JPS61146504A - Manufacture of centrifugal mortar lining pipe having flexibility - Google Patents
Manufacture of centrifugal mortar lining pipe having flexibilityInfo
- Publication number
- JPS61146504A JPS61146504A JP26936584A JP26936584A JPS61146504A JP S61146504 A JPS61146504 A JP S61146504A JP 26936584 A JP26936584 A JP 26936584A JP 26936584 A JP26936584 A JP 26936584A JP S61146504 A JPS61146504 A JP S61146504A
- Authority
- JP
- Japan
- Prior art keywords
- mortar
- pipe
- centrifugal
- flexibility
- manufacture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
（産業上の利用分野）
この発明は遠心モルタルライニングパイプの製作に際し
てモルタルクラック防止剤全モルタル層内に含有させる
ことにより可撓性を付与する遠心モルタルライニングパ
イプの製造方法に関する。Detailed Description of the Invention (Industrial Application Field) This invention provides a method for manufacturing a centrifugal mortar lined pipe in which flexibility is imparted by incorporating a mortar crack inhibitor into the entire mortar layer during the production of the centrifugal mortar lined pipe. Regarding.
（従来の技術）
一般にバイブ内ライニング法としては例えば特開昭５０
−１１０４６０号などで知られるように遠心力により内
層ライニングを行なうことが知られている。(Prior art) Generally, as a vibrator lining method, for example,
It is known that inner lining is performed using centrifugal force, as is known from Japanese Patent No. 110460.
而して、従来の遠心モルタルライニングパイプはモルタ
ル層の乾燥及び取扱い等によるパイプの変形や衝撃によ
りモルタル層忙クラックやパイプ内側表面との剥離が発
生し、問題視されている。Conventional centrifugal mortar-lined pipes have been viewed as problematic because cracks in the mortar layer and separation from the inner surface of the pipe occur due to deformation and impact of the pipe due to drying of the mortar layer and handling.
この対策として手車シのモルタルライニングパイプの製
作の分野ではモルタル配合材料中にクラック防止剤を配
合することにより、可撓性のあるモルタル層が得られる
ことは知られているＯ
しかしながら同じように遠心ライニング用のモルタル配
合材料中にクラック防止剤を配合するとクラック防止剤
も遠心力によりモルタル層外に抜は出てしまい、モルタ
ル層内に留めることができない。As a countermeasure to this problem, it is known in the field of manufacturing mortar lining pipes for handcarts that a flexible mortar layer can be obtained by incorporating a crack preventive agent into the mortar compound. When a crack preventive agent is blended into the mortar compounding material for centrifugal lining, the crack preventive agent also comes out of the mortar layer due to centrifugal force and cannot be retained within the mortar layer.
（発明が解決しようとする問題点）
本発明は遠心力金かけた後にクラック防止剤をモルタル
中に留めて、モルタル層に発生するクラックやパイプ内
側表面とモルタル層との剥離を防止することを目的とす
るものである。(Problems to be Solved by the Invention) The present invention retains a crack preventive agent in the mortar after applying centrifugal force to prevent cracks occurring in the mortar layer and separation of the mortar layer from the inner surface of the pipe. This is the purpose.
（問題点を解決するための手段）
本発明は以上の様な問題点を有利に解決したものであシ
、その要旨はモルタルクラック防止剤をパイプ内面に塗
布後その内周にモルタルライニングを施し回転により遠
心力を付与すること全特徴とする可撓性を有する遠心モ
ルタルライニングパイプの製造方法である。(Means for Solving the Problems) The present invention advantageously solves the above-mentioned problems, and its gist is to apply mortar crack preventive agent to the inner surface of the pipe and then apply mortar lining to the inner periphery of the pipe. This is a method for manufacturing a flexible centrifugal mortar lining pipe characterized by applying centrifugal force through rotation.
以下本発明を図面に示す実施例、態様例に基づいて具体
的に説明する。The present invention will be specifically described below based on embodiments and embodiments shown in the drawings.
