JPS6141537A - Method of bonding metallic plate - Google Patents

Method of bonding metallic plate

Info

Publication number
JPS6141537A
JPS6141537A JP16373884A JP16373884A JPS6141537A JP S6141537 A JPS6141537 A JP S6141537A JP 16373884 A JP16373884 A JP 16373884A JP 16373884 A JP16373884 A JP 16373884A JP S6141537 A JPS6141537 A JP S6141537A
Authority
JP
Japan
Prior art keywords
adhesive sheet
epoxy resin
bonding method
adhesive
metal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP16373884A
Other languages
Japanese (ja)
Inventor
和彦 山本
阿蘇品 英志
六車 忠裕
孝志 富永
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nitto Denko Corp
Original Assignee
Nitto Electric Industrial Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nitto Electric Industrial Co Ltd filed Critical Nitto Electric Industrial Co Ltd
Priority to JP16373884A priority Critical patent/JPS6141537A/en
Publication of JPS6141537A publication Critical patent/JPS6141537A/en
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.

Description

【発明の詳細な説明】 本発明は自動車、飛行機、船舶等の車体、家電製品その
他各種機器の金属部材就中鋼板部材の接着方法に関し、
更に詳しくは上記金属部材就中鋼板部材の接着特にヘム
加工部に対し極めて好適な接着シール方法に関する。
DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a method for adhering metal members, especially steel plate members, of vehicle bodies such as automobiles, airplanes, and ships, home appliances, and various other devices.
More specifically, the present invention relates to an adhesive sealing method which is extremely suitable for adhering metal members, particularly steel plate members, particularly hemmed parts.

従来金属製構造物は各部材ごとに所定の形状に成形され
た金属板を溶接、接合して所定の形状の構造物となし、
その後通常大部分のものは、塗装が施こされる。そして
これ等金属製構造物は通常溶接等の接合工程や塗装工程
の前に各種ゴムや樹脂組成物から成る液状組成物を用い
て接着やシールを行なっており、特に複雑な形状の部分
、例えばヘム加工部等の加工に際しては必須不可欠の工
程となっている。
Conventionally, metal structures are made by welding and joining metal plates formed into a predetermined shape for each member to create a structure with a predetermined shape.
After that, most things are usually painted. These metal structures are usually bonded or sealed using a liquid composition made of various rubbers or resin compositions before joining processes such as welding or painting processes, and parts with particularly complex shapes, such as This is an indispensable process when processing hem parts, etc.

例えば代表例として自動車々体を例にとれば、自動車車
体は各部材ごとにプレス成形された鋼板を溶接、接合し
ていわゆるホワイトボデーを作製し、その後脱脂処理及
び化成処理を経た後電着塗装し、さらに中塗り及び上塗
りからなる表面塗装工程を含む一連のラインを通すこと
により製造されている。そしてフード、ドア等のヘム加
工部には上記液状組成物から成る接着剤組成物を塗布し
、接着シールを行なっている。
For example, if we take automobile bodies as a typical example, automobile bodies are made by welding and joining press-formed steel plates for each member to create a so-called white body, which is then subjected to degreasing and chemical conversion treatment, and then electroplated. It is manufactured by passing through a series of lines including a surface coating process consisting of an intermediate coating and a top coating. Then, an adhesive composition made of the above-mentioned liquid composition is applied to hem-processed parts of hoods, doors, etc., and adhesive sealing is performed.

しかしながらこれ等組成物は本来絶縁体であり、接着、
シール用として使用した場合、電着塗膜が形成されず、
このため樹脂接着又はシール層と金属板との界面に於い
て塗膜が形成され難く錆の発生等好ましくない弊害が生
じる。これを防ぐため金属粉等の導電性粉末を配合した
組成物を用いる方法も開発されているが、耐熱性や耐久
性が低下し、また被接着、シール部材に油膜等が付着し
ている場合には、密着性が悪く作業性が劣ったり、シー
ル漏れを起こす等の不都合があった。
However, these compositions are originally insulators, and adhesives and
When used for sealing, no electrodeposition film is formed,
For this reason, it is difficult to form a coating film at the interface between the resin adhesive or sealing layer and the metal plate, resulting in undesirable problems such as rust formation. In order to prevent this, a method using a composition containing conductive powder such as metal powder has been developed, but the heat resistance and durability are reduced, and there are cases where an oil film etc. adheres to the adhered or sealing member. However, there were disadvantages such as poor adhesion, poor workability, and seal leakage.

更に加えてこれ等組成物を使用する場合次のような難点
が生じる。即ちこれ等組成物を塗布した後加工、例えば
ヘム加工を行なうと、塗膜の膜厚が一定にならず接着力
が不均一になったり、シール特性が不均一になり錆発生
の原因となる場合があり、また加工時の加圧により、余
分な組成物がはみ出し、手作業でのふき取り等が必要と
なり作業性が著しく悪くなる。特に熱硬化性樹脂を使用
した組成物の場合は熱硬化時の収縮を安定させるため、
このふき取り作業は欠かせないものである。
In addition, the following difficulties arise when using these compositions. In other words, if these compositions are processed after being applied, such as hemming, the thickness of the coating film will not be constant, resulting in uneven adhesion and uneven sealing properties, which may cause rust. In addition, due to the pressure applied during processing, excess composition may spill out, requiring manual wiping or the like, resulting in significantly poor workability. In particular, in the case of compositions using thermosetting resins, in order to stabilize shrinkage during thermosetting,
This wiping work is essential.

本発明者は上記従来の組成物を使用する場合に生ずる難
点を解消するため従来より鋭意研究を続けて来たが、こ
の研究に於いて組成物を塗布するという従来の手段に代
えて、接着シートを貼付するという新しい手段を採用す
るという全く新しい着想に至り、この着想に基づき更に
研究を続けた結果、エポキシ樹脂就中好ましくはある特
定のエポキシ樹脂を主体とし、これに導電性フィラー、
硬化剤及び発泡剤とを配合して調製した接着シートを使
用するときは従来の難点を解消出来ることを見出し、こ
こに本発明を完成するに至った。
The present inventor has been conducting extensive research in order to resolve the difficulties that arise when using the above-mentioned conventional compositions, and in this research, instead of the conventional means of applying the composition, adhesive We came up with a completely new idea of adopting a new method of pasting sheets, and as a result of further research based on this idea, we found that epoxy resin, preferably a certain epoxy resin, is the main ingredient, and conductive filler,
It has been discovered that the conventional difficulties can be overcome when using an adhesive sheet prepared by blending a curing agent and a foaming agent, and the present invention has now been completed.

即ち本発明は、金属板に、予めエポキシ樹脂、導電性フ
ィラー、硬化剤及び発泡剤を含有して成る接着シートを
貼付け、必要に応じて加工を施こした後、電着塗装を施
こし、次いで該電着塗膜を加熱焼付ける際に該接着シー
トを発泡硬化させることを特徴とする金属板の接着方法
に係るものである。
That is, in the present invention, an adhesive sheet containing an epoxy resin, a conductive filler, a hardening agent, and a foaming agent is attached to a metal plate in advance, and after being processed as necessary, electrodeposition coating is applied, The present invention relates to a method for bonding metal plates, characterized in that the adhesive sheet is foamed and cured when the electrodeposited coating film is then heated and baked.

