JPS60251160A - Mortar composition - Google Patents
Mortar compositionInfo
- Publication number
- JPS60251160A JPS60251160A JP10805584A JP10805584A JPS60251160A JP S60251160 A JPS60251160 A JP S60251160A JP 10805584 A JP10805584 A JP 10805584A JP 10805584 A JP10805584 A JP 10805584A JP S60251160 A JPS60251160 A JP S60251160A
- Authority
- JP
- Japan
- Prior art keywords
- gypsum
- mortar
- portland cement
- mortar composition
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Abstract] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
本発明はモルタル組成物に関するものであり、詳しくは
、特に可撓性があり（変形能にすぐれた）、および、／
又は弾力性があるモルタル組成物に関するものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a mortar composition, in particular a mortar composition that is particularly flexible (highly deformable) and/or
Or it relates to an elastic mortar composition.
１「産業上の利用分野」
本発明のモルタル組成物は、建築、土木、船舶、車輌、
橋梁等の他、種々の分野に利用されるものである。1 "Industrial Application Fields" The mortar composition of the present invention is applicable to architecture, civil engineering, ships, vehicles,
In addition to bridges, it is used in a variety of other fields.
「従来の技術」
例えば、ポルトランドセメントにポリマーディスパーン
ョン及び適宜の骨材を配合したモルタル組成物はいわゆ
る、ポリマーセメントコンクリートとして公知である。"Prior Art" For example, a mortar composition prepared by blending Portland cement with a polymer dispersion and a suitable aggregate is known as a so-called polymer cement concrete.
このモルタル組成物は耐水性に優れており、通常、主に
、建造物の内壁あるいは外壁、電車又は船舶などの床材
の表面を化粧するためのモルタルとして利用されている
。そのため、モルタルを基材となる金属板、発泡コンク
リート板、石膏板または合成樹脂等にスプレーすること
により、その表面に塗布されるが、硬化後のモルタルに
クランクが入りやすい欠点がある。This mortar composition has excellent water resistance, and is usually used as a mortar for decorating the surfaces of flooring materials for interior or exterior walls of buildings, trains, ships, etc. For this reason, mortar is applied to the surface of a metal plate, foamed concrete plate, gypsum board, synthetic resin, or the like as a base material by spraying it, but it has the disadvantage that cranks tend to get stuck in the mortar after hardening.
この原因はモルタル自体の収縮により発生する場合と基
板自身がたわみを生じた際に、モルタルに可撓性がない
ために発生する場合と二つが考えられる。There are two possible causes for this: one is caused by shrinkage of the mortar itself, and the other is caused by the mortar's lack of flexibility when the substrate itself bends.
「発明が解決しようとする問題点」
本発明者等は上記実情に鑑み、従来のポリマーセメント
コンクリートとしての特性を保ちながら、モルタルの弾
性を改善することにより、モルタルのクランク発生を防
止する方法について種々検討した結果、ある特定の成分
を特定の割合で配合して得たモルタル組成物を用いると
きには、モルタル自体の収縮によるクラック発生も、ま
た、基材自身のたわみによるクラック発生も著しく抑制
できることを見い出し本発明を完成するに至った。"Problems to be Solved by the Invention" In view of the above-mentioned circumstances, the present inventors have proposed a method for preventing the occurrence of mortar cranks by improving the elasticity of mortar while maintaining the characteristics of conventional polymer cement concrete. As a result of various studies, we have found that when using a mortar composition obtained by blending certain ingredients in a specific ratio, it is possible to significantly suppress the occurrence of cracks due to the shrinkage of the mortar itself, as well as the occurrence of cracks due to the deflection of the base material itself. Heading: The present invention has been completed.
