JPS61209258A - Amino resin molding material - Google Patents
Amino resin molding materialInfo
- Publication number
- JPS61209258A JPS61209258A JP5144485A JP5144485A JPS61209258A JP S61209258 A JPS61209258 A JP S61209258A JP 5144485 A JP5144485 A JP 5144485A JP 5144485 A JP5144485 A JP 5144485A JP S61209258 A JPS61209258 A JP S61209258A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- molding material
- vinyl chloride
- amino resin
- amino
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔技術分野〕
本発明は配線器具、電気器具、厨房器具等に用いられる
アミノ樹脂成形材料に関するものである。DETAILED DESCRIPTION OF THE INVENTION [Technical Field] The present invention relates to an amino resin molding material used for wiring appliances, electrical appliances, kitchen appliances, etc.
従来、アミノ樹脂成形材料はその優れた耐アーク性、耐
トラツキング性、電気絶縁性、耐燃性、着色性、表面硬
度、耐溶剤性Kかかわらず耐インサートクツツク性に欠
点があった。この対策として有機長繊維を添加すること
が試みられたがこれでも成形時、金型から成形品を取出
し冷却する迄の成形品が暖かい間に圧入金属を圧入する
必要のある時間的制約、正大穴と圧入金属の寸法精度管
理醇KMMがあった。Conventionally, amino resin molding materials have had drawbacks in insert resistance despite their excellent arc resistance, tracking resistance, electrical insulation, flame resistance, coloring properties, surface hardness, and solvent resistance. As a countermeasure to this problem, attempts have been made to add organic long fibers, but even with this, there are time constraints and the need to press-fit the press-fit metal while the molded product is still warm before the molded product is removed from the mold and cooled. There was KMM, a tool for controlling the dimensional accuracy of large holes and press-fit metal.
本発明の目的とするところは耐インサートクラツク性に
優れたアミノ樹脂成形材料を提供することにある。An object of the present invention is to provide an amino resin molding material with excellent insert crack resistance.
本発明はアミノ樹脂に、補強材、充填剤、硬化剤、離型
剤、着色剤等を添加してなるアミノ樹脂成形材料におい
て、更Km化ビニ〜樹脂を添加したことを特徴とするア
ミノ樹脂成形材料で、塩化ビニル樹脂の添加によりアミ
ノ樹脂の曲げ弾性率が低下するため耐インサートクツツ
ク性を大巾に向上せしめることができたもので、以下本
発明の詳細な説明する。The present invention is an amino resin molding material made by adding a reinforcing material, a filler, a curing agent, a mold release agent, a coloring agent, etc. to an amino resin. This molding material is a molding material whose insertion resistance can be greatly improved because the flexural modulus of the amino resin is lowered by adding vinyl chloride resin.The present invention will be described in detail below.
本発明に用いる塩化ビニル樹脂は塩化ビニル樹脂、塩化
ビニリデン樹脂、ビニルフオ〃マール樹脂、塩素化塩化
ビニ/I/樹脂、ビニルプチヲー〜樹脂、プロピレン塩
ビ共重合樹脂、塩ビ酢ビ共重合樹脂等のようにストレー
ト塩化ビニル樹脂やその共重合樹脂の単独、混合物の樹
脂のみ或は該樹脂に安定剤、充填剤、離型剤等を添加し
た成形材料であって本よく任意であるが好ましくは10
0メツシユアンダーの粒径であることが分散性、耐イン
サートクラツク性のパフツキを防止するために望ましい
ことである。又、塩化ビニル樹脂の量は全体量の1〜2
0重量%(以下単に%と記す)であることが望ましい。Vinyl chloride resins used in the present invention include vinyl chloride resin, vinylidene chloride resin, vinyl formal resin, chlorinated vinyl chloride/I/resin, vinyl petio resin, propylene vinyl chloride copolymer resin, vinyl chloride vinyl acetate copolymer resin, etc. A molding material consisting of a straight vinyl chloride resin or a copolymer resin thereof alone, a mixture thereof, or a stabilizer, a filler, a mold release agent, etc. added to the resin, which may be optional but preferably 10
A particle size of 0 mesh under is desirable in order to prevent puffiness in dispersibility and insert crack resistance. Also, the amount of vinyl chloride resin is 1 to 2 of the total amount.
