layer of 50 μm remained on the most convex portion. Finally, pressure was applied using a mirror-finished metal plate to finish the surface into a flat surface as shown in FIG. 3 (first embodiment). [Example 2] A pattern was printed on the surface resin layer of the decorative material obtained in Example 1, and the surface resin layer was embossed with a pattern different from the embossed pattern of the intermediate resin layer of Example 1. A decorative material as shown in Figure 5 was manufactured (fourth embodiment). (Example 3) On the decorative material obtained in Example 2, the pearl pigment-containing paste used in Example 1 was further applied to a thickness of 50 μm, and pressed with a mirrored metal plate to make the surface flat. A decorative material as shown in Figure 6 was manufactured (sixth embodiment).1 Kawarui 43 The decorative material of the present invention has a three-dimensional and deep pattern like marble, rather than a flat pattern. It is highly designed.
第１図ないし第３図は、本発明の化粧材の一例について
、その製造工程を示す模式的な断面図であって、
第１図は、基材シート上に絵柄の印刷を施した合成樹脂
の層を設けた段階を、
第２図は、第１図の表面にエンボス加工を施して中間樹
脂層を形成した段階を、そして、第３図は、第２図の表
面に表面樹脂層を設けた段階を、それぞれ示す。
第４図は、本発明の化粧材の別の例を示す、同様に模式
的な断面図であって、第３図の表面樹脂層の上に絵柄の
印刷を施したものを示す。
第５図は、さらに別の例を示す模式的な断面図であって
、第４図の表面樹脂層の上にエンボス加工を施したもの
を示す。
第６図は、なお別の例を示す模式的な断面図であって、
第５図の表面樹脂層の上に第二の表面樹脂層を施したも
のを示す。
１・・・基材シート
２Ａ・・・合成樹脂の層 ２・・・中間樹脂層３．６
・・・絵柄の印刷
４．７・・・エンボス
５．８・・・表面樹脂層
特許出願人 大日本印刷株式会社
代理人 弁理士 須 賀 総 大
箱 １ 図
第２図
第３図1 to 3 are schematic cross-sectional views showing the manufacturing process of an example of the decorative material of the present invention. FIG. 1 shows a synthetic resin with a pattern printed on a base sheet. Figure 2 shows the stage in which the surface shown in Figure 1 is embossed to form an intermediate resin layer, and Figure 3 shows the stage in which the surface resin layer is formed on the surface shown in Figure 2. Each stage is shown below. FIG. 4 is a similar schematic sectional view showing another example of the decorative material of the present invention, in which a pattern is printed on the surface resin layer of FIG. 3. FIG. 5 is a schematic cross-sectional view showing still another example, in which the surface resin layer of FIG. 4 is embossed. FIG. 6 is a schematic cross-sectional view showing still another example,
A second surface resin layer is shown on the surface resin layer of FIG. 5. 1... Base sheet 2A... Synthetic resin layer 2... Intermediate resin layer 3.6
...Picture printing 4.7...Embossing 5.8...Surface resin layer Patent applicant Dai Nippon Printing Co., Ltd. Agent Patent attorney Suga So Daibako 1 Figure 2 Figure 3
Claims (10)
らなり表面に絵柄の印刷およびエンボス加工を施した中
間樹脂層を設け、その上に少なくとも一層の表面樹脂層
を設けた化粧材。(1) A decorative material in which an intermediate resin layer made of a synthetic resin containing a colored pigment and having a pattern printed and embossed on the surface is provided on a base sheet, and at least one surface resin layer is provided thereon.
第１項に記載の化粧材。(2) The cosmetic material according to claim 1, wherein the surface resin layer contains a colored pigment.
は酸化鉄で被覆したマイカ片からなるパール顔料である
特許請求の範囲第２項に記載の化粧材。(3) The cosmetic material according to claim 2, wherein the colored pigment of the surface resin layer is a pearl pigment made of mica flakes whose surface is coated with titanium oxide or iron oxide.
ソイントリノン、スレンブルー、シアニンブルー、キナ
クリドンのいずれかの有機顔料である特許請求の範囲第
２項に記載の化粧材。(4) The cosmetic material according to claim 2, wherein the colored pigment of the surface resin layer is an organic pigment selected from disazo yellow, isointhrinone, thren blue, cyanine blue, and quinacridone.
１項に記載の化粧材。(5) The decorative material according to claim 1, wherein the surface of the surface resin layer is flat.
求の範囲第１項に記載の化粧材。(6) The decorative material according to claim 1, wherein the surface of the surface resin layer is embossed.
の範囲第１項に記載の化粧材。(7) The decorative material according to claim 1, wherein a pattern is printed on the surface of the surface resin layer.
る特許請求の範囲第１項に記載の化粧材。(8) The decorative material according to claim 1, wherein the surface resin layer contains a matte material made of fine powder.
ンボス加工を施してある特許請求の範囲第１項に記載の
化粧材。(9) The decorative material according to claim 1, wherein there are two or more surface resin layers, and the surface of the inner layer is embossed.
第１項に記載の化粧材。(10) The decorative material according to claim 1, wherein the intermediate resin layer is made of a foamed resin.