「問題点を解決するための手段」
すなわち、本発明の要旨は、■ポルトランドセメント、
■ポルトランドセメントに対し０．１〜１重量倍の石膏
、■ポルトランドセメント、石膏の和に対してポリマー
成分として０．０５〜０゜８重量倍のポリマーディスパ
ージョンと■適宜の骨材及び■ポルトランドセメント、
石膏の和に対してポリマーディスパージョン中の水を含
めて０゜３５〜１重量倍の水を配合することを構成とし
ている。"Means for solving the problems" That is, the gist of the present invention is: ■Portland cement,
■Gypsum in an amount of 0.1 to 1 times the weight of Portland cement, ■Polymer dispersion as a polymer component of 0.05 to 0.8 times the weight of the sum of Portland cement and gypsum, ■Appropriate aggregate, and ■Portland cement. nt,
The composition is such that 0.35 to 1 times the weight of water, including the water in the polymer dispersion, is blended with respect to the total amount of gypsum.
本発明においては、モルタル組成物としてポルトランド
セメント、石膏、ポリマーディスパージョン、骨材およ
び水の五成分を含有することを必須条件としている。In the present invention, it is essential that the mortar composition contains five components: portland cement, gypsum, polymer dispersion, aggregate, and water.
ポルトランドセメントとしては、通常の市販品が挙げら
れ、石膏は半水石膏、三水石膏ともに本発明に使用でき
るが、半水石膏がより効果的である。石膏の含有量はポ
ルトランドセメントに対して０，１〜１重量倍、好まし
くは０．２〜０．５−重量倍である。As Portland cement, common commercially available products can be mentioned, and both gypsum hemihydrate and gypsum trihydrate can be used in the present invention, but gypsum hemihydrate is more effective. The content of gypsum is 0.1 to 1 times by weight, preferably 0.2 to 0.5 times by weight relative to Portland cement.
次に本発明で用いられるポリマーディスパージョンとし
ては、水性のものであれば、特に限定されるものではな
く、従来、公知の種々のものが使用できるが、通常、ポ
リアクリル酸エステル、ポリ酢酸ビニル、ポリ塩化ビニ
リデン−ポリ塩化ビニル、ポリプロピオン酸ビニル、ポ
リエチレン−ポリ酢酸ビニル、ポリプロピレンなどの熱
可塑性樹脂エマルジョン；エポキシ樹脂などの熱硬化性
樹脂エマルジョン；アスファルト、ゴムアスファルト、
パラフィンなどの瀝青質エマルジョン；りロロプレンゴ
ム、スチレン−ブタジェンゴム、アクリロニトリル−ブ
タジェンゴム、メタクリル酸メチル−ブタジェンゴム、
ブタジェンゴムなどの合成ゴムラテックス等及びこれら
の混合物が挙げられる。これらのポリマーディスパージ
ョンの含有量は、ポルトランドセメント、石膏の和に対
してポリマー成分として、０．０５〜０．８重量倍、好
ましくは０．１〜０．５重量倍である。この含有量が上
記範囲より低いと、可撓性が著しく小さくなり、又モル
タルの耐水性も劣り、逆に、前記範囲より多い場合、可
撓性は大きくなるものの、硬化速度が遅くなり、強度、
耐久性が劣り又、火に対する抵抗性も弱くなり、原材料
費も極端に大きくなるので好ましくない。Next, the polymer dispersion used in the present invention is not particularly limited as long as it is aqueous, and various conventionally known ones can be used, but usually polyacrylate, polyvinyl acetate, etc. , thermoplastic resin emulsions such as polyvinylidene chloride-polyvinyl chloride, polyvinyl propionate, polyethylene-polyvinyl acetate, polypropylene; thermosetting resin emulsions such as epoxy resins; asphalt, rubber asphalt,
Bituminous emulsions such as paraffin; polypropylene rubber, styrene-butadiene rubber, acrylonitrile-butadiene rubber, methyl methacrylate-butadiene rubber,
Examples include synthetic rubber latex such as butadiene rubber, and mixtures thereof. The content of these polymer dispersions is 0.05 to 0.8 times by weight, preferably 0.1 to 0.5 times by weight, as a polymer component relative to the sum of Portland cement and gypsum. If this content is lower than the above range, the flexibility will be significantly reduced and the water resistance of the mortar will also be poor.On the other hand, if it is higher than the above range, the flexibility will be high but the curing speed will be slow and the strength will be low. ,
It is undesirable because it has poor durability, weak resistance to fire, and extremely high raw material costs.