本発明に依れば、接着シートを貼付するという手段を採
用しているので、接着剤を一定量均一に付着することが
可能となり、加工時に接着剤の膜厚が変化することもな
く、また加圧により接着性組成物がはみ出すことも極め
て少なく、作業性を著しく改善することが出来る。また
塗装の焼付工程で接着シートを同時に硬化させることに
より、機械的強度、耐熱性、耐久性の優れた接着シール
層を形成出来、接着力も均質で安定したものとなる。更
に加えてエポキシ樹脂として前記(イ)又は(ロ)のエ
ポキシ樹脂を使用する場合は油膜金属板に対しても初期
接着性が優れ、これに基づ〈従来の欠点も防ぐことが出
来る。また形成される接着シール層はスポット溶接性や
電着塗装性が良好なため金属板との界面において錆の発
生をきたすことなく外観にも優れたものとなる。特に本
発明に於いて注目すべきことは発泡剤を使用しているこ
とであり、電着塗装の焼付時に接着シート中の発泡剤は
加熱発泡し、被着体への密着、シール性が一段と向上し
、また金属板の複雑な加工部分たとえばヘム加工部等に
於いて時々生ずる恐れのあるシートと金属板とのすき間
部分等にも発泡することによりこれ等すき間部分が埋め
られ密着、シール性がこの点からも著しく優れる。また
このために貼付は作業性にもゆとりが生じ融通性が生じ
作業性が一段と向上する。
According to the present invention, since the method of pasting an adhesive sheet is adopted, it is possible to apply a certain amount of adhesive uniformly, and the film thickness of the adhesive does not change during processing. There is very little chance that the adhesive composition will protrude when pressure is applied, and workability can be significantly improved. Furthermore, by simultaneously curing the adhesive sheet during the painting baking process, it is possible to form an adhesive sealing layer with excellent mechanical strength, heat resistance, and durability, and the adhesive strength is also uniform and stable. In addition, when the epoxy resin (a) or (b) is used as the epoxy resin, it has excellent initial adhesion even to oil film metal plates, and based on this, the conventional drawbacks can be avoided. In addition, the formed adhesive sealing layer has good spot weldability and electrodeposition coating properties, so it does not cause rust at the interface with the metal plate and has an excellent appearance. What is particularly noteworthy about the present invention is the use of a foaming agent, and when the electrodeposition coating is baked, the foaming agent in the adhesive sheet is heated and foamed, further improving the adhesion and sealing properties to the adherend. The foam also fills the gaps between the sheet and the metal plate, which can sometimes occur in complex processed parts of the metal plate, such as hem processing parts, and improves adhesion and sealing properties. is significantly superior in this respect as well. In addition, for this reason, the workability of pasting is also more flexible, and the workability is further improved.

本発明に用いられる接着シートを構成するエポキシ樹脂
は通常のエポキシ樹脂を用いることができるが、好まし
くは(イ)長鎖アルキル鎮を有す室温で液状乃至半固形
状のエポキシ樹脂にビスフェノールAとエピクロルヒド
リンとから誘導された高分子量の熱可塑性樹脂を配合し
たものが用いられ、これらエポキシ樹脂は鎖状構成分子
が疎水性基であるため油脂骨との相溶性が良く、油膜網
板との初期接着性の向上に寄与する。又比較的長鎖の成
分を含むため樹脂の凝集力が高くシート形成能にすぐれ
る。
The epoxy resin constituting the adhesive sheet used in the present invention can be a normal epoxy resin, but preferably (a) bisphenol A is added to an epoxy resin that is liquid or semi-solid at room temperature and has a long-chain alkyl group. Epoxy resins containing high molecular weight thermoplastic resins derived from epichlorohydrin are used, and since the chain constituent molecules of these epoxy resins are hydrophobic groups, they have good compatibility with oil and fat bones, and the initial contact with oil film network plates. Contributes to improved adhesion. Also, since it contains a relatively long chain component, the resin has a high cohesive force and excellent sheet forming ability.

長鎖アルキル主鎖としては炭素数5〜50程度好ましく
は8〜30程度のものである。このような樹脂としては
、ポリエチレングリコール、ポリプロピレングリコール
、エチレンオキシドとプロピレンオキシドとのブロック
状コポリマーのα・ω−グリコールなどのポリマーとエ
ピクロルヒドリンとの反応によるエポキシ樹脂;ポリア
クロレインやポリビニルケトンのカルボニル基とS−イ
リドの反応より誘導されたエポキシ樹脂;ダイマー酸、
トリマー酸、不飽和高級脂肪酸またはそのエステルから
誘導されたエポキシ樹脂等が挙げられる。
The long alkyl main chain has about 5 to 50 carbon atoms, preferably about 8 to 30 carbon atoms. Such resins include epoxy resins produced by reacting epichlorohydrin with polymers such as polyethylene glycol, polypropylene glycol, and α/ω-glycol, which is a block copolymer of ethylene oxide and propylene oxide; - Epoxy resin derived from reaction of ylide; dimer acid,
Examples include epoxy resins derived from trimer acids, unsaturated higher fatty acids, or esters thereof.

上記エポキシ樹脂のなかでも炭素数10〜20の長鎖ダ
イマー酸より誘導されたエポキシ樹脂が好ましく用いら
れ、例としてリノール酸ダイマーとエピクロルヒドリン
とから誘導されたエポキシ樹脂等が挙げられる。これら
の樹脂を用いると、油面接着性にとくに好結果が得られ
、また耐水性や耐薬品性等に優れた接着シートが得られ
る。
Among the above epoxy resins, epoxy resins derived from long chain dimer acids having 10 to 20 carbon atoms are preferably used, and examples include epoxy resins derived from linoleic acid dimer and epichlorohydrin. When these resins are used, particularly good results can be obtained in terms of adhesion to oil surfaces, and adhesive sheets with excellent water resistance, chemical resistance, etc. can be obtained.

なお、上記の長鎖アルキル主鎖を有するエポキシ樹脂と
共に通常のエポキシ樹脂を全体の50重量%以下の割合
で併用することは可能である。
Note that it is possible to use an ordinary epoxy resin together with the above-mentioned epoxy resin having a long alkyl main chain in a proportion of 50% by weight or less of the total.

又この発明に用いられるビスフェノールAとエピクロル
ヒドリンとから誘導される高分子量の熱可塑性樹脂とは
、次の構造式; であられされる反復単位を含む平均分子量が少なくとも
10,000以上のものである。このような熱可塑性樹
脂の代表的な市販品としてユニオンカーバイド社製商品
名フェノキシ樹脂(1分子当たりの反復単位が82〜1
23個、軟化点212F1平均分子量25,000〜3
5,000)を挙げることが出来る。これ等ビスフェノ
ールAとエピクロルヒドリンとから誘導される高分子量
の熱可塑性樹脂は、その使用に際しては液状または半固
形状のエポキシ樹脂と配合して使用される。
Further, the high molecular weight thermoplastic resin derived from bisphenol A and epichlorohydrin used in the present invention has an average molecular weight of at least 10,000 or more including repeating units represented by the following structural formula. A typical commercially available thermoplastic resin is a phenoxy resin manufactured by Union Carbide Co., Ltd. (having a repeating unit of 82 to 1 repeating unit per molecule).
23 pieces, softening point 212F1 average molecular weight 25,000-3
5,000). These high molecular weight thermoplastic resins derived from bisphenol A and epichlorohydrin are used in combination with liquid or semi-solid epoxy resins.