第１図において２はパイプ１内面の遠心モルタルライニ
ング装置であり、ミキサー３より供給されたモルタル等
混線材４は回転するパイＩプ１内に装入される。遠心モ
ルタルライニングパイプの製作に際し、パイプ内面の表
面調整を行い、清浄にした後モルタル投入前にパイプ内
面にクラック防止剤５ｔ２０〜２００ ｆ／ｄ散布又は
刷毛等で塗布する。０〜３０分間程度の乾燥硬化時間を
取った後予め適正な硬さくフロー値１３５〜１６５）に
調整したモルタル混線材４をパイプ内面に投入して２０
〜４０Ｇの遠心力を７〜３０分程度かける。In FIG. 1, reference numeral 2 denotes a centrifugal mortar lining device for the inner surface of the pipe 1, and a mixing material 4 such as mortar supplied from a mixer 3 is charged into the rotating pipe 1. When manufacturing a centrifugal mortar lined pipe, the inner surface of the pipe is prepared and cleaned, and then a crack preventive agent of 5t20 to 200 f/d is sprayed or applied with a brush or the like on the inner surface of the pipe before mortar is added. After drying and curing for about 0 to 30 minutes, a mortar mixed wire material 4 adjusted in advance to an appropriate hardness and flow value of 135 to 165) was poured into the inner surface of the pipe.
Apply centrifugal force of ~40G for about 7 to 30 minutes.
遠心モルタルライニング前に塗布されたクラック防止剤
５は遠心力によって、モルタル内の水分がモルタル層の
表面に抜は出るのと同時にパイプ内側表面からモルタル
層内に入り、遠心力により脱水され密度金高められたモ
ルタル内に留まる。The crack preventive agent 5 applied before centrifugal mortar lining enters into the mortar layer from the inner surface of the pipe at the same time as the water in the mortar is drawn out to the surface of the mortar layer by centrifugal force, and is dehydrated by centrifugal force and becomes dense gold. Remains within the raised mortar.
クラック防止剤の分布は、パイプ内側表面からモルタル
層内及び極く一部はモルタル層の表面に至ることもある
。The crack inhibitor may be distributed from the inner surface of the pipe into the mortar layer and, to a very small extent, to the surface of the mortar layer.
第２図は本発明によって得られたパイプ断面の一部を示
しておシ、パイプ１の内面にはクラック防止剤５が付着
し、そのさらに内面にはモルタル混線剤４とクラック防
止剤５とが混合された状態となる。FIG. 2 shows a part of a cross section of a pipe obtained according to the present invention. A crack preventive agent 5 is attached to the inner surface of the pipe 1, and a mortar mixer 4 and a crack preventive agent 5 are attached to the inner surface of the pipe 1. becomes a mixed state.
（発明の効果）
本発明は前記の通シであシ、本発明に従えば従来の遠心
モルタルライニングパイプに発生する
（ａ） モルタル層に発生するクラック及び（ｂ）
パイプ内側表面とモルタル層の剥離を無くすることが
できる。(Effects of the Invention) The present invention solves the above-mentioned problems, and according to the present invention, it solves (a) cracks that occur in the mortar layer and (b)
Peeling of the mortar layer from the inner surface of the pipe can be eliminated.
第１図は本発明を説明するための遠心モルタルライニン
グ装置を示し、第２図は本発明によって得られたパイプ
の一部断面図である。
１・・・パイプ ２・・・遠心モルタルラ
イニング装置３・・・ミキサー ４・・・モルタル
等混線材５・・・クラック防止剤FIG. 1 shows a centrifugal mortar lining device for explaining the present invention, and FIG. 2 is a partial sectional view of a pipe obtained by the present invention. 1... Pipe 2... Centrifugal mortar lining device 3... Mixer 4... Mixing material such as mortar 5... Crack prevention agent
Claims (1)
にモルタルライニングを施し回転により遠心力を付与す
ることを特徴とする可撓性を有する遠心モルタルライニ
ングパイプの製造方法。A method for manufacturing a flexible centrifugal mortar lined pipe, which comprises applying a mortar crack preventive agent to the inner surface of the pipe, applying mortar lining to the inner circumference, and applying centrifugal force by rotation.