本発明では、この石膏とポリマーディスパージョンの存
在によって、より一層、可撓性に優れ、しかも、強度も
高く、クラックなどの発生しに（い良好なモルタル層を
得ることができる。In the present invention, due to the presence of the gypsum and the polymer dispersion, it is possible to obtain a mortar layer that is even more flexible, has high strength, and is free from cracks and the like.
又、骨材の種類としては、通常、例えば５〜７号の砕砂
、川砂利、川砂、砕石、砕砂などが必要に応じて用いら
れるが、砕砂を用いるのが最も好ましい。骨材の含有量
は通常、ポルトランドセメント、石膏の和に対して０．
３〜４重量倍、好ましくは０．５〜３重量倍である。As for the type of aggregate, for example, crushed sand of size 5 to 7, river gravel, river sand, crushed stone, crushed sand, etc. are usually used as required, but it is most preferable to use crushed sand. The content of aggregate is usually 0.0% relative to the sum of Portland cement and gypsum.
The amount is 3 to 4 times by weight, preferably 0.5 to 3 times by weight.
本発明では上述の各成分の他に、本発明の特性を失わな
い範囲において、例えば、顔料、分散剤、充填剤などを
適宜、加えても差し支えない。In the present invention, in addition to the above-mentioned components, for example, pigments, dispersants, fillers, etc. may be appropriately added as long as the characteristics of the present invention are not lost.
上述の各成分を用いてモルタル層を実際に形成させるに
は、通常、各成分の混合物を常法に従って、該混合物に
対して０．３５−１重量倍の水（但し、ポリマーディス
パージョン中の水を含む）とともに充分に混練し、次い
で、これをモルタルタルスプレーガンなどでスプレーす
ることにより、実施することができる。In order to actually form a mortar layer using each of the above-mentioned components, the mixture of each component is usually prepared according to a conventional method, and the amount of water (0.35 to 1 times the weight of the mixture) (however, the amount of water in the polymer dispersion is This can be carried out by thoroughly kneading the mixture with water (including water) and then spraying the mixture with a mortar spray gun or the like.
「作用」
本発明のモルタル組成物の特徴である可撓性の発現す−
る原因は、前述の特定の割合でモルタルを調整した場合
、ポルトランドセメント、石膏、ポリマーディスパージ
ョン、水の複合系で以下のような相互作用によるものと
思われる。"Action" The flexibility characteristic of the mortar composition of the present invention is expressed.
This is thought to be due to the following interactions in the composite system of Portland cement, gypsum, polymer dispersion, and water when the mortar is adjusted to the specific proportions mentioned above.
すなわち、ポルトランドセメントの水和に関与するセメ
ント化合物であるＣ３５（ニーライト；３ ＣａＯ・Ｓ
ｉｏｗ ）、ＣｚＳ （ビーライト；２ＣａＯ−３ｔｏ
ｗ）、ＣａＡ （アルミネート；３ＣａＯ−Ａ１．２０
３）、ＣａＡＦ−（フェライト；３ＣａＯＨＡｌ２Ｏ２
・Ｆｅｚｅ３）が主に関与をするが、これに上記割合の
石膏が存在することによりＣ３Ａ （！： Ｃａ Ａ
Ｆは以下のような形で過剰のエトリンガイト （３Ｃａ
０−ＡｌｚＯ３・３ ＣａＳＯ４・３２Ｈ２０）が生成
する。That is, C35 (neerite; 3CaO・S) is a cement compound involved in the hydration of Portland cement.
iow ), CzS (Belite; 2CaO-3to
w), CaA (aluminate; 3CaO-A1.20
3), CaAF-(ferrite; 3CaOHAl2O2
・Feze3) is mainly involved, but due to the presence of gypsum in the above proportion, C3A (!: Ca A
F is excess ettringite (3Ca
0-AlzO3.3CaSO4.32H20) is generated.