この際上記熱可塑性樹脂は通常5〜70重量%好ましく
は10〜40重量%の割合で使用され、これ単独で使用
されることは極めて少ない。併用される液状または半固
形状のエポキシ樹脂としては特に制限されないが、通常
上記長鎖アルキル鎖を有するものは使用しない。
In this case, the thermoplastic resin is usually used in an amount of 5 to 70% by weight, preferably 10 to 40% by weight, and is rarely used alone. The liquid or semi-solid epoxy resin used in combination is not particularly limited, but those having the above-mentioned long alkyl chains are usually not used.

尚本発明で使用するエポキシ樹脂についての液状または
半固形状は通常室温での性状を示す。
The liquid or semi-solid state of the epoxy resin used in the present invention usually exhibits properties at room temperature.

また硬化剤としては室温で安定で高温下で活性を示すも
のが好ましく、特に高温下で分解して少なくとも1個の
活性水素含有アミンを生ずるような窒素含有化合物たと
えばモノユレア、ボリュレア、ヒドラジド、チオユレア
などを使用するのが望ましい。具体的には3−(p−ク
ロロフヱニル)−1・1−ジメチルユレア、2・4−ビ
ス(N・N−ジメチルカルバミド)トルエン、ジシアン
ジアミドなどが挙げられる。
The curing agent is preferably one that is stable at room temperature and exhibits activity at high temperatures, particularly nitrogen-containing compounds that decompose at high temperatures to produce at least one active hydrogen-containing amine, such as monourea, volurea, hydrazide, thiourea, etc. It is preferable to use Specific examples include 3-(p-chlorophenyl)-1,1-dimethylurea, 2,4-bis(N,N-dimethylcarbamide)toluene, and dicyandiamide.

もちろんその他の硬化剤たとえば酸無水物、イミダゾー
ル類、イミダシリン類などを用いることも可能であり、
これらの具体例としては無水フタル酸、無水マレイン酸
、無水ドデシルコハク酸、無水へキサヒドロフタル酸、
無水メチルナジック酸、無水ピロメリット酸、無水ベン
ゾフェノンテトラカルボン酸、無水ジクロルコハク酸、
無水クロレンディソク酸、2−メチルイミダゾール、2
−エチル−4−メチルイミダゾール、2−フェニルイミ
ダール、2−ウンデシルイミダゾール、2−ヘプタデシ
ルイミダゾール、2−エチルイミダゾール、2−イソプ
ロピルイミダゾール、2・4−シメチルイミダゾ−ル、
2−フェニル−4−メチルイミダゾール、2−メチルイ
ミダシリン、2−エチル−4−メチルイミダシリン、2
−フェニルイミダシリン、2−ウンデシルイミダシリン
、2−ヘプタデシルイミダシリン、2−エチルイミダシ
リン、2−イソプロピルイミダシリン、2・4−ジメチ
ルイミダシリン、2−フェニル−4−メチルイミダシリ
ンなどが挙げられる。
Of course, it is also possible to use other curing agents such as acid anhydrides, imidazoles, imidacillins, etc.
Specific examples of these include phthalic anhydride, maleic anhydride, dodecylsuccinic anhydride, hexahydrophthalic anhydride,
Methylnadic anhydride, pyromellitic anhydride, benzophenonetetracarboxylic anhydride, dichlorosuccinic anhydride,
Chlorenedisocyanic anhydride, 2-methylimidazole, 2
-ethyl-4-methylimidazole, 2-phenylimidal, 2-undecylimidazole, 2-heptadecyl imidazole, 2-ethylimidazole, 2-isopropylimidazole, 2,4-dimethylimidazole,
2-phenyl-4-methylimidazole, 2-methylimidacillin, 2-ethyl-4-methylimidacillin, 2
-Phenylimidacilline, 2-undecylimidacilline, 2-heptadecylimidacilline, 2-ethylimidacilline, 2-isopropylimidacilline, 2,4-dimethylimidacillin, 2-phenyl-4 - Methylimidacillin and the like.

これら硬化剤の種類および配合量としては、電着塗膜を
加熱焼付ける際に接着シートがほぼ硬化する(ここで完
全に硬化しなくとも後工程での中塗りおよび上塗り工程
での加熱焼付は時に完全硬化してもよい)ように、加熱
焼付けの条件に応じて適宜設定することができる。一般
的な配合量としては、エポキシ樹脂100重量部に対し
て0.5〜130、好ましくは5〜50重量部程置部あ
る。
The type and amount of these curing agents should be such that the adhesive sheet is almost cured when the electrodeposited coating is heated and baked (even if it is not completely cured, the heat baking in the intermediate coating and top coating processes in the subsequent process is sufficient). It can be set as appropriate depending on the conditions of heating and baking. The general amount is 0.5 to 130, preferably 5 to 50 parts by weight per 100 parts by weight of the epoxy resin.

この発明においては導電性充てん剤を混合することが重
要であるが、このような充てん剤としては銀、パラジウ
ム、銅、アルミニウム、鉄、ニッケル等の金属粉末や、
カーボンブラック、グラファイト等の金属粉末以外の無
機物質が挙げられる。
In this invention, it is important to mix a conductive filler, and such fillers include metal powders such as silver, palladium, copper, aluminum, iron, nickel, etc.
Examples include inorganic substances other than metal powders such as carbon black and graphite.

使用量は導電性充てん剤の種類、形状、粒子径等により
異なるが通常エポキシ樹脂100重量部に対して10〜
700重量部、好ましくは20〜200重量部程度の置
部で用いられる。また形状、粒子径等も広い範囲から適
宜に選択して決定されれば良いが、たとえば粒状、針状
、鱗片状の形状が例示出来る。粒状の場合は粒径的0.
1〜400μ好ましくは0.5〜200μ程度、針状の
場合は直径(短かい方)約0.1〜500μ好ましくは
0.5〜300μ程度;アスペクト比が5〜200好ま
しくはlO〜150程度である。
The amount used varies depending on the type, shape, particle size, etc. of the conductive filler, but it is usually 10 to 10 parts by weight per 100 parts by weight of the epoxy resin.
It is used in an amount of about 700 parts by weight, preferably about 20 to 200 parts by weight. Further, the shape, particle diameter, etc. may be appropriately selected and determined from a wide range, and examples thereof include granular, acicular, and scaly shapes. In the case of granules, the particle size is 0.
1 to 400μ, preferably about 0.5 to 200μ; if needle-shaped, the diameter (shorter one) is about 0.1 to 500μ, preferably about 0.5 to 300μ; aspect ratio is about 5 to 200, preferably about 10 to 150 It is.

また鱗片状の場合は厚さ約0.1〜500μ好ましくは
0.1〜300μで、アスペクト比は5〜200好まし
くは10〜150程度である。
In the case of scales, the thickness is approximately 0.1 to 500 μm, preferably 0.1 to 300 μm, and the aspect ratio is approximately 5 to 200, preferably 10 to 150.

また本発明に於いて使用される発泡剤としては、各種の
この種組成物に使用される発泡剤が広い範囲から適宜に
選択して使用されるが、通常一般的には、アゾジカルボ
ンアミド、アゾビスイブチロニトリルのようなアゾ系化
合物、ジニトロソペンタメチレンテトラミンのようなニ
トロソ化合物、バラトルエンスルホニルヒドラジッド、
4・4′−オキシビスベンゼンスルホニルヒドラジソド
のようなヒドラジッド系化合物などを広く使用できる。
The blowing agent used in the present invention is appropriately selected from a wide range of blowing agents used in various compositions of this type, but generally, azodicarbonamide, Azo compounds such as azobisbutyronitrile, nitroso compounds such as dinitrosopentamethylenetetramine, valatoluenesulfonyl hydrazide,
A wide variety of hydrazide compounds such as 4,4'-oxybisbenzenesulfonylhydrazisodo can be used.