It is desirable that the content be 0% by weight (hereinafter simply referred to as %).
即ち1%未満では耐インサートクラツク性が低下する傾
向にあり、り%をこえると耐熱性が低下する傾向にある
からである。アミノ樹脂としてはエリア樹脂、メラミン
樹脂、グアナミン樹fgj等のアミノ樹脂の単独、混合
物、変性物を用いることができる。補強材、充填剤、硬
化−剤、離型剤、着色剤等についてはアミノ樹脂成形材
料に用いられるものをそのまま用いることができる。塩
化ビニル樹脂の添加方法としては特に@定するものでな
くアミノ樹脂と補強材をニーダ−等で混練する樹脂含浸
段階で添加してもよく又、ポールミμ等で粉砕着色する
段階で添加してもよく任意である。That is, if it is less than 1%, insert crack resistance tends to decrease, and if it exceeds 1%, heat resistance tends to decrease. As the amino resin, amino resins such as area resin, melamine resin, and guanamine resin can be used alone, as a mixture, or as a modified product. As for reinforcing materials, fillers, curing agents, mold release agents, colorants, etc., those used in amino resin molding materials can be used as they are. There is no particular method for adding the vinyl chloride resin, and it may be added at the resin impregnation stage where the amino resin and reinforcing material are kneaded with a kneader or the like, or it may be added at the stage of crushing and coloring with a Paulmi μ or the like. is also often optional.
以下本発明を実施例にもとすいて説明する。The present invention will be explained below using examples.
実施例1乃至4と従来例
第1表のN合表に従って材料をポールミルで6時間粉砕
、着色してメラミン樹脂成形材料を得、該成形材料を成
形して成形品を得た。The materials were ground in a pole mill for 6 hours and colored according to the combination of Examples 1 to 4 and Conventional Example N in Table 1 to obtain a melamine resin molding material, and the molding material was molded to obtain a molded article.
第 1 表
重量部
注
帯1樹脂量50%
牽2平均分子量1100 、粒度150メツシユ、スト
レート塩化ビニル樹脂
〔発明の効果〕
*源側1乃至4と従来例のメラミン樹脂成形品に成形品
の冷却後直径2.4藺の真鍮ビスを圧入する圧入試験及
び成形品の曲げ弾性率は第2表に明白なように本発明の
アミノ樹脂成形材料から得られた成形品の性能はよく本
発明のアミノ樹脂成形材料の優れていることを確認した
。Table 1 Parts by weight Note: Resin amount 50%, average molecular weight 1100, particle size 150 mesh, straight vinyl chloride resin [Effects of the invention] * Cooling of the melamine resin molded products of the source side 1 to 4 and the conventional example As clearly shown in Table 2, the performance of the molded products obtained from the amino resin molding material of the present invention was good in the press-fit test in which a brass screw with a diameter of 2.4 mm was inserted and the flexural modulus of the molded products. The superiority of amino resin molding materials was confirmed.
第2表Table 2
Claims (2)
着色剤等を添加してなるアミノ樹脂成形材料において、
更に塩化ビニル樹脂を添加したことを特徴とするアミノ
樹脂成形材料。(1) Amino resin with reinforcing material, filler, curing agent, mold release agent,
In amino resin molding materials with addition of colorants, etc.
An amino resin molding material characterized by further adding vinyl chloride resin.
あることを特徴とする特許請求の範囲第1項記載のアミ
ノ樹脂成形材料。(2) The amino resin molding material according to claim 1, wherein the amount of vinyl chloride resin is 1 to 20% by weight based on the total amount.