このエトリンガイトは針状結晶で、石膏の水和による石
膏水和物の針状結晶とも絡み合い、この結晶相の間隙に
ポリマー分が適度に入り込むことにより優れた可撓性が
発現するものと考えられる。This ettringite is a needle-like crystal, which is intertwined with the needle-like crystals of gypsum hydrate caused by hydration of gypsum, and it is thought that excellent flexibility is achieved by appropriately entering the gap between the crystal phases of this ettringite. .
すなわち、Ｃ’３Ｓ、Ｃｐｓの水和物は得られるモルタ
ルの強度に寄与し、Ｃ３Ａ、Ｃ，ＡＦ及びＣａ５Ｏａよ
り得られる水和物がポリマーディスパージョンと絡み合
い適度の可撓性を発現するものと考えられる。In other words, the hydrates of C'3S and Cps contribute to the strength of the obtained mortar, and the hydrates obtained from C3A, C, AF and Ca5Oa are entangled with the polymer dispersion and develop appropriate flexibility. Conceivable.
更に、本発明では、その組成中のエトリンガイトの持つ
多量の結晶水の影響により、有機質を含む材料としても
、不燃性または難燃性に優れているという特性を持つ。Further, in the present invention, due to the influence of a large amount of crystallization water of ettringite in its composition, the material has excellent nonflammability or flame retardancy even as a material containing an organic substance.
−
したがって、本発明のモルタル組成物は、例えば、建築
物の壁、床等に使用し、その特性を充分に活かすことが
出来る。- Therefore, the mortar composition of the present invention can be used, for example, for walls and floors of buildings, and its properties can be fully utilized.
「実施例、比較例」
実施例１〜３及び比較例１〜３
ポルトランドセメント１００重量部に対して、第１表に
示す半水石膏及び７号珪砂を混合し、更に、これに第１
表に示すポリマーディスパージョンと水とともに、約５
分間ミキサーで混練し、モルタルスプレーガンにより、
７ｃｍＸ１５ｃｍ角で厚さになるように塗装し、１４日
間２０ ’Ｃ１６０％ＲＨの条件で養生後、直径Ｉｏｎ
■の円柱物体に沿って折り曲げテストを行ったが、その
結果は第２表の通りである。"Examples, Comparative Examples" Examples 1 to 3 and Comparative Examples 1 to 3 100 parts by weight of Portland cement was mixed with hemihydrate gypsum and No. 7 silica sand shown in Table 1, and further mixed with No.
With the polymer dispersion shown in the table and water, approx.
Knead with a mixer for a minute and then mix with a mortar spray gun.
Paint it to a thickness of 7cm x 15cm square, and after curing for 14 days at 20'C160%RH, the diameter of Ion
A bending test was conducted along the cylindrical object (2), and the results are shown in Table 2.
第１表
但し、第１表中に示される量を示す数値は重量部を示し
、ポリマーディスパージョンは固形分５θ％の合成樹脂
エマルジョンを使用し、その重量を示す。Table 1 However, the numerical values showing the amounts shown in Table 1 show parts by weight, and the polymer dispersion used was a synthetic resin emulsion with a solid content of 5θ%, and the weight is shown.
第２表
なお、折り曲げテストの試験方法を図をもって示したの
が、第１図、第２図であり、第１図は折り曲げ前の断面
図を示し、第２図は９０°の折り曲げを行った時の断面
図である。Table 2 Figures 1 and 2 show the test method for the bending test. Figure 1 shows a cross-sectional view before bending, and Figure 2 shows a 90° bend. FIG.