これらは単独又は混合して場合によっては尿素、カルボ
ン酸の金属塩などの発泡助剤と共に用いてもよい。この
ような発泡剤(もしくはこれと発泡助剤)の使用割合は
一般に樹脂分100重量部に対して0.5〜5重量部程
度であって、硬化させる温度で発泡が起こり、加熱後の
発泡倍率が実用上的1.1〜5倍となるようにするのが
よい。
These may be used alone or in combination, optionally together with foaming aids such as urea and metal salts of carboxylic acids. The proportion of such blowing agents (or foaming aids) is generally about 0.5 to 5 parts by weight per 100 parts by weight of the resin, and foaming occurs at the curing temperature and foaming after heating. Practically speaking, the magnification is preferably set to 1.1 to 5 times.

この発明における接着、シール用導電性樹脂組成物には
、上記の各成分の他に必要に応じて各種の配合剤を添加
することができる。たとえば耐熱性をより向上させる目
的でフェニル−β−ナフチルアミン、ジフェニル−p−
フェニレンジアミン、ジターシャリブチル−4−メチル
フェノール、バラフェニルフェノール、ステアリン酸カ
ルシウム、ジラウリルチオジプロピオネートなどの安定
剤や老化防止剤を、接着性をより向上させる目的でジエ
ステル類、エステルガム、アルキッド樹脂、クマロン樹
脂を、タレ防止やコストダウンを図る目的でクレー、タ
ルク、炭酸カルシウム、シリカ、炭酸バリウム、アスベ
ストなどの充てん剤を、それぞれ添加することできる。
In addition to the above-mentioned components, various compounding agents can be added to the conductive resin composition for adhesion and sealing according to the present invention, if necessary. For example, phenyl-β-naphthylamine, diphenyl-p-
Stabilizers and anti-aging agents such as phenylene diamine, di-tert-butyl-4-methylphenol, paraphenylphenol, calcium stearate, and dilaurylthiodipropionate are added to diesters, ester gums, and alkyds for the purpose of further improving adhesive properties. Fillers such as clay, talc, calcium carbonate, silica, barium carbonate, and asbestos can be added to the resin and coumaron resin for the purpose of preventing sagging and reducing costs.

その抱着色剤などを配合してもよい。これらの配合量は
、エポキシ樹脂100重量部に対して5〜300重量部
程度置部ればよい。
A coloring agent and the like may also be added. The blending amount of these components may be about 5 to 300 parts by weight per 100 parts by weight of the epoxy resin.

本発明に於いて使用する接着シートを調製するに際して
は、その調製方法自体は同等限定されず、各種の方法で
製造することが出来るが、通常法のような方法で行なう
。まず前記エポキシ樹脂、硬化剤、導電性フィラー、発
泡剤、その他必要に応じて各種のその他の添加剤を、常
温又は硬化の起こらない程度の温度(但しわずかに起こ
っても良い)で適宜な手段たとえば撹拌釜、各種ニーダ
−1二本又は三本ミキシングロール等で混合し、導電性
樹脂組成物を作製する。次いで該組成物を未硬化又は半
硬化の状態で適宜な成形手段、たとえばロールコータ−
、ナイフコーター等のコーター類、各種プレス成形、押
出成形等によりシート状に成形して接着シートを調製す
る。
When preparing the adhesive sheet used in the present invention, the method of preparation itself is not equally limited and can be produced by various methods, but it is carried out by a conventional method. First, the epoxy resin, curing agent, conductive filler, foaming agent, and various other additives as necessary are added at room temperature or at a temperature that does not cause curing (however, a slight amount of curing may occur) using appropriate means. For example, the conductive resin composition is prepared by mixing in a stirring pot, various kneaders, two or three mixing rolls, and the like. Next, the composition is molded in an uncured or semi-cured state using a suitable molding means, such as a roll coater.
, a coater such as a knife coater, various press moldings, extrusion molding, etc. to form the adhesive sheet into a sheet shape.

本発明に於いては上記接着シートを調製するに際して各
種基材を挿入することが出来、これによりシート形状保
持性並びにシートの補強の効果を賦与することが出来る
。このような基材としては寒冷紗、各種材質の粗目シー
ト、金網等の網状物、各種材質の織布、不織布等の多孔
性材料からなるものが好ましいものとして例示出来る。
In the present invention, various base materials can be inserted when preparing the adhesive sheet, thereby imparting sheet shape retention and sheet reinforcement effects. Preferred examples of such substrates include those made of porous materials such as cheesecloth, coarse sheets made of various materials, net-like materials such as wire mesh, and woven fabrics and nonwoven fabrics made of various materials.

かくして調製された本発明に係る接着シートを用いて本
発明法を実施するに際しては、該接着シートを被着体た
る金属板就中好ましくは鋼板等に貼付け、必要に応じ各
種の加工たとえばヘム加工を行ない、常法に準じて脱脂
処理、化成処理等を行なった後電着塗装を行なう。この
際の電着塗料としても従来からこの種分野に於いて使用
されて来たものが広い範囲で使用出来、たとえばエポキ
シ樹脂やアクリル樹脂系のものを例示出来る。次いで電
着塗膜の加熱焼付けを行なって電着塗膜の金属板面に対
する密着性を向上せしめる一方、接着シートの樹脂層を
ほぼ硬化させると共に発泡剤を分解発泡せしめ、発泡せ
しめながら徐々に硬化を行なって、接着シール特性を発
現せしめる。そして元来電着塗装の付き廻り性の悪い接
着剤と金属板の界面や狭さく部にも電着塗装され、優れ
た防錆性が賦与される。
When carrying out the method of the present invention using the adhesive sheet according to the present invention thus prepared, the adhesive sheet is attached to a metal plate, preferably a steel plate, etc. as an adherend, and is subjected to various processing, such as hemming, as necessary. After performing degreasing treatment, chemical conversion treatment, etc. according to conventional methods, electrodeposition coating is performed. In this case, a wide range of electrodeposition paints that have been conventionally used in this field can be used, such as epoxy resins and acrylic resins. Next, the electrodeposition coating is heated and baked to improve the adhesion of the electrodeposition coating to the metal plate surface, while the resin layer of the adhesive sheet is almost cured, and the foaming agent is decomposed and foamed, gradually curing while foaming. to develop adhesive sealing properties. Electrodeposition coating is also applied to the interface between the adhesive and the metal plate, which originally had poor coverage, and to the narrow areas, providing excellent rust prevention properties.

かくして電着塗装された金属板は必要に応じ更に中塗り
、上塗り等の塗装が行なわれる。
The metal plate thus electrodeposited is further coated with intermediate coats, top coats, etc. as necessary.

本発明法が適用される金属板としては各種の金属または
その合金の板状体が含まれ、たとえば代表例としては鉄
またはその合金たとえば鋼、アルミニウムまたはその合
金、銅またはその合金等を挙げることが出来、特に各種
鋼板を好ましいものとして例示出来る。鋼板の代表例と
しては熱延鋼板、冷延鋼板、亜鉛メッキ鋼板、亜鉛系合
金メッキ鋼板、プレコート鋼板等を挙げることが出来る
Metal plates to which the method of the present invention is applied include plates made of various metals or alloys thereof; typical examples include iron or alloys thereof, such as steel, aluminum or alloys thereof, copper or alloys thereof, etc. In particular, various steel plates can be exemplified as preferred. Typical examples of steel sheets include hot-rolled steel sheets, cold-rolled steel sheets, galvanized steel sheets, zinc alloy-plated steel sheets, and pre-coated steel sheets.

これ等金属板を接着する代表的な具体例はヘム加工時の
金属板の接着であるが、本発明法は何等このヘム加工の
場合に限定されることはなく、広く各種の接着、シール
等に適用される。
A typical example of bonding these metal plates is bonding metal plates during hemming, but the method of the present invention is not limited to this hemming process, and can be used for a wide variety of adhesives, seals, etc. Applies to.

以下に本発明法の代表例の一例として鋼板のヘム加工部
を形成する場合を採り上げて、図面を参考にして本発明
法を説明する。
The method of the present invention will be described below with reference to the drawings, taking up the case of forming a hemmed portion of a steel plate as a typical example of the method of the present invention.

第1図及び第2図は自動車々体のヘム加工部に本発明方
法を適用した一例を示すもので、第1図の内板(11と
外板(2)を本発明接着シートを介してヘム加工し、第
2図の如くヘム加工部を形成する。
Figures 1 and 2 show an example in which the method of the present invention is applied to the hem processing part of an automobile body. The hem is processed to form a hem processed part as shown in FIG.

更に詳しくはまず第1図のヘム加工部を形成する鋼板に
接着シート(3)を貼付ける。貼付部位は第1図aの内
板(1)あるいは第1図すの外板(2)のいずれでも良
く、適用箇所により適宜選択される。又貼付は幅は形成
されるヘム加工部の内板と外板の重ね合わせ部と同じ幅
又は少しはみ出した程度に予め設定する。尚この際これ
等鋼板は防錆油等が付着しているが、エポキシ樹脂とし
て前記(イ)又は(ロ)のものを使用した場合は、これ
等油膜鋼板にそのまま貼付けることが出来る。そしてそ
の後常法に従い組立、成形しヘム加工部が形成される。
More specifically, first, an adhesive sheet (3) is attached to the steel plate that will form the hemmed portion shown in FIG. The application site may be either the inner plate (1) in Fig. 1a or the outer plate (2) in Fig. 1, and is appropriately selected depending on the application location. Further, the width of the pasting is set in advance to be the same width as the overlapping part of the inner plate and outer plate of the hem processing part to be formed, or to the extent that it slightly protrudes. At this time, these steel plates are coated with rust preventive oil, but if the epoxy resin (a) or (b) is used as the epoxy resin, it can be directly attached to these oil film steel plates. Thereafter, the hem processing portion is formed by assembling and molding according to a conventional method.

尚念のために、本発明接着シートを用いて加工された上
記ヘム加工部の後工程を下記に記す。
As a reminder, the post-process of the hemmed part processed using the adhesive sheet of the present invention is described below.

上記ヘム加工部はその後常法による必要な処理が行なわ
れた後電着塗装され電着塗膜(4)が形成される。この
電着塗膜(4)に加熱焼付を行なって、鋼板面に対する
膜(4)の密着性を向上せしめると共に、接着シート(
3)中の樹脂層を発泡させ、同時にほぼ硬化させること
により良好な接着、シール特性が発現される。そして本
来電着塗装の付き廻り性の悪い接着剤と鋼板の界面Xや
狭さく部Yにも樹脂の導電性に起因して電着塗装性が良
好でありすぐれた防錆効果が得られる。さらに後工程で
の中塗りおよび上塗り塗装後の加熱焼付で完全硬化し、
耐熱性、耐久性などによりすぐれる硬化発泡接着シール
層を構成することになり、界面Xや狭さく部Yの防錆効
果は一層高められる。
The hemmed portion is then subjected to necessary treatments by conventional methods and then electrocoated to form an electrocoated film (4). This electrodeposited coating film (4) is heated and baked to improve the adhesion of the film (4) to the steel plate surface, and also to improve the adhesion of the film (4) to the steel sheet surface.
3) Good adhesion and sealing properties are achieved by foaming the resin layer inside and substantially curing it at the same time. Furthermore, due to the conductivity of the resin, the electrodeposition coating property is good even on the interface X and the narrowed part Y between the adhesive and the steel plate, which originally have poor coverage for electrodeposition coating, and an excellent antirust effect can be obtained. Furthermore, it is completely cured by heating and baking after the intermediate coating and top coating in the subsequent process.
A cured foam adhesive sealing layer with excellent heat resistance and durability is formed, and the rust prevention effect of the interface X and narrowed portion Y is further enhanced.

このようにして電着塗膜(4)を形成した後常法に準じ
て内外板(1)、(2)の中塗り及び上塗り塗装を行な
い、さらに所定のラインを通すことにより防錆効果のす
ぐれた自動車々体が得られる。
After forming the electrodeposited coating film (4) in this way, the inner and outer panels (1) and (2) are coated with an intermediate coat and a top coat according to a conventional method. Excellent car bodies can be obtained.

本発明接着シートには、前記で説明した通り各種基材が
挿入される場合があるが、この基材として下記に示す特
定の基材を選択して使用することにより、その基材使用
に基づく独特の効果が更に付加され著しく優れた接着方
法となる。これ等基材とその優れた効果について下記に
説明する。
As explained above, various base materials may be inserted into the adhesive sheet of the present invention, but by selecting and using the specific base material shown below as the base material, it is possible to It has additional unique effects and becomes an extremely superior bonding method. These base materials and their excellent effects will be explained below.

この場合は次の様な効果が期待出来る。即ち第3〜4図
は基材として熱収縮性基材を単独で使用した接着シート
、また第5〜6図は熱収縮性基材と非熱収縮性基材とを
組合わせて使用した接着シートを用いてヘム加工する場
合の例を夫々示したものである。第3図に示す様に熱風
を矢印の方向から吹付けると、その風圧で接着シート(
3)が第4図の様に弯曲し、同時に熱風の熱により熱収
縮性基材(5)が熱収縮を起こすため、後作業としての
接着シート(3)の貼付は作業が容易となる。第5〜6
図に於いても第3〜4図と同様に接着シート(3)は風
圧並びに熱風により内板(11側に弯曲するが、この際
非収縮性基材(6)が拘束層となり、より一層内板il
l側に曲がり更に作業性が向上する。また第7図に示す
様に、接着シートとして通常の基材(即ち非熱収縮性基
材)を用いてヘム加工する場合に外板(2)、接着シー
ト(3)及び内板(1)とで空隙部(7)が生じる場合
があるが、基材として熱収縮性基材を用いた接着シート
の場合は第8図に示す様に、加熱−こより接着シートの
厚みが大きくなり、ヘム加工時に空隙部(7)に樹脂が
注入され外板(2)に密着されることとなり、極めて有
利である。
In this case, the following effects can be expected. That is, Figures 3 and 4 show adhesive sheets using a heat-shrinkable base material alone, and Figures 5-6 show adhesive sheets that use a combination of a heat-shrinkable base material and a non-heat-shrinkable base material. Examples of hemming using sheets are shown. As shown in Fig. 3, when hot air is blown from the direction of the arrow, the pressure of the air is applied to the adhesive sheet (
3) is curved as shown in FIG. 4, and at the same time the heat-shrinkable base material (5) undergoes heat shrinkage due to the heat of the hot air, making it easier to attach the adhesive sheet (3) as a post-work. 5th to 6th
In the figure, as in Figures 3 and 4, the adhesive sheet (3) bends toward the inner plate (11) due to wind pressure and hot air, but at this time, the non-shrinkable base material (6) acts as a restraining layer, making it even more difficult to bend. Inner plate il
It bends toward the l side, further improving workability. Furthermore, as shown in Fig. 7, when hemming is performed using a normal base material (i.e., non-heat shrinkable base material) as an adhesive sheet, the outer panel (2), the adhesive sheet (3), and the inner panel (1) are used. However, in the case of an adhesive sheet using a heat-shrinkable base material, as shown in Figure 8, the thickness of the adhesive sheet increases due to heating, and the hem During processing, resin is injected into the gap (7) and is brought into close contact with the outer plate (2), which is extremely advantageous.