本発明の効果として、従来のポリマーセメントコンクリ
ートを構築物等に使用した場合、たわみ、振動、衝撃等
の原因によってヒビ割れたり、剥離したりすることがあ
ったが、本発明のモルタル組成物を使用することにより
、前述の欠陥が発生しなくなった。従って、従来はたわ
みの発生する場所では使用不可能であった不燃、もしく
は難燃性のモルタル組成物を使用することが可能となっ
た。As an effect of the present invention, when conventional polymer cement concrete is used for structures etc., it may crack or peel due to causes such as deflection, vibration, impact, etc., but the mortar composition of the present invention can be used. As a result, the above-mentioned defects no longer occur. Therefore, it has become possible to use non-combustible or flame-retardant mortar compositions, which could not previously be used in areas where deflection occurs.
第１図、第２図は実施例、比較例のモルタル組成物を折
り曲げ試験に供した場合の断面図を示すもので、第１図
は折り曲げ前、第２図は９０°折り曲げた時の状態を示
している。
１ −一一−−モルタル組成物、２ −−−−亜鉛メッ
キ板。
３−−−−−円柱物体
特許出願人 菊水化学工業株式会社
代表者 遠 山 昌 夫
図 面
第１図
第２図
亜船声ツキ板２
手続補正書
昭和５９年１２月１ユ日
１、事件の表示 昭和５９年特許顧第１０８０５５号２
、発明の名称 モルタル組成物
３、補正をする者
事件との関係 特許出願人
１４番１６号東洋ビル
５、補正の対象
明細書の「発明の詳細な説明」の欄
６、補正の内容
（１）第１０頁、第１表の実施例３のポリマーディスパ
ーノヨンの種類を示す「ポリアクリル酸エステルを「ポ
リアクリル酸エステル」と補正する。Figures 1 and 2 show cross-sectional views of the mortar compositions of Examples and Comparative Examples when subjected to a bending test. Figure 1 shows the state before bending, and Figure 2 shows the state after 90° bending. It shows. 1 -11--Mortar composition, 2 ---- Galvanized plate. 3----Cylindrical object patent applicant Masao Toyama Representative of Kikusui Chemical Co., Ltd. Figure 1 Figure 2 Subtitled board 2 Procedural amendments December 1, 1980, Case 1 Indication of 1982 Patent Registration No. 108055 2
, Title of the invention Mortar composition 3, Relationship with the case of the person making the amendment Patent applicant No. 14-16 Toyo Building 5, "Detailed description of the invention" column 6 of the specification subject to the amendment, Contents of the amendment (1) ) "Polyacrylic ester" indicating the type of polymer dispanyon in Example 3 in Table 1 on page 10 is corrected to "Polyacrylic ester."
Claims (1)
に対し、０．１〜１重量倍の石膏、■ポルトランドセメ
ント、石膏の和に対してポリマー成分として０．０５〜
０．８重量倍のポリマーディスパージョンと■適宜の骨
材及び■ポルトランドセメント、石膏の和に対してポリ
マーディスパージョン中の水を含めて、０．３５〜１重
量倍の水を配合することを特徴とするモルタル組成物。 ２ 骨材の含有量がポルトランドセメント、石膏の和に
対して０．３〜４重量倍である特許請求の範囲第一項記
載のモルタル組成物。 ３ 骨材が、珪砂である特許請求の範囲第１項又は第２
項記載のモルタル組成物。 ４ ポリマーディスパージョンが、水性の熱可塑性樹脂
エマルジョンである特許請求の範囲第１項又は第２項又
は第３項記載のモルタル組成物。[Claims] 1. Portland cement, ■ 0.1 to 1 times the weight of gypsum to Portland cement, ■ 0.05 to 100% of polymer component to the sum of Portland cement and gypsum.
It is recommended to mix 0.35 to 1 times the weight of water, including the water in the polymer dispersion, to the sum of 0.8 times the weight of the polymer dispersion, ■ appropriate aggregate, and ■ portland cement and gypsum. Characteristic mortar composition. 2. The mortar composition according to claim 1, wherein the content of aggregate is 0.3 to 4 times the weight of the sum of Portland cement and gypsum. 3 Claims 1 or 2 in which the aggregate is silica sand
The mortar composition described in . 4. The mortar composition according to claim 1, 2, or 3, wherein the polymer dispersion is an aqueous thermoplastic resin emulsion.