(B)    として中 生  を  するとき。(B) When starting junior high school as a student.

この場合は被着体が曲面を有するときに接着シートをこ
の被着体に貼付する際の作業が特に容易となる。換言す
れば曲面被着体に対する接着シートの貼付時の追従性が
著しく優れるという効果がある。
In this case, when the adherend has a curved surface, the work of attaching the adhesive sheet to the adherend becomes particularly easy. In other words, there is an effect that the followability when applying the adhesive sheet to a curved adherend is extremely excellent.

第9図は伸縮性基材(12)に樹脂組成物を積層して調
製した本発明接着シー) (11)を示し、これを第1
0図に示す如く曲面を有する鋼板(内板、13)に貼付
ける。この際通常の基材を使用した接着シートでは曲面
に対する追従性が悪く、しわになったり、鋼板より浮き
上がることがあり、作業性が悪くなる場合がある。この
様な場合にヘム加工を行なうとこれ等しわや浮き上がっ
た部分は完全にシールされていないために錆発生の原因
となり、またスポット溶接を行なう際にはスポット溶接
が行ない難い。而して本発明法に従って接着シート(1
1)を貼付けるに際しては、第10図に示す通り平板部
分は伸縮性基材(12)が伸びない樺に貼付ける。
Figure 9 shows an adhesive sheet (11) of the present invention prepared by laminating a resin composition on a stretchable base material (12).
Attach it to a steel plate (inner plate, 13) that has a curved surface as shown in Figure 0. At this time, adhesive sheets using ordinary base materials have poor followability to curved surfaces and may wrinkle or rise above the steel plate, resulting in poor workability. If hemming is performed in such a case, these wrinkles and raised areas will not be completely sealed and will cause rust, and spot welding will be difficult to perform. According to the method of the present invention, the adhesive sheet (1
When pasting 1), as shown in FIG. 10, the flat plate portion is pasted to birch where the stretchable base material (12) does not stretch.

その際、−片(14)または他端(14’)を固定して
おくと貼付は作業が一段と容易になる。第11図に示す
如く曲面(15)、(15’)の凸曲面(1め部では接
着シートを若干伸ばしながら貼付けるのが好ましい。次
いで第12図に示す如く外板(16)を内板(13)と
接着シー) (11)を介して一体化し、溶接してヘム
加工部を形成する。
At that time, if the - piece (14) or the other end (14') is fixed, the work of pasting becomes easier. As shown in Fig. 11, the convex curved surfaces (15) and (15') (at the first part, it is preferable to stretch the adhesive sheet a little while attaching it.) Next, as shown in Fig. 12, attach the outer panel (16) to the inner panel. (13) and adhesive sheet) (11) and weld to form a hem processing part.

この際使用する伸縮性基材としては、1.1〜゛5.0
倍、好ましくは1.1〜3.0倍の伸縮倍率のものが使
用される。この際該倍率が5倍以上のものは樹脂塗布む
らが生じ易い。好ましい例としては例えば東洋結社製商
品名CLBあるいはウェザ−クロスUS 2000等が
挙げられる。伸縮方向としては長さ方向に伸縮する基材
が好ましい。
The elastic base material used at this time is 1.1 to 5.0
A material with an expansion/contraction ratio of 1.1 to 3.0 times, preferably 1.1 to 3.0 times, is used. In this case, if the magnification is 5 times or more, uneven resin coating is likely to occur. Preferred examples include CLB (trade name) manufactured by Toyo Keisha, Weather Cloth US 2000, and the like. As for the direction of expansion and contraction, a base material that expands and contracts in the length direction is preferable.

この基材を使用する場合、エポキシ樹脂組成物としては
30℃での粘度が1×lO〜1×lOボイズ(高化式フ
ローテスター、ノズル径1.0mm、10kg/荷重)
であるものを使用することが望ましい。
When using this base material, the epoxy resin composition has a viscosity of 1 x 1 O to 1 x 1 O at 30°C (Koka flow tester, nozzle diameter 1.0 mm, 10 kg/load)
It is desirable to use one that is.

この際粘度が1×103 ボイズに達しないと樹脂の凝
集力が低下しシート保持性が困難となる場合があり、ま
たlXl0’ ボイズより高くなると接着シートとした
場合表面のタンクが欠乏し、基材の伸縮に追従出来ず樹
脂層にクラックが入ったり、初期の油面粘着性が劣る場
合がある。
At this time, if the viscosity does not reach 1 x 103 voids, the cohesive force of the resin may decrease and sheet retention may become difficult, and if the viscosity exceeds 1 Cracks may appear in the resin layer due to the inability to follow the expansion and contraction of the material, and the initial oil surface tack may be poor.

この場合は賦形性を有する金属製シート状物であるため
に、被着体の形状に沿って貼付可能となり、貼付作業性
が極めて容易となる効果ばかりでなく、特に上記金属製
シート状物が、被着体である金属板と接触すること(た
とえばスポット溶接等により接触すること)により犠牲
陽極となり、防錆効果が一段と優れるという効果がある
In this case, since it is a metal sheet with formability, it can be pasted along the shape of the adherend, and the pasting work is extremely easy. However, when it comes into contact with the metal plate that is the adherend (for example, by spot welding or the like), it becomes a sacrificial anode, which has the effect of further improving the rust prevention effect.

この際使用される金属製シート状物としては、手で簡単
に被金属板に沿わせて貼付けが出来る程度の賦形性を有
する物が使用され、たとえば連続シート板や各種金属線
を適宜組合わせてネット状にしたものや適当な間隔を有
する様に金属線を平行に並べたもの等が例示出来る。金
属の種類としてはマグネシウム、アルミニウム、亜鉛等
のものが好ましく、これ等のものは、金属板就中鋼板と
接触することによって鋼板に対し犠牲陽極となるもので
あり、これにより防錆性が著しく向上する。
The metal sheet material used at this time is one with shapeability that allows it to be easily pasted along the metal plate by hand; for example, continuous sheet plates and various metal wires are assembled as appropriate. Examples include a net-like structure and a structure in which metal wires are arranged in parallel at appropriate intervals. Preferable types of metal include magnesium, aluminum, zinc, etc. These metals act as sacrificial anodes for the steel plate when they come into contact with the metal plate, especially the steel plate, and as a result, they have excellent rust prevention properties. improves.

これ等金属製シート状物を基材とした接着シートを製造
するに際しては、前記樹脂組成物を未硬化または半硬化
の状態で金属製シート状物の表裏両面に塗布、ラミネー
ト、又は押出成形等の適宜の手段で積層一体化すれば良
い。この際粘着性に差異のある2種類の樹脂組成物を夫
々片面づつに積層したものは、賦形時に粘着性の弱い樹
脂層側を押圧することとなり、直接賦形加工出来るので
作業性が一段と優れたものとなる。
When producing an adhesive sheet using a metal sheet as a base material, the resin composition is coated on both the front and back surfaces of the metal sheet in an uncured or semi-cured state, laminated, extruded, etc. They may be laminated and integrated by any suitable means. In this case, when two types of resin compositions with different adhesive properties are laminated on one side each, the resin layer side with weaker adhesiveness is pressed during shaping, and the shaping process can be performed directly, which further improves work efficiency. It will be excellent.

また本発明に於いては、接着シートを調製するに際し、
特に樹脂層を高粘着性の第1の樹脂層と、非または弱粘
着性の第2の樹脂層との積層体とすることにより、次の
様な効果を得ることが出来る。
In addition, in the present invention, when preparing the adhesive sheet,
In particular, by forming the resin layer into a laminate of a highly adhesive first resin layer and a non- or weakly adhesive second resin layer, the following effects can be obtained.

即ち高粘着樹脂層側で被着金属体との貼付を行ない、一
方同時に非または弱粘着樹脂層側より、手または適宜な
治具により押圧して貼付けが出来るために著しく貼付作
業性が優れる。この場合をヘム加工を例にとって第13
〜14図に基づき説明する。
That is, the adhesive can be attached to the adherend metal body on the side of the high-adhesive resin layer, and at the same time, the adhesive can be applied by pressing by hand or with an appropriate jig from the side of the non- or weakly-adhesive resin layer, resulting in extremely excellent adhesion workability. Taking this case as an example of hem processing, the 13th
This will be explained based on FIGS.

先ず接着シー) (23)の高粘着層(24)を第13
図の内板(21)に貼付し、一方同時に弱又は非粘着層
(25)を押圧して所定の位置に密着せしめ固定し、そ
の後常法に従い成形し、スポット溶接を行なってヘム加
工部が形成される。尚この際、弱又は非粘着層(25)
と外板(22)、または内板(21)との間では、成形
時の圧着及びスポット溶接により完全に固定される。高
粘着層たる第1の樹脂層は通常50℃での溶融粘度が5
×10+ボイズ未満、好ましくは5.0X10” 〜3
.0X10” ボイズ程度であり、また第2の樹脂層は
50℃での溶融粘度が5X104ボイズ以上、好ましく
は6.0Xl(1”〜1.0×106 ボイズ程度であ
る。この様な所定の粘度を有する第1及び第2の樹脂層
は上記組成物の配合比を適宜に選択することによって容
易に得ることが出来る。上記配合比を調製した組成物か
ら常法に従って夫々のシートを調製する。かくして得ら
れたシートを夫々積層して一体化させて2層からなる本
発明シートを調製する。この際の積層一体化は第1樹脂
層の粘着性をそのまま利用して行なってもよいし、ある
いは完全に硬化が進まない程度に加熱して融着させても
良い。
First, the high adhesive layer (24) of (23)
Attach it to the inner plate (21) shown in the figure, and press the weak or non-adhesive layer (25) at the same time to firmly adhere and fix it in place. Then, form it according to the usual method and spot weld it to make the hem processing part. It is formed. At this time, a weak or non-adhesive layer (25)
and the outer plate (22) or the inner plate (21) are completely fixed by crimping and spot welding during molding. The first resin layer, which is a high adhesive layer, usually has a melt viscosity of 5 at 50°C.
Less than ×10+boys, preferably 5.0X10” ~3
.. The melt viscosity of the second resin layer at 50°C is about 5 x 104 voids or more, preferably about 6.0 x l (1" to 1.0 x 106 voids). Such a predetermined viscosity The first and second resin layers having the above composition can be easily obtained by appropriately selecting the blending ratio of the above composition.The respective sheets are prepared from the composition having the above blending ratio according to a conventional method. The sheets thus obtained are laminated and integrated to prepare a two-layer sheet of the present invention. At this time, the lamination and integration may be carried out by directly utilizing the adhesiveness of the first resin layer, or Alternatively, it may be heated and fused to such an extent that curing does not proceed completely.

以下に実施例を示して本発明を具体的に説明するが、以
下の例に於いて部とあるは重量部を示すものとする。
The present invention will be specifically explained below with reference to Examples, in which parts are by weight.

実施例 エピコート#871(油化シェル社製ダイマー酸変性エ
ポキシ樹脂)80部、エピコート#1001  (油化
シェル社製ビスフェノールA型固形エポキシ樹脂)20
部を溶解釜にて溶融混合し、粘稠な組成物を得た。この
組成物100部にジシアンジアミド(日本カーバイド社
製エポキシ樹脂硬化剤)5部、キュアゾール2MZ−A
ZTNE(四国化成社製エポキシ樹脂硬化剤)5部、F
E−9(水和化成社製発泡剤)0.5部、グラファイト
粉末100部、アスベスト粉末3部を配合し、通常のミ
キシングロールで混練りし、導電性樹脂組成物を得た。
Examples Epicoat #871 (dimer acid-modified epoxy resin manufactured by Yuka Shell Co., Ltd.) 80 parts, Epicoat #1001 (bisphenol A type solid epoxy resin manufactured by Yuka Shell Co., Ltd.) 20 parts
The components were melted and mixed in a melting pot to obtain a viscous composition. To 100 parts of this composition, 5 parts of dicyandiamide (an epoxy resin curing agent manufactured by Nippon Carbide Co., Ltd.) and Curesol 2MZ-A were added.
ZTNE (epoxy resin curing agent manufactured by Shikoku Kasei Co., Ltd.) 5 parts, F
0.5 parts of E-9 (a blowing agent manufactured by Hydraulic Chemical Co., Ltd.), 100 parts of graphite powder, and 3 parts of asbestos powder were blended and kneaded using a normal mixing roll to obtain a conductive resin composition.

この組成物を100℃に加熱し、ロールコルターを用い
て0.3■1厚にシート成形し、導電性接着シートを得
た。
This composition was heated to 100° C. and formed into a sheet with a thickness of 0.3×1 using a roll coulter to obtain a conductive adhesive sheet.

次に板厚0.6〜0.81の冷延鋼板から成る車体の組
立てにおいて、第1図(alに示す如く内板illの端
面に予め上記接着シートを貼付け、その後ヘム加工を行
ない、内板(11と外板(21を接着シート(3)を介
して一体化し、スポット溶接を行ない、ヘム加工部を形
成した。この車体に脱脂処理、化成処理および電着塗装
処理を施こし、ついで焼付炉にて180℃で20分間加
熱焼付けた。尚電着塗料としては、エポキシ樹脂系のも
のを用いた。
Next, in assembling a car body made of cold-rolled steel plates with a plate thickness of 0.6 to 0.81, the adhesive sheet described above is pasted on the end face of the inner plate ill in advance, as shown in Figure 1 (al), and then hemmed. The plate (11) and the outer plate (21) were integrated via an adhesive sheet (3) and spot welded to form a hem processing section.This car body was subjected to degreasing treatment, chemical conversion treatment, and electrodeposition painting treatment, and then It was heated and baked in a baking oven at 180° C. for 20 minutes.The electrodeposition paint used was an epoxy resin-based one.

上記の加熱焼付けで接着シートは発泡・硬化反応を起こ
し、均一で強固な接着シールが行なわれた。さらに接着
剤露出表面が電着塗膜で完全に覆われ、さらにシール特
性が向上した。その後、中塗りおよび上塗り塗装工程で
それぞれ】40℃で30分の加熱焼付けが行なわれ、こ
の加熱焼付けによって上記接着剤がほぼ完全に硬化した
The adhesive sheet caused a foaming and hardening reaction during the heating and baking process, resulting in a uniform and strong adhesive seal. Furthermore, the exposed surface of the adhesive was completely covered with an electrodeposition coating, further improving sealing properties. Thereafter, heating baking was carried out at 40° C. for 30 minutes in each of the intermediate coating and top coating steps, and the adhesive was almost completely cured by this heating baking.

このようにして製造した車体は錆の発生が起こりにくり
、耐腐食性はきわめて良好であった。
The vehicle body manufactured in this way was less susceptible to rust and had extremely good corrosion resistance.

【図面の簡単な説明】[Brief explanation of the drawing]

第1〜14図はいずれも本発明法実施の一例を示す図面
であり、各図面中の番号は夫々次のことを示す。 +l) 、 、 、 、内板      (21) 、
 、内板f21 、 、 、 、外板      (2
2) 、 、外板+31 、 、 、 、接着シート 
  (23) 、 、接着シート+41 、 、 、 
、電着塗膜    (24) 、 、高粘着層+51 
、 、 、 、熱収縮基材   (25) 、 、非粘
着層+61 、 、 、 、非収縮基材 (7) 、 、 、 、空隙部 (11) 、 、接着シート (12) 、 、伸縮性基材 (13) 、 、内板 (14) 、 、一端 (15)、、曲面 (16)、、外板 (以上) 特許出願人 日東電気工事株式会社 第1図 第2図
1 to 14 are drawings showing an example of implementing the method of the present invention, and the numbers in each drawing indicate the following, respectively. +l) , , , , inner plate (21) ,
, inner plate f21 , , , outer plate (2
2) , , Outer panel +31 , , , , Adhesive sheet
(23) , , Adhesive sheet +41 , , ,
, Electrodeposition coating (24) , High adhesive layer +51
, , , , Heat-shrinkable base material (25) , , Non-adhesive layer +61 , , , , Non-shrinkable base material (7) , , , Gap portion (11) , , Adhesive sheet (12) , , Stretchable base material (13) , , Inner plate (14) , One end (15) , Curved surface (16) , Outer plate (and above) Patent applicant Nitto Electric Works Co., Ltd. Figure 1 Figure 2

Claims (1)

【特許請求の範囲】 1、金属板に、予めエポキシ樹脂、導電性フィラー、硬
化剤及び発泡剤を含有して成る接着シートを貼付け、必
要に応じて加工を施した後、電着塗装を施こし、次いで
該電着塗膜を加熱焼付ける際に該接着シートを発泡硬化
させることを特徴とする金属板の接着方法。 2、上記接着シートが、金属板に充分密着、貼付出来る
程度の高い粘着性をもつ第1の樹脂層と、金属板に対し
粘着性をもたないか又は充分に密着、貼付出来ない程度
の弱い粘着性しか有しない第2の樹脂層とを積層して成
るものである特許請求の範囲第1項記載の接着方法。 3、上記接着シートが熱収縮性基材またはこれと非収縮
性基材に、エポキシ樹脂、導電性フィラー、硬化剤及び
発泡剤を含浸一体化させたものである特許請求の範囲第
1または2項記載の接着方法。 4、上記接着シートが伸縮性基材に、エポキシ樹脂、導
電性フィラー、硬化剤及び発泡剤を含浸一体化させたも
のである特許請求の範囲第1または2項記載の接着方法
。 5、上記接着シートが賦形性を有する金属製シート状物
に、エポキシ樹脂、導電性フィラー、硬化剤及び発泡剤
を含浸一体化させたものである特許請求の範囲第1また
は2項記載の接着方法。 6、エポキシ樹脂が長鎖アルキル主鎖を有する液状乃至
半固形状のエポキシ樹脂、若しくは液状乃至半固形状の
エポキシ樹脂にビスフェノールAとエピクロルヒドリン
とから誘導された高分子量の熱可塑性樹脂を配合したも
のから成る油面接着性にすぐれる接着シートである特許
請求の範囲第1項〜5項のいずれかの項に記載の接着方
法。 7、導電性フィラーが金属粉末又は(及び)カーボンブ
ラックやグラファイトの如き無機物質から成る特許請求
の範囲第1〜6項のいずれかの項に記載の接着方法。 8、金属板が鋼板、アルミニウム又はその合金板、銅ま
たはその合金板である特許請求の範囲第1〜7項のいず
れかの項に記載の接着方法。 9、加工がヘム加工部を形成するものである特許請求の
範囲第1〜8項のいずれかの項に記載の接着方法。 10、金属板が自動車車体等の鋼板であり、加工がヘム
加工部を形成する加工である特許請求の範囲第1〜8項
のいずれかの項に記載の接着方法。
[Claims] 1. An adhesive sheet containing an epoxy resin, a conductive filler, a hardening agent, and a foaming agent is pasted on a metal plate in advance, processed as necessary, and then electrocoated. A method for adhering metal plates, which comprises curing and foaming the adhesive sheet when baking the electrodeposited coating film. 2. The adhesive sheet has a first resin layer that has high adhesiveness enough to adhere to and stick to the metal plate, and a first resin layer that does not have adhesiveness to the metal plate or has a high adhesiveness that does not allow it to adhere and stick to the metal plate sufficiently. The bonding method according to claim 1, wherein the bonding method is formed by laminating a second resin layer having only weak adhesiveness. 3. Claim 1 or 2, wherein the adhesive sheet is a heat-shrinkable base material or a non-shrinkable base material impregnated with an epoxy resin, a conductive filler, a curing agent, and a foaming agent. Adhesion method described in section. 4. The bonding method according to claim 1 or 2, wherein the adhesive sheet is a stretchable base material impregnated with an epoxy resin, a conductive filler, a curing agent, and a foaming agent. 5. The adhesive sheet according to claim 1 or 2, wherein the adhesive sheet is formed by impregnating and integrating an epoxy resin, a conductive filler, a curing agent, and a foaming agent into a metal sheet-like material having formability. Adhesion method. 6. A liquid or semi-solid epoxy resin having a long alkyl main chain, or a liquid or semi-solid epoxy resin blended with a high molecular weight thermoplastic resin derived from bisphenol A and epichlorohydrin. The bonding method according to any one of claims 1 to 5, which is an adhesive sheet having excellent oil surface adhesion. 7. The bonding method according to any one of claims 1 to 6, wherein the conductive filler comprises metal powder and/or an inorganic substance such as carbon black or graphite. 8. The bonding method according to any one of claims 1 to 7, wherein the metal plate is a steel plate, an aluminum or its alloy plate, or a copper or its alloy plate. 9. The bonding method according to any one of claims 1 to 8, wherein the processing is to form a hem processed portion. 10. The bonding method according to any one of claims 1 to 8, wherein the metal plate is a steel plate for an automobile body or the like, and the processing is processing to form a hem processing part.
JP16373884A 1984-08-02 1984-08-02 Method of bonding metallic plate Pending JPS6141537